Search Documents

By P. Bolsaitis, L. Skolnick

A model of metallic solutions is postulated which explains the energy of formation of alloys on the basis of changes in electron density around solute and solvent atoms and changes in pairwise interactions between atoms. The model is based on the Wigner-Seitz cell model of metals, with the electronegativities of the metals as the parameter for the electron-attracting power of the constituent atoms. In contrast to models based on the description of cohesive energy in terms of pairwise interactions only, which require an empirical, adjustable correction parameter to the Berthe-lot relations in order to predict negative energies of formation, the electron cell model accounts for both negative and positive energies on the basis of parameters of the pure components. Calculated heats of mixing based on published parameters of the pure metals are found to compare favorably to experimental values, despite the absence of any adjustable parameters in the model. THE formulation of an "exact" quantum mechanical model for the energy of cohesion of metals reduces ultimately to the many-body problem and for a complete solution would require the knowledge of wave functions and energy levels of all the particles in the system. The case of alloys is further complicated by the fact that the potential fields around the constituent atoms are different and the matching of boundary conditions in terms of the resulting wave functions is still an unresolved mathematical problem. It appears that in spite of the numerous investigations that have led to an elucidation of many properties of the metallic state, the formulation of the Hume-Rothery rules in 1931 marks the lone accomplishment toward simple, qualitative prediction of the energy of formation of alloys. More recently Friedel'' and Arafa have utilized the modern concepts of the electronic structure in metals in combination with the Hume-Rothery rules to arrive at quantitative estimates of the energy of formation of alloys with low solute contents. The relative success of the Hume-Rothery rules and Friedel's and Arafa's studies encouraged broaching the subject of formulation of a model based on realistic physical parameters and of conceptual and mathematical simplicity that could be applied to alloys regardless of concentration. On the basis of the free-electron theory, the cohesive energy of pure metals can be expressed as a function of "valence" (number of free electrons per atom), lattice parameter (or density), and the ioniza-tion energy. In addition to the electronic contributions to cohesion, one has to consider the pairwise exchange interaction energy between neighboring ion cores and the contribution from van der Waals forces. The energy changes upon alloying are viewed as resulting primarily from a redistribution of electron densities around the ions (a simplification of the more basic concept of a change of the wave functions of the electrons in the presence of a perturbing potential field). In addition there is a change in the pairwise interactions between neighboring ions which is usually the only factor taken into account in commonly used adaptations of the quasichemical theory. The electronegativities of the metals forming the alloy are used as the measure of the electron-attracting power of the ions in the alloy and the difference in electronegativities as the driving force for changes in electron energy on alloying. The interplay of pairwise interactions and electronic forces results in positive or negative energies of formation of alloys. Results obtained for systems to which the free electron model is best applicable are in good agreement with experimental values. 1) COHESIVE ENERGY OF METALS IN TERMS OF THE ELECTRON CELL MODEL The simplest physical model of a metal is that of a lattice of positive charges immersed in a sea of uniform, negative charge distribution represented by the

Jan 1, 1969

By M. E. Wadsworth, T. D. Chatwin

The kinetics of sulfidization of hematite (Fe203) by H2S gas at various partial pressures have been determined over the temperature range of 170° to 500°C. The process was controlled by thin films of pyrite (FeS2) and troilite (FeS) which were protective and formed diffusional layers. At higher temperatures the thermodynamic drive to form FeS2 decreased, and consequently the rate of formation of FeS, decreased. Conditions for the development of thin layers of FeSz consisting of 10 to 100 atomic diameters are presented. Laboratory flotation results on synethetic ores indicate floatability identical to that of pyrite of normal xanthate flotation. The prospect of high-temperature sulfidization of metal oxides using H2S, S, or other sulfur bearing compounds is intriguing as a potential activation process for flotation since the thermodynamics are very favorable for a large number of systems. If the kinetic parameters are sufficiently well understood it may be possible to provide surface sulfide layers a few angstroms thick, thus imparting normal sulfide floatability characteristics to the oxide. For thin layers the total sulfur pick-up would be small except for very high surface area materials but in most cases this sulfur could be readily removed by roasting if necessary. The general reactions for the sul-fidization of metal oxide MxO, to a metal sulfide MpSq using H2S may be written for the three conditions py > xq; py < xq; and py = xq: A large thermodynamic advantage is obtained in many systems because of the relatively large negative free energy of formation of H,O compared to H,S. For the temperature range 2S° to 1500°C &apos; where AFOis the standard free energy and T is absolute temperature. As is evident from Eqs. 4 and 5, the free energy of formation of H ,0 is approximately 35 to 37 kilocalories per mole greater than that for H,S over broad variations of temperature. For oxide-sulfide systems as outlined above, sulfidization may be expected to occur for the conditions: Groups I and 111: that is, if the terms on the right are more negative than those on the left the reaction is expected to occur thermodynamically. The value hFg,(,) is included in Eq. 6 since hFLzs is based upon gaseous S2 rather than the normal reference state, orthorhombic sulfur. The

Jan 1, 1969

By G. R. Speich

The interlarnmelm spacing, growth rate, and degree of segregation that accompany cellular precipitation in four Fe-Zn alloys containing 9.7, 15.2, 23.5, and 30.5 at. pct Zn have been determined in the temperature range 400" to 600°C. The chemical free-energy change for the reaction was calculated from the available thermodynamic data and the known compositions of the phases. The fraction of the chemical free-energy change for equilibrium segregation that is converted into interfacial free energy decreases from 0.43 to 0.08 as the magnitude of this free-energy change increases from 35 to 270 cal per mole. At constant temperature the cellular growth rate is proportional to the cube of the dissipated free energy. At 600°C newly 100 pct of the equilibrium segregation is achieved during cellulm precipitation whereas at 400°C only 85 pct of the equilibrium segregation is attained. During cellular growth, mass transport of zinc occurs by grain boundary diffusion; excess zinc remaining in the a! phase after the completion of growth is removed slowly by volume diffusion. A modified Cahn theory of cellular precipitation predicts the observed interlamellar spacing within a factor of two. In cellular precipitation reactions such as pearlite formation or discontinuous precipitation, the basic problem is to predict the variation of growth rate G, interlamellar spacing S, and degree of segregation P with composition and temperature. To accomplish this we need three independent equations relating these quantities. One of these equations comes from the diffusion solution. To obtain two additional independent equations, some assumptions must be made. cahnl has suggested recently that two plausible assumptions are 1) that growth rate is proportional to the dissipated free energy and 2) that the spacing which occurs is that which maximizes the dissipated free energy. According to the first assumption, this spacing also maximizes the growth rate and the rate of decrease of free energy per unit area of cell boundary. The present work was undertaken to test these assumptions. To test the first assumption it is necessary to study a cellular reaction over a wide range of supersatura-tions to establish a relationship between G and the dissipated free energy at constant temperature. This is possible only in discontinuous precipitation reactions since in pearlite reactions constituents other than pearlite form if the composition of the parent phase deviates even slightly from the eutectoid composition. The Fe-Zn system was chosen for study because 1) discontinuous precipitation proceeds to completion over a wide temperature and concentration range, 2) the degree of segregation within the cell can be measured by lattice parameter measurements,2 and 3) the thermodynamics of this system have recently been determined by Wriedt.3 In this system the cells consisting d alternate lamellae of a and r phases form from supercooled iron-rich a phase. The a phase within the cells is bcc as is the original a phase, cia, but has a different orientation and a slightly lower zinc content than the original a phase. The r phase has a zinc content of about 70 at. pct and a crystal structure isomor-phous with T brass. EXPERIMENTAL PROCEDURE Four Fe-Zn alloys with 9.7, 15.2, 23.5, and 30.5 at. pct Zn were prepared from carbonyl-iron powder (400 mesh, 99.8 wt pct Fe) and zinc powder (200 mesh, 99.99 wt pct Zn). The powders were ball-milled together and cold-pressed under 60,000 psi to discs $ in. thick by $ in. diam. The cold-pressed discs of the alloys with 9.7 and 15.2 at. pct Zn were sealed in evacuated silica capsules and heated slowly to 1100°C over a period of 1 week (3 days at 600°C, then 3 days at 80O°C, then 1 day at 1100°C). The alloys with 23.5 and 30.5 at. pct Zn were treated similarly except that the final homogenization temperatures were 1000" and 85O°C, respectively, to prevent melting. The alloys were quenched in iced brine from the final homogenization temperature. Specimens of each alloy were subsequently aged in salt pots at temperatures of 400°, 450°, 500°, 550°, 600°, and 650°C for times that varied from a few minutes to several hundred hours. At a late stage of this work, an alloy containing 11.2 at. pct Zn was prepared by vapor-impregnation of iron foil with zinc vapor at 890°C. This alloy proved useful for electron microscope studies because it was free of porosity. The homogenization and aging conditions were based on the recent Fe-Zn phase diagram of Stadelmaier and Bridgers4 rather than the earlier diagram of ansen.5 They consist of a homogenization heat treatment in the homogeneous a field followed by an aging treatment in the two-phase a + r field. The aged specimens were metallographically polished and etched in 2 pct nital and the radius of the largest cell in the microstructure determined. This radius plotted vs time gave a straight line whose slope is the boundary migration rate or growth rate G of the cell. To determine the interlamellar spacing, specimens were examined by surface-replica and thin-section electron microscope techniques. Because of the irregular nature of the lamellae within the cell, the average interlamellar spacing S .of the cell was measured by the method of Cahn and Hagel,6 where S is defined by:

Jan 1, 1969

By Adrian C. Dorenfeld, Theodore Balberyszski, Strathmore R. B. Cooke

This paper reports results of studies of sulfidiza-tion of base-metal oxides and silicates with gaseous sulfur, hydrogen sulfide gas and pyrite and of their subsequent flotation with xanthate collectors. It has been established that a 100% conversion of the oxides of lead, zinc, copper and manganese into their respective sulfides is possible and is a function of reaction time and temperature. Sulfidization of chrysocolla (with malachite and azurite inclusions) resulted in a product containing covellite, chalcocite and digenite in proportions depending on conditions of sulfidization. Reacting cassiterite with gaseous sulfur, H2S or pyrite at various reaction temperatures resulted in its partial conversion to a tin sulfide. Flotation of the products of sulfidization indicated that their behavior is similar to that of natural sulfide minerals, the recovery being a function of the con-version of the oxides to their respective sulfides. The gradual depletion of high-grade sulfide mineral deposits has turned the attention of the mineral industry to the recovery of metals from the oxides and silicates. Anionic (fatty acid) and cationic collectors have in some cases made flotation of nonsulfides possible, although, in general, flotation of oxide ores is not as yet an economic process. Consequently, many attempts have been made to sulfidize the surface of the relevant oxide mineral and thus make it amenable to to In recent years, Bautista and sollenberger4 have investigated the conversion of a number of oxides to sulfides by reacting them with molten sulfur. This paper presents the results of .investigations carried out at the School of Mineral and Metallurgical Engineering at the University of Minnesota to study the flotation characteristics of some sulfidized minerals. It is divided into two parts: The first describes the sulfidization of a number of oxides and a silicate, and the second presents the flotation behavior of the products of sulfidization. SULFIDIZATION OF METAL OXIDES AND SILICATES Experimental Procedure: SULFIDIZATION WITH HYDROGEN SULFIDE GAS — Sulfidization with H2S gas was carried out in a horizontal tube furnace (Fig. 1). The temperature of the furnace was regulated by means of a Variac and determined with a chromel-alumel thermocouple. The constant temperature zone in the furnace was about 6 in. in length, and it was within this zone that the experiments were carried out. The gases employed were supplied from standard compressed gas cylinders, and passed through a glass-wool filtering tower before entering the Pyrex reaction tube. Gaseous products were bubbled through a water tower (used as a flow indicator) and excess H2S was burned off at the end of the outlet tube. Samples of reagents or minerals were placed in a 3-in. Alundum boat and inserted within the constant temperature zone of the furnace. Nitrogen gas (6 ppm O2 content) was passed through the tubes at room temperature to remove air in the tube, and continued to pass while the furnace was heating up. When the required temperature was reached, H2S was allowed to enter the tube and the supply of nitrogen was shut off. At the end of the reaction period, the reverse procedure was carried out, the samples being cooled to room temperature in a nitrogen atmosphere. The flow rate of H2S gas was maintained fairly constant in all experiments, although the rate was not determined. SULFIDIZATION WITH SULFUR POWDER - To study the sulfidization of minerals with sulfur (liquid or gaseous), samples of the mineral, together with a measured quantity of sulfur powder, were placed in a stainless steel (SS316) reaction vessel (Fig. 2). The reaction vessel was heated in a vertical resistance coil furnace, the temperature being regulated through a Variac. At the end of the experiment the vessel was cooled to room temperature before the sample was removed. Cooled products were leached with CS2 to remove any free sulfur. SULFIDIZATION OF TIN CONCENTRATES - Fifty gram samples of sulfidized tin ore were prepared by mixing -48 mesh Bolivian tin concentrate with -48 mesh Ottawa sand in various proportions and sulfi-dizing these samples with H2S in the horizontal tube

Jan 1, 1969

By Pierre I. Desré, Donald T. Hawkins, Ralph Hultgren

The torsion effusion method has been used to measure the vapor pressure of thallium over pure thallium in the temperature range 931" to 996&apos;k The resulting 100 cal per g-atom is in excellent agreement with previous values. Vapor pressures of T1 above seven Ag-Tl alloys ranging from 33 to 90 at. pct T1 were measured at 979K. Calculated silver activities show a positive deviation from Raoult&apos;s law, approaching ideality near the liquidus. Measured thallium activities scatter less than previous measurements using the electromotive force technique. Values for the silver component were calculated by Gibbs-Duhem integration. This paper reports the results of a study of the liquid Ag-T1 system by the torsion effusion method. The method has been discussed in detail previously1 and will be only briefly summarized here. The sample is contained in a cell which is suspended on a torsion wire. Vapors effusing from orifices on opposite sides of the cell exert a torque on the wire. The torque is related to the vapor pressure by the following relation: where D is the torsion constant of the wire, 4 the angle of torque, fl and f2 the correction factors determined by Freeman and seamy2 to account for orifice length, a1 and a2 the areas of the orifices, and ql and q2 the distances of the orifices from the axis of rotation. By using the same cell for pure thallium and the alloy, it follows that: so that most systematic errors are eliminated in determining the activities. EXPERIMENTAL 99.999+ pct T1 was obtained from the American Smelting and Refining Co. and 99.999 pct Ag was obtained from Cominco American, Inc. Seven Ag-T1 alloys, ranging in composition from x^\ = 0.33 to 0.90, were prepared by melting together weighed amounts of the pure metals in sealed, evacuated Vycor tubes and quenching the melts in water. The apparatus and graphite cells were the same as those used by Hawkins and Hultgren3 in their study of the Pb-Sn system. RESULTS Ten measurements were made on pure thallium in the temperature range 931" to 996K, and the results are presented in Table I. Values of were calculated using tabulated Gibbs (free) energy functions.4 No dependence of on temperature or orifice size was found, indicating that equilibrium was attained. Data for the Ag-T1 alloys are shown in Table 11. Values were smoothed with respect to composition by a plot of where . DISCUSSION The value = 43,520 * 100 cal per g-atom for pure thallium (95 pct uncertainty limit) is in excellent agreement with previous investigations.4 In the Ag-T1 system, this study shows positive deviations from Raoult&apos;s law at all compositions. Fig. l gives the phase diagram according to Hansen, and Fig. 2 presents the activity values measured in this study as well as those from electromotive force measurements at 950°K by Terpilowski, Kundys, and slaby.&apos;

Jan 1, 1969

By Koichi Kashida, Mayumi Someno, Kazuhiro Goto

The present work has two objectives: first to develop an experimental method which would give some new information on the micromechanism of the reduction of oxides by gases at elevated temperature; second to clari,fy the intermediate phases of the W-0 system, formed during the reduction. A Galvanic cell with the solid electrolyte , ZrO2 . CaO, was imbedded in powders of W03, CuO, or Fe20s with two measuring electvodes and with a reference electrode. The change of the intraparticle gas composition was measured at An oxygen concentration cell consists of two electrodes separated by an electrolyte through which the transference of electrical charge is accomplished predominantly by the migration of oxygen ions. Many works have been reported on the oxygen con- 600" to loo@ C during the reduction by the gas mixture of hydrogen and argon. The intraparticle gas composition changes stepwise with time. The electromotive force of such temporary interruption corresponds to the equilibrium electromotive force of two solid phases formed during the reduction. The intermediate phases of W-0 system, which are formed in a large quantity during the reduction by hydrogen, are W0 2 W02.72 and WOz. The micromechanism of the reduction of oxides by gases is discussed. centration cells with the solid electrolyte of solid solution of zirconia and lime, since Kuikkola and wagnerl demonstrated the possibility of determination of standard free energy of formation of oxides by an electromotive-force method with the Galvanic cell. One of the present authors (K.G.) and his coworkers have applied the cells with the solid electrolyte of zirconia and lime to the following measurements:

Jan 1, 1969

By A. McLean, D. W. Gomersall, R. G. Ward

An experimental study has been made of the solubility of nitrogen in liquid iron and liquid Fe-C alloys using levitation melting and a rapid quenching device. Iron alloy droplets were equilibrated with nitrogen gas at 1 atm pressure, quenched, and analyzed. Previous techniques for studying the Fe-C-N system have produced data which me in marked disagreement. This disagreement is due largely to errors caused by reaction between the molten alloy and the crucible material. With the levitation procedure, errors from this source have been eliminated and precise solubility data obtained for temperatures between 1450° and 1750°C. C-N interactions in molten iron have been expressed in terms of first- and second-order free energy, enthalpy, and entropy parameters. ALTHOUGH the solubility of nitrogen in iron base alloys is in general small, the effects of nitrogen on the properties of steel may be quite profound. For most purposes nitrogen in finished steels is undesirable, particularly in the low-carbon grades, since on cooling to room temperature the solubility limit of nitrogen in the steel may be exceeded and this can lead to embrittlement and loss of ductility on aging. On the other hand, nitrogen can improve the work-hardening properties and machinability of steels while in certain stainless grades nitrogen is important in order to stabilize the austenite phase. It is, therefore, desirable that one should be able to predict the solubility of nitrogen in liquid iron alloys. To do this, information is required concerning the interactions between nitrogen and the various alloying elements which may be present in liquid iron. There have been several investigations of these effects in recent years1"7 and the interactions between nitrogen and many elements dissolved in liquid iron are now known to a high degree of precision at steel-making temperatures. Unfortunately, a number of iron alloy systems which are of interest in steelmaking have been difficult to deal with by the experimental techniques generally used for this type of investigation. Among the most important of these are the Fe-C alloys. In the past, two methods have been widely used for determining nitrogen solubilities: the Sieverts&apos; technique, in which the amount of nitrogen required to saturate a given mass of liquid metal at a particular temperature and pressure is measured volumetrically, and the sampled-bath technique in which liquid metal held in a crucible is equilibrated with a gas phase containing a known partial pressure of nitrogen, and samples drawn from the melt are quenched and analyzed. These two methods have been discussed in detail elsewhere.5,8 With the Sieverts&apos; technique, errors may be introduced from the following sources: i) Gas adsorption on metal films which have condensed on the cooler parts of the reaction chamber. ii) Uncertainty in the determination of "hot volume" calibrations. iii) Crucible-melt interaction, particularly if a gaseous reaction product is formed or if the melt becomes contaminated with material from the crucible walls. The sampled-bath method may also suffer from errors due to reaction between the melt and the crucible material. In addition, there is the possibility that gas may be lost from the sample during solidification and cooling. In the present investigation, the solubility of nitrogen in liquid iron alloys has been studied by means of a new technique based on the use of levitation melting equipment and a rapid quenching device. In addition to the fact that problems of the type outlined above are avoided, this particular approach has the following advantages: i) The high-frequency current induces vigorous stirring within the levitated droplet so that gas-metal equilibration is rapidly attained. ii) The gas phase surrounding the melt can be changed very quickly and is easily controlled. For example, a droplet may be levitated in helium, deoxidized in hydrogen, equilibrated with nitrogen, and quenched, within a period of 15 min. ii) Melts can be readily under cooled or superheated, thus extending the effective temperature range of an investigation and allowing temperature-dependent data to be determined with a high degree of precision. Excellent reviews of levitation melting techniques and their application to physical-chemistry studies at high temperature have been published recently by Jenkins et al.,9 Peifer,10 and Rostron.11 In the present investigation a levitation melting technique has been used to obtain data for the solubility of nitrogen in pure liquid iron and liquid Fe-C alloys at temperatures between 1450° and 1750°C. The solution of nitrogen in liquid iron can be described by the reaction:

Jan 1, 1969

By J. E. Zeilinger

This Bureau of Mines report describes the preparation characteristics of the significant coalbeds of Clay, Gilmer, and Lewis Counties, W. Va. In 1966, almost 1.3 million tons of coal was mined in these counties, of which more than one-half was from the Pittsburgh coalbed. Washability analyses were made of 16 coalbed samples. Of these, only 11 samples could be upgraded to metallurgical quality. For steam or power generation five of the coals were of low sulfur content as received. The remaining samples were generally of medium sulfur content even after upgrading.

Jan 1, 1969

Two structurally and mineralogically distinct sulphiderich veins cross-cutting the disseminated sulphides of the Nairne Pyrite Member appear to be products of local remobilization of sulphides under fracture-induced free energy gradients during regional metamorphism and tectonic deformation.The contrasting mineralogy of the two vein types may have arisen as a result of differences in the structural orientation of the veins and!or the relative ages of the veins.

Jan 1, 1969

By Charles Prasky

The Bureau of Mines investigated the conversion of nonmagnetic iron minerals to magnetic form through reduction Toasting operations. The primary objective was to obtain a concentrate that could be used as a direct shipping material for blast furnace consumption. Crude iron materials from the Steep Rock Lakes, Ontario, area were prepared into a blend of 8 parts siliceous ore, 3 parts pyritic ore, and 1 part tailings. Experimental work included laboratory reduction roasting tests, two continuous 10-day campaigns, and one 12-hour test all in a 34-inch by 36¬-foot rotary kiln. The objective of the project was achieved in producing an iron concentrate containing about 66 percent iron with over 90 percent iron recovery. Desirable operating conditions were developed in the kiln but optimum process variables were not completely established.

Jan 1, 1969

By R. K. Koch

The vapor pressures of liquid titanium and liquid platinum were studied under the Bureau of Mines program for the determination of thermochemical data on the transition elements. Beating was done in a 2-kw electron-beam furnace with a water-cooled copper crucible to contain the melt. Temperature was measured with a disappearing-filament brightness pyrometer. The vapor pressure data for liquid titanium in the range 2,008° to 2,379° K are represented by the least-squares derived equation [log p (atm) = 6.268 - 22, T] Two series of determinations were made on liquid platinum. Results of the first series are expressed by the least-squares derived equation [log p (atm) = 8.240 - 30,460T] for the range 2,0860 to 2,4200 K. Results of the second series are expressed by the least-squares derived equation [log p (atm) = 7.795 - 29,580 T] in the range 2,045° to 2,442° K. Third-law evaluations of each series gave mean standard heats of sublimation of 112.4 kcal/mole, 133.3 kcal/mole, and 133.8 kcal/mole for titanium first series on platinum, and second series on platinum, respectively. Second-law heats of sublimation and equations for heats, free energies, and entropies of vaporization were obtained from sigma plots of each data set.

Jan 1, 1969

By J. H. Swisher

When an Fe-Mn alloy is internally oxidized, the inclusions formed are MnO which contains some dissolzled FeO. In the internal oxidation reaction, not all of the manganese is oxidized; some remains in solid solution as a result of the high Mn-0 solubility product in iron. Taking these factors into consideration, the rate of internal oxidation of an Fe-1.0 pct Mn alloy is computed as a function of temperature, using available thermodynanzic data and recently published data for the solubility and diffusivity of oxygen in iron. The predicted and experimentally determined rates for the temperature range from 950 to 1350°C are in good agreement. ThE rates of internal oxidation of austenitic Fe-A1 and Fe-Si alloys have been studied extensively.1"4 Schenck et al. report the results of a few experiments with Fe-Mn alloys at 854" and 956C, and Bradford5 has studied the rate of internal oxidation of commercial alloys containing manganese in the temperature range from 677" to 899°C. When Fe-Mn alloys are internally oxidized, the inclusions formed are solutions of FeO in MnO, the composition depending on the experimental conditions. Since the thermodynamics of the Fe-Mn and FeO-MnO systems have been investigated,6"9 and since the solubility and diffusion coefficient of oxygen in y iron have been determined recently,&apos; it is possible to predict the rate of internal oxidation from known data. The calculations used in predicting the rate of internal oxidation will first be outlined, then the results of the prediction will be compared with the experimental results of this investigation. PREDICTION OF PERMEABILITY FROM THERMODYNAMIC AND DIFFUSIVITY DATA Oxygen is provided for internal oxidation in these experiments by the dissociation of water vapor on the surface of the alloy. The dissociation reaction is: + H2(g) + [O] [1] where [0] denotes oxygen in solution. The equilibrium constant for this reaction is known as a function of temperature:&apos; log As oxygen diffuses into the alloy, oxide inclusions are formed which are MnO with some FeO in solid solution. The reactions occurring are: [Mn] + [0] = (MnO) [31 and [Fe] + [0] = (FeO) [41 where [ Mn] is manganese dissolved in iron and (FeO) is iron oxide dissolved in MnO. The overall reactions may be written as follows: [Mn] + HOte) = (MnO) + H2(£) [5] and [Fe] + H20(g) = (FeO) + Hz(R) [61 The standard free-energy changes and equilibrium constants for Reactions [5] and [6] are known.6 Therefore the equilibrium constants for Reactions [3] and [4] may be obtained by combining known thermodynamic data for Reactions [I], [5], and [6]. For Reactions [3] and [4]: K = and For the present purpose, both the Fe-Mn7,8 and FeO-~n0&apos; systems can be considered to be ideal, i.e., [amn] = [NM~] and (aFeO) = (NM~~) = 1 - (NFeO) where the Ns are mole fractions. These relations, together with Eqs. [I] and [8], permit us to compute both the oxide and metal compositions as a function of temperature and oxygen potential at any point in the specimen. For cases where the oxygen concentration gradient between the surface and the subscale-base metal interface is linear, the kinetics of internal oxidation is an application of Fick&apos;s first law: where dn/dt is the instantaneous flux of oxygen into the specimen, g-atom per sq cm sec; 6 is the instantaneous thickness of the subscale, cm; Do is the diffusion coefficient of oxygen in iron, sq cm per sec; p is density of iron, g per cu cm; h[%O] is the oxygen concentration difference between the surface and sub-scale-base metal interface, wt pct. B6hm and ~ahlweit" derived an exact solution to the diffusion equation for systems in which there is a stoichiometric oxide formed. They showed that the oxygen concentration gradient is given by a rather complex error function relation. For the Fe-Mn-0 system and for most other systems that have been studied, however, variations in oxide compositions are small and rates of internal oxidation are sufficiently slow that the deviation from linearity in the concentration gradient of oxygen is negligible. The mass of oxygen transported across a unit area of the specimen for the total time of the experiment is given by the mass balance equation:

Jan 1, 1969

By R. L. Bishops

This paper discusses some of the materials, processes and systems used in motor insulation. Among the materials mentioned are epoxies, polyesters, mica paper composites and wire enamels. Two processes developed to take advantage of the special characteristics of two of these materials are described, and how these materials are used in several new insulation systems now on the market is discussed. Finally, future trends in motor insulation are outlined.

Jan 1, 1969

By P. Somasundaran, D. W. Fuerstenau

The length of the collector is found to influence the flotation of the mineral even at incipient conditions, which are below the concentration at which interaction at the solid-liquid interface begins to take place to form hemi-micelles. To study this dependence, concentration for incipient flotation of quartz was determined as a function of pH with collectors of various chain lengths. The observed effect of chain length on flotation is ascribed to that of collector adsorbed on the bubble surface. In previous studies, it was shown that at low concentrations the alkyl collector ions adsorb at the solid-liquid interface as individuals.&apos;&apos;2 At higher concentrations, the collector ions adsorbed at the solid-liquid interface associate with each other to form two-dimensional aggregates called hemi-micelles. Above the hemi-micelle concentration, the length of the hydrocarbon chain is extremely important since the hydrocarbons are in effect removed from water during the association, making the energetic conditions more favorable for adsorption at the interface. Because of this enhanced adsorption, one observes a very rapid increase in flotation associated with the hemi-micelle formation at the solid-liquid interface. However, a dependence of flotation on the chain length at concentrations below that required for hemi-micelle association was also observed,&apos; and this cannot be explained by the above mechanism which postulated hydrocarbon chain interactions only at the solid-liquid interface. This prompted an investigation into other possible reactions of the hydrocarbon chains and an examination of the conditions at the bubble surface involved in the flotation system and how these observations might explain the reactions at the solid-gas interface which cause the particle-bubble attachment required for flotation. To obtain more information on chain length effects, flotation, under incipient conditions, was tested by vacuum flotation techniques. The collector-concen-tration-pH relationships for flotation of quartz with alkyl ammonium acetate collectors was delineated by observing the pH at which quartz particles begin to float to the liquid surface. By investigating flotation as a function of pH, it was also possible to study the effect of neutral molecules on incipient flotation conditions, since the aminium ions hydrolyze to amine molecules at higher pH values. EXPERIMENTAL WORK Brazilian quartz specimens were crushed and sized, and the 270 x 400 mesh fraction was used for flotation studies. The samples were leached with concentrated hydrochloric acid until no coloration of the acid occurred. The leached material was washed free of chloride ions and stored in distilled water. The vacuum flotation technique developed by Schuhmann and prakash3 was used to determine the critical pH-concentration curves. This method, which can be used to delineate conditions for incipient flotation, is fairly simple and rapid. About 0.5 gm of 270 x 400 mesh quartz was placed in a 100 ml graduated cylinder which was then filled to the 100 ml mark with the collector solution made from high-purity alkyl ammonium acetate salts. The water used for the test was conductivity water saturated with air that had been passed through a cleansing train consisting of Drierite, Ascarite, a water wash bottle, and a trap. After the pH was adjusted, the cylinder was then conditioned for thirty minutes. In the tests where an acid pH was desired, sufficient acid was added before the collector solution to avoid any effect due to slow desorption of collector from the quartz surface. After conditioning, vacuum was applied to the system and the flotation or nonflotation of the quartz was noted. The pH at which the quartz particles began to float to the liquid-gas interface was taken as the critical PH. Critical pH curves were thus determined for different concentrations of the various collectors. Hallimond tube flotation data were taken from the authors&apos; previous publication1 for correlation with that from the vacuum flotation. RESULTS AND DISCUSSION The results of vacuum flotation studies for determining critical pH-concentration curves, i.e., curves which delineate conditions for incipient flotation, are shown in Fig. I. In generaI, all the curves exhibit an upper and lower pH limit between which flotation will

Jan 1, 1969

By Jack L. Henry

The ternary system A14C3-AIN-Al203 has been examined to determine compositions which may display desirable high-temperature refractory properties. Powder methods were employed in the synthesis of all test compositions. Forming and sintering behavior was examined and hot-pressing parameters were measured. Several properties were studied for each composition of interest in the system. The properties included hydrolysis rate in moist air, elevated temperature oxidation rate, density, softening point, tensile strength, and rupture strength. In most cases equilibrium was not achieved, and the data are representative of a nonequilibrium system. Approximately 16 separate phases have been observed in the system. Forming behavior and selected properties of five compositions of interest were compared with those of aluminum oxide and aluminum nitride. None of the compositions compared favorably. Oxidation and vaporization appear to be serious drawbacks to the use of these compositions at elevated temperatures.

Jan 1, 1969

By M. M. Fine

Research on the solid-fuel reduction of Knob Lake iron or was conducted to upgrade lean and high-grade ores and recover metallized products suitable for ironmaking or steelmaking. The program included bench-scale tests plus a number of continuous campaigns in a 34-inch by 36-foot rotary kiln. In the laboratory, metallizations in excess of 90 percent were achieved by reduction of crushed ore with lignite at 950° C. Subsequent grinding (to minus 200 mesh) and wet magnetic separation yielded concentrates analyzing less than 3.0 percent SiO2 and more than 90 percent Fe. Virtually complete recovery of the iron occurred. During early continuous tests the crushed ore created a serious ringing in the kiln which was solved by balling the fines with bentonite. Unfortunately, at this temperature (950° C) the bentonite militates against the concentratability of the metallized product. For example, a run on direct-shipping ore produced concentrates of 89.5 percent Fe and 4.5 percent SiO2. At 500° C the adverse effect of bentonite disappeared and concentrates of 88.4 Fe and only 2.5 percent SiO2 resulted. However, with comparable feed r Los, the metallization dropped to 73 percent.

Jan 1, 1969

By H. T. Shore, J. M. Schultz

A number of experimental rnethods—X-ray powder diffractometry, Laue photography, X-ray small-angle scattering, and transmission electron microscopy and dijfraction—have been utilized to examine the morphology associated with precipitation from the terminal, g, solid solution of a Zn-1 pct Cu alloy. A significant age hardening was observed in a 1 pct Cu alloy. X-ray and electron diffraction results showed that the structural inhomogeneities associated with the hardening were isotructural with the matrix. The average size and shape of the inhomogeneities were deduced from the electron microscopy and X-ray small-angle scattering. The preprecipitates are hexagonal platelets some 300? in diam. and some twelve unit cells thick. The orientation of the platelets was deduced from Laue photographs and electron diffraction. The platelet plane is (0001). When a large amount of pre-precipitation is present in a localized volume the new lattice is often disoriented by a rotation about (0001) of of the matrix. WhILE dilute Zn-Cu alloys have been commercially important for some 50 years, relatively very little is known metallographically about this material. The "Zilloys", zinc with about 1 wt pct Cu and sometimes a small addition of magnesium, are used to produce rolled zinc which is harder and stronger than that produced by other rollable zinc alloys.&apos; According to the phase diagrams of the zinc-rich side of the Cu-Zn system, such dilute Zn-Cu alloys should age-harden;2-5 the solubility of copper in zinc, g-phase, at 424°C is 2.68 pct, while at 0°C it is only to 0.3 pct. However, the published literature on the aging of this system appears to be limited to a documentation of the contraction of 1, 2, and 3 pct Cu alloys aging at 95°c,6 and an attempt to measure changes in lattice parameters during aging.&apos; In the latter work, no lattice parameter changes were detected, although a broadening of the highest-angle lines was detected and considerable diffuse scattering was observed. Micro-structural investigations have been limited to the latest stage of aging, wherein Widmanstatten precipitates are formed.3,47 These alloys are of interest for still another reason. The two most zinc-rich phases in the Cu-Zn system, 77 and E, are both hcp. Moreover, the change in a, between 17 and t for a 1 wt pct Cu alloy is onlv 3.64 -,~ct: the change in Co is 12.0 ict. It would be anticipated that precipitation in such a material might occur through metastable phases or G.P. zones with epitaxy along mutual 0001 planes. The goals of the present work are aimed at partially filling the void of knowledge concerning the early stages of precipitation from the g phase. In particular, we have attempted to document the magnitude of the age hardening of this system and to determine the size, shape, and orientation within the matrix of the elements of precipitation in an early stage of condensation. EXPERIMENTAL A) Specimen Preparation. Specimens were prepared In two somewhat different ways, one method being used for X-ray Laue and diffractometer measurements, optical microscopy, and Rockwell hardness measurements and the other used for electron microscopy and X-ray small-angle scattering. In the first case zinc and copper in the proper proportions to yield a 1 wt pct Cu alloy were melted together in a closed graphite crucible. Castings so made were free of apparent segregation or oxidation. The castings were then solution-annealed at 400°C for several days and then quenched in water to room temperature. Filings of portions of the specimens were made for use as X-ray powder diffractometry specimens. The electron microscope material was made as follows. Castings were made under vacuum with copper powder placed inside a hollow zinc cylinder to insure good contact of the materials. These 1 wt pct Cu pieces were then rolled to 0.1 mm with an intermediate anneal in vacuo. The rolled sheets so formed were then annealed for about 6 hr at 225°C. Finally the specimens were electropolished slowly until thin enough for transmission electron microscopy. The polishing is discussed in greater detail in the Results section. B) Measurements. X-ray measurements of three types were performed. A G.E. XRD-5 diffractometer was used to examine powders of the alloy for identification of second-phase material. A Kratky small-angle camera, also operating from a G.E. tube, was used to investigate the sizes of small precipitate particles. In both cases, nickel-filtered copper radiation was utilized. Finally, individual grains of the large-grained castings were examined in the back-reflection Laue geometry. Electron microscope studies were carried out with a J.E.O.L. Model 6A instrument. RESULTS A) Hardness Measurements. Hardness measurements performed at room temperature on the large-grained polycrystalline specimens showed a hardening which was essentially complete in 3 hr. Fig. 1 shows a typical plot of hardness vs aging time. The relative magnitude of the ultimate hardening varied from run to run between 150 and 200 pct of the value for the material immediately after quenching from the solution anneal. Most probably the variations reflect small changes in the time taken to remove the specimen from the vacuum furnace after the solution anneal.

Jan 1, 1969

By J. M. Oblak, W. A. Owczarski

A cellular appearing recrystallization product formed by annealing a cold-worked nickel-base super-alloy at 1800°F has been studied by electron nzicroscopy. Prior to deformation, an equilibrium micro-structure of fcc matrix y and cuboidal ,,&apos;, Ni (Al, Ti), precipitates of CuzAu structure had been established by an age at 1825°F. The strain-free recrystallization cells consist of very large rodular y&apos; particles in a y matrix. They precipitate is oriented and coherent both before and after recrystallization. The results showed that y&apos; coarsening accompanies recrystallization at 1800°F. However, it does so as a secondary effect and does not necessarily take place at lower temperatures. The structural similarity of this reaction to cellular precipitation in other systems indicates that lattice strain may also play a significant role during some cellular precipitation reactions. THERE have been numerous microstructural investigations of recrystallization in single-phase materials but two-phase systems have received much less attention. The second phase can either remain inert or be altered along with the matrix during recrystallization. If the second phase is an oxidelm3 or a relatively inert pre~ipitate,~, recrystallization is retarded when the interparticle spacing is less than 1 p. Prior to the onset of recrystallization, these materials show a well-polygonized substructure with the subgrain size limited by the interparticle spacing. Since recrystallization by the motion of preexisting grain boundaries6 is not observed, retardation has been related to particle pinning of the subboundaries. This pinning prevents coalescence&apos; or growth8 of subgrains to a critical size (formation of a high-angle boundary) necessary to initiate recrystallization. In a material such as a nickel-base superalloy both y matrix and y&apos; precipitate are altered by the recrystallization reaction. Haessner et al.&apos; studied the recrystallization of a cold-rolled Ni-Cr-A1 alloy by electron microscopy. The material was initially cold-rolled in the supersaturated condition. upon annealing at 750°C, immediate precipitation of 7&apos;occurred. Presence of this 7&apos; greatly retarded the onset of recrystallization which eventually took place by the development of randomly oriented, strain-free grains. The original •/ was dissolved at the recrystallization interface and reprecipitated as oriented, coherent par-tiles in the new grain. Recrystallization caused a refinement of .)&apos; particle size. Recently ~hillips&apos;&apos; investigated recrystallization of Ni-12.7 at. pct Al. Reduction by cold rolling presumably elongated the p&apos; precipitate into lamellae that remained coherent with the matrix. After recrystallization at 600" to 750°C, there was no unusual change in y&apos; particle size al- though there was a tendency toward clustering along the prior rolling direction at 750°C. Above 750°C, the recrystallized grains were generally free of precipitate. Studies in the somewhat analogous Cu-3.23 wt pct CO" and Cu-2 wt pct&apos;2 systems demonstrated that the coherent cobalt-rich fcc precipitate in these alloys obstructed softening, initiation, and completion of recrystallization. The precipitates were deformed into lam~llae during rolling and those of diameter less than 250A remained coherent. Recrystallization took place by the growth of new grains into the recovered or poly-gonized material. In the first study," both matrix and precipitate reoriented in the same manner upon passage of the recrystallization interface. There was no change in particle size or morphology. Tanner and ~ervi,~ on the other hand, observed that motion of the recrystallization fronts was strongly hindered by the pinning action of coherent precipitates in the deformed material. Particles in contact with a pinned boundary coarsened and coalesced leaving a denuded zone in the unrecrystallized region. When the number of pinning points was sufficiently reduced by coalescence, the boundary swept past these particles and through the denuded zone. The authors1&apos; considered this as a variation of discontinuous precipitation with both chemical driving force and deformation strain energy contributing to recrystallization. Preliminary observations by the present authors had revealed that recrystallization in Udimet 700, a nickel-base superalloy, occurred in an entirely different manner. Optical metallography showed that the recrystallized product formed as cellular colonies containing coarse y&apos; particles elongated in the direction of cell growth. In this investigation the structural features of this reaction were investigated by transmission electron microscopy. EXPERIMENTAL PROCEDURE As-received I$-in. rounds of Udimet 700* were (wtpct) 18.4 15.2 4.95 4.42 3.43 0.06 0.031 0.14 Bal. solution-annealed for 4 hr at 2150" and then fast air-cooled. An initial y-~&apos; structure was established by a 4-hr age at 1825°F followed by a fast air,cool. Essentially the equilibrium volume fraction of ?&apos; at 1825°F is precipitated within 4 hr. Microstructural examination showed no measurable increase in the amount of precipitate after longer aging times. Deformation consisted of swaging to 52 pct RA with 6 pct reduction per pass at room temperature. To reduce the precipitation potential to a negligible amount, recrystallization anneals were conducted at 1800"~ (982"~). Microstructures were investigated by optical and transmission electron microscopy. To prepare foils for electron microscopy, the material was first sliced into 30-mil slabs parallel to the swaging direction. Discs were dimpled and electrolytically cut from

Jan 1, 1969

By Bruce F. Bohor

Silica sand has been mined in Illinois from the St. Peter Sandstone since the turn of the century, especially in the area around Ottawa on the Illinois River in the north-central part of the state. Production of this sand, consumed mainly by the glass and foundry industries but also sought after for many other uses, has grown with the economy, and last year&apos;s output in Illinois exceeded 4,000,000 tons. Such an important commodity was given the early attention of the Illinois State Geological Survey, and a very complete report was issued in 1928, authored by J. E. Lamar. The mining and processing of the sand has changed very little during the intervening 40 years, so that much of Lamar&apos;s data and descriptions are applicable today. More recently, the stratigraphy of the St. Peter Sandstone in north-central Illinois has become better known from the work of Willman and Payne (1942). The present authors have borrowed generously from Lamar&apos;s publication, and we wish to acknowledge the contribution of both of these studies to our work.

Jan 1, 1969

By Arnt Solbu, Jomar Thonstad

The reaction between CO, and aluminum in cryolite-alumina melts in contact with aluminum has been studied by passing CO2 over the melt. In unstirred melts a homogeneous reaction between dissolved metal and dissolved CO2 was observed. In stirred melts in which convection was induced by bubbling argon through the melt, the dissolved metal apparently reacted mainly with gaseous CO2. The rate of formation of CO increased slightly with increasing depth of the melt, and it did not depend on whether CO2 was passed over or bubbled through the melt. The rate of formation of CO increased with increasing area of the metal/melt interface and with the application of anodic current to the metal. It is concluded that the dissolution of metal into the melt is the rate-determining reaction. THE current efficiency in aluminum electrolysis is determined by the rate of the recombination reaction between the anode gas and the metal: 2A1 + 3CO2—A12O3 + 3CO [1] as originally stated by Pearson and waddington.1 The occurrence of this reaction in cryolite-alumina melts in contact with aluminum was first verified experimentally by Schadinger.2 Thonstad3 has shown that the reaction may proceed further to give free carbon: 2A1 + 3CO— A12O3 + 3C [2] Normally only a few percent of the CO formed undergoes such reduction. The mechanism of these reactions has not yet been clarified. Aluminum, as well as CO,, is soluble in the melt. The solubility of aluminum in cryolite-alumina melts at around 1000°C corresponds to 75 x 10- 6 mole A1 per cu cm,4 while that of CO2 is only 3 x 10-6 mole CO, per cu cm.5 Taking into account the stoichiometry of Reaction [I], the ratio between dissolved aluminum and dissolved CO2 available for the reaction in a saturated melt is about 40. Therefore, as will be shown in the following, the reaction probably mainly occurs between gaseous COa and dissolved aluminum. The dissolved aluminum presumably consists of subvalent ions of aluminum and sodium.4&apos;6 Since the interpretation of the present results is not dependent upon the nature of this solution, the dissolved metal will be designated solely as Al+ in the following. The reaction can then be divided into four steps: A) dissolution of metal, e.g., 2A1 + Al3 — 3A1+ [3] B) diffusion of dissolved metal through a boundary layer; C) transport of dissolved metal through the bulk of the melt; D) Reaction [1]. If dissolved CO, takes part in the reaction, three additional steps embodying the dissolution and transport of CO2 must be added. schadinger2 observed, when bubbling CO2 through the melt, that the rate of formation of CO (in the following designated rfco) did not depend on the distance from the metal surface. The results also indicate that the rate of bubbling did not affect the rfco. When passing CO, over the melt, Revazyan7 found that the loss of metal did not depend on the depth of the melt above the metal or on the flow rate of CO2, and concluded that Step A is rate-determining. In an unstirred melt, however, Gjerstad and welch8 found that the rfCo decreased with increasing depth of the melt, indicating that step C was rate-determining. It thus appears that the rate control of the process depends on the experimental conditions, particularly on the convection. In the present measurements the reaction has been studied in unstirred as well as in stirred melts. EXPERIMENTAL AND RESULTS The experiments were carried out at 1000°C in a Kanthal furnace with a 10-cm uniform temperature zone (±0.l°C). The melts were made up of "super purity" aluminum (99.998 pct), hand-picked natural cryolite, and reagent-grade alumina. In experiments where alumina crucibles were used, the alumina content in the melt was close to saturation (13.5 wt pct9); otherwise it was 4 wt pct. Pure Co2 (99.85 pct) was passed over the melt, and the exit gas was analyzed for CO2 and CO by the conventional absorption method.3 From the weighed amount of CO (as CO2) the rfco was calculated as the number of moles of CO formed per min per sq cm of the surface area of the melt. The amount of carbon formed by Reaction [2] was not determined. As already indicated the rfco is much higher than the rfC, by Reaction [2]. Since the rfC probably is proportional to the rfco, the measured rfco should then the proportional to, but slightly lower than, the total rate of Reactions [I] and 121. In general the scatter of results obtained in duplicate measurements was ±5 to 10 pct, while within a given run a precision of ±3 to 5 pct was obtained. The various crucible assemblies that were used will be described below. Measurements in Unstirred Melts. When carrying out aluminum electrolysis in small alumina crucibles. Tuset10 observed that after solidification the lower part of the electrolyte was gray and contained free metal, while the upper part near the anode was white and contained no metal. One may test for the presence of free metal by treating with dilute hydrochlorid acid.

Jan 1, 1969