Acid mine drainage containing heavy metal ions is a large environmental problem facing the mining and mineral processing industry. The femte coprecipitation is a novel technique for removing heavy metal ions from waste water, recently applied to acid mine drainage. The fenite precipitation is usually performed at high temperature and therefore if applied in conventional manner, it becomes uneconomical to treat large quantities of acid mine drainage. In this paper the ferrite precipitation at ambient temperature-is &died. The possible mechanism of ferrite formation is discussed Experimental results from Noranda Tailing and Berkeley Pit water treated by this process are presented.

Jan 1, 1994

By K. Moriyamo

Operation improvement efforts at Hyuga Smelting Co., Ltd. have focused on calcining capacity in the reduction rotary kilns ("the kilns"), whose limited feed rate capacity had capped production at around 18,000t-NiN since 1995. To improve the kilns' feed rate capacity of 80 wet t/hr, attempts were made to increase the gas flow in the kilns by increasing the capacity of the off-gas fans. However, as the increased gas flow resulted in only limited improvement of the kilns' feed rate, a scoop feeder was installed on each kiln to add coal to the middle of each kiln's interior to gain a higher efficiency of thermal supply and conversion. With these gas flow and coal charge addition operations, the kilns' feed rate capacity increased up to 120 wet t/hr, with burner fuel efficiency increasing by approx. 10% (approx. 5% in total with the additional coal included). As a result, production was raised to a level of 22.000t-Ni/Y Keywords: reduction rotary kiln, scoop feeder, additional coal charge.

Jan 1, 2004

By Sutham Niyomwas

Biomorphic Cellular TiCIC ceramics were produced by vacuum-infiltrating carbon preforms with Ti02 sol and subsequent synthesis by the carbothermal reduction process. The carbon preforms used in the study were obtained by pyrolysis of parawood and neem wood. The effect of infiltration time on the composition and microstructure of the biomorphic TiCIC ceramic was analyzed by X-ray diffractometry and scanning electron microscopy. The biomorphic structure of the TiCIC ceramic is consistent with that of the biotemplate natural parawood and neem wood.

Jan 1, 2008

By M. R. Barkhudarov

Semi-solid metal can be formed into useful products of near net shape and high quality. Use of this method has been limited, however, because of the difficulty of working with metal in the semi-solid state, which has strong shear rate, temperature and time-dependent properties. In this paper we describe a thixotropic model and apply it to the problem of small metal droplets impacting on a flat plate.

Jan 1, 1997

By Robert E. Moore

Synthetic spinel is proving to be a highly effective refractory for specific applications, but its cost limits applications. Formation of spinel from a raw material such as diaspore or bauxite could provide a simple and less costly starting material. In the study reported here, finely ground (-325 mesh) diaspore from Missouri and bauxite from Guyana and China are combined with hard burned MgO (-325 mesh) in appropriate proportions to yield spinel and spinel with secondary phases. A classical sintering and dilatometer study was completed, followed by a microstructure study to determine completeness of the reactions and morphologies of the reaction products.

Jan 1, 1993

By K. R. Barrett

The cupellation of dore/lead bullion to recover precious metals is one of the oldest metallurgical processes known to man. In recent times this has been carried out in small reverberatory furnaces but the process suffers from a number of disadvantages. A new process has been developed at the Northfleet refinery of Britannia Refined Metals Ltd, which gives much improved performance. The process depends upon the injection of oxygen through a nitrogen shrouded lance at the bottom of the furnace. The lance is consumable and of unique design. Reaction rates are high giving short process time; fuel consumption is low; oxygen efficiency is high and dore recirculation is low. The new process has resulted in substantially lower operation costs.

Jan 1, 1989

By Adolfo Pillihuaman Zambrano

Fe-Cr-C production is a very high electrical energy consuming process. Decrease up to 10% of this electrical energy is expected when self-reducing agglomerates are used. This research aims to understand how the synergetic effects are when stronger reductant, like Fe-Si, is substituted for coke in self reducing pellets. Brazilian chromites containing 41.2%Cr2O3 were mixed with petroleum coke and agglomerated with cement as the binder. Small amounts of 1%, 2% and 4% of Fe-75%Si were substituted for the equivalent petroleum coke, and pure silica plus hydrated lime were added for adjusting the slag composition. The mixture was pelletized, dried and submitted at 1773K up to complete the reactions. The results showed that the reduction reactions were 1.4 and 2 times faster with 1% and 2%Fe-Si addition, respectively, than with no addition. The microscopic analysis showed that it was formed a liquid phase, but the pellet did not collapse what indicates that the coalescence of the metallic phase depends on the dissolution of the pre-reduced particles of the chromites into slag.

Jan 1, 2008

By Gabriel Riveros, Ariel Balocchi, Andrzej Warczok, Daniel Smith

Blister copper from converting of copper matte is processed by fire refining prior to electrorefining. The fire refining consists of two steps: copper oxidation with impurities slagging and copper reduction. The classical batch process is carried out in vascular or reverberatory furnaces called anode furnaces. A new process for continuous copper fire refining has been proposed. The copper flows through two reactors in cascade, where is oxidized and reduced. The flow of a liquid copper through a ceramic packed bed increases the surface area and the rate of oxidation as well as the rate of reduction in the packed bed of charcoal. Mathematical modelling allowed for the design of a laboratory scale demonstration installation and industrial-pilot installation in Hernan Videla Lira Smelter (Paipote). The results have demonstrated the process feasibility and flexibility in operation.

Jan 1, 2009

By A. A. Trickett

In the treatment of gases from pyrometallurgical processes prior to acid manufacture, volatile components, sulphur trioxide and particulates ,are removed in wet gas cleantng systems. In the process a weak acid stream is generated, typically less than 10% H2S04, contaminated with volatiles such as arsenic, fluoride and chloride', plus metallic particulates. This effluent stream has, in the past, been disposed of in a variety of different ways. As a result of changing environmental legislation, smelters are having to review alternative solutions for treating this effluent stream. This paper' will describe a process developed by Chemetics which treats this effluent stream, generating a small dry metal sulphate stream plus a clean acid stream which is suitable for recycling to the smelter acid plant.

Jan 1, 1992

By Ruirui Wei, Yanhui Liu, Fangqing Yin, Meilong Hu

In China, Basic Oxygen Furnace (BOF) slag is traditionally used as an aggregate for civil engineering, for road engineering and fertilizer. In order to make full use of BOF slag, the experiments of BOF slag with high temperature roasting has been carried out and the phase transformation is studied. The BOF slag from Chongqing Iron & Steel is roasted in the electric muffle furnace at three different temperature. The influences of the high temperature roasting on change the phase composition of BOF slag was characterized by XRD. The results revealed that SFCA was produced at the high temperature in air atmosphere and melting temperature of slag was lowered. Therefore, if the BOF slag which treated by roasting was utilized in the sintering process, it is advantageous to improve the sintering strength and the formation of the liquid phase and reduce fuel consumption in the sintering production process.

Jan 1, 2015

By Xuemei Zheng, Aiyuan Ma, Yonggang Zuo, Jinhui Peng, Shiwei Li, Libo Zhang

The effect of moisture content on the dielectric properties and microwave drying behavior of zirconium hydroxide was studied by using an open-ended sensor dielectric measurement system at the frequency of 2.45 GHz. The experimental results showed that moisture content can significantly influence the variation of dielectric properties. Dielectric constant, loss factor and loss tangent all increase with the increasing moisture content. Compared with the conventional drying method, the microwave-assisted drying method resulted in a substantial decrease (81.8%) in the drying time, and the drying effect was better at the lower power level of 600 W. This study offers the useful information on dielectric properties of zirconium hydroxide, which can be used for developing microwave drying applications in mineral processing and designing better microwave sensors for measuring zirconium hydroxide moisture content.

Jan 1, 2015

By Shengli Wu, Wei Huang, Xinliang Liu, Kaifa Zhang

The slagging behavior, the phase of primary blast furnace slag and its transformation law of structure for the single furnace burden were studied in this paper. The results showed that the formation of primary slag was controlled by CaO/SiO2, Al2O3 content, MgO content, reducibility, iron content and porosity of the furnace burden. Fayalite (2FeO•SiO2) was easily formed from acid ferrous furnace burden while kirschsteinite (2(Fe,Ca)O•SiO2) was produced from alkaline ferrous furnace burden

Jan 1, 2015

By Yuzuru Sato

Viscosity has been measured for various molten binary alloys of nickel with iron, cobalt and chromium in order to clarify the behavior of viscous flow of molten nickel alloys. The entire concentration range for iron and cobalt and 0-67at% of chromium content were studied. The measurement method was an oscillating cup viscometry using an alumina crucible that was precisely machined. The temperature was up to about 1880K for all the measurements. The results represented good Arrhenian relationship although some measurements included overcooled temperatures. The isothermal viscosities increased monotonously with an addition of iron and chromium into nickel. The addition of cobalt increased after stationariness. The isothermal viscosities showed concave curves. Activation energies increased monotonously by adding all the elements into nickel. These phenomena were considered to be related to the thermodynamic properties such as the heat of mixing and the structures of mixture melts.

Jan 1, 2003

By C. M. F. Vieira

Crushed fired brick waste, known as grog, screened at two different particle size, 840 (20 mesh) and 180 µm (80 mesh), was used in mixtures with clayey body to make typical red ceramics for bricks. The effect of the grog addition up to 20 wt.% on the properties of bricks fired at 700oC was evaluated. The results indicated that both the particle size and the amount of grog addition changed the fired properties of the clayey body. Additions above 5 wt.% of grog, with a coarser particle size, decreased the mechanical strength of both the dry body and the fired ceramic pieces. By contrast, grog with a finer particle size may be used up to 10% wt. without deteriorate the properties and corresponding microstructure of the clayey body.

Jan 1, 2009

By Ze-Qiang Xie, Bai-hui Wang, Feng Chen, Ling-zhi Yang, Yu-feng Guo

In this paper, based on the big data in steelmaking process, equation about the relationship between steel composition (especially the oxygen content) and the element yield is established by using mathematical analysis method to analyze the factors influencing yield. Meanwhile, combining the alloy yield data-base that were established based on self-learning of historical data and computer technology in steelmaking process, a method of yield prediction of alloy elements is studied. To provide support for this method, alloying elements yield prediction software is developed to realize the rapid and intuitive site operation guidance, and to realize the precise control of dosage of alloy material.

Mar 1, 2017

By Tarek M. Hatem, Salah M. Bedair, Khaled H. Khafagy

Our understanding for intrinsic stresses and defects evolution in photovoltaic devices has became an essential part of new developments. In particular, Multi-Junction Photovoltaic (MJ-PV) modules depend on multi-layer structures that may suffer high dislocation-densities as a result of high lattice and thermal expansion coefficient mismatch. These defects limit the performance, reliability, and lifetime of PV devices. In the current study, a three-dimensional multiple-slip crystal-plasticity model and specialized finite-element formulations are used to investigate InGaN growth on Si substrates. The formulation is based on accounting for thermal and intrinsic stresses as a result of different processing conditions and microstructures. Furthermore, the formulation was used to investigate a recently developed technique, Embedded Void Approach (EVA), which can be used to address both the high density of defects and the cracking/bowing of InGaN growth on Si. The current work lays the groundwork for more extensive use of silicon in MJ-PV devices.

Mar 1, 2018

By Patricia Negrini Siqueira Poveda, Leonardo G. A. Silva

Thermoplastic materials are sensitive to ultraviolet radiation (UV), which can cause structural changes, causing variation in mechanical properties and appearance. UV range between 250 and 400 nm is considered the most aggressive to polymers, and prolonged exposure to it results in breakage and/or crosslinking chains. Light stabilizer additives, blockers or absorbers are added to the polymers for protection in order to extend the life of the final product. The choice of the adequate light stabilizer additive system depends on factors such as resin final application, thickness, geographic location of exposure, presence of fillers in the composition, contact with chemicals, among others. This study evaluates different additive systems: conventional organic, inorganic nanotechnologyc base and the synergy between them when applied to polyethylene considering carbonyl index and UV/VIS results after aging by QUV chamber.

Mar 1, 2017

By Yijun Cao, Shengpeng Su, Guihong Han, Xiangyu Song, Yanfang Huang

Binder is indispensable in the production of iron ore pellets and the quality of pellets seems to be related to the interactions between binders and iron minerals. Humic acid is proved a suitable binder for iron ore pelletizing. In this paper, the interactions between humic acid and iron minerals were investigated by adsorption experiments and molecular dynamic simulations. Adsorption experi- mentalresultsshowthattheadsorptionofhumicacidonhematiteiseasierthanthat on magnetite, and the maximum adsorption capacities of humic acid on hematite and magnetite reach 17.1, 7.39 mg/g, respectively. The results of adsorption iso- therms indicate that the Langmuir model provides the best correlation of the experimental data, while the thermodynamics results demonstrate that the adsorp- tion process is a spontaneous exothermic process. Molecular dynamic simulations reveal that the interaction between hematite and humic acid is stronger than that between humic acid and magnetite. (cid:1) (cid:1) (cid:1)

Mar 1, 2018

By Sudha Goel, Manis Kumar Jha, Deblina Dutta, Rekha Panda

Based on the placement of lead and its consumption in industry bran- ches, the paper deals with the composition of lead in the massive of Kopaonik. Removal, tenuity and grinding of galenit. The paper in particular treats the flotation process, and also treats physico-chemical bases of reagents in the process, as well as decanting, drying, filtering and storage of concentrates. Veri fication of the chemical composition of Pb concentrates with Pb, Zn, Bi, As, Sb, In, Au, Ag, etc. It is special that in Kopaonik massive the ratio of Pb: Zn composition is 1.4:1.0 and during the flotation lead is inclined to go with pirotines concentrate more than is allowed. We are strongly focused to maximally decrease the Pb amount that goes with pirotine concentrates and wastes. The paper as such gave the first effects in optimizing of these parameters with positive effects in flotation process in Trepca.

Mar 1, 2018

By P. K. Jimack, C. E. Goodyer, A. M. Mullis, P. C. Bollada

"We review the application of advanced numerical techniques such as adaptive mesh refmement, implicit time-stepping, multigrid solvers and massively parallel implementations as a route to obtaining solutions to the 3-dimensional phase-field problem with a domain size and interface resolution previously possible only in 2-dimensions. Using such techniques it is shown that such models are tractable even as the interface width approaches the solute capillary length.IntroductionMulti-scale modelling impinges upon many areas of science, engineering and technology where the interplay between processes occurring on disparate length and/or timescales can affect the properties of systems in a complex, and sometimes unforeseen, manner. One such is the processing of materials where interactions at the atomic scale, through the nano- and microstructural scale can have a profound affect on the macro-scale response of engineering components. Here we focus on one such problem, the crystallisation of alloy melts, to illustrate how a range of advanced numerical techniques make the modelling of such systems tractable.The modelling of solidification structures, in particular the growth of dendritic crystals, is a subject of intense and enduring interest within the scientific community, both because dendrites are a prime example of spontaneous pattern formation and they have a pervasive influence on the engineering properties of metals. For alloy systems, which form the vast majority of engineering materials, solidification involves the rejection of both solute and latent heat from the growing solid, forming a coupled diffusion problem in which both the chemical and thermal diffusion equations should be solved. The multi-scale nature of this problem arises from the disparity between the thermal and solutal diffusivities for most liquid metals, which are typically 10-5 m2 s-1 and 10-9 m2 s-1 respectively. The ratio of these two, referred to as the Lewis number (Le =Dia), is therefore typically of the order 10,000 and gives a measure of the multi-scale nature of the problem. In fact, in many cases the thermal diffusivity is so much larger than its solutal counterpart that thermal diffusion is considered instantaneous, wherein the system can be approximated as isothermal such that the multi-scale calculation does not need to be performed. This is certainly a reasonable approach in most conventional castings. However, there is a class of solidification problem in which this approach is far from satisfactory, namely Rapid Solidification (RS). The application of isothermal phase-field models in such situations are highly likely to produce spurious results or to fail totally, particularly for temperatures below To (the temperature at which the free energies of the solid and liquid phases are equal at the concentration of the bulk alloy), wherein partitionless solidification may occur."

Jan 1, 2013