By C. Y. Garber

Interest in the sink-float plant operated by the Bunker Hill and Sullivan Mining and Concentrating Co. at Kellogg, Idaho, has recently been largely confined to the preparation and reconditioning of the galena medium. The ease and simplicity of these operations in a concentrating mill producing a flotation lead concentrate has occasioned enough comment to possibly justify a brief description. The subject is treated from an operator's viewpoint only; no effort is made to discuss it in a theoretical or technical manner. Plant at Bunker Hill The sink-float plant was first operated in December 1941. It was built for the purpose of quickly increasing mill capacity with a minimum of equipment. It is the Huntington-Heberlein sink and float process using galena medium and is operated under license from the Sink and Float Corporation, New York city. Lead-zinc ore from the Bunker Hill mine is crushed to pass a 1¼ in, screen and is then washed and separated on vibrating screens having 4½-mm. round-hole punched plates. The screen under-size, amounting to 33 per cent of the mill feed, is dewatered and sent to the ball-mill feed bins. The screen oversize goes to the sink-float plant, where 50 per cent of the oversize, or 33 per cent of the mill feed, is float, which is washed free of medium and disposed of as a tailing. The remaining 33 per cent is sink, which, after washing, is crushed to pass 36 in. and joins the under-size in the ball-mill feed bins. The normal plant capacity is 1700 tons per 24 hr. About 1.7 per cent of the total lead and 3.3 per cent of the total zinc in the feed is lost with the sink-float tailings (Table I). More complete descriptions of the H. H. process and Bunker Hill sink-float plant are given in several recent articles, listed at the end of the paper. Preparation OF Medium at Bunker Hill New medium is made intermittently as needed, usually 12 hr. in each 6 days. A small portion of the current mill flotation concentrate is diverted from the lead cleaner cells to a I-in. vertical sand pump and pumped to a two-cell 36-in. Agitair flotation machine, where NaCn and ZnSO4 are added and the grade of concentrate is improved as shown in Table 2. Tailing from this operation is returned by gravity

Jan 1, 1947

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By Robert W. Elayer

In August 1973, Fluor Utah, Inc. was awarded a contract by the Office of Coal Research (now part of the Energy Research and Development Administration), Department of the Interior, for the examination of the unique problems of large-scale surface coal mining to supply coal conversion complexes. The project consists of two phases: (I) data base development and organization and the formulation of a mathematical computer modeling system for surface mining; and (II) computer manipulation of the data base in accordance with the model to formulate several typical preliminary mine and preparation plant designs. Phase I is scheduled for completion by the end of July 1975 and Phase II is scheduled to be complete by the end of January 1977. This paper briefly discusses the effort for only one aspect of this project-the foundation for geologic modeling developed in Phase I. The Phase I task of geologic modeling can be broken down into two subtasks: (1) identify areas containing sufficient resources of surface-minable coal to support at least one large-scale mining complex, and (2) characterize the coal deposits in these areas for computer storage and retrieval. Identification of Resource Regions The basic production design criteria for large-scale surface mining, as stated in the contract, is the production of 75,000 tpd, or more, of bituminous coal. Based on a constant total Btu delivered to the preparation plant, daily production requirements for the different coals are as follows: Bituminous Coal 75,000 tons Subbituminous Coal 99,500 tons Lignite 143,500 tons Although surface mining on this scale is presently non-existent, it is deemed that future operations, in order to meet the increased energy demands, will have to look forward to much larger scale mining complexes. These tonnage requirements are meant to be used only for the delineation of general areas suitable for large-scale surface mining, termed "Strippable Coal Resource Regions." They were determined largely from the latest complete detailed coal resource estimates of the U.S. Bureau of Mines. Nine strippable coal resource regions, containing over 100 billion tons of strippable coal resources, were identified [(see Fig. 1)]. The delineation of these regions was based entirely upon estimates of surface-minable coal resources and the production design criteria for large-scale surface mining. If surface-mined coal was combined with underground production, or if smaller production rates were specified, then other areas which were omitted here would be included in the regions. Changing the outline of the regions, however, would not add any new mining situations to be studied in Phase II. Characterization of Coal Deposits The second subtask involved the general characterization of the coal deposits contained in the strippable coal resource regions. The geological information gathered

Jan 1, 1976

By C. M. White

CITIZENSHIP is a rather abstract subject on which a great deal could be said-a subject on which a great deal is said -and still one which too many of us seldom think about and seldom work at. Too many of us engineers and business men have but a vague idea of citizenship. We think that if we go to the polls on election day and obey the laws scrupulously, with the exception of an occasional traffic violation, we are pretty good citizens and are doing our duty by our city, state, and nation. But when you think it over, that&apos;s a very passive observance of the important right of counting oneself a citizen of a country. There is nothing very positive in that attitude. There is nothing that indicates that we have sufficient interest to really go out and do a job for the -welfare of our country, forgetting any personal advantages or inconveniences that might arise. In other words, this type of voting-on-election- day, law-abiding citizenship does not keep us awake a single minute; it does not take any particular thought or require the expenditure of any time or energy.

Jan 1, 1939

By G. L. Coleman, D. S. Hutton, W. C. Leslie

The occurrence of twins in a iron, generated during cooling through the ?-a transformation, is well established,1-8 but this phenomenon has been nearly ignored during the past 20 years. It is the purpose of this note to call attention to the prevalence of such twins and to illustrate their appearance. The work of paxton7 and Kelly8 has demonstrated beyond reasonable doubt that for Neumann bands (mechanical twins) in a iron the twinning plane is (112) and the twinning direction <III>. The agreement with McKeehan&apos;s earlier work4 on transformation twins indicates that both types of twins in ferrite follow the same twinning law. There is little doubt of this conclusion, but it could be strengthened by a microbeam X-ray determination of the orientation relationship between a single ferrite grain and a transformation twin within that grain, as in the technique used by Kelly8 on Neumann bands. RESULTS AND DISCUSSION Transformation twins, identified by their appearance on a polished and etched section, were found in

Jan 1, 1960

By W. A. Jr. Slippy, E. P. Dahlberg, R. B. Reed-Hill

A large room-temperature mechanical-hysteresis effect under cyclic tensile loading was observed in zivconium specimens prestrained at 77°K so as to form large numbers of (1121) twins. The observed hysteresis loss was a maximum when the prestrain was just under 1 pct It also depended strongly on the maximum applied cyclic stress, but only moderately on loading rate and temperature (-72°to 100°C). The phenotnena have also been studied in terms of the elastic aftereffect where the data has been found to cotlforln closely to the functional relationship between strain and time, c = -RT/a In tank ft. t to)/Zr, for strains cts large as about 10-4 This eyication can be derived directly from the strain-rate equation There may be important commercial implications to the present discovery since it appears that within rather wide limits it may be possible to obtain any desired magnitude of damping capacity in zirconium melal. The damping propevties may also be given directional characteristics. It is shown that the observed anelaslic phenomena can he explained on the assumiplion that they are the resuilt of stress-induced twin-boundary movements in which the average twin increases its thickness by only a few percent. In polycrystalline zirconium, a grain is least favorably oriented for slip when its basal plane, containing the (1130) slip directions, lies nearly perpendicular to the principle normal stress. Mechanical twinning is favored by this orientation and under simple tensile deformation at room temperature the primary twinning mode is {1012).&apos; The (1012) twinning shear is small (0.17) so that, during deformation, twin growth does not greatly enhance ductility. At 77°K, on the other hand, the predominant twinning mode shifts to {1121), and many thin (1121) twins can form at small strains.&apos; Twins thus nucleated can grow readily during subsequent room-temperature deformation and permit easy deformation in unfavorably oriented grains. In addition, the (1131) twinning shear is large: 0.63. These facts have lead to a process&apos; for greatly improving the room-temperature ductility of zirconium when it contains a sizable fraction of grains with basal planes nearly normal to the stress axis. Optimum results are obtained by slightly less than 1 pct prestrain. The effect is large so that a 50 pct elongation increase is readily attained. A large room-temperature mechanical-hysteresis effect has also been observed in zirconium specimens prestrained at 77°K. The present paper is concerned with some aspects of this effect which the experimental observations strongly indicate is primarily the result of strain-induced {1121) twin-boundary movements. This clearly suggests that mechanical twins formed by plastic deformation can cause anelastic effects similar to those previously observed2 for annealing twins and twins associated with phase transformations. EXPERIMENTAL PROCEDURES All specimens were prepared from arc-melted sponge zirconium plate stock as previously described,3 which has a preferred orientation with basal planes aligned parallel to and uniformly distributed around the rolling direction. Both lonti-tudinal and transverse tensile specimens, with axes parallel and transverse, respectively, to the plate rolling direction, were cut from this plate. In a longitudinal specimen most grains are favorably oriented for slip, while in a transverse specimen a large fraction are unfavorably oriented. Prestraining at 77°K was performed in two ways. In one, annealed zirconium plate stock was cooled in liquid nitrogen and then rolled in the transverse plate direction to strains varying from 0.5 to 12 pct. Cylindrical 1/8-in.-diameter by 1-1/4-in.-gage-length tensile specimens were machined from this material. In the other, previously machined tensile specimens were prestrained in tension at 77°K between 0.2 and 3.8 pct. Type FA 25-12 SR4 strain gages were cemented to all specimen gage sections. All tests were performed on an Instron testing machine of 10,000-lb capacity. EXPERIMENTAL RESULTS Fig. 1 shows a typical two-cycle room-temperature stress-strain diagram for a specimen prestrained 0.65 pct by rolling at 77°K. The maximum stress in both cycles was 14,500 psi. Note that in the first cycle the loading and unloading curves are unsymmetrical so that a residual strain, er, remains after unloading. In the second cycle the stress-strain curves form a nearly symmetrical hystere-

Jan 1, 1965

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By C. E. Shoenfelt, D. E. Winchester

NO important discoveries of petroleum during 1933 were reported from New Mexico. Lea and Eddy counties were the centers of activity during the drilling season and each had a number of interesting completions. The Hobbs pool, in Lea County, was definitely outlined on the east, north and northwest. Under an agreement reached last summer by state officials and operators, the Hobbs pool was continued under proration throughout the year. One hundred eighty-four units of 40 acres each were being produced at the end of 1933. The allowable was 21,306 bbl. daily at the beginning of 1933, but when the agreement was revised in the spring the minimum was raised to 30,000 bbl., and by the end of the year had been raised to 33,473 bbl. At present the field is being prorated on the basis of 25 per cent on acreage and 75 per cent on potentials except in the southwestern edge of the field, where water encroachment is a problem. In this area the basis of proration is 40 per cent on acreage and 60 per cent on potentials. A corrective method employed in this part of the field has been partly successful. The water is advancing in the upper part of the pay, a dolomitic limestone, and in a number of instances packers have been set in the pay below the water and above the oil. The locating of a satisfactory seat for a packer is difficult and in some instances has not been a complete success. Pipe line runs from the field during the year aggregated 11,413,218 bbl., bringing the total gross production up to 41,093,681 bbl., of which 39,000,-000 bbl. has been produced under proration, which went into effect on July 10, 1930. On Nov. 30, potentials were determined on the assigned pressure basis and the total was reduced 71,165 bbl. daily, to 1,265,-332 barrels. The outstanding completions in the Hobbs pool were three in number, of which the best was the Humble Oil & Refining Company&apos;s No. 3B Bowers in sec. 20, 18S., 38E., with an initial production of 11,664 bbl. of oil and 10,000,000 cu. ft. of gas. The Shell Petroleum Company&apos;s No. 4B McKinley, in the same section, produced at the rate of 22,940 bbl. of oil while flowing open, but when tubed, flowed at the rate of 6610 bbl. The third outstanding well, No. 4 Hardin of the Tidal Oil Co., and located in

Jan 1, 1934

By C. R. Fettke, Bela Hubbard

During the summer of 1916, while on a visit to the United States Agricultural Experiment Station at Mayaguez, Porto Rico, the writers were told by D. W. May, the director, that an occurrence of manganese ore had been reported from the mesa southeast of Mayaguez. A visit to the locality showed that the mesa is covered by a mantle of bright red soil resting upon serpentine. Here and there over its surface concretionary masses of limonite have been mashed out of this soil. These were apparently mistaken for manganese ore. On account of the similarity of this occurrence to the extensive iron deposits of northeastern Cuba, it was thought that a brief description based upon a two days&apos;reconnaissance survey of the area mould be of scientific interest. Mayaguez is on the west coast of Porto Rico, at Mayaguez Bay, which is the third in importance of the harbors of the island. The city itself is about 3/4 mile inland on the low-lying plain at the mouth of the

Jan 1, 1920

The Rio Tinto - Cerro Colorado operation was the first major cyanide plant built out of South Africa since the Carlin and Corte mills came on-stream in 1965 and 1969. Its flowsheet was presented in the original monograph, "Gold and Silver Cyanidation Plant Practice, " published in 1975, with a brief description of the plant but without the operating costs. The authors have recently received these data and it was believed worthwhile to present them in this volume along with the aforementioned flowsheet. The Cerro Colorado ore deposit is located at Minas de Rio Tinto in the province of Huelva, Spain, approximately 88 km (55 miles) north- west of Seville. The previously mined copper ore bodies lie on either side of the deposit which is mainly copper ore. The crest of the deposit is a capping of "gossan" containing hematite, limonite, gold, and silver. Separate facilities for primary crushing, concentration of copper ores and cyanidation of gold-silver ores are provided. Fine crushing is common to both ores. The run-of-mine open-pit ore is fed from a stockpile via a surge bin and apron feeder to a jaw crusher. After crushing to minus 150 mm (6 in. ), the ore is washed in a rotary scrubber to remove the clay material ahead of fine crushing. Minus 6 mm (1/4 in. ) screen undersize is pumped directly to the grinding circuit with the screen oversize being crushed to minus 19 mm (3/4 in. ) for feed to the primary ball mill; this is followed by two subsequent stages of ball mill grinding to 80% minus 43 microns (325 mesh). Grinding is with water only; no cyanide is used. After thickening, lime is added to the first two of seven Pachuca tanks for conditioning ahead of cyanide addition in each of the five remaining Pachuca tanks. This flowsheet indicates rapid cyanide consumption and the need to maintain a high strength cyanide solution for silver extraction. Agitation for dissolution of the gold and silver is followed by standard CCD practice employing four 67 m (220 ft) washing thickeners in series, with repulping between each thickener. A departure from American and Canadian practice is the use of Stellar filters developed in South Africa for pregnant solution clarification and recovery of zinc-gold-silver precipitates. The precipitate is treated with acid for zinc removal, the sludge filtered in presses, dried, calcined and smelted to produce dore bullion of 900 fineness containing 12% gold and 78% silver.

Jan 1, 1981

JOHN H. NELSON, Worcester, Mass.-At our plant we have done considerable work on notch-bar testing and are farther at sea now than when we started. So far, we have been unable to get the notch-bar test to be consistent with any other known test. Lately, I have been investi-gating the effect of the position of the notch-bar specimen in a, bar. To do this I took a 3, ½ in. square bar and quartered it, then heat treated the four quarters. Each of these pieces was again quartered and a specimen machined and notched. "In this way we would have notch-bar tests from the exterior to the interior of the bar. These were made of such lengths that it was possible to make four impact tests on each speci-men. Extreme care was taken in marking the position of these test speci-mens in the original bar. The notches were then cut with relation to position of the specimen in the original bar. The second notch was cut 90° from the first, and so on around the specimen. In this way, we have found that, with a 3 ½ in. bar of 0.4 or 0.5. per cent. carbon steel when properly heat treated, we could get impact values ranging from 15 to 100 ft.-lb. Just why this is the case we are unable to state; but it does appear to be a fact that along the outside of the original bar the notch-bar test seems to be low and increases toward the center, but it is not always consistent. For instance, we may have, on a single specimen; one notch-bar test giving us 15 ft.-lb. and another 100 ft.-lb. We have not found such inconsistencies in alloy steels. Alloy steel is consistently good or consistently bad. If it. is good, you cannot readily destroy the impact value, no matter what you do; if it is bad-that is, if it is a poor notch-bar steel-and you have sufficient latitude in your draw, you may correct it. In other words, if the hardness you are working to will allow you to draw to about 1050° F.(561° C.) or over and then quench this steel from the draw heat, you. can raise the im-pact value of the steel from about 4 or 10 ft.-lb. up to-40-or 50 ft.-lb: Just what occurs I do not know. There is evidently a critical-point in steels that have poor impact value, in the neighborhood of 1000 F. to 1050° F. (536° to 561° C.).

Jan 12, 1919

By E. C. Franz

IN an effort to understand high cycle fatigue, as well as to study the mechanism of fracture in general, a number of researches have been undertaken whereby the fracture properties of a metal have been determined under conditions of repeated cyclic prestsain employing high strains with relatively few cycles. Liu, Lynch, Ripling, and Sachs&apos; showed the effect of a definite strain history consisting of small increments of tensile or compressive prestrain upon the flow and fracture characteristics of metals after a limited number of repeated loadings. Liu and SachsW emonstrated by cyclic straining of the aluminum alloy 24s-T4 that the least reduction in ductility was obtained when the compressive stress was nearly equal to the tensile stress. Attempts have been made to correlate the reduction in ductility under such prestraining with conventional fatigue data, as was done by Liu and co-workers.&apos; The following research was conducted to determine if such reduction as has been noted could be correlated with conventional fatigue data or whether the effect resulted from causes extraneous to the basic mechanism of fatigue failure such as strain aging. It might be pointed out in this connection that the reduction in ductility has occurred in alloys that might be susceptible to strain aging or similar behavior, such as alloy 24s-T4. In the present investigation, the test specimens were prepared from the aluminum alloy 75s-T6 and annealed electrolytic copper. Alloy 75s-T6 is a complex precipitation hardenable alloy, whereas electrolytic copper would not be expected to exhibit strain aging effects, particularly at room temperature. The experimental procedure consisted of prestraining test specimens repeatedly by increasing tension in small increments to various total prestrain values, followed by testing to failure in a tension test. The prestraining as well as the final testing was performed on a tensile machine using special fixtures9 0 maintain concentricity of the specimens. After prestraining, the specimens were unloaded as rapidly as possible and immediately reloaded so that the total time lapse between strains was held to a few seconds. Logarithmic or true natural strain was used in all calculations. The results are presented in Figs. 1 and 2. In Fig. 1, the retained ductility, area after prestrain area at fracture is plotted against the tensile prestrain, initial area area after prestrain as abscissa with the number of stress reversals executed to attain the required prestrain plotted as parameter. Several specimens that fractured during

Jan 1, 1955

By James J. Bailey

Percussive drills have been in commercial use for many decades. Until relatively recently there was little serious effort to analyze the stresses in such devices in any detail. Within the last few years such analyses have been developed and have been reported by a number of authors.1-4 We present here an investigation of the impact systems of a family of conventional down-hole drills with optimization the objective. We have assumed that maximum drilling speed was the quality most desired and that this was to be achieved within conventional practice. In fact the methods that are demonstrated in principle below can readily be adapted to other percussive devices, whether conventional or not, and to other constraints. SOME PERFORMANCE PARAMETERS FOR PERCUSSIVE DRILLS Consider a percussive drill with an air motor operating with the following parameters: p-supply air pressure a-effective piston area W-piston mass S-piston stroke If we consider a simple (constant pressure) cycle, the following relationships can be derived. The blow frequency [N~ pa lie WS 377]

Jan 1, 1968

By W. F. Hower, W. Brown

Large-scale sand consolidation tests were conducted in an effort to determine the reasons for the successes and failures of this method of sand control. Several different consolidating materials were used in treating both clean and bentonitic sands that were packed in a chamber having a capacity of 3.3 cu ft. The results were essentially the same for all of the different consolidating materials, The data show that low-viscosity consolidating materials pumped at a relatively slow rate gave the best results. Where the formation has produced sand, the treating fluids can compress the formation, thus permitting the channeling of fluids to another horizon. Pressure-packing these zones before attempting to consolidate is recommended. Sands containing more than 4 per cent of water-swelling clays are not good candidates for consolidation. It is indicated that loose sand, particularly when it is bentonitic, can be fractured during the placement of the treating fluids. INTRODUCTION Sand production in oil and gas wells has plagued the industry for many years, and numerous cures for this problem have been suggested. Most methods have been successful to a certain degree, but the great variety of well conditions that exist in the different areas has magni- fied the problem and limited the successful use of the various systems. Four review papers1-4 present a wealth of information concerning the degrees of success that have been obtained by the different sand-control methods. The bridging of sand grains by the use of gravel packs and screens has been quite successful. However, these methods do not leave the casing clear for all types of multiple completions, and the cure does not last for the production life of the well in some instance:;. The control of loose sands by sand consolidation with resins has never been as successful as desired. It has always been hoped that such a treatment would eliminate all sand problems for the life of the well, but. initial applications, starting in the middle 1940&apos;s, were only moderately successful. Lott, et a1,3 reported a success ratio of approximately 50 per cent and made the following conclusions. The highest percentage of successes were obtained where: a. Consolidation of a zone was made at the time of initial completion or prior to the production of sand. b. The interval treated was less than 12 ft in length. c. Between 30 and 50 gill plastic/ft of producing interval was displaced through the perforations. REASONS FOR SAND CONSOLIDATION FAILURES Our own experiences in the field of sand consolidation point toward the following conditions as the major reasons for the failure of sand consolidation attempts. 1. Mud-plugged perforations and mud invasion of the formation. 2. Sand in the casing covering all or part of the perforations. This sand could be either formation sand or one of the coarser sands used as propping agents in hydraulic fracturing. 3. Holes in the casing. 4. Channels behind the casing. 5. Attempting to treat too long a perforated section. 6. Too high a percentage of water-swelling clays in the formation. 7. Formations that have produced sand. Recent attempts were made to treat perforated sections ranging from 10 to 30 ft, in wells that have produced sand, by using a straddle packer that was raised and lowered through the perforations as the consolidating material was being pumped. In most instances, the pressure required to pump fluid into the formation varied considerably as the tool was raised and lowered. This suggested the possibility that significant differences in permeability were present or that only part of the formation had produced sand. There were times when a sudden break in pressure indicated that a fracture was being formed. Research conducted several years ago concerning the problem of the control of water in air and gas drilling indicated that shale sections could be fractured quite easily. In addition, it was determined that it was easier to pump fluids into shale bodies by fracturing the shale itself, or the interface between the shale and sand, than to pump into a fluid-saturated formation. Formations that produce sand are usually adjacent to shale bodies and frequently have shale streaks of various thicknesses inter-bedded in the sand. Therefore, where shale is exposed to fluid pressure it

By W. W. Stephen, J. P. Walsted, W. J. Kroll

FOR the production of carbides, various furnace types are available, especially those using arc, resistance, and high-frequency heating. Selection of a specific means of heating depends primarily on the material to be treated and the physical properties of the carbide produced. In the present case, zirconium carbide had to be prepared on an industrial scale as a raw material for the production of anhydrous zirconium chloride. Considering that a rather expensive pure oxide was to be used, the arc-furnace treatment recommended for zircon sands in a previous publication&apos; was ruled out because of the considerable volatilization and dust losses caused by the blast of the arc. For this reason, either high-frequency or resistance heating seemed to offer more promise. Since there was not enough capacity of the former available, resistance heating was chosen. It was first thought that the Acheson silicon carbide furnace would be suitable for the present purpose, but the voltage in such a furnace, in which the current passes through the batch, varies from 220 to 75 v from the start to the end of a run. This variation is so great that a special tap transformer would have been required. Trouble was also expected by local melting of the carbide. Pure zirconium carbide melts at about 3527°C, but the melting point is brought down to 2427°C, according to Agte,2 when an excess of 6 pct C is present in the carbide. This we found confirmed by experiments in a high-frequency furnace. Excess carbon is needed in the batch to obtain a complete reduction. Fusion of the charge would cause great difficulties in an Acheson-type furnace because of the good electrical conductivity of the carbide as compared with that of the loose batch. Also, fused carbide is much more difficult to chlorinate than the spongy product that can be made in the radiation furnace described below. It was apparent that, to obtain a good-qual-ity zirconium carbide, the heat input would have to be well-controlled. The hairpin-resistor principle seemed to offer possibilities in this regard, and a furnace of this type was therefore developed. The advantages of the hairpin-resistor radiation principle have been discussed in previous publications, and a split-tube graphite-resistor furnace," now increasingly used in various laboratories, as well as a centrifugal quartz melting furnace4 of this type, has demonstrated the usefulness of this heating method. The hairpin-heater element has the following definite advantages over a straight resistor of the type used, for instance, by Georges:5 Its resistance is four times greater; it can expand freely; it is sturdier because of the larger diameter, and it has a larger radiation surface; there are no hot contacts that might wear out or overheat; only one clamp is used which permits assembling all electrical leads at one side of the furnace, making the other sides easily accessible to the operator. The shorter element and its larger diameter permit greater concentration of heat. The furnace developed is shown in fig. 1. The box (I), made of 2 1/2-in. graphite plates, has inside dimensions of 23x17x16 in. It contains the briquet-ted batch (2). The box is embedded in lampblack (3) up to the cover plate. The cover plate contains an opening for the gas escape (4) and for the observation hole (5), which permits measuring the temperature with an optical pyrometer. The cover plate is embedded in charcoal (6). The lampblack is contained in the insulating brick lining (7), held in the 1/4-in. sheet steel box (8). The graphite box is set on two rows of triangular graphite bars (9). The hairpin-heater element (10), the dimensions of which are given below the main drawing, extends horizontally in the graphite chamber and radiates freely on the batch. A graphite tube (11) keeps the lampblack from falling into the slot. The split electrode, which in reality is turned 90" against the drawing, is so arranged that the slot is vertical. The water-cooled packing gland (12) is insulated by an airgap from the heater element. A thin pipe (13)

Jan 1, 1951

By Lyall Zickrick

EXPERIMENTS of previous investigations have indicated that calcium-copper alloy, when used as a deoxidizer for molten copper, results in a sound copper casting of good physical and electrical properties. Bradenberg and Wiens1 have obtained successful results in casting sound copper using calcium for deoxidizing. Masing2 has obtained deoxidized copper of high density and high conductivity by use of calcium. Pratt,3 in 1907, patented the use of calcium for the deoxidation and degasification of, copper. Schumacher, Ellis and Eckel 4 in 1929, conducted a series of experiments on deoxidizing copper with calcium. They concluded that so long as there is only a small percentage of residual calcium the mechanical and electrical properties of the copper deoxidized are not impaired; and the deoxidation is thorough. For this investigation, a, copper-calcium alloy high in calcium and 10 variously deoxidized copper ingots were prepared. The investigation concerns itself with the casting properties and structure of these variously deoxidized ingots, their working and annealing characteristics, and the resulting physical and electrical properties of the worked materials.

Jan 1, 1932

By A. R. Troiano, A. B. Greninger

There is need for an adequate working hypothesis that would describe at least qualitatively the crystallographic mechanism for the transformation from austenite to martensite in steel. A general theory would not only be of great assistance in the correlation of existing data and in planning future experimentation, but would also form the basis for an eventual explanation of the property changes that accompany lattice transformations. The mechanism of martensite formation described in the following pages is the outcome of two new experimental determinations: (1) the accurate evaluation of the lattice relationship between austenite and individual crystals of martensite, and (2) the measurement and analysis of the change in position that a volume of austenite undergoes when it transforms into a crystal of martensite. For this latter study, the stereographic analysis of shear was employed; this method greatly simplifies the solution of lattice-shear problems, and some space is devoted to its description. Lattiice Relationships and Habits PREVIOUS WORK The lattice relationships between austenite and martensite in carbon steels have been studied by Kurdjurnow-and Sachs,&apos; and by Wassermann;2 and in iron-nickel alloys by Nishiyama.3 Wassermann,2 and Mehl and Derge.4 The studies by Kurdjumow and Sachs and by Wassermann were made on single (austenite) crystals of quenched 1.4 pct carbon steel, and the results of these two independent studies agree closely with the postulated lattice relationships: (III)r||(0ll)a [101]r [111]a [1] Both Nishiyama and Wassermann worked with an alloy of iron plus 30 pct nickel (all austenite at room temperature), and "martensitic alpha" was formed by cooling in liquid air. They agree that the lattice relationships for these conditions are: (lll)r||(011)a [112]r[011]a [2] Mehl and Derge worked with a range of iron-nickel alloy compositions centered about 30 pct nickel. They concluded that when the transformation takes place near room temperature or above, relationship [l] holds, but if the same specimen is made to transform at -195°C, relationship [2] obtains;intermediate temperatures evidently produced a combination of these two relationships. Sachs and co-worker~,1,7 as well as Nishiyama,3 have proposed transformation mechanisms for martensite formation.* Both of the mechanisms picture the transformation as initiated by shearing movements along the octahedral [Ill] plane of austenite, followed by suitable expansion and contraction to complete the transformation. These mechanisms have been described and commented upon by Mehl, Barrett, and Smith,8 Mehl and Derge,4 Wassermann,2 and others, and generally accepted by investigators in this field. Greninger and Troiano9 have recently published the results of a detailed study of the shapes and orientation habits of martensite crystals in plain-carbon and nickel steels. They found that, contrary to previous assumptions, martensite plates form not along the octahedral planes but along austenite planes of very high indices; these results were in line with those of previous studies of martensite reactions in nonferrous alloy systems by Greninger and coworkers.6,10 Greninger and Troiano concluded that the transformation theories of Kurdjumow and Sachsl and of Nishiyama3 are untenable. Phragmén11 reached a similar conclusion. EXPERlMENTAL METHODS The object of this particular study was the evaluation of (1) lattice relationship between austenite and martensite, and (2) relationship between the martensite lattice and the martensite plate. The technique used for solving these problems was similar to that used by Greninger6 on martensitic structures in 8 copper-aluminum alloys. Briefly, the method consists of grinding and polishing a specimen on a surface parallel to an individual martensite plate and thus exposing a single martensite crystal for an area of l to 3 mm. The orientation of this exposed martensite crystal is then determined by means of a back-reflection Laue X ray pattern.12 Another pattern is obtained from the matrix crystal, and a stereo-graphic plot of data from these two patterns then provides the solution to the problem. It is necessary to repeat this process on several crystals in order to determine whether or not the solution is unique.

Jan 1, 1950

By G. A. Colligan, G. L. F. Powell

A new experimental technique has been developed to study nucleation behavior in eutectic alloys. It is somewhat similar to that applied by Sundquist and Mondolfo1 but with the advantages that: 1) bulk samples are undercooled instead of small droplets thus allowing the thermal behavior to be monitored by a thermocouple immersed in the sample, and 2) nucleation behavior is investigated in the same sample on either side of the eutectic composition by adding additional component to the sample under controlled conditions which preclude the addition of nu-cleation contaminants. Sundquist and Mondolfo carried out ]nucleation ex-periments on a large number of eutectic alloy sys-tems and concluded that nonreciprocal nucleation operated. If one phase a was a good nucleant for the other phase 0, then B was a poor nucleant for a. This was determined experinlentally by comparing the nucleation temperatures of 100 to 300 u diameter droplets of hypereutectic and hypoeutectic composition cooled from above the liquidus and from a temperature between the liquidus and the eutectic temperature. Primary phase a was concluded to be an efficient nucleant for the other phase B, if the following experimental result was obtained. Referring to Fig. 1, the temperature TI at which a drop of hypereutectic alloy of composition B froze when cooled from above the B liquidus was noted. This was the nucleation temperature for B in the absence of a. A drop of hypoeutectic alloy of composition A was then frozen from temperature T2 between the a liquidus and the eutectic temperature. The temperature T3 at which the eutectic nucleated in the presence of the primary or proeutec-tic a was noted. If this temperature T3 was higher than the temperature TI at which the B nucleated in a hypereutectic alloy, it was concluded that the primary a had nucleated the 6. This temperature T3, representing a certain undercooling below the equilibrium eutectic temperature Te , was designated ?TB by a> the undercooling below T, for nucleation of 13 by a. If there was no substantial difference in nucleation temperature between the hypereutectic drop cooled from above the /3 liquidus and the hypo-eutectic drop cooled from a temperature between the a liquidus and the eutectic temperature, it was considered that the a nucleated B at an undercooling equal to or greater than that at which P nucleated from a hypereutectic alloy. Sundquist and Mondolfo1 found that faceted primary crystals were good nucle-ants for metals that grow as orthogonal dendrites when present as the primary phase. Jackson2 has questioned Sundquist and Mondolfo&apos;s technique and proposed that in Sundquist and Mon-dolfo&apos;s samples, such as composition A, primary a retained B in reentrant grooves at their surfaces when heated to a temperature above the eutectic but below the a liquidus. This objection was suggested by experiments with organic eutectics where reten-

Jan 1, 1970

By E. J. Nielsen, P. R. Strutt

A study has been made of the progressive changes in the distribution of etch-pit structures occurring during high-temperature creep in copper + 7 wt pct Al single crystals oriented with a [113] tensile axis. The two equally stressed glide systems with the highest Schmid factor would be expected to form subboundaries of the type predicted by Kear.2 The alignments of etch-pits on sections parallel to different (111} planes consistent with these types of boundaries were not observed. However, they were consistent with planar subboundaries (on a macroscopic scale). From an analysis of Amelinckx1 it may be shown that stable cross-grid dislocation boundaries may form in the primary slip planes. These boundaries form when dislocations with a Burgers vector not in the slip plane move into the plane by combination of climb and glide. THE geometry of subboundaries formed by the interaction of dislocations of two glide systems has been analyzed by Amelinckx,1 and the particular types produced by deforming fee crystals are predicted by ear.&apos; In this paper types of boundaries which may be formed when climb as well as glide occur are discussed as this is relevant in high-temperature creep. It is assumed in the present investigation that the etch-pits observed in Cu + 7 wt pct A1 on surfaces parallel to {111} planes delineate the sites of dislocations. Although there is no direct evidence for this previous work on a-Cu/Al single crystals by Mitchell, Chevrier, Hockey, and Mon-aghan,3 would show this assumption to be reasonable. The alignments of etch-pits which form during creep are studied on sections parallel to each {111) plane. It is then deduced that these alignments are consistent with a specific type of planar subboundary. The Cu + 7 wt pct A1 single crystals had a [113] tensile axis and Fig. 1(a) shows schematically the relation of the slip planes and slip directions (as represented by tetrahedron ABCD) with reference to the tensile axis. The two equally stressed glide systems with the maximum Schmid factor namely ß-AD and (a-BD, from the analysis of Kear,2 would be expected to form the boundaries shown in Fig. l(a) and (b), also Fig. 5(a) and (b). EXPERIMENTAL PROCEDURE The a-Cu/Al single crystals were grown and annealed in a "gettered" argon atmosphere. Chemical analysis showed the aluminum content to be uniform in each crystal and the difference between crystals was maintained to an accuracy of ± 0.25 wt pct. The initial dislocation density and mean subgrain diameter after annealing was -106 cm-2 and 250 µ, respectively. Surfaces parallel to (111) planes were produced by specially developed electrolytic machining processes. The {111} faces were next electropolished for 5 min in a solution consisting of 25 g chromium trioxide, 113 ml glacial acetic acid and 40 ml water; the applied potential was 8 v. Dislocation etch-pits were revealed using l an etchant described by 1 ml bromine, 45 ml HCl, and - 250 ml water. RESULTS In crystals strained into secondary creep at higher stresses (443 and 750 g - mm-2 at 650° C aligned rows of etch-pits parallel to slip plane traces were evident in sections parallel to the (1111, (ill), and (111) planes, see Fig. 3. As well as the longitudinal alignments in Fig. 3, well formed randomly oriented arrays indicative of an equiaxed subgrain structure are evident. At the lower stresses (100 to 230 g . mm-2) only an equiaxed structure formed during creep. The sections in Fig. 3 are from a crystal crept for 70 hr at 650°C with a CRSS of 443 g.mm-2. Two identically oriented crystals were also deformed at the same temperature and stress for 5 min and 4 hr. In the crystal crept for 5 min, the etch-pits were randomly distributed with no tendency for directional alignment, see Fig. 2(a). As shown in Fig. 2(b) aligned arrays were evident after 4 hr creep but they were not nearly so well defined as in Fig. 3. The alignments (parallel to the arrows) in Fig. 3 are consistent with the existence of boundaries in the two main slip planes a and ß. The way in which this is deduced is seen by reference to Fig. l(c), where the existence of boundaries in the a and ß planes is verified by sectioning parallel to a,ß, and d. The (111) and ß(111) planes intersect the d(111) plane along BC [101 ] and AT [011] and alignments parallel to [101] and [011] are clearly evident in Fig. 3(c) in a section parallel to the d(111) plane. Similarly the a, and ß planes in Fig. l(a) intersect each other along DC [110] and hence there will be an alignment parallel to [110 ] in sections parallel to the a-plane and the ß-plane; this is evident in Fig. 3(a) and Fig. 3(b). It is interesting to note that alignments of etch-pits consistent with the boundaries predicted by Kear2 were not observed; see Figs. l(a) and l(b). The geometry of boundaries in {111} planes as shown in Fig. l(c) is discussed later. In Fig. 4(a) the individual etch-pits are resolved and the alignments are exactly parallel to the slip trace direction [101]. However, in some areas alignments deviate away from the slip trace direction by as much as 10 to 15 deg, this is evident in Fig. 4(b), and in Fig.

Jan 1, 1969

By Howard Martens, Pol Duwez

XPERIMENTS were performed on a Cr-Fc alloy Econtaining 44.7 pet Cr in order to determine the heat evolved during the transformation of the a solid solution into the s phase, and the change in volume accompanying the transformation. Since previous measurements on the rate of formation of a from s indicated that the reaction was quite fast as soon as the equilibrium temperature of 820°C was exceeded by some 50°, standard thermal analysis experiments were performed on heating specimens of s at the rate of approximately 40°C per sec. A definite thermal arrest was observed at 870"C, Fig. 1. This result indicates that the reverse seaction of into a is exothermic. From the heating curve of Fig. 1, taking 15°C per sec as the heating rate in the neighborhood of the transformation, 2.4 sec as the time for transformation, and assuming that the specific heat of the alloy at 850°C is an average between iron and chromium, namely 9.5 cal per mol per "C, the latent heat of transformation is approximately 342 cal per mol. The order of magnitude of this latent heat was also obtained by comparing the heating curve of Fig. 1 with a similar curve obtained with pure iron under identical experimental conditions. It was found that the length of the thermal arrest for s was about 1.8 times as long as that for iron. Since the latent heat of the a to 7 iron transformation is 203 cal per mol1, 2 the latent heat of it to a would be 365 cal per mol, which is in relatively good agreement with the value determined from the heating curve. For the determination of volume change, thermal expansion curves were recorded using a specimen containing 44.7 pet Cr and completely transformed to cr by previous treatment. The curves were recorded at a rate of heating of about 4°C per min and at approximately 840°C a sharr, increase in length of about 0.08 pet took place. Fig. 2. It is therefore established that the specific volume of a near the transformation temperature is about 0.24 pet smaller than that of a, and consequently, when the s phase forms in an a matrix, it would tend to shrink away from the matrix. Since the s phase is known to be extremely brittle, these results offer an explanation for the microscopic cracks often observed in the a phase under the microscope. The results of this study are in qualitative agreement with previously published data on stainless steel 19-9DLa and on a Cr-Fe alloy containing 45 pet Cr.&apos; The increase in density due to the transformation from n to s given in ref. 4 is 0.90 pet. These measurements, however, were made at room temperature. whereas the presently reported 0.24 pet is the change at the temperature at which the transformation takes place during heating. In the graph of Fig. 2, the percentage change in length that would be observed at room temperature is given by the length X, which is about 0.27 pet. This would correspond to 0.81 pet in volume change. Acknowledgment This work was done at the Jet Propulsion Laboratory, California Institute of Technology, under Contract No. DA-04-495-ORD-18 with the Army Ordnance Corps, Washington, D. C. The authors wish to thank this agency for permission to publish the results of this investigation. References I H. Klinkhardt: Measurements of True Specific Heats at High Temperatures. Annalen der Physik (1927) 84, pp. 167-200. - H. Esser and W. Runghardt: Influence of the Method, of Dctcrmination on the Measured Heat Content of Iron. Archtvo ffur Dct Eisenhiittenwesen 11934) 8, pp. 37-38. J. J. Gilman, P. K. Koh, and 0. Zmeskal. Delta Ferrite Formation and its influence on the Formation of Sigma in a Wrought Heat Resisting Steel. Trans. ASM 1 1949) 11, pp. 1371-1388. 1 J. M. Thomas: Discussion of ref. 3. Trans. ASM (1949) 41, pp. 3 390-1392.

Jan 1, 1957