Plasma Quench production of titanium is the thermal dissociation of titanium tetrachloride into gaseous titanium and chlorine followed by rapid quenching to prevent back reactions. Titanium tetrachloride dissociates into titanium and chlorine atoms at 5000 K. Expansion through a Delaval nozzle accelerates the gas to supersonic speed cooling it very rapidly. Cooling rates are as high as 7exp 1 0 Kelvins per second. Injected hydrogen reacts with condensed titanium particles to form titanium hydride and with the chlorine to form hydrogen chloride. We have produced titanium powder at 20 kglh in a continuous reactor. Costs are projected to be lower than the Kroll Process at large enough scale. Most of the cost reduction would result from elimination of magnesium as a reducing agent and much lower capital costs.

Jan 1, 2001

By A. Krishnan

Keywords: Tantalum extraction, SOM Technology, inert anode, membrane stability The Solid Oxide Oxygen Ion conducting Membrane (SOM) technology offers great potential for environment friendly and energy efficient extraction of high-energy content metals. This work was performed to demonstrate the technical and commercial viability of the technology to produce tantalum metal directly from tantalum oxide and ore concentrates using a solid-oxide, oxygen-ion-conducting membrane (SOM). The process can be used to efficiently produce tantalum metal without expensive pre-processing of raw materials and without harmful by products. The work reported in this paper is: the proof that high purity tantalum metal can be produced, study of the electrochemical behavior of the cell and the method to increase membrane stability.

Jan 1, 2005

By P. N. Anyalebechi

Keywords: Aluminum alloy 3004, Solidification rate, Homogenization, Second phase particles The effects of the fineness of as-solidified cast microstructure and temperature on the response of aluminum alloy 3004 to homogenization heat treatment (a.k.a. preheat) have been investigated. The study was conducted at 538oC and 595oC on directionally solidified laboratory-size ingots with a range of solidification rate of 0.10oC/s to 29.4oC/s. Optical and electron microscopy, quantitative image analysis, electrical conductivity, and electron probe microanalysis were used to quantify the effects of the homogenization heat treatment on the microstructure of aluminum alloy 3004. In general, increase in fineness of as-cast microstructure and homogenization temperature enhances the a-transformation reaction, dissolution of Mg2Si, elimination of dendritic microsegregation, and dispersoid formation. The homogenization heat treatment reduces the average size of second phase particles in castings solidified at <1oC/s. However, in castings solidified at above 1oC /s, homogenization causes the coarsening of the second phase particles. Mn in solid solution is independent of homogenization heat treatment temperature.

Jan 1, 2005

By J. K. Brimacombe, I. V. Samarasekera, B. G. Thomas

"Mathematical models have been developed for the processing of static cast steel ingots and are app1ied to investigate the mechanisms for the formation of panel cracks. Panel cracking is an intermittent but persistent defect that causes affected steel ingots to be scrapped. A two-dimensional, finite-element, heat-transfer model was formulated and employed to calculate the temperature distribution in both large and small steel ingots during the various processing stages from initial casting to the start of rolling, including solidification, cooling in the mold and in air, reheating in the soaking pit, and subsequent air cooling. The stress state in the ingot arising from the calculated temperature variations was then determined. This involved the development of a transient, elasto-visco-plastic, finite element, thermal stress model, including the effects of phase transformation volume changes and kinetics creep, and temperature-dependent, mechanical properties. The results of the mathematical model predictions of temperature and stress were then used to determine the mechanisms and to suggest solutions for two different types of panel crack formation. Mid-face panel cracks apparently form during air cooling when the mid-face surface temperature is between the Arl and 500~C. Off-corner panel cracks appear to initiate internally during the early stages of reheating but do not propagate to the surface until much later. IntroductionPanel crack formation in static-cast steel ingots is a defect that has been plaguing the steel industry for several decades. Although the problem is intermittent, it is also serious since affected ingots must be scrapped. Panel cracks are manifested as two distinct types of cracking problems. ""Mid-face"" panel cracks are found exclusively in small, 2 to 6 ton, medium carbon steel (0.3 to 0.7% C) ingots and usually exhibit a single, continuous, longitudinal crack down the center of one of the ingot faces as shown in Fig. l (l). ""Off-corner"" panel cracks often form roughly oval, discontinuous crack patterns on the wide faces of large, 20 to 30 ton ingots as seen in Fig. 2 (2). They affect only low carbon steels (0. l to 0.2% C) with high manganese content. Both defects affect only aluminum-treated steels and are caused by a combination of intermediate temperature ductility loss involving aluminum-nitride precipitation and thermal stress generation. The ductility problem has received a good deal of attention which was the subject of a recent review (3). The present study was undertaken to investigate the thermal stress aspects of the problem through the development of mathematical models of heat transfer and stress generation in static-cast steel ingots. The ultimate objective was to elucidate the mechanisms of formation for both types of panel crack and to evaluate possible solutions to the problem."

Jan 1, 1986

By R. Schuhmann

The thermodynamic data and calculations which underlie the design of the Q-S process for coppermaking are summarized. The efficient production of crude copper and slag of low copper content in a single con¬tinuous converter requires the establishment and control of gradients in oxygen activity and other physico-chemical variables throughout the reactor. These gradients are established by stagewise introduction of oxygen and solid feed materials to provide: (a) flash oxidation of sulfides above the bath, utilizing the great bulk of the oxygen, (b) conversion of high grade matte or white metal to crude copper by bottom blowing with restricted bath turbulence, (c) close approach to equilibrium staging of converting and deconverting reactions along the length of the slag layer, from a maximum oxygen activity near the metal discharge end to a minimum at the slag discharge end, and (d) completion of slag cleansing by deconverting. In terms of the Phase Rule, the Q-S process involves a system with a minimum of 5 components (Cu, Fe, S, O, and SiO2) and several liquid, solid, and gaseous phases. Accordingly, basic data from previously reported studies on simpler systems are utilized to prepare an equilibrium diagram for the 5-component system and to generate a quantitative thermodynamic model for the Q-S process. This model shows in particular the ranges of oxygen activities (measured by equivalent CO2/CO ratios) involved in the Q-S process and the relations of oxygen activity to temperature and other important physico-chemical variables of coppermaking.

Jan 1, 1976

By Theo Lehner

"The Boliden Rönnskär Smelter operates in the European Context of tight EH&S limits, with ever increasing regulations and tribulations. The near future promises to bring new burdens in the form of C02 trading, miners and pre-treaters increased appetite for a larger share of contained values, and changing compositions and competition in raw materials. On the other hand, European Smelters such as Rönnskär, Harjavalta have demonstrated an astonishing power of survival. This presentation lists and comments on current challenges but opportunities for increased survival power are also presented. One example of the latter is the ongoing investment into increased treatment capacity for e-scrap.UPDATE ON RÖNNSKÄR OPERATIONSThe Rönnskär Smelter has achieved 80 years of age with no signs of retirement. The smelter is most active in spite of its age! And it has undergone some face lift operations to maintain its attractiveness.Raw material, processing facilities and a market for the products are some essential prerequisites for a viable operation. To justify long term survival, economic terms such as return on investments and positive cash flow need to be considered. Below, we illustrate how the Rönnskär Smelter complies with these terms. To update the reader on current operations, our current flow sheet is depicted in Figure 1. The figure summarizes our current input and output."

Jan 1, 2012

By Peter Ryan

A patented process for agglomeration of Smelter ESP dusts is described. Addition of suitable binders followed by compaction, transforms fine, difficult to handle material into a dry, flowable agglomerate suitable for plant reentry. Details for the agglomeration process metallurgy and laboratory pilot plant testing are discussed. An example of full scale plant operations is described.

Jan 1, 1999

By Takahiro Miki

Soldering material widely used is Sn-Pb alloy, which have low melting point and excellent electrical, strength properties and wettability. However, Pb is one of the toxic elements, which is undesirable due to environmental and safety reasons, thus Pb-free alternative alloy is preferred for new soldering materiaL Sn-Ag and Sn-Zn based alloys have been viewed as very promising candidates, among many potential substitutes. Addition of third element to these alloys will decrease melting point of the alloys. Hence, Sn-Ag-In and Sn-Zn-Mg alloys are expected to be suitable for replacing Sn-Pb solder alloy. In order to dcsign new Pb-free soldering materials, it is crucial to understand precise thermodynamic properties and phase diagrams of alloy systems. In the present work, ion current ratios of Ag to In and Mg to Zn were measured for Sn-Ag-In and Sn-Zn-Mg alloys by mass spectrometry, respectively. Also, the authors reviewed the thermodynamic properties of terminal binary alloys determined by other researchers and evaluated a thermodynamic functions to express the excess Gibbs free energy of each binary alloy. Thermodynamic functions to express the excess Gibbs free energy of liquid Sn-Ag-In and Sn-Zn-Mg ternary alloys were determined, utilizing the assessed Gibbs free energy of terminal binary alloys with the measured ion current ratios using mass speetrometer.

Jan 1, 2003

By Kunihiko Takeda, Kimio Imaizumi, Tsuyoshi Arai

"The study on the preparation of mono-dispersed liquid droplet was performed using ultrasonic as one of the steps of producing the perfectly mono-dispersed particle. The ultrasonic system was a 33.6kHz ultrasonic generator, an amplifier, an electric distortion element, and a bolted Langevin type horn installed in .a cell. For the first time, a liquid pillar under a nozzle of the cell ·was stably formed. Then, dense and coarse parts were alternatively constructed by oscillating the wavelength of the ultrasonic.· The diameter of those liquid droplets were found to be· perfectly uniform, therefore, it was measured by ""multiplex photography"" using a synchronized stroboscope with the ultrasonic.- From the results, more than 30,000 of perfectly uniform liquid droplets in 1 second were observed by this method.IntroductionRecently, research on the control of physical form is done in various fields of industry. Some examples are the processing technology of the minute compound material of micro-machines and integrated circuits, and the form control of molecule size like catalysts. There is a need for such material to take on various forms in correspondence to its use. ""Form control"" as used in this study will indicate ""research on physical chemistry factors which determine the size of the material"" and will refer to the contour uniformity of comparatively little particles. A well-known method of preparing particles is to spout a mist of liquid and slurry from a nozzle l) 2). Particles for metals, catalysts and food have been prepared by this method. In this case, although an approximate particle diameter can be decided by controlling the nozzle diameter and the violent outflow velocity, it is not easy to completely control ·the contour and to prepare a particle with uniform diameter. ·However, the preparation of perfectly uniform particles is necessary for solders for the adhesion of electronic wiring 3), ion exchange resins4), catalysts and so on. Large quantities of fine particles and super-fine particles are generated when manufactured in the usual way. Large quantities of these fine· particles and super-fine particles have polluted the internal and external' environments of factories. The products yield' ·decreases, also. From such a background, this study examines the preparation of perfectly uniform particles that could be· collected -100% as products. Recently, NASA has succeeded in the preparation of perfectly uniform particles in zero gravity 5). But the preparation of 'perfectly uniform particles by this method is difficult, and it can not be used in general industry"

Jan 1, 2000

By B. J. Jody

At Argonne National Laboratory, we have been developing a potentially economical process to recycle automobile shredder residue (ASR). We identified three potentially marketable materials that can be recovered from ASR and developed technologies to recover and upgrade these materials. We built and tested a field-demonstration plant for recycling polyurethane foam and produced about 2,000 lb (907 kg) of recycled foam. Several 300-lb (I36-kg) samples were sent for evaluation and were found to be of marketable quality. We are also preparing for a large-scale test in which about 200 tons (181 tonnes) of ASR-derived fines «0.25 in. [<0.62 cm]) will be used as a raw material in cement making. A major cement company has evaluated small samples of fines prepared in the laboratory and found that they meet its requirements as a substitute for iron ore or mill scale. We also produced about 50 lb (23 kg) of recycled acrylonitrile butadiene styrene (ABS) from obsolete automobiles and found that it has properties that could be readily upgraded to meet the specifications of the automotive industry. In this paper, we briefly discuss the process as a whole and summarize the results obtained from the field work on foam and fines recycling.

Jan 1, 1996

By Jianjun Wang, Jiaqing Peng, Lingen Luo, Zhenbang li, Yinghe Lin

Copper removal from ferronickel by FeS has been exploring studied. It is found that the decopperizing agent FeS makes the copper removal in ferronickel effectively. The effects of FeS addition amount, carbon content in ferronickel and experimental temperature were investigated. The results showed that the removal rate of copper in ferronickel increased with the amount of FeS increasing. When the dosage of FeS is 20% (mass percentage)，the removal rate of copper can reach higher than 11%. The rate of copper removal rises with the amount of carbon content increasing in ferronickel. When the amount of carbon content is 1.86%, the removal ratio of copper is 41.3%. Higher experimental temperature promotes the copper removal reaction in certain extent. The flux is acidity and weak oxidative can also promote the reaction of copper removal.

Jan 1, 2015

By Takahiro Miki

Soldering material widely used is Sn-Pb alloy, which have low melting point and excellent electrical, strength properties and wettability. However, Pb is one of the toxic elements, which is undesirable due to environmental and safety reasons, thus Pb-free alternative alloy is preferred for new soldering material. Sn-Ag and Sn-Zn based alloys have been viewed as very promising candidates, among many potential substitutes. Addition of third element to these alloys will decrease melting point of the alloys. Hence, Sn-Ag-In and Sn-Zn-Mg alloys are expected to be suitable for replacing Sn-Pb solder alloy. In order to design new Pb-free soldering materials, it is crucial to understand precise thermodynamic properties and phase diagrams of alloy systems. In the present work, ion current ratios of Ag to In and Mg to Zn were measured for Sn-Ag-In and Sn-Zn-Mg alloys by mass spectrometry, respectively. Also, the authors reviewed the thermodynamic properties of terminal binary alloys determined by other researchers and evaluated a thermodynamic functions to express the excess Gibbs free energy of each binary alloy. Thermodynamic functions to express the excess Gibbs free energy of liquid Sn-Ag-In and Sn-Zn-Mg ternary alloys were determined, utilizing the assessed Gibbs free energy of terminal binary alloys with the measured ion current ratios using mass spectrometer.

Jan 1, 2003

By T. Asahina, M. Nakamura, M. Mabuchi, I. Shigematsu, M. Nakanishi, G. Yamauchi

"Commercial stainless steels (SUS304L and SUS430) were subjected to equal channel angular extrusion (ECAE) at room temperature to a total strain of 2.3 to 9.2. For each type of stainless steel, it was shown that the sample processed by ECAE showed higher room temperature strength than the as-quenched sample. This is probably due to the heavily worked structure. On the other hand, both strength and elongation of the ECAE processed SUS430 were increased by annealing at 773K. It is likely that higher strength is attributed to both the heavily worked structure and fine substructures. It is also likely that higher elongation is attributed to the fine substructures. It is concluded that ECAE is available for improving the room temperature strength of commercial stainless steels.INTRODUCTIONEqual channel angular extrusion ( ECAE ) is a technique that provides the repetitive deformation and allows to high intensity of deformation. With this procedure, a sample is pressed through a channel that has an equal cross section but bent at an angle of ?> [1-2]. Shear strain is introduced when a sample passes through the bending point of the channel. Repetitive processing is feasible because the cross-sectional dimension of a sample has no change during processing. To date, many reports have described that ECAE is available for the fabrication of fine-grained materials [3-14]. On the other hand, an ECAE processed sample can achieve high intensity of deformation through repetitive deformation. According to the equation given by Segal [ 2 ], a strain of about 1 is introduced in each pass through die if the angle ? is 90 deg.It is well known that high tensile strength can be achieved in metallic materials through work hardening [15]. It is also known that metallic materials with fine grain size show high strength [16]. Hence, it is expected that ECAE is available for strengthening method in metallic materials. In the present paper, we will report the mechanical properties of stainless steels processed by ECAE. As samples, SUS304L austenite stainless steel and SUS430 ferritic stainless steel were chosen. Each alloy has a single-phase structure (fee or bee) and shows no phase transformation, so that transformation strengthening cannot be applied. Hence, a heavy cold work such as ECAE may be effective for strengthening of this stainless steel. Annealing was conducted for the ECAE processed SUS430 to vary its microstructure. Then, the effect of annealing on the strength of the ECAE processed SUS430 was also investigated."

Jan 1, 2000

By Neil E. Ryan

Because of their chemical reactivity and affinity for oxygen, rare-earth elements are difficult to extract, and due to their close chemical similarity, it is an exacting task to separate one from the other. Nevertheless, these same characteristics can be used to benefit other metals by enhancing their resistance to high-temperture oxidation/corrosion and by inhibiting their corrosion in aqueous environments. This paper gives an overview of the use of rare-earths: [a] as alloy additions, [b] in coatings, and [c] when added to hostile environments, to retard rates of high- temperature oxidation and inhibit aqueous corrosion.

Jan 1, 1992

By S. B. Johnson

Keywords: Spray, Aluminum, Simulation A stochastic, droplet-resolved model has been developed to describe the behavior of a binary aluminum alloy spray during the spray-rolling process. In this process, a molten aluminum alloy is atomized and the resulting spray is deposited on the rolls of a twin-roll caster to produce aluminum strip. The one-way coupled spray model allows the prediction of spray characteristics such as enthalpy and solid fraction, and their distribution between the nozzle and the deposition surface. This paper outlines the model development and compares the predicted spray dynamics to PDI measurements performed in a controlled configuration. Predicted and measured droplet velocity and size distributions are presented for two points along the spray centerline along with predicted spray averaged specific enthalpy and solid fraction curves.

Jan 1, 2005

By A. Barba, M. P. Gómez, F. Puertas, M. Palacios, M. F. Gazulla, S. Martínez-Ramírez, I. García-Díaz

"The present study explores the reactivity and burnability of cement raw mixes containing fired red or white ceramic tile wastes or combinations of the two as alternative raw materials. The results showed that the new raw mixes containing these wastes are technically viable. The reactivity and burnability of the new raw mixes have been evaluated; confirming very good results when the particle size of wastes was less than 90 µm. The chemical and mineralogical compositions of the new clinkers were comparable to clinker manufactured with conventional raw materials. The mix of red and white ceramic tile waste was found to perform as well or better than each type of waste separately, a promising indication that separation of the two would be unnecessary for these purposes.IntroductionPortland cement clinker production consumes large amounts of energy (850 kcal/kg clinker) and has a considerable environmental impact. This involves massive quarrying for raw materials (limestone, clay etc), as it takes 1.7 tonnes to produce one tonne of clinker, as well as the emission of greenhouse and other gases (NOx, SO2, CO2) into the atmosphere. Around 850 kg of CO2 are emitted per tonne of clinker produced.The cement industry is looking for solutions to these problems, to attain sustainability and comply with the Kyoto Protocol commitments [1,2]. For that reason, experimental ways are being explored to develop cements whose manufacture is less energy-intensive, less damaging to the surrounding environment and with lower tendency to emit polluting gas. One of the reach this objective is the use of industrial waste and by-products as alternative materials for cement manufacture. Such alternative materials may partially replace fuel [3,4], conventional raw materials [5-8] or clinker in the final composition of the cement [9]."

Jan 1, 2008

By Godwin Beene

During recent years, copper and acid production from Nkana Smelter has formed a significant proportion of ZCCM&apos;s total output, but a number of problems affecting the smelter over the last decade have only been recently overcome. This paper discusses recent developments in the smelting practice, highlighting some of the operational problems experienced and associated solutions. The smelter performance over the decade is discussed and the innovations in the smelting technology employed to sustain production in the wake of limited re-capitalization are dealt with in detail.

Jan 1, 1999

By W. L. Dalmijn

The processing of scrap and scrap cars starts with size reduction by a hammermill, or shredder. After the liberation the magnetic fraction is removed. The remaining non¬magnetic fraction mixed with other materials is screened and each fraction is processed separately. The increased use of plastic has a negative effect on the recovery of metals and waste production. At Huron Valley, Belleville Michigen, USA, the non-ferrous fraction from 5 million obsolete cars per year, containing 200,000 tons of non-ferrous metal, is processed. Aluminium Is recovered with a heavy medium separation process and concentrated with eddy current separators. The remaining heavy non-ferrous fraction is concentrated by a new combination of eddy current separation and image processing. After this separation process the zinc fraction is melted and refined and the copper, brass, stainless steel and other high-quality concentrates are sold to the secondary industries. The recycling of car scrap has become an important source of metals and materials for the secondary. materials processing industry.

Jan 1, 1995

By K. Narayana Swamy

Experimental results of 3-phase mixing in a physical model of a CCRL for metals refining, at high levels of bottom gas injection (up to a superfIcial gas velocity (Us) of 12.5 cm/min), are presented. A thermal tracer technique was used to elucidate both longitudinal mixing and interphase heat transfer. The results indicate that even under conditions of significant bottom gas injection, it should be possible to maintain acceptably low longitudinal mixing (D. < 20 cm2/s and D/uL < 0.1) in the CCRL. Interphase mass-transfer coefficients of the order of 0.02 cm/s and higher, are predicted from the measured interphase heat transfer coefficients using the mass and heat transfer analogy. Adequate performance is likely to be possible for an industrial CCRL, based on extrapolation of these results to full-scale conditions.

Jan 1, 1996

"The theoretical basis of ideal smelting reduction using coal as reductant in a process employing closed loop forced-circulation of hot metal is outlined. In the proposed process, an extensive area of relatively slag-free hot metal is available as a heat sink for absorbing the large amount of heat produced by complete combustion of CO within the furnace. Any slag that is formed within the oxidizing arm of the furnace loop is quickly swept away as a thin floating layer by the bulk movement of hot metal which is induced positively by forced melt circulation and sustained by causing the hot metal and the thin slag layer to overflow into a lower level hearth in which coal is carbonised and dissolved directly into the circulating melt.The proposed process is shown to offer very substantial cost savings over all other direct smelting technology. This is mainly because of its inherently low capital cost and its high energy efficiency. Furthermore, the favourable economics are not reliant on fuel gas credits as all the process gas is combusted within the reactor itself.IntroductionMetallurgical processes in the year 2000 will be compromise solutions to the metallurgical problems that already exist today. It is common knowledge that the mineralogical complexity of certain polymetallic sulphides, for example, precludes high degrees of separation and recovery by conventional mineral beneficiation. steps are therefore being taken towards the development of a truly polymetallic smelting process which will produce simultaneously zinc lead and copper as, metals from complex ores without prior beneficiation(l). In the ferrous extraction industry, the shortcomings of the highly efficient modern blast' furnace are well known and world-wide there is considerable effort being directed towards coal-based ironmaking without the requirement of metallurgical coke as a process intermediate. The current status 0f2Joal-based ironmaking has recently been reviewed by Smith and Corbett. (2)"

Jan 1, 1988