Search Documents

By Fernando Castro

Electric furnace steelmaking dust is a polluting residue that needs to be treated in order to recover metals contained and to produce an environmentally acceptable residue. Some hydrometallurgical approaches for its treatment have been evaluated, namely: caustic soda leaching followed by electrolytic recovery of zinc, ammonia leaching followed by zinc compounds precipitation and acetic acid leaching followed by lead, zinc hydroxide and gypsum precipitation.

Jan 1, 1992

By Jürgen Antrekowitsch

Typical zinc oxides recovered from wastes like steel mill dusts and neutral leaching residues are of a low quality because of impurities like fluorine, chlorine, lead and others. Therefore, they are not comparable to technical grade zinc oxides produced in “French” or “American Process”. Some new developments, most of them still in pilot scale, try to establish processes where higher qualities of the product should be achieved. Zinc oxides are not only supposed to be an input material for electrolytic zinc production. Far more, they should find their way into the zinc oxide market as a substitute for technical grade zinc oxides. Furthermore, a new field of application for these oxides has been investigated at the department of Nonferrous Metallurgy, University of Leoben. Because of a higher acceptance concerning different impurities in relation to zinc winning electrolyses, a use in electrolytic galvanizing shows an interesting option. Therefore, synthetic zinc oxides with different impurities were generated to study the effect of these impurities especially on the quality of the zinc layer. Typical steel sheets, as used for car bodies, were electrolytically galvanized and the resulting layer was analysed, as main impurities compounds of fluorine, chlorine, iron, lead and calcium were used for the investigations. Beside the layer quality, the current efficiency and the possible galvanizing speed were examined. The results give an indication, weather such an alternative application can be feasible from a technical and economical point of view or not. 597

Jan 1, 2008

By V. Bojarevics, K. Pericleous

"A number of different methods have been developed for noncontact electromagnetic treatment of liquid metal and to investigate the melting/solidification processes. Applying AC magnetic field in terrestrial conditions, along with the buoyancy and thermo-capillary forces, results in turbulent flow. The use of a homogenous DC magnetic field allows damping both of the turbulence and the large scale flow at different rates leading to surprising results at some stages. The dynamic interaction of the turbulent flow with the oscillating interface needs to be accounted if it is required to levitate liquid metal of up to few kilograms without the contact to container walls. At the high values of magnetic field some oscillation modes are damped quickly, while others are modified with a considerable shift of the oscillating droplet frequencies and the damping constants from the non-magnetic case. Numerical models are used to investigate behavior of liquid metal suspended in high DC magnetic fields providing microgravity-like conditions with laminar viscosity and heat transfer to the surroundings.IntroductionSince the early Electro Magnetic (EM) levitation experiments [1] in AC magnetic field it became apparent that the levitated liquid metal is prone to oscillation and instability. The EM and electrostatic levitation experiments with liquid metal droplets show difficulties related to confinement stability and a need for complex correction functions to establish a correlation between the measurements and the droplet material properties [2,3]. Intense internal fluid flow is visually observed, apparently being in the turbulent regime for earthbound conditions."

Jan 1, 2012

By Wei Yin, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Copper anode slime is an increasingly significant resource for precious metals such as Au, Ag and Pd. The extraction of Au, Ag and Pd from decopperized anode slime by different pretreatments and different lixiviants including cyanide, chloride, thiourea and thiosulfate have been investigated. When oxidizing roasting pretreatment was carried out under the conditions of roasting time 120min and temperature 625 ℃, the removal ratios of S and Sb could reach 82.18% and 98.52%, respectively. And the following alkaline leaching of calcine could result in the dissolution of 46.40% Cu and 98.48% Pb. The optima leaching ratios of Au, Ag and Pd reached 99.48%, 97.69%, 94.79% by cyanide leaching, and 95.01%, 79.84%, 96.59% by chloride leaching, and about 95.21%, 95.66%, 48.79% by thiourea/thiosulfate leaching.

Jan 1, 2015

By Lars O. Werme

Already the KBS Project proposed copper as a suitable material for encapsulation of spent nuclear fuel. The basis for this choice was the thermodynamic stability of copper in water and the fact that deep granitic groundwaters in Sweden are oxygen free. With a limited supply of oxidants, a copper canister would have the potential for a very long service life. The research and development work aiming at encapsulating nuclear fuel entered a new phase in 1993, when SKB launched its Encapsulation Plant Project. Within this project, SKB has: ? designed a facility for encapsulation of nuclear fuel, ? laid down the design premises for a canister for disposal of nuclear fuel, ? tested and developed fabrication methods for copper canisters, ? evaluated the long term chemical and mechanical behavior of the canister, ? made preliminary plans for a factory for the production of copper canister, ? constructed a canister laboratory for full scale testing of the key operations in an encapsulation plant. The conclusions of this project were that a canister consisting of an outer layer (50 mm) of copper over an insert of cast nodular iron would provide sufficient corrosion protection and would have sufficient mechanical strength. This canister can be produced by several methods of which forming from rolled plates, hot extrusion, and "pierce and draw" have been tested at full scale. The canister will be sealed by electron beam welding in the encapsulation plant, and the integrity of the weld will be verified by ultrasonic testing and' high-energy radiography. The final development work in this area will be performed in the canister laboratory.

Jan 1, 1999

By O. E. Omotoso

This study is part of an ongoing investigation to understand the mechanism of stabilization/solidification of hazardous chromium wastes in ordinary Portland cement (OPC). Tricalcium silicate (C3S*),a major component of OPC is mixed with reagent grade Cr(lll) and Cr(VI) solutions, to simulate complex cementiCr waste systems. Scanning electron microscopy (SEM) and energy disperse spectrometry (EDS) were employed to provide microstructural and chemical information. Transmission electron microscopy (TEMlEDS), apart from complimenting the SEM, was used to probe the distribution of Cr in the hydration products of C3S and to provide crystallographic information. 29Si MAS NMR (magic angle spinning - nuclear magnetic resonance) Was used to characterize the influence of Cr on the hydrated silicate structure.

Jan 1, 1995

By Munyaradzi Kwatara, Ron Schonewille, Edgar Peek, Juzer Tayabally

"The potential recovery of nickel from a South-American saprolitic laterite ore using the segregation roasting technique was investigated. The ore was heated to temperatures that ranged between 900 and 1 000°C in a rotary kiln. In all the tests, the laterite ore was first mixed with a predetermined amount of calcium chloride and either coal or coke. By varying the temperature, calcium chloride and reductant in the different tests, a preliminary set of optimal conditions was established for the specific laterite ore that was tested. A combination of chemical analysis and electron-probe-micro-analysis (EPMA) were used to determine and evaluate the effectiveness of segregation roasting on the recovery of nickel. The present paper describes the test procedure and the results that were obtained.IntroductionIt is known that laterite ore resources account for an estimated 72% of the world's nickel resources, with sulfide sources accounting for the remaining 28%. Yet sulfide resources account for 58% of the world's primary nickel production while laterite resources account for the remaining 42% [I]. There are numerous reasons for this discrepancy, but the most important one is the mineralogical and compositional complexity that is associated with laterite ore deposits. For example, this complexity currently offers only limited opportunities for upgrading, thereby creating capital intensive whole ore processing facilities. It then follows logically that the identification and application of a low-cost processing option for the treatment of laterites could potentially open up an opportunity for exploiting these vast untapped laterite resources.To this end, a preliminary screening investigation was initiated by Xstrata Process Support to evaluate the potential application of the so-called (nickel) segregation process as a unit operation that could potentially be integrated into a laterite processing flow sheet. Laboratory bench tests were performed on this segregation process and this paper details some of the findings from this preliminary investigation."

Jan 1, 2011

By Fuqiang Zheng, Shuai Wang, Ting Duan, Yufeng Guo, Tao Jiang, Andrew Yakovlevich Travyanov

Organic compound binder can effectively enhance the strength of green pellet and reduce the addition amount of binder during pelletizing. However, compared with traditional bentonite binder pellet, the compressive strength of the preheated and roasted pellets significantly declined. It is of significance to resolve this problem for the application of organic compound binder. In this paper, magnetite concentrate was used as raw material, carboxymethyl cellulose (CMC)- bentonite compound was used as binder, characteristics of preheated and roasted pellets and the effects of additives on that were systematically studied, The results show that sodium acetate can effectively improve the characteristics of the finished compound binder pellets. The compressive strength of the preheated and roasted pellets were increased by 52/N·p-1 and 342/N·p-1 respectively when the addition amount of sodium acetate is 2.2%wt of compound binder. Moreover, sodium acetate has no adverse effect on pelletizing process and drying characteristics of green balls.

Jan 1, 2015

Silver has the highest electrical conductivity of all metals and consequently this property is an attractive feature which makes it a leading candidate for use in electronic devices. The research conducted was focused primarily on the development of a process for obtaining a deposited silver-coating onto alumina, for applications related to electrical-conducting devices and, ancillarily, catalysts. Alumina balls and plane substrates were utilized for the investigation. The coating process employed an aqueous arnmoniacal silver-nitrate electrolytes with a formaldehyde solution as the reductant. Modifying additives - an activator which would be expected to promote good deposition-characteristics onto the (dielectric) substrate and an inhibitor which would obviate homogeneous reduction (precipitation) of silver was observed when the activator-containing silver-electrolyte reductant constituents were combined. However, the silver-electrolyte/reductant system with inhibitor could be employed (at 80°C) to achieve a viable (subject to future research optimization) coating on alumina. The influence of the processing temperature on the deposition process was delineated during the course of the research. The morphology of the deposited-silver on the alumina balls was assessed by SEM imaging. A tape-peel test was employed, with the plane substrates, to semi-quantitatively characterize the adhesion to the alumina.

Jan 1, 1998

By Kazuya Kitatani, Gen Sasaki, Naoto Ohta, Hideharu Fukunaga, Makoto Yoshida, Jin Pan, Kenya Nagahisa, Toshihiro Ishikawa

"A sintered SiC (Tyranno-SA) fiber-reinforced MAS glass matrix composite was fabricated by using a slurry infiltration method and hot-pressing. The microstructure and mechanical properties were investigated: To prepare the preform, the MAS glass slurry including a dispersing agent was infiltrated into a bundle of the fibers. The preform was then hot-pressed under the conditions of 1473 K, 30 MPa, 3.6 ksec. A unidirectionally-reinforced oxide matrix composite with 50% Vf. of the fiber and a density of 2.84 g/cm3 was obtained. As the mechanical properties at room temperature, the three-point flexural strength- and quasi-static adsorbed energy were 500 MPa arid 6,000 J/m2, respectively. Without graphite or an h-BN pre-coating on the surface of the fiber, pull-out and bridging of the fibers from the matrix was found, and this leads to a high value of the adsorbed energy. By TEM observation, nano-scale crystalline products were found between the fibers and the glass matrix. The push-out test reveals that this layer causes the appropriate debonding of the interface during the fracture process of the composite.Introduction It is known that the CFCCs (continuous-fiber-reinforced ceramic matrix composites) are characterized by their non-linear fracture behavior, which is' hardly found in monolithic ceramic materials. It is inevitable for the CFCCs to exhibit a large fracture toughness so 'that debonding of the fiber/matrix interface; pull-out and bridging of the fibers then' occurs during the fracture process. This series of fracture behavior is known as the so-called ""the mechanism of toughening of the CFCCs"". Thus, different from the MMCs in which strong interfacial bonding is necessary, the interfacial strength of the CFCCs has to be controlled. As techniques for controlling the interfacial strength, it is also known that both a CVD-graphite coating and an h-BN coating are effective to induce the mechanism of toughening[1,2]. In the case, of the Si-C-O or Si-Ti-C-O fibers/glass or crystalline oxide matrix composites, it is reported that the formation of the in-situ graphite layer, which is also effective to increase the fracture toughness of the CFCCs, is often found during the fabrication process such as hot-pressing. The lower the crystallinity of the Si-C-O fibers, the higher is the tendency to form the in-situ graphite layer as found by the chemical reaction between the fibers and the glass matrices[3-12]. On the-other hand crystallized stoichiometric 'SiC fibers are attractive for high temperature service because of the higher phase stability compared to the Si¬C-O or Si-Ti-C-O fibers. However, in the previous, studies, the mechanical properties and the interfacial chemical reaction of the crystallized SiC fibers / glass matrix Composites have still been unknown. In this study, a polycrystalline 'sintered SiC fiber-reinforced MAS glass composite was fabricated. The mechanical properties and microstructure were then investigated. The slurry infiltration technique followed by hot-pressing was used to prepare the composites. The formation of the in-situ graphite layer and the relationship between microstructure and mechanical properties at room temperature were examined by the TEM observation of the fiber/matrix interface."

Jan 1, 2000

By Christian Trassy, Pierre Proulx

"Inductive plasmas are now commonly used in material processing: spraying, powder synthesis, densification or spheroidization. An inductive discharge presents, in the coil region, recirculation eddies due to the Lorentz forces, resulting in an axial backflow. If the central jet is strong enough to ""pierce"" the recirculation this axial backflow disappears on the centerline, but the external layer of the injection flow is skimmed by the remaining eddy, and particulates are rejected to the discharge periphery. To avoid this disadvantage, it is common to introduce the injection pipe inside the discharge, so that its outlet is positioned after the recirculation eddy. The powders remain confined in the axial zone, to the expense of shortened residence time.In order to increase the efficiency of the particle trajectories, a double flow injector has been designed. It enables the particles to travel closer to the axis, while the outer schrouding gas is skimmed and passes through the electromagnetic eddies. This injector is made up of two concentric tubes. The powders are injected with the carrier gas in the inner tube. A schrouding gas is injected in the annular space between the inner and the outer tubes. The powder is confined to the vicinity of the axis, resulting in a more homogeneous thermal treatment.Tungsten powders have been spheroidized with and without this device. Using the double flow injection, the spheroidization yield has been increased from 70 % up to 95 %.The design of such an injection device has. been studied and improved using numerical modelling. Another useful tool, a visualisation technique described elsewhere, has been used for the experimental study, that drastically simplifies the comparison between experimental and theoretical results: injecting yttrium oxide into the discharge results in a colorful display of the 4000 K isothenn: the ""cold"" zone, below 4000, appearing as red, and the ""hot"" zone as blue. Furthermore, it is of great industrial interest since it is a very cheap and efficient way to obtain a picture of an important isotherm."

Jan 1, 1999

By Shadia J. Ikhmayies

SnO2:F/CdS:In bilayers were produced by the spray pyrolysis technique on glass substrates. The structures were characterized by recording and investigating their transmittance curves, I-V plots, X-ray difractograms (XRD) and by observing their scanning electron microscope (SEM) images. From the I-V plots it was found that the SnO2:F forms an ohmic or quasi-ohmic contact with CdS:In. XRD patterns show the polycrystalline nature of the films and show that there is a small shift in the position of the (200) line of SnO2:F without the appearance of new peaks. The morphology of the structures are compared with those of SnO2:F alone and CdS:In alone on glass substrates.

Jan 1, 2009

By Kinya Atsumi, Kanjana Khunathai, Hisaya Kato, Hidetka Kawakita, Keisuke Ohto, Katsutoshi Inoue

"Crosslinked microalgae were prepared from the residue generated in the production of biofuel, by crosslinking-condensation in concentrated sulfuric acid. These microalgae were tested for adsorption of various metal ions in hydrochloric acid medium. The crosslinked microalgae exhibited high selectivity for Au(III) over other precious and base metal ions. From an isotherm experiment, the maximum adsorption capacity was evaluated to be 3.25 mol/kg of dry gel for Au(III) which was many times higher than that of the original microalgae residue. SEM and X-ray diffraction confirmed the formation of metallic gold particles, suggesting the occurrence of a redox reaction between surface functional groups on the gel surface and trivalent gold ion.IntroductionSubstantial quantities of precious metals are being used by the electronic industry because of their excellent electrical conductivity and resistance to corrosion. In recent years, recovery of precious metals from secondary sources such as electronic scrap [1,2 ], and leach liquors is being favored because of environmental concerns. Of course, recovery is only practical, if its cost is lower than the value of the metals (gold, platinum and palladium) recovered.Traditional methods of separation and refining do not fulfill this requirement. In order to overcome this problem, attempts have been made in recent years to develop new processes including total leaching in hydrochloric acid containing chlorine gas or hypochlorite, followed by solvent extraction and ion exchange [3]. In the new processes, new solvent extraction reagents or ion exchange resins with high selectivity and high loading capacity are used to simplify the process and to reduce the operating costs."

Jan 1, 2011

By H. Walqui

Southern Peru Copper Corporation (SPCC) are currently modernizing the Ilo copper smelter. A single ISASMELT furnace will start smelting 1,200,000 tonnes per year of concentrate during the second half of 2006. The existing Peirce Smith converters are being upgraded for converting the matte to blister copper and a new acid plant and oxygen plant are being installed. Two new anode furnaces and a twin anode casting wheel have been installed in 2005 and commissioned in January 2006. The modernization project will ensure the smelter satisfies new environmental regulations due to come into force in January 2007. This paper summarises the background to the modernization project, describes the main design features of the new copper smelter and summarises progress on the smelter construction as of early 2006. This paper describes the genesis of the Ilo Smelter Modernization Project and describes in details the scope and current status of the project.

Jan 1, 2006

By Chikabumi Yamauchi, Mitsuru Tanahashi, Tsuyoshi Taniguchi, Nobuo Furuta, Toshiharu Fujisawa

"It is essential to clarify the equilibrium relations among nonmetallic inclusions of the Mn0-SiO2-CrOx system and molten stainless steel in order to control non-metallic inclusions formed by the deoxidation of stainless steel with silicon. In the present study, the phase equilibria of the MnO-SiO2-CrOx system were measured by conducting the following experiments under controlled oxygen partial pressure, Po2, at 1873 K:1) Phase equilibria of the MnO-Cr20 3 binary system were measured for Po2 = 2 x 10-6 ~2 x 102 Pa.2) Phase equilibria of the MnO-SiO2-CrOx ternary system were measured for Po2 = 2 X 10-6 Pa.Based on the results, the phase diagram of this ternary system was established under the condition of the Si-deoxidation process of stainless steel (Po2 = 2 x 10-6 Pa and T = 1873 K).IntroductionAt the deoxidation stage in steelmaking process, generally multiple deoxidizers participate in deoxidation reactions, and the composition of deoxidation products ""non-metallic inclusions"" greatly varies depending on deoxidizing efoments and their contents. In order to control non-metallic inclusions formed by the refining process of steel, it is essential to clarify the equilibrium relations among non-metallic inclusions and molten steel.Especially, during the refining process of stainless steel, nonmetallic inclusions in molten steel seem to- change as follows. After the oxidation refining, Mn-chromite is formed in molten steel as non-metallic inclusion. By the deoxidation with silicon addition (mainly less than 1 mass%), Mn-chromite inclusions are changed their compositions to Mn-silicate. Segawa et al.[l] have reported the effect of amount of silicon addition on composition and mass ratio· of non-metallic inclusions during the Sideoxidation process of 18Cr-8Ni stainless steel at 1873 K, as shown in Figuri; L At higher silicon content than 0.5 mass%, only Mn-silicate was identified as non-metallic inclusion. On the other hand, at lower silicon content, both of Mn-chromite (MnO Cr2O 3) and Mn-silicate were identified. However, the thermodynamic and the kinetic analyses of the above-mentioned Sicdeoxidation process have not been made due to lack in the thermodynamic data for the non-metallic inclusions· of the MnO-SiO2-CrOx system, such as the phase diagrams, the activities of the components, and the free energy of intermediate compounds. In relation to the phase diagram of this system, those of the MnO-SiO2 [2] and the SiO2-Cr2O 3 [3] binary systems have been only reported"

Jan 1, 2000

Lance based copper-nickel matte converters have become an established technology in the field of base metal sulphide smelting and converting. An Ausmmelt® converter is currently being constructed at Anglo Platinum in South Africa to convert a nickel-copper rich matte containing platinum group metals (PGM's). The accurate prediction of the matte chemistry is required to control the composition at the endpoint which influences segregation of PGM's during the subsequent slow cooling and magnetic separation processes. A hybrid modelling approach is introduced in this paper that incorporates both the effect of thermochemistry and system dynamics. It will be shown how the model relates to fundamental conservation laws, while still providing enough flexibility to adapt to changing operating conditions. It will also show how off-line modelling can be incorporated into a robust on-line model. Based on the data from many pilot plant trials, the model prediction performance is shown to be within the accuracy requirement set by industry and therefore constitutes a reliable basis for model based control. The final generic model structure takes on the form of an thermodynamically integrated ARMAX hybrid model. The final model has the advantages of being dynamic, adaptive, robust and it can be related to thermochemical fundamentals.

Jan 1, 2002

By Youngkook Lee

The precipitation kinetics of NbC in ferrite matrix of the Nb microalloyed steel was investigated experimentally and numerically. The mole fractions of NbC precipitates formed at different isothermal temperatures were measured as a function of holding time by electrical resistivity test and were compared with both a mathematical model based on time-dependent nucleation and growth rates and the hardness. There is a good match among the calculated and measured precipitation kinetics of NbC and the hardness. The isothermal precipitation-temperature-time diagram of NbC in ferrite matrix of the Nb microalloyed steel was newly generated. Keywords: Precipitation, Carbide, Ferrite, Nucleation, Growth, etc

Jan 1, 2003

By G.A Subagyo

The condition of slag in a pyrometallurgical reactor is vital to ensuring control of the process. A new technique based on multivariate image analysis (MIA) of digital images has been developed to provide an online measurement of important slag characteristics, such as the presence of exposed metal, the presence of solid phases, and temperature. This paper shall describe the technique and provide some results from analysis using industrial plant data.

Jan 1, 2003

By S. S. B Wang

Zirconia-based ceramic materials have potential applications in high temperature furnace insulation, hot extrusion and casting dies, pressure nozzles, cutting tools, engine parts and electronic materials. High purity and superfine powders of zirconium oxide (baddelyte) were synthesized from a solution containing zirconium oxychloride and urea under hydrothermal conditions. crystallization of the metastable tetragonal zirconia using magnesium oxide or yttrium oxide as stabilizing agents was successfully achieved. The mechanism of hydrothermal reaction to produce these powders are discussed.

Jan 1, 1989

By David S. Dolan

To beat capital costs of US$10 per pound of installed capacity has appeared as a major hurdle for the "third generation laterite nickel plants. Forecast costs are escalating. Where can savings come from? Ore beneficiation can reduce the tonnage rate to be processed. High pressure acid leach options include the use of indirect slurry heating and higher operating temperatures to reduce flow rates and residence time. Progress has been reported in atmospheric leaching. High counter current decantation circuit settling rates and high underflow densities reduce CCD costs. Metal recovery options include direct from leach solution to metal production, as used by Bulong and espoused by Goro, and indirect recovery as used by Moa Bay, Murrin Murrin and Cawse. Plant location impacts on the costs of tailings disposal, power and energy costs, supply of consumables and labour costs, among others. Final nickel and cobalt metal production routes are electrowinning, hydrogen reduction or some innovative routes being proposed for Goro. This paper reviews the status in these developments, with particular reference to equipment and processes that offer lower capital costs. Keywords: Laterite, Nickel, Plant, Capital Cost

Jan 1, 2004