By W. D. Robertson, Raymond C. Boettner

A study was made of the change in density during the first (transient) and second (linear) stages of the creep curve of polycrystalline copper as a function of 1) stress, 2) temperature, 3) plastic strain, 4) impurity and atmosphere effects, and 5) structure, including single crystals. Voids were not observed in single crystals strained 15 pct at 500°C, or in a polycrystal-line aggregate produced by recrystallizing a single crystal, within the limit of sensitivity, Ae/e = 1 x 10-4. It appears that voids are heterogeneously nucleated at grain boundaries by an insoluble phase, or phases, which can be removed by directional solidification. The principal controlling mechanism of void growth appears to be condensation of vacancies at grain boundaries. Vacancies are transported to a boundary and condense as a consequence of the tensile stress component across the boundary, which depends on the orientation and configuration of the boundary plane and on boundary shear across ledges and other irregularities. The ultimate source of vacancies is the free surface and diffusional transport is by way of the boundary plane. PREVIOUS investigations have dealt with the nucle-ation of voids at grain boundaries under creep condition~'-~ and with the connection between grain boundary voids and subsequent brittle fracture.5-7 Growth of voids during the creep process, particularly in the transient and linear stages of creep, has not been studied with the same intensity. Therefore, it seems pertinent to investigate the process of void growth with respect to the related creep curve, and the morphology of growing voids with respect to the structure.

Jan 1, 1962

By F. D. Rosi, C. H. Mathews

THE plastic properties of face-centered cubic metals below room temperature present a field of investigation which has not been extensively ex-plored. The work by Schmid and Boas1 has demonstrated the importance of temperature upon such properties as strain hardening and critical resolved shear stress. The work by Yamaguchi2 upon the shear stress as related to the number of slip bands accentuates the necessity for further experiments of a similar nature. The approach to a mechanical equation of state from the standpoint of thermal fluctuations and activation energies by Becker3 and more recently by Kauzmann4 further emphasizes the need for a quantitative and more comprehensive analysis of the dependence of fundamental plastic properties on temperature. The purpose of the present work was to investigate specifically: (1) The gross shape of the stress-strain curves at several temperatures, (2) the change in the critical shear stress as a function of temperature, and (3) the number and appearance of slip bands as a function of strain and temperature. Preparation of Specimens Single-crystal specimens of 99.996+ pct alumi-num, 1/2 in. in diam and 5 to 6 in. in length, were made by the Bridgman method of gradual solidification from the liquid state. The crystallographic orientation of the single crystals was determined from back-reflection, Laue X-ray photograms ac-cording to the method described by Greninger.6 In most specimens the Laue photograms showed double diffraction spots indicative of the lineage structure type of imperfection, discussed in great detail by Buerger.7 The angular spread of these spots was never observed to exceed 2". Most of the crystals were radiographed to insure against microporosity. In preparing the metal surface for optical microscopy, the following sequence of operations gave good results: The as-cast crystals were turned down in a lathe, 0.001 in. per cut, to obtain a 2.5 in. gauge length. The cold-worked layer resulting from this operation was removed chemically by etching with Tucker's reagent. Then the specimen was polished mechanically through 2/0 metallographic emery paper, after which it was etched again to remove the cold-worked layer resulting from the mechanical treatment. A 48-hr anneal at 580°C ±10°C followed so as to insure an essentially stress-free single crystal. After the annealing treatment, the specimen was electrolytically polished in a 2:l solution of methyl alcohol and concentrated nitric acid. With a current density of 10 amp per sq dm (decimeter) the time required to obtain a satisfactory surface varied from 10 to 12 min. The polish-ing was carried out for short periods of 2 min to avoid rapid deterioration of the solution as well as to enable the rotation of the specimen 180" for uniformity of polish. It was necessary to place the solution in a bath of dry ice in view of its explosive nature at room temperature. Etching of the electrolytically polished surface was accomplished by using the fuming etch-pit method recommended by Lacombe and Beaujard8 for high-purity aluminum. Method for Tensile Testing A modification of the loading equipment devised by Miller9 was used. In this apparatus, the specimen was suspended from a chain and gimbal arrangement (for axial loading) in a heavy steel framework connected at the bottom to a balanced 6:1 lever and bucket system. Loading of the specimen was accomplished by allowing sand to flow from a reservoir into the bucket suspended from the longer end of the lever-arm at a rate of approximately 3 lb per min. Strain measurements were made using the Baldwin SR-4, bonded, resistance-wire, strain gauge and an SR-4 portable strain indicator (type K), which permits a reading accuracy of 2 microinches per inch. For low-temperature study, the gauge was calibrated by measuring the elastic modulus of an annealed stainless steel rod, which is known to be independent of temperature."

Jan 1, 1951

By W. S. Hyler, W. L. Bruckart

The powder metallurgy and arc-cast types of wrought molybdenum stock were studied in rotating beam fatigue. Endurance ratios of unnotched specimens after 5x10 cycles were found to be 0.74 and 0.81, respectively. Fatigue notch factors (K,) of 1.36 and 2.05, respectively, were obtained on V-notched specimens having a theoretical stress-concentration factor Kt = 3.1. MOLYBDENUM and its alloys are rapidly gaining importance as engineering materials of construction for high temperature applications. AS a wrought material, molybdenum and its alloys are outstanding above 1800°F. It is necessary, however, with molybdenum to provide elevated temperature oxidation protection. This is currently being studied by a number of investigators. Thus far, there have been no published data on the fatigue behavior of molybdenum either at room temperature or at elevated temperature. The knowledge of fatigue behavior, particularly notched fatigue behavior, becomes increasingly important as the engineering importance of a material increases, especially from the design standpoint. The work described here was directed toward determination of the notched and unnotched rotating beam fatigue characteristics of molybdenum at room temperature. Also, it was desired to learn whether any difference exists between wrought molybdenum of the powder metallurgy and the are-cast types. Fabrication History of Bar Stock For this work, bar stock was procured from Climax Molybdenum Co. (are-cast type) and from Westing-house Electric Corp. (powder metallurgy type). The processing histories of these materials are listed in Table I. The first lot of are-cast molybdenum was deoxidized by aluminum additions. The second lot was deoxidized by carbon." Both lots of the powder Microstructure A microscopic examination of these materials, as received, revealed the powder metallurgy molybdenum to be free of inclusions and to be finely fibered. On the other hand, the are-cast C molybdenum possessed numerous carbide inclusions, and the arc-cast A appeared to have coarse grained fibers. These are shown in Fig. 1. Owing to the large apparent difference in fineness of fiber between the are-cast A and the powder product and are-cast C, a check was made of the recrystallized grain sizes to determine whether these differences persisted. A series of recrystallization anneals revealed mixed grain sizes in both the are-cast A and the powder product. Variations in grain diameter of as much as 50 times were found after full recrystallization at 1200°C for 30 min. There was no distinction between the two. Arc-cast C was not checked. Room Temperature Mechanical Properties Prior to subjecting the materials to fatigue tests, room temperature mechanical properties were determined. These data, together with the tensil: strength of the notched bars, data,togetherare listed in Table tensil: There were no significant differences in the tensile strengths of the two types of molybdenum. However, the powder metallurgy material was generally more ductile and yielded at a somewhat lower stress than the arc-cast material. Tensile strengths of the notched specimens indicated a slightly greater notch strengthening effect in the are-cast C than in the powder product, lot 2. Room Temperature Fatigue Properties Sample Preparation: Specimens were prepared for use in R. R. Moore rotating beam fatigue machines. These specimens had a continuous radius test section with a minimum diameter of 0.260 in. The specimens were prepared by grinding to shape and polishing to produce a smooth unworked surface. Polishing consisted of rotating a disk in the continuous radius section on which were attached, successively, emery belts of 240, 400, and 600 grit. The specimens were slowly rotated during the operation. The belt speed was high, and rotation was such that polishing scratches were longitudinal. Unnotched Fatigue Properties: Unnotched fatigue data were obtained from a number of specimens of each of the four lots of molybdenum. The results of the tests are presented in Fig. 2. From this figure,

Jan 1, 1956

By R. F. Mehl, M. L. Swanson, J. P. Hirth, G. M. Pound

The sorption of zinc in a-brass was investigated. By analyzing the elliPtically polarized light reflected from the surfaces of a-brass solid-vapor couples, their optical constants and surface compositions were determined. It was shown that the surface compositions approached an equilibrium value exponentially with time. The bulk diffusion coefficient, surface diffusion coefficient and condensation coefficient for a-brass solid-vapor couples were calculated near 350°C from the experimental results. It has been assumed during various diffusion experiments with bimetallic solid-vapor couples (Dunn,1 Seith and Kraus,2 Jenkins,3 Balluffi and Seigle,4 and others) that the surface composition of such couples reaches its equilibrium value immediately. Although this assumption is probably valid at elevated temperatures, it is certainly not expected to be confirmed at lower temperatures.* consequently, it was decided that a fundamental experiment, designed to solve this problem as well as to examine all aspects of bimetallic sorption, would be the investigation of the rate of approach to equilibrium of the surface composition of solid-vapor couples. The sorption (i.e., adsorption, absorption, and desorption) of metals is obviously dependent on the state of the metallic surface and substrate. Much recent theoretical8"9 and experimental10-12 work on condensation and evaporation of pure metals has shown that the surface contour in atomic dimensions is a critical factor in sorption, so that any deformation or contamination13,14 of the surface exerts a profound influence. It is also known that absorption or diffusion occurs much more rapidly along grain were and in other deformed regions. Thus an effective sorption experiment must utilize a strain-free and clean surface, or at least a clearly defined and reproducible surface state. A mechanically polished surface is in a highly deformed17-l9 state. Because the degree of this deformation is uncertain, it is clear that for most experimental purposes a strain-free (i.e., etched, chemically polished, or electropolished) surface is desirable. Although adsorbed gas molecules on metallic surfaces are unavoidable even in the highest vacuum,20 oxide films can in some cases be removed by suitable vacuum annealing. Electrolytically polished and annealed surfaces, being relatively without strain, smooth and free of bulk oxides, were considered adequate for the present sorption experiments. Measurement of the surface composition of a solid-vapor couple presents a unique problem. Since experiments to determine the approach to equilibrium of the surface composition must be performed at temperatures where diffusion is very slow, solute penetration is so small that conventional analytical methods are unsuitable. An optical reflectivity method utilizing a polarization spectroscope was employed because of the relatively small penetration (~200A) of visible light in metals. By this method, elliptically polarized light reflected from the metal surface was analyzed and compared with that reflected from samples of known composition. The a phase of the copper-zinc system was

Jan 1, 1962

By R. W. Armstrong, D. H. Feisel

Self-diffusion in pure crystalline solids has been described through extension of the Cohen and Tum-hull volume -fluctuation model originally proposed for diffusion in simple liquids. It is shown, for a number of crystalline solids, that the self-diffusion coefficient, D, obeys the relationship where a is the lattice spacing, v the Debye frequency, Z' the lattice-volume fluctuation per atom required for a diffusion jump, and (?V/Vo) the relative increase in the lattice volume resulting from thermal expansion between O°K and the temperature under consideration. The calculated value of Z' is dependent upon the difiusion mechanism and the lattice geometry. ThE need for an increased understanding of mass-transport processes in crystalline solids has resulted in much research to determine rates of self-diffusion.' For several metals (e.g., copper, silver, and iron), the experimental values of the self-diffusion coefficient, D, have been determined over a large interval of temperature and the accuracy of D has been investigated through repeated experiments. Also, a number of empirical and theoretical diffusion studies have established a rational basis for understanding the D values for the different elements.2"6 The empirical diffusion analysis by Sherby and simnad6 supplied the main stimulus for the present study. Sherby and Simnad, reviewing the self-diffusion data for a substantial number of pure crystalline solids, suggested that sufficient data were available to establish with some certainty the apparent intrinsic material properties which influence D. Without explicit regard for any mechanism of diffusion, these investigators obtained an empirical relationship for D which correlated the self- diffusion coefficient for each element with the melting temperature, crystal structure, and valence of the particular element. Their analysis is only unsatisfactory in that the effect on D of crystal structure is not very clear and the valence to be assigned to an element is not always straightforward. The present study is an attempt, from a very different viewpoint from that of Sherby and Simnad, to establish a basis for understanding the self-diffusion coefficients for crystalline solids. This analysis was undertaken for the purpose of developing a general expression for D which would explicitly depend on the mechanism of diffusion. The main result of the study is that diffusion in crystalline solids may be described in terms of a volume-fluctuation model which was originally proposed by Cohen and Turnbull7 to describe diffusion in simple liquids. The model appears to be useful for predicting self-diffusion coefficients in crystals. The following sections describe the volume-fluctuation model for diffusion, the application of this model to crystals, and the resultant agreement with experimental data. 1) THE VOLUME-FLUCTUATION MODEL FOR DIFFUSION Cohen and Turnbull7'8 developed their model for liquid self-diffusivity for the purpose of describing certain properties of liquids, glasses, and the liquid-glass transition. A hard-sphere model for the liquid structure is used. In this model, the size of a spherical molecule or atom is fixed for all temperatures by the interatomic spacing at the absolute zero of temperature. At any temperature above O°K, the atom is viewed as being contained within a larger spherical cage defined by the interatomic spacing of the atoms at that temperature. A random distribution of varying cage sizes is assumed to exist in the liquid. An individual diffusion jump occurs when the free volume of an atom (the volume of the cage containing the atom minus the volume of the atom) is large enough for the atom to jump out of its cage. With this physical picture of diffusion in liquids, Cohen and Turnbull derive the following equation for self-diffusivity: D=Doe-yv*/vf [1] where Do is the product of three factors which are the diffusion-path geometry, the diffusion-jump distance, and the velocity of the diffusing atom, v*

Jan 1, 1964

By M. Herman, G. J. London

A series of dilute Fe-Co alloy specimens were prepared from zone-melted iron. The iron used was given ten floating-zone passes in purified hydrogen. Alloying was accomplished by plating a gradient of metallic cobalt onto a 1/4-in.-diam bar of material from a pure plating bath. The deposit was radioac-tively tagged by a small addition of co80 to the plating bath. Alloy homogenization was accomplished by passing an additional floating-zone pass through the plated section of the bar. The final concentration gradient achieved was from residual to about 1000 ppm (0.1 pct) added Co. After homogenization, the bar was swaged to 0.057 in. wire and cut to tensile specimen blanks 1-1/16 in. long. Each specimen was counted in a well-type scintillation counter. The concentration of cobalt was computed by combining the normalized specimen counting rate with the known weight (measured to the nearest 0.01 mg) of cobalt added during plating. Fig. 1 shows the cobalt gradient obtained, exclusive of residual cobalt which was estimated by neutron-activation analysis to be approximately 50 ppm. Results of recrystallization for 1 hr at 750°, 700°, 650°, and 600°C with specimens containing 40, 170, 470, and 870 ppm added Co are shown in Figs. 2, 3, 4, and 5. Recrystallization was accomplished in a dynamic vacuum of less than 1 x 10 torr. The specimens were mounted and polished parallel to the swaging direction. The recrystallization re- sults show a radical coarsening of structure with increasing cobalt concentration. The coarsest structure obtained was at the 470-ppm level (at all recrystallization temperatures) with a slight grain refinement at the 870-ppm level shown. A more normal solid-solution effect is seen in Fig. 5 (60OoC, 1 hr) where the only specimen completely recrystallized is the one containing 47 ppm Co. Since the possibility existed that some atmosphere-contamination phenomenon might be responsible for the observed results the recrystallization series was repeated using sealed quartz capsules. These were filled with purified argon which was gettered during heat treatment on metallic titanium included in the capsules. The results obtained were essentially the same as shown. Another identical alloy was made using a 5-mm-diam bar of Westinghouse Puron. Specimen preparation and recrystallization treatment were also as described. The results obtained (see Table I) were somewhat erratic. Some coarsening in structure does appear at the highest cobalt concentrations. There is no apparent relationship between the coarse, columnar, directionally solidified structure of the as-melted bars and any of the recrystallized grain structures observed, all of which are much finer than the former structure. A recrystallization process can be most simply described as one of homogeneous nucleation of recrystallized grains in a cold-worked matrix followed by more or less uniform growth of the strain free grain into the cold-worked material.' An impurity element may influence one or both of these processes. Aust and utter' have shown that impurities strongly influence grain boundary mobility in lead. Moreover, definite recrystallization textures are produced by small concentrations of tin,3 while additions of silver or gold4 produce large boundary in-

Jan 1, 1964

By P. D. Southgate

VIBRATION, both ultrasonic and sonic, can affect the course of a variety of metallurgical processes. Reports of work on this subject have appeared at intervals over the last twenty years and a thorough review has been made by Hiedemann,' who gives a full list of references. It has been established that both refinement of structure and outgassing of the melt can be produced in most metals with sufficiently intense vibration. Many of the experiments in this field have been carried out using alloys of direct commercial interest in production- type casting equipment. Here a different approach is adopted, and simple binary alloys which exhibit different types of structure are used to facilitate examination of the effects produced under well-controlled conditions. Results from this kind of experiment should enable the basis of larger scale experiments with similar types of materials to be better substantiated. The alloys selected for this work are: 1) aluminum of 99.2 pct purity, the principal impurity being iron, near 0.4 pct; 2) A1-1.8 pct Fe, which is near eutectic composition; 3) A1-4 pct Fe—the second phase, of composition FeAl3, forms distinct acicular crystals; and 4) A1-12 pct Si—although this is of eutectic composition, the silicon normally appears in the form of large plates. Experimental Method There are three practicable methods by which acoustic vibration can be transferred to liquid metals: a) vibration of the whole of the container; b) electromagnetic induction; and c) insertion of a vibrating probe into the liquid. Method c is chosen here, and a frequency of 8 kc per sec is used. The end of the probe is electrically heated so that the metal near it will be the last to solidify. This ensures that vibration is transmitted directly to the liquid metal without passing through any solidifying and pasty intermediate region, which would attenuate acoustic waves severely. In addition, the heating prevents solid metal adhering to the probe, with consequent detuning. The transducer assembly is shown in Fig. 1. A stack of Permendur laminations 30 cm long acts as a half-wave vibrator and a winding along its length carries polarizing and energizing currents. It is joined by a half-wave coupling bar to a mild steel exponential horn, which tapers from 3.8 to 1.1 cm diam. A stainless steel stub 3 cm in length is welded on the free end. The assembly is supported by a plate located at the node of the coupling bar. Acoustic radiation losses are minimized by allowing the free end of the transducer to protrude above the surface of the cooling water. The exponential horn serves the function of matching the acoustic output impedance of the transducer to the radiation resistance of the probe into the melt. Electrical drive is provided by a 1 kw generator. Measurements of probe vibration amplitude during melt treatment are obtained from a gramophone pick-up with the needle attached to the wide end of the horn. This device is calibrated with a microscope before use. Liquid aluminum is very actively erosive and solution of materials with which the molten metal comes into contactcauses difficulties. Erosion of the probes in particular can be severe since it is greatly accelerated by the vibration. Tests of various acous-

Jan 1, 1958

By B. F. Decker, D. Harker

The recrystallization reaction in OFHC and spectroscopically pure copper has been followed by X ray diffraction determinations of the amount of material with the cold-worked and recrystallized textures in specimens which had been given various heat treatments. The heats of activation for recrystallization are found to be: 29.9 kcal per rnol for OFHC copper and 22.4 kcal per rnol for spectroscopic copper. A reliable and speedy method for measuring the amount of recrystallized material in a piece of rolled metal, together with a new scheme for low temperature heat treatment, have made possible a determination of the activation energy for recrystallization in rolled copper. This method for studying recrystallization rates is different from others reported in the literature.' Oxygen free, high conductivity copper—OFHC copper—of purity 99.98 pct gave an activation energy for recrystallization of 29.9 kcal per mol with recrystallization data taken in the temperature range 208-245°C. Copper of purity 99.999 pct from the American Smelting & Refining Co. gave an activation energy for recrystallization of 22.4 kcal per mol with recrystallization data taken in the temperature range 43-135°C. The great change in activation energy for recrystallization as the small amount of impurity in the metal is decreased suggests that the motion of grain boundaries is conditioned by the impurities which must be concentrated in them. Thus the OFHC copper recrystallizes with an activation energy of the order of magnitude to be expected for the diffusion of the kind of impurities likely to be present. The high purity copper, on the other hand, recrystallizes with a much lower activation energy, in accord with the notion that the grain boundaries need not wait for the impurities to diffuse with them. Copper when strongly cold-rolled has a well-defined crystallite texture which can be described by saying that the [111] direction of the face- centered cubic crystals is aligned approximately in the cross-rolling direction and that faces of the form {110} lie approximately in the rolling plane. When such rolled copper is completely annealed the crystallite texture is quite different: the [loo] direction is in the cross-rolling direction and faces of the form (100) are in the rolling plane. At intermediate stages of annealing, the copper contains both textures. If a Geiger counter X ray diffraction spectrometer is set up so as to measure the intensity of the (200) Bragg reflection from the rolled surface of a piece of copper strip, this intensity increases from a very small value in the cold-worked state to a maximum as the specimen is annealed. The same would be true for (200) reflections from planes normal to the rolling or cross-rolling directions. In view of this fact, the amount of material in the copper which has recrystallized can be measured by comparing the intensities of one of these reflections just mentioned with the intensity from a similar specimen after complete annealing. In much the same way the intensity of (111) reflections from planes normal to the cross-rolling direction could be used to measure the amount of unrecrystallized material in the specimen. In the work to be described here the amounts of recrystallized and unrecrystallized material in partly annealed rolled copper specimens were determined in this way. Experimental Procedure Samples of oxygen free high conductivity (OFHC) copper, cold-rolled 99.7 pct to 0.002 in. thickness, were subjected to heat treatments for various chosen times at four different temperatures, and high purity copper samples, cold-rolled 98.0 pct to 0.0015 in. thickness, at six different temperatures. Each sample, after treatment, was placed in an orientation sample holder for use with a Geiger counter X ray spectrometer and a reading was taken of the intensity of the (200) reflection from planes perpendicular to

Jan 1, 1951

By J. E. McDonald, J. G. Eberhart

A model is discussed from which the work of adhcslon .tor liquid transition metals on aluminum oxide surfaces can he calculated, A close-packed (00011 oxygen surface on A12O3 is assumed with two different types of surface sites: one type involving metal-oxygen bonds and the other man der Waals into actions. The work of adhesion is thus expressed as the sum of these two bonsding free energies. Calculated works of adhesion for nickel, titanium, chromium, and zirconium on sapphire agree well with the experimentally determined quantities. The model is extentled to the calculation of the work of adhesion and shear stress required to remove a thin metal film from a sapphire substrate and is in good agreement with experimental values. The obsewed dependence of the work of adhesion on the free energy of oxide formation of the metal is shown to also provide an interpretation of the tittle dependence of thin-film adhesion. THIS paper presents a model for the type of bonding which occurs across a metal-A12O3 interface. The model is used to explain the results of two types of experiments in which such an interface exists: 1) the adhesion of thin metal films on Al2O3 substrates and 2) the wetting of A12O3 by liquid metal drops. The adhesion of thin films to various substrates has been the subject of a variety of investigations.'-' Benjamin and weaver3 and Bowie,6 using the scratch test developed by Heavens,10 studied the adhesion of metallic films to glass substrates. Their observations for noble-metal film adhesion agree well with an adhesion model involving a van der Waals type of bonding between the film and the substrate. For films of metals whose free energy of oxide formation. ?F°f, has a negative value. Benjamin and weaver3 and Bowie6 found a time-dependent adhesion with an initial value that can be interpreted in terms of van der Waals interactions but a larger terminal value which was related to ?F°f, Karnow-sky and Estill7 deposited films on sapphire at elevated temperatures and noticed no time dependence of film adhesion but a similar correlation with ?F°f. Because of the kinetic problems associated with thin-film adhesion it is desirable to examine adhesion in an equilibrium system. The wetting behavior of liquid-metal drops on Al2O3 provides such a system. Systems of this metal-ceramic type have been studied extensively.11 Humenik and Kingeryl2 have measured the wetting of A12O3 (and other substrates) by several metals and have pointed out that the wetting ability of these metals increases with increasing values of -?F°f. It is thus seen that thin-film adhesion and metal wetting on A12O3 are both related to the tendency of the metal to react with the surface oxide ions of the Al2O3 substrate and, because of this, both phenomena should be explainable by an appropriate model for the metal-Al2O3 interfacial bonding. In the sections that follow, wetting and adhesion data on A2O3 are reviewed and a model is presented by which these phenomena can be interpreted. ANALYSIS OF WETTING EXPERIMENTS In an equilibrium system involving a liquid-metal drop on a solid Al2O3 substrate, the work of adhesion, WAD, is defined by the Dupre, equation as WAD = ?s + ?L -?sL [1] where ?s and ?L are the surface free energies of the solid substrate and the liquid drop, respectively, and ?sL is the interfacial free energy. The work of adhesion is the work required to separate a unit area of the solid-liquid interface into two surfaces. The work of adhesion is usually determined from a sessile-drop experiment in which yL and the contact angle, ?, are measured. The Young-Dupr6 equation is then used to calculate WAD Wad = ?L (1+ cos ?) [2] The literature of this subject has been examined and Table I shows work of adhesion data for various liquid metals as measured on A12O3 substrates. The standard free energy of oxide formation of the metal at the temperature of the wetting experiment, ?F°f . is also tabulated in kcal per g-atom of oxygen. The data is grouped according to the gaseous atmos-

Jan 1, 1965

By J. G. Kura, P. D. Frost, L. W. Eastwood

THE preparation and general properties of mag-nesium-lithium base alloys have been described in earlier papers.l,2 Lithium forms solid solutions with pure magnesium, lowers its density, and improves its formability. The improved isotropy and better formability of these alloys are attributed to the ability of lithium to convert the magnesium lattice from hexagonal (alpha phase) to body-centered-cubic (beta phase) structure. This change in structure is, however, accompanied by some limitations which make it difficult, if not impossible, to combine all the desirable properties in one composition. The most important of these limitations is the tendency of the high-strength alloys to overage and lose strength at temperatures of the order of 150" to 200°F. A study was made of the effects of composition and heat treatment on the age-hardening character- istics of the alloys. Stability of properties was determined by hardness and tensile testing of the alloys at room temperature after various periods of exposure to elevated temperatures. Precipitation-hardening curves are shown for a number of magnesium-lithium-zinc alloys in fig. 1. All the alloys were solution treated at 700°F and aged at 200°F. The reason for using the drastic quench, toluene at —105°F, was to reduce the rapid precipitation of the hardening phase which takes place at room temperature. Previous experience has shown that a hardness of about 90 to 95 Rockwell E is indicative of yield strengths in the range of 35,000 to 40,000 psi. This is a desirable strength level for magnesium-lithium base alloys with specific gravities of the order of 1.65 or less. Although the hardness level is raised by large zinc contents, a corresponding decrease in the cold formability of these alloys occurs with increasing zinc content. Thus, alloys containing up to about 10 pct Zn and having hardnesses of the order of 70 to 75 Rockwell E may be bent over a very small radius; however, the 16 pct Zn alloy requires a bend radius of more than 8T. The hardness relationships illustrated in fig. 1 can be explained by the partial phase diagram shown in fig. 2. The zinc-free magnesium-lithium alloys are entirely body-centered cubic (100 pct beta phase) when the lithium content of the binary is 10.3 pct or higher. When zinc is added, the boundary between the beta and alpha-plus-beta fields at 700°F is shifted to lower lithium contents. In addition, the solubility of zinc at 700°F decreases with decreasing lithium content. It is shown by a study of micro-structures that the limit of solid solubility of zinc in the 6Mg/Li* matrix at 700°F is about 19 pct. It is believed from a study of the aging curves that this limit is about 2 to 3 pct at 200°F. Zinc additions up to about 2 pct increase the hardness and strength of the magnesium-lithium base solid solution. Larger additions of zinc effect further hardness increases, but precipitate during prolonged aging at 200°F. Alloys having 14 to 20 pct Zn precipitation harden extremely rapidly during quenching, even when quenched in toluene at —105° F. The high-zinc alloys overage at 200°F but are capable of maintaining reasonably high hardnesses for periods up to 1000 hr.

Jan 1, 1951

By J. H. Westbrook, R. W. Guard

The influence of a number of alloying additions on the structure and hardness of Ni3Al (?') has been studied. Three general effects have been observed.. solid-solution hardening, strain aging, and defect hardening arising from deviations from stoichiometry. The solid-solution hardening phenomena are complicated relative to binary terminal solid solutions due to the possibility of virtually independent substitution for the component elements and to the concomitant effects of strain aging. In many superior nickel-base high-temperature alloys the elevated temperature strength is attributable to the presence of a dispersion of Ni3A1 (?') in a solid-solution matrix. Examples of such alloys are Inconel X-550, Inco 713, Waspalloy, and Nimonic 80. It is, therefore, appropriate to seek a further understanding of the properties and alloying behavior of this compound. Ni3Al, the compound most rich in nickel in the nickel-aluminum binary system, was first detected by litakal but not established with certainty until the much later studies of Bradley and Taylor' and Alexander and Vaughan.3 More recently the mechanism of formation was clarified by Floyd4 who showed that Ni3Al is the product of a peritectic reaction at 1395°C between the melt and the compound NiAl in agreement with the original suggestion of Alexander and Vaughan.3 Ni3Al has the ordered face-centered-cubic or Cu3Au structure in which the nickel atoms occupy the face centers and the aluminum atoms the cube corners, a0 = 3.570A. Despite earlier reports to the contrary. the compound apparently remains ordered at least to 1000oC.5 It exists over a narrow range of compositions (-3 pct wide) whose limits and temperature dependencies thereof have been reviewed recently by Taylor and Floyd.' Most previous workers have found Ni3Al to be both hard and brittle7,8 although Maxwell and Grala8 obtained 2.5 to 6 pct tensile elongation at room temperature and Alexander and vaughan3 described the material as "hard and tough" on the basis of observations made while preparing metallographic specimens. In a recent study one of the present authors found that although considerable intergranu-lar brittleness was evident: individual grains of a coarse-grained inert atmosphere arc-melted specimen were readily deformable.l0 The same study also showed Ni3Al to have an anomalous temperature dependence of hardness in that such a curve exhibits a number of peaks between room temperature and 800°C which could not be associated with any microscopically observable precipitation reactions or polymorphic transformations. It was, therefore, proposed in the present study to elucidate the anomalous high-temperature strength behavior and to examine the solid-solution alloying of this compound and the effects of such alloying on hardness. Sample Preparation and Experimental Procedure-Samples, both of pure Ni,Al and of various alloyed solid solutions based on Ni3Al, were prepared by arc melting 100-g buttons in an inert atmosphere arc furnace. All buttons were heat treated for 4 hr at 1275oC and examined metallographically for homogeneity. Microstructures were typically homogeneous and single phase with ASTM grain size about 1 and unusually clean grain boundaries. Chemical analyses showed good correspondence (within a few tenths of a percent) with intended compositions. Microindentation hardness data were obtained from room temperature to 800°C in vacuo using a balanced-beam type loading system in an instrument to be described in detail elsewhere." In general a 100-g load, a loading rate of 1 mm per min and an indentation time of 15 sec were used. Various indenter materials were used according to the materials bein tested because of specimen-indenter interaction. Fl Measurements of the Vickers-type indentations were made at room temperature. Hardness-temperature curves were run at least twice on each sample to ensure that surface work-hardening effects had been eliminated." Precision lattice-parameter measurements were made on powder samples using a back-reflection

Jan 1, 1960

By C. S. Smith, E. W. Palmer

IN 1934, when Gregg and Daniloffl wrote their excellent monograph on the alloys of iron and copper, the most recent literature on the constitution of the alloys indicated a narrow single-liquid area for 20" above the liquidus with a closed liquid mis-cibility gap above this. Since that time, however, a number of investigators have confirmed the much earlier studies of Mushet2 and Stead3 who, among others in the nineteenth century, had described the true state of affairs. Liquid copper and iron are completely miscible in the absence of carbon, but small amounts of carbon cause liquid segregation. In 1934, one of the writers' mentioned evidence for the absence of liquid separation in carbon-free alloys at temperatures up to 1700°C. Two years later, Mad-docks and Claussen5 unequivocally established the absence of liquid segregation and published a revised diagram, reproduced in fig. 1. They also studied the limits of the two-liquid area in ternary alloys of iron, copper, and carbon as a function of carbon and iron content. In the same year Simpson and Bannister" and Schumacher and Souden7 described in some detail the properties of alloys containing 50 to 75 pct Cu. More recently Hodges et al.16 have developed the copper-rich alloys for use as high-strength conductors. In 1937, Iwase, Okamoto, and Ameniya8 published data on the miscibility gap in ternary alloys of iron, copper, and carbon that supported the conclusions of Maddocks and Claussen, and definitely located the two-liquid area at temperatures of 1450" and 1540°C. They also reported that additions of 1 pct Al, Ni, Pb, Sn, or Zn caused no segregation in 50 pct Cu alloys at 1540°C. The use of copper in amounts approximating 1 pct has found industrial employment to an increasing degree in both wrought and cast steels, for such steels are capable of being precipitation-hardened following normalizing, and have high yield strengths. This is summarized by Gregg and Daniloff,1 Sallitt,9 and Lorig and Adams,10 while Alexander" gives additional information on the heat treatment of copper-steel castings. Lippert12 has described Digby's two-phase steels containing copper and chromium. The work described in the present paper was done in the years 1932 to 1934, at which time much of the information was new. The excellent work subsequently done in other laboratories but more promptly published makes the present paper in part only a confirmation of what is now well known. There has not, however, been published any unified study of

Jan 1, 1951

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

IN THE past year, Jaffee and Campbell&apos; and Finlay and Snyder2 reported on the mechanical properties of titanium-base alloys, some of which were in the same ranges of composition as are covered in this paper. In this paper, evidence confirming that given by Finlay and Snyder on the effects of carbon, oxygen, and nitrogen on titanium will be presented; and, in addition, new data will be given on the effects of these elements on the flow properties and phase transformation of titanium. Materials and Preparation of Alloys The preparation and general properties of iodide titanium have been adequately described elsewhere.&apos; , As-deposited iodide titanium rod, prepared at Battelle, of Vickers hardness less than 90 was employed as the base metal in the present work. This was the same material as that used by Finlay and Snyder.2 The probable analysis reported by them for standard quality metal holds here also: N 0.005 pct, 0 0.01 pct, C 0.03 pct, Fe <0.04 pct, A1 <0.05 pct, Si <0.03 pct, and Ti 99.85 pct. Carbon was added in the form of flake graphite supplied by the Joseph Dixon Crucible Co. Oxygen was added in the form of c.p. grade TiO, powder, produced by J. T. Baker Chemical Co. Nitrogen was added in Ti3N4 powder, supplied by the Remington Arms Co. Individual ingots weighed 7 or 8 g. Carbon, oxygen, or nitrogen was added by placing the corresponding powder in a capsule made from as-deposited iodide titanium rods and melting the capsule with the balance of the charge. The charge was are-melted with a tungsten electrode on a water-cooled copper hearth under a partial vacuum of very pure argon (99.92 pct minimum). Melting was practically contamination free. Vick-ers hardness increases of less than 10 points were normal for unalloyed iodide titanium control melts. Nitrogen analyses of are-melted iodide titanium showed a nitrogen content of 0.005 pct, about the same as is present in the as-deposited rod. No tungsten pickup was found in a melt of iodide titanium analyzed for tungsten. Weight losses in melting nitrogen-free alloys were very small and varied consistently from nil to 0.015 g (0 to 0.2 pct). This permitted the use of nominal composition for these alloys. Chemical analyses made for carbon, which can be analyzed conveniently by combustion methods, justified this procedure. Where nitrogen was added, considerable splattering took place. Here it was necessary to analyze for nitrogen by the Kjeldahl method. The ingots were hot rolled at 850°C to about 0.045 in. thick. After hot rolling, the strips were descaled by mechanical grinding, and then given a cold reduction of 5 to 10 pct to insure a uniform thickness throughout the length of the specimen. The edge strips and the tensile strips were annealed in a vacuum of 1x10-4 mm Hg pressure for 3 1/2 hr at 850°C and furnace cooled. Methods of Investigation Hardness Measurements: At least five Vickers hardness measurements were taken using a 10-kg load on each sample in the following conditions: (1) top and bottom of each ingot, (2) top and bottom surface of as-rolled and annealed sheet, and (3) on cross-section of annealed sheet and all quenched specimens. Tensile Tests: Tensile tests were conducted on Baldwin-Southwark testing machines having load ranges of 600 or 2000 lb. Tests were made on 1-in. gauge-length specimens, 3 1/4-in. overall length, 1/2 in. wide, 0.040 in. thick, with a reduced section 1 1/4 in. long and 0.250 in. wide. Two SR-4, A-7 strain gauges, one mounted on each side of the specimen, were used to measure the strain over a limited range to determine the modulus of elasticity. After the modulus of elasticity readings had been taken, load vs. strain readings were taken, using only one strain gauge, at increments of 0.0001 in. until the yield points were passed and then at 0.001-in. increments to the limit of the strain-gauge indicator (0.02 in.). Strain readings above 0.02 in. per in. were taken every 0.01 in., using dividers to measure the strain between the 1-in. gauge marks until the maximum load had been reached. Crosshead speed, when using the SR-4 gauges, was 0.005 in. per min, and, when using dividers, 0.01 in. per min. Flow Curves: Flow curves were determined using the true stress-true strain data obtained during the tension test. The usefulness of this type of information has been dealt with very adequately elsewhere by L. R. Jackson,&apos; J. H. Hollomon,6 and many others. Flow curves of true stress vs. true strain could be converted to the more conventional cold-work curve of 0.2 pct offset yield strength vs. percentage of cold reduction by means of the transformation, 1/1 = 1/1-R, where R is the fraction reduction in cold working. Thus, the true strains corresponding to percentage reduction can be calculated, and the 0.2 pct offset yield strengths scaled off the — 6 curve by taking the true stresses corresponding to the values of 6 + 0.002 strain. Heat Treatment: For the transformation studies, the alloys were heat treated in a horizontal-tube furnace using a dried 99.92 pct argon atmosphere, and quenched into water. Essentially no contamination was found after several hours of heat treatment at temperatures up to 1050°C. Metallography: Specimens were prepared in the

Jan 1, 1951

By J. E. Hilliard, J. W. Cahn

calculation has been made of the standard deviations to be expected in the measurement of volume fractions by areal analysis, lineal analysis and four point-counting Procedures. The effect of experimetztal errors is not included. Our conclusion is that a point count using a two-dimensional grid will be the most efficient method of volume fraction analvsis providing the grid spacing IS coarse enough. The predicted standard deviation for such an analysis is shown to he in good agreement with that determined experimentally. A metallurgist wishing to estimate a structural property by means of quantitative metallography is often faced with a choice between several different procedures. In such a case, he will naturally wish to know: a) Which procedure is the most efficient in the sense of requiring the least effort for a given precision? b) For a given procedure, what are the conditions for maximum efficiency? c) Under these conditions, how many measurements are required to attain a given precision? It is our aim in this paper to provide at least partial answers to these queries as they relate to the estimation of volume fractions from measurements on a random two-dimensional section of an opaque specimen. The commonly used techniques1,2 for volume-fraction analyses are based on one or more of the following principles: i) For an areal or Delesse3 analysis: That the areal fraction of a three-dimensional feature intercepted by a random plane provides an unbiased estimate of the volume fraction of that feature. ii) For a lineal or Rosiwal4 analysis: That the fractional intercept on a line passing at random through a two-or three-dimensional feature provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. iii) For a point-count analysis: That the fractional number of randomly or regularly dispersed points falling within the boundaries of a two-dimensional feature on a plane, or within the boundaries of a three-dimensional feature in a volume, provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. The absence of bias referred to in these principles does not, of course, imply that the results of an analysis will be free of error, but only that the expected result is equal to the true one. Application of the foregoing principles provide the following six possible experimental procedures: a) An Areal Analysis—This involves the measurement with a planimeter (or other means) of the area of a constitutent intercepted by the plane of polish b) A Two-Dimensional Random Point Count—Apos-sible experimental procedure for this analysis is to superimpose a sheet of transparent graph paper on a micrograph, and then use a table of random numbers to select coordinates for the points. c) A Two-Dimensiotuzl Systematic Point Count-Similar to b) except that the points are distributed in a prescribed manner, usually at the corners of a lattice superimposed on a micrograph or the screen of a projection microscope. d)A Lineal Analysis—A measurement of the fractional line length intercepted. It is usually performed by traversing the specimen under the cross hairs of a microscope and recording the distance travelled in each constituent. e) 4 One-Dimensional Random-Point Count— This could be performed by traversing the specimen with stops at random intervals to identify the constituent then present under the cross hairs. f) A One-Dimensionul Systematic Point Count— Similar to e) except that the traverse is stopped at prescribed (usually equal) intervals. It will be noted that the point-counting procedures b) and c) can be regarded as methods of estimating the areal fraction. Similarly, e) and f) are indirect methods of making a lineal analysis. All of the six procedures described above involve at least one stage of sampling. Thus, quite apart from any experimental errors, there will always be a statistical uncertainty associated with the final results. It is with the calculation of this uncertainty that we will be concerned. To avoid unnecessary repetition, the statistical relationships that will be used in the calculations are collected together in the appendix. For a fuller discussion reference should be made to one of the many textbooks5,6 on statistics. For symbols relating to the specimen structure we will follow as far as possible the terminology used by Smith and Guttman.7

Jan 1, 1962

By R. M. Asimow

Both smith1 and wells2 have shown that the dif-fusivity of carbon in austenite increases rapidly with increasing carbon concentration. Smith has shown, in addition, that part but not all of this increase can be attributed to the concentration dependence of the activity coefficient of carbon in austenite. From the work of Eshelby&apos;, it is known that, because of the image displacements, there is a uniform dilatation of the material in a body containing random centers of dilatation. It is thus tempting to explain the enhanced diffusivity as resulting from this apparent negative pressure caused by the interstitial carbon atoms.* That is, the activation free energy for diffusion is not directly a function of concentration if we consider that the alloy is subjected to a concentration-dependent pressure. To proceed with a quantitative solution, it is necessary to determine the activation volume AV for the diffusion process. An exact calculation of AV is quite a difficult problem and does not appear to have been solved as yet. A simpler procedure is to use the semiempirical, macroscopic theory of seyes&apos; which relates the activation free energy AG to AV. Keyes has shown that for many types of diffusion processes the following relationship is valid Where p is the Gruneisen constant and x the compressibility. This relationship is based on the assumption that AG can be identified with strain-energy terms. In general there will also be contributions to AG due to a change in the energy of the valence electrons of the metal; thus the relation must be considered largely empirical. Surprisingly, for self-diffusion where it is well-known that the electronic contribution is quite important,&apos; the Keyes relation works quite well for many systems. For interstitial diffusion where it might be expected that the relationship is on a firmer theoretical basis, the limited experimental data available is not in particularly good agreement as can be seen from Table I. However, it must be remembered that besides the uncertain basis of the Keyes formula there is considerable uncertainty in some of the experimental values of AV. The only real justification for using the Keyes formula in the present analysis is that it gives a result which satisfactorily solves the problem at hand and, further, there are no more reliable procedures for calculating AV available. The coefficient 3 in Eq. [I] is determined such that the room-temperature value for x is to be used. The activation entropy AS is estimated as 8.95 x 10"3 kcal per OK mole using the values in Table I1 and the Zener" relation AS = PAHIT, where p is a dimensionless thermal coefficient of Young&apos;s modulus which is to be evaluated at low values of T/T,, aH is the activation enthalpy, and T, is the melting temperature of the alloy. The resulting value of AG at 1000°C is 25.6 kcal per mole. The Gruneisen constant (p = 3cup/XC,), where p is the density, is evaluated from the room-temperature data in Table I1 after calculating C, from the relation. A value of p = 8.32 g per cu cm based on the value of a. in Table I is used. The result is C, = 5.0 x lo6 erg per g, H = 2.32, and AV = 3.41 cu cm per mole at 1000°C and infinite carbon dilution. It is assumed that the activation volume is not a function of carbon concentration. The theory could be refined to consider AV a function of concentration, but due to the uncertainties in the parameters there seems little justification for this. Carbon dissolved in austenite forms a nonideal solid solution, so that in writing an equation for. the diffusivity of carbon it is necessary to take into account the change in activity coefficient with concentration. The resulting equation is16

Jan 1, 1964

By W. Rosotoker

Using an expression for the free energy of a homogeneous phase as a function of composition, a relationship is derived which interrelates the phase boundaries extending from the allotropic transformation of the solvent metal. Comparisons between observed and calculated phase boundaries in the systems Fe-Ni, Fe-Mn, Fe-W, Ti-Mo, and Ti-Cb are presented. IT is the purpose of this paper to illustrate how the general free energy equations for two phases in equilibrium may be used to derive an expression which interrelates the phase boundaries extending from the allotropic transformation of the solvent metal. The free energy per gram atom of a disordered solid solution may, for many purposes, be represented by the equation:&apos; F = ½NZ [C-V,, + (1-C) VbB + 2C (l-C)V] + K(T) +RT[C-lnC+ (l-C)ln(l-C) ] [1] where N is Avogadro&apos;s number; Z, the coordination number; C, the concentration of the solute element in atomic percent; the subscripts refer to concentrations at phase mixture boundaries; VAA, VBB, and V,, are the bond energies between like and unlike adjacent atoms, respectively, at the interatomic spacing characteristic of the phase. The bond energies are usually assumed to be independent of small changes in the lattice parameter occasioned by solute additions and variations in temperature; V = VAB ---------------—— ; K(T) is the sum of the heat con- tent and heat entropy; R, the molar gas constant; and T, the temperature in degrees Kelvin. The free energy of a homogeneous phase is there- fore the sum of an internal energy, a specific heat, and a configurational entropy term, respectively. The compositions of two phases in equilibrium at a given temperature are governed by the minimum total free energy principle. Graphically, this is represented by the points of tangency of the tangent common to the free energy vs. concentration curves of the two phases. Analytically, this may be expressed as: ( df) = (df) [2] dc dc Expanding both sides using eq 1, the following equation is obtained after convenient readjustment of the terms: RT In[(ca)(1-c)]-½N (Vaa-Vbb)(Za-Zb) +NV [Za(l-2Ca)-Z,(l-2C,)] [3] The following assumptions have been made at this point: 1—The specific heats of the two phases are independent of composition variations within the range under consideration. Accordingly, the K(T) terms disappear on differentiation. 2— (Vaa)o = (VAA); (VBB). = (VBB); Va = V, Theyjustification for these assumptions can lie only in the successful application of the resultant equation. It may be noted that Zener2 has used assumption 1 in the calculation of the boundaries limiting the (a+j3) phase mixture in the Cu-Zn system.

Jan 1, 1952

By L. D. Hall, D. R. Mash

The paper presents the results of experiments on the anelastic. behavior of gold, as manifested by grain boundary relaxation. Two grain boundary internal friction peaks are found for 99.9998 pct Au. It is found that the peaks are associated with primary and secondary recrystallization. However, the existence of two discrete peaks cannot be explained on the basis of grain size and shape alone. It is suggested that grain boundary stability, as determined by orientation, plays a role in the observed effects. EVIDENCE for the viscous behavior of grain boundaries in metals has been presented in recent years by several investigators, based upon studies of various anelastic effects, especially internal friction. KG1 has contributed greatly to this field, having put forward a coherent body of evidence for stress relaxation by the viscous intercrystalline flow mechanism. In this connection, he has made extensive use of pure aluminum (99.991 pct) as the test material, although he has also studied other metals and alloys, including pure iron (Puron).² Rotherham, Smith, and Greenough³ have studied the internal friction of pure tin, interpreting their results in a manner similar to that of KG. In view of the importance of such studies in shedding light upon the fundamental structure and behavior of the grain boundaries in pure metals, it appears that the use of a very pure test material which is inert to its environment should provide useful information on anelastic properties and the source of such behavior in pure metals. The present work was carried out on spectrograph-ically pure, 99.9998 pct Au, free of all impurities except for a trace of silver, estimated to be present to the extent of about 0.0002 pct. The term "pure gold" will hereafter refer to this very pure material. Gold of commercial purity, 99.98 pct, was also studied to observe the effects of small amounts of impurities. A pure gold "single crystal" specimen was also tested for comparison. The variation of the internal friction and rigidity modulus as a function of temperature was determined by means of a torsion pendulum apparatus employing extremely low stress amplitudes and a frequency of vibration of the order of 1 cycle per sec. A 12 in. length of 0.031 in. (20 gage) gold wire formed the suspension element. The apparatus was similar to that described by Ke.l The test procedure and the basic requirements to be met for obtaining useful experimental data by this method have been given elsewhere.1,2 It should be made clear that in all of the experiments to be described, the internal friction and rigidity were independent of the amplitude of torsional vibration. The semilog plot of amplitude of vibration vs ordinal number of vibration was a straight line. This was carefully verified for each internal friction measurement. The linear variation shows that the internal friction was independent of stress; i.e., that the specimens were not being cold-worked during testing. The reproducibility of the internal friction curves, which were obtained by cyclic heating and cooling, indicates that the gold was unaffected by its environment during the tests. The measure of internal friction adopted in the present study is the conventional "logarithmic decrement," defined as follows: log. dec. = l/n In A0/An [I] where n is the number of cycles or vibrations; A,, the initial amplitude of vibration; and An, the amplitude after the nth cycle. When the logarithmic decrement is small, the shear modulus, G, of the wire is proportional to the square of the frequency of vibration provided the length and radius of the wire are kept constant. A plot of frequency squared vs temperature gives the following ratio:&apos; This expresses the fraction of the stress which has not been relaxed at a given temperature. Gr and Gv are the relaxed and unrelaxed moduli, respectively. The frequency of vibration in the polycrys-talline specimen is fp, and the frequency of vibration of a single crystal is f8. This latter quantity is obtained simply by extrapolating the linear, low temperature portion of the curve of frequency squared vs temperature for the polycrystalline specimens. The theory of viscous grain boundary stress relaxation as demonstrated by the anelastic behavior of metals has been discussed in detail by Zener4 and need not be reproduced here. Experimental Results Initial measurements of the internal friction of pure gold were carried out on specimens which had been drawn with no intermediate annealing, resulting in a material which had undergone approximately 99 pct reduction of area in final processing. Annealing was then carried out at successively higher temperatures starting at 400°F for 1 hr and proceeding in this manner to as high as 1600°F in 100°F intervals. After each annealing treatment an internal friction and rigidity vs temperature curve was obtained over the range from room temperature to the particular annealing temperature. The resulting internal friction curves did not exhibit well defined maxima (peaks), but rather several fairly flat

Jan 1, 1954

By Jei Y. Choi, P. G. Shewmon

Using a scratch smoothing technique, the magnitude and the ratio of the surface diffusion coefficients (D,) in two orthogonal directions have been measured on copper for over 100 different surface orientations. Anisotropy was found for all surface orientations except those lying near the (100) and (111); however, these anisotropies were rarely greater than 2.0. The direction of maximum D, appears to coincide with the direction of step edges on any given surface, and if no such steps exist, no anisotropy is found. Thus the jump frequency along a step edge is shown to be faster than the frequency of a jump over the step. The values of Ds and AH for the (100) and the (111) orientations agree quite well with those obtained earlier by the grain boundary grooving technique. It is proven that the directions of maximum and minimum D, (the principal axes) for any surface orientation are known if the perfectly ordered plane corresponding to the given surface orientation possesses a plane of mirror symmetry. Thus the principal axes of D, for orientations lying along the sides of the unit stereo-graphic triangle are always known independent of the extent of thermal disorder or impurity adsorption. The merits and shortcomings of King and Mullins&apos; recently published equations relating Ds to the rate of scratch smoothing are discussed. 1N an earlier paper the authors have reported the variation of the surface diffusion coefficient (Ds) with surface orientation on copper.&apos; In that study Ds was determined from the rate of growth of grain boundary grooves on symmetric bicrystals. This gave values of Ds from 850° to 1070°C in a given direction on each of the six surfaces. It was found that the activation energy for surface diffusion was essentially the same for all six surfaces. The theory developed to explain these data assumed that the free energy of any given type of surface site depends only on the number of nearest neighbors the atom has. This same theory predicted that on any given surface Ds should be independent of direction. The primary aim of this study was to check the validity of this prediction for a wide range of surface orientations on copper. The growth of grain boundary grooves is ideal for studying Ds in a given direction on a given surface over a range of temperatures, because the same specimen can be repolished and used again. However, there is considerable work involved in growing a symmetric bicrystal, and for a survey of Ds in two or more directions on many surface orientations, the technique would be arduous. A better technique appeared to be the scratch method used primarily by Mykura. 2 If a scratch is placed in a surface whose surface tension is independent of orientation, the surface will smooth out in time under the influence of surface tension. To determine D, from this flattening, Blakely and Mykura2 used an approximate solution which was assumed to describe the rate of flattening. Recently King and Mullins3 (hereinafter K and M) have given a more exact analysis of the flattening of an isolated scratch. A second aim of this paper was to check the validity of this newer analysis and compare the values of Ds determined thereby with the values obtained from grain boundary grooving techniques. EXPERIMENTAL PROCEDURE In an effort to work with a particular predetermined surface orientation, light orthogonal scratches

Jan 1, 1963

By P. A. Beck, A. H. Lutts

IN the classical picture of recrystallization the growth of strain-free grains at the expense of a strained and work hardened matrix is responsible for the softening of cold worked metals on annealing. It has been commonly assumed that the release of the stored energy of cold work, softening, and re-orientation take place simultaneously, as the high angle boundaries of the new recrystallized grains sweep over the cold worked matrix. However, recent evidence indicates&apos;,&apos; that, at least in some cases, considerable or even complete soften- ing may take place essentially without reorientation (i.e., without the migration of ordinary high angle grain boundaries, or "recrystallization&apos;&apos;) and the release of most of the stored energy of cold work may precede softening. These cases suggest that the property changes, taking place during the annealing of cold worked metals, may be associated with various distinct processes. The study of such situations is of considerable interest, since quantitative data are still scarce. In the present work, isothermal softening curves were determined for a heavily rolled aluminum single crystal, under such conditions that no "recrystallization" occurred until after complete softening. The hardness data were correlated with X-ray diffraction pinhole patterns in order to detect any reorientation that may occur and with measure-

Jan 1, 1955

By P. A. Beck, Hsun Hu

As described by means of quantitative pole figures, the annealing texture of highly rolled aluminum consists of the four retained components of the rolling texture near (123) [121], rather more sharply developed, and of a cube texture component. Local reorientation corresponds fairly well to 40 rotation around a [111] axis. In copper strip rolled 96 pct, the annealing texture is mainly the cube texture, with the four twin orientations as minor components. The annealing texture of highly rolled brass strip consists of four components of the (225) [734] type. REVIEWS by Wassermann,&apos; Barrett,&apos; Dunn,3 and Richards&apos; give detailed accounts of the numerous publications dealing with annealing textures in rolled polycrystalline metals. Although a considerable amount of information of an empirical nature has been available for many years, even relatively recently the state of recrystallization-texture theory was considered uncertain. The reviews referred to above deal mainly with the description of experimental results, without developing generally applicable principles, suitable for explaining the observed annealing textures. The investigations of Burgers and Louwerse5 and Barrett6 showed that in deformed single crystals of aluminum the orientation of the recrystallized grains deviates drastically from that of the deformed matrix. According to Barrett and to Beck and Hu,7 the relationship between the two orientations can be best described as a rotation of about 40° around a [111] axis. Recent investigations led to similar orientation relationships for various face-centered cubic metals with a simple texture, regardless of whether the annealing process was recrystallization (strain-free grains growing in a highly deformed large crystal of aluminum&apos; or copper: or in deformed cube texture copper") or coarsening (strain-free grains growing at the expense of an essentially strain-free, fine grained, polycrystalline matrix of single orientation texture copper,&apos;" aluminum,&apos; or nickel-iron). Barrett" pointed out the possibility that this orientation relationship may be a result of the orientation dependence of the rate of grain boundary migration. More recently, considerable evidence became available in favor of this view.12,13 In apparent contradiction to the above results, it has been known for a long time that the recrystallization texture of polycrystalline metals is often similar to the deformation texture. This was found, in particular, for the fiber textures obtained by wire drawing, compression, or compression rolling.&apos; Following a suggestion by Barrett,2 Kronberg and Wilson and Beck and Hu7 described a mechanism by which a [Ill] fiber texture, resulting from plastic deformation, may be retained upon recrystallization, even though the orientation of individual recrystallized grains differs from that of the local area of the matrix in which they grow. This mechanism assumes that the reorientation corresponds to a rotation around the [1ll] axis, which is also the fiber axis. The present investigation was undertaken to examine in detail the orientation relationship between deformation texture and recrystallization texture in rolled face-centered cubic metals, using the quantitative methods of texture determination that have recently become available.", &apos;" Quantitative pole figures for the rolling textures of such metals were reported recently." Quantitative pole figures for annealing textures are given in the present paper. It was planned to investigate whether or not the orientation relationship previously found for the recrystallization of deformed single crystals, and for coarsening of single-orientation texture material, is capable of accounting for the observed, often complex, annealing textures in rolled polycrystalline metals. The question whether local reorientation is predominant, even in the early phases of the annealing process, was to be studied with high purity aluminum. by making use of an oxide film and sensitive tint illum-

Jan 1, 1953