By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By W. B. Boggs, J. N. Anderson

An account of the operation of the Noranda smelter covering the period from December, 1927, when the smelter started, until December, 1929, was given in a paper published by the Canadian Institute of Mining and Metallurgy early in 1930.' The object of the present paper is to review matters of interest in the original paper and to describe the present construction and operation of the smelter, with particular reference to the reverberatory-furnace practice. The Noranda smelter was built by Noranda Mines, Ltd., from the designs of A. E. Wheeler, consulting metallurgist of New York, for the reduction of ores and concentrates from the Horne mine and to treat, on a custom basis, ores and concentrates from other mines in the Rouyn district. The smelter is at Noranda, about 330 miles directly north of Toronto. Construction work was started in June, 1926, and copper was first produced in December, 1927. The smelter was built throughout as two duplicate units, each with a rated capacity of 500 tons of ore per day. Operations were started with one unit and after several months it was found that one unit alone could smelt 1000 tons of ore a day. At that time there was only one hoisting shaft, No. 3, and its hoisting capacity and the capacity of the original crushing plant were insufficient to supply ore for the two units at the increased tonnage. Accordingly No. 4 shaft was sunk and a new crushing plant provided to handle the ore hoisted there. Operating two units at capacity also required the installation of two more converters to treat the additional quantity of matte produced. This work was completed in the latter part of November, 1929, and since then both smelter units have been operating continuously. In 1928, a mill to treat 500 tons a day of concentrating ore was completed. Since then the concentrator capacity has been increased twice, and at present 2000 tons a day of ore are being concentrated. The layout of the surface plant of the mine, concentrator and smelter is shown in Fig. 1 and the general plan in Fig. 2. The smelter is shown in more detail in Fig. 3. The original hoisting shaft, No. 3, is now used only for handling men, supplies and waste rock, and the original crushing

Jan 1, 1934

By M. A. Scheil

Austenitic stainless alloys are susceptible to stress-corrosion cracking which may occur under certain corrosion environments irrespective of their susceptibility to intergranular corrosion. Test samples are described for investigating stress-corrosion susceptibility of alloys for industrial equipment. A laboratory test using a solution of magnesium chloride boiling at 309 F. was found to produce transgranular cracks in several alloys investigated and in types 347 and 316 stainless steel tubing a residual stress of the order of 10,000 psi. was observed to initiate cracking. The susceptibility to stress-corrosion cracking as judged by the boiling magnesium chloride test indicates that alloys may be selected which will withstand a high stress in service Stressed specimens of stainless alloys included in a corrosion testing program will aid in determining the acceptibility of these fabricated alloys, when stressed, to the service conditions.

Jan 1, 1945

By J. M. Ross

THE Homestake mine is situated in Whitewood mining district, in the northern Black Hills of South Dakota, in the city of Lead, Lawrence County. The entire property, comprising 557 lode claims with a total area of 3343 acres, is held under United States Patent. The older claims were 300 by 1500 ft. under local regulations, the newer ones 600 by 1500 ft. The Homestake was discovered April 9, 1876, by Moses and Fred Manuel, and Jake Harney, who were drawn into the northern hills, from the Custer placer district, by news of the discovery of rich placer deposits in Deadwood Gulch. They located a number of additional lode claims and, in a short time, the whole country was covered with locations. The Manuel brothers built an arrastre the following winter and took out $5000. The next year the Homestake lode was sold to Senator George Hearst and associates, who organized the Homestake Mining Co. Other companies were formed to exploit other groups of claims and at one time five companies were operating on this deposit, the Father DeSmet, the Deadwood-Terra, the Caledonia, the Highland, and. the Homestake Mining Co. These companies, however, have been merged into the Homestake Mining Company. The first stamp mill, known as the "Eighty Mill," commenced operation on July, 12, 1878, and production has been nearly continuous since that time.

Jan 2, 1925

Jan 1, 1925

By Philip Bucky

THE term "longwall mining" is best known to coal men, although modifications of the method are continually being used in other fields. Longwall mining is of interest today because it makes for greater mecha-nization and better supervision at the working face, and therefore lower production costs and increased safety. It is an approach to the factory system of production, the high efficiency of which as compared to that in mines is well known. There is available an accumulation of experience regarding this work but coordination of experience is lacking and this series of experiments was undertaken to help serve this purpose. Model experiments were used for reasons of safety, cost and time, and because it has been previously shown1,2,3 that a scalar model built of the same material as the prototype will behave in a manner similar to that of the prototype, with time effects the same, if the effective weight of the model is increased in the same proportion as its linear dimensions are decreased. This is accomplished by substituting a centrifugal for the gravitational field; i.e., placing the model in a centrifuge and controlling the strength of the centrifugal field by varying the rate of rotation. Many factors affect the behavior of the geologic material overlying a bed, therefore results and conclusions contained in this paper apply only to the conditions presented herein.

Jan 1, 1938

By John D. Morgan

Prior to World War I there was no Government stockpiling program. Prior to World War I1 relatively few items were included in Government stockpiling and the start of that war found most objectives for even these few materials far from complete. Profiting from the experience of materials shortages in two wars, Congress in 1946 passed the Strategic and Critical Materials Stock Piling Act, which stated that it is the policy to decrease and prevent wherever possible a dangerous and costly dependence of the U. S. upon foreign nations for supplies of strategic and critical materials in times of national emergency. However, as of mid-1950 few stockpile objectives had been achieved. Shortly after the start of the Korean War it was obvious that in the absence of adequate stockpiles, the defense program could not be successfully carried out without broad authority to expand supplies of strategic and critical metals and minerals and at the same time to channel limited supplies of these materials to essential defense purposes. Accordingly, in September 1950 Congress passed the Defense Production Act, which provided broad powers for allocating materials and for making arrangements, including financial, to expand supplies.

Nov 1, 1955

[IRVING, JOHN D. :-(Continued.) Some Features of Replacement Ore-Bodies, and the Criteria by Means of Which They May be Discovered, XLII, [xlvii]. Discussions: on A Concise Method of Showing Ore-Reserves, XLIII, 714; on The Iron Deposits of Daiquiri, Cuba, LIII, 65; I on Recrystallization of Limestone at Igneous Contacts, XLVIII, 214; I on To What Extent is Chalcocite a Primary, and to what Extent a Secondary, Mineral in Ore Deposits, XLVIII, 194. minerals of gold deposits, Homestake belt, Black Hills, S. D., XLII, 54.]

Jan 1, 1918

By William L. Fink, Dana W. Smith

In parts I1 and II2 of this series, there were presented results of investigations on the age-hardening of an aluminum-copper and an aluminum-magnesium alloy. It was shown that the simple precipitation theory of hardening3 adequately explained the aging phenomena, including certain so-called "anomalous" behaviors which had caused other investigators to reject or modify the precipitation theory. However, these papers did not discuss the double aging peaks, which have been stressed in recent articles by Dr. M. Cohen4 and Dr. M. L. V. Gayler.6 The present paper is devoted to an explanation of this "anomaly." Fig. 1 is a generalized schematic representation of aging curves at different temperatures. Curve A corresponds to the aging at the lowest temperature, and D at the highest temperature. Certain previous investigators have explained curve A and the initial peaks

Jan 1, 1938

By William L. Fink, Dana W. Smith

In parts I1 and II2 of this series, there were presented results of investigations on the age-hardening of an aluminum-copper and an aluminum-magnesium alloy. It was shown that the simple precipitation theory of hardening3 adequately explained the aging phenomena, including certain so-called "anomalous" behaviors which had caused other investigators to reject or modify the precipitation theory. However, these papers did not discuss the double aging peaks, which have been stressed in recent articles by Dr. M. Cohen4 and Dr. M. L. V. Gayler.6 The present paper is devoted to an explanation of this "anomaly." Fig. 1 is a generalized schematic representation of aging curves at different temperatures. Curve A corresponds to the aging at the lowest temperature, and D at the highest temperature. Certain previous investigators have explained curve A and the initial peaks

Jan 1, 1938

By Norman Weiss

Most papers on xanthate have dealt with principles rather than practice. On the assumption that many millmen are interested in knowing where and in what manner the xanthates are being used in mills other than their own, this paper will summarize the results of a recent survey of North American plants. A brief background story and a description of the xanthates will be followed with the results of that survey; then a few observations will be made on storage, feeding, and ore testing. The first xanthate was made in 1822 by Zeise of the University of Copenhagen. With commendable scientific detachment (or perhaps a bad cold) Zeise ignored a more pervading quality of the substance and named it for its color, after the Greek word "xanthos," meaning yellow. During the first 80 years of its recorded existence xanthate found use only in small quantity as an insecticide; after the turn of the century there was some further demand for it in the vulcanization of rubber. It was not until 1922, by coincidence the centennial of Zeise's discovery, that C. H. Keller of San Francisco, seeking sul-phidizing agents, recalled xanthate in connection with his experience years earlier when he had seen this material used in Europe to combat grape phylloxera. His successful tests with the new flotation reagent culminated in the basic xanthate patent (U. S. 1,554,216) in 1925. In the minds of many metallurgists the introduction of xanthate as a flotation reagent is identified with the beginnings of alkaline circuits, the first use of chemical collectors, and the beginning of selective flotation. Actually, these preceded xanthate by a number of years. The alkaline circuit in lead-zinc flotation was introduced by Lyster as early as 1912. In 1922 Sheridan and Griswold made their momentous discovery (Timber Butte) that alkali cyanides and zinc sulphate effectively inhibited the flotation of pyrite and sphalerite in pulps made alkaline with sodium carbonate or bicarbonate. The use of lime to retard pyrite in copper flotation began within two years after Ralston directed attention to its possibilities in 1917. These were the beginnings of modern selective flotation, which was practiced successfully on copper-iron ores at Nacozari in 1922, and at Inspiration, Cananea, and others only shortly afterward. In the lead-zinc mills, selective flotation was of even greater economic importance at that time. The Sunnyside plant of U. S. Smelting, Refining, and Mining Co. used the process earlier than 1920, and Consolidated, Timber Butte, and others soon followed. As a chemical collector xanthate was relatively a latecomer, for the Corliss patent of 1917 covered the first of these, alpha-naphthylamine, and the Perkins patent of 1919 the second, thiocarbanilid. Both of these were in extensive use before Keller's xanthate made its commercial debut in 1923. There is general agreement, nonetheless, that the introduction of xanthate was

Jan 1, 1949

By R. J. Cowan

IN the art of cementation a controversy has been going on for years as to whether solid or gaseous carbon is the active agent in carburizing steel. More recently opinion has crystallized into a compromise to the effect that carburizing is a gaseous cementation of steel in the presence of solid carbon. The importance of this theory has a particular bearing upon the work to be described. In the art of carburizing, use is commonly made of such words as "catalytic," "atomic," "nascent" and "activated;" in an attempt to describe the process. These words are used indiscriminately. For, instance, the gas is said to be "catalytic" and carbon to be "nascent," or vice versa. In using these expressions, investigators are confirming the acceptance in their minds of the active conditions of both gas and carbon in the cementation process.

Jan 1, 1931

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By Herbert Clark Hoover, Lou Henry Hoover

PREVIOUSLY I have dealt with the methods of separating silver from copper. There now remains the portion which treats of solidified juices ; and whereas they might be considered as alien to things metallic, nevertheless, the reasons why they should not be separated from it I have explained in the second book. Solidified juices are either prepared from waters in which nature or art has infused them, or they are produced from the liquid juices themselves, or from stony minerals. Sagacious people, at first observing the waters of some lakes to be naturally full of juices which thickened on being dried up by the heat of the sun and thus became solidified juices, drew such waters into other places, or diverted them into low-lying places adjoining hills, so that the heat of the sun should likewise cause them to condense. Subsequently, because they observed that in this wise the solidified juices could be made only in summer, and then not in all countries, but only in hot and temperate regions in which it seldom rains in summer, they boiled them in vessels over a fire until they began to thicken. In this manner, at all times of the year, in all regions, even the coldest, solidified juices could be obtained from solutions of such juices, whether made by nature or by art. Afterward, when they saw juices drip from some roasted stones, they cooked these in pots in order to obtain solidified juices in this wise also. It is worth the trouble to learn the pro- portions and the methods by which these are made. I will therefore began with salt, which is made from water either salty by nature, or by the labour of man, or else from a solution of salt, or from lye, likewise salty. Water which is salty by nature, is condensed and converted into salt in salt-pits by the heat of the sun, or else by the heat of a fire in pans or pts or trenches. That which is made salty by art, is also condensed by fire and changed into salt. There should be as many salt-pits dug as the circumstance of the place permits, but there should not be more made than can be used, although we ought to make as much salt as we can sell. The depth of salt-pits should be moderate, and the bottom should be level, so that all the water is evaporated from the salt by the heat of the sun. The salt-pits should first be encrusted with salt, so that they may not suck up the water. The method of pouring or leading sea-water into salt-pits is very old, and is still in use in many places. The method is not less old, but less common, to pour well-water into salt-pits, as was done in Babylon, for which Pliny is the authority, and in Cappadocia, where they used not only well-water, but also spring-water. In all hot countries salt-water and lake-water are conducted, poured or carried into salt-pits, and, being dried by the heat of the sun, are converted into

Jan 1, 1950

By William Wraith

1. INTRODUCTION. AT the Washoe smelter,. Anaconda, Mont., the blister-copper from the converters is transferred, by means of a crane, to a refining-furnace,, in which it is brought to proper pitch by means of air and poles. From this furnace the refined copper, containing gold and silver, is poured into cast-iron molds placed on a platform-conveyor, giving an anode 36.75 in. long, 28 in. wide, and 21 in. thick. By reason of a disagreement between the smelter and the refinery, in reference to the silver-content of the anodes, it became necessary to investigate the methods of sampling used. II. SMELTER METHOD OF SAMPLING. At the smelter the sampling is done by " spotting " into water a small portion of the molten stream of copper as it flows from the furnace, by batting" the stream with a wooden paddle. The first sample is taken 30, min. after the pouring is started, three. other samples being taken at 1-hr. intervals, each sample weighing from 4 to 6 oz. The samples are dried, examined for particle's of burnt wood, screened on a 10-mesh screen of No. 8 wire to remove the fines, the oversize then screened on a 4-mesh screen of No. 20 wire to remove the coarse, the undersize of this screen being taken as the sample. Teh four portions thus obtained are thoroughly mixed and spli in half by passing over a 16-slot splitting-device, slots being 0.5 in. wide. One-half of the sample is sent to the laboratory for analysis and one-half kept as a duplicate. III. REFINERY METHOD OF SAMPLING. The method used at the refinery and also used in this investigation is the one developed by Dr. Edward Seller, of

Mar 1, 1910

Jan 1, 1951

By George F. Weaton

Although an almost continuous campaign had been carried on by various experimenters since 1885 to find a commercial process of smelting zinc by electrothermic means, no commercial success was attained in the United States. The St. Joseph Lead Co., appreciating the theoretical possibilities of such a process, such as the ability to construct units of large capacity, quality control, and the possibility of treating complex and refractory ores, decided in 1926 that the process was worthy of further investigation, and in that year, at one of its southeast Missouri plants, began the development of the electrothermic zinc-smelting process according to the invention of the late Earl C. Gaskill. Late in 1929 the process reached a stage of commercial significance, and in 1930 the erection of a modern electrothermic zinc smelter was begun, at Josephtown, Beaver County, Pa. The site is 3 miles from Monaca, which is on the main line of the Pittsburgh & Lake Erie Railroad, and a spur of the railroad has been constructed to the plant site. The site borders upon the Ohio River, which is navigable for 600 to 800-ton barges. This district was selected for the plant after an economic survey involving such questions as cost and availability of electric power, reduction fuel, transportation facilities, and the transportation charges on raw and finished materials, labor conditions, and taxes. The initial unit of the plant was designed to treat daily 120 tons of 58 per cent zinc sulphide concentrates from the company's mines in St. Lawrence County, New York. The plant equipment is housed in seven modern steel-frame buildings, and includes: Roasting and Acid Plants 3000-ton concentrate storage. Two Nichols-Herreshoff 21 ft. 6-in. diameter, 12-hearth roasters with usual cast-iron airshaft supporting chromium-alloy rabble arms and rabbles. SO2 gas purification system consisting of: One double-compartment hot-dust Cottrell precipitator. Cast-iron sinuous air-contact gas cooler.

Jan 1, 1937

By H. C. Howarth

THIS paper gives observations on ground movement and subsidence resulting from pillar drawing in the Lick Run section of Montour No. 10 mine of the Pittsburgh Coal Co. adjacent to solid coal owned by the U. S. Bureau of Mines at its Experimental mine in Snowden Township, Allegheny County, Pennsylvania. The investigation was planned by George S. Rice, chief mining engineer of the Bureau, who arranged the necessary cooperation with Dr. L. E. Young, vice president of the Pittsburgh Coal Co. Engineers of that company placed permanent monuments on the surface to establish the boundaries of the coal owned by the Bureau and to furnish fixed points to which all levels were referred. Engineers of the Experimental mine staff then covered the ground under observation with a checkerwork of monuments made of oak pegs set into the ground at 50-ft. intervals in two directions at right angles to each other. The level of these pegs was determined first from Dec. 16 to 30, 1929; again from May 25 to June 5, 1930, and finally from July 7 to 15, 1931. Observations were then discontinued because work had been stopped temporarily in this part on Montour 10 mine.

Jan 1, 1933

By Y. G. Shiau, J. E. Burke

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By J. E. Burke, Y. G. Shiau

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949