Search Documents

By Matthew C. Binsfield

The simultaneous electro winning of zinc and manganese from waste water treatment plant sludge was studied as a part of the overall research program, which was conducted to develop the methods for removal of environmentally hazardous metals from the Bunker Hill Superfund Site. This paper discusses the electrolytic method for recovery of zinc and manganese from the solution produced by leaching of sludge with S02 + H2S04. After three stage purification of the leaching solution, zinc and manganese were electro won simultaneously in an undivided electrolytic cell. Zinc was deposited on an aluminum cathode, while manganese was simultaneously produced (as Mn02) on a lead silver anode. The electrowinning parameters studied were the effects of: temperature, current density, electrode material, spacing of electrodes, composition of electrolyte, and electrolyte additives. Anodic and cathodic efficiencies were 30 and 91%, respectively. In light of the process design parameters discussed in the paper, which are affecting the electrowinning, these efficiencies were found as acceptable with regard to the quality and marketability of the products.

Jan 1, 1996

By B. Grinbaum, A. Mazuelos, F. Carranza, N. Iglesias, M. Avila, J. L. Lozano, G. Perez, R. Romero, M. \/aliente

Following a failure of a tailings pond darn at a mine in Andalusia, Spain, a huge effluent stream, that contained about 1 g/1 Zn and significant amounts of ferrous, ferric, calcium, copper, aluminium and manganese cations has to be treated, to prevent pollution of a nature reserve. EGMASA, as the regional government environmental agency, suggested to improve the current depuration process by recovery of the Zn from the effluent. A solvent extraction (SX) followed by electrowinning (EW) was proposed and developed to remove zinc.. A pre-treatment stage consisting in bio-oxidation of ferrous iron by using a bacterial process followed by an alkaline precipitation was employed because iron in the effluent is incompatible with both the SX and the EW processes. The SX process was developed successfully at the laboratory scale and verified in a pilot plant on-site, using two Bateman Pulsed Columns for extraction and stripping of zinc. The results were satisfactory obtaining a recovery of 90% of Zn. The process was suitable for industrial application.

Jan 1, 2008

By M. A. Barakat

Large amounts of zinc ash and flue dust containing more than 80 % zinc are accumulated during galvanization processes at the surface of molten zinc bath and in the chimney respectively. Pyrometallurgical recovery of zinc from both of the ash and dust samples has been carried out. The ash was sieved with the help of an industrial sieve shaker provided with mesh sieve having a pore size 0.9 mm. The oversize fraction cut (+ 0.9 mm) was melted at 550 °C under ambient conditions. The produced ingot (1) was analyzed whereas the coarse fraction of the produced slag (+ 0.9 mm) was treated as the coarse ash or added to it. The dust was enriched with suitable fluxing salt prior to heat treatment at 600 °C for 1 h. The produced ingot (2) was analyzed whereas the resulting slag was mixed with the fines of the ash and treated by hydrometallurgical processing to prepare valuable salts of zinc. Parameters affecting recovery processes such as time, temperature and flux percentage were studied. Results obtained revealed that the two prepared ingots (1&2) were successfully recovered with recovery efficiency amounts to =85 %. The obtained samples meet the standard specifications with relatively low price. Also in the light of the strict environmental regulations of pollution control, reuse of these wastes materials will help in keeping the environment clean.

Jan 1, 2000

By B. Garcia-Egocheaga, J. Rutten, N. Goicoechea, U. Meurer, Mager K., W. Saage, Simonettim F.

Because of the increasing use of zinc as an active and passive anticorrosion agent for steel, leading to constantly growing return rates of galvanized steel components, especially through the automotive industry, major Electric Arc Furnace (EAF) flue dust amounts with higher zinc contents will accumulate in future. Landfilling of steel plant flue dusts is no longer allowable for ecological reasons. These dusts are classified as hazardous by law. Waelz technology is safe and reliable. The range .of treatable feed materials has been extended by process modifications and state-of-the-art offgas technology. Waelz oxide, the product, is delivered to metal smelters for zinc production and the byproduct, Waelz slag, can be used in road construction. Despite the fact that Waelz technology is among the best available techniques (BAT), it is continuously being optimized further with respect to energy input, product and offgas quality in order to comply with the ever more stringent environmental regulations. However, if these flue-dusts are treated, the loops between the steel and the zinc industry can be closed by reusing recovered zinc which in tum leads to savings in natural resources and a more reasonable use of landfills.

Jan 1, 2000

By J. -F. Blais, M. -O. Simonnot, P. Charbonnier, J. Mocellin, Université de Lorraine INRA, G. Mercier

"Huge amounts of air pollution scrubber sludge have been generated during ferromanganese production using blast furnace. These residues have been historically deposited in ponds near steel making plants. They are very rich in zinc, manganese and lead (5 to 40 %) and also contain aluminum and iron. Considering the market value of these metals, brownfield sites can now be used as secondary resources. These ponds also have to be cleaned up to meet the environmental regulations.We have developed a hydrometallurgical process to recover Zn, Mn and Pb in order to produce valuable compounds of Mn and Zn and recover the final Pb residue by pyrometallurgy. The Zn and Mn compounds need to be pure enough to be economically valuable. Batch laboratory tests were carried out to determine suitable selective leaching conditions. The investigated operating conditions were acid concentration, pulp density and temperature. Optimal conditions to maximize zinc extraction (100 %) and manganese extraction (95.9 %) were found using sulfuric acid and sodium metabisulfide. The final residue contained 14.8 to 23.8 % of Pb. Then, Zn was recovered in the form of ZnO or ZnS by precipitation and Zn metal by electrowinning, while Mn was recovered as MnCO3 with a fairly acceptable concentration of impurities.INTRODUCTIONFerromanganese has been produced by pyrometallurgy in much of Western Europe for centuries. Use of wet scrubber to remove pollutant and dust particles from gas stream was common for most of these operations. Those residues contain high concentration of Zn, Mn and Pb. They have been left to decant in settling ponds installed close to the steel production plants. They now constitute heavily contaminated artificial soils. Those sludges are so contaminated with Zn, Mn and Pb that they can be used for metal production. Currently, no method is available to decontaminate these residues and recover Zn, Mn and Pb. Therefore, an approach considering these brownfield sites as secondary resource is in development. Doing so would achieve two goals, decontaminate the site and produce metals.. (Huot, Faure, Biache, Lorgeoux, Simonnot, & Morel, 2014a; Huot, Simonnot, Marion, Yvon, De Donato, & Morel, 2012; Huot, Simonnot, Watteau, Marion, Yvon, De Donato, & Morel, 2014b)."

Jan 1, 2016

By Joshua Hoffman

The recruitment and retention of future talent into the explosives industry is becoming increasingly important. Student chapters help with this effort but what are they doing and are there things they could learn from each other? This paper discusses the University of Kentucky Student Chapter's efforts to grow membership, retain its recruits, and integrate them into the explosives industry. Several social and professional events during which the students are able to meet and network with members of their future industry are introduced. The special relationship that has been fostered between the University of Kentucky and Missouri University of Science and Technology is discussed. Professional development initiatives which are critical for a student to become vested in the industry are shared in this paper. These opportunities which range from internships to research positions allow a person to get a better understanding of the explosives industry and find the niche that best suits them. Many of the student chapters are closely connected with engineering programs. While this makes sense and both entities benefit from these arrangements there is a trend of job placement primarily in the engineering industry. By providing these students with the chance to learn more about the explosives industry and get hands on experience more of these future engineers and professionals can be retained after their graduation.

Jan 1, 2013

By J. E. Burke, C. W. Mason

IN attempting to study precipitation from a tetragonal lattice using solid solutions of bismuth in tin, it was found that although a Widnmanstatten pattern is observed 1 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process MICROSCOPICAL STUDIES Alloys were made from Chempur tin (Standard samples 42b and 42c, National Bureau of Standards), and bismuth (Kahlbaum C P ) by melting neighed quantities together under palm oil, stirring well, and casting in a heated graphite mold The polishing and etching techniques employed largely govern the visibility of the structural changes The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through BehrManning 3/o abrasive papers, lubricated by a solution of paraffin in kerosene A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution, repeated etching and polishing served to remove disturbed metal For high-power examination better preparation was necessary It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a Heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use A better procedure was as follows The metal lap was warmed slightly, and a 4-in circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C was poured over it, allowed to stand for 1 to 2 min and then washed off It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample The cloth was then charged with a paste of the relevigated alumina in water Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deteriorates after about 24 hr This is not serious, because a new lap can be prepared in about 5 min, and only small pieces of cloth are used Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer For the final etching, the most satisfactory reagent was that of Taffs,7 the formula for which is FeC13 6H20, 2 grams, HC1, 5 c c , H2O, 30 c c , C2H5OH (95 per cent), 60 c c This etchant reveals differences in com-

Jan 1, 1941

By George Langford

Introduction The manufacture of ductile beryllium is one of the most interesting problems confronting the metallurgist today, and one which becomes more acutely in need of resolution as the uses for beryllium increase. Beryllium belongs to the hexagonal group of metals along with zinc, magnesium, and cadmium. The melting point of the metal is about l,280°C. ± 5°C. Due to its brittleness, the metal's chief use is as an alloying agent in copper and iron. The very low absorption coefficient of beryllium for x-rays makes the metal ideal for x-ray windows, and, similarly, because of its low capture cross-section for neutrons, the metal holds a preferred position in the field of nuclear physics. Modern x-ray diffraction methods were responsible for explaining the mechanism whereby zinc metal, although brittle when cast, could be made ductile at room temperature. The diffraction patterns of zinc and magnesium indicated the importance of the parts played by recrystallization and preferred orientation in this mechanism. It was with this in mind that an Investigation into the recrystallization and preferred orientation of beryllium was undertaken. The investigation, after a series of experiments were conducted involving cold-working and annealing, yielded the recrystallization temperature curve for beryllium. Both the texture of preferred orientation and the effect of recrystallization on this texture when subjected to compressive stresses were also determined. W. A. Alexander, J. K. Swinton and L. M. Pidgeon, in their investigation on The Recrystallization Temperature of Beryllium (C.I.M., Trans., Vol. L, 1947, pp. 657-664), utilized the Brinell ball as a means of cold straining the metal. Sufficient strain was developed to estimate the recrystallization curve for the metal. However, in order to determine the lowest recrystallization curve, as well as to develop a preferred orientation structure, larger deformation than that possible with a Brinell ball was required. The plastic deformation of beryllium can be carried out at an elevated temperature above 700°C. Above 850°C., the metal is quite ductile and can be readily compressed or extruded.

Jan 1, 1948

By W. A. Anderson, R. F. Mehl

RECRYSTALLIZATION of cold-worked metals has long been known to proceed by a process of nucleation and growth.1 When a cold-worked metal is heated to a temperature at which recrystallization will ensue, nuclei of new grains, essentially strain-free, appear and grow. As the process proceeds, nuclei continue to appear and to grow, until the cold-worked matrix has been entirely consumed and recrystallization has been completed (Fig. I). Conducted isothermally, a measurement of the fraction of the matrix recrystallized plotted against time, yields an isothermal recrystallization curve, showing the time course of the recrystallization process (Fig. 2).2 Evidently, then, the rate of recrystallization is determined by the rate at which nuclei form and the rate at which they grow. The rate of nucleation N is the number of nuclei that form in unit time in unit volume of the unrecrystallized matrix, and the rate of growth G is the increase in radius of the recrystallized grain per unit time. In recent years attempts have been made to determine N and G as these vary with the well-recognized variables affecting recrystallization: time, temperature, degree of deformation, etc.' Such studies yield information that is more fundamental than that conveyed by the conventional recrystallization diagram,' since the rate of recrystallization is thus analyzed into its two component rates.2 Methods are now available by which N and G can be measured, and analytical expressions have been developed for the interrelationships among N, G, the isothermal recrystallization curve, and the final grain size, which greatly facilitate analysis.2-4 The application of these methods has been demonstrated recently for the recrystallization of silicon ferrite.2 Data on N and G in dependence upon the recognized recrystallization variables are, however, very fragmentary;* values of N and G have been determined for some metals, but the effect of temperature, which would yield the fundamentally important activation energies, has been too little studied. Thus far there has been no detailed study of the recrystallization of any one metal in terms of N and G over appreciable ranges of the variables time, temperature, degree of deformation, and original grain size. It is the purpose of the present paper to provide such a study, employing aluminum.

Jan 1, 1945

By Abu Syed H. Kabir, Mehdi Sanjari, Steve Yue, Jing Su, In-ho Jung

AZ31 magnesium alloy sheets were produced by high speed rolling (HSR) at 1000 m/min at a low temperature of 100 ?. A high reduction of 72% can be achieved in single pass. At the reduction of 30%, the microstructure was covered by shear bands and twins. When the reduction was increased to 49%, dynamic recrystallization (DRX) was clearly observed in the vicinity of shear bands and twins and the full recrystallization was seen at a reduction of 72%. In order to study the static recrystallization (SRX) behavior on the heavily twinned structure, annealing was then carried out at 200 ? on the as-rolled specimens at the reduction of 30% for different times. Static recrystallized grains were also firstly observed on shear bands and twins after 45 s and the microstructure was mostly fully recrystallized after 1 h annealing with a few retained large elongated un-recrystallized grains. Texture weakening was found during annealing on the heavily twinned specimens by SRX, but not during high speed rolling by DRX. In the present study, effect of DRX and SRX on microstructure and texture evolutions during rolling and annealing were compared.

Jan 1, 2015

By C. H. Mathewson

(New York Meeting, February, 1916) DURING the past year considerable work dealing with the mechanical properties and microstructure following the anneal under uniform conditions of certain types of commercial rolled brass has been done in this laboratory. Since these experiments were conducted with the active cooperation of the Bridgeport Brass Co., involving free use of its product, and have thus furnished information which is characteristic of some of its special mixtures, full publication of the numerical relationships and comparative results encountered does not seem justifiable. Some of the more general features of this work are, however, available and it is our present purpose to use the material in question, along with some results of special tests, in discussing the characteristics of recrystallization as related to the degree of hardening by strain and the ordinary annealing variables. We desire to make acknowledgment of the many courtesies extended by Mr. Charles Ferry, Metallurgist of the Bridgeport Brass Co., and the value of his cooperation, which has greatly stimulated the study of brass in this laboratory. A clear and systematic presentation of the principal relations between temperature and time of anneal, the changing physical properties and microstructure and the degree of previous reduction by cold-rolling, was first made, in the case of rolled brass and copper, by the French engineer, C. Grard,1 in 1909, although much fragmentary information of this general character had appeared earlier and the main facts involved were undoubtedly known to many brass specialists through their own private research. From this work, it appears that in the cartridge mixture (67 per cent. copper, 33 per cent. zinc) the properties imparted by cold-working within the limits, 13 to 75 per cent. reduction of area by rolling

Jan 1, 1916

By Julien Favre, Akihiko Chiba, Damien Fabregue, Yuichiro Koizumi, Eric Maire

"The mechanical behavior of Co-20Cr-15W-10Ni alloy is studied by compression tests at high temperature. Microstructures after deformation are evaluated using SEM-EBSD. Significant grain refinement occurs by dynamic recrystallization for high temperature and low strain rate (T>1100°C, <0.1s-1), and at high strain rate (~10s-1). Dynamic recrystallization is discontinuous and occurs by grain boundaries nucleation, leading to a necklace structure. The nucleation mechanism is most likely to be bulging of grain boundaries. However, recrystallization occurs also by rotation of annealing twins which can bulge as well. The modeling of mechanical behavior gives a fair quantification of flow softening due to dynamic recrystallization, indicating the progress of dynamic recrystallization with deformation.IntroductionCobalt-chromium alloys are used in biomedical applications for the elaboration of implants due to their outstanding mechanical properties and their high resistance to corrosion. For stent application a large ductile behavior is required in addition to the high mechanical strength. Indeed stents have to undergo a deformation until e˜40% during their expansion [1]. Conventional Co-Cr-Mo (CCM) alloys exhibit limited ductility (maximal deformation about e˜30%) [2]. Co-Cr-W-Ni (L-605) alloy is a better candidate for stent elaboration since its fracture strain can exceed 40% (comparable to nickel superalloys (Figure 1), while it keeps high mechanical strength. In spite of the presence of nickel element in this alloy, biocompatibility is sufficient for vascular implants, therefore L-605 alloy is extensively used for heart valves and stent elaboration [3]."

Jan 1, 2012

By H. V. R. von Rhaden

Systematic quantitative X-ray diffraction analyses performed on diamond-drill cores originating from the Aandenk formation at the Loraine Gold Mine, located in the Welkom goldfield, Orange Free State, South Africa, have revealed the presence of a number of phyllosilicate mineral assemblages which have not hitherto been reported from this region. Rectorite, a regularly interstratified 1:1 mica-montmorillonite "swelling clay", is found to occur together with paragonite, muscovite, pyrophyllite, kaolinite, and chlorite in highly-altered friable rocks. The presence of rectorite in mill feeds may have potentially serious implications with respect to gold recovery. Quantitative X-ray diffraction analysis for phyllosilicates can be used as an aid to correlation, and also to guide the widths of stopes in underground mining. Rectorite has a unique mode of origin, which is discussed.

Jan 1, 1991

By Diógenes Uceda Herrera

La refinería de cobre en Ilo, procesa el cobre ampolloso que proviene de la fundición de Southern Perú Cooper Corporation, la cual trata los concentrados cupríferos de las minas de Toquepala y Cuajone. En este proceso, el cobre ampolloso se vuelve pre-refinado a través del fuego para así eliminar algunas impurezas y moldear los ánodos de cobre. Posteriormente en la electrólisis, este cobre de ánodo se deposita en el cátodo, liberándose los demás elementos para constituirse en lodos anódicos y así luego ser lixiados con ácidos para recuperar el cobre y centrifugados completamente. En este sentido, el texto señala el método de tostación oxidante con Na2CO3 y en agua como uno de los que más se adecúa a la composición química particular de los lodos anódicos de esta refinería.

Nov 20, 1978

By Paula Aliprandini

O licor de lixiviação do minério limonítico tem como foco a recuperação dos metais níquel e cobalto. No entanto, o minério apresenta em sua composição outros metais como o cobre. Este metal não é o foco do beneficiamento, porém tem valor comercial, o que faz com que a recuperação desse metal agrege valor ao tratamento do minério. A técnica de extração por solventes é uma técnica conhecida na hidrometalurgia para recuperação de metais. Para a recuperação de cobre alguns extratantes são conhecidos, como os do tipo hidroximas. Pertencente a essa classe, o extratante Acorga M5640 é usado na extração do cobre. Esse trabalho buscou avaliar o pH de extração do cobre a partir de uma solução sintética baseada no licor de lixiviação do minério limonítico. Foi levada em consideração a solução após o pré-tratamento de remoção do ferro. Além disso, foram avaliadas diferentes concentrações do extratante Acorga M5640 na fase orgânica a fim de avaliar a quantidade necessária para a extração total do cobre sem que houvesse coextração dos demais metais. Foi possível extrair 99% do cobre em solução usando Acorga M5640 na concentração de 5% em volume e pH de trabalho igual a 2..

Oct 30, 2017

By Susana Marraccini Giampietri Lebrão, Jorge Alberto Soares Tenório, Renato Souza e Silva, Guilherme Wolf Lebrão, Viviane Tavares de Moraes

Os resíduos eletroeletrônicos podem ser compostos por equipamentos ou parte deles, que se tornaram obsoletos, pararam de funcionar ou ainda por apresentar defeitos durante a sua produção. As placas de circuito impresso (PCIs) são peças presentes em equipamentos eletroeletrônicos compostos por materiais metálicos, cerâmicos e poliméricos. Para alguns destes metais já existem processos para recuperação, contudo estes processos baseiam-se em técnicas pirometalúrgicas que podem liberar substâncias tóxicas. A fim de minimizar os impactos ambientais propõe-se o beneficiamento das PCIs através de rota hidrometalúrgica para a obtenção de cobre em solução e, posteriormente fazer a redução do cobre. Para tanto se fez a moagem das PCIs, seguida de caracterização química. Partiu-se para rota hidrometalúrgica em meio ácido e em meio oxidante. A solução resultante de cobre foi reduzida para cobre metálico por reação de redução com ácido ascórbico. Os resultados apresentam recuperação de 97 % de cobre das PCIs com obtenção de cobre metálico.

Oct 11, 2019

By Mário César Mantovani

Um dos principais problemas enfrentados pelas aciarias é o descarte dos resíduos gerados durante a produção do aço. Além de se pagar pelo descarte em aterros monitorados, ocorre também a perda de elementos de liga, tais como Cr, Ni, Mo, V, etc. O objetivo deste trabalho é estudar a viabilidade de se aglomerar alguns resíduos gerados durante a produção do aço (lama de VOD/VD, poeira de forno panela e carepa de forjaria) na forma de pelotas autorredutoras e adiciona-las ao forno elétrico a arco (FEA). Primeiramente os resíduos foram misturados com finos de coque de petróleo e cimento. Após a pelotização e o período de cura, as pelotas autorredutoras foram fundidas num forno de indução (teste laboratorial), visando avaliar o nível de recuperação dos elementos de liga a partir dos resíduos. O rendimento dos elementos Cr, Ni e Mo variaram de 84% a 99% nos teste laboratoriais. Nos testes industriais envolvendo as pelotas autorredutoras de carepa de forjaria (aço ferramenta H13), os rendimentos dos elementos Cr, Mo e V variaram de 51%-92%, 94%-99% e 27,5%-88%, respectivamente.

Jul 30, 2018

By P. Fleming, W. Pascheto

"Rod mills processing nickel and copper ore experienced recurring failures of liner bolts. In some cases failures became very frequent, requiring constant mill intervention and consequently impacting process stability and operating costs. Investigation related to the causes of bolt failures involved a multidisciplinary approach with the participation of engineering, maintenance and operation. It included the determination of bolt failure mechanisms as well as the assessment of mechanical properties, fabrication quality and handling and installation procedures. In addition, other parameters affecting bolt performance such as mill and liner design, operating parameters and maintenance practices were studied. This paper reports the failure investigation results and proposed solutions for failure prevention. INTRODUCTIONOccasional liner bolt failures are common in rod mills. However, chronic bolt failures developed in rod mills processing nickel and copper ore caused frequent shutdowns for bolt replacement to an extent that affected process stability. At first, it was thought that the cause of recurring failures was related to bolt quality. The operation then submitted several failed bolts to failure analysis. However, it became apparent that bolt quality was unlikely to be the main cause of failures. The determination of root cause (s) then became more complex, requiring a multi-disciplinary approach to failure investigation, requiring the assessment of bolt installation methods, mill design, operating conditions and maintenance practices. The results of the metallurgical failure analysis and investigation of other possible causes of failures are reported here."

Jan 1, 2016

By Drew Sinha

Success of the environmentally benign semiconductor manufacturing depends on the cost-effective integration of the principles of reduce, recover, reuse and recycle from source material to final product disposal. Increasing demand combined with current shortage of polysilicon provided unique opportunities to recover the silicon waste, caused by various defects, in wafer manufacturing process. Current practices relating to recovery and reuse of waste silicon produced, from crystal growth process to finally polished and epitaxially deposited silicon wafer, at Mitsubishi Silicon America is presented. Future plan to recycle the process generated silicon fines produced during the intermediate steps of the wafer manufacturing process such as grinding, slicing, lapping and polishing is also discussed.

Jan 1, 1998

By John L. Sundstrom

Complete systems were designed -and are in operation to recycle the effluent streams and to remove impurities from tankhouse. electrolyte, Heavy em¬phasis was placed on making usable products from as many streams as poss¬ible at minimum capital and operating costs. Almost complete recycling: and reuse of water and sulfuric acid were paramount. Techniques used in-clude solvent extraction - electrowinning, evaporation - crystallization and filtration.

Jan 1, 1992