By Thomas C. Wilder

The activities of both components and the partial and integral molar thermodynamic properties of mixing for the liquid Al-Ge system at 1200°K and for the gertnanium-rich Al-Ge liquidus have been determined from data for eighteen alloys of compositions in the range 0.0593 < 0.880 using the reuersible gal-vanic. cell in the temperature interval 9320 to 1258°K. The liqui-dus compositions above 93 2 °K loere also ve determined by observing the discontinuities in the C us T plots for the high-melting alloys. This system shows moderate negative deviation from ideality throughout, the values for y° being 0.212 and 0.189 for aluminum and germanium, respectively, at 1200°K. Pavtial molar Properties of aluminum on the germanium-rich solidus and at infinite dilution in Ge(s) oboue 932°K were estimated from the foregozng measurements and the equlibrium data of previous investzgators. RECENT compilations of data1" have shown an increasing demand for knowledge of the thermodynamic properties of mixing of metallic alloy systems. In the case of binary-liquid systems where one of the components is a semiconductor this information is useful because, primarily, properties of the second (dopant) component on the liquidus, solidus, and at infinite dilution may be determined more accurately than from calculations based on the phase diagram. In this investigation a reversible galvanic cell was used to determine the chemical potential of aluminum in the two-phase region, liquid + [Ge], on the germanium-rich side of the A1-Ge system in the temperature range 932" to 1193°K. In addition, similar measurements for homogeneous liquid A1-Ge alloys for the entire composition range were obtained for the temperature interval 932" to 1258°K. The cell used was: The experimental technique and the treatment of the data were essentially the same as described earlier394 and are elaborated upon only briefly here. Each cell consisted of a liquid aluminum anode and three A1-Ge alloy cathodes of different composition which were held in Morganite alumina crucibles. The alloys were made up from aluminum and germanium weighed to the nearest 0.1 mg to a total weight of 5 to 10 g. Aluminum was a gift of Aluminum Co. of America and had a purity of 99.995+ pct. Germanium of transistor grade was a gift of Bell Telephone Laboratories. The four electrodes were contained in a larger alumina crucible which also held the prepurified fused chloride electrolyte. Contact to the electrodes was made by tantalum wire leads sheathed in alumina. The tantalum leads were centered in the electrodes by suitable positioning of an alumina radiation shield which fitted on the top of the - alulnina crucible. Two chrome l-alumel thermocouples, sheathed in quartz wells, completed the internal cell arrangement. The entire assembly was enclosed in an alumina tube, fitted with a water-cooled copper head so the system could be evacuated and then flushed with purified argon. *

Jan 1, 1967

Two sessions during the recent AMC Mining Convention in Los Angeles, September 23-26, served to update industry personnel on the status of health and safety regulations in the US. As reflected by the American Mining Congress resolution on mine safety and health, "Based on experience with the federal Coal Mine Health and Safety Act of 1969 and the federal Mine Safety and Health Act of 1977, (AMC) does not believe that laws designed to force compliance with regulations through the imposition of criminal or civil penalties will result in safer mines. (AMC) feels that the government&apos;s participation will be much more productive if greater emphasis is placed on research, training, and inspections aimed primarily at assisting operators and employees in recognizing and eliminating hazardous conditions and practices.

Jan 11, 1979

By EDWARHD HALSE

Discussion of the Paper of Dr. H. M. Chance, presented at the Lake Superior Meeting, September, 1904. EDWARD HALSE, Puerto Berrio, Colombia, So. Amer. (communication to the Secretary*) : The Taviche mining-district is generally known as a Taviches," being named from the two villages called respectively San Pedro Taviche and San Jeronimo Taviche. It is so called by José G. Aguilera, in his paper on the Geographical and Geological Distribution of the Mineral Deposits of Mexico;&apos; and in published reports by the late N. W. Rudston Read ;2 and by Juan de Dios Villarello.3 The region is a large one, measuring about 24 miles long and 7 miles wide. Dr. Chance, in his interesting paper, tells us very little about the nature of the ores, and, with regard to the geology of the district, contents himself with observing that ? the country, as a rule, consists of eruptive rocks; and no evidences of sedimentary strata appear near the mines.? The latter part of the above statement is hardly correct. The formation is mainly eruptive, being hornblende-audesite of Tertiary age, which is limited on the east by the calcareous (Cretaceous) formation, and on the west by the Huronian rocks of Ocotlan. Limestone is seen close to the Santa Càtarina mine, at the northern end of the region. In the surface-working known as La Cueva, a little northeast of San Pedro, limestone forms the eastern wall of the deposit which consists of spots (moscas) of pyrargyrite in white opaque or transparent quartz. Ill one place the ore is associated with stibnite, and the quartz frequently exhibts a

Sep 1, 1905

By AIME AIME

Annual net production of crude oil from the Anglo-Iranian, Oil Company&apos;s fields in Iran for the years 1940 through 1945 amounted to: YEAR TOTAL PRODUCTION (Long Tons) 1940 8,626,639 1941 6,605,320 1942 9,399,231 1943 9,705,769 1944 13,274,243 1945 16,835,000 (preliminary figure) All developed fields were on almost continuous production throughout the war, though their operation naturally was hampered by war conditions, which affected particularly supplies of equipment.

Jan 1, 1946

By Cecil H. Desch

THE progress of metallurgical practice and the demands made by the engineering industry on our foundries and mills have made the crystalline structure of metals a subject of far more than academic interest. Metals and alloys are made up of crystals. Even if we accept the view, so ably maintained by some metallurgists, that the crystals are separated from one another by an amorphous layer, it remains true that all but a very minute fraction of any metallic mass is crystalline. The conditions which affect the growth of crystals are therefore of importance in metallurgy. It is not only castings whose properties depend on the arrangement of their crystals, for the more we learn of the behavior of forged, rolled and drawn metals, the more certain it becomes that it is profoundly influenced by the size and arrangement of the crystals in the original ingot, deter- mining a structure which may persist in a modified form through a long series of mechanical operations and annealings. This is mainly due to the concentration of much of the impurities in the last portions of the liquid to freeze, so that the boundaries between single crystals or groups of crystals are marked out by a zone of segregated material, differing in properties from the mass, and offering a barrier to diffusion and equalization of composition throughout the whole. The importance of this fact has been fully recognized by steel manufacturers, who have to deal with ingots which are sometimes very large, and are cast at a high temperature, containing impurities which have a marked effect on the properties even when present in very small quantity. For this reason the Iron and Steel Institute has set up a committee to examine the whole question of the heterogeneity of steel ingots,(l)f and a report has been issued, containing an account of the structure of 16 ingots, ranging in weight from 15 cwt. to 172 tons, each of which was sectioned and examined by chemical analysis and by etching. A valuable body of data concerning segregation has thus been collected. The work of the committee is being prosecuted with great activity, and at the same time researches are in progress to determine the physical

Jan 1, 1927

By H. I. Aaronson, H. A. Domian, G. M. Pound

The thernodyna,nics of I the Proeutectoid ferrite re-action ha1.e been investigated on the bases of three diifevent descviptions of the statistical thernzodynamics of interstitzal solid solutions. Especially at low ternperatures, substantial dijeretzces are found in the valltes of the extrapolated y/y + a and cr/a + y equilibriurn curls, and in the To- co7nposilion metastable eqliilibriunz curl-es thus co,npited. Although neither actiztity nor phase-diagram date are able to distingrish udeqiutely among the various descviptions, the statustics of Lacher, Fouller, and Guggenheinz provide the ?nost conplete epresentation az3ailable of the single carbon-ctrbon interaction energy (w) nzodel of an intevstitiril solid solution, and the relationships deduced frojrl then2 are accordingly pre.ferred. The findings tlzut w in austenite &apos;aries significu?ztly uith tenpevntrue and that phase-diagawr data arc not accurately con?palible usith eqcrctions deduced on the basis of actility infoation indicate, hou&apos;e13er, that a wzore cornplex nlodel of the uustenite , und pvobably of the .feyrite, solirl solutions will have to forn the basis of f4tuve statistical t1.eat1nents. Some suggestions for such a ruodel arc advanced. Althoug11 w represents a vepltlsio energy in austozite, it was found to corvcsporzd in ferrite to a binding energy, in qualitatit.e accord zc,itlz the internal-friclion results of Keefer and wert. ThE transformation of austenite to proeutectoid fer-rite is becoming recognized as an exceptionally useful vehicle for quantitative studies of the kinetics of phase transformations.&apos;" Reasons for this popularity include well-characterized microstructures which develop on a convenient scale with acceptable kinetics within a considerable temperature-composition region, the absence of great sensitivity to common impurities, and, especially. the availability of a unique wealth of the ancillary information indispensable for the quantitative interpretation of kinetic measurements, including phase diagram,3 crystallographies diffusivity,5 inter-facial energy,=17 elastiit," specific vlume, &apos;&apos;&apos; and ativity&apos;-&apos; data. Development of considerable amounts of additional thermodynamic information from activity data is of particular importance with respect to kinetic studies, since much of this information is needed in temperature-composition regions not directly accessible to presently available techniques for the measurement of equilibrium properties. A generally useful approach to the thermodynamics of solid solutions, which is of especial value in this situation, is based upon the formulation of the free energy of such solutions as a function of temperature and composition. The free energy of solid solutions has been resolved into many components. Particularly in the case of interstitial solutions, with which we shall be concerned in the present study, however, only the positional entropy component has been intensively studied. The other components are conventionally taken into account by fitting equations for the activity of the interstitial species or the temperature-composition path of phase boundaries, derived principally from positional entropy considerations, to experimental information on these quantities through adjustment of one or more constants in the equations. A number of studies of the thermodynamics of interstitial solid solutions have been made primarily on this basis,&apos;"25 but only Kaufman, Radcliffe, and cohenZ2 (hereafter KRC) and ener&apos;&apos;% ave applied the results of such studies to develop relationships for the thermodynamic quantities of interest in the austenite —- proeutectoid ferrite transformation. KRC made use of a model developed by cheil&apos;&apos; (on the basis of a previous study by ohansson&apos;), and subsequently rede-rived correctly by Speiser and retnak,&apos; in which a carbon atom is considered to inhibit occupancy of a certain number of its nearest-neighboring interstitial sites. schei120 determined the number of sites in austenite thus excluded by matching calculated and experimentally measured curves for the variation of carbon activity with the mole fraction of carbon. zener17 used a different approach. He assumed that the positional entropy of carbon is ideal both in austenite and in ferrite (i.e., no excluded interstitial sites), and included all other contributions of carbon in a temperature-independent "free-energy change" accompanying the transfer of 1 mole of carbon between the two phases. This quantity was determined by "pinning" an equation derived for the boundaries of the a + y region to experimental data on the compositions of these boundaries at a single temperature. In the present investigation, three different approaches to the thermodynamics of the proeutectoid ferrite reaction are examined comparatively: I) the method of Zener; 2) the model employed by KRC and predecessors; and 3) the more detailed statistical thermodynamic treatment of the same model developed by acher and Fowler and uenheim, &apos; in which the problem of overlapping regions of influence of individual interstitial atoms is resolved. In order to make these comparisons, it is necessary to undertake an extension of one aspect of Zener&apos;s method; since the Lacher- Fowler -Guggenheim (LFG) treatment has not been previously used in the present context, the necessary thermodynamic "superstructure" for this treatment will be developed in parallel

Jan 1, 1967

By L. A. Cranson

WHEN I came out of Stanford University in 1922, the out-look for men trained in geology, petroleum engineering, and mining was indeed dismal; in fact, so much so that most of us looked upon our future in those fields as pretty hopeless. Neither our professors nor those men in industry with whom we came in contact gave us any enthusiastic encouragement as to the future of ourselves or the fields we had chosen for our labors. I believe that the attitude of pessimism which saturates everyone about graduation time is lament able and short-sighted, and may often start a young man on his way with an attitude of defeatism. Instead, he should be starting out knowing that he can expect hard work and keen competition, but that the fields of his labours are expanding at an accelerated rate, and that strong, energetic efforts will as always accomplish highly satisfactory results.

Jan 1, 1941

By B. A. Kulp, R. R. Reeber

Lattice parameters for the wurtzite form of&apos; CdS mere measured by powder X-ray diffraction techniques over the temperature range 26° to 1000 K&apos;. A negative thermal -expansion coefficient was determined parallel and perpendicular to the c axis below 13.5°K. Near 808°K, the curves of the a, parameter, the differential thermal expansion, and the resistivitv vs absolute temperature exhibited a reversible discontinuity. j\. direct determination of the lattice parameters of CdS over an extended temperature range is of particular use in interpretation of the effects of high pressure on the band structure of semiconductor materials. For example, Langer&apos; has studied the effects of pressure on the absorption edge of CdS from 77°K to room temperature. In order to properly interpret his results it is necessary to know the change in lattice constants as a function of temperature for the wurtzite, zincblende, and rocksalt2 modifications of this material. Thermal-expansion measurements for CdS, wurtzite phase, have previously been determined over a limited temperature range.s74&apos;5 The zincblende phases, of other compounds with similar bonding, have been investigated by Novikova et a! .&apos;&apos; Previous thermal-expansion measurements for metals with hexagonal symmetry have for the most part used bulk sample techniques for low-temperature result. Most X-ray measurements at low temperature have been on materials with cubic symmetry.&apos;jQ The use of X-ray powder-diffraction techniques offers a convenient and accurate method of measurement over a wide temperature range. The X-ray method, besides measuring unit cell size, also provides information about change in structure type and the nature of some of the stacking defects present. I) EXPERIMENTAL PROCEDURE The thermal expansion was measured by X-ray powder-diffraction techniques. Lattice parameters for the range 300" to 1000°K were determined in a 19-cm Unicam camera. From 26" to 300°K a 34-cm back-reflection camera with the Van Arkel" film arrangement was used. The sample was bonded to a copper cold finger below a helium, hydrogen, nitrogen, oxygen, dry ice, or ice brine bath in a metal cryistat. che inner bath was surrounded by another one for radiation shielding. Nitrogen was used in this outer bath for the very low-temperature runs while dry ice and acetone was used for the 195°K point. CuKa X-rays, filtered with a nickel foil, entered the cryostat through a 0.001-in.-thick aluminum window. During a typical 9-hr exposure the sample was continuously rotated through a 30-deg arc. Heat losses from the sample holder limited the minimum temperature attained to 26°K with helium in the inner dewar. Temperature calibration between 25" and 125°K was determined with an Allen Bradley 300-ohm carbon resistor. The resistor was attached to the back of the copper finger with a thin layer of silicone grease. Liquid He, HZ, N2, and O2 baths were used to calibrate the resistor. Temperature variation is estimated to be *2"K with a slightly higher uncertainty at room temperature and 264°K. The thermal expansion of high-purity germanium from 373" to 900°K was measured as a calibration for the Unicam camera. This value was compared with the known value1&apos; for the thermal expansion. A discontinuity in the thermal-expansion coefficient of the CdS a, parameter was observed. Similar discontinuities in the resistivity and differential thermal analysis at the same absolute temperature indicate that the temperature error is *5°K in the temperature range above 500°K. Temperature errors in the Unicam camera below 500°K are appreciably higher due to large gradients in the resistance furnace. II) SAMPLE PREPARATION The CdS was Eagle Picher ultrapure grade. The crystallite size range of the as-received powder

Jan 1, 1965

The Pueblo Viejo Mine, a 7, 250 mtpd (8,000 stpd) gold-silver cyanidation plant built by Rosario Dominicana S. A., was described in Volume I of this monograph. At the time of writing that volume, Pueblo Viejo had not yet gone on-stream and operating data or costs could not be presented. Since that time this information has been obtained and several interesting modifications and an expansion have been made to the plant. Because Pueblo Viejo is the largest open-pit gold mine in the world and one of the world&apos;s leading gold-silver operations with production of approximately 31 kg (1,000 oz) gold and 125 to 155 kg (4,000 to 5, 000 oz) silver per day, the authors have updated the previous data and flow sheet. The Dominican Government, which held a 4670 interest in Rosario Dominicana S. A., completed purchase of the mine to gain full control in 1979. Rosario Resources will continue to manage the mine, at least until the end of 1980. Gold was produced at Pueblo Viejo almost 500 years ago with initial production in the year 1505. Rosario Resources became interested in the property in 1969 and found surface oxidation had rendered the upper portion of the ore body amenable to direct cyanide treatment. The treatment of the underlying gold-bearing sulfide zone is still undergoing metallurgical studies. The ore is considered to be a laterite; and because there appeared to be few boulders in the ore zone, only a 400 m (16 in. ) square grizzly was initially installed ahead of the mills when the plant went on-stream in late 1974 at a design capacity of 7,250 mtpd (8,000 stpd). Operation also proved the ore to be harder than was originally anticipated. During 1967 a 1. 25 m by 1. 5 m (48 in. by 60 in. ) jaw crusher was installed to -feed the 1, 000 mt (1, 100 st) mill bin. Minus 200 mm (8 in.) crushed ore is fed directly to two 5.5 m by 1. 8 m (18 ft by 6 ft) semi-autogenous mills re-powered with 750 km (1,000 hp) motors and 50 mm (2 in.) grates. Each mill product is screened at 13 mm (1 /2 in.) by a vibrating screen. Screen oversize from each mill is combined on a single return belt equipped with a magnetic head pulley for grinding ball removal. The non-magnetic oversize is then split into two fractions for return to the primary mills. Originally, a minus 6 mm (1/4 in ) product was made on each screen and fed to a 300 kw (400 hp) 2.6 m by 3. 7 m (8-1/2 ft by 12 ft) regrind mill. During a plant expansion in 1978, an intermediate mill of 746 kw (1,000 hp) was installed to operate in open circuit on the combined primary mill

Jan 1, 1981

By David J. Mack, Chin Bea Kim

The decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was studied by isothermal transformation. Its progress was followed by metallographic, hardness, and X-ray diffraction methods. Three transformation products were found: lamellar pearlite at high temperatures; an intermediate temperature structure; and martensite at the lower temperaCures. No transition structu,ves were found. THE decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was stuadied as part of a long-range program of study on the eutectoid transformation in alloy systems which do not have one or more components which exhibit allotropy. Available information on the Ni-Zn eutectoid transformation is limited to that presented in connection with the determination of the phase dilagram. No systematic studies of the eutectoid were found in the literature, alkhough the microstructures of the Ni-Zn eutectoid were reported by Tamuru.3 X-ray diffraction data exist for the ß, ß1, y , and y1 phases.&apos; EXPERIMENTAL PROCEDURE The eutectoid alloy was prepared from "A" nickel shot and Bunker Hill super-purity zinc (99.998 pct).

Jan 1, 1962

The Industrial Minerals Division met jointly with the Materials and Equipment Division of the American Ceramic Society at State College, Pa, Sept 24-26 Headquarters were at the Nittany Lion Inn Thurs- day afternoon was devoted to a tour of inspection of the Bell Mine, American Lime and Stone Co , Bellefonte, Pa The party returned to State College for dinner and in the evening the Division&apos;s executive committee held a brief session There were four technical sessions Friday morning, Mining, afternoon, Beneficiation, Saturday morning, Industrial Minerals and Beneficiation There was an informal banquet at the Nittany Lion Inn Friday night with 93 present Edward Steidle was toastmaster Brief talks were made by President F C Flint and Secretary Ross Purdy, of the American Ceramic Society, Oliver Bowles, Chairman, Industrial Minerals Division, Adrian Morse, assistant to the president, Pennsylvania State College, and George Otis Smith, past president A I R&apos;I E

Jan 1, 1937

By B. A. Wilcox

ThERE are several reports in the literature which indicate that both solid-solution hydrogen and hydride precipitates can promote low-temperature em-brittlement of tantalum.1-3 For example, Imgram et al.2 showed that hydrogen additions in the range of 140 to 580 ppm promoted a ductile-to-brittle transition at slightly above room temperature in both wrought and recrystallized tantalum. This contrasts with the observation that tantalum of norma1 purity is very ductile, even at liquid-nitrogen temperature. Imgram et al. also found that hydrogen additions caused a deterioration of notch tensile properties of tantalum. The purpose of this communication is to present some limited evidence that hydrogen can also cause fatigue embrittlement of tantalum. The material used in this investigation was wrought, stress-relieved (1000°C, 1 hr), are-melted tantalum rod (5/8-in. diameter) containing the following impurities in weight percent: 0.005 C, 0.007 02, 0.0005 H2, 0.003 N2, 0.08 Cb, 0.01 W, and 0.01 Fe. Hydrogen charging was done in an atmosphere of flowing dry hydrogen for 3 hr at 600°C, followed by an homogenizing anneal in purified argon for 15 min at 600°C, and cooling in an argon atmosphere. Typical micro-structures of the hydrogen-free and the hydrogen-charged materials are shown in Fig. 1(a) and Fig. 1(b), respectively. Fig. 1(b) shows the appearance of hydride precipitates which, in many cases, formed preferentially parallel to the rod axis. The hydride dispersion was uniform across the diameter of the specimen. The fact that the precipitate was a tantalum hydride was tentatively confirmed by X-ray diffraction on a metallographically prepared surface. After hydrogen charging, chemical analyses by vacuum fusion revealed the hydrogen content to be 0.0295 wt pct. In addition, the oxygen and nitrogen contents were slightly raised to 0.0095 O2 and 0.005 N2.

Jan 1, 1964

By J. A. Bailey, J. H. Tundermann

The dihedral angles of the solid-liquid interfaces were measured at various temperatures above the solidus and the interfacial energies calculated when small additions of copper, indium, lithium, magnesium, antimony, and silicon were made to an aluminum alloy containing 3 pct Sn. When the results were compared with those of the Al-Sn alloy some differences were found which could be interpreted in terms of the ability of the added element to enter into solution or form intermetallic compounds with the aluminum and tin. It was shown that in some cases considerable changes in the shape of intergvanular liquid films can be brought about by comparatively small compositional changes in the alloy. DURING the melting or solidification of an alloy a temperature range is usually found where the presence of a liquid phase may be detected at the grain boundaries of a solid. It is believed that the presence of this liquid phase is responsible for hot tearing in castings and welds and hot shortness in the working of some alloys at elevated temperatures. Rosenberg, Flemings, and Taylor1 in a study of the solidification of aluminum castings have indicated the importance of intergranular liquid films and shown that their shape and distribution at the end of solidification effect the hot tearing characteristics of the material. The shape of such intergranular liquid films are determined largely by the ratio between the solid-liquid interfacial energy (yLS) and the grain boundary energy (ySS). A measure of this ratio (yLS/ySS , relative interfacial energy) is the dihedral angle 8. The dihedral angle 0 is related to the relative interfacial energy by the following expression: Rogerson and Borland 2 have also suggested that the shape of the intergranular liquid is an important factor in determining the susceptibility of a material to hot shortness. They showed that on a comparative basis materials having the lowest dihedral angles at a given temperature gave the greatest severity of cracking. They stated that liquid in the form of globules should be less harmful than liquid in the form of extensive films as more intergranular cohesion should be possible. Rogerson and Borlland 2 also showed that the susceptibility of an A1-Sn alloy to hot cracking can be reduced by small additions of cad- mium. It was found that the cadmium gave an increase in the dihedral angle at all temperatures. Ikeuye and smith3 investigated changes in the dihedral angle and relative interfacial energy with temperature for a number of ternary alloys formed when small additions of bismuth, cadmium, copper, lead, and zinc were made to an A1-Sn alloy. They found that in most instances changes in the dihedral angle were caused by compositional changes in the liquid phase; as the composition of the liquid approached that of the solid the dihedral angle decreased. They noted that the addition of a third element which was soluble in both the liquid and solid phases at a given temperature may decrease the dihedral angle (e.g., the addition of copper or zinc) but otherwise the ternary alloys formed exhibited dihedral angles between those of the A1-Sn binary alloy and those of the binary alloy of aluminum with the added element. Dwarakadasa and Krishnan4 investigated the changes in dihedral angle and relative interfacial energy with temperature when small additions of magnesium, iron, silicon, manganese, sulfur, cobalt, and silver were made to a copper alloy containing 3 pct Bi. They found that in all cases the added elements gave an increase in the dihedral angle and relative interfacial energy when compared with the values obtained for the simple binary alloy at the same temperature. It was noted that an increase in temperature gave a decrease in dihedral angle and relative interfacial energy in each of the ternary alloys studied. Similar results have been obtained by Ramachandran and Krishnan5 for the addition of small quantities of lead. This paper describes the application of dihedral angle measurement to the determination of the shapes of liquid phases at various temperatures above the solidus when small additions of copper, indium, magnesium, lithium, antimony, and silicon are made to an aluminum alloy containing nominally 3 pct Sn. An attempt is made to correlate the measurements with the relative solubility of the added elements in tin and aluminum. The work was undertaken to provide more data concerning the effects of temperature and composition on the shape of liquid films above the solidus. EXPERIMENTAL PROCEDURE In the present work ternary aluminum alloys containing nominally 3 pct Sn and small additions of high-purity copper, indium, lithium, magnesium, antimony, and silicon were made. The alloys were melted in a graphite crucible under an inert atmosphere of argon and cast into ingots 6 in. long by 0.5 in. diam. The ingots were then cut into rods 1.5 in. long, given a 50 pct cold reduction, and machined into test pieces 0.5 in. long by 0.5 in, diam for heat treatment. The alloy samples were annealed at the various test temperatures between the liquidus and solidus for approxi-

Jan 1, 1967

By A. J. Phillips, A. A. Smith, J. S. Smart

THE preparation of a sufficient quantity of high-purity copper for extensive laboratory use in the study of impurity effects has been an integral part of a research program in progress at the Central Research Laboratory of the American Smelting and Refining Co. for the past several years. Initially the degree of purity desired was that necessary to meet two essential requirements for experimental accuracy: (I) no impurity was to be present in the copper in an amount capable of producing a detectable effect on the properties to be studied, (2) even the minor changes in properties caused by the addition of extremely small amounts of individual elements were to be measured without significant interference from contaminants. In the course of the investigation, evidence has accumulated to justify the conclusion that this copper is of exceptional purity; in fact, no impurity can be detected by any chemical method or spectrographic technique known to the authors. The present paper describes the method of production of the copper and presents some of its properties. PREPARATION OF HIGH-PURITY COPPER The elimination of impurities from commercial electrolytic copper is accomplished by a three-step purification process. The first operation consists of an electrolysis through a purified CuS04-H2SO4 electrolyte using bagged anodes, low current .density (5 amp. per sq. ft.) and low temperature (25°C. max.). The electrolyte is prepared from commercial Cu2SO4 and is purified by heating the solution and adding I gram Fe as Fe 2(S04)3 to each 100 grams dissolved copper; sufficient hydrated oxide of copper, prepared from Cu2SO4 and NaOH, is supplied to precipitate Fe(OH)3, which carries down arsenic, antimony, tin, selenium, tellurium and other minor constituents. Silver and remaining traces of lead are removed by addition of Na2S to the acidified filtrate, which is then refiltered after standing hot overnight. The cold solution is made up to 30 grams per liter Cu and 150 grams per liter H2S04 and introduced without addition agents into the electrolytic system, which consists of a double row of hard-rubber battery boxes with the inside webbing and partitions removed, arranged in seven steps of ascending height. Electrolyte is uniformly supplied to the two highest cells by glass siphons operating from a constant-level reservoir, and flows by gravity through the bank of seven cells, entering each at the bottom and leaving at the top. Glass air lifts continuously supply the returning liquid to the constant-level reservoir for recirculation. Each cell contains three 434 by 43a by I-in anodes cast from high-quality electrolytic wire bar copper, various lots of which have been used with equal success. The anodes are pinned to sheet copper hangars shaped to prevent crawl of the electrolyte to the multiple-wired bus bars-which would result in fouling of the contacts and hang inside wool flannel bags stretched over open wood frames. The deposit

Jan 1, 1941

By Luther M. Krupp

A 3 ½ -mile asphalt mixed mat haulage road joins American Smelting & Refining Co.&apos;s El Tiro copper pit northwest of Tucson and its Silver Bell mill. Two-axle trucks operate continuously over the road- way but the asphalt top shows none of the wash- board wear usually seen on dirt haulage roads during use by heavy vehicles. The following data cover construction of this road, and results of its use by Asarco and Isbell Construction Co., the road&apos;s builder.

Jan 11, 1958

By William P. Shinn

IT seems proper to present in the Transactions of the Institute, from time to time, formal record of the advances made in the arts and sciences to which our organization is devoted-milestones in the highway of progress-from which our successors may measure what they in their turn have gained. The admirable address of the Hon. Abram S. Hewitt, then president elect of the Institute, on "A Century of Mining and Metallurgy in the United States," read at the opening of the meeting held in this hall in June, 1876, forms a point of departure, and the conclusion of the eighth decade of the nineteenth century and the end of the first five years of our country&apos;s second century seem to offer a fitting time for again making up our record. The period since 1875 has been marked by a degree of activity in mining and metallurgical industry never before equalled in our history, while the progress made in the science and art has been, if possible, still more noticeable. Whether we consider the mining of iron, ore, and coal, or of the precious metals,-the advances made in smelting the former and in reducing the latter, the extraordinary increase in the production of Bessemer steel, or the science of Thomas and. Gilchrist, which makes the hitherto rejected phosphorus the corner-stone of success,-the past five years are alike memorable for the progress they have shown and to some of the most marked features of this progress I will now oriefly call your attention. It may be of interest in this connection to note the following figures, showing the growth of the population of the United-States during the last three decades :

Jan 1, 1881

By Edward H. Robie

MANY engineers currently are working harder than usual, in part because of the demands being made upon them for increased production in the war effort, and in part because engineers are in short supply so that there is more to do for those who are available. In some instances the question has come up as to what additional payment, if any, should properly be made for overtime work, and to what extent is such payment legally permitted under the rules of the Salary Stabilization Board. Most engineers employed in an executive, administrative, or outside salesman capacity are not paid for overtime. They are paid for doing a job instead of for the hours they put in, and are free to do all the unpaid home work they feel they should do after dinner, as well as to do a bit of thinking and worrying during wakeful hours in bed. But engineers employed in a strictly professional capacity normally have standard office hours. Some employers pay for overtime and some don&apos;t. Their practice as it existed on Jan. 25, 1951 may be continued. In the absence of such practice at that time, the Salary Stabilization Board says that the engineer may now receive additional compensation up to his straight-time rate for an extended work week. No formal approval of the Board is required. "A professional engineer," in the mind of the Board, "is a person employed in a professional capacity, who, by reason of his special knowledge of the mathematical and physical sciences and the principles and methods of engineering analysis and design, acquired by professional education and practical experience, is qualified to practice engineering." Inducted Engineers A letter from a young man just inducted into the service and fearful that his engineering training is not going to be utilized reached us last week from Fort Riley, Kan. The AIME, cooperating with the other Founder Societies, is doing what it can, through the Engineering Manpower Commission, to see that engineers are not being wasted in the military establishment. So we passed this young man&apos;s letter along to T. A. Marshall Jr., executive secretary of that Commission. Mr. Marshall tells us that the normal procedure now being followed by the Army in handling Selective Service inductees is to have them first complete 16 weeks of basic training before assignment to specialized categories. During that time they are classified. If one has an engineering degree he should be classified as scientific and engineering personnel at the end of the basic training period. He should then be transferred to a technical detachment and assigned an MOS (Military Occupational Specialties) reflecting his education. If a young man is looking for a commission, it might be added that the current policy in the Army is to transfer to OCS (Officer Candidate School) applicants for commissions in the infantry only. The local unit commander can give information on this point, based upon the aptitude shown in tests. In view of the current shortage of engineers, it is believed that a young man should seriously consider remaining in enlisted status unless he can obtain a commission in a branch of the service that can make full use of his technical skills. His work may thus be more to his liking even if his uniform is not. New York or Atlantic City? In which place is it preferable to hold the annual meeting of a professional society like the AIME-New York or Atlantic City? That is, a winter meeting. The American Society of Mechanical Engineers has held its recent meetings at Atlantic City, with increasing attendance and satisfaction. The American Institute of Chemical Engineers chose Atlantic City for its recent December annual meeting. Only twice has the AIME ever met in this famous seashore resort: in 1898 and 1904. Chief advantages of going to Atlantic City over New York are that technical sessions are better attended, there being little else to do there in Winter; the cost to members is less, and hotel facilities are better adapted to a large meeting. As to cost, take a banquet, for instance. The Chalfonte-Haddon Hall, which caters especially to winter conventions, charges about $7 for a banquet dinner of standard quality. A similar dinner at the Statler in New York would cost about $8.50, and about $10.50 at the Waldorf-Astoria. (The charge for tickets is somewhat greater than this because of the cost of music, programs, flowers, and other incidentals.) Rooms, too, are somewhat less at Atlantic City, two in a room being accommodated for about $7 per day each, compared with $7 to $10 at a headquarters hotel in New York. On the other hand, AIME headquarters is put to some extra expense for staff travel, food and lodging, and members living in New York and environs are forced to pay a hotel bill. New York, of course, has more varied amusements to offer, plenty of big stores, and the glamour of a big city. The choice may be discussed at the forthcoming meeting in New York. In the meantime if any reader cares to express an opinion one way or the other we shall be glad to hear it. College Scholarships Most parents of children in the later stages of high school find it necessary to give some consideration to the cost of a college education. Although salaries have increased substantially it seems that the cost of the necessities of life, such as food, housing, and maintaining the family automobile, have gone up even more, so the problem of financing the children&apos;s education is as acute as ever. Many overlook the possibility of scholarships, or feel that only a student at or near the top of his class has a chance to get one. As a matter of fact, close to 150,000 scholarships and more than 15,000 fellowships, worth some $42,000,000, are available in 1200 American colleges and universities. Those who are interested should send 55¢ to the Superintendent of Documents, Government Printing Office, Washington 25, D. C. for a 248-page publication just issued by the U. S. Office of Education, entitled "Scholarships and Fellowships Available at Institutions of Higher Education."

Jan 1, 1952

OFFICERS AND DIRECTORS For the year ending February, 1934 PRESIDENT AND DIRECTOR FREDERICK M. BECKET NEW YORK ,N . Y. PAST PRESIDENTS AND DIRECTORS ROBERT E. TALLY JEROME ARIZ SCOTT TURNER WASHINGTON D. C.

Jan 1, 1932

OFFICERS AND DIRECTORS For the year ending February, 1932 PRESIDENT ROBERT E. TALLY JEROME, ARIZ. FREDERICK W. BRADLEY SAN FRANCISCO, CAL. WILLIAM H. BASSETT,P WATERBURY, CONN KARL EILERS NEW YORK N. Y.

Jan 1, 1929

By A. W. Hale

IN a work published in 1838, De Morgan, the author of the article on "Probabilities,&apos; in the Encyclopedia Metropolitana, says " The method of least squares is not yet introduced into the affairs of common life,….that many things which are demonstrable only by the higher branches of mathematics are looked upon as useless." And he mentions an instance in which "a method was suggested for estimating the relative importance of boroughs, by considering their population and contributions to the revenue com-

Jan 1, 1881