Search Documents

By Oliver C. Ralston, Foster Fraas

INTRODUCTION ELECTROSTATIC methods of separation are used only when some peculiar advantage is gained. Such cases are minerals that are not separable by differences in specific gravity or magnetic response and that are desired in particles as large as 10-mesh, a size on which flotation separation is inefficient. This paper covers several separations of this type and others. It includes studies in the electrostatic behavior of kyanite, sillimanite, and zircon, simple silicates that cannot be called either acid or basic but are more nearly neutral. Kyanite and sillimanite are both desired in 10-mesh size and are difficult to beneficiate from low-grade ores to give that type of concentrate. A separation of garnet from diopside was studied because this mixture had been removed from a wollastonite product by drying and magnetic separation, and no special or extra-preparation for electrostatic separation was necessary. THE SEPARATOR The separator used in these tests is of the nonhomogeneous field type shown in Fig I[a]. It consists of a 11.4-cm-diam rotating metal roll 2 at ground potential over which the dry mixture of minerals is fed. The roll serves as one electrode of the separating field, and the other electrode is that of 3, a smaller 5-cm-diam rotating metal cylinder which is held at a high direct-current potential. In this paper the term "electrode" will be confined to the electrode at 3, roll 2 being designated only as "roll." [ ]

Jan 1, 1947

By W. A. Clark

THE production of sand in an oil well increases operating costs because of abnormal wear in subsurface equipment, the necessity for frequent cleanouts, and the need for a means of disposing of the sand. Moreover, removal of sand from the zone can bring about the creation of cavities from which bodies of formation, sand or shale, may slough into the hole, endangering the shutoff, impeding production or collapsing the liner. The procedure known as gravel packing is attracting attention as a means of controlling these factors and contributing to the productive life of a well. That gravel packing is now substantially beyond the preliminary stage on the Pacific Coast is reflected in the 191,000 bbl, of oil produced monthly by the 66 gravel-packed wells in 11 different producing sectors. REASONS FOR GRAVEL-PACKING Gravel packing, if properly carried out, can be expected to provide the following benefits: 1. Prevent the movement of sand and thus eliminate sand production and sand fills, and prevent the formation of cavities. 2. Provide a practical, relatively inexpensive, large-diameter hole, which will provide well-known theoretical advantages. 3. Support the walls of the hole by completely filling the space between the liner and the formation, regardless of its irregularities, and afford a support for liners. 4. Provide for more efficient pumping operations in wells by: (a) possibly utilizing the gravel as a gas trap in pumping gaseous fluids, (b). allowing deep submergence of the pump into the oil zone.

Jan 1, 1939

By B. A. Wilcox, A. H. Clauer

The steady-state creep of TD Nickel NL + 2 001 pct TltOz) has been studied orer the telirperatve range 325&apos; to 1100O and the stress range 15,000 to 36,000 psi. At high temperatures (aboue 0.5 T& gran-boundary slzding is the )nost znportant )node of creep deformation, and the steady-state creep rate, is, can be related to stress and temperature by: where Q = 190 kcal pev mole and n has an unusually high value of 40. A creep mechanism based on cross slip of dislocations around The O2 particles can satisfactovily explain the low-temperature (T < 0.5 T,) cveep behavior, and the follo wing relation is applicable: Q, (a) is found to decrease from 57 to 46 kcal per mole as the stress is increased from 32,000 to 36,000 psi. THERE have been a variety of theories proposed to explain the influence of dispersed second-phase particles on the yield strength and flow stress of metals, and these have been reviewed recently by Kelly and icholson.&apos; However, only several attempts2"4 have been made to develop mechanistic treatments which characterize the creep behavior of dispersion-strengthened metals, and to date these have not been fully evaluated experimentally. weertman2 and Ansell and weertman3 proposed a quantitative creep theory for coarse-grairzed dispersion-strengthened metals, based on the concept that the rate-controlling process for steady-state creep was the climb of dislocations over second-phase particles, as suggested by choeck. The theory predicted that the steady-state creep rate, <,, was proportional to the applied stress, a, for low stresses and that is a4 o for high stresses. The activation energy for creep, Q,, was equivalent to that for self-diffusion, Qs.d., in the matrix. Some limited experimental evidence in support of this theory was obtained on a recrystallized Al-Alz03 S.A.P.-type alloy by Ansell and Lenel.6 Ansell and weertman3 also developed a semiquanti-tative theory for high-temperature creep of lineg-rained dispersion-strengthened metals in order to explain their results on an extruded S:A.P.-type alloy, which had a fine-grained fibrous structure. They suggested that the rate of dislocation generation from grain boundaries was the rate-controlling process, and fitted their results to the equation: where Q, was found to be 150 kcal per mole, i.e., QC- 4Q,.d. in aluminum. Similar high activation energies for creep7-&apos;&apos; and tensile deformation" of dispersion-strengthened alloys have been observed by other investigators for S.A.P.,&apos;" indium-glass bead omosites, and Ni + A1203 alls.&apos; There is no general agreement regarding the mechanisms involved in the creep of dispersion-strengthened metals, and this is due in part to the lack of detailed studies relating the structures of crept specimens to the mechanical behavior. The present investigation on thoriated nickel was undertaken with the aim of studying the structural changes which occur during creep of a dispersion-strengthened alloy and rationalizing the observed mechanical behavior in terms of the creep structures. EXPERIMENTAL METHODS The material used in this investigation was 1/2-in.-diam TD Nickel bar, which contained 2.3 vol pct Tho,. Obtained from E. I. duPont de Nemours & Co., Inc. The final fabrication treatment by DuPont consisted of -95 pct reduction by swaging followed by a 1-hr anneal at 1000°C. Transmission and replica electron microscopy revealed that the material had a fine-grained fibered structure with an average transverse grain size of -1 p and a longitudinal grain size of 10 to 15 p. Selected-area diffraction indicated that the fiber axis was parallel to (OOl), in agreement with the results of Inman eta1." All creep specimens were vacuum-annealed at 1300°C for 3 hr prior to testing. Transmission electron microscopy showed that the only structural change due to annealing was a slight decrease in dislocation density, confirming the reported high degree of structural stability.13 Furthermore, recrys-tallization or grain growth during creep was never observed. The structure typical of uncrept material (after the 1300 C, 3-hr anneal) is shown in Fig. 1. The grain boundaries are predominantly high angle and. although some areas show a tangled cell structure, the grain interiors are relatively dislocation-free. Individual dislocations are strongly pinned by the Tho2 particles; i.e., very rarely did dislocations move within a thin foil. The grey "halos" around some of the larger particles which protrude out of the foil surface arise from contamination in the electron microscoge. The Tho, particle size ranged from -100 to IOOOA, and the distribution is shown in Fig. 2. The technique used to obtain the data in Fig. 2 consisted of dissolving the nickel matrix in acid, collecting the Tho2 particles on cellulose acetate, and measuring about 1000 particle diameters in the electron microscope. Similar results were obtained by measuring about 600 particles in thin foils, an; the average particle size was found to be 2r, = 370A. Using the data in Fig. 2 (annealed structure), the mean planar center-to-center particle

Jan 1, 1967

By Frederic L. Kadey

Diatomite is a siliceous, sedimentary rock consisting principally of the fossilized skeletal remains of the diatom, a unicellular aquatic plant related to the algae. Thus, it has been formed by the induration of diatomaceous ooze, and consists mainly of diatomaceous silica, a form or variety of opal which is first formed in the cell walls of the living diatom. Diatomaceous silica is not generally regarded as a synonym or the equivalent for diatomite, although it has been so used at various times. Accurately, diatomaceous silica is the preferred name for the principal mineral component of which the rock, diatomite, is composed. The terms diatomaceous earth and kieselguhr are used as synonymous with diatomite. The designations tripoli, tripolite, infusorial earth, etc., were used at one time but are now obsolete. With the changing nomenclature, these terms that were at one time correct when proposed and used for generations would be considered incorrect if used today in the light of current knowledge. The designation diatomite is reserved for those accumulations of diatomaceous silica that are of sufficient quality, size, and minability to be considered of potential commercial value. Processed diatomite possesses an unusual particulate structure and chemical stability that lends itself to applications not filled by any other form of silica. Foremost among these applications is its use as a filter aid, which accounts for over half of its current consumption. Its unique diatom structure, low bulk density, high absorptive capacity, high surface area, and relatively low abrasion are attributes responsible for its utility as a functional filler and as an extender in paint, paper, rubber, and in plastics; and as an anti-caking agent; thermal insulating material; catalyst carrier; and chromatographic support; polish, abrasive, and pesticide extender to name a few representative applications. The United States is the principal producing country, although diatomite is found in numerous other locations. Geology Composition and Morphology Diatomaceous silica qualifies as a. mineral of organic origin in much the same way that aragonite and collophane do. The silica of the fossilized diatom skeleton closely resembles opal or hydrous silica in composition (SiO2 • nH2O) .4, 12, 203 The silica is of acute biological significance, not only for the cell wall component, but also for the basic life process.45, 51 Without silica, cell development ceases .31 In addition to bound water, varying between 3.5 and 8%, the siliceous skeleton may also contain, in solid solution, or as part of the Si02 complex, small amounts of associated inorganic components-alumina, principally-and lesser amounts of iron, 46, 49, 55 alkaline earths, alkali metals, and other minor constituents.59, 63, 67 Boron is reported to be an essential element for diatom growth .52, 58 Since diatomaceous silica is not pure hydrous silica but contains other intimately associated elements, there is good reason to consider it a distinct type or variety.4 Associated with the diatomaceous silica, and integrated as part of the diatomite, may be variable amounts of organic matter, soluble salts, and particles of rock-forming minerals that were syngenetically deposited or precipitated with the diatom frustules. Sand, clay, carbonate, and volcanic ash are typical common contaminants. Other contaminating minerals may be present, such as feldspar, mica, amphiboles, pyroxenes, rutile, zircon-the result of weathering, then transporting, and subsequent redeposition of surrounding land masses. Commercial diatomite may also contain fragments and particles of

Jan 1, 1983

By S. L. Couling, D. J-P. Adenis

i2) twinning in poly crystalline magnesium does not usually occur homogeneously but is concentrated in localized regions or bands inclined at about 45 deg to the stress axis. These bands of twinning are in many ways similar to the Luders bands seen in mild steel alzd Al-Mg alloys. Within a hand the percentage of the volume twinned may approach 100 with no twinning outside the band. Bands are not produced in specimens of grain size a3 x 10-= in. or in samples deformed at temperatures 300°F. Annealing of heavily twinned regions leads to re crystallization textures markedly different from those found in the starting material. The exact preferred orientation appears to depend on the starting grain size, the amount of compres-sive strain and the manner in which it is introduced. MAGNESIUM, with its hexagonal crystal structure, deforms plastically at room temperature by a variety of deformation mechanisms, one of the most important of which is (1012) twinning. In single crystals such twinning occurs on compression parallel to the basal plane or tension perpendicular to it. In wrought polycrystalline magnesium, such as rolled sheet, the preferred orientation is such that almost all the grains have their basal planes nearly parallel to the sheet surface. Therefore, if sheet material is deformed by cold rolling or by tension in the plane of the sheet, deformation of the grains by (1012) twinning is not favored. On the other hand, twins form readily on compression parallel to the plane of the sheet as in a compression test, on the compression side of a bent sample, or at the outer rim of a drawn cup. The first part of this paper deals with the morphology of (1012) twinning in polycrystalline magnesium. Some aspects of this subject were covered by Barrett and ~aller.&apos; Of direct bearing on the work to be reported here are the comments of Jetter&apos; in discussion to Ref. 1. He shows that Mg + 1.5 pct Mn alloy sheet when bent about a transverse axis develops a pattern of transverse bands on the surface of compression. A longitudinal section through the sheet shows that the bands are wedge-shaped and inclined to the rolling direction. The bands were identified as "outcrops of regions in which deformation is localized as the result of the reorientation brought about by (1012) twinning". The second part of the paper treats the recrys-tallization texture of the specimens twinned by compression. Magnesium deformed and then annealed generally recrystallizes with no change in orientation.1&apos;3&apos;4 This statement is true provided that the amount of (1012) twinning occurring during deformation is small. In an isolated observation, Anse15 has shown that, when deformation produces much (1072) twinning, annealing causes new maxima to appear in the pole figure. The second part of the paper elaborates on this point. I) MATERIALS AND PROCEDURES All of the experimental work to be reported was done using the commercial sheet and plate alloy AZ31B (nominal composition: 3 pct Al, 1 pct Zn, 0.4 pct Mn, balance magnesium). This alloy is available commercially in two tempers, -0 (fully annealed) and -H24 (partially annealed), and specimens of both tempers were used in various experiments. The average grain. diameter (AGD) for -0 temper 0.125-in. sheet is about 0.5 x 10- in.; where material of larger grain size was desired, anneals at elevated temperature were used to grow the grains. compression tests were made on a screw-driven "hard" machine. The specimens were clamped in a

Jan 1, 1964

By F. G. Miller, T. D. Mueller, L. B. Davidson

A mathematical model of reservoir behavior during one cycle of the intermittent steam injection process is presented in this paper. A cycle of the process is considered to be composed of three stages: injection, condensation and production. The model concentrates on behavior during the production stage. The influence of several parameters on production improvement is described, using the results obtained with a numerical equivalent of the model. Reservoir system parameters considered are thickness, reservoir thermal conductivity, oil viscosity, solution gas-oil ratio and the change in oil effective permeability with temperature. Operating parameters investigated are heat injection rate, steam temperature and cumulative injection time. In the face of considerable uncertainty, the model appears to give a fair prediction of the behavior observed during an actual test. This makes the model a useful means of selecting projects. It is shown that the model may also be utilized to select an optimum set of operating conditions for a particular project. Results of this study show the extent to which production improvement depends on each of the parameters investigated and give an indication of the range of system conditions within which the process would be effective. INTRODUCTION In recent years the intermittent steam injection or steam soak process of oil recovery has become a popular method of improving recovery in reservoirs bearing high-viscosity hydrocarbons. Production improvement due to the process results from heating the reservoir near the wellbore. The process is applied on an individual well basis and is executed in a series of cycles, each consisting of three stages: injection, condensation (the soaking period) and production. During the injection stage, high-pressure steam is injected into the reservoir surrounding the well-bore. This study assumes that injection is carried out over the entire vertical section of the reservoir rock that can be exposed to fluid injection. The condition of steam entering the reservoir is considered to fall within the following limits: (1) steam pressures less than 1,000 psig, (2) steam temperatures between 300 and 700F and (3) steam quality less than 90 percent. The last restriction is due to equipment limitations. Normally, injection re maintained for less than 3 weeks. After termination of injection, the condensation stage begins. The well is shut in for several days, supposedly to make certain that the injected steam condenses. This condensation would insure the retention of injected heat. The production stage is initiated when the well is opened again. Reservoir response during this stage determines the effectiveness of the process (response is defined as the oil production rates, the water production rates and the wellbore temperatures observed during the entire production stage). The immediate response of the reservoir is sometimes quite good. Sets of case histories by Longl and by Owens and Suter2 give some typical figures for response. Duration of the production stage is equal to the time needed for the oil production rate to decline to some predetermined value. This usually requires 4 to 6 months. Termination of the production stage coincides with the start of the next cycle. The process is continued, cycle by cycle, until it becomes unprofitable to continue. One simple model2 and two more sophisticated models3,4 of the process have been presented. These are based on fundamentally different assumptions than those used in this investigation. Although the three models might be modified to fit the assumptions used in this study, it is felt that greater rigor would result by developing a

By R. L. Vaughn, A. G. Moon

In 1972 a major renovation of the flotation and regrinding circuits was completed at Kennecott Copper Corporation&apos;s Chino Mines Division concentrator at Hurley, New Mexico. At that time a new lime distribution and control system was placed in operation. Lime is used to depress pyrite, and flotation at a high pH or alkalinity is required for optimum recovery of principal copper minerals, chalcopyrite and chalcocite with good rejection of the pyrite. Regrinding is also required to liberate chalcocite, much of which occurs as intimately associated chalcocite-pyrite middling grains. Accurate control of the lime addition is necessary to obtain both optimum metallurgy and minimum lime usage. At low pH levels, flotation cell control is difficult due to excess froth, but excessively high pH levels can go unnoticed because froth characteristics do not change from those experienced at the desired pH. With manual control of the lime addition, the desired pH can be exceeded for periods of up to two hours. Test Work Plant test work on a lime control system using conventional pH probes gave disappointing results with high electrode maintenance and poor control characteristics. For example, the rougher flotation cells are operated at a pH between 11.4 and 11.6 and the probes required cleaning at least once a day, and occasionally every shift. These high maintenance requirements were considered unreasonable for a plant-wide system using six or more control loops.

Jan 1, 1979

By P. Dayal, L. S. Darken

THE migration of carbon in austenite under the influence of an electric current has been observed qualitatively several times.14 Lebedev and Guterman5 recently have reported quantitative measurements; their method consisted of welding a low-carbon to a high-carbon wire, passing current, and later estimating the carbon distribution metal-lographically. We believe the method reported in this paper is superior in principle since electrolytic migration and ordinary diffusion are not necessarily coupled as in the weld method; also for the first time the extent of migration is determined by combustion analysis for carbon. A uniform tubular specimen (S.A.E. 1045 or 1095) was mounted as illustrated in the figures. the whole assembly being in an atmosphere of purified nitrogen. Direct current (129 to 226 amp at 0.65 to 1.0 v) served as source both of heat and of potential gradient for carbon migration. The duration of experiment was 7.5 to 12 hr, during which time the temperature was controlled (±10°C) manually. The experimental conditions are indicated in the first five columns of table I. With this experimental arrangement, the temperature initially has a maximum value at the central plane. Also, in this vicinity (by virtue of the symmetry), the carbon entering any volume element is equal in quantity to that leaving; the loss or accumulation of carbon occurs near the electrodes since the carbon moves uniformly near the center and is "frozen" at the cold ends. Hence, providing the time of experiment is not sufficiently long to seriously influence the conditions at the central plane, carbon crosses this plane only under the influence of the electrical potential gradient and not under the influence of temperature or concentration gradient. The amount of carbon which has crossed this plane was determined by combustion analysis of the two halves of the specimen. The results of these analyses are shown in the sixth and seventh columns of table I. It will be noted that substantial amounts of carbon migrated from the anode portion to the cathode portion (except at 920°C, which temperature was too low to exhibit the effect in the allotted time). In spite of precau-tions taken, considerable decarburization occurred as may be seen by comparing cols. 8 and 5. In three cases (indicated by asterisks in table I) the specimen was ground on one side, polished, and examined metallographically before analysis. One specimen was normalized and re-examined. Micrographs of selected areas in specimens 4 and 6 are shown in figs. 1 and 2, respectively. Evidence of carbon migration from the anode toward the cathode is quite apparent. Fig. 2 shows abundant graphite as well as cementite in a region near the cathode. The temperature of this zone is estimated at about 800°C. In fig. 1, particularly in the micrograph on the extreme right (the right side of which is of unaltered carbon content), there is evidence of slight depletion of carbon in the immediate vicinity of the cathode as contrasted to the general increase in carbon of the cathode half of the specimen. Although this may be attributed in part to decarbur-ization, it is believed that it is occasioned also by thermal diffusion—migration (of carbon) from a cool to a hot zone4—a phenomenon superimposed upon the electrical migration. Evidence of carbon migration was visible particu-larly during the course of the high-temperature,

Jan 1, 1951

By E. P. Barrett

THE high-frequency laboratory induction furnace with a rotating liquid crucible enables research workers to conduct certain investigations heretofore very difficult or impossible to realize because vessels are not obtainable that are capable of resisting the physical conditions or the chemical actions to which they are subjected. Applications for patents covering commercial uses of centrifugal liquid crucibles were filed in the United States in 1919,1 in France in 1925, in the United States and Germany in 1926,2 and in France in 1927.3 In 1928, Schuette and Maier,4 of the Bureau of Mines, reported the construction of a whirling table beneath a high-frequency induction furnace. SHAPE AND SIZE OF CENTRIFUGAL LIQUID CRUCIBLES When a vessel containing a liquid is rotated, the inner surface of the liquid takes the shape f a paraboloid under the simultaneous action of centrifugal force and gravity. The internal dimensions of the paraboloid rotating liquid crucible are governed by the diameter of the container and its speed of rotation. Melted Wood&apos;s metal was poured into cylinders 2 ½ in. in diameter, which were rotated at 180, 300, and 468 r.p.m. When the metal was solid, a slurry of plaster of Paris was added, and rotation continued until the plaster had set. Fig. 1, a photograph of sections f the cylinders, shows the effect f speed f rotation of the containers upon the shape f the inner surface f the rotating liquid crucibles.

Jan 1, 1938

By C. L. Dake

Chemistry of Iron Solution IRON is much more soluble in the ferrous than in the ferric form. Where, as in the case of the ferrous silicates and the sulphides, the iron is already in the ferrous form, it may go at once into solution and be removed, upon the breaking down of the parent rock. If in the ferric form, it must first be reduced; usually by the decay of organic matter, the demand of the decaying carbonaceous matter for oxygen being so great that the latter is abstracted from the ferric compounds and the iron is thereby reduced and rendered&apos; soluble. The iron may go into solution as the sulphate, or in the presence of excess CO2 as ferrous carbonate. It is probably soluble as salts of the organic acids.1 Recent work indicates that these are important in the formation of bog ores.2 There is considerable variety of opinion concerning the behavior of these organic compounds.3 The secretions about the roots of plants and trees also cause the solution and removal of iron and a consequent bleaching of the soil.4 While the matter is not yet well understood, we can probably say definitely that the so-called organic acids are a group of colloids which possess slightly acid properties, and the salts of which are partly soluble

Jan 7, 1915

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.&apos; It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By Shun-ichi Satoh

A NEW method of treating steel by ammonia has recently been intro¬duced into the metallurgical industry, by means of which piston cylinders of internal combustion engines, shafts and other similar steel products can be made more resistant to wear than formerly. In 1929 the writer&apos; published the historical notes and some experiments upon nitrification. He believes that the corrosion of nitrified steel is a matter of importance and worth studying; and as there have been few studies thereof, he has conducted experiments in this respect. L. Guillet,2 in 1927, reported corrosion tests made on nitrified and cemented steels with acid and salt solutions. In 1928, 0. Hengstenberg3 reported the high resistance of nitrified steel to water vapor and air. V. 0. Homerberg4 stated that nitrified steel has high resistance to water, air and salt solution; and G. Hagg5 studied nitrified layers of iron by means of the X-ray. Though F. Hanaman6 in 1913, measured the single potential difference of steel treated with ammonia at above 650° C., no one, it seems, has ever measured the single potential difference of the so-called nitrified steels having extraordinary hardness. The writer measured the single potential differences of nitrified special steels in various solutions with the object of studying the corrosion problem and, if possible, of knowing whether any new physical property would be caused by nitrification.

Jan 1, 1932

By R. V. Smith, E. J. Dewees, R. H. Williams

Before this paper was presented, the terms "f" and "v1/f in flow equations had been called "friction coefficient" and "friction factor," respectively. However, many authors have used the names for the terms interchangeably, with the result that considerable confusion has existed in the literature on flow of fluids. In an effort to establish a clear and concise terminology for these terms, the authors have designated f as "resistance coefficient" and dm as "transmission factor." Transmission factors for the flow strings of gas wells were determined by tests on wells in six fields of Oklahoma, Texas, and Louisiana. Data were collected on 14 gas wells while gas was flowing through 1 1/4, 2, 21/2, and 3-in. tubing and 51/2 and 7-in. casing. The transmission factors developed from these data were found to follow the resistance equation published by Nikuradse1 for turbulent flow in "rough" pipes with an average absolute roughness of 0.000,65 in. This average absolute roughness is believed to be representative generally of the flow strings of gas wells with the exception of those that have been exposed to corrosion or other conditions causing undue roughness. Also, use of an absolute roughness of 0.000,65 in. probably will result in transmission factors that are more representative of gas-well conditions than those in common use today, provided that the transmission factors are calculated by the methods outlined in this report. The authors believe that use of these transmission factors will permit calculation of more accurate subsurface pressures in gas wells than those in use today. Engineers use transmission factors in flow equations to compute subsurface pressures in flowing gas wells from measured wellhead pressures. These subsurface pressures are necessary for determining the productivity of gas wells from "back-pressure" tests. The methods of calculating pressures in flowing gas wells, as outlined by Rawlins and Schellhardt2 in Bureau of Mines Monograph 7, are based on the transmission factors in the well-known Weymouth formula" Natural gas engineers have realized that errors introduced by using transmission factors as given by the Weymouth formula are relatively unimportant in testing low-capacity gas wells; but they also know that such factors are important considerations in testing large-capacity wells. Accordingly, the research described in this report was undertaken to fulfill the need for more accurate means of calculating subsurface pressures in gas wells. This report is part of the Bureau&apos;s study of the flow of natural gas through pipe and commercial pipelines. Several of the conclusions regarding flow in the flow strings of gas wells were influenced by the results of the study of flow in horizontal pipelines. These instances are mentioned in the text of this report. METHODS OF COMPUTING TRANSMISSION FACTORS Methods and procedures for computing transmission factors for turbulent flow in circular pipes from test data taken on gas wells have been derived and explained in detail in a paper by Smith4. As these methods were used to calculate the transmission factors presented in this report, a summary is included. Starting with

Jan 1, 1955

By W. H. Emmons

THIS paper is the third of a series treating of the relations of ores of the metals to igneous rocks. The first1 outlined the general problem; the second2 proposed a classification of lode ores, and showed how the distribution of the deposits is in a certain measure controlled by the contour of the roof of the parent batholith. A number of mining districts were discussed, the examples being selected chiefly from group 2 of the classification. The proposed classification of lode deposits, briefly stated, is as follows: 1. Cryptobatholithic: near hidden batholiths which have not yet been exhumed by erosion. 2. Acrobatholithic: in and near cupolas or domes of batholiths-the high points of larger underlying masses. 3. Epibatholithic: on batholiths, near their rims, but below eroded cupolas, or below the highest points of the roofs. 4. Embatholithic: among closely-spaced outcrops which probably are parts of a single batholith. The outcrops of invaded rocks predominate. 5. Endobatholithic: in and near roof pendants of large batholiths. The invading rocks predominate. 6. Hypobatholithic: in deeply-eroded batholiths, where even roof pendants, have been -eroded. Deposits of certain metals on the roofs of the batholiths are much more numerous in some positions than deposits of other metals, and the horizontal zonal arrangements of lodes of different metals are shown characteristically only in certain groups. In a large measure, also, the character of the fracturing and metallization is determined by, the-position on the roof, of the batholith.

Jan 1, 1927

By H. C. Rolseth, R. H. Kohler

Jet channeling made its entry into the granite industry in 1955 and quickly gained acceptance as an economical method of quarrying. Developed by the Linde Division of Union Carbide Corp., this method employs a small rocket-jet burner with a high-temperature, high-velocity exhaust flame that causes granite to disintegrate. It can thus make continuous vertical cuts to free large blocks from granite formations. The Thermal Spalling Process The effect of a thermal device on rock depends upon the rock&apos;s spallability. In simplest terms, spalling is the decrepitation resulting from differential expansion of rock crystals due to thermally induced stresses.1 the individual rock properties influencing the spalling characteristic are so numerous and their interaction is so complex that it has so far been impossible to predict with accuracy the reaction of any particular rock to a high-temperature source of heat. Perhaps computers will eventually make such predictions possible, but for the present it is necessary to impose the thermal shock conditions on a sample of the rock to establish its spalling characteristics. The properties most favorable to a high degree of spallability are: (1) Large linear thermal expansion at temperatures below 700º C. (2) High thermal diffusivity at temperatures below 400º C. (3) Equigranular interlocking structure with little or no fine-grained clay or mica alteration products. (4) No significant amounts of soft, low-melting, or elastic minerals or materials which yield after thermal decomposition.

Jan 7, 1969

By Y. C. Liu, G. A. Alers

measurements of the anisotropy in Young&apos;s modulus produced in copper by rolling 95 pct reduction in thickness below room temperature have been carried out in order to study the dependence of the texture on rolling temperature. The results clearly show the transition from a copper-type texture to a brass-type texture as the temperature of rolling is lowered. The intermediate textures observed can be described very well as a simple mixture of the two terminal textures. These results cormbined with other texture measurements make possible afresh review of the experimental facts velating to rolling textures in fee metals and, as a consequence, a critical examination of the current theories is presented. PREVIOUS experiments have shown that the transition from the copper- to the brass-type rolling texture is clearly displayed and can be quantitatively analyzed by measurements of the anisotropy of Young&apos;s modulus.&apos; Application of this method to the Cu-Zn alloy system showed that the description of the texture transition as a gradual rotation of the grains from the orientation characteristic of the copper texture to the {110}(112) texture of brass2 was inconsistent with the data. Instead, the data suggested that the texture within the transition region could be described as a simple mixture of the two terminal textures.5 Unfortunately, it was difficult to establish this point conclusively because of the inadequacy of corrections for the composition dependence of the single-crystal elastic constants. Since a rigorous establishment of the nature of this texture transition is essential to our understanding of the formation of rolling textures in fee metals, it is clearly important to undertake an investigation in which the composition dependence of the elastic constants would not enter. A suitable composition-independent texture transition is provided by the well-established variation in the rolling texture of copper with rolling temperature. This temperature-dependent texture transformation has been studied by smallman&apos; in several fee alloys and by Müller5 and others"&apos; in copper. They observed that the texture characteristic of copper rolled at room temperature changed to a brass-type texture when the rolling temperature was lowered to 77°K. Although it is not possible to decide unequivocally from the published pole figures whether or not the 77°K rolling texture of copper is entirely of the brass type,&apos; this complication does not affect the main purpose of the present investigation. In addition to establishing the nature of the texture within the transition region, the modulus data should also provide a determination of the temperature at which the transition occurs as well as the temperature range over which the transition extends. This information when combined with the modulus data on Cu-Zn alloys would then provide a considerable body of new information on textures in fee metals. Since these modulus results and the data obtained from pole-figure studies must be internally consistent, it is appropriate to compile a brief summary of the experimental observations based on all available methods rather than on the pole-figure data alone as has been done in the past. The primary purpose of such a summary would be to yield a more precise definition of the experimental facts on the rolling textures of fee metals, and thus greatly facilitate our evaluation of various proposed theories in this field. The final section of this paper is devoted to this compilation of consistent, experimental facts and their application to the various theories. EXPERIMENTAL PROCEDURE Two 18-lb ingots of cathode copper of 99.99 pct purity were induction-melted under a nitrogen atmosphere in a graphite crucible and chill-cast into a steel mold. The ingots were repeatedly cold-rolled and annealed (I hr at 500°C) into slabs about 1 1/8 in. thick. Blocks 3 1/4 in. wide, 2 1/4 in. long, and 1.000 in. thick were machined from each slab. The rolling schedule used was the same as in the previous investigation1 and the final thickness of the sheet was 0.050 in. with a rolling reduction of thickness of 95 pct instead of 97.5 pct as in the previous work.&apos; The compositions and temperatures of the cold baths used for the low-temperature rolling were as shown in Table I. After each pass the rolled strip was immediately immersed in the cold bath for about 1 min or until the bubbling of the bath had subsided. The modulus data were taken within 2 hr after the rolled strip was warmed to room temperature for the first time, so that effects due to recrystallization were minimized. The modulus specimens were in the shape of flat bars, 3 in. long, 4 in. wide, and 0.050 in. thick, cut with their long dimensions oriented at 15-deg intervals between the rolling direction and the transverse direction. The values of Young&apos;s modulus were deduced from measurements of the frequency at which these long narrow bars were set into longitudinal, resonant vibration as previously described.9 To excite the mechanical vibrations in the specimen, an electromagnetic drive similar to that employed by Thompson and lass" was used. The maximum in the amplitude of

Jan 1, 1968

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By R. S. Busk

A PREVIOUS paper1 has summarized the effect of A all metallic elements on the lattice parameters of magnesium. The present paper deals with the effect of temperature on the lattice parameters and the way in which that effect is modified by alloyed elements. The experimental techniques for sample preparation, exposure to the X-ray beam, measurement of line diameters, and calculation of the parameters were the same as reported in the previous paper. The temperature of the specimen was raised by surrounding the mounted compact with a conical Glas-Col,* the base of which was sealed with Saran film. In this way the temperature of the specimen could be raised to 200 °C, which was the maximum desired in the present study. Control of temperature was effected by maintaining a constant, desired voltage to the resistance coils of the Glas-Col through a Variac. Temperature was measured by an iron constantan thermocouple embedded in the body of the specimerl so that the thermocouple bead was within 1/16 in. of the surface exposed to the X-ray beam. Variation of temperature during an exposure was less than + 1/4 oF. A series of eight alloys, consisting of pure Mg, Mg+Ag, Mg+Al, and Mg+Sn were studied. All percentage values are in atomic percent. The results are given in Table I. The density values given in Table I were calculated from the lattice parameters, using an equation due to Foote and Jette:"

Jan 1, 1953

By Oliver C. Ralston, Foster Fraas

Electrostatic methods of separation are used only when some peculiar advantage is gained. Such cases are minerals that are not separable by differences in specific gravity or magnetic response and that are desired in particles as large as 10-mesh, a size on which flotation separation is inefficient. This paper covers several separations of this type and others. It includes studies in the electrostatic behavior of kyanite, sillimanite, and zircon, simple silicates that cannot be called either acid or basic but are more nearly neutral. Kyanite and sillimanite are both desired in 10-mesh size and are difficult to bene-ficiate from low-grade ores to give that type of concentrate. A separation of garnet from diopside was studied because this mixture had been removed from a wollas-tonite product by drying and magnetic separation, and no special or extra-preparation for electrostatic separation was necessary. The Separator The separator used in these tests is of the nonhomogeneous field type shown in Fig Ia. It consists of a 11.4-cm-diam rotating metal roll 2 at ground potential over which the dry mixture of minerals is fed. The roll serves as one electrode of the separating field, and the other electrode is that of 3, a smaller 5-cm-diam rotating metal cylinder which is held at a high direct-current potential. In this paper the term "electrode" will be confined to the electrode at 3, roll 2 being designated only as "roll."

Jan 1, 1949

By D. G. Westlake

NUMEROUS hydride habit planes in zirconium, Zircaloy-2, and Zircaloy-4 have been observed by various researchers and have been compiled by Louthan and Angerman.1 While only partial agreement exists on the identification of these habit planes, there is a growing consensus that a tensile stress applied on a polycrystalline rod during slow cooling will cause the hydride platelets to lie perpendicular to the tensile axis. walters2 agrees with Louthan and Angerman who reason that "The particular plane on which precipitation will occur is the plane that will result in the maximum relief of stress by precipitation of the low-density hydride." The experiment described below was initiated to test this hypothesis on a single crystal of zirconium. A single-crystalline tensile specimen of zone-refined zirconium, designated number 13 in a previous study,3 had a square cross section with one pair of parallel faces only 4 deg from the basal plane of the hcp structure. The tensile axis was about 86 deg from the (0001) pole, 14 deg from the (1010) pole, and 16 deg from the (1150) pole. The specimen was charged to 50 ppm H by allowing reaction with the correct amount of hydrogen at 1073°K, homogenizing at this temperature for 2 hr, and cooling in the furnace. Two- surface analysis revealed that hydride platelets had precipitated parallel to the three {1010} prism planes. The specimen was heated to 673°K, in air, for 16 hr to bring the hydrogen back into solid solution, and furnace-cooled to 573°K.* It was then stressed in ten- sion at 1.2 kg per sq mm. (This produced a resolved shear stress of 0.6 kg per sq mm for glide on the prism plane with the highest Schmid factor. A higher stress would have produced significant strain at this temperature because the critical resolved shear stress for prism-plane glide in this crystal was only 1.0 kg per sq mm at ambient temperature.) The poles of the three prism planes were at angles of 14, 46, and 74 deg to the tensile axis so that an applied stress would exert normal stresses on the three planes in the approximate ratios 10:5:1, respectively. As soon as the stress was applied, the sample was furnace-cooled to room temperature. It was ground on wet Sic paper and chemically polished in 50 parts HNO3, 50 parts water, and 7 parts HF before examination. The result of the experiment was negative; i.e., the three (1010) planes were of equal importance as hydride habit planes.* It must be admitted that the ex- periment is not entirely comparable to those performed by walters,2 Louthan,5 and Louthan and Marshall6 on polycrystalline materials. They have found that some critical stress (below the macroscopic yield stress) is required for stress-orienting the hydrides. The applied stress in the present experiment was, by necessity, smaller by an order of magnitude than the critical stresses they report for the various materials. If the critical stress was related to the microstructure, one might postulate that it should be decreased by increasing the degree of perfection of the metal lattice and by increasing the grain size. But the experiment above suggests that, for the extreme case of a zone-refined single crystal of zirconium, the critical stress lies above that which one can apply without introducing gross plastic strain as another variable.

Jan 1, 1967