Literally hundreds of designs of mill liners are in use in current grinding operations, varying in contour from smooth to the roughest of surfaces, and in materials from scrap rail to alloy steels. A certain amount of variation in materials can be expected, owing to differences in local market conditions and the character of ores. However, when one attempts to rationalize the designs in current operations of a parallel nature, there is little that can be called standard practice. Designs and opinions of designs are as divergent as day and night. Somewhere in this maze there must be dues to better practice. The purpose of this paper is to examine the factors for consideration in liner design, and to propose a vigorous campaign of exploration in this phase of grinding operations. The paramount considerations in the choice of mill liners for a grinding operation are: (I) durability, in view of the cost, and (2) developed grinding capacity. Because of the strategic nature of grinding circuits in controlling the production of most mining operations: grinding capacity usually is the greater consideration. Grinding Capacity Mill liners affect grinding capacity in two ways: (I) by establishing dead space within a mill shell, which could be usefully occupied by live grinding media, and (2) by controlling the grinding action of the media. The extent to which liner thickness affects the potential volume of live grinding media, and thereby the grinding capacity, is shown in Table I. In a ball mill 7 ft. in diameter, for example, an inch of liner thickness reduces ball volume and corresponding grinding capacity by 5 per cent. With grinding capacity at a premium, this makes consideration something more than first cost of liner materials. A low-cost, voluminous material, made extra thick to secure adequate life, can be very expensive in terms of grinding capacity. On the other hand, in increased grinding capacity, a long-wearing material in a thinner pattern can save many times its value. From the standpoint of mechanics, the function of mill liners is to provide the means of driving or tumbling the load of grinding media. In this respect, an internal-spur gear-and-pinion assembly resembles a rotating mill shell with its contained load of grinding media, the mill-shell linen

Jan 1, 1947

By F. V. Lenel

R. P. Seelig.*—Dr. Lenel is to be congratulated on his presentation of a particularly interesting paper describing the use of the powder metallurgy process for the production of magnetic pole pieces. The only thing that might be added is that we have been successful in producing pole . pieces with a narrow hysteresis curve by the use of considerably lower sintering temperatures than the ones used by Dr. Lenel. It is quite possible that this use of lowe- temperatures has considerably widened the field of commercial application for pole pieces made from metal powders. Development work is currently being done on an a.c. application of a sintered iron part. However, I am in full agreement with Dr. Lenel that if eddy currents are an important factor in the application, we cannot substitute sintered material for laminated sheet-metal structures. Mr. Peters' remarks concerning the limitations of machine parts were well taken. The emphasis of the limitations makes it easier to define clearly what we can do and-what the advantages are of machine parts made of metal powders. When I mention metal-powder machine parts, I mean those of relatively high density, although complete elimination of porosity is not possible at this time. The limitations of the field for this type of parts are largely economical. I believe that Mr. Langhammer has made that point very clear. The following questions are very often asked: How large a part can you make? How close can you hold the dimensions ? How fast can a part be produced? In a majority of the cases, it depends on the cost at which the part can be produced. A large variety of shapes and sizes of a number of materials can be formed. However, the main requirement in this field of endeavor is whether this can be done more economically by powder metallurgy than by other manufacturing methods. As a general indication, it may be stated that densities up to 95 per cent of that of rolled material can now be produced commercially in simpler parts. Tolerances of plus or minus 0.001 in. are common, but where special conditions justify, closer tolerances can be held; we are producing a part of which one dimension is held to 0.0003 inch. Finally, as far as maximum size is concerned, technically this would depend on the capacity of the press and furnace equipment available. Actually, we find that the economical limit of powder-metallurgy machine parts is approximately one pound. From there on, each individual case must he studied on its own merits.

Jan 1, 1945

By John K. Dienes

The permeability of sands and soils seems to be adequately de- scribed by Darcy's law, but the permeability of rocks is complicated by a number of factors related to the probability of crack intersections. During the last few years we have developed a statistical theory of fragmentation which has been successful in explaining the observed behavior of rocks. In this paper, a theory of permeability is developed which draws on the concepts employed in previous work. The permeability involves three factors, the average fluid flux per crack, the number of cracks per unit area, and the fraction of cracks that are not isolated. Probabilistic ideas are used in connection with the hydrodynamic theory of flow through a single crack to develop an integral expression for permeability. The result has the form of Darcy's law for anistropic media. Although the current work is motivated by the need to develop optimized oil-shale retorts, we believe that the theory can be applied to a variety of other problems.

Jan 1, 1982

By William P. Blake

THE importance to the growing steel industry of the United States of a domestic supply of ferro-manganese or "spiegel" of a high grade, induces me to bring to your notice some details of the method by which a superior article is produced in the Austro-Hungarian Empire. At Reschitza, Hungary, and probably at Laibach also (the Krainische Industrie Gesellschaft), ferro-manganese is made in a blast-furnace, with charcoal as fuel, and limestone as the flux. The ore is a ferruginous mixture, containing about 37 per cent. of sesquioxide of manganese. It is silicious, and somewhat resembles, in its appearance, the manganese ore from Red Island, in the Bay of San Francisco, California. It contains about 29 per cent. of silica and some alumina, shown by the subjoined analysis

Jan 1, 1876

Charles Mather MacNeill, President of the Utah Copper CO. and of the Chino Copper Co., and a life member of the Institute since 1899, died at his home in New York on March 17, after a very brief illness with pneumonia. Mr. MacNeill was born at Oak Park, Ill., in 1871, and began his connection with mining enterprises immediately after graduating from high school, his first position being that of cashier with the Pueblo Smelting and Refining Co. He later went to Aspen, Colo., as manager of the Holden lixiviation plant. In 1893, he went to Cripple Creek as manager of the Lawrence Reduction Works, in which Mr. Holden and the late Capt. J. R. DeLamar were large owners. It was at this plant that Mr. Jackling became associated with him. The plant was destroyed by fire and, early in 1894, Mr. MacNeill became associated with Messrs. Spencer Penrose and Charles L. Tutt in a plan to finance and erect a chlorination plant at Colorado City, Colo., for the treatment of Cripple Creek ores. This plant was erected and was known as the Colorado-Philadelphia Reduction Works. Mr. MacNeill was general manager of the plant, Mr. Tutt having been president and Mr. Penrose, secretary and treasurer. The plant was very successful and was expanded, hally being reorganized under the name of the United States Reduction & Refining Company. Late in 1903, or very early in 1904, D. C. Jackling called the attention of Messrs. MacNeill and Penrose to the copper properties in Bingham Cañon, Utah, which have since become the main properties of the Utah Copper Co. After extended examinations and milling tests, these properties were bought, Mr. MacNeill becoming president of the Utah Copper Co., Mr. Penrose, secretary-treasurer, and Mr. Jackling, general manager. Mr. MacNeill remained president of the company to the time of his death. Mr. MacNeill was also a director, a member of the executive committee, and was largely interested in the Ray Consolidated Copper Co.; he was also president and a member of the executive committee of the Chino Copper Co. He had a variety of other mining interests, but the ones mentioned were distinctly the meost important. He was a director

Jan 1, 1923

Charles Mather MacNeill, President of the Utah Copper CO. and of the Chino Copper Co., and a life member of the Institute since 1899, died at his home in New York on March 17, after a very brief illness with pneumonia. Mr. MacNeill was born at Oak Park, Ill., in 1871, and began his connection with mining enterprises immediately after graduating from high school, his first position being that of cashier with the Pueblo Smelting and Refining Co. He later went to Aspen, Colo., as manager of the Holden lixiviation plant. In 1893, he went to Cripple Creek as manager of the Lawrence Reduction Works, in which Mr. Holden and the late Capt. J. R. DeLamar were large owners. It was at this plant that Mr. Jackling became associated with him. The plant was destroyed by fire and, early in 1894, Mr. MacNeill became associated with Messrs. Spencer Penrose and Charles L. Tutt in a plan to finance and erect a chlorination plant at Colorado City, Colo., for the treatment of Cripple Creek ores. This plant was erected and was known as the Colorado-Philadelphia Reduction Works. Mr. MacNeill was general manager of the plant, Mr. Tutt having been president and Mr. Penrose, secretary and treasurer. The plant was very successful and was expanded, hally being reorganized under the name of the United States Reduction & Refining Company. Late in 1903, or very early in 1904, D. C. Jackling called the attention of Messrs. MacNeill and Penrose to the copper properties in Bingham Cañon, Utah, which have since become the main properties of the Utah Copper Co. After extended examinations and milling tests, these properties were bought, Mr. MacNeill becoming president of the Utah Copper Co., Mr. Penrose, secretary-treasurer, and Mr. Jackling, general manager. Mr. MacNeill remained president of the company to the time of his death. Mr. MacNeill was also a director, a member of the executive committee, and was largely interested in the Ray Consolidated Copper Co.; he was also president and a member of the executive committee of the Chino Copper Co. He had a variety of other mining interests, but the ones mentioned were distinctly the meost important. He was a director

Jan 1, 1923

Draftsman and transitman for coal mine work in Middle West. Salary $125 per month. No. 277. Technical graduate wanted for metallurgical work in experimental laboratory of large New England manufacturing concern. A knowledge of metallography of steel is essential. Practical experience is desirable but not required. No. 305. High-class man to install and take charge of a coal mining property. Must be experienced in handling labor and of good sound judgment. Work will require a man to be on the grounds practically all the time. The work is drift mining and is not gaseous. No. 306. Engineer familiar with the acid treatment and melting of cyanide precipitates; also a competent assayer. Applicant must be able to furnish good references. No. 307. Wanted-practical mining man, foreman, or superintendent for work in middle or southern Atlantic States. Salary $200 per month. No. 308.

Jan 5, 1918

By C. A. Heiland

THERE once was a little kid, whose lot was a very tough one until he grew up. His parents did not have much in common; from all indica-tions, it is probable that the child was not wanted. His father Geology and his mother Physics separated shortly after his birth, which occurred during the World War amid a smoke screen of mathematics. He was kicked around a great deal. His parents could not agree on a name, and they finally christened him "Geophysics," for short. His relatives insisted that the name should be "Geophysical Prospecting," "Geophys-ical Exploration" or "Exploratory Geophysics"; though the youngster has grown up by now, this battle is still going on. His father did not think the child would amount to much until he began to show some unexpected talents, which were acquired, no doubt, from his mother Physics. His progress caused his father no little worry, and he began to wonder whether his offspring would help him in his business when he grew up or would set up shop in competition with the old man. His aunt Petroleum watched his growth with benevolent interest; his uncle Mining remained rather skeptical and cousin Civil Engineering not only assumed the attitude of the man from Missouri but was not much con-vinced even after he had been shown. Making a long story short, the kid decided that he had to stand on his own feet and get along as best he could. Having come from a good family . he possessed some outstanding characteristics such as resourcefulness and a reasonable amount of business ability. He therefore decided that it would be to his advantage to follow in his father's and mother's foot-steps as much as possible, and develop the good qualities of both. As a result, the youngster did fairly well for himself, and his relatives decided that it might be to their advantage to be on better terms with him. Father Geology had come to the conclusion that the boy could be very helpful to him and now wanted him to live in his house. His mother, who had brought him through the teething and measles stages, felt quite capable of bringing up the boy without the help of his father; and, as the fairer sex will do, would confide to a neighbor every now and then that his

Jan 1, 1938

By P. A. Beck, W. D. Manly

In a recent note Sully and Head1 showed that the Cr-Fe sigma phase is isomorplious with the Cr-Co gamma phase, and that the lattice constants are also nearly identical. In a preliminary investigation of the ternary Cr-Co-Fe system at 800°C at this laboratory the above findings were confirmed, and it was found by microscopic techniques, using various etching reagents, that the two binary phases form an urinterrupted series of solid solutions with each other. These solid solutions occupy a straight narrow band which cuts across the 800°C isothermal section of the ternary system, connecting the two binary phases. A detailed investigation of the Cr-Co-Ni ternary system at 1200°C disclosed that here, too, the Cr-Co gamma phase extends deep into the ternary system in the form of a long narrow lip. The fact that this sigma type lattice is sustained even when well over half of the Co atoms in it are replaced by Ni atoms, with relatively little change in the Cr content, clearly indicates that Ni itself has a certain tendency to form the sigma phase with chromium. This tendency is hidden in the binary Cr-Ni alloys, where the sigma phase is not known to occur, but it becomes operative in the presence of a suficient amount of Co. The interpretation of these facts in terms of electron concentrations is rendered difficult by the uncertainty of our present knowledge of the valency electron structure of the transition elements in their alloys. However, Sully and Heal's results and the present work suggest that intermetallic phases with signla type lattice may occur more frequently in these little investigated alloys than heretofore suspected. In particular, it is expected that a similar phase may exist in the V-Co and perhaps in the V-Ni system, in analogy to the known sigma type phase in the V-Fe system, and that all these sigma type phases may form extensive solid solutions with one another.

Jan 1, 1950

Horace F. Lunt, York, Montana* :—Two years ago I visited the region described by Mr. Jennings and assisted in the examination of a somewhat similar group of deposits in the White Mesa sandstone on the Navajo Indian Reservation, 125 miles north of Flagstaff and 50 miles east of the Kaibab plateau. There, the Triassic red sandstone is less than 200 ft. thick, and is overlain by a stratum from 200 to 250 ft. thick of white sandstone, which gives the name of " White Mesa" to that locality. The white sandstone shows all phases of crossbedding in great complexity, and evidently marks a period of oscillation and subsidence of the water, or an elevation of the land, at the close of a geological epoch. The prevailing color is white or gray, but occasionally it is red. In structure, it is composed of well-worn grains of quartzsand, from which most of the cementing material has been leached out, leaving it soft and friable. Possibly the cement was ferruginous, as is indicated by occasional traces of red color. The copper-deposits consist of a replacement of the cement of one particular cross-bedded stratum of the sandstone by chrysocolla, having also at times various quantities of tenorite in grains or masses. Some specimens of the ore contain as much as 32 per cent. of copper. Generally the copper-deposits are a few hundred cubic feet in size, and no strict line of demarcation is shown between them and the surrounding sandstone, the bluish-green color of the chrysocolla gradually fading into the white of the sandstone. The ore is apparently associated with small vertical crevices or fissures. Some of the deposits show a distinct vein-structure, while others do not. The origin of the ore is not very clear. Undoubtedly the solutions, coursing through the crevices noted above, played a prominent part in its deposition, as possibly

Jan 1, 1904

By J. L. Gregg

A study of copper-base and silver-base alloys was made with the object of finding, if possible, useful alloys subject to dispersion hardening. These studies led to the discovery of several alloys showing considerable dispersion hardening, the most important of which, the alloys of copper with iron, nickel, cobalt and chromium silicides, have since been very ably reported by M. G. Corson.l This paper is offered as a few notes covering alloys other than those described by Corson and some further data on the silicide alloys. Copper Alloys For the purpose of making a rapid survey of copper alloys that might show useful dispersion-hardening phenomena, various alloys were prepared containing 3 per cent. of additional elements added in such proportion that possible compounds could be formed without an excess of either added element. These alloys in the form of rolled or forged pieces were quenched in water from a temperature of 871" C. (1800" F.) and subsequently aged at various lower temperatures for l-hr. periods. The comparison of the Rockwell hardness of the quenched alloys with the maximum hardness of the alloys after aging was used as a measure of the dispersion hardening. Table 1 shows the Rockwell "E" hardness 1/8-in. ball, 100-kg. load) of the quenched alloys, together with the maximum hardness resulting from aging. The reheating temperature given in this table is the aging temperature at which maximum hardness resulted from a l-hr. sojourn. From this table it may be observed that only the silicide alloys showed significant dispersion hardening. Of these, the only one not described by Corson is the Cu-Be-Si alloy. This alloy contained 1.35 per cent. beryllium and 1.78 per cent. silicon, which is approximately equivalent to 3 per cent. Be2Si. It had a yellow color and scaled much less than the other silicide alloys upon heating. It could be worked easily either hot or cold but hardened very rapidly on cold working. The annealed alloy upon drawing from a diameter

Jan 1, 1929

By J. L. Gregg

A study of copper-base and silver-base alloys was made with the object of finding, if possible, useful alloys subject to dispersion hardening. These studies led to the discovery of several alloys showing considerable dispersion hardening, the most important of which, the alloys of copper with iron, nickel, cobalt and chromium silicides, have since been very ably reported by M. G. Corson.l This paper is offered as a few notes covering alloys other than those described by Corson and some further data on the silicide alloys. Copper Alloys For the purpose of making a rapid survey of copper alloys that might show useful dispersion-hardening phenomena, various alloys were prepared containing 3 per cent. of additional elements added in such proportion that possible compounds could be formed without an excess of either added element. These alloys in the form of rolled or forged pieces were quenched in water from a temperature of 871" C. (1800" F.) and subsequently aged at various lower temperatures for l-hr. periods. The comparison of the Rockwell hardness of the quenched alloys with the maximum hardness of the alloys after aging was used as a measure of the dispersion hardening. Table 1 shows the Rockwell "E" hardness 1/8-in. ball, 100-kg. load) of the quenched alloys, together with the maximum hardness resulting from aging. The reheating temperature given in this table is the aging temperature at which maximum hardness resulted from a l-hr. sojourn. From this table it may be observed that only the silicide alloys showed significant dispersion hardening. Of these, the only one not described by Corson is the Cu-Be-Si alloy. This alloy contained 1.35 per cent. beryllium and 1.78 per cent. silicon, which is approximately equivalent to 3 per cent. Be2Si. It had a yellow color and scaled much less than the other silicide alloys upon heating. It could be worked easily either hot or cold but hardened very rapidly on cold working. The annealed alloy upon drawing from a diameter

Jan 1, 1929

By T. Sterry Hunt

At the meeting of the Institute in Easton, October, 1873,I made a communication on the Ore Knob copper mine, in Ashe County, North Carolina (Transactions, vol. ii, p. 123), in which I called attention to the chemical decomposition alike of the pyritous lode and the inclosing gneiss rock to a depth of 60 feet, by which the feldspar of the latter had been converted into clay, and the whole rock very much softened. Such a decomposition is well known to be almost universal in the crystalline rocks of the Appalachians south of the Potomac; and if it is only seen in rare and exceptional cases farther to the northward, this, as I have elsewhere pointed out, is due to the fact that the decomposition began and ended in the ages anterior to the drift period, and that the decayed portions which still remained were at that time removed from the surface, except in some localities which were protected from the emding agency. I have lately had an opportunity of studying a remarkable instance of this kind in an examination made last month for the corporators of the Hoosac Tunnel.* The locality is at the western base of Hoosac Mountain, the western slope of which rises rapidly 1300 feet above the town of North Adams, in Berkshire County, Massachusetts, itself 700 feet above the sea level. Through this mountain, as is well known, a tunnel for the Troy and Boston Railroad has lately been opened, a distance of 25,081 feet from east to west. The rock of the mountain consists of mica schist and micaceous gneiss, including in its western half a great mass of harder feldspathic and quartzose strata in part a granitoid gneiss, the strata for the most part dipping to the eastward with variable angles, but with occasional western dips, apparently due to inversion. The crystalline strata of the mountain crest and sides are in many places exposed, and present rounded surfaces, often deeply grooved and striated, but with no appearance of decay. At the western base of the mountain, however, the gneissic rock is in a state of complete decomposition, which was well displayed in opening the tunnel, which, for a distance of several hundred feet, was driven through highly inclined strata so much decomposed that they were excavated with pick and shovel, and without the aid of blast-

By Alden B. Greninger, Alexander R. Troiano

The crystallographic mechanism for the austenite-to-martensite trensformation has been deduced from the results of the following new experimental determinations: (I) the accurate evaluation of the lattice relationship between austenite and individual crystals of martensite—and thus the relationship between the martensite lattice and the martensite plate, and (2) the measurement and analysis of the change in positions that a volume of austenite unclergoes when it transforms into a crystal of martensite. For the latter study, a new tool was developed, the stereographic analysis of shear. Lattice relationship.—Thirty-five separate 50-gram melts of an alloy containing about 22 per cent nickel and 0.8 per cent carbon were prepared in a high-vacuum furnace. This alloy is all-austenite at room temperature; grain size was about I cm. Specimens of the alloy were cooled to about — 70°C. to form a few martensite crystals, and suitable specimens were ground and polished on a surface parallel to a single martensite plate, exposing the martensite crystal for an area of 1 mm. or more. Four martensite cystals from four diffierent ingots were prepared in this manner; the largest crystal of this group is illuslratecl in Fig. I. Back-reflection Laue patterns were obtained from martensite crystals (and the matrix austenite) both before and after tempering. The locations of the basal-plane pole of martensite was checked by means of oscillating crystal X-ray patterns. All four crystals studied yielded the same solution ( ± 0.5°), and these relationships are expressed in gnomonic projection in Fig. 3.* The narrow dark-etching bands often visible in martensite "needles" were found to be parallel to (112) and thus are undoubtedly twin bands in the martensite crystal.

Jan 1, 1941

By T. Sterry Hunt

THE essential principle of this new process, now in operation in Chili and in North Carolina, for the extraction of copper from its ores, is the dissolving of the oxides of copper by a hot solution of protochloride of iron and common salt. In the action which takes place, the protochloride of iron is converted into peroxide, while the oxides of copper are changed into protochloride and dichloride, the latter of which, though insoluble in water, is readily soluble in a hot strong brine. From the solution thus obtained, metallic iron throws down the copper in a metallic state, regenerating the protochloride of iron; which is then ready for the treatment of a fresh portion of oxidized copper ore. In the case of slimy ores, the contact of the bath with the ore is effected by agitation in tubs; but when the ores are granular, lixiviation in large vats is equally efficient and simpler. The hot solutions, charged with chlorides of copper, are digested in tanks with scrap-iron, or better, are made to flow through covered channels containing the scrap-iron, and in their passage lose the whole of their copper; the reaction at the same time evolving so much heat as to keep up the temperature of the liquid. In order to prevent a certain loss of chlorine, which otherwise takes place from the production of some basic ferric chloride in the reaction between the ferrous chloride and the oxides of copper (both protoxide and dinoxide being generally present in calcined ores), a portion of sulphurous fumes from the roasting is made to pass through the regenerated bath before adding it to fresh ore. This has hitherto been effected by injection, with the aid of a jet of steam.

By Alden B. Greninger, Alexander R. Troiano

The crystallographic mechanism for the austenite-to-martensite trensformation has been deduced from the results of the following new experimental determinations: (I) the accurate evaluation of the lattice relationship between austenite and individual crystals of martensite—and thus the relationship between the martensite lattice and the martensite plate, and (2) the measurement and analysis of the change in positions that a volume of austenite unclergoes when it transforms into a crystal of martensite. For the latter study, a new tool was developed, the stereographic analysis of shear. Lattice relationship.—Thirty-five separate 50-gram melts of an alloy containing about 22 per cent nickel and 0.8 per cent carbon were prepared in a high-vacuum furnace. This alloy is all-austenite at room temperature; grain size was about I cm. Specimens of the alloy were cooled to about — 70°C. to form a few martensite crystals, and suitable specimens were ground and polished on a surface parallel to a single martensite plate, exposing the martensite crystal for an area of 1 mm. or more. Four martensite cystals from four diffierent ingots were prepared in this manner; the largest crystal of this group is illuslratecl in Fig. I. Back-reflection Laue patterns were obtained from martensite crystals (and the matrix austenite) both before and after tempering. The locations of the basal-plane pole of martensite was checked by means of oscillating crystal X-ray patterns. All four crystals studied yielded the same solution ( ± 0.5°), and these relationships are expressed in gnomonic projection in Fig. 3.* The narrow dark-etching bands often visible in martensite "needles" were found to be parallel to (112) and thus are undoubtedly twin bands in the martensite crystal.

Jan 1, 1941

By Joseph E. Pogue

New economic forces are at work in the petroleum industry. In order to visualize these forces and to see clearly their bearing upon the producer, refiner, and marketer, it is necessary, first, to go back and gain a perspective of the economic evolution of the business. Early Trend to Integration For several decades prior to 1911, the outstanding feature of the petroleum industry was a trend toward integration, culminating in a huge combine, the Standard Oil Co. An important aspect of this integrative trend, however, was its concentration upon a combination and control of refining and marketing, leaving crude oil production, for the most part, to the exigencies of small-unit competition. It is a noteworthy coincidence that during this era the law of oil and gas was formulated and applied, whereby these substances had to be reduced to possession to establish ownership; and the forces of competition in crude oil production were thereby intensified. It was to the interest of an industry, safeguarded in its control of manufacturing and markets, to have supply stimulated by legal convention as well as by individual initiative in order that the growing demand could be met without interruption. And so overproduction of crude oil during this era was no handicap, but rather an aid, to the progress of the industry. Disintegration But the idea of superintegration, despite its efficiencies, became repugnant to the temper of the times and so the Standard Oil Co. was dissolved by Court decree—disintegrated into over 30 parts. And thus, in 1911, was ushered in the second era of the petroleum industry, a period of intense competition. This era coincided with the development of automotive transportation, and a tremendous growth resulted in the effort to keep pace with the mounting demand for gasoline. An intense individualism and unbridled competition were appropriate to this period of entry

Jan 1, 1930

By P. R. Sperry

A METHOD was recently devised to indicate two or more successive stages of the migration of grain boundaries in aluminum, and to record the direction of the migration. This technique was used for the study of the various types of boundary migration occurring in high purity aluminum.' The method employs alternate annealing and electrolytic etching treatments, repeated as many times as desired. All successive sets of grain boun- dary positions revealed by the various etches appear superimposed on each other. The last etch is designed to leave an oxide film on the surface which is optically anisotropic. The orientation of the oxide film at each point is determined by the orientation of the underlying aluminum grain. When viewed with polarized light using crossed nicols and a Biot-Klein quartz plate, grains with differing orientations appear in different colors, as described by Hone and Pearson.' The last boundary positions are revealed by these color differences. The first step of the process is to obtain a desired starting grain size by annealing, for example, if high

Jan 1, 1951

By Carle Hayward

AT THE February, 1916, meeting of the Institute, a paper presented by Hayward and Raymond gave the results of a study on the effect of time in tempering medium-carbon steel, when the following conclusions were reached: It is not fair to consider the question settled when only three specimens were used for each treatment, but the results obtained indicate that for reheating quenched medium-carbon steel to temperatures below 500° it is only necessary to heat it through. Longer heating has little or no effect on the tensile strength, ductility, or hardness. At temperatures above 500°, increasing the time of treatment causes a slight falling off in hardness and tensile strength with a corresponding increase in ductility. In the discussion of the paper these conclusions were attacked and evidence presented that seemed to throw doubt on their accuracy. The authors, however, showed that this evidence was based on high-carbon or alloy steels and no facts regarding medium-carbon steel were presented. During this study the heat treatment was carried out in a small electric resistance furnace. It held nine specimens, but when these were placed in the furnace the temperature was lowered to such an extent that 30 to 40 min. were required to reach the desired heat. The authors pointed to this as a weak point in the investigation and it seemed wise to supplement the research by work on similar steel but using a different method of heating. This has been done and the results are given in the present paper. The Rhode Island Tool Co. cooperated by furnishing the steel and turning the tensile specimens.

Jan 1, 1922

By T. Sterry Hunt

AT the meeting of the Institute in Easton, October, 1873, I made a communication on the Ore Knob copper mine, in Ashe County, North Carolina (Transactions, vol. ii, p. 123), in which I called attention to the chemical decomposition alike of the pyritous lode and the inclosing gneiss rock to a depth of 60 feet, by which the feldspar of the latter had been converted into clay, and the whole rock very much softened. Such a decomposition is well known to be almost universal in the crystalline rocks of the Appalachians south of the Potomac ; and if it is only seen in rare and exceptional cases farther to the northward, this, as I have elsewhere pointed out, is due to the fact that the decomposition began and ended in the ages anterior to the drift period, and that the decayed portions which still remained were at that time removed from the surface, except in some localities which were protected from the eroding agency. I have lately had an opportunity of studying a remarkable instance of this kind in an examination made last month for the corporators of the Hoosac Tunnel.* The locality is at the western base of Hoosac Mountain, the western slope of which rises rapidly 1300 feet above the town of North Adams, in Berkshire County, Massachusetts, itself 700 feet above the sea level. Through this mountain, as is well known, a tunnel for the Troy and Boston Railroad has lately been opened, a distance of 25,081 feet from east to west. The rock of the mountain consists of mica schist and micaceous gneiss, including in its western half a great mass of harder feldspathic and quartzose strata in part a granitoid gneiss, the strata for the most part dipping to the eastward with variable angles, but with occasional western dips, apparently due to inversion. The crystalline strata of the mountain crest and sides are in many places exposed, and present rounded surfaces, often deeply grooved and striated, but with no appearance of decay. At the western base of the mountain, however, the gneissic rock is in a state of complete decomposition, which was well displayed in opening the tunnel, which, for a distance of several hundred feet, was driven through highly inclined strata so much decomposed that they were excavated with pick and shovel, and without the aid of blast- * See, for a detailed account of this examination, Dr. Hunt's report, published by the General Court of Massachusetts in House Document No. 9, 1875.

Jan 1, 1875