By George R. Gardner, Kenneth B. Ray

The application of wet cleaning processes for the beneficiation of bituminous coal has created in some localities a problem in the recovery and disposal of fine solids in the washery water. The maximum allowable concentration of these solids in the washery circuit that is consistent with satisfactory operation of the cleaning units remains a controversial point. It has, however, been generally recognized for a number of years that some degree of control should be exerted over the concentration of such material. Early methods of control involved intermittent or continuous discharge of a portion of the plant slurry into near-by streams or settling ponds, and this persisted even after the adoption of settling tanks or cones. The practice is not always economical, for two reasons: first, because of the waste of coal, and, second, because it is sometimes difficult and expensive to obtain an adequate supply of water. The latter condition often is aggravated by chemical treatment of the make-up water that is necessary to prevent excessive corrosion of plant equipment. The modern approach to this problem has been the adoption of continuous thickening devices. However, because such equipment occupies considerable plant space and is somewhat expensive to construct, the practice of loading these thickeners beyond their rated capacity is widespread, therefore often the performance of such units is not altogether satisfactory. In recent years, European washeries have increased the rate of settling of the fine coal from the slurry by the addition of specially prepared starch solutions. These reagents cause flocculation of the solid particles and thereby increase the rate of sedimentation. The first important work on the flocculation and clarification of coal slurry was done by Henry, who developed the Henry process and used it successfully in Belgian preparation plants. Soon after the initiation in Belgium, the process was introduced into England, where subsequent investigation developed similar processes, which were successfully used in

Jan 1, 1940

By E. N. Pennebaker

The concept of "unitization" comes from the petroleum industry. Of this, Campbell says: "Unitization is the process whereby the owners of adjoining properties pool their reserves and form a single unit for the operation of the properties. The revenue from operation of this unit is then divided in accordance with the basis established in the unit agreement. "The purpose of such an agreement is to produce the reserves more efficiently and thus to increase the profit to every participant."'

Jan 8, 1973

By D. J. Rose, W. M. Armstrong, A. C. D. Chaklader

The wetiability of single crystals of MgO by specimens of vacuum-cast iron was studied using the sessile drop technique in vacuo at 1550ºC. Formation of FeO at the liquid-vapor interface caused the contact angle (6) to decrease from 117 to 65 deg during the first minute. After cooling, all specimens possessed a peculiar annular interfacial deposit of Fe,O,. Within the annulus the interface showed no sign of chemical attack. Chemical reaction occurred where the iron was alloyed with Ti, V, Cr, Nb(Cb), Ta, cmd Zr. Vnriation of 6 with alloy concentration was studied. Although vanadium md chromium improved the wettability of MgO by iron, the effect of Zr, Ti, Nb, and Ta was indeterminable because the 8 derived from sessile drop considerations was that of the metal against a restrictive peripheral volume of liquid oxide wetting the substrate. INTEREST in the nature of metal-ceramic interactions has been stimulated by progressive development of metal-ceramic combinations. One of the more valuable methods used for bond investigation is the sessile drop technique. Recent attempts to improve wettability through solute additions to the drop have revealed that the solute may a) react with the oxide creating new compounds at the solid-liquid interface, b) adsorb at the interface in a monolayer formation, or c) distribute throughout the drop uniformly causing no wettability variation. This work, part m in a series1,2 of investigations of interface reactions between metals and ceramics, embraces a study of the Fe-MgO system. MgO possesses a large negative free energy of formation (-173 kcal per g mole 0, at 1550ºC) compared to FeO at this temperature (-73 kcal per g mole 02). Hence the electronegativity difference between the drop and substrate allows selection from an extensive group of metal solutes with intermediate electronegativity differences that would, in the absence of chemical reactions, be expected to adsorb pre- ferentially at the solid-liquid interface. However, the high oxygen pressure of MgO in vacuo creates an oxidation environment which influences the solute behavior. Recent studies of the Fe-MgO systemJ74 have been restricted by chemical reactions that obscured observations. In view of the current interest in liquid-phase sintering of metal-ceramic combinations under partial oxidizing conditions,5 a more comprehensive study of the Fe-MgO system seemed beneficial. EXPERIMENTAL PROCEDURE 1) Specimen Preparation. Optical-grade MgO single crystals and Ferrovac vacuum-cast iron were used in all experiments. A spectrographic analysis of the iron indicated 0.008 C, 0.05 V, 0.005 Mo, 0.01 Ti, 0.002 S, 0.01 Cr, 0.001 Mg, 0.01 Si, 0.003 A1 (wt pct). The MgO crystals were cleaved along (100) planes into plates approximately 20 by 20 by 1 mm. Following annealing in vactto at 1100°C for 3 hr, surface irregularities were removed by a chemical etch in phosphoric acid at 100°C. The iron rod was machined into small cylinders approximately 0.250 in. in diam and length and these were carefully cleaned in organic and acidic solutions to remove surface impurities. All specimens were weighed to the nearest 0.1 mg. 2) Apparatus. The apparatus described in detail by previous authors1,2 was modified for this work. A Polaroid Land Camera was incorporated into the optical system so that drop measurements at ten-second intervals after melting were possible with ultra-high-speed self-develop ing film. 3) Procedure. The iron cylinders were placed upright on the MgO plates and positioned in the molybdenum susceptor. After furnace assembly the system was pumped down to a vacuum of 1 µ and flushed with H2 at 800°C. The system was again evacuated to 5 x 10-5 mm of mercury and the temperature raised to 1550°C within 2 min. The molten drops were photographed at appropriate time intervals. TWO min after melting the iron vapor pressure caused gas discharge, or corona, within the tube. The specimens were then slowly cooled to room temperature, sectioned and examined metallographi-cally. X-ray identification of interfacial reaction products was attempted by the powder diffraction technique. Alloying elements (Ti, V, Cr, Zr, Ta, Nb) were added to the iron in various concentrations up

Jan 1, 1963

By Strathmore R. B. Cooke, Iwao Iwasaki, Hyung Sup Choi

The effect of temperature as a parameter in ore flotation has not been systematically studied, although for some ores it has been known for many years that selectivity and grade of concentrates can be improved by conditioning or flotation at moderately or substantially elevated temperatures. In 1934 Coghill and Clemmer' stated that "elevated temperature seems to make hard water more tolerable" in soap flotation, and a cursory examination of the literature indicates that some earlier investigators were aware of beneficial results obtained by floating above room or mill-water temperatures. Tartaron,' Mitchell et al.,3 and particularly Hamilton et al." have shown that high pulp temperatures give high recovery and selectivity in soap flotation of fluorite from a variety of gangue minerals. As a result of the work of these and of other investigators, high-temperature flotation has been successfully applied to industrial flotation of fluorite. Falconer" stated: "The use of high temperature conditioning (above 35°C and preferably above 60°C) in connection with the soap flotation of nonsulphide ores, as covered in B. Kalinowski's French Patent No. 847,- 215, Dec. 7, 1938, is claimed to provide more intense activation, better separation of values from gangue, and reduction in quantity of reagents." The various investigations quoted above clearly demonstrate the improvements to be realized by increasing the temperature at which fluorite is floated, and it is surprising that little or no information has been published on systematic investigation of the same method as applied to other ores.

Jan 5, 1960

By Fred H. Poettmann, A. L. Benham

correlation of waters and identification of mixtures of two and three waters is important in secondary recovery evaluation studies and studies involving underground movement of waters. The importance of such studies suggests the need for a method to correlate a great number of water analyses to accurately identify and improve the understanding of mixtures of waters. Geochemical analyses of waters furnish a quantitative measure of each of the ions present in a water. Table L shows a portion of the data on many oilfield water analysis report forms in use today. Under "parts per million" are listed the quantitative amounts of each ion in milligrams per liter. Following the work of Stabler' and Palmer", some laboratories have reported additional data to indicate the reaction capacity, or reacting value of each ion. Table I lists data under two subheads for the "reacting value". Under the first subhead, the reacting value is reported in gram equivalents per million, hereinafter called equivalents per million. This value is determined by multiplying milligrams per liter of the ion by a factor equal to the reciprocal of the equivalent weight of the ion. Under the second subhead (per cent) is listed the percentage of each ion based on the total equivalents per million. Sodium is not usually an analyzed value in routine analyses, but is determined by the difference between total negative equivalent per million values and the sum of all of positive ion values for which analyses were made. This difference is reported as sodium, hereafter labelled "sodium". On this basis, the subtotals of the equivalent per million and per cent reacting values of the positive and negative ions are equal. CORRELATION OF WATER ANALYSES DATA Previously reported methods for correlating oilfield waters have used part of the data in Table 1, and can be classified into two categories. Correlation by Chemical Character Correlation methods using the chemical character of waters, as represented by the per cent reacting values of the ionic constituents, have been used by Palmer2 and Tickell. These methods have the limitation of neglecting the ionic concentration of the waters. This limitation can be serious in areas where waters have the same chemical character, but differ in concentration. Correlation by Concentration of the Ionic Constituents The Reistle' and the Stiff methods use the ionic concentration in parts per million and equivalents per million. These methods are effective in differentiating waters of similar chemical character and varying concentration, as in the highly saline waters of the Mid-Continent area. These methods have the disadvantage that they correlate waters by comparing many graphs of individual water analyses to determine the similarity to, or the variance from "type" waters. PROPOSED METHOD OF CORRELATING WATER ANALYSES DATA Correlation graphs presented in Fig. 1 represent water analyses data as points to facilitate the correlation of waters. The graph on the left of Fig. 1 is a plot of per cent reacting value of magnesium vs calcium. The right

By W. R. Purcell, C. S. Brooks

The internal surfaces of rocks which are in contact with interstitial fluids are known to influence in some degree the recovery of hydrocarbons from pay zones. Despite the admitted importance of the influence of solid surfaces on hydrocarbon recovery, little information is available concerning the extent of surface of reservoir rocks. In this paper a description is given of the apparatus and procedure employed in the determination of the surface areas of sedimentary rocks, and values are reported for a variety of sandstone and limestone cores. In addition, consideration is given to the Kozeny equation, which relates surface area to porosity and permeability. A colliparison is made between the surface areas as calculated from this equation and the geometrical areas of a series of packs of spherical glass beads. Also, for a group of sandstone cores. Kozeny areas are compared with surface areas as determined by the gas adsorption method employed in this investigation. INTRODUCTION It has long been recognized that many processes which are of importance to hydrocarbon production are controlled in some degree by the extent of the surface of the reservoir rock through which the hydrocarbons move. For example, the recovery efficiency that is obtained in a given reservoir is certainly determined in part by the action of interfacial forces between the reservoir fluids and rock, and this action is influenced in turn by the extent of solid surface. Despite the admitted importance of surface effects to problems of petroleum recovery, little information is available concerning the extent of surface of reservoir rocks." It is the purpose of this paper to describe an apparatus which has been employed for the measurement of the surface areas of rock samples and to present the values which have been obtained for a variety of sandstone and limestone cores. In addition, the relationship of surface area to permeability and porosity, as given by the Kozeny equation, will be discussed. METHOD OF MEASURING SURFACE AREA The method of determining surface areas as employed in this work has previously found wide use in studies of porous solids such as catalysts. The method involves the measurement of the amount of physical adsorption of an inert gas, such as nitrogen or argon, on the bare surface of the solid at reduced pressure and constant temperature near the normal liquefaction temperature of the gas. With the aid of the theory of isothermal adsorption as developed by Brunauer, Emmett, and Teller,' it is possible to ascertain the amount of gas (and hence the number of molecules) which is required to cover the solid surface with a single layer of molecules. From a knowledge of the covering area per molecule the total surface ares of the solid can be computed. Since the Brunauer. Emmett, Teller (BET) theory has been adequately discussed elsewhere: it will suffice here merely to present their final equation as ordinarily employed for surface-area calculations. This equation relates the volume of gas, V, which is adsorbed at pressure, P, to the liquefaction pressure, Po, of the gas, and to the volume of gas, V.,, that is required to form a monomolecular layer: In this equation C is a quantity which is related to the heats of adsorption and liquefaction of the gas; for a particular solid-gas system at Constant temperature, C is considered to have a constant value. The basic adsorption data can be presented in the form of Equation (1) by plotting the quantity P/V(Po- P) as a func-

Jan 1, 1952

By Richard Ely

Conservation Means Preservation, Improvement, Justice CONSERVATION, narrowly and strictly considered, means the preservation in unimpaired efficiency of the resources of the earth; or in a condition so nearly unimpaired as the nature of the case, or wise exhaustion, admits. And broadly considered, it means more than the word itself implies, for it naturally includes an examination of methods whereby the natural inheritance of the human race. may he improved; and still more broadly considered-and as used in popular discussion-it includes a treatment of the effects of productive conservation measures upon distribution. We shall give our attention briefly to the main points in this informal definition before we pass on to the thesis that conservation is largely a matter of property relations-that a wise conservation policy means wise property relations. Preservation of Natural Resources First, conservation suggests simply preservation, and, in the treatment of the subject which we have had in the United States, emphasis has been laid upon the past and present waste of natural resources and upon the means of putting a stop to this waste. The forests have been depleted; soil has been washed by rapidly flowing surface water from mountain sides. These rapidly flowing waters have produced high streams and devastating inundations, followed by low streams and impeded navigation. The forests have, moreover, been so removed as to bring great danger of fire, and destructive conflagrations have resulted in large waste of resources, including in some cases a destruction of the humus, supplying essential elements in the fertile soil. As a remedy we must have measures to reforest mountain sides, and this means large social control, very frequently taking the form of public ownership and management; but in addition we always find actual and proposed

Jan 2, 1916

By Leon Merker

FLAME fusion growth of strontium titanate crystals was undertaken to obtain large transparent crystals on which physical data could be gathered. The fact that strontium titanate is a cubic crystal and probably has a high index of refraction indicated that it might be useful in optics. No large boules* of strontium titanate had been synthesized previously, and none have been found as natural occurrences. The flame fusion process, invented by Verneuil in 1904,1 was first applied to grow large crystals of ruby and has since been used extensively to grow crystals of corundum and spinel on a commercial scale. Only during the past nine years has this technique been applied to the growth of large single crystals of other high melting compounds such as rutile,2 mullite,3 and ferrites4 One of several significant advantages of the flame fusion technique over more conventional methods of growing crystals from a melt is that the crystals are grown without the use of melt containers. This fact alone excludes other methods of growing crystals from a melt whenever there are compounds with a melting point near 2000°C or above. Growth of the crystal, similar to that of a stalagmite, takes place inside a circular refractory furnace that does not contact the crystal, Fig. 1. This eliminates a serious source of impurities as well as the likelihood of multi-crystalline solidification along the container walls. The flame fusion technique is particularly advantageous for research because it produces large crystals quickly and at lower cost. A corundum crystal 25 mm long and 12 mm in diam can be grown in 2 to 3 hr. Operating conditions permit observation of the growing crystal during any stage of the process. The various flame patterns and a wide range of oxidation-reduction conditions can be investigated in a relatively short time. It should be pointed out that formation of the foot of the boule is the most critical step in growing an unfractured boule. When the tip of the sintered cone is fused to initiate crystal growth, the original area of fusion should be kept as small as possible so that one crystallite can assume dominance over all the others and propagate as a single crystal. If the boule start happens to consist of several crystals, usually the entire boule also contains several crystals. In many cases these tightly cohering crystals exhibit different crystallographic orientations. Although the basic technique of the original Verneuil process has been retained, refinements in method and burner design have been developed in recent years. For example, boule growth may be initiated on a seed crystal rather than by fusion of a sintered cone. The danger of multicrystalline or twinned boule starts is thus eliminated, and this procedure may also be used to grow boules of predetermined crystallographic orientation. Prior Art: Of the many attempts to produce artificial gem crystals, most early efforts% ere directed toward synthesis of .rubies and sapphires and diamonds. None of these efforts resulted in a process that was commercially practical. Without exception only tiny crystals of corundum were obtained, and those at excessive cost. Verneuil announced his process in 1904; Ravier6 in 1934 presented a detailed description of a commercial boule production plant. Descriptions of the German synthetic stone industry, the process details, and the equipment used have been published by Barnes7 and by Merker.'

Jan 1, 1956

By Kenyon Burch

ONE of the advantages presented by electric drive in many classes of work is the ease with which the electric motor can be controlled automatically. In a large number of cases certain features of the control are automatic-for example, the rate of acceleration may be limited automatically or the equipment may be stopped automatically at the limit of travel-but the equipment is started and ordinarily is stopped by hand. . In other cases the motion of the machinery is utilized to start, control the: speed, and stop the motor automatically, independently of any operator. A considerable proportion of the large mine hoists now in use have certain automatic features, particularly protective devices against over-winding, and, in some classes of electric hoists, devices for preventing excessive acceleration or retardation. The large automatic hoists discussed in this paper, however, are completely automatic, i.e., capable of snaking their trips without the presence of an operator at the control levers. According to circumstances, various advantages may be obtained by automatic control, chief of which are decreased power consumption', increased precision and safety of operation, and decreased, cost of attendance. The first step in the analysis of a prospective automatic mine hoist is to determine whether automatic operation is feasible at all. If men are to be hoisted, or levels changed, the attention of an operator is required for these purposes; but tinder some conditions it may be entirely practicable and advantageous to build the equipment so that, while provision is made for hoisting mien or changing levels, ore can be hoisted automatically from, any one level. If, however, an operator's attention is required every few minutes for changing levels, handling men or drills, or other work requiring hand control, it is obvious that automatic operation between times will not be of any, practical benefit.

Jan 3, 1916

By Paul C. Merritt

For more than 100 years, British Columbia has been considered a mountainous mining province, rich with potential but relatively poor in actual production. Times have changed. Today, Japanese interests and money have altered the difficult, if not once impossible, economic conditions and market factors which until recently precluded any great growth of the British Columbia mineral industry. The mining boom now underway in British Columbia has carried the total value of mineral production in the Province to a record height in 1962 as it rang up a 27% increase over that of 1961. Breaking the $200 million barrier for the first time, total value of British Columbia's mineral output reached $229- 276,385. Of this amount, metals accounted for 70%; industrial minerals, 6 %; structural materials, 9 %; and fuels, 15%. The substantial increase is attributed to the record production of copper, iron, asbestos, natural gas and petroleum, in addition to the continuing high production rate and favorable prices of other mineral commodities.

Jan 12, 1963

By W. L. Phillips

The plastic properties of lithium fluoride and magnesium oxide under compression were investigated in the temperature range 25° to 1000°C. At the higher test temperatures, the critical resolved shear stress and the rate of work-hardening of both materials decreased. At the same time, the number of stress lines decreased and the individual stress lines became wider. The density of dislocations decreased for a given strain the higher the test temperature for lithium fluoride. The decrease in the critical resolved shear stress as a function of temperature could be fitted by the equation 7 = Toe-KT. THE influence of temperature on the stress-strain curves of a variety of metal single crystals has been studied for a wide range of temperature.1"5 In general, it has been found that both the critical resolved shear stress and the rate of work-hardening decrease rapidly with increasing temperature and fall to a value of essentially zero well before the melting point is reached. AS the test temperature is increased, the density of slip lines has been found to decrease, while the width of the individual lines increases. Recently, Gallagher,' Graf et al.,7 and Pate1 and Alexander8 have found that single crystals of germanium and silicon, which have a covalent bond, can be plastically deformed at elevated temperatures. In compressing germanium it has been found that the strain-hardening coefficient decreased very rapidly as the temperature was increased. The coefficient did not tend to zero, however, as the melting point was approached. The plastic properties of ionic crystals at elevated temperatures have not been extensively investigated. In the only work previously reported Tamman and salge9 and Theile10 have shown that the yield point of sodium chloride single crystals tested in tension and compression decreased slowly with increasing temperature, falling to zero at the melting point. As the temperature was increased, they found a substantial increase in the amount of plastic deformation that could be sustained before fracture; and at temperatures above 400°C in tension tests there was an obvious necking which produced local extensions of up to 3000 pct. The purpose of the present work is to extend the knowledge of high-temperature deformation to the ionic crystals, lithium fluoride and magnesium oxide. The following were investigated: 1) The gross shape of the stress-strain curve at several temperatures. 2) The change in the critical resolved shear stress as a function of temperature. 3) The appearance of slip bands and the density of dislocations as a function of strain and temperature. EXPERIMENTAL TECHNIQUES The lithium fluoride and magnesium oxide used in this investigation were purchased from the Harshaw

Jan 1, 1961

By John C. Shyne, Eric R. Morgan

WHEN temper rolled low carbon sheet is stored at room temperature before use, changes take place in its mechanical properties. This phenomenon is known as strain aging. Normally these changes are observed by means of Olsen ductility and Rockwell B hardness tests but' unfortunately such tests are relatively insensitive. Strain aging can be readily observed in the laboratory by means of tensile tests. The tensile test method is even more sensitive if the aging is allowed to take place in specimens which have been prestrained in tension rather than by cold rolling. In fact one of the great benefits of commercial temper rolling is that it introduces a residual stress pattern which tends to mask the effects of strain aging when the sheet is finally used in a pressing operation. Curves B, C, and D of Fig. 1 illustrate the changes that take place during the aging of commercial rimmed steel at room temperature following straining in tension, curve A, Fig. 1. The first important change that can be observed is an increase in the stress required to produce plastic flow. This increase is, in this paper, called the aging index. As aging proceeds and the aging index increases, there is also an observable return of the yield point, an increase in the ultimate tensile strength, and a decrease in elongation to fracture. The results of strain aging in deep drawing steel manifest themselves as stretcher strains (L?ders bands) buckling, 2nd tearing. In deep drawn parts such effects are undesirable and strain aging is a serious problem. The rate of strain aging of a steel depends upon its composition and prior mechanical and thermal history? but for most temper rolled ope

Jan 1, 1958

By William Y. Holland, Roger H. Cook

Dexter H. Reynolds (Chapman and Wood, Mining Engineers and Consulting Geologists, Albuquerque, N. M.)—A number of questions are raised by conclusions and inferences made in the above-mentioned paper. The more troublesome of these concern use of the various pozzolans to combat the deleterious effects of the alkali-aggregate reaction. The most alkali-reactive materials listed are opal and rocks containing opaline silica. The pozzolans mentioned specifically for use as amelioratives are opaline shales and cherts. These are stated to retard the expansion caused by the alkali-aggregate reaction. Another well-recognized pozzolan is diatomaceous earth, which consists principally of opaline silica. A pozzolan presumably owes its effectiveness to its high reactivity with the alkaline liquid phase of the concrete mix. It appears reasonable to expect that finely divided opaline silica added as a pozzolan would be more susceptible to reaction with the alkalies present than would larger particles of the same material. The authors report that work with high and low alkali cements indicates that in the presence of alkali-reactive materials, deleterious expansion depends upon the alkali content of the cement. The total effect, therefore, should be more or less independent of the amount of reactive aggregate present, and still more independent of its state of subdivision. The deleterious effects should, if anything, be aggravated by the addition of a finely divided, highly reactive pozzolan. Further, if the alkali-aggregate reaction is of great importance in the long-term soundness of concrete structures, the addition of a pozzolan to a concrete made with aggregate free from known deleterious materials would be a questionable procedure. The benefits reportedly accruing from such use of pozzolans are greater ultimate strength for a given cement content, increased resistance to deterioration by exposure to sulphate solutions and other mineral waters, and greater resistance to damage by wetting and drying and freezing and thawing. In view of the deleterious effects of highly reactive materials are these benefits ephemeral? The same considerations apply to another alkali-reactive material, chalcedony, which appears to consist of ultrafine-grained quartz, with opal absent in detectable amounts. Quartz flour is notably reactive chemically and physiologically (cf. Ref. 11 of Holland and Cook's paper), a fact borne out by its effectiveness as a pozzolan, which presumably might be expected to offset the deleterious effects of the presence of chalcedony in the aggregate. A second question of some importance concerns the reportedly highly deleterious reactivity of acidic and intermediate volcanic glasses, such as rhyolite, perlite, and pumice. Air entrainment is listed as one of the ameliorative measures to combat the deleterious effects of the alkali-aggregate reaction. The alkalic-silica gel formed by the reaction may expand into air bubbles and thus not cause appreciable expansion of the concrete mass. It would appear then that pumice and perlite, particularly perlites of the pumiceous types and other types after expansion, would also tend to counteract the expansion, since these materials consist largely of voids and air bubbles. Certainly this would be expected of structural concrete in which pumice or perlite is used as total aggregate. Finely ground pumice, perlite, and volcanic ash have been demonstrated to be active pozzolans (cf. Pumice as Aggregate for Lightweight Structural Concrete by Wagner, Gay, and Reynolds, Univ. of New Mexico Publications in Engineering No. 5, Albuquerque, 1950). In fact, the term pozzolan was first associated with finely divided pumice or volcanic ash. Such materials were used with hydrated lime as the sole cementitious agent in constructing public buildings, roads, and aqueducts by the ancient Romans. The deleterious alkali reactivity of the volcanic glass, itself containing several percent of the alkalies, apparently did not contribute to the remarkable state of preservation of those ancient structures, as exemplified by the Appian Way and the Pantheon Dome. Still a third question involves .the reactivity of constituents of concrete when exposed to various salt solutions. Resistance to. deleterious expansion and cracking as a result of contact with mineral waters and its relationship to the mineral content of the aggregate are not mentioned by the authors. Yet the phenomena pictured in Fig. 1, and especially in Fig. 2, appear very much like those caused by exposure to mineral waters. The deterioration of concretes exposed to sulphate waters is generally considered related to the chemical constituency of the cement itself, particularly to the relative amount of tricalcium alum-inate contained. Could not many of the ill effects presently blamed on alkali-aggregate reaction really have been caused by contact with sulphate or other salt-containing mineral waters? Or perhaps their use as mixing waters? May not the deleterious expansion be as much a function of the chemical makeup of the cement as it is of the mineral constituency of the aggregate? Would it not be just as important to use alkali-free mixing water as it is to use a low-alkali cement? It appears obvious that resistance of cements and concretes to sulphate and other salt solutions cannot be left out of account in discussion of deterioration of concrete structures with time. This factor may be of equal or even greater importance than the alkali-aggregate reaction, particularly for concrete subjected to wetting and drying cycles, such as airstrip paving, water-retaining dams, and highway structures. Another very important factor is called to attention on page 1022 of the article in Mining Engineering, October 1953, in that failure of concrete structures may result from poor construction practices and use of too high water-cement ratios. Both of these can contribute remarkably to decreased resistance to attack by sulphate waters, and presumably could have an equally remarkable effect upon extent of damage resulting from the alkali-aggregate reaction. From the above remarks it appears that while alkali-aggregate reaction may be an important factor in decreasing the useful. life of a concrete structure, it is not the only factor involved, and it may not be even a controlling factor. Likewise, many of the phenomena apparently associated with the alkali-aggregate reaction may have resulted from cond'itions which had little relationship to the alkali-reactivity of a constituent of the aggregate. Certainly if alkali-aggregate reactivity is a major factor in bringing about early failure, one cannot help feeling anxiety concerning the future of the many concrete structures in this country and abroad in which pumice and perlite were used as total or partial aggregates. This anxiety can only be dispelled by calling to mind that among the best-preserved relics coming down to us from ancient times are structures made with mortars containing highly alkali-reactive aggregates.

Jan 1, 1955

By F. Weinberg

The distribution of solute during the progressive solidification of dilute Sn-Ag alloys was determined in both solid and liquid as a jbnction of growth rate, rod diameter, temperature gradient, and solute concentration, using radioactive tracer techniques. The results indicated that partial mixing occurs in the liquid during freezing for most of the conditions investigated, approaching complete mixing for larger rod diameters (>2mm) and slow growth rates. Measured solute distributions were fitted to distribution functions based on diffusion controlled solute transport in the liquid state, by treating the normal solute diffusion constant and distribution coefficient as variable solute transport and segregation parameters. Values of these parameters were determined for the growth conditions investigated. Observations were made to determine whether mixing in the liquid was primarily due to volume changes in freezing or to differences in density between solute and solvent. The former effect was investigated using a selected Sn-Bi alloy as a solvent with zero volume change on fusion, and the density effect was studied using vertical solidifications of Sn-In and Sn-Ag alloys, systems having, respectively, very small and large differences in density between solute and solvent. The result indicate that mixing in the liquid cannot be primarily attributed to either volume changes or density differences. THE solute distribution in progressively solidified rods of dilute alloys, in which there is complete mixing in the liquid, is given by the expression1 where C, is the solute concentration in the solid at the point where the fraction g of the material has solidified, C, is the initial solute concentration and k is the equilibrium distribution coefficient. If it is assumed that there is no significant con-vective mixing in the liquid, then the solute distribution in the initial portion of a semi-infinite rod has been calculated to be2 where t is the time from the start of freezing and x1 is the distance in the liquid ahead of the solid-liquid interface at time t. Expressions [1] and [2] describe the limiting cases of solute distribution in the liquid, i.e., complete mixing, or no convective mixing; in practice it might be expected that the solute distribution would be somewhere between these two cases. pfann3 has suggested that Eq. [I] is applicable for partial mixing, as well as complete mixing, if an effective distribution coefficient k1 is used instead satisfactorily describes solute distributions in rods of magnesium, n-g, and b-sb6 alloys that were progressively solidified from the melt without mechanical mixing. The values of kl were observed to depend on the growth rate4-6 and the temperature gradient.6 The purpose of the present investigation was to measure solute distributions in both the solidified rods and the melt as a function of the solidification variables, and to determine to what extent the observed solute distributions could be described by the above theoretical expressions, keeping in mind that expressions [2] and [3] have been derived solely for the case of diffusion controlled solute transport in the liquid and are not theoretically applicable to

Jan 1, 1963

By ALFRED KAUFFMAN

NO matter what position we hold, workman, foreman, superintendent, manager, president, or what not, let us fail to give or to make good products, then see how quickly we'll be called to account for- our work by the buying public. The waves of progress taught us that millions were wasted in unnecessary strikes-we also learned that many losses were due to neglect on the part of manufacturers to give the same consideration and attention to the human element of their factory as they gave to their machinery. The employees learned also that the employer was their agent who found purchasers for the product of their labor. So between the two we learned that many years of labor were needed in order for a worker to recover his wasted savings, or for the manu¬facturer to replenish his loss. Treat 'em rough, and tell 'em nothing, was not very far from the true relationship between management and employees in manufacturing plants in the early days. Today just exactly the opposite views are held by executives whose function is the handling of employees. Men today want to know what it is all about. They are intelligent enough to comprehend the facts, and to use them constructively, and it is good business to give them the information.

Jan 1, 1929

By R. B. Russell

The expansion coefficients of hexagonal (a) zirconium have been calculated from the lattice expansionparameters of both coefficientsofhexagonallow and high hafnium alloys in the range 0° to 600°C. It is found parametersofboththat the coefficients are straight-line functions of the temperature and that the effect of hafnium is to depress the mean coefficients by about 1 pct at room thattemperature and 9 pct at 600°C. The cubic (ß) form was stabilized so that its coefficient could be determined from 400' to 900°C. COEFFICIENTS of thermal expansion for hexagonal-close-packed (a) zirconium were determined up to 600°C (1112°F), without any interference from the effects of preferred orientation, by measurement of the lattice parameters obtained from a symmetrical back-reflection focusing X-ray camera. This paper combines the results for a 1.2 atomic pct hafnium alloy from an earlier report' with those for hafnium-free zirconium. The problem confronting the investigator is essentially that of getting sharp, high-angle diffraction lines which represent the material at a known constanl. temperature and chemical composition. In order to do this, it was necessary to use the proper X-ray emission wave length (Co K was chosen) and to have a fine-grained metal whose atomic spacings would be free from effects of cold work (the specimen was annealed) and to prevent a changing composition owing to gas absorption during the heating of the metal to temperature (the sample was heated in a vacuum). A summary of the effect of temperature on properties is listed in Table I which gives data for ordinary zirconium, as well as new values for the low hafnium metal. The coefficients of the linear thermal expansion that have been reported are given in Table 11. The discrepancies shown may be explained perhaps by the effect of preferred orientation, and McGeary and Lustman2 have done this successfully for sheet metal. The differences in texture cannot explain all the differences in expansion coefficient shown in Table II. liesults by the author agree most closely with those of Kroll.3 Chemical analysis of the high hafnium metal pre- viously reported1 showed that it was 98.22 atomic pct (97.40 wt pct) pure. The low hafnium metal was dehydrogenated Westinghouse crystal bar, designated SMZ-137A. Its analysis was as given in Table 111 (chemical analyses 5377, 5431, and 5432).

Jan 1, 1955

By Donivan L. Gordon, Fred H. Dorheim

Often, as viewed by the public and many in the mining industry, abandoned limestone and gypsum quarries offer a simple, economic solution to the twofold problem of solid-waste disposal and land reclamation. In a state where about 75% of the existing quarries are in hydrologic connection with carbonate aquifiers the rationale for considering the storage of solid waste in them must be critically examined. Consistent with the requirements of water resources protection, criteria are suggested to evaluate the potentiality of using abandoned limestone and gypsum quarries as sanitary landfill sites.

Jan 1, 1975

By H. M. Roche

MAGNETITE is the important iron ore of New Jersey although bog ore, limonite and red hematite were mined in sizable quantity early in the state's min-ing history. The deposits of mag-netite are found in the Highland area in the northern part of the state. These ores outcrop a broad belt 20 miles wide, extending in a northeasterly direction from Phil-lipsburg, on the Delaware River, to Greenwood Lake, at the southern boundary of the state of New York, a distance of 60 miles. The area in which the magnetite is found (see map, Fig. 1) contains 1200 square miles and the center of the area is at Dover, 40 miles west of New York City. In the general area are found 18 parallel ranges or lines of ore deposits. These ranges may be re-garded as mineralized zones in which occur orebodies that are rich enough in magnetite to war-rant mining. Usually a number of the orebodies lie one above the other in the same plane, all dipping and pitching in the same direction. Within the ranges, there may be several parallel orebodies of work-able size. The average strike of the orebodies is N.41° 30' E., with an average dip of 55° southeast and an average pitch of 15 ° to the northeast. Orebodies suitable for mining range from 6 to 100 ft. wide, as measured from foot wall to hanging wall. Their heights, as measured on the dip and normal to the long axis of the orebody, vary from 200 to 3,000 ft. The length along the pitch has never been determined by mining, al-though several of the orebodies have been worked to lengths of 10,000 ft. The grade of the ore as mined today varies from 30 to 60 per cent iron, and the gangue min-erals are chiefly silica, alumina, magnesia, lime and phosphorus.

Jan 1, 1937

By H. A. Hamza, N. E. Andersen

Emulsions have long occupied an important position in many industries. In the petroleum industry, where enhanced oil recovery techniques such as steam stimulation, flooding, etc. are being increasingly practiced, emulsions are very frequently produced. Characterization of these emulsions are an important prerequisite for monitoring and evaluation of the recovery processes. Emulsion properties will also determine the type of treatment required to separate and recover the oil phase. A variety of laboratory, pilot-scale and field-generated emulsions were characterized. Coulter technique results for size analysis are compared with microscopy (image analysis) and laser light scattering methods; Coulter determined oil contents are compared with gravimetric and volumetric methods of analysis.

Jan 1, 1980