By J. V. Vogel

Jan 1, 1969

By J. F. Smith, J. E. Davison

The heat capacity of CaMg2 was measured over the temperature interval, 4.8° to 287°K, by the technique of low-temperature adiabatic calorimetry. Heat content measurements were performed with a drop calorimeter over the temperature interval, 273" to 673°K. From these data the thermodynamic functions, (FT - H0)/T, ST - So, and & - Ho, were evaluated. A third-Law calculation of the standard entropy of formation of CaMg2 yields a value of -0.25 * 0.06 cal per (°K g-atom) , and the free-energy function derived from this study when combined with existing equilibria data yields a value for the standard enthalpy of formation which is in agreement with direct calorimetric enthalpy measurements. The accompanying paper' shows that the enthalpy of formation of CaMg2 has been determined with good precision by three different calorimetric techniques.'-= TWO independent determinations of the Gibbs free energy of formation of CaMg2 have also been made; both determinations were based on vapor pressure measurements, being in one case hydrogen vapor pressures over ternary Ca-Mg-H alloys4 and in the other case magnesium vapor pressures over binary Ca-Mg alloys.5 The present determination of heat capacity of CaMg2 below room temperature and of the heat content of CaMg2 above room temperature was undertaken to provide supplementary data. These data are useful in their own right but can in addition be used to evaluate an entropy of formation for CaMg2 which, because of the interrelation of free energy, enthalpy, and entropy, can be used as a check of the self-consistency of the composite of the presently available information. LOW-TEMPERATURE HEAT CAPACITY The heat capacity of CaMg2 was measured over the temperature interval 4.87° to 286.64°K in an adiabatic calorimeter. The physical details of the calorimeter and the experimental procedure for measuring the heat capacity of a specimen have been adequately described by Gerstein et a1.6 The source and purity of the calcium and magnesium are described together with the methods of sample preparation and chemical analyses in the accompanying paper.' Results of chemical analyses of the material which was used in the present investigation are shown in Table I. These analyses show that, on the basis of the published phase diagram,7 the heat capacity sample contained a slight excess of a calcium while the heat content sample contained a slight excess of magnesium. However, in both cases the excess was small, and X-ray diffraction patterns showed reflections which were without exception attributable to CaMg2. The sample which was used for heat capacity measurements weighed 69 g while the sample container and addenda weighed 132 g. The sample was in the form of annealed powder, 50 to 60 mesh, and was sealed into the sample container under 0.1 atm of helium. Copper fins inside the sample container facilitated thermal equilibrium of the powdered Sample. Time intervals of the order of 10 min were required for thermal equilibration, and such times are normal for this calorimeter regardless of the form of the sample. The observed heat capacities were corrected for the small excess of a calcium through use of the heat capacity values tabulated by Hultgren et a1.8 The corrected heat capacities are tabulated as a function of temperature in Table II. The free-energy function and the absolute entropy of CaMg2, which were calculated from the experimental heat capacity data, are listed in Table 111. A smooth curve was fitted to a plot of the experimental values of the heat capacity and in only two instances above 30°K did the plotted points deviate from the curve by more than 0.2 pct. Below 10°K the deviation of several of the points was as much as 50 pct. These large percentage deviations were attributed to the small value of the heat capacity and to the low sensitivity of the platinum resistance thermometer in this temperature range. The deviations in the region of 10°to 30°K were less than 5 pct. Although the percentage deviations of some of the low-temperature measurements are large, the actual value of these deviations is small since the magnitude of the heat capacity in that temperature range is small. The error in the value of the third-law entropy at 298.15°K was estimated to be less than 0.01 cal per (°K g-atom). A value of -0.25 ±0.06 cal per (°K g-atom) was obtained for the standard entropy of formation at 298.15°K from the relation:

Jan 1, 1969

By J. P. McGee

A 1,000-hour test with a gas turbine at 1,200° F showed a working fluid of 1 gr of ash per 100 scf of power gas (79 percent of the ash 7 to 35 microns in diameter) to be excessive for acceptable blade wear for commercial practicability. Blades in the turbine consisted of about 20 percent each of chromium, cobalt, and nickel; 3 percent molybdenum; 2-1/2 percent tungsten; and smaller amounts of manganese, columbium, and tantalum. Erosion of both the fronts and backs of the turbine nozzles was particularly heavy, the trailing edges being worn to a featheredge. Erosion of the buckets was less marked, although the leading edges were somewhat pitted. A refractory-lined combustor performed efficiently and with little abrasion of the lining by the ash-laden gas.

Jan 1, 1969

By John Ward Smith

An analytical method developed by the Bureau of Mines to determine dawsonite, nahcolite, and nondawsonite alumina (called excess alumina) extractable from Green River Formation oil shales is presented. The method requires water extraction of nahcolite followed by HCI-extraction of dawsonite and an unidentified mineral yielding excess alumina from the water-leached residue. Instrumental determination of sodium in the water extract and sodium and aluminum in the HCI extract measures the sample's content of the minerals. Detailed evaluation shows the method to be adequately specific, precise, and reproducible and free from uncorrectable interferences. The method's results define precisely the production of sodium carbonates and alumina possible from a sample of oil shale and the interval it represents. Shale-oil yields, nahcolite contents, and yields of extractable alumina determined on 83 samples representing an 821-foot section of dawsonite-nahcolite-bearing shale from .Colorado Corehole No.3, drilled in the north part of Colorado's Piceance Creek Basin, are presented. These samples resulted in nahcolite contents to 53.3 percent, oil yields to 48.3 gallons per ton, and alumina yields to 5.80 percent. Use of these data to evaluate the production potential of a section of the formation are suggested.

Jan 1, 1969

By David A. Sterling

Approximately 50 percent of the uranium resource of the Free World is in deposits of Precambrian age, principally in lower Proterozoic conglomerates in Canada and South Africa (Uranium Resources, Joint Report, ENEA and IAEA, 1967). Most of the uranium resource of the United States is in Mesozoic and Cenozoic continental clastic sedimentary rocks that fill intracratonic basins. The Atomic Energy Commission is investigating the distribution of uranium and thorium in the Precambrian of the Western United States and the relationship of, time-space-facies patterns of uranium and thorium enrichment in the Precambrian to the major resources of uranium in the Mesozoic and Cenozoic host sedimentary rocks. This paper summarizes the results of preliminary studies of the Precambrian in the Southwestern United States including New Mexico, Arizona, southern Nevada, and southern California (Fig. 1). The host rock provenances for the major uranium resources in epigenetic deposits of Mesozoic and Cenozoic age in the Western United States were in areas of extensive Precambrian exposure along the eastern margin of the Phanerozoic geosynclinal belt (Fig. 2). Mesozoic continental clastic sediments in the Colorado Plateau contain about two-thirds of the uranium resource of the United States. These sediments formed from detritus derived from the Mogollon highland in the Southwestern United States where the Precambrian was extensively exposed (Stewart, et al., 19593 McKee, et al., 1959; McKee, et al., 1956; Craig, et al., 1955) (Fig. 2). A genetic relationship may exist between this provenance and the major uranium deposits of the Colorado Plateau. The Precambrian might be equally important in the genesis of uranium deposits whether the most important process in the formation of these deposits was the leaching of low-order intrinsic amounts of uranium from Precambrian granite or from Mesozoic pyroclastics derived from syntexis of the Precambrian basement rocks (Malan, 1968).

Jan 1, 1969

By K. M. Myles

The vapor pressure of palladium over a series of Rlz-Pd alloys has been measured by the torsion-effusion method. The thermodynamic properties of the alloy system at 1575=K have been calculated from the vapor pressure data. The activities and the free energies of formation exhibit large positive deviations from ideal behavior. The enthalpies of formation are endother-mic. The entropies of formation are positive and larger than the ideal entropy of mixing. All of the thermodynamic properties suggest that a strong tendency toward phase separation exists in the solid solutions. The possible origin of the phase instability and the various factors that influence the thermodynamic properties are discussed. RECENT studies of the thermodynamic properties of alloys of palladium with nontransition elements have indicated that a significant contribution to the enthalpy of formation is related to the redistribution of the conduction electrons upon alloy formation.'-' The present work was undertaken to ascertain the importance of this contribution in Pd/transition-metal alloys. The Rh-Pd system was chosen for this investigation for several reasons: 1) The thermodynamics of the system were unknown. 2) Rhodium and palladium are completely soluble at high temperatures; below 1118OK the solid solution becomes immiscible.', 3) The difference in magnitude between the vapor pressures of rhodium and palladium permitted the use of an existing effusion apparatus. 4) Additional information was known about the alloy system that would facilitate the interpretation of the thermodynamic results. EXPERIMENTAL PROCEDURE The thermodynamic properties of the Rh-Pd alloy system were calculated from the vapor pressure of palladium over solid palladium and over several solid Rh-Pd alloys. The vapor pressure was measured by means of the torsion-effusion apparatus that has been described previously. In this method, an effusion cell is suspended from a tungsten filament inside a high-temperature furnace. Two orifices are located eccentrically such that the effusion of the vapor creates a rotational torque in the filament. The angle of rotation is directly related to the total vapor pressure within the cell. As the vapor pressures of rhodium and palladium are approximately five orders of magnitude apart," the total vapor pressure was considered to be effectively equal to the equilibrium vapor pressure of palladium. The effusion cells were made from high-purity alumina since auxiliary experiments indicated that essentially no reaction occurs between alumina and solid Rh-Pd alloys. Unfortunately, because the orifices were irregular, an accurate calculation of the Free- man-Searcy correction factors" could not be made. The constants were determined in an independent experiment where the vapor pressure of copper, as measured in the alumina cell, was compared with an accurate value of the vapor pressure, which had been determined previously.4 Depletion of palladium from the surfaces of the specimens was minimal as the deflection of the cell remained constant, for at least 15 minutes, at each of the experimental temperatures. Lattice parameter measurements of the postrun alloys also indicated that no changes in the composition of the surfaces had occurred. The alloys were prepared by arc melting the requisite amounts of the 99.99 pct pure elements. The four most palladium-rich alloys were remelted in a levita-tion furnace since complete melting of the components had not occurred in the arc furnace. All of the alloys were subsequently homogenized at elevated temperatures in sealed alumina thimbles. After heat treatment, the alloys were analyzed chemically and were in essential agreement with the nominal compositions. The thermal histories and nominal compositions of the alloys are given in Table I. Lattice parameters of the heat-treated alloys were computed, by means of the method described by Mueller et a1. ,I2 from X-ray diffraction powder patterns obtained with filtered copper radiation in a 114.6-mm-diam Straumanis-type Debye-Scherrer camera. The results, which are tabulated in Table I, exhibit a slightly greater negative deviation from Vegards' law than the values reported by Raub et al.13 The diffraction lines were sharp and well-resolved and thus indicated that the alloys were homogenous. RESULTS The logarithms of the individual values of the vapor pressure of palladium were fit, by the least-squares method, as a linear function of the reciprocal of the absolute temperatures. The constants of the equations are given in Table I along with the temperature range over which the data was accumulated. The latent heat of vaporization at 298.15"K for pure palladium, calculated by the third-law method,14 showed no systematic temperature dependence. The average value of 88,920 * 20 cal per g-atom agrees favorably with the average of the results obtained in the most reliable previous investigations.15"19 The activities of palladium were computed from the vapor pressure data at 1525', 1575", and 1625OK. Consistent with the mass spectrometric study of the atomicity of palladium vapor,lg the vapor was assumed to be monoatomic. The activities of rhodium were determined by integrating the Gibbs-Duhem equation with the aid of the a function.20 In the calculations, the activities of the pure solid metals were assigned the value of unity. From the activities, the partial and integral free energies, entropies, and enthalpies of formation at 1575° K were computed; they are assembled in Table 11.

Jan 1, 1969

By H. E. Cline, J. L. Walter

Grain boundary sliding and migration were studied in pure aluminum bicrystal and polycrystal samples with two-dimensional grain structure. Scratches, 50 P apart, were used for measurement of sliding and migration distanceso. Samples were deformed at constant rate at 315C and events recorded continuously on wrotion picture film. Electron micrograPhs of boundary-scratch intersections were obtained. Yield and flow stress values were measured. The sequence of sliding and migration events for a three-grain junction is described in detail. Sliding depended only on the resolved shear stress imparted to the boundary. Sliding was accowmodated by formation of shear zones in grains opposite triple points and adjacent to curved boundaries. These shear zones provided the driving force for grain boundary migration. Migration caused rumpling of the boundaries, decreasing the sliding rate. Sliding and migration generally began at the same time, occurred simultaneously and ended at the same time. In the bicrystal, sliding and migration rates were proportional. Initial sliding rules of 5 X joe cm per sec. were measured for the polycrystal and bicrystal samples. These sliding rates agree wilh the internal friction experirnents of K;. The observations seem consistent with a viscous boundary sliding nzechanism. GRAIN boundary sliding is the translation of one grain relative to its neighbor by a shear motion along their common boundary. Sliding is thought to be an important mode of deformation at elevated temperatures and at low strain rates such as prevail in creep,' and perhaps in the area of superplastic behavior.2"4 Although much work has been done to investigate grain boundary sliding, the effort has not led to the identification of a mehanism. KG showed that grain boundaries in aluminum exhibit a viscous nature under very small displacements of internal friction measrements. Various dislocation mechanisms have been proposed but are without conclusive experimental support. Attempts to relate sliding to 6's viscous boundaries have been unsuccessful in that measured rates of sliding are always several orders of magnitude lower than KG'S results would predict.= In bi crystals7and polycrystalsR of aluminum tested under constant load, the grain boundary sliding was found to be proportional to the total creep elongation which indicated that sliding might be controlled by deformation of the grains. Shear zones were observed to extend beyond grain boundaries at triple points to accommodate the sliding.8 Surface observations brought forth the opinion that sliding and migration occurred alternately, in sequence.' Measurements of sliding at the surface have been criticized because they might not be representative of the interior of the sample. Generally speaking, it seemed that much of the previous work and knowledge was based on observations made at relatively low magnification and examination of samples after deformation had been accomplished. Thus, it was the purpose of the present study to continuously record, at high magnification, the events occurring during the deformation of pure aluminum. Samples with two-dimensional grain structures were used to simplify interpretation of the results. The sliding and migration of small areas of many samples were continuously recorded by time-lapse motion pictures. Replicas of the surface were used to provide high-resolution electron micrographs. These observations, coupled with tmsile strength data, provide sufficient information to arrive at an understanding of the phenomenon. EXPERIMENTAL PROCEDURE An ingot of 99.999 pct A1 was rolled to sheet, 0.127-cm thick. Tensile specimens, with a gage length of 0.85 cm, were machined from the sheet. Bicrystal tensile specimens, of the same dimensions, were spark cut from a large bicrystal ingot. The grain boundary was oriented at 45 deg to the tensile axis. The surfaces of the tensile samples were ground flat on fine metallographic paper and were then electropolished in a solution of 75 parts absolute alcohol and 25 parts of perchloric acid. The solution was cooled in an ice-water bath. Using a weighted sewing needle suspended from a small pivot on a precision milling machine, a grid of fine scratches, 50 p apart, was scribed on one surface of the sample. The polycrystalline samples were then annealed in hydrogen for 15 min at 350" to 400°C to produce a two-dimensional grain structure of about 0.2-cm average grain diameter which would not undergo further growth at the test temperature, 315OC. Examination of both surfaces of the samples showed that the grain boundaries were perpendicular to the surface of the polycrystal and bicrystal samples. A hot-stage tensile machine was constructed for use with an optical microscope as shown in Fig. 1. The specimen is shown mounted in the grips. The grips ride in V-ways so that the sample can be mounted without damage. The rear grip is free to slide so that when the sample expands during heating it is not put under a compressive stress. When the grips and samples are at temperature, the rear grip is locked in place by two set-screws. The other grip is connected to a synchronous drive motor which, through a worm gear and a fine-threaded rod, deforms the

Jan 1, 1969

By C. Dalton, H. L. McGill

The purpose of this study was to develop a method for predicting the time delay created by metering a fluid through an annular restriction with translational motion of the boundaries. This time delay is utilized to control the opening of valves in various down-hole oilfield tools and forms the basis for the "hydraulic jar". The hydraulic jar is used to give upward impact forces to tubing or other tools that become lodged down-hole. The design of these jars has primarily been by trial and error; varying the clearances, fluid viscosities and dimensions of the jar until a satisfactory time delay was achieved. Obviously, a better understanding of the fluid flow characteristics is required to produce designs that are satisfactory and to eliminate the trial-and-error approach. Previous studies of flow in annular spaces were based on constant length of the annular restriction. Any motion of the boundaries of the annular space was confined to a rotational motion, like that encountered in journal bearing design. Consideration of the effect of translational motion of one boundary with respect to the other was necessary in applying this previous work to a time delay device. A prediction method was developed that takes into account this relative translational motion. Equations were developed to predict the relative velocity, the flow rate, and the time delay in a concentric annular space. The effect of eccentricity also was included. Experimental data were obtained and closely correlated with the prediction method. This correlation is presented graphically in terms of predicted and actual relative velocities for various annular clearances and pressure drops. This extension provides design equations which predict the performance of the hydraulic jar, thereby eliminating trial-and-error solutions and reducing the development time required for satisfactory designs. INTRODUCTION The design of down-hole oilfield tools which use hydraulic delay systems based on flow through annular orifices with relative motion of the boundaries is usually a trial-and-error process. The annular clearances, fluid viscosities and dimensions of the mechanisms were varied until satisfactory delay times were obtained. The development of these tools has been expensive, and a better understanding of the characteristics of annular flow with relative motion of the boundaries could result in superior and less expensive designs. The purpose of this investigation was to provide a method of predicting the performance of down-hole tools which use annular flow and, in particular, the performance of a down-hole tool known as the "hydraulic jar". The hydraulic jar is used to free pipe, packers and other tools that become lodged down-hole. The jar, located in the tubing string between the surface and the object which is stuck, releases the object though the repeated application of upward impact blows. The jar is basically a slip joint that is restrained in a collapsed condition until the desired tubing tension has been developed. The slip joint is then released and accelerates rapidly until it shoulders, delivering an impact blow or jar to the object. The delay obtained by metering the fluid through the annulus formed by the jar valve and housing provides the time delay necessary to stretch and apply tension to the tubing or pipe. Fig. 1A gives a schematic diagram of the hydraulic jar and brief details of its operation. The metering of the hydraulic jar begins when the tension force being applied to the jar by the pipe creates a pressure differential across the valve that is approximately equal to the force divided by the displacement area of the valve. This pressure differential induces flow through the annular restriction formed between the valve and housing. The valve moves with respect to the housing as the

Jan 1, 1969

By R. C. Gould, A. M. Skov, L. F. Elkins

Comparison of long term decline in oil production during cyclic waterflooding or pressure pulsing of part of the Driver Unit with steady injection-imbibition flooding in the Tex Harvey area led to large expansion of flood in the Driver Unit on the steady injection basis. While the flood has been successful, the major problem has been attainment of satisfactory oil production rates in most of the wells. Large volume fracture treatments of low capacity wells were unsuccessful in achieving sustained increases in production. A two-section area in the Driver Unit has already recovered 620 bbl of oil per acre by waterflood but other areas have not performed so well. Sun Andres water containing 300 to 500 ppm H,S is sweetened to 0.5 to 1 ppm H,S by extraction with oxygen-free flue gas. This prevents contamination of gas produced in the area and apparently it has reduced corrosion in minimum investment, thin-wall, cement-lined water dktribution systems. Cement-lined tubing in injection wells has mitigated corrosion as effectively as thick polyvinyl chloride films have, and at less cost. Introduction As reported in the literature the Spraberry field of West Texas has presented unusual problems for both primary production and waterflood ing. Earlier information from the Spraberry Driver Unit included conception and evaluation of cyclic waterflooding or pressure pulsing in a nine-section pilot test as an aid to extraction of oil from the tight matrix rock and as a boost to normal capillary imbibition forces An additional 5 years' operation in that area, and performance of expanded steady injection water-flood, now covering a total of 68 sq miles, are reported herein. In addition, since the Driver Unit is one of the largest waterfloods in areal extent in the U. S., many operating experiences are presented for the benefit of engineers concerned with operation of other Spraberry floods or with other waterfloods where this reservoir technology and/or water handling technology may be adaptable in part. These include: (1) attempts to improve producing well capacity through large volume fracture treatments, (2) long-term performance of water treating plants utilizing oxygen-free flue gas to extract H,S from sour San Andres water, (3) performance of thin-wall cement-lined pipe in water distribution systems including comparison between those sections carrying raw San Andres water and those carrying treated water, and (4) comparison of performance of various lining materials and subsurface equipment in water supply and water injection wells. These experiences are reported without regard to whether results are good, bad or indifferent. Since the operations reported are limited to the techniques, materials, and equipment actually used in the Driver Unit, no comparison is possible with results of other approaches used in other Spraberry floods or in waterfloods generally under different conditions. However, an attempt is made to quantify these experiences as much as possible in the space available to permit other engineers to select those parts applicable to eheir problems. Background The Spraberry, discovered in Feb., 1949, is a 1,000-ft section of sandstones, shales and limestones with two main oil productive members—a 10- to 15-ft sand near the top and a 10- to 15-ft sand near the base, having permeabilities of 1 md or less and porosities of 8 to 15 percent. Extensive interconnected vertical fractures permitted recovery of oil on 160-acre spacing from this fractional-millidarcy sandstone, but they made capillary end effects dominant. Primary recovery by solution gas drive is less than 10 percent of oil in place, with most wells declining to oil production of a few barrels per day when reservoir pressures are still in the range of 400 to 1,000 psi. Partial closing of the fractures with declining reservoir pressure is believed to be the cause of such low production rates at these relatively high reservoir pressures. In 1952 Brownscombe and Dyes proposed that displacement of oil by capillary imbibition of water from the fractures into the matrix rock might significantly increase oil recovery from the Spraberry, overcoming otherwise serious channelling of water through the fractures." A pilot test conducted by the Atlantic Refining Co. during 1952 through 1955 indicated technical feasibility of the process; but low oil production rates averaging I5 to 20 bbl/well/D failed to create significant interest in large-scale waterflooding at that time." Humble Oil & Refining Co. conducted a highly successful 80-acre pilot test during 1955 through 1958 with

Jan 1, 1969

By Jonas Svensson

The Grangcold Pellet Process - for which patents have been applied or already granted in a number of countries - uses a hydraulic adhesive such as Portland cement, slag cements, pozzolanic cements, etc., for the production of cold bonded pellets. The idea of using a hydraulic binder for the agglomeration of iron ore fines is not new. Portland cement was proposed as an adhesive for cold bonded iron ore briquettes in patents granted more than 50 years ago (1). In a report on the briquetting of iron ore fines, published in Stahl and Eisen 1959 (2), it is stated that briquettes bonded with Portland cement are used on a small scale at on ironwork in Germany. According to the report, the briquettes showed excellent strength in the blast furnace although their general use was made impossible because they required a long hardening time, during which they are sticky, soft and difficult to store and handle. The Grangcold Pellet "recess has overcome this particular disadvantage by mixing the balls with a suitable amount of the balling concentrate before storing them. The pellets are embedded in the concentrate during storing in such a way that they are isolated from each other and thus prevented from sticking together to form clusters. Thanks to the embedding concentrate, the pellets are subjected to a more or less uniform pressure from all sides which does not deform them. Thus the mixture can he stored in a stockpile or in a silo until the pellets have hardened sufficiently. The concentrate is separated from the pellets by means of screening. The concentrate is returned to the balling operation and the pellets are either shipped to the blast furnace or stored for final hardening.

Jan 1, 1969

By L. H. Van Vlack, T. Y. Tien, R. J. Martin

The phase relationships of the MnTe-MnS system were studied by DTA procedures. There is an eutectic at 810°C with about 10 mole pct MnS-90 mole pct MnTe. An eutectoid occurs at about 710°C with approximately 7 mole pct MnS where the MnTe(NaCl) solid solution dissociates on cooling to MnTe(NiAs) and MnS. There is very little solid solubility of MnTe in MnS. ALTHOUGH MnS may exist in three different crystal forms,' only the NaC1-type phase is stable.2 Above 1040°C, MnTe also has the cubic NaC1-type structure. Below that temperature, MnTe changes to the NiAs-type structure.3 This phase transition is rapid for both heating and cooling. As a result the high-temperature crystal form of MnTe cannot be retained at room temperature. Because MnO, MnS, and MnSe are all stable with the NaC1-type structure, and MnTe has this structure at high temperatures,4 solid solution formation could be expected among these compounds. It is interesting to note, however, that a complete series of solid solutions exist only in the MnS-MnSe system,' and that the solid solution is quite limited in the MnO-MnS system.' The MnSe-MnTe system possesses a complete series of solid solutions at high temperatures with separation at lower temperatures.7 Although ion size may be critical in the miscibility of MnO-MnS, it is quite possible that the bond type plays a more important role with the miscibility of MnSe-MnTe. This would permit us to speculate that the miscibility gap would be extensive in the MnTe-MnS system. EXPERIMENTAL Preparation. The samples were prepared by mixing and compacting MnTe and MnS powders. The MnS was previously prepared through the sulfur reduction of Mnso4.8 The MnTe had been prepared by mixing and compacting double vacuum distilled metallic manganese and high-purity tellurium in stoichiometric ratio modified with 1 wt pct excess tellurium. The compacted powders were put in a graphite crucible which was sealed in an evacuated vycor tube. The free space in the vycor tube was made minimal to reduce the loss of tellurium. The sealed assembly was then heated slowly to about 500° C where the free manganese and tellurium reacted vigorously, melting the MnTe which formed. Only one phase, MnTe, was detected by X-ray powder patterns and metallographic techniques. Each compact of MnTe-MnS was placed in a graphite crucible and then sealed in an evacuated vycor tube. The samples were heated at 1250°C for 4 hr and furnace-cooled. Microscopic examination revealed no third phase beyond MnS and MnTe. A typical microstructure is presented in Fig. 1. Identification. X-ray powder patterns were obtained using 114.6 mm Debye-Scherrer camera and Fe-Ka radiation. Mixtures of cubic MnS and hexagonal MnTe were observed in all of the compositions prepared. No lattice parameter change was noticed among different compositions, indicating no solid solution could be retained at room temperatures between these two end-members. A lattice parameter of 5.244Å for MnS was obtained by the Nelson and Riley9 extrapolation method using the diffraction lines of (h2 + k2 + 12) equal 12, 16, 20, and 24. The values, a = 4.145Å and c = 6.708Å, for hexagonal MnTe were obtained from the (006) and (220) lines in the back-reflection region. These values agree well with the values reported by Taylor and Kag1e.10 Differential Thermal Analysis. A differential thermal analysis procedure was used to determine phase relationships since the high-temperature equilibrium conditions could not be retained for examination at room temperature, even when the sealed samples (~0.5 g) were quenched in water. The samples were sealed in an evacuated 4 mm vycor tube with a recess in the bottom to accept a thermocouple. An Al2O3 reference was similarly prepared and the two placed within a piece of insulating fire brick to dampen spurious temperature changes within the furnace. The furnace was controlled by a mechanically driven rheostat which increased the temperature at a rate of about 15°C per min. Known phase changes in the Pb-Sn system1' and the a-to-ß quartz inversion12 were used for calibration

Jan 1, 1969

By W. F. Chiao

Ultrasonic attenuation, a, measurements in the frequency range of 5 to 55 mc per sec have been studied to determine their quantitative relationship with the following three variables of mixed microstructures in steels: 1) the volume percent, XF, of polygonal fer-rite in mixed structures of martensite and polygonal ferrite in Fe-Mo-B alloys: 2) volume percent, XA, of retained austenite plus martensite aggregates in high-carbon steel; and 3) substructural differences between 100 pct bainitic ferrite structures formed at various temperatures. The quantitative relationship obtained in the first two conditions by plotting a us the known structural parameters can be expressed, respectively, as: where al, a 2 and C1, Cz are constants. In the third condition the nature of the attenuation depends on the state of dislocations generated at the transformation temperatures and also on the alloy composition. From these measured results, the mechanism of ultrasonic attenuation caused by these mixed microstructures can also be studied. MUCH interest has recently been shown in the application of ultrasonic attenuation and wave velocity measurements to the study of the microstructural characteristics of steels. The general aims of most of the investigations in this field can be grouped into two categories: one is to study the mechanisms of ultrasonic losses caused by the characteristic phases in the microstructure of steel,''' and the other is to develop nondestructive test methods and applications for quality control.~' 4 Apparently no work has been done on the evaluation of ultrasonic attenuation meas -urements as a means of quantitative determination of a given phase in the microstructure of a steel. It is well-established that the decomposition of austenite results in four main microstructural constituents—polygonal ferrite, pearlite, bainite, and martensite—and that each phase has different mechanical properties. Thus, when a steel consists of mixed microstructures, the mechanical properties can often be related to a quantitative measure of the volume percent of each phase present. This study relates ultrasonic attenuation measurements to: 1) the volume percent of polygonal ferrite in mixtures of martensite and polygonal ferrite in Fe-Mo-B alloys; 2) the substructural differences between 100 pct bainitic ferrite structures formed at various temperatures; and 3) the vol- ume percent of austenite in austenite plus martensite aggregates in a high-carbon steel. The choice of the specimen materials was based on the laboratory stocks which were suitable to produce the required mixed microstructures for this study. EXPERIMENTAL PROCEDURES Materials and Heat Treatment. Polygonal Ferrite Plus Martensite Structures. This mixture of phases was produced in a vacuum-melted Fe-Mo-B alloy. The alloy was hammer-forged at 1900" ~ to a -f-in.-sq bar. By isothermally heat treating the alloy at 1300° F for various times and then water quenching, variations in the amount of polygonal (or proeutectoid) ferrite can be controlled in a microstructure in which the balance of the material is martensite. In the present work, four different times of isothermal transformation were adopted; after heat treatment, the four specimens were machined for ultrasonic measurements. The compositions, heat treatments, and dimensions of the four specimens are listed in Table I. 100 pct Bainite Structures Formed at Different Temperatures. It has been well-established by Irvine et al.= that the presence of molybdenum and boron in ferrous alloys can retard the formation of polygonal proeutectoid ferrite and expose the bainitic transformation bay, so that a more acicular or bainitic ferrite can be obtained over a wide range of cooling rates. Their investigation6 also showed that the mechanical properties of fully bainitic steels are usually closely dependent on the substructural characteristics of the steels. For studying the substructural characteristics in completely bainitic structures, six Fe-Ni-Mo alloys, of which five were free from carbon addition and one with 0.055 pct C addition, were selected so that a wide range of hardness values for 100 pct bainitic ferrite structures could be produced by normalizing at 1900" F followed by air cooling. The different bainitic transformation temperatures were recorded during air cooling. All of the alloys were vacuum-melted and then forged at 1900" F to square bars. Data on the six specimens of these structure series are summarized in Table 11. Austenite Plus Martensite Structures. The high-carbon steel used to study austenite plus martensite structures was vacuum-melted and then forged into Q-in.-sq bar. The series of mixed structures of austenite plus martensite was produced by quenching the specimens from the austenitizing temperature to room temperature and then refrigerating them at various temperatures within the range of martensite transformation to produce different amounts of retained austenite. Data on the four specimens of this series are listed in Table 111. Quantitative Analysis of the Microstructures. The microstructures containing martensite plus polygonal ferrite were analyzed by the point-counting technique.

Jan 1, 1969

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By Richard B. Reese, George R. St. Pierre, Robert A. Rapp

The vapor pressures of pure iron and pure chromium have been measured using a Knudsen cell coupled with a mass spectrometer. The experimental results agree well with some previously reported data; heats of sublimation and vaporization have been calculated. From vapor pressure rr~easurernents, the activities of iron and chromium in their binary alloys have been determined for NcY = 0.10 to 0.65 over a 1400" to 1700~ temperature range. The activity of chromium in the liquid alloys was found to exhibit positive deviation from ideal behavior when referred to solid chromium as the standard state; however, for the activity of chromium referred to nonequilibrium undercooled liquid chromium as standard state, the activity behavior is almost ideal. ALTHOUGH the Fe-Cr system is important as the basic system of alloy steels, the thermodynamic properties of this system have not been thoroughly investigated at elevated temperatures. In view of the potential practical applications of such data as well as their contribution to alloy theory, further study of the Fe-Cr system was undertaken. In addition, further development of experimental techniques for equilibrium measurements at high temperature is required. The present research involved an application of the Knudsen effusion method in conjunction with a time-of-flight mass spectrometer. Belton and ~ruehan' have measured the activities in Fe-Ni and Fe-Co alloys by a similar method. Speiser, Johnston, and lackbburn' have determined the vapor pressure of pure solid chromium between 1283" and 1561°K by a Langmuir free evaporation technique. The vapor pressure of chromium was described by the expression: over the temperature range 1283" to 1561°K. McCabe, Hudson, and paxton3 have measured the vapor pressures of pure iron and pure chromium by the Knudsen cell technique around 1500°K. The vapor pressure and heat of sublimation at O°K, AH,", for pure chromium agreed within experimental error with the measurements of Speiser et al. at 1200°C. Kubaschewski and HeYmer~ determined the vapor pressure of pure solid chromium in the temperature range 1170" to 1400°C by the Knudsen effusion technique combined with a radioactive tracer analysis of crS1. Their results agreed with the work of previous investigators. Edwards, Johnston, and Ditmars5 have measured the vapor pressure of pure solid iron by the Langmuir technique between 1356" and 1519°K. The vapor pressure of solid iron in the temperature range studied was given by: The data of McCabe, Hudson, and paxton3 on the vapor pressure of pure iron around 1500°K by the Knudsen effusion technique were in good agreement with those obtained by Edwards et a~.~ Hultgren, Orr, Anderson, and Kelley give the selected values for the AH: of pure iron and pure chromium as 98,990 *200 and 94,340 * 500 cal per mole, respectively. These values are the average values determined in the several investigations by different methods. The Fe-Cr phase diagram7 is shown in Fig. 1. Previous determinations of activities in this system have been carried out by several investigators, but most of the work has been done on solid alloys. Using a Knudsen effusion method with cr5', Kubaschewski and Heymer4 reported that the Fe-Cr system exhibits positive deviation from the ideal behavior for compositions ranging from NCr = 0.0398 to 0.699 at 1170"

Jan 1, 1969

By D. M. Thayer

Laboratory and pilot plant investigations have indicated that copper recoveries of 50% can be achieved with fine grinding and flotation of a copper reverberatory furnace slag, Microscopic and microprobe studies indicate that the recoverable copper is in the form of matte, chalcocite, and metallic copper; the percentage of copper in particles appearing to be copper-free was from 0.23 - 0.54%.

Jan 1, 1969

By Alla D. Mah

The heats of combustion of three chromium carbides, Cr23C6, Cr7C3, and Cr3C2, were determined by combustion calorimetry. Heats of formation calculated from the results follow: ?Hf°298 (Cr23C6) = -94.7 ± 5.0 kcal/mole, ?Hf°298 (Cr7C3) = -43.3 ± 1.7 kcal/mole, and ?Hf°298 (Cr3C2) = -22.5 ± 0.8 kcal/mole.

Jan 1, 1969

By T. E. Hill

The Bureau of Mines investigated the possibility of physically separating Missouri and Minnesota granites into commercially usable fractions of feldspar, quartz, and mica by mineral dressing techniques. The probability of r covering a feldspar fraction from raw granite suitable for commercial uses was developed through correlation of the iron oxide content by extensive petrographic studies. This probability evaluation also included Wisconsin granites and a high-feldspar iron ore concentration tailing from Missouri. Laboratory recoveries of feldspar and quartz were on the order of 80 percent. Mineral content of each fraction was generally over 95 percent, indicating excellent response to separatory techniques, Acid leaching of feldspar and quartz concentrates to remove iron oxide improved the grades chemically; however, occluded iron oxide particles in the leached products prevented attaining top grades of feldspar. Mica was removed as scrap grade at low recoveries. Each concentrate conformed to some category of commercial feldspar, quartz, or mica.

Jan 1, 1969

By O. R. Morris, G. L. Hawkes

A galvanic cell, using as electrolyte a fused salt solution of calcium carbide and as electrodes carbon and a Fe-C alloy of known composition, has been set up to study the thermodynamics of Fe-C alloys in the temperature rmzge 800" to 1000°C. Time independence and reproducibility of the cell electromotive force were taken as evidence of the reversible behavior of the cell. Carbon was believed to be present in the electrolyte as the so-called acetylide ion, C;-. The plots of the cell electromotive force us temperature for a specific alloy composition were straight lines within the limits of experimental error. The average Partial molar enthalpy of carbon in iron relative to pure carbon was found to be +10,610 i 93 cal per g-atom C. Thermodynamic analysis of the data has led to the following equation for the carbon activity, ac, based upon pure carbon as the standard state: In ac = In Zc + 10,560/RT + (10.02 + 77O/T)ZC - 2.350 where ZC is the lattice ratio [nC/(nF, - nc )] and T is the absolute temperature. This equalion gives carbon activity values generally slightly lower than those from gas equilibration studies reported in the literature. METAL LOGRAPHIC examination of a polished cross section of the steel anode used in the electrolysis studies of fused salt solutions of calcium carbide by Morris and Harry revealed extensive carburization of the steel by the electrodeposited carbon. This carburization was reflected in the variability, with time, of the applied potential to the electrolysis cell, necessary to maintain a constant current density at the electrodes. This observation suggested the setting up of a galvanic cell of the "alloy concentration" type to study the thermodynamics of some metal-carbon alloys. Cells of this general type have been widely used for the study of alloy systems.2 In view of the availability of published data in respect of the austenite phase of the Fe-C system, it was decided to carry out measurements upon these alloys before proceeding to studies of less well documented systems. The galvanic cell may be written: where [C] is carbon dissolved in iron. The electrolyte was a fused salt solution of calcium carbide, containing some 5 to 10 mol pct of carbide. The cell reaction is believed to be: C(s)-[CI [I1 Carbon forms an interstitial solid solution in iron, with the atoms located in the octahedral interstices. In the fcc crystal structure of austenite there is one octahedral interstice per iron atom. Thus, the lattice ratio, ZC, shown by Gurney3 to be the fundamental concentration parameter in the context of interstitial solutions, is given by: where nc and nFe are the number of carbon and iron atoms, respectively. chipman4 has recently shown empirically the advantages of using this concentration parameter instead of the more usual atom ratio or atom fraction. The cell electromotive force, E, assuming reversible behavior, is related to the carbon potential or the partial molar free energy of carbon in the solid solution relative to pure carbon at the same temperature and pressure, GP at the composition ZC, by the equation: where z is the carbide ion valency and F is the Faraday constant. An activity of carbon, ac, in the solution relative to the value of unity assigned to pure carbon, and an activity coefficient, qC , are defined such that: where R is the gas constant and T the absolute temperature. GF is further related to the relative partial molar enthalpy Hm, and the temperature coefficient of the cell electromotive force, (aE/aT)Zc, by the equations: Measurement of the cell electromotive force thus enables calculation of the relative partial molar thermodynamic properties of carbon in iron, if z is known. At E = 0, the solid solution is in equilibrium with pure carbon. More convenient for many purposes is the standard state based upon the infinitely dilute solution, Henry's law. The relationship between the activity coefficient of carbon based upon this standard state, and that based upon the pure carbon standard state, qC , may be obtained by considering the free energy of transfer of carbon from the latter standard state to the former. The relationship is: where +:H is the activity coefficient of carbon in the hypothetical standard state based on a reference of

Jan 1, 1969

By G. L. F. Powell, L. M. Hogan

Large degrees of undercooling have been produced in bulk samples, 400 g, of copper and Cu-O alloys by melting in a slag of commercial soda-lime glass. The maximum degrees of undercooling obtained for copper, hypoeutectic and hypereutectic Cu-O alloy samples were 208°, 218°, and 97°C, respectively. No grain refinement as a function of undercooling was observed for the pure copper samples although in Cu-O alloys there was a marked decrease in grain size at degrees of undercooling greater than 150°C. The grain size change is the result of recrystallization during or immediately following the freezing process. THE first report of a large degree of undercooling in a bulk sample of metal was that by Bardenheuer and Bleckmann1 who produced 258°C undercooling in a 150-g sample of iron by melting in a glass slag. Garbeck2 extended this technique to nickel, cobalt, and copper and reported maximum undercoolings of 220°, 230°, and 60°C, respectively, while Fehling and schei13 undercooled a large number of metals as 2 to 20-g samples slagged in glass. Subsequently, one of the authors4 applied the glass slag technique to bulk samples, -500 g, of silver and obtained a maximum undercooling of 250°C. It was concluded that impurities which normally catalyze nucleation at small degrees of undercooling could be removed by oxidation and solution in a glass slag. Large undercooling of bulk samples of iron, nickel, cobalt, and their alloys has also been reported by other authors.8'10'11 Of the five metals mentioned above, copper was the only one which had not been undercooled by at least 200°C in the form of a large bulk sample. Since copper exhibits high liquid solubility for oxygen, as do iron, nickel, cobalt, and silver, it was considered that a much larger degree of undercooling than that observed by Garbeck for copper should be possible. This was obtained by modification of the technique applied previously to silver and the results of undercooling experiments with 400-g samples of copper form part of this paper. The undercooling behavior of Cu-O alloys was also studied, and the influence of a small oxygen content on the grain structure of undercooled copper was observed metallographically. 1) EXPERIMENTAL The copper was obtained as oxygen-free high-conductivity copper, the major impurities of which were Fe 0.01 pct, Zn 0.015 pct, and Si 0.02 pct. Melting was carried out in an open-ended vertical cylindrical fur- nace wound with Kanthal wire. A schematic diagram of the experimental setup is shown in Fig. 1. The undercooling technique previously used for silver4 involved preoxidation of the samples by melting the silver in contact with the atmosphere. The oxygen content was subsequently reduced by freezing the samples under a glass slag, whereby the oxygen was evolved as gas and the continuous glass cover over the surface prevented re-solution of oxygen when the sample was remelted. Since oxygen is not released as gas when a Cu-O alloy is frozen. the technique had to be modified for use with copper. Also, copper is oxidized during fire refining so that an in situ preoxidation treatment of the samples was not considered to be a prerequisite to large undercooling. Experimentation proved that this supposition was correct. Instead, it was found that care was necessary during melting of the copper under glass to minimize oxygen pickup. Samples of copper weighing 400 g were prepared by adding 50-g pieces of copper to a vitreous silica crucible partly filled with soda lime glass at a temperature of approximately 1000°C. Each piece was quickly immersed in the glass slag and held at this temperature until the oxide coating on the surface decomposed. This change was easily observed and coincided with the formation of gas bubbles in the glass

Jan 1, 1969

The only economically significant deposit of dolomite in New Zealand is at Mount Burnett, in north-west Nelson. The dolomite, associated with marbles and schists, is complexly deformed, and is of Paleozoic age.A very large quantity is present, although the recoverable amount is to some extent limited by the difficult terrain.Physically the quality of the dolomite is excellent. It is a tough, durable, fine grained rock. Chemically it is a little more variable. The range and frequency o~ the more important impurities are illustrated by hlstograms, as is the "dolomite factor"-a measure of the amount of the mineral dolomite in the rock. lbe dolomite factor averages 84 per cent, the remainder of the rock consisting largely of calcite. Quarrying, milling, production, and uses are described. In 1966 production reached 13,250 tons.

Jan 1, 1969