By Dai Xi

In the present work, the viscosities of molten FenO-MgO-Si02 and FenO-MgO-CaO-Si02 semi-synthetic slags for nickel flash smelting were measured in the temperature range from 1473 to 1723K by a rotational viscometer. The ratio of Fe to Si02 was fixed at 1.2, calcium and magnesium oxide contents varied in the range from 2 to 8 mass% and 9 to 12 mass%, respectively. The results showed that silicate anions became smaller by increasing CaO content, which results in a decrease of the viscosity of the slag. In the case of MgO addition the viscosity behavior was complicated. At MgO content below 11 mass%, the viscosity increased with the increase of MgO at all temperatures tested. However, when the MgO content was above II mass%, the viscosity decreased slightly for FenO-MgO-CaO-Si02 system. At higher MgO contents, low-viscosity slags can be obtained by adding CaO. At a given composition, the viscosity decreased with increasing temperature. The higher the temperature, the more MgO can be added before saturation. The effect of Fe304 on the viscosity was quite significant. The viscosity of slag increased by 300mPa's at l573K when Fe304 content varied from 3 to 9 mass%. The viscosity values are presented as the functions of temperature and composition. A comparison between FenO-MgO-Si02 and FenO-MgO-CaO-Si02 systems is given in this study.

Jan 1, 2003

By Katsuyoshi Kondoh

The synthesis processing of Mg2Si or Mg2Si/MgO at lower temperature from the elemental magnesium alloy powder/chips and Si or SiO2 powder mixture was established via the repeated plastic working (RPW) based on Powder Metallurgy (P/M) process. RPW is much effective on the mechanical breakage of MgO surface films, which prevent from the solid-state reaction between Mg and Si powder. The solid-state synthesized Mg2Si particle of 200nm-2JIm is extremely fine, compared to that via the conventional casting process, causing the coarse one of 50-100um. This is because of not coarsening during the solid-state synthesis of Mg2Si. By using in-situ forming process of Mg2Si via RPW and pre-heating before hot working such as extrusion and forging, the magnesium composite material with Mg2Si or Mg2Si/MgO dispersions was developed in employing Si or SiO2 particles, respectively. For example, when employing AZ31 chips as raw materials of the matrix, it has low density of 1.85g/cm) and extremely superior mechanical properties, such as tensile strength over 350MPa with 5-10% elongation and Young's modulus of 47-50GPa, to the conventional Mg-Al-Zn alloys. The Mg composite alloy wires and pipes were produced via the hot extrusion process in the manufacturing plant, and also showed excellent mechanical properties.

Jan 1, 2003

By Jie E. Zhou, Yu U. Wang

"Development of crystallographic texture in polycrystals during templated grain growth process is studied by phase field modeling and computer simulation. To characterize the grain texture development, X-ray diffraction peak intensities are computed for the evolving grain structures as simulated by the phase field model, based on which Lotgering factor is further calculated as a quantitative measurement of uniaxial texturing. While the phase field modeling allows direct comparison between simulated grain structures and experimental microscopy observations, the computational diffraction allows convenient correlation between computer simulation and experimental X-ray diffraction characterization. The latter feature is especially desirable, since microscopy experiments normally require more efforts than X-ray diffraction, and diffraction is usually the preferred choice for material characterization.IntroductionThe properties of individual grains in polycrystals are generally anisotropic, while untextured polycrystalline materials with random grain orientations exhibit isotropic macroscopic properties that are independent of directions. In order to achieve anisotropic response in polycrystals, crystallographic texturing of grains is required [1]. Texture refers to the collective distribution of grain orientations towards preferred orientation in a polycrystal. To develop texture, special processing routes are needed, such as templated grain growth (TGG) for uniaxial texture [2]. TGG has been shown to provide uniaxial texture in wide variety of materials. For example, [001]-textured ferroelectric polycrystalline ceramics have been fabricated by TGG process, which exhibit enhanced piezoelectric properties [3]. Such highly textured polycrystalline materials offer better cost-performance ratio than single crystals. Thus, texture development in polycrystals is of technological importance for material applications.In this computational work, grain texture development in polycrystals during TGG process is studied. Grain structure evolution is simulated by phase field model, X-ray diffraction peak intensities for the evolving grain structures are computed, and Lotgering factor is calculated to quantitatively measure the development of uniaxial texturing. The phase field modeling allows direct comparison between simulated grain structures and experimental microscopy observations using imaging techniques such as scanning electron microscopy or optical microscopy. The computational diffraction allows convenient correlation between computer simulation and experimental X-ray diffraction characterization. The latter feature is especially desirable, because microscopy experiments normally require more efforts than X-ray diffraction, thus diffraction is usually the preferred choice for material characterization."

Jan 1, 2014

By Youn-Bae Kang

Evaporation mechanism of S from liquid Fe–C–S alloys at 1873 K was proposed by analyzing available experimental data. It has been known that increasing C content in liquid alloy increases activity coefficient of S ðfSÞ, and it could raise driving force for the evaporation reaction S = S(g). However, experimental data of the evaporation of S in the Fe–C–S alloys could not be accounted for only by considering the increases of fS. In the present study, formation of carbosulfides, CS(g) and CS2(g), was additionally taken into account in order to explain role of C for the accelerated S evaporation. Surface adsorption of S was also taken into account, which retards the evaporation rate of S. An evaporation model equation was formulated. It can be applied to calculate the evaporation rate of S over wider C content (from zero to its saturation to liquid alloy).

By Yuzura Sato

Viscosity has been measured for various molten binary alloys of nickel with iron, cobalt and chromium in order to clarify the behavior of viscous flow of molten nickel alloys. The entire concentration range for iron and cobalt and 0-67at% of chromium content were studied. The measurement method was an oscillating cup viscometry using an alumina crucible that was precisely machined. The temperature was up to about I 880K for all the measurements. The results represented good Arrhenian relationship although some measurements included overcooled temperatures. The isothermal viscosities increased monotonously with an addition of iron and chromium into nickel. The addition of cobalt increased after stationariness. The isothermal viscosities showed concave curves. Activation energies increased monotonously by adding all the elements into nickel. These phenomena were considered to be related to the thermodynamic properties 'such as the heat of mixing and the structures of mixture melts.

Jan 1, 2003

By M. E. Myers

An experimental program is being carried out to determine the thermodynamic characteristics of zinc solubilization in high-temperature iron and iron-carbon alloys. Two versions of an isopiestic technique are being used, with zinc at a lower temperature being equilibrated with pure iron foils or molten iron-carbon alloys at a higher one. The lower temperature sets the partial pressure of zinc vapor, and thus the activity relative to a given reference state. Initial results show Henrian behavior for dilute zinc solutions in austenite and a molten 4.6% C alloy, with unit-pressure solubilities in pure Fe that closely match the predictions of Wriedt.

Jan 1, 1992

By J. Alberto Vázquez M.

A sensor employing yttria-stabilized zirconia (YSZ) was used to determine the oxygen activity of molten copper at laboratory scale at temperatures of 1200° and 1300 dc. The reference electrode was a Ni-NiO mixture. The amount of the deoxidizing agent (CU3P) ranged from I to 3% of the mass of copper. Thermodynamic analysis of the Cu-O-P liquid system was carried out to predict the required deoxidizing agent and the final composition of the molten copper. Both results, calculated and experimental, show that the oxygen removal is more efficient at lower temperatures. The kinetics of the deoxidizing reaction is very fast in the first minutes of the treatment. A metalography analysis of rapid cooled samples show the oxygen and phosphorus distribution

Jan 1, 2003

By Saskia Duyvesteyn

Ion flotation is a technique applicable to the removal of metal ions from dilute solutions, using ionic surfactants.- While there are a number of physical and chemical parameters that influence the ion flotation process, this paper focuses on two of the important chemical ones, namely frother concentration and ionic strength. The effect of several frothers, including ethanol, iso-propanol and MIBC at concentrations ranging from 0% to 0.4%, was studied for the model Cd-dodecylsulfate and Cu-dodecylsulfate systems. The ionic strength, as well as the effect of monovalent and multivalent counter ions, was also studied in the range of 1@3 - 1 M, at constant pH. The results are discussed in terms of applicability to a range of effluents from minerals and materials processing operations.

Jan 1, 1994

By K. E. Gonsalves, G. M. Chow

"Nanostructured powders (particle diameter of 1 - 100 nm) have uses in electronic, magnetic, structural, thermal applications as well as advanced processing of materials. Among many methods of making nanostructured powders, chemical routes offer many attractive features such as feasibility of cost-effective bulk quantity production, design of chemistry at the molecular scale, and chemical homogeneity of the powders. In this talk, two systems of chemically synthesized nanocomposite powders are presented, namely, granular magnetic materials of Fe-Cu and Co-Cu, and thermal-structural materials of AIN-BN. Synthesis and processing, characterization and properties of these materials are discussed.IntroductionNanostructured powders (particle diameter of 1 - 100 nm) are attractive materials because of many useful properties (e.g. catalytic, optical, magnetic etc.) and processing advantages (e.g. lower sintering temperature) [1]. There are many methods of making nanostructured powders, for example, physical and chemical vapor deposition, mechanical attrition, and solution chemistry [1, 2]. A common method of making composite powders involves the grinding, mixing and blending of constituents powders, but it has the limitation of inhomogeneous mixing. Chemical routes have many useful features. Using solution chemistry, precursors can be molecularly tailored and homogeneously mixed at the molecular level. The chemical approach may result in better properties of the final product. Compared to vapor-phase fabrication techniques, chemical routes are more cost-effective in producing large quantity of material. In addition, control of particle size, size distribution and stabilization of the nanoscale particles against agglomeration can be more effectively manipulated via solution chemistry.In this paper, we present an overview of some of our work in nanocomposite powders prepared by solution chemistry. Metallic systems of FeCu and Co-Cu, and ceramic system of AIN-BN are discussed. The powders were characterized using x-ray diffraction (XRD) , scanning electron microscopy (SEM), conventional and high resolution transmission electron microscopy (TEM, HRTEM), vibrating sample magnetometry (VSM), inductively coupled plasmaatomic emission spectroscopy (ICP-AES)."

Jan 1, 1994

By C. Ramasamy

The tariff reductions on imports, as a part of on-going liberalisation process in India, has fueled competition within and outside India and has, in turn provided an opportunity to reach global markets. This change calls for quality upgrades and cost-competitiveness without impairing the environment. In this context, gas based processes, contributing to improvement in quality and environment as well as processes where controls are applied when gases inimical to environment are involved, are discussed in a remelt/cast-house scenario. The impact of such processes on fabrication cost of sheet ingot is seen alongwith consumption and cost of materials and compared with a world class standard plant in North America.

Jan 1, 1996

By Leonid N. Shekhter, Corby G. Anderson, Esra Cankaya-Yalcin, Daniel G. Gribbin, Joseph D. Lessard, Larry F. McHugh

"A new process for smelting copper, Looping Sulfide Oxidation™ (LSO™) significantly and positively alters the smelting energy balance. This process uses copper oxide in conjunction with air for the desulfurization of copper and chalcopyrite concentrates. Copper oxide is regenerated in a flash type furnace and then ""looped"" back for the oxidation of the copper concentrate. Heat and material balances show that the Looping Sulfide Oxidation™ process requires significantly lower net energy than conventional technology. This process produces anode copper and higher S02 content off-gases for efficient formation of sulfuric acid. Additionally, the process yields slags with lower copper solubility as compared to the conventional technology.IntroductionBased on the positive results from LSO™ investigations [1], further lab investigations into co=on sulfides and metal oxides were performed. It was discovered that chalcopyrite (CuFeS2) is oxidized with copper (II) oxide. In this reaction over 98.5% of sulfur was removed as S02, while a significantly improved energy balance was observed. This paper intends to analyze both the conventional flash smelting process and the newly developed Looping Sulfide Oxidation™ process, comparing heat and material balance results. LSO™ yields improvements to the energy footprint for copper, opening the door to new copper processing opportunities."

Jan 1, 2013

By Supachai Surapunt

The distribution behavior of V A minor elements (As, Sb and Bi) in the smelting stage of the Mitsubishi process were evaluated thermodynamically based on thermodynamic data and operating data. The fractional distributions between the gas, slag and matte phases considered as the degree of vapor saturation of 1.0 are as follows: 53.8, 27.2 and 19% for As, 23.6, 56.6 and 19.8% for Sb, and 91.3, 1.1 and 7.6% for Bi, respectively. Arsenic is mostly distributed to the gas and slag phases. It is effectively eliminated by volatilizing and slagging. Antimony is mainly in the slag phase, which is suitably removed by slagging. Bismuth is easily vaporized to gas phase. The degree of vapor saturation has a large effeet on the distribution behaviors of the three elements between the three phases. The amount of a minor element in the charge has an effect on the distribution of As but no effect on the distributions of Sb and Bi. Increasing matte grade and temperature results in the change of distributions for As and Sb, significantly. The change in the distribution ratio between slag and matte phases also considerably affects the distributions of As and Sb. The distribution behavior of Bi is not significantly changed by the change in matte grade, temperature and distribution ratio.

Jan 1, 2003

By Shufang Ding, Fukun Yan, Zhiqiang Shan, Wei Chen, Cuicui Ji

"To remove aluminum ion from chlorinated rare earth solution, this paper used hydrolysis method to explore the hydrolysis behavior of aluminum ion in aluminum chloride solution and confirm the optimum conditions of aluminum ion hydrolysis, which are pH value, temperature and initial concentration of Al203 and so on. The experimental results show that single treatment can make aluminum precipitation rates of chlorinated rare earth solution reach about 90% by hydrolysis precipitation; and then several recycle disposal can get precipitation rates of 89% for aluminum and 2.86% for rare earth.IntroductionIn China, rare earth resources are very rich and unique minerals, complete variety, and rare earth products are very large in the domestic reserves. Rare-earth and application products have been deep into all areas of our life, permanent magnet material of rare earth is one of the most popular application areas[11. Binary oxides such as praseodymium neodymium have been widely applied in the fields of glass, ceramics, magnetic materials, catalysts and so on. Especially, the advent of the Pr-Nd-Fe-B magnets which makes the world magnetic material into a new stage of development [2•3]With the development of science and technology, for industrial, physical and chemical indicators of raw materials Pr-Nd oxides (such as particle size, specific surface area and non rare earth impurities etc.) are also getting higher and higher. The oxide size has an important influence on sludge formation in the electrolytic process. If the size is too large, added oxides have settled on the bottom of slot before melting, and then generated sludge; if the particle is too small, it can cause dust dispersion, enlarge oxide unit consumption and increase the cost of production in the charging process. Some early processes use oxalic acid to make chloride neodymium praseodymium settle, and impurity can be removed cleanly, but the cost is high, it is not suitable for production. At present, most enterprises are using ammonium hydrogen carbonate to precipitate chlorinated neodymium praseodymium, but chlorinated neodymium praseodymium such as iron and aluminum and so on can easily form gel in the precipitation process, seriously affect the growth of neodymium praseodymium carbonate crystal and often leads to particle meticulous, even may also generate gel-like neodymium praseodymium sediments and cause centrifugal or suction filtration difficult. Now the actions and their removal of impurity such as iron and aluminum have done a lot of research in the production process of rare earth, removing aluminum craft with alkaline (sodium hydroxide) and acid (oxalic acid) has good effect, but the cost is higher[41; used adding complex agent to remove aluminum method which is simple and easy to operate, but aluminum removal rate is not high, and also changed the sediment of crystal type[51, and etc. This paper discusses the removal of chlorine from rare earth solution on the basis of the hydrolysis property differences betweenAJ3+ and rare earth ion."

Jan 1, 2013

By Bradford C. Wesstrom

The extraction of metals from Copper Refinery Slimes may involve many different processes. This paper describes the use of pressure leaching for decopperizing of copper refinery slimes at the El Paso Refinery. Process equipment will be described, along with the process chemistry, unit operations and unit processes associated with the decopperizing process. Copper contained in the raw slimes ranges from 15-35%. After autoclaving less than 1 % copper remains.

Jan 1, 2000

By Wayne Bell, Shivanand A. Borkar, Anish Upadhyaya, Matthew D. Andriese, Jiann-Yang Hwang, Zhiwei Peng

"A refractory ore body located in Michigan’s Upper Peninsula contains high concentrations of nickel and copper chiefly occurring in the minerals pyrrhotite, chalcopyrite, and pentlandite. Refractory ore bodies are difficult to treat by conventional mineral processing methods so microwave pre-treatment of the ore is employed to increase metallic-particle/host rock liberation by making use the differential thermal expansion properties of the mineral phases that absorb microwave energy. The Curie temperature measurement of metallic-bearing particles is in agreement with the known value for pyrrhotite occurring at 325°C. A nickel-rich iron sulfide mineral is found to be in occurrence and also appears to be magnetic under BSE imaging. It is shown the ore particles heat rapidly when exposed to microwave radiation for short durations of time mainly due to the high concentration of ferromagnetic mineral phases. Rapid heating causes thermal expansion of constituent mineral phases that produce cracks within ore particles. SEM imaging shows fracture occurring along grain boundaries and throughout host rock matrix. Ball milling experiments show an increased grindability of the ore resulting in a decrease in work index values.IntroductionCrushing and grinding operations consume 50-70% amount of energy used in mineral processing operations [1]. All these processes involve high energy impact of surfaces to develop compressive stresses that produce cracks to initiate breakage of particles. Microwave pre-treatment of certain types of ore might provide an energy savings to these type grinding processes by taking advantage of the tensional forces produced by selectively heating microwave absorbing type mineral phases. The heating of ore particles produces cracking by thermal expansion of the constituent mineral phases. Conventional heating has been investigated and shown to positively aid in grinding processes but determined energy inefficient to be used commercially."

Jan 1, 2011

By H. Palkowski

Recent trends in the automotive industry lead to increasing interest in advanced high strength steels (AHSS). Those steels often have a high bake hardening potential (BH), giving additional contribution to the strength of structural parts, subjected to the paint baking process. For hot rolled AHSS, namely dual phase and martensitic steels, the effect of process conditions on mechanical properties had been investigated. However, the influence of chemical composition within the range in industrial production has not been investigated sufficiently yet. In the current research, samples with different chemical compositions within the characteristic interval for industrial production are under investigation under different preload conditions and simulating the thermo-mechanical production process. The samples were then subjected to BH process. Tensile tests were performed to study the influence of varying chemical composition on the BH effect. The results of investigations on dual phase steels will be presented in this paper.

Jan 1, 2008

By K. S. Izbakhanov

The Chimkent Lead Plant was constructed in 1934 and since that time has undergone many revisions. In 1975 the slag fuming operation was changed from pulverized coal to natural gas fuel. In 1981 the slag fuming furnace water jacket system was converted to evaporative cooling with high pressure steam production. The impact of these changes and the method of their application are described.

Jan 1, 1990

By Susumu Okabe

Top blow injection has been applied to continuous copper smelting and converting by Mitsubishi Materials Corporation since 1974. In this process, injected feeds are captured by and dispersed in the molten bath immediately and effectively, and the reaction is enhanced by the agitation of the bath. The continuous motion of the molten bath, however, may cause severe damage of furnace lining materials, if the injection is not controlled and the furnace is not designed properly. In order to suppress refractory wear, especially at the bath line, surface wave of the molten bath should be moderated. A cold model study was carried out with water bath in a cylindrical vessel and the physical model was derived which correlates the oscillation of gas jet impingement on the bath surface and the surface wave. It was found that a half of the proper frequency of the gas jet impingement coincides the proper frequency of the surface wave.

Jan 1, 1998

By Musa Karakus

Reflected light microscopic (RLM) examination of dust particles from lead and copper smelters can effectively characterize their mineralogy, texture, and origin. Scanning electron microscopic-energy dispersive spectroscopic (SEM-EDS) analysis provides confirmation of the optical identifications and chemical data on the phases. Studied lead smelter dust samples were from the: I) blast furnace, 2) sinter plant scrubber, 3) sinter plant crusher, 4) dross furnace, and 5) refinery. Phases identified included galena fragments, melted PbS, metallic Pb and Cu, Cu-Ni, Cu-Zn, Zn-Ag, Zn-Cu-Ag, Ni-Cu-Sb, and Ni-Cu-Zn-Ag metal alloys, Ni-sulfide, Cu-sulfide, and Cu-Pb-sulfide dross .phases; slag and sinter particles, coke fragments, unreacted original feed phases: pyrite, chalcopyrite, sphalerite, siegenite, bravoite; and oxidized particles: iss, bornite, chalcocite, covellite, magnetite, hematite, and goethite. Dust from a secondary copper refinery were found by RLM and SEM to consist of tenorite, cuprite, cassiterite, two silicate phases. Magnetite, hematite, Fe-Al-Cr-Mg spinel, periclase, forsterite, and wollastonite were derived from the furnace linings during initial cleaning.

Jan 1, 1992

By Balladares V. Eduardo

Most of the arsenic contained in copper concentrates is removed in the gas phase during the smelting and converting processes and, according to recent environmental regulations, it is required to fix it in a solid stable form. In this regards, ferric arsenate has been reported as thermal and aqueous stable compound. Therefore, various alternatives for treating gas containing arsenic were considered in this work. From data obtained at laboratory scale on fixation of arsenic using iron oxide, a new process to treat copper concentrates containing arsenic was evaluated. The effect of temperature, oxygen potential and the sample porosity on the fixation of arsenic contained in a gaseous stream was studied, and the iron oxide converted into ferric arsenate was up to 10%. The obtained results suggest a new alternative for gas treatment with an interesting and attractive technical development. The arsenic was retained as ferric arsenate with thermal and aqueous stability, and it allows a safe disposal keeping the environmental restrictions. The kinetics parameters are used to scale up laboratory results to higher processing rates.

Jan 1, 2005