Search Documents

By R. J. Mellen

IN a chloridizing roasting and cyanidation plant treating a manganese-silver ore, certain experiments pointed out the way to an improvement in roasting conditions by a change in the degree of crushing. The following short article is simply a description of the various changes that were necessary throughout the plant and of the results obtained. There is nothing unusual in these changes but they are of some interest in that they constitute a good many of the alterations usually resorted to in increasing production. In the beginning, the changes were brought about by an experiment that was not successful, but which clearly pointed to means of improving the operation, and is an example of the fact that often experimental work may result in failure and still be of value in arriving at correct fundamentals. This experiment also shows how far a metallurgist can get out of line in his deductions, particularly in a field with which he is not thoroughly familiar. The ore at the plant of Compania Minera Kildun y Anexas is crushed through a 13-in. gyratory, a 3-ft. standard Symons cone crusher and a set of 16 by 42in. rolls, the latter in closed circuit with two Tyler 400-mesh screens. The crushed ore is then conveyed to two fine-ore bins. These provide storage and feed for two 6 by 90-ft. kiln roasters, which discharge directly to coolers. The coolers in turn discharge to a 6 by 12-ft. ball mill, where the ore is ground for cyanidation. Laboratory and pilot-plant tests previous to the mill construction had indicated that minus ¼ -in. crushing was satisfactory for roasting, although results did not vary greatly with some coarser or considerably finer crushing. The plant was designed for a capacity of 300 tons per day on this basis. After a few months operation, the initial operating problems were overcome and the anticipated milling rate was reached but the results being obtained were not really good. The plant seemingly did not have much excess capacity in any department but the roasting operation was the most critically limiting factor both as to tonnage and the results obtained. If this could be improved there seemed some possibility of improving the total tonnage rate to some extent. Segregation of the calcine into various screen sizes showed that the coarser sizes ,were not giving the expected recoveries. In all of the laboratory and pilot-plant testing, any limiting conditions as to the percentage of salt used, temperatures, feed rates, etc., had affected the fine material more than it had the coarse, and even in making laboratory tests at this time the mill conditions could not be exactly duplicated. Further laboratory testing indicated that a segregation of the crushed ore into a coarse and fine product for roasting might result in some improvement in roast-

Jan 1, 1945

By C. A. Allen

FOR over three years we have been endeavoring to reduce the number of fatalities and minor accidents in Utah. The physical condition of the o? Represents the average of 4 States mentioned excluding the catastrophes indicated. FIG. 1.-NUMBER KILLED PER MILLION SHORT TONS OF COAL PRODUCED IN COLO¬RADO, NEW MEXICO, UTAH, WYOMING, AND BITUMINOUS MINES OF THE UNITED STATES, 1914 TO 1920. mines, concentrators, and smelters is good, yet the number of accidents,

Jan 5, 1922

By Lucius W. Mayer

WHILE the mind of the financier does not normally run along channels similar to those of his technical adviser, engineers, because of their exactness, are ever more called upon to manage affairs where financial matters are involved. It is, true, not a relatively large number have thus far functioned in this capacity. It is also true that the essentially financial mind could not serve in a responsible engineering position; for to be a successful engineer one requires precise thinking, making due allowance for factors of safety. To be a financier seems to require less aptitude for exact thinking than of enthusiasm and confidence in capitalizing prospective possibilities. Both require imagination, the engineer being, more conscious of the limitations of natural conditions. It is to be regretted that the engineer' stands so far aloof from financial matters. Many consider them- selves successful, as did Steinmetz, as long as their reward is the consciousness that they are giving supreme service to mankind. They are 'generally happy in their work and, like our honored brothers who are teachers, gain their greatest satisfaction, not in the amount of their remuneration so much as in the service rendered society and in the excellence of results achieved. Indeed, these sentiments bespeak character and command respect.

Jan 1, 1924

By G. Das, S. V. Radcliffe

The substructural features developed in tungsten as a function of annealing temperature (up to 2200°C) and type of material [undoped and doped powder metallurgy (PM) tungsten and electron beam melted tungsten] have been investigated by transmission electron microscopy. For doped PM tungsten wires, characteristic "par-ticulate" substructural features developed rapidly with increase in annealing temperature above 700°C. The features consisted of parallel rows of elongated or circular shapes (500 to 1000A diam) lying along the direction of the wire axis and were identified as internal voids by diffraction contrast experiments. In recrystallized doped PM rod, larger voids were observed and were identified by precision dark field analysis to be cubic in shape and bounded by (100) planes. In marked contrast with both the doped PM materials, recrystallized undoped PM rod exhibited only very occasional and randomly arranged voids. Furthermore, no voids were observed in either material after electron beam melting. The high concentration of voids in the doped PM materials is attributed primarily to vaporization of doping additions or their pvoducts situated at the original grain boundaries , whereas the few voids in undoped material are considered to be traces of microporosity which were not eliminated during sintering. A tentative mechanism is suggested for the dezlelopment of the voids in relation to the processing sequences (sintering and working) and to the subsequent annealing. In recent years, a characteristic substructural feature consisting of rows of small elongated or circular regions of light contrast lying along the direction of working has been seen in thin foil electron microscopy studies of annealed sheet, wire, and rod tungsten. These features were present in the published micrographs of sheet by Weissmann et al.1 and of wire by Meieran and Thomas2, although the authors did not draw attention to them. Wronski and Fourdeux3 observed similar features in sintered rod tungsten (it was not specified whether or not the material was doped*) and interpreted them on the basis of their ap- particles, based on extraction replica evidence from the fracture surface of the initial hot-rolled slab material from which the sheet was prepared. No diffraction contrast experiments on the features were reported in any of these studies. The present investigation was undertaken with the primary objectives of: a) identifying the nature of these substructural features in tungsten by electron diffraction contrast experiments, since the contrast for voids can be expected to differ from that for crystalline or glassy particles, and b) elucidating the origin of the features and their development. For the latter purpose, doped and undoped powder metallurgy tungsten was obtained as rod and wire to represent different stages of reduction during final processing. These materials were examined both in the as-processed condition and after annealing to successively higher temperatures. In addition, the same doped and undoped materials were examined after vacuum melting in rod form. I) MATERIALS AND PROCEDURE Doped powder metallurgy (PM) tungsten wire (commercial purity 99.9 pct W) was obtained in the as-drawn and surface ground condition (0.030 in. diam "ground seal rod"). Doped and undoped tungsten rod (0.075 in. diam) representing an earlier stage of final processing was obtained from the same commercial source (Refractory Metals Division, General Electric Co.). Lengths of both the doped and undoped rod materials were single-pass melted in an electron-beam zone refiner to examine the effect of vacuum melting on the substructure. Annealing was carried out in a tungsten crucible in a tantalum strip resistance furnace under a vacuum of l0-15 mm Hg. Longitudinal sections of the wire and rod materials were examined by light and electron microscopy. The preparation of thin foils suitable for electron transmission from 0.030 in. diam tungsten wire and the rod specimens was carried out by means of a high-precision microjet technique developed to provide lack of jet stability and precise control of the area thinned. The method is described in detail elsewhere.' The foils were examined in a JEM 6A electron microscope using a goniometer stage (±20 deg tilt, 360 deg rotation) and operated at 100 kV. To minimize contamination problems a 200 µ condenser aperture was used in conjunction with a useful beam current of 50 µA. II) RESULTS AND DISCUSSION A) Diffraction Contrast Analysis. In order to determine the optimum conditions for the development of the substructural feature, a series of isochronal 30 min annealing experiments were carried out on specimens of the doped PM tungsten wire. The transmission electron microscopy analysis showed that the as-drawn wire, Fig. 1(a), consists of 'fibers' whose long axis is closely parallel to the wire axis of (110). The fiber width averages some 0.5 µ. Dense disloca-

Jan 1, 1969

By T. Y. Yan, W. F. Espewheid

The various ion exchange reactions occurring during restoration of formations contaminated with ammonia during in situ uranium leaching are reviewed. Data are presented on the restoration of a previously leached laboratory packed column wing lime saturated brine. Although this restoration fluid selectively and effectively removed the ammonia, 24.5 pore volumes are required to reduce the ammonia concentration from 500-3 mg/L (29- 0.18 gr per gal). The essence of NaCl in the restoration fluid at levels in formation water is beneficial in improving the selectivity of the system for NH4+ removal and reducing Ca + + ion consumption

Jan 1, 1984

[NUMERICAL CODE TO MAPS (Region Listed in Roman Numerals after Each Petroleum Section) 1 Alaska 2 Arizona 3 Black Hills 4 Boston 5 Carlsbad Potash 6 Central Appalachia 7 Chicago 8 Cleveland 9 Colorado 10 Columbia 11 Connecticut 12 Delta (VIII) 13 Detroit 14 East Texas (VI) 15 El Paso 16 Gulf Coast (VII) 17 Kansas (IX) 18 Lehigh Volley 19 Mid-Continent (IX) 20 Minnesota 21 Montana 22 Nevada 23 New York]

Jan 1, 1961

By E. R. Gilbert, D. E. Munson

Creep of copper under 75 to 1.50 kg per sq cm stresses at temperatures near the melting point was found to he a complex reaction controlled by three mechanisms acting in parallel. In order of appearance with decreasing temperature, the auerage activation energies, Qc , are 168, 79, and 24 kcal per mole. Stress dependence of the minimum creep rate was found to he an exponential for the two high-Qc processes and a power law for the low-Qc, process. Transition of control occurs from one mechanism to another. The relative transition temperature depends upon the applied stress, and the range oiler which the transition occurs depends upon the difference in the activation energies of the mechanisms. The creep behavior at high temperature is explained by the climb of dislocations through thermally or mechanically formed jogs, CREEP in pure fcc metals at temperatures in excess of one half the absolute melting point is normally controlled by dislocation c1imb.1,2 A climb model which seems applicable, according to an extensive analysis of data,3 was derived by Weert-man.4 This model assumes jog-saturated dislocations and predicts an activation energy, Qc, nearly equal to that for self-diffusion, USd. Although the requirement of jog saturation is restrictive, agreement between theory and experiment seems adequate. Many other theoretical treatments, including an early model by Mott,5 include detailed consideration of jog formation as an initial requirement for climb. These models predict activation energies for creep which differ from those of self-diffusion. Seeger6,7 postulates an observed activation energy related to the stacking-fault energy. Thus, Usd <Qc<5Usd + Uj where Uj is the jog-formation energy. Seeger incorporated qualitatively the influence of the relative numbers of thermal and athermal jogs. Expanding this concept, Shoeck8 explicitly states a function based on formation mode and relative numbers of vacancies: e r ci exp {-uf/k T} exp {-Um/k T} [ 1 ] where Uf and Um are energies of vacancy formation and migration, respectively. The concentration of jogs, Cj, depends upon the manner of jog production. For intersection jogs, Cj is not sensitive E. R. GILBERT, Junior Member AIME, formerly with De- to temperature; for thermal jogs, Cj is proportional to exp {—Uj /k T}. Schoeck regards each mode as a distinct mechanism; therefore, the mechanisms may act together.299 The diversity predicted by theory, surprisingly, has not been substantiated by experimental results. A significant investigation must include the extremes in stacking-fault energy. Extensive creep studies of aluminum10 and nickel,11,12 high stacking-fault energy metals, have been made. Comparable studies on a low stacking-fault energy metal, such as copper, have not. It is the purpose of this paper to report the results of an investigation of the creep of copper under conditions which favor thermal jogs. EXPERIMENTAL Cylindrical compression creep specimens (0.240 in. in diameter by 0.400 in. long) were machined from cold-drawn rods of electrolytic tough-pitch copper containing 0.0007 Mg, 0.002 Fe, 0.001 Ni, 0.0005 Ag, Cd < 0.005, and Pb < 0.005 wt pct impurities. Undetected spectrographically was a nominal 0.04 wt pct 0, which occurs as a Cu2O constituent distributed discontinuously at grain boundaries. Vacuum annealing at 900°C for 15 min produced a stable 0.03-mm average grain diameter. Testing was carried out using apparatus similar to that described by sherby,13 modified by enclosing platens and a push rod in a vacuum cylinder. Normally this arrangement resulted in pressures less than 10 Only a slight surface tarnish, less than 0.0005 in. in thickness, occurred during the test. The applied stress, corrected for atmospheric pressure, was maintained within 2 pct of the desired true stress by the addition of lead shot at fixed strain increments. Creep strain was measured with dial gages as a relative displacement of the upper and lower platens; accuracy of measurement was 0.0001 in. Two creep-test methods were used, the differential or cyclic temperature14 and the isothermal, to obtain creep data at stress levels of 150, 100, and 75 kg per sq cm over the temperature range of 620° to 1032°C. Minimum creep rates were used from both test methods; this was considered proper because comparable temperature tests or cycling to the same temperature gave the same creep rate, within experimental error. The cold vacuum test chamber, with the unstressed specimen in place, was heated to temperature by placing a preheated furnace over the chamber. Temperature equilibrium was attained within 30 min. For the cyclic tests, the stress was removed during the 5 to 10 min necessary to effect the temperature change and re-

Jan 1, 1965

By A. Gemperle

Electron diffraction and transmission electron microscopy on foils at room temperature were used to investigate the ordering of Fe-Si alloys containing 10 to 23 at. pct Si. A certain degree of DO3 order was found in all alloys. With the exception of the lowest silicon concentration for which the antiphase domains could not be clearly resolved, the alloys have a domain structure of two-domain type with boundaries having 1/4a01<111> displacement vectors for less than 12.3 at. pct Si and with boundaries having 1/2 a0<100> displacement vectors for more than 12.3 at. pct Si. The alloys with 12.3 at. pct Si have a domain structure consisting of fine domains with 1/2a&apos;o<100> boundaries within much larger domains with 1/4a&apos;o<111> boundaries. The development of these structures can be explained by transition of the alloy from the disordered state into the B2-type order and then into the D03-type order by the mechanism proposed previously for the FeSAl alloys. The existence of the B2 structure in the lower part of the investigated concentration range reported in some articles can be explained by fine domains with 1/2a&apos;o<100> boundaries formed by several disordered planes within large domains with 1/4a&apos;o<111> boundaries. The ordered structure predicted by the theory —with practically no domain boundaries —is found in the alloys having 12.3 at. pct Si where it develops in the B2 structure region. ORDERING in Fe-Si alloys was first studied by phragmenl who found that beginning with 13 at. pct Si the DO3 (Fe3Si) superlattice reflections appear in the diffraction patterns. The equilibrium diagrams constructed later by corson2 and Haughton3 from various measurements proposed the existence of a homogeneous solid solution (a phase) in the range from 0 to 25 at. pct Si. Jette and Greiner4 and Farquhar et al.5 measured the relation between lattice parameter and composition and they considered the break in the curve at 9 to 10 at. pct Si to be caused by the ordered solution a"(Fe3Si). Glaser and Ivanick6 Determined critical ordering temperatures of the alloys containing from 10.9 to 27.9 at. pct Si from the measurement of the electric resistivity of quenched samples. In all cases the critical temperature was lower than the melting point and it was highest for 25 at. pct Si. Lihl and Ebel7 measured the lattice parameter curves at various temperatures up to 1000°C. The region between two breaks on these curves, corresponding to 10 to 12.5 at. pct Si at room temperature, was considered by them to be two-phase (a + a"). They concluded by extrapolation of the measured values that a" in the alloy having 25 at. pct Si is stable up to the melting point. Davies8 studied superlattice reflections in the X-ray diffraction patterns of an alloy containing 8.7 at. pct Si. He found the B2 structure and short-range order in the slowly cooled samples and the DO3 A. GEMPERLE is Research Scientist, Institute of PhysicS, Czechoslovak Academy of Sciences, Prague, Czechoslovakia. __Manuscript submitted January 2, 1968. IMD structure in the quenched and annealed samples. This investigation first reports the presence of the B2 structure, phase a&apos;: in Fe-Si alloys. Meinhardt and krisement9,10 also found its existence in Fe-Si alloys by neutron diffraction. No order was detected by them in the alloy containing 8 at. pct Si. The onset of B2 order was observed at a composition of 9.2 at. pct Si. They found almost perfect B2-type order with partial DO3-type order at room temperature in the 10 to 12.5 at. pct Si range and almost perfect DO3-type order in the 12.5 to 25 at. pct Si range. They established the critical temperatures Tc of both the structures through measurement at higher temperatures. The critical temperature for the B2 structure was found to be always higher than the critical temperature for the DO3 structure of the same alloy. They extrapolated the curves of the critical temperatures and concluded that the alloys with more than 17 at. pct Si have the B2 structure up to the melting point and the alloys with more than 23 at. pct Si have the DO3 structure up to the melting point. The results of Meinhardt and krisement9,10 were confirmed by Dokken&apos;s measurement" of the temperature dependence of the electrical resistivity in the 10.8 to 15 at. pct Si range. On the other hand chessin12 detected by X-ray diffraction a considerably lower degree of order in the 12.7 at. pct Si alloy. ANTIPHASE DOMAIN STRUCTURE IN ALLOYS WITH B2- AND DO$-TYPE ORDER The ordered structures B2 and DO3 can be described in terms of a subdivision of the bcc lattice into four fcc sublattices with a parameter double that of the bcc lattice. Following Marcinkowski13 we will label them I. 11, 111, IV. The B2 structure in the AB alloy is formed by placing A atoms on sublattices I and II and B atoms on sublattices III and IV. In a non-stoichiometric perfectly ordered alloy having concentration (A) > (B), A atoms occupy sublattices I and 11. and A and B atoms distributed at random occupy sublattices III and IV. The DO3 structure in an A3B alloy is formed by placing A atoms on sublattices I, 11, and 111, and B atoms on sublattice IV. In a nonstoichiometric, perfectly ordered alloy having concentration (A)/3 > (B), A atoms occupy sublattices I, 11, and 111, and A and B atoms distributed at random occupy sublattice IV. As further shown in Ref. 13, two types of domains are possible in the B2 superlattice and the antiphase domain structure has associated with it boundaries with displacement vectors 1/4 a&apos;o<ll1> only. Four types of domains are possible in the DO3 superlattice and the antiphase domain structure has associated with it boundaries with displacement vectors 1/4a&apos;o<111> and 1/2a&apos;o<l00>. Bethe14 suggested on the basis of theoretical considerations that in a structure with two sublattices at low temperatures only one domain should be present in the whole crystal at equilibrium. Similarly Bragg15 concluded that at low temperatures the domain struc-

Jan 1, 1969

By Don M. Jackson, Robert W. Howard

Techniques for the epilaxial growth of single -crystal silicon carbide films on silicon were developed. The vapor-phase decomposition and bydrogen reduction of silicon tetrachloride (SiC14) and Propane (C3H8) resulted in clear films of silicon carbide, lip to seveval microns in thickness. The growth took place in a horizontal . silicon epilaxial reactor at 1100°C (pyrometer) at a rate of- 3000Å per minute. Electron diffraction and X-ray diffraction studies demonstrated that the films were single-cyrstal, ß -phase, or cubic silicon carbide. SiO2 film were used to mask areas of the silicon sur-lace in order that the silicon carbide might be grown in controlled geometries. Both n- and p-type films were grown on p-type silicon waters.. Heavily doped silicon films of the same conductivity type as the silicon carbide films were deposited over the silicon carbide in order to affect better probe contact to the structures. when n-type silicon carbide mesas were grown on p-type silicon substrates the de vollage-current relationships between films and substrates were that of junction diodes. These diodes showed a sensitivity to while light ill that the incident light increased forward- and reverse-satro,ation currents, P-type silicon carbide mesas grown on p-type silicon were ohmic rather than rectifying in their voltage -current relationship. No conclusions could he reached concerning heterojunc-tiou rectification in the structure. SILICON carbide is a semiconductor with many interesting properties. It decomposes at temperatures above 2200°C.1 It occurs in two general crys-tallographic forms—hexagonal (a Sic) and cubic (ß Sic)—with the cubic form having a forbidden-gap energy of 2.32 ev and the hexagonal form (specifically the 6H polytype) a gap energy of 2.86 ev.3 It behaves as an extrinsic semiconductor at temperatures approaching 5003C. It has been shown to have a high resistance to radiation damage4 and p-n junctions formed in Sic have been shown to radiate visible light under forward- or reverse-bias conditions. Epitaxial silicon carbide on silicon carbide has been successfully grown through the use of a variety of techniques, such as gaseous cracking of SiCL4 and CC4, nearly all of which require a deposition temperature above 1500°C.6 This paper will cover very recent work on the gas-phase deposition of highly ordered films of silicon carbide on high-quality silicon single-crystal substrates. The films have been shown to ex- hibit junction-rectification properties when geometrically isolated regions are electrically biased with reference to the silicon substrate. There will be no discussion of the mechanism of heterojunction rectification, but the methods of film fabrication, geometry control, and structural evaluations will be covered in detail. Electron diffraction, X-ray diffraction, and diode electrical properties were used to characterize the films and the junctions. GAS-PHASE DEPOSITION OF Sic The techniques for the deposition of silicon carbide films were a logical outgrowth of the standard silicon epitaxial process. The major premise followed was that, for any film to nucleate in an ordered fashion where there is considerable mismatch in lattice parameters (in this case 22 pct), an extremely clean, damage-free substrate surface must be presented to the gas stream. Thus a standard gas-phase HCl etching step was used to prepare the substrates for growth. A minimum of 5 µ of substrate-surface material was removed prior to the deposition of Sic overgrowth films. The techniques used for growing silicon carbide films were those of growing silicon alone, with the added injection of a hydrocarbon gas into the hydrogen and silicon tetrachloride gas stream. The hydrocarbon gases used thus far have been research-grade (99.99 pct) methane (CH4) and propane (C3H8). Propane ultimately gave the best results. The gas flows were controlled through a panel shown schematically in Fig. 1. A hydrogen main stream of 30 liters per min passed through the horizontal quartz-tube epitaxial reactor, while SiC14, C3H8, HC1, and doping gases were injected as side streams. The

Jan 1, 1965

By Howard Martens, Pol Duwez

IN two papers published in 1949, alloys of chromium with the refractory metals tungsten, molybdenum, tantalum, and columbium were investigated in view of their possible use as high temperature resisting materials. For the Cr-Ta system, a partial phase diagram was presented and the only intermediate phase was identified at Ta2Cr3. A phase of the same composition was also observed in the Cb-Cr system. The X-ray diffraction data presented in these papers, however, were insufficient for crystal structure determination. It is shown in the present study that the only intermediate phase in both the Ta-Cr and the Cb-Cr systems corresponds to the ideal stoichiometric ratio TaCr2, or CbCr2. Both structures are cubic, MgCu, type. At high temperature, however, TaCr2 has a hexagonal MgZn, type structure, which can be retained at room temperature by fast cooling. The alloys were prepared by melting in a helium arc furnace on a water-cooled plate. The design of the furnace was essentially the same as that described in ref. 3. Some alloys were also obtained by sintering compacts made of the mixed powders pressed at 80,000 psi. The sintering was carried on for 4 hr at 1375°C. The tantalum and columbium powders were supplied by Fansteel Metallurgical Corp., North Chicago, 111. The tantalum powder was the reagent grade, with a particle size smaller than 400 mesh and a total impurity content less than 0.1 pct. The columbium powder was smaller than 325 mesh and contained approximately 0.1 pct C and traces of Fe, Ti, and Zr. The electrolytic chromium powder from Charles Hardy, Inc., New York, was smaller than 300 mesh and contained about 0.1 pct Na, 0.05 pct Ca, and traces of Cu, Al, Mg, Si, and Co. Powder diffraction patterns were obtained with a 14.32 cm camera, using copper Ka radiation filtered through nickel foil. The powder pattern of the TaCr2 alloy obtained by sintering at 1375&apos;C was different from that obtained on the same alloy rapidly cooled from the melt. Contrary to this result, the powder pattern of CbCr2 was the same, whether the alloy was made by sintering at 1375°C or by melting, and was similar to that of the TaCr, sintered. It was also found that the structure of the TaCr2 specimen obtained by melting was retained after heating for 4 hr at 1590°C, but transformed into the structure found in the sintered specimen after heating for 4 hr at 1375°C. Hence, the structural change of TaCr2, appears to be a reversible polymorphic transformation. CbCr2 and ToCr2 Structure, Low Temperature Form By using large scale Hull-Davey charts, the powder pattern of CbCr, and of the low temperature form of TaCr2 were readily interpreted on the basis of a face-centered cubic lattice with a parameter of approximately 6.95 kX. The indices of the reflections together with the values of sin&apos; 0 are given in Tables I and 11. From this list of observed reflections, it appears that the (200), (600), (024), (046), and (028) reflections are missing. The lack of (h00) reflections for h 4n indicates a four-fold screw axis. The missing (Okl) spectra for k + 1 An indicate the existence of a diamond glide d. The combination of these symmetry elements can be found in the O— Fd3m space group, which is therefore the most probable one. After having determined the approximate density of TaCr, by the immersion method, the number of molecules per unit cell was calculated and found to be nearly eight. This information, added to the fact that the most probable space group is O leads to the consideration of a structure of the MgCu2 type, in which the atoms have the following positions: 8 magnesium in a and 16 copper in d. On the basis of this structure, intensities were computed by means of the usual formula: 1 cos&apos;20 I a sin2 cos where F is the structure factor; 8, the Bragg angle: and p, the multiplicity factor. As shown in Tables I

Jan 1, 1953

By E. DeGolyer

I. INTRODUCTION VOLCANIC origin. was among the first of the theories advanced to account for the occurrence of the salt domes of the Gulf coastal plain, northern Louisiana., and eastern Texas, and it is still being re-stated in various forms by the most recent contributors to our knowledge of the geology of such deposits. Argument has been largely by analogy and attention has repeatedly been called to the Mexican oil fields, particularly those of the Tampico-Tuxpam region, because of the occurrence of oil in close proximity to volcanic plugs in those fields, an occurrence supposed to have some resemblance to the common occurrence of oil in the salt domes of the United States. The author, having spent several months of the past year in a general study of salt domes and in a detailed study of certain domes in the United States, and having been acquainted for some time with the exploration of similar domes in the Isthmus of Tehuantepec region, Mexico, and with the general geology of the Tampico-Tuxpam region, Mexico, has reviewed the various theories of volcanic origin for salt domes which have been advanced to the present time. The purpose of this paper is to present such review and to discuss the supposed Mexican analogy.

Jan 5, 1918

By W. C. Muehlhof, L. D. Lamont

THROUGHOUT the anthracite industry&apos;s history, the problem of handling and dis¬posing of refuse material has been one of major importance. In the early days of the industry&apos;s activities, only the large sizes of anthracite were satisfactory for market requirements and the smaller sizes were deposited as refuse. As time went by, more efficient coal-burning equipment was developed and a market demand was created for the finer sizes of coal. This demand made it possible to recover market¬able coal from banks deposited as refuse in the earlier days of mining. The same condition holds good today and we can see a definite trend toward the objective of utilizing the No. 4 and No. 5 buckwheat sizes. Under present conditions, we know that a limited market exists for No. 4 and 5 buckwheat; we know that the finer sizes of anthracite can be burned as pulverized fuel; we know that these fine sizes can be processed and sold as bri¬quettes, and we also know that the heat content of these fine sizes of coal is compar¬able with that of the sizes now merchan¬dized. Therefore, it should be the objective of the industry to conserve these fine sizes of coal in such manner that if and when processing facilities are developed, and market demands exist, the material can be salvaged and made available to meet these demands. From the standpoint of economical future reclamation, the ideal method of disposing of refuse containing the finer sizes of coal is to deposit it in banks separate and apart from other breaker refuse. By this procedure, the minimum amount of material will be processed in future salvage operations to recover the No. 4 and No. 5 buckwheat sizes. Many collieries in the anthracite region are operated under leases that have a specific term. These lease agreements provide that, upon expiration of the lease by term, exhaustion or otherwise, the ownership of the refuse material reverts to the lessor. Therefore, a question was raised in the minds of these operators: Why should I assume the expense of such pro¬cedure when I have no assurance that I will benefit by the future processing and sale of these fine sizes? Under present conditions, the answer to this question is not one of choice but of necessity, as restrictions imposed by legislation make it mandatory on operators of preparation plants to take necessary steps to properly treat silt-laden waters before permitting them to enter the streams. By reason of these restrictions, the disposal of fine sizes becomes a secondary_ rather than a primary operating con sideration, and the procedure for disposing of this refuse becomes a matter of choice governed principally by topographical and geographical conditions. METHODS OF HANDLING REFUSE There are three principal methods of handling and disposing of fine-size refuse; namely :

Jan 1, 1946

By H. N. Eavenson

EaRly in 1917, the United States Coal & Coke Co. secured options on several tracts in Harlan County, Ky., aggregating about 19,000 acres in area, and after careful prospecting by outcrop openings and diamond drilling, completed the purchase late in July of that year. This property is situated in the eastern end of Harlan County, south of the Poor Fork of Cumberland River, and extending across Big Black Mountain to the Clover Fork of Cumberland River, a distance of about 7 mi. (11.3 kg.). It extends from the Kentucky-Virginia line westward for about 6 mi. Looney Creek, which empties into Poor Fork, crosses the property for about 4 mi. (6.4 kg.), and as several of the seams within the property outcrop along this stream, it afforded an easy, and the logical, place for development. The property is on the northern side of the geological trough formed by the uplifting of Stone Mountain, on the southern, and Pine Mountain, on the northern side; the northern boundary along Poor Fork is practically at the base of Pine Mountain. This area has been described in various geological reports. The main seam on this property is the one known variously as the "C," Benham, Keokee, Taggart, and Roda; it is also called, by the Kentucky Geological Survey, the Kellioka seam of the western portion of Harlan County. This seam averages, in this property, about 5 ft. (1.5 m.) in thickness, although local rolls reduce this thickness considerably over small areas, and at the extreme western end of the property the seam splits. It is usually clean, although occasionally a small parting occurs within a few inches of the bottom of the seam; it is one of the best coking and gas coals in the United States. The average analysis of this coal is given in Table 1.

Jan 1, 1922

By Howard Eavenson

EARLY in 1917, the United States Coal & Coke Co. secured options on several tracts in Harlan County, Ky., aggregating about 1.9,000 acres in area, and after careful prospecting by outcrop openings and diamond drilling, completed the purchase late in July of that year. This property is situated in the eastern end of Harlan County, south of the Poor Fork f Cumberland River, and extending across Big Black Mountain to the Clover Fork of Cumberland River, a distance of about 7 mi. (11.3 kg.). It extends from the Kentucky-Virginia line westward for about 6 mi. Looney Creek, which empties into Poor Fork, crosses the property for about 4 mi. (6.4 kg.), and as several of the seams within the property outcrop along this stream, it afforded an easy, and the logical, place for development. The property is on the northern side of the geological trough formed by the uplifting of Stone Mountain, on the southern, and Pine Mountain, on the northern side; the northern boundary along Poor Fork is practically at the base of Pine Mountain. This, area has been described in various geological reports.1 The main seam on this property is the one known variously as the "C," Benham, Keokee, Taggart, and Roda; it is, also called, by the Kentucky Geological Survey, the Kellioka seam of the western portion of Harlan County. This seam averages, in this property, about 5 ft. (1.5 m.) in thickness, although local rolls reduce this thickness considerably over small areas; and at the extreme western end of the property the seam splits. It is usually clean, although occasionally a small parting occurs within a few inches f the bottom f the seam; it is one f the best

Jan 9, 1921

By Donald O. Rausch, Adolph Soderberg

4.1-1. Introduction. Open pit mine planning must be correlated to all phases of a mining operation. The factors that must be considered in planning an open pit mine are numerous and must reflect the characteristics and surrounding conditions of a particular orebody. Therefore, only an outline of the subject can be presented here to aid the planning engineer in pointing out procedures that are generally applicable to pit design. The presentation is directed toward the planning of an open pit copper mine, but the procedures discussed should apply in most cases to any type of metallic or nonmetallic orebody. In planning an open pit mine the pertinent elements that must be included are: assays, geology, tonnage and areal extent of ore reserves, topography, mining equipment, economic factors of operating costs, capital expenditures, profit, types of ore, pit limits, cut-off grade, stripping ratio, rate of production, pit slopes, bench heights, road grades, ore metallurgical characteristics, hydrological conditions, property lines, and marketing considerations. 4.1-2. Sampling. Sampling must be adequate to classify the various materials to be removed from an open pit mine. Drillhole assays are plotted on sections and plan maps with ore and waste blocked out by selected bench intervals. These maps are prepared to depict the geological and other conditions existing on each mine level. The confidence factor to be applied to sampling and the resultant assays values must be given careful consideration. In uniformly disseminated de- posits, the confidence factor will approach unity. For widely fluctuating values, the average assay values should be discounted somewhat, the degree depending upon such factors as drillhole spacing. Such samples, at best, represent a very few pounds for hundreds to thousands of tons of ore

Jan 1, 1968

By J. P. Morgan, J. R. Dawson

A review of Jones & Laughlin&apos;s Vesta coal preparation plant flowsheet in 1959 indicated that, of the three sizes making up the company&apos;s metallurgical product, the -48-mesh fraction offered the greatest potential for improvement. Efforts to improve quality and yield were directed toward the use of froth flotation. After laboratory and plant tests were completed, it was decided that treatment of the entire -@-mesh fraction of the coal mix by flotation was a significant step forward in providing better coal quality and recovery. Reduction of ash in the metallurgical coal from 6.75 to 6.25% provided material savings at the coal washer, coke plant and blast furnace. The Vesta preparation plant of the Jones & Laughlin Steel Corp. is located on the Monongahela River, eight miles south of Brownsville, Pa. This plant is capable of cleaning 2400 tph of a mixture of Pittsburgh seam high volatile coals from the Vesta and Shannopin mines to produce a metallurgical coal of 6.75% ash and a steam coal containing 14% ash. Heavy media vessels are utilized to upgrade the coarse coal while launders and tables handle the -1/4-in. fraction of the raw coal feed. Cleaned -1/4-in. coal goes to boot classifiers where the 48 mesh material settles and is removed by bucket elevators. This 1/4x48 mesh material is then sent to centrifugal dryers for dewatering. As designed, the -48 mesh fraction overflows the boot as a 7 to 8% solids slurry and is recovered by cyclones and a thickener and then dewatered by filtration. The products of the heavy media circuit, the launder-table-boot-dryer circuit and the cyclone-thickener-filter circuit, are combined to constitute the shipped metallurgical coal. The Vesta-Shannopin mix is combined at Jones & Laughlin&apos;s Pittsburgh and Aliquippa Works with purchased low and medium volatile coals for the production of metallurgical coke. A review of the preparation plant flowsheet in 1959 indicated that of the three sizes making up the metallurgical product, the -48-mesh fraction, containing 16.7% ash, offered the greatest potential for improvement of coal quality. This fraction was considered low, averaging 55%, while the rejects averaged only 33% ash. It was evident that while the boot overflow fraction represented only 6% of the product mix, a reduction in ash to 6 or 7% would reduce the ash of the metallurgical coal by 0.5%. The original plant flowsheet handling the boot overflow (Fig. 1) consisted of ten 14-in. cyclones treating 70% of the overflow and producing a 48x150-mesh underflow and a -150-mesh overflow. The cyclone overflow was combined with the remaining 30% of the boot overflow to constitute the feed to a 150-ft thickener. The cyclone underflow and the 48x325-mesh thickener underflow were fed to vacuum disk filters for dewatering prior to combination with the coarse metallurgical coal. The thickener overflow stream containing the -325-mesh material was split, 40% being recycled directly to the plant water system and 60% being flocculated and clarified in an 85-ft thickener. The underflow of this thickener was pumped to waste. Efforts to improve quality and yield on the -48-mesh coal were directed toward the use of froth flotation early in the investigation. A review of the fine coal flowsheet indicated that three streams should be considered for treatment by froth flotation. These were the -325-mesh thickener overflow, the -150-mesh cyclone overflow and the -48-mesh boot overflow. Flotation of the thickener overflow was considered basically to improve recovery by upgrading the reject stream so that it could be fed to the filters along with the thickener and cyclone underflows. The overflow from the thickener contained 3.7% solids and had an ash analysis of 33%. Flotation of the cyclone overflow and boot overflow were considered to upgrade coal quality as well as yield. Treatment of the cyclone overflow, a 5.4% solids slurry averaging 27% ash, would eliminate the coal thickener and provide a feed of flotation concentrate and cyclone underflow to the filters. Treatment of the boot overflow would eliminate both the cyclones and thickener and feed only flotation concentrates to the filters. Flotation feed in this

Jan 1, 1962

By M. Cohen, R. J. Teitel

There is considerable interest in beryllium because of its low density (1.84 g per cu cm), high modulus of elasticity (40 X 106 psi), high melting point (1280°C), and special nuclear characteristics. Moreover, it has fair resistance to corrosion and oxidation. However, the purest beryllium known to the authors is relatively brittle at room temperature, and cannot be fabricated readily. The search for improved properties leads naturally to investigations of beryllium alloys and the phase relationships upon which they are based. The present paper is concerned with the alloys of beryllium and iron, primarily from the standpoint of the equilibrium diagram. Iron was selected (1) because of its all-round importance in metallurgy, and (2) because the beryllium-iron system is known to be quite complex. The most recent diagram in the literature is that of Gaev and Sokolov,&apos; and covers only the iron-rich end up to 16 wt pct beryllium. Beryllium markedly restricts the austenitic field, closing the gamma loop at about 0.4 wt pct (3 at. pct). On the other hand, beryllium is soluble in a-ferrite up to a maximum of 7.5 wt pct (34 at. pct) at the eutectic temperature of 1160"C. The eutectic composition lies at 10 wt pct beryllium (42 at. pct) and corresponds to a mixture of or and FeBez (called j3 in the present paper). The solid solubility of beryllium in the a phase decreases with decreasing temperature, and makes precipitation-hardening possible. These findings substantiate the earlier work of Oester-held,2 Wever and Mueller3 and Laissus.4 In addition to the FeBe2 (ß) mentioned above, Misch6 has reported on FeBes, and indicated evidence for another compound containing still more beryllium. A preliminary diagram by Gordon,5 not hitherto published, is given in Fig 1. Besides the phases previously named, there are shown a solid solution of extended range (e), a compound of limited solubility (t), and a high temperature phase (7). Beryllium is designated as 8. The t field contains the compound composition FeBea, and the f phase undoubtedly corresponds to the beryllium-rich compound found by Misch.6 The region around the { phase was proposed by R. J. Teitel based on Gordon&apos;s data. The details of the diagram are self-explanatory. It was the unusual complexity of this system that prompted the authors to undertake the present studies. By the same token, more emphasis was placed on the beryllium-rich than the iron-rich end of the diagram. Exprimental Details RAW MATERIALS The beryllium employed in this investigation was one of the purest grades available. Its chemical analysis after vacuum melting is given in Table 1. The metal assayed 99.4 wt pct beryllium. Vacuum melted electrolytic iron of purity shown in Table 1 was the source of iron.

Jan 1, 1950

By Raymond E. Byler

THE challenge of unprecedented need for more metals to meet present-day re-armament and domestic requirements is being met with minerals beneficiation projects of great number and variety, and with new and improved methods, techniques, and. equipment. Iron Range Developments Much attention has been given during the year to the tremendous program for beneficiation of taconites and intermediate iron ores which is progressing through large pilot-plant tests preparatory to full-scale production operations. The greatest activity has been directed toward concentration of magnetic taconites on the Mesabi Range. The Reserve Mining Co. has let $75 million in construction contracts for the 2 ½ million-ton-per-yr project (concentrates) at Beaver Bay, Minn., and is building a 300,000-ton-per-yr pilot plant to prove up the magnetic separation and pelletizing operations. Oliver Iron Mining Co. has a pilot plant under construction near Mountain Iron for concentrating magnetic taconites, and is operating experimentally a sintering and nodulizing plant on fine ore screenings and concentrates at Virginia to fully develop agglomeration technique. The Erie Mining Co. plant at Aurora continues its production of concentrates from magnetic taconites which was begun three years ago. No plans have been announced to treat the Mesabi Range nonmagnetic taconites, but F. D. Devaney, Pickands Mather and Co., is studying a new process for magnetically roasting lean ores to make them amenable to low-intensity magnetic concentration. W. R. Van Slyke, Cleveland-Cliffs Iron Co., calls attention to several noteworthy developments in the field of intermediate ores, perhaps the most significant of which has been the first commercial operation of a Dutch State Mines (DSM) cyclone plant at the Buckeye mine of the M. A. Hanna Co. The plant concentrates the +1/4 in. fraction by means of conventional heavy-media treatment after suitable crushing, screening, and washing. The -1/4 in. +65 mesh material is treated in two 12-in. cyclones, the -65 mesh fraction being sent to tailing storage. The plant is operating successfully on feed rates up to 120 tons per hr, and indicates that successful treatment of the fine fractions of Mesabi intermediate ores is imminent. Another commercial-size DSM plant was placed in operation late in the year by Cleveland-Cliffs at the Holman mine, and two additional ones are expected to be in operation next year. Various other methods are also in use at different plants for treatment of the fine fractions, including classification, abrasion milling followed by classification, jigging, and Humphrey spirals. Where it can be economically justified, it seems at present that heavy-media treatment of the -1/4 in. fine fraction will also come into increasing use on the intermediate ores. During 1951 a one-unit, heavy-media plant to treat hematitic crude ore was erected at the Ohio mine on the Marquette Range by Cleveland-Cliffs and plans for another plant at Humboldt to produce 2000 tons of concentrates annually is contemplated, as is also the construction of a plant for agglomera-

Jan 1, 1952

By John J. McKetta. Jr., Louis B. Lesem, George H. Fancher

The proration of oil produced in the field frequently is based partially or entirely upon the gas-oil ratio of wells. The measurement of the gas-oil ratio is one of the more important field tests in regulatory and pro-ration work, and the test always should be conducted according to standardized methods and procedure. Obviously, the gas-oil ratio and the volume of gas produced by a well depend upon many factors but should be independent of the method of measurement and of the devices used to measure gas and oil. Consequently, the volume of gas accompanying a barrel of oil produced by a well may be measured by any reliable and accurate device or instrument. Frequently either a critical flow prover or an orifice well tester is used for this purpose, and for a particular well the same rate of flow of gas should be obtained regardless of whether a critical flow prover or an orifice well tester is employed in the test. In Texas, when using either instrument, either Capacity Table 1 or 5&apos; is employed in making the necessary computations. If the tables are used, a discrepancy always is found whenever the two instruments are compared by extrapolation to the same conditions of flow. Clearly, Tables 1 and 5 must be at fault in some respects. The orifice well tester and the Bureau of Mines type of critical flow prover are essentially the same instrument; both devices utilize a square-edged orifice 1/8 in. in di-ameter as the primary element, and both freely discharge gas to the atmosphere. Tables for the orifice well tester&apos; have been published in the ranges of 0 to 15 in, of water and 0 to 40 in. of mercury (Hg) differential in pressure. Coefficients for the critical flow prover have been published for differentials in pressure greater than 75 psia. An extrapolation of either differs from the other set of data as much as 18 per cent at some points. No immediately obvious reasons for the discrepancy was found, and data available from the literature were insufficient to effect reconciliation. Consequently, a series of experiments was performed to check the available data and to determine discharge coefficients for the two devices in an overlapping range of differential pressure. The correlating equation used in preparation of tables such as Tables 1 and 5&apos; is the so-called hydraulic equation, Q = C1 vh .....(1) The tables cover orifice sizes from 1/8 through 1 1/4 in. A second set of tables, for use with greater differentials in pressure, apply only to the 3/4, 1, and 1 1/4-in. orifice plates over a pressure range of 0 to 40 in. of Hg. The correlating equation used in preparation of the tables is Q = C2 vH(29.32 + 0.3H)/G . (2) Each of these equations is valid only for the range to which it has been applied, and neither equation is valid for extrapolation. Theoretical equations for flow through an orifice are based upon assumptions of fractionless flow and an emergent jet the size of the orifice. A multiplier, C,, called the discharge coefficient, is inserted into the theoretical expression to compensate for both frictional losses and the contraction of the jet experienced in the plane of the orifice. Buckingham3 shows that C, should vary with the ratio of upstream to downstream pressure for flow of a compressible fluid at any average linear velocity through the orifice less than the velocity of sound. Work published by the National Advisory Committee for Aeronautics4 indicates that the variation continues into the so-called critical flow region until the vena contracta coincides with the plane of the orifice. The NACA work, however, does not indicate a leveling off of the coefficient. The work of the Bureau of Mines5 for the critical flow prover was based on differential pressures greater than 75 psi and indicates that the discharge coefficient, Cd, is constant in this region at a value of about 0.86.

Jan 1, 1958

By F. F. ESPIE

Giving the keynote address in the final session of a conference dealing with closely related topics has a disadvantage in that much of what can be said has been said. It also has an advantage, however, because it presents the speaker with the opportunity to integrate and analyse the material presented by the various speakers. I would like to look to the near future in Australia and the United States of America, to the risks, problem areas, and changes of a rapidly evolving post-industrial era-an era we are beginning to experience where industry no longer &apos;calls the tune&apos;. We miners have been quick to point out and emphasize, that ours is a &apos;high-risk&apos; industry in the world of business and commerce. Yet, clearly those who have survived, and been successful, have learned to anticipate and cope with risk and change. This ability has been a &apos;distinguishing feature of the industry&apos;s leaders who, in market studies and commodity selection, exploration and development, mine planning, metallurgical pro- cessing, and general administration and operation 1. identify areas-of risk or inevitable change, 2. analyse, test and quantify those factors of risk or change, and 3. design methods, systems, equipment to eliminate, moderate, or control or economically compensate for predicted risks or changes.

Jan 1, 1978