Search Documents

By Jr. Gabler

Methods for the direct spectrochemical determination of impurities at the parts-per-million level in tungsten metal and oxide are presented. Several published procedures were investigated and numerous modifications were made in establishing procedures with improved precision and extended lower levels of determinability. Details of standards preparation are presented, experimental work is described, and three preferred methods are described in detail. A germanium carrier-distillation procedure is applicable to the determination of 13 elements in tungsten powder; a silver chloride carrier-distillation procedure provides for the determination of 24 elements in tungstic oxide, and a sustaining ac arc method is applicable to 26 elements in tungstic oxide. The choice of methods to be used depends upon sample form, elements and concentrations to be determined, and the precision and accuracy required. The investigations reported here were undertaken to develop direct spec-trochemical methods with increased accuracy and precision to determine impurities in high-purity tungsten and tungstic oxide, to define the lower concentration levels of detectability and measurement for the common impurities in tungsten by direct spectrographic means, and to present the details of the developed or modified methods that have proved applicable.

Jan 1, 1965

By T. C. Davis

Nine organic derivatives of fluorine, silicon, boron, and aluminum were purified for thermodynamic studies using distillation, zone melting, and gas liquid chromatography, The unusual properties of these compounds required the development of special techniques for handling and purification. To determine purities of purified samples, new techniques for analyzing spectral data were developed.

Jan 1, 1965

By M. Copeland

Phase relations of gadolinium alloyed, up to 40 weight-percent (wt pct), with AISI 304-type stainless steel were established. Body-and face-centered cubic iron-rich solid solution phases and several intermetallic gadolinium-containing compounds of variable composition that approximated the formulas Fe9Gd, Ni7Gd2, Ni3Gd, Fe2Gd, NiGd, and NiGd3 were identified. The intermetallic phases Fe9Gd and Ni7Gd2 were noted to melt at about 1,080° C at about 0 to 2 wt pct gadolinium. The melting temperature of Fe9Gd increased with increas-ing gadolinium content to a plateau at about 1,230°C and 30 wt pct gadolinium, and the melting point of Ni7Gd2 decreased to a plateau at 900° C and 30 wt pct gadolinium where Ni3Gd, NiGd, and Fe2Gd coexist. Body-centered cubic iron solid solution was stable from 1 to 2 wt pct gadolinium to higher contents, 30 wt pct gadolinium or possibly more, and face-centered cubic iron up to 12 wt pct gadolinium below 1,200° C. The stability of these phases above 1,200° C was not resolved except for the mel points. A limited number of fabrication variables as well as mechanical and corrosion properties of alloys containing up to 5 wt pct gadolinium were studied. Equilibrating and forming operations were best conducted at about 940° to 1,080° C. Some variability in the yield and tensile strengths of alloys was noted; however, there was a continual decrease in ductility and impact resistance with increasing gadolinium contents. The resistance of gadolinium alloys to corrosion in water at 354° C was about the same as stainless steel.

Jan 1, 1965

By D. R. Mathews

Electrorefined vanadium was evaluated with respect to tensile properties and the effects of interstitial contaminants in the temperature range of 77° to 273° K. The yield strength of 18,500 psi and hardness of 63 diamond pyra-mid hardness (DPH) of electrorefined vanadium are approximately equal to that of iodide crystal bar vanadium. The ductile-brittle transition temperature was found to be below 77° K, but with 0.175 weight-percent oxygen or 0.10 weight-percent nitrogen, it increased to between 123° and 190° K. With carbon content up to 0.11 weight-percent, the transition temperature remained below 77° K. The yield strength of the interstitial-containing alloys can be expressed by: au = 7.5 + 480 (pct N) + 290 (pct 0) + 280 (pct C), where au is the upper yield stress in 1,000 psi at 273° K. Profuse deformation twinning occurred in the alloys tested at 77° K. However, twinning could be suppressed by dissolved oxygen or nitrogen in excess of 0.15 and 0.086 weight-percent, respectively. Carbon, even though present in excess of the solubility limit, did not affect twinning.

Jan 1, 1965

By Jr. Norman

Thermoelectric properties of depleted uranium selenides and tellurides were investigated from room temperature to 700 C. Several depleted uranium monoselenides and monotellurides were doped with selected cationic and anionic materials to determine the effect of impurity additions on the thermoelectric properties. The undoped uranium selenides and tellurides were semimetallic conductors exhibiting low Seebeck coefficients and electrical resistivities. Partial or complete degeneracy was in evidence, indicating a charge carrier energy distribution similar to that in a metal. Doping increased the Seebeck coefficients of the uranium monoselenides and monotellurides; however, the corresponding change in the power factor in the figure of merit was small because of the increase in electrical resistivity.

Jan 1, 1965

By A. Gene Collins

This report discusses some of the chemistry and geochemistry of cesium and rubidium. Knowledge of the cesium and rubidium content of oilfield waters aids in resolving the origin of waters and petroleum, exploring for petroleum and other valuable minerals, discovering water pollution sources, and augmenting the knowledge of geologic formations. The methods described in this report permit the detection of less than 0.01 mg/l of cesium and/or rubidium in a complex oilfield brine or water. Solvents possessing high-dielectric constants were evaluated for their ability to extract cesium and rubidium tetraphenylboron from oilfield waters and for their flame emission characteristics. Nitroethane was selected and used for the extraction and flame spectrophotometric determinations because it gave the highest sensitivity. Cesium 137 and rubidium 86 were used to determine the extraction efficiencies, which were about 87 percent and 58 percent respectively using a single 10 ml nitroethane extraction from a distilled water matrix. The standard deviation of the determination was 0.0008 mg for cesium and 0.0007 mg for rubidium in the 0.01 mg range.

Jan 1, 1965

By H. E. Powell

Basic data were recorded on the decompositions that take place during thermal decomposition of siderite (FeC03). Both the naturally occurring and a synthetically prepared mineral were studied by differential thermal, thermo-gravimetric, X-ray-diffraction, and chemical (including gas) analyses. Thermal decomposition was studied in the media of dry air, moist air, dry carbon dioxide, dry helium, and dry carbon monoxide and at atmospheric and at reduced pressures. Results showed the thermal decomposition of FeC03 to be an extremely complex process, dependent on environmental factors and side reactions that cannot now be completely controlled. Therefore, full understanding of the reaction involved must depend on additional research with advanced evaluation techniques.

Jan 1, 1965

By George R. Schottler

The objective of this research is to find the extent of the range of applicability of previously developed statistical methods for determining grade and tonnage of ore to bedded uranium deposits. Uranium assays obtained from gamma-ray logs of exploratory drill holes are used to compute grade and tonnage of ore in the deposit by a standard polygonal method and by statistical analysis. The results obtained by the two methods are compared. The uranium-assay frequency distributions are shown to be lognormal and a simple transformation permits the use of standard normal curve statistics. The effects on the assay frequency distributions of stratified sampling, a required minimum mining thickness, and increased assay-interval length are investigated. The addition of low-grade mineralization to make up the required minimum mining thickness results in a distinct change in the skewness of the assay frequency distribution. Any statistical inference regarding grade-tonnage relationships that will be produced, using the minimum mining thickness, should be made on the basis of this "revised" assay frequency distribution.

Jan 1, 1965

By Arne Landsberg

A study of the chlorination kinetics of germanium, silicon, iron, tungsten, molybdenum, columbium, and tantalum has been made to determine the effects of temperature, chlorine concentration, geometric surface area and gamma radiation. The reaction products were volatile at the temperatures used this making it possible to follow the reaction rates by weight loss of the solid. Chlorination rates of germanium, silicon, and iron were found to be directly proportional to chlorine concentration while the rates for tungsten, molybdenum, columbium, and tantalum were proportional to the 0.5 to 0.6 power of chlorine concentration. A good correlation of reaction rate and geometric surface areas was not obtained because the true surface area of the samples could not be measured. Intense gamma radiation had no effect on reaction rates. The Arrhenius activation energies determined over the temperatures used are as follows: Germanium, 27 kcal/mole (233°-241° C); silicon 33 kcaL/mole (375°-517° C); iron, cold rolled, 20 kcal/mGle (259°-325° C) annealed, 21 kcal/mole (293°-337° C); tungsten, 43 kcal/mole (617-776° C); molybdenum, 37 kcal/mole (445°-4910 C); columbium) 34 kcal/mole (229°?255° C); and tantalum, 29 kcal/mole (370°-449° C).

Jan 1, 1965

By Jack I. Paige

The devitrification of lithium silicate glasses was studied to determine the effect of annealing temperature, composition, and additives on nucleation and crystallization. High-purity glasses, prepared from reagent-grade chemicals, had close to optical quality when prepared by a vacuum induction melting method developed during this research, The progress of devitrification was traced by differential thermal analysis and thermal expansion for those lithium metasilicate-silica compositions containing 80 to 90 percent silica. Microscopic studies of glasses partially devitrified at various temperatures and annealing times indicated that the primary initial mode of formation of individual crystals ,vas from densely crystalline zones that filled in as crystallization advanced Of the additives tested, calcium, potassium, and sodium helped promote devitrification with the least cracking or surface deformation. Tin oxide was most effective in reducing volume contrast ion during devitrification, but was not ClS effective in preventing cracking as calcium or potassium additions.

Jan 1, 1965

By Joseph A. Cavallaro

This report describes the timed release analysis technique that was developed to serve as a tool for assessing the froth flotation cleaning potentials of fine-size coals. Using this developed technique, 16 coals from 10 different coalbeds were tested. All of the coals included in this study were quite amenable to froth flotation with float coal yields ranging from 80.7 to 99.5 percentage points. Float-and-sink analyses of the coals tested are shown to be of limited value in predicting froth flotation cleaning potential. Generally the float-and-sink analyses indicated a better product could be obtained than froth flotation could provide; although, in four of the coals tested froth flotation results were superior to those expected from the gravimetric analysis. The fixed carbon content of the samples collected was found to correlate with the floatability of the coals. The higher rank coals were the most readily floatable coals while the lower rank coals did not respond quite as well to flotation.

Jan 1, 1965

By C. O. Hawk

Distillable oils derived from coal were desulfurized and hydrogenated at 2,500 psig in a two-step vapor-phase catalytic operation to give a product rich in saturated cyclic hydrocarbons. The first step was mainly a desulfurization at 400 C, the second a saturation at 300 C. One of the oils used as feed stock was from low-temperature carbonization of a bituminous coal, the other was from the liquid-phase hydrogenation of coal in the Bureau's pilot plant. The product from the saturation step was distilled to remove the light ends and high-boiling residue and to recover a fraction having acceptable properties with respect to heating value, density, freezing point, viscosity, and boiling range according to specifications suggested by the Air Force for ultra-high-speed aircraft fuel. Quantities of the fuel fraction available were too small for the thermal stability test approved by the Air Force. The experiments, performed on laboratory scale, comprised mostly a study of the effect of varying the oil feed rate (at constant oil-to-hydrogen ratio) on the yield of the desired fuel fraction. The yield of the fuel fraction made from low-temperature carbonization oil was a little more than 1 percent of the weight of coal carbonized; that from coal-hydrogenation oil was about 12 percent of the weight of coal hydrogenated. A few attempts to do both desulfurization and saturation in one operation with sulfur resistant catalysts, developed for vapor-phase hydrogenation or hydroforming, were unsuccessful. By leaving the low-boiling ends in both feed stocks to desulfurization, another product was obtained: a low-sulfur aromatic cut boiling below 200 C. This material would be suitable as a solvent or a chemical raw material.

Jan 1, 1965

By K. C. Dean

This report is the first of a series concerned with processes for producing magnesium. These reports will evaluate metallothermic, carbothermic , and electrolytic production methods, and will furnish a cost basis for comparing the processes. Areas deemed most promising for future research will be delineated for each procedure. This report presents briefly the history of the metallothermic process, and describes the operations of the Defense Plant Corp. (DPC) plants that employed the process. A hypothetical plant designed to produce 12,000 tons of magnesium per year, using ferrosilicon as a reductant, is described, and raw materials, energy, and major equipment requirements are estimated. Several process modifications are suggested for future research.

Jan 1, 1965

By Jerry W. Ramsey

The Bureau of Mines examined a low-, a medium-, and a high-volatile Pennsylvania anthracite by densimetric methods using four mesh si.s of each anthracite. Using high-pressure mercury the macropore volumes and distributions of these pore volumes determined, densities in mercury were calculated, and specific pore vo1.r. ware obtained from these mercury densities in conjunction with helium densities. The helium densities were also used with the ultimate analyses of these anthracites in calculating structural parameters by statistical densimetric methods. The effect of 106 or 108 rads of gamma irradiation in the presence of air and in vacuum upon the properties studied with two mesh sizes of each anthracite. Results of the statistical densimetric method seem to show some breakdown of condensed ring structural units at the lower irradiation level, with subsequent polymerization at the longer period of gamma irradiation. The structural parameters obtained also indicated that in going from high- to low-volatile anthracite, either the number of condensed rings per structural unit increased, or the degree of polymerization increased.

Jan 1, 1965

By W. E. Anable

The Bureau of Mines studied the purification of commercially available yttrium by melting it in a 100-kw electron-beam furnace. Button-scale melts were made to determine the ultimate purification that could be attained by melting yttrium at 1,733° to 1,770° C at low pressure (0.05 to 0.1 micron) for 1 to 120 minutes. In addition, numerous melts were made to study the effect of doping yttrium with carbon, 17 selected metallic additions, and 3 compounds. Except for nickel and zirconium, the metallic impurities in yttrium were lowered significantly on extended treatment; silicon was lowered only slightly. The nonmetallic impurities} oxygen, nitrogen, and carbon, were not lowered except on short exposures. In isolated instances, the oxygen content was lowered from 5,860 ppm to about 5,000 ppm. In most instances the carbon con-tent was lowered from 545 to about 220 ppm in 20 minutes and then increased again. It was concluded that yttrium cannot be purified by direct heating or by the doping technique employed.

Jan 1, 1965

By J. D. Spagnola

The Bureau of Mines conducted research to obtain comparative data on the extent of reduction of galena and sphalerite with molecular hydrogen and with hydrogen from the thermal cracking of ammonia and methane at various time intervals. Galena reductions of 95 to 99 percent were obtained with H2 and with decomposed NH3 while reductions of 70 to 80 percent were obtained with cracked CH4? Sphalerite reductions of 99 percent were obtained at 1,000° C with Hz and with decomposed NBs; however, complete volatilization of the free zinc from the remaining concentrate and the subsequent recombination of zinc and sulfur vapors resulted. A promoted iron catalyst brought about a decrease of 100° C in the temperature required for complete decomposition of ammonia. It was found that H2S retards NB3 decomposition and that nitrogen retards the reduction of galena by H2? A mixture of N2 and He in about the same ratio as that obtained by the thermal cracking of NBs gave about 15 percent less reduction of galena than was obtained with decomposed NB3; this indicates that a portion of the hydrogen obtained by NBs decomposition is in an active form.

Jan 1, 1965

By Alla D. Mah

The heat of combustion of TaC0.996 was determined by oxygen bomb calorimetry to be -302.8 ±0.4 kcal/mole. The corresponding heat of formation of TaC0.996 is -35.4 ±0.5 kcal/mole, and the calculated heat of formation of TaC1.00 is -35.5 ±0.5 kcal/mole.

Jan 1, 1965

By A. R. Taylor Jr.

The heat capacities of a-quartz form beryllium fluoride were measured at approximately 3° intervals from 8° to 300° K., using an adiabatic calorimeter. At 298.15° K the heat capacity and entropy were 12.39 cal/deg mole and 12.75 ±0.04 eu respectively. Enthalpy measurements were made with an ice calorimeter at approximately 30° intervals on the quartz and glassy forms of beryllium fluoride between 300° and 1,200° K. A melting point of 825° K and an 0,-8 type transition at 500° K with a heat effect of 75 ca1/mole were deter-mined from the enthalpy data for the quartz-type sample. Beryllium fluoride glass crystallized spontaneously into the quartz modification at 500° K. The heat of the reaction BeF2 (a-quartz) .... BeF2 (glass) was found to be 1,125 ±16 cal/mole at 298° K by solution calorimetry. This value, when corrected to 273° K, was used to correct for the heat absorbed by the formation of glassy BeF2 when the sample was dropped into the ice calorimeter from temperatures above the melting point. Using corrected enthalpy measurements, the heat of fusion was determined to be 1.13 kcal/mole at 825° K.

Jan 1, 1965

By Albert W. Deurbrouck

This report describes the preparation characteristics of 23 coal samples collected from nine of the more significant coalbeds of Fayette County, W. Va. In 1963 almost 5.4 million tons of medium to high volatile B coals of excellent quality for metallurgical and steam markets were produced in Fayette County. Of the 23 coal samples collected 11 would require some upgrading to pro-vide metallurgical quality products, 11 were acceptable as received, and 1 was a noncaking coal. Cleaning these coals to metallurgical standards would require only the removal of the sink 1.58 specific gravity material which would be quite easy as very little near-separating-gravity material was present at this gravity.

Jan 1, 1965

By R. L. Solmer

During 1959-61, the Bureau of Mines investigated the strain and deformation induced in rock and concrete linings around mine openings by retreat panel caving at the Climax Molybdenum mine. Two concrete-lined slusher drifts on the Phillipson level of the mine were instrumented with both electrical strain gages and extensometers. Changes in strain and deformation were recorded over an 18-month period during the undercutting and caving of the mining panel. General agreement was found between the strain and deformation measurements and the hypothesis that the vertical component of the stress field on the openings is almost completely removed by undercutting. This phenomenon is a possible explanation for the structural failures that occur in the slusher drifts during the undercutting cycle.

Jan 1, 1965