Search Documents

By B. Wilshire, P. W. Davis

It has been shown that grain-boundary migration during high-temperature creep can reduce or even prevent the formation of intercrystalline voids, giving a considerable increase in ductility.' A similar observation has been made in a recent investigation of the creep properties of various grades of nickel and nickel alloys. The results can be illustrated by the observations made on: a) Pure vacuum-cast nickel (99.993 pct Ni) b) Impure vacuum-cast nickel (99.97 pct Ni) c) Pure nickel containing internal voids (produced by a process of intering). d) A substitutional solid solution alloy of pure nickel containing 1.16 pct Sn. All the materials were given a high-temperature anneal (>850°C) to produce a stable grain size of 7 to 10 grains per linear mm. The apparatus and techniques used to obtain the present results have been described elsewhere.' In this series, grain growth was observed only in the highest-purity, vacuum-cast metal. Thus we may consider that in the other materials grain-boundary migration was prevented by either preexisting voids or solute atoms. The effect of migration on the creep ductility of the above materials can be seen from Fig. 1, which

Jan 1, 1962

By Robert Leach

THIS paper gives a brief summary of the process of manufacture of sterling silver, and some of its more important physical properties, as observed in commercial production of rolled sheet and wire. Although papers have been published by Turner and Smith,1 Rose,2 Sperry3 and Jordan,4 there are few technical data available, and unfortunately the time allowed for the preparation of this paper has not been sufficient to make it as comprehensive as the title might indicate. ANALYSIS OF STERLING SILVER Fine or pure silver is too soft for coinage and the manufacture of articles in which strength and resistance to wear are desired. From the earliest times of which we have record, copper has been the metal generally used to harden silver. Analyses of coins and silver articles from ancient tombs show varying amounts of copper, and old Roman silver objects in the British Museum have approximately the same analysis as our sterling. The first authentic record of the establishment of a standard alloy is during the reign of Henry II in England. During the twelfth and thirteenth centuries, the people in the Eastern Provinces of Germany had a reputation for the standard and purity of their silver coinage, and it is said that Henry II employed some of these Easterlings, as they were called, to improve and standardize the English coinage, which had become debased. The peculiar standard adopted is probably accounted for by the system of weights used. A troy pound contains

Jan 1, 1928

By Frances Hurd

WHEN 60:40 brass is heated to 825° C., given a drastic quench to obtain the beta solid solution, and reheated, various changes take place in the structure. Reheating at 200' C. causes a fine, granular, sorbitic structure to appear which has been considered alpha solid solution. These particles coalesce at higher temperatures of reheating, and at 470° C., the alpha forms twins. A further study of these transformations was considered worth investigating.

Jan 1, 1927

By Allen J. Johnson

With a realization of the rapidly increasing importance of automatic stokers as a medium for domestic heating, the Anthracite Institute Laboratory has conducted extensive investigations, over a period of several years, to determine the various outstanding characteristics of stoker design and performance. The purpose of this paper is to summarize these findings as a guide to current practices. Stokees Investigated One or more models of the underfeed stokers listed below were included in the various phases of this investigation: Beckley Gilkoal Burnwell Iron Fireman Combustioneer Motor Stokor Electric Furnace Man Norristown Super-stoker Erie Heat Generator Whitney Fire Ball (Tests Incomplete.) Fuel Saver Principles of Construction.—The operating principle of the leading makes of underfeed stokers is similar (Fig. 1). A plunger1 or slowly revolving worm2, conveys the buckwheat or rice sizes of anthracite to the center of a specially constructed tuyere pot where air is admitted to the coal through suitable ports of varying design. As the fuel burns, it is slowly forced to the outside circumference of the tuyere by the pressure of the incoming coal; eventually the ash falls over the edge of the pot, either entirely by gravity or aided by mechanical sweepers. In at least one model, the entire firepot revolves. While various special details have been included in the design of a number of stokers, they do not affect the general principles as described above, and therefore have not been included in this discussion.

Jan 1, 1936

By Allen J. Johnson

With a realization of the rapidly increasing importance of automatic stokers as a medium for domestic heating, the Anthracite Institute Laboratory has conducted extensive investigations, over a period of several years, to determine the various outstanding characteristics of stoker design and performance. The purpose of this paper is to summarize these findings as a guide to current practices. Stokees Investigated One or more models of the underfeed stokers listed below were included in the various phases of this investigation: Beckley Gilkoal Burnwell Iron Fireman Combustioneer Motor Stokor Electric Furnace Man Norristown Super-stoker Erie Heat Generator Whitney Fire Ball (Tests Incomplete.) Fuel Saver Principles of Construction.—The operating principle of the leading makes of underfeed stokers is similar (Fig. 1). A plunger1 or slowly revolving worm2, conveys the buckwheat or rice sizes of anthracite to the center of a specially constructed tuyere pot where air is admitted to the coal through suitable ports of varying design. As the fuel burns, it is slowly forced to the outside circumference of the tuyere by the pressure of the incoming coal; eventually the ash falls over the edge of the pot, either entirely by gravity or aided by mechanical sweepers. In at least one model, the entire firepot revolves. While various special details have been included in the design of a number of stokers, they do not affect the general principles as described above, and therefore have not been included in this discussion.

Jan 1, 1936

By H. J. de Haan, L. Schenk

Scope for Thermal Recovery in Shell's Heavy Oil Fields in Venezuela The main heavy oil reservoirs on the East coast of Lake Maracaibo (Fig. I), known as "Bolivar Coast", initially contained some 20 billion bbl of oil in place with gravities in the range of 10 to 15° API. The current total production rate is about 400,000 B/D. Since the recovery to date is on an average only 12.5 percent of the initial oil in place, these fields offer a vast potential for secondary recovery methods. The reservoirs are characterized by moderate depth (generally 1,000 to 3,000 ft; maximum 5,000 ft), good formation properties such as net oil sand thickness (50 to 300 ft), high porosity (30 to 40 percent) permeability (1 to 3 darcies) and oil saturation (initially about 80 percent) and high oil viscosity (100 to 10,000 cp in situ), all of which are favorable for the application of thermal recovery processes. Since 1957, steam drive, steam "soak" and underground combustion have been tested or are being tested in this area.1-3 This paper deals with a major steam drive test in the Tia Juana field. The test was commenced in Sept., 1961, on the basis of encouraging results of laboratory experiments and pilot field tests, which will be discussed briefly. Early Laboratory Investigation of the Steam Drive Process In 1956 a series of model experiments was carried out in the Koninklijke/Shell Laboratorium, Amster- dam, to investigate the displacement of heavy oil by steam.' The prototype studied was a horizontal, un-consolidated heavy oil reservoir, subjected to a linear steam drive. The model, representing a slab from this reservoir along the main flow direction, consisted of a steel tube filled with oil-saturated sand, provided with layers of rock at the top and bottom to simulate conductive heat losses to cap and base rock. Lateral heat losses, perpendicular to the main flow direction, were minimized by insulating the sides of the model. Heat flow and viscosity and gravity forces were scaled by taking the steam injection rate and sand permeability inversely proportional to the geometric reduction factor of the model, and using materials (oil, steam, cap rock, etc.) identical with those of the prototype. The main feature of the process was a frontal displacement mechanism that was observed within wide ranges of injection pressure and rate, oil viscosity, initial oil saturation and sand permeability. The high stability of this front can be attributed to the high volumetric steam flow rates, combined with the reduction in oil viscosity. High recoveries were obtained due to the low residual oil saturation of about 15 percent in the zone swept by steam. The latter value pertains to the specific test conditions (heavy oil, uncon-solidated sand) and may be lower for light oil, due to the effects of steam distillation. The applicability of this experimental approach is limited, as it does not take into account the fact that

Jan 1, 1970

By Edward Capillon

THE problem of scrap is probably of greater importance inn the production of gold, silver and other precious metal alloys than is the case for base metals and alloys. Remelting of gold and silver scrap in the shop is always a costly process because it involves losses by oxidation of the base metals in the alloy with a consequent increase in the percentage of precious metal. This is most marked in the case of alloys containing the low-boiling and easily oxidized metals zinc and cadmium. Since it is. not generally feasible to assay every shop remelt it follows that the possibilities of lost values are large. So-called rolled gold and silver plate is made by soldering or welding the precious metal alloys onto base, metal. Such plate when defective must be sent to the refinery to recover the gold and silver values, thereby involving additional expense in the form of refining charges. It is obvious therefore that gold and silver alloy scrap is an important item in manufacturing cost and must be reduced to a minimum. The amount of scrap resulting from poor metal will depend on a number of factors in the manufacturing operations, not least among which is the melting and casting practice. The notes which follow are a summary of experiments performed at various times to determine what variables in melting and casting are influential in the production of sound alloys.

Jan 1, 1930

By Nicholas J. Grant, H. C. Chang

TRANSCRYSTALLINE fracture surfaces of the cleavage type have been examined by microscopy and X-rays for several metals.' These investigations revealed that the fractured surfaces were not flat and invariably had cleavage and other deformation markings on them. On the other hand, the study of inter crystalline fracture surfaces has been limited. Perryman, in a recently published paper on the inter crystalline fracture of ß-brasses,' found that a thin layer of heavily deformed metal was invariably associated with these surfaces. Furthermore, the thickness of this layer was found to depend on the orientation of the grain boundary surface with respect to the applied stress. The mechanisms of grain boundary sliding and intercrystalline fracture have been presented in two previous papers,which described certain aspects of the deformation of a 20 pct Zn-A1 alloy. It is the purpose of this paper to present some observations on the structure of intercrystalline fracture surfaces and to correlate the structure of such surfaces with the mechanism of intercrystalline fracture. Experimental Techniques—The high purity 20 pct Zn-Al alloy was generously supplied by the Research Laboratories of the Aluminum Co. of America. Two sizes of specimen were used; the first had two parallel flat surfaces of dimensions 1x0.17x0.09 in. and the second was round with a 0.25 in. diam. A grain diameter of 1 to 3 mm was obtained by annealing the specimens at 1000°F for 24 hr. The specimens were then air cooled. The specimens were subjected to creep at 500°F and 2300 psi. The rupture times ranged from % to 3 hr, with one room temperature tensile test. It has been mentioned previous1y" that the intercrystalline fracture surfaces of this alloy, when tested under the conditions given above, are sharply defined. In the optical examination of the fracture surfaces, whenever possible, magnifications of at least X250 were used. The locations of the regions examined, both optically and by X-rays, were selected to give several fracture surface orientations with respect to the stress axis and to the specimen surfaces. This was possible for the X-ray studies since the grain diameters were large compared to the X-ray beam. A film to specimen distance of 3 cm, a 1 mm pinhole and Cr radiation were used for the Laue back reflection pictures.

Jan 1, 1957

By N. G. W., Cook

When an excavation is made underground the original rock stresses are removed from the surfaces of the excavation. These surfaces converge to partially close the excavation and the superincumbent rock mass moves down towards the excavation. If the convergence of the surfaces of the excavation were controlled, energy generated by their motion against the controlling forces could be extracted. Since the total forces in the rock mass are not significantly affected by the excavation, stress concentrations arise around the excavation, which compensate exactly for those stresses no longer transmitted through the excavation. These phenomena give rise to two general principles which provide the basis for analyzing the effects of making any underground excavation. The first of these is that the total force resulting from the stresses across any plane in the rock, including any plane through the excavation, must be the same before and after the excavation is made. The second of these is that energy must necessarily be released as a result of making an underground excavation.

Jan 1, 1969

P. H. Dudley, Yew York, N. Y. (communication to the Secretary*) :—The characteristics of Professor Home's metallurgical papers are, that he is able, from the mass of confusing evidence on the subject, to make an analysis and present hypothetical and essential principles in concrete form for consideration and discussion. I can appreciate, from the practical side of the subject, the labor of collecting and investigating the data which was essential to prepare the paper. Much of it necessarily came from material of preceding years of manufacture in which time was allowed for chemical reactions of the re-carburizer, and for the elimination of the oxidation-products before teeming the ingots. This practice gave a favorable time-element to free the metal from slag and other impurities— a requisite condition for the production of sound steel in the ingots. But, in allowing them to become cold before they were charged into the furnace, a subsequent time-element entered as a detrimental factor in the development of the pipe or shrinkage-cavities, which gave an ingot-structure deficient in soundness, at least in the upper portion. (The term slag is used in a general rather than in a strictly technical sense.) Traces of manganese sulphide are often associated with manganese silicates in the same thread or seam, and at other places they are separate and distinct. Interpretations from material thus manufactured must be made with due allowances for the methods of fabrication and the requirements of service. The only way we now have to estimate what the degree of soundness of the ingot-structure was, in the early foreign and American manufacture of steel rails, is by examination of the worn and failed material after years of service. We must remember also that the poorest material was long since consigned to the scrap-heap without any full record of its history. The rails from a given ingot cannot now be identified ; and in many

Jan 1, 1909

By N. R. Morrow, C. C. Harris

The experimental points which describe capillary pressure curves are determined at apparent equilibria which are observed after bydrodynamic flow has ceased. For most systems, the time required to obtain equalization of pressure throughout the discontinuous part of a phase is prohibitive. To permit experimental points to be described as equilibria, a model of capillary behavior is proposed where mass transfer is restricted to bulk fluid flow. Model capillary pressure curves follow if the path described by such points is independent of the rate at which the saturation was changed to attain a capillary pressure point. Aemodified suction potential technique is used to study cyclic relationships between capillary pressure and moisture content for a porous mass. The time taken to complete an experiment was greatly reduced by using small samples. INTRODUCTION Capillary retention of liquid by porous materials has been investigated in the fields of hydrology,l soil science,2 oil reservoir engineering,3 chemical engineering," soil mechanics,5 textiles: paper making: and building materials In studies of the immiscible displacement of one fluid by another within a porous bed, drainage columnsl and suction potential techniques2 have been used to obtain relationships between pressure deficiency and saturation (Fig. 1). Except where there is no hysteresis of contact angle and the solid is of simple geometry, such as a tube of uniform cross section, there is hysteresis in the relationship between capillary pressure and saturation.2 The relationship which has received most attention is displacement of fluid from an initially saturated bed (Fig. 1, Curve R2), the final condition being an irreducible minimum fluid saturation Swr. Imbibition (Fig. 1, Curve A), further desaturation (Fig. 1, Curve R), and intermediate scanning curves have been studied to a lesser but increasing extent.2 ,3,9-12 This paper first considers the nature of the experimental points tracing the capillary pressure curves with respect to the modes and rates of mass transfer which are operative during the course of measurement. There are clear indications that the experimental points which describe these curves are obtained at apparent equilibria which are observed when viscous fluid flow has ceased; and any further changes in the fluid distribution are the result of much slower mass transfer processes, such as diffusion. Unless stated otherwise, this discussion applies to a stable packing of equal, smooth, hydrophilic spheres supported by a suction plate5 with water as the wetting phase and air as the nonwetting phase. The discussion can also be applied, in many

Jan 1, 1966

By T. A. Rickard

The key-note of good writing, as of good manners, is B natural. Sincerity is the first requisite for effective writing. When a man says what he knows or believes, he is likely to be interesting, because each human being possesses an individuality, a point of view, or a range of sympathy that makes him different from his fellows. To say or to write what you do no6 think, for the mere sake of talking or writing, is a verbal exercise that must be performed with extraordinary skill if it is to be attractive. Affectations are rarely attractive, rarely effective. To be natural is to be yourself, not a poseur; to give the reader the best of yourself, instead of re-warming the baked meats of yesterday. Quotations-which are second-hand thoughts-will serve occasionally when the thing you want to say has been said so well by another that it would be waste of energy to try to say it better; but, as a rule, the utterance of the writer himself is more interesting than the quotation, because the writer brings something of himself to bear on the subject, and for the moment is more in touch with the reader than any dear departed author. Therefore, say things as best you can in your own way, neither in borrowed words nor in the phraseology that mimics another. Write as if you were speaking to a person whom you desire to persuade or convince. You will then write better than you speak, because, in the first place, you can be more deliberate, and, secondly, you can revise what you have written. Speaking and writing are similar mental acts, with a difference: the difference between eating food raw and eating it cooked. Some kinds of food gain nothing by being cooked; likewise some kinds of utterance are not bettered by being written down first; but most expressions of thought, especially

Jan 1, 1931

Strain-Hardening Exponent of Cross-Rolled Beryllium Sheet by S. R. Maloff, Vol. 215, No. 5, page 872, was omitted from Table of Contents for the October issue. Stabilization Phenomena in Beta Phase Au-Cd Alloys by Howard Birnbaum, Vol. 215, No. 5, page 786. The figure denoted Fig. 1 should be Fig. 3, Fig. 3 should be Fig. 4 and Fig. 4 should be Fig. 1. The captions are in the proper sequence. Activity of Carbon in Liquid Iron Alloys by Tasuku Fuwa and John Chipman, Vol. 215, No. 4, page 708. First equation, right hand column, page 710 should read

Jan 1, 1960

By R. E. Holmes, T. W. Leland

The solution to the unsteady-state mass- and heat-transfer equations describing the adsorption of a dilute component from a gas stream flowing through a packed bed is readily applicable to the design of hydrocarbon recovery units. The solution to these equations depends on the assumption of a linear equilibrium equation to relate concentrations on the surface to concentrations in the gas. This assumption is shown to be justifiable for components which are very dilute in the gas stream. This approach permits the prediction of the effects of bed shape and size, cycle time, and gas mass velocity on the recovery of each component. It also allows the time and gas flow rate needed for regeneration to be determined. The equations involve a constant for each component and another constant characterized by the type of adsorbent. These constants must be evaluated from operating data. Values of these constants determined for silica gel are presented. This paper points out the type of experitrrental data needed for a thorough design of hydrocarbon adsorption units. INTRODUCTION The growing importance of adsorption processes to recover hydrocarbons from natural-gas streams has created an urgent need for better methods to design and predict the performance of these processes. Since the original use of solid adsorbents in natural-gas processing was for dehydration, most of the current design methods for hydrocarbon recovery re extensions of those developed earlier for dehydration. These methods are based on an adsorptivity or bed loading factor defined as the amount of a particular component adsorbed per unit weight or per unit volume of the packed bed. The recovery of a given component is then expressed as an empirical function of its adsorptivity on a given adsorbent. In spite of the simplicity and initial utility of these methods, they are not completely satisfactory in that they do not predict the effect of the dimensions of the bed in relation to flow rate and cycle time, and do not predict the distribution of various components along the length of the bed. It is possible, however, to make a considerable improvement in the design of these processes by applying the basic equations of mass and heat transfer applicable to gases containing small concentrations of adsorbing components flowing through granular beds. These equations have been developed and solved by Anzelius,' Furnas,% nd Hougen and Marshall." where G = mass velocity of the inert constituents (assumed to be methane), lb/hr-sq ft, y = weight of an adsorbing component in the gas per unit weight of inert, lb of a given constituent per lb of methane, x = bed length, ft, p, = packed bed density, lb/cu ft, P, = gas density, Ib/cu ft, f = void fraction in the bed, t = time, hours, and w = weight of a given component adsorbed per unit weight of adsorbate free solid, Ib/lb pure adsorbent. The term on the left side of Eq. 1 represents the flow rate per unit bed volume of a component entering less the flow rate per unit bed volume of that component leaving the differential bed length. The terms on the right side represent, respectively, the accumulation rates per unit bed volume on the solid and in the gas phase within the differential bed section. The last term is negligible for this application since pgfv is quite small in comparison with p, and G. The partial differential is determined by the mass-transfer rate between gas and solid in the differential section.

By D. H. Woodard, G. W. Geil, W. D. Jenkins

In a series of papers, the authors and their associates have shown the influence of four important factors on the technical cohesion limit.3-l6 By "technical cohesion limitv is meant the technically determin-able resistance to fracture. The four importarlt factors are the stress system, plastic deformation, temperature, and the strain rate, The influence of any one of these factors may be represented by a curve of cohesion limits, although only one point on the curve may represent actual fracture. As the term "fracture stress" has come into general use with the same significance as technical cohesion limit, the authors are here using the shorter term with the understanding that it does not always refer to actual fracture. The previously mentioned series of papers contains ample evidence that plastic extension increases the fracture stress of any polycrystalline metal, In a recent paper of the series,l5 moreover, it has been shown that the effect of plastic deformation on the fracture stress cannot be attributed to reorientation of internal flaws but is a work-strengthening effect, similar to the effect on the flow stress, $ Plastic deformation of steels, however, may not only cause work hardening, but may result in additional hardness because of strain aging. Some evidence that strain aging affects not only the flow stress but also the fracture stress, has been presented in a recent paper.14 In that paper, a study is made of the influence Of Plastic deformstion at room temperature on the fracture stress of ferritic steels at -188°C. The study is based on the results Of two-stage tests. In the first stage each specimen was extended a predetermined amount at room temperature; in the second stage the specimen was tested to fracture in liquid air. In most Of these tests the specimen remained in the testing machine during the interval of about one hour between the first and second stages, it was kept under a tensile load of about 500 lb and maintained at liquid air temperature. The effects of various amounts of .plastic deformation on the fracture stress were thus determined and curves were obtained to represent the influence of plastic deformation at room temperature on the stress at brittle fracture in liquid air.14 Two specimens Of ingot iron, however, were removed from the testing machine at the end of the first stage and several days elapsed before the specimens were tested to fracture in liquid air, As shown in Fig 8 of that paper," the points representing fracture of these specimens are far above the curve representing the results of two-stage tests without a rest interval between the stages. The evidence thus indicated that the fracture stresses of these two specimens were increased not

Jan 1, 1949

By G. W. Geil, D. H. Woodard, W. D. Jenkins

In a series of papers, the authors and their associates have shown the influence of four important factors on the technical cohesion limit.3-l6 By "technical cohesion limitv is meant the technically determin-able resistance to fracture. The four importarlt factors are the stress system, plastic deformation, temperature, and the strain rate, The influence of any one of these factors may be represented by a curve of cohesion limits, although only one point on the curve may represent actual fracture. As the term "fracture stress" has come into general use with the same significance as technical cohesion limit, the authors are here using the shorter term with the understanding that it does not always refer to actual fracture. The previously mentioned series of papers contains ample evidence that plastic extension increases the fracture stress of any polycrystalline metal, In a recent paper of the series,l5 moreover, it has been shown that the effect of plastic deformation on the fracture stress cannot be attributed to reorientation of internal flaws but is a work-strengthening effect, similar to the effect on the flow stress, $ Plastic deformation of steels, however, may not only cause work hardening, but may result in additional hardness because of strain aging. Some evidence that strain aging affects not only the flow stress but also the fracture stress, has been presented in a recent paper.14 In that paper, a study is made of the influence Of Plastic deformstion at room temperature on the fracture stress of ferritic steels at -188°C. The study is based on the results Of two-stage tests. In the first stage each specimen was extended a predetermined amount at room temperature; in the second stage the specimen was tested to fracture in liquid air. In most Of these tests the specimen remained in the testing machine during the interval of about one hour between the first and second stages, it was kept under a tensile load of about 500 lb and maintained at liquid air temperature. The effects of various amounts of .plastic deformation on the fracture stress were thus determined and curves were obtained to represent the influence of plastic deformation at room temperature on the stress at brittle fracture in liquid air.14 Two specimens Of ingot iron, however, were removed from the testing machine at the end of the first stage and several days elapsed before the specimens were tested to fracture in liquid air, As shown in Fig 8 of that paper," the points representing fracture of these specimens are far above the curve representing the results of two-stage tests without a rest interval between the stages. The evidence thus indicated that the fracture stresses of these two specimens were increased not

Jan 1, 1949

By Robert W. Hunt

I have repeatedly said that the mechanical treatment of the metal forming a steel rail, during its manufacture, was comparatively of much greater importance than its chemical composition; and years of observation have confirmed and emphasized this fact. ' The comparison of the wear of the earlier steel rails with that of later ones, and to the great disadvantage of the latter, ia still being constantly made by railway oficials. And while some of us, with experience covering the whole history of the manufacture of steel rails, are aware of the great differences in the conditions governing their production at various periods, I do not think the engineering world generally appreciates the direct and imperative influence which these variations have had, and are having, upon the wearing-quality of the rails. In the earlier days, the steel was poured into ingots which would make but two 30-ft. rails not exceeding a weight of 60 lb. per yard—giving a mass weighing, say about 1,400 lb., and of a section of about 12 in. square. To-day the ingots are about 22 in. square, and weigh more than 4,000 lb. Of course, the interior of the larger ingots must remain hot and liquid longer than that of the smaller ones, and from this condition arises the steel-rail makers béte noire—segregation of the metalloids and piping of the steel. Ingots of the smallest section will pipe, but with the increase of the size, so will follow that of the interior cavity. This well-known tendency demands that special care should be exercised to avoid the evils arising from it.

Jan 1, 1905

By Paul R. Dingess, Edward H. Hare, Douglas C. Brockie

Mining in the Tri-State district of Missouri, Kansas, and Oklahoma has been nearly continuous from about 1848 until the present day, although the major activity was from about 1880 to 1955. The district, which has produced over $2 billion in zinc and lead concentrates, ranks as one of the greatest mining districts in the world. Unlike other Mississippi Valleytype deposits in the United States, which occur in Cambrian and Ordovician limestones and dolomites, the Tri-State district ores occur in Mississippian limestones containing abundant chert. Zinc is 5 to 6 times more abundant than lead. In the Picher Field, the principal sub-district which has accounted for 61 percent of the total district production, most of the ore has been mined from the single horizon, M bed. Most ore bodies, other than those of the "Sheet Ground" or blanket-type, are in large, essentially flat-lying breccia zones and have a definite mineral zonal pattern. An irregular, generally elongated central dolomitic core is surrounded progressively outward by the main ore run, the jasperoid zone, the muddy or shaly and bouldery zone, the sparry calcite limestone zone, and the fossiliferous, dominantly crinoidal, limestone zone. Some of the zones may be absent or nearly so and may overlap to some extent with an adjacent zone. Although the district has been studied by many authors, much controversy still exists about such items as genesis, paragenesis, and time of emplacement. These subjects are discussed in the paper.

Jan 1, 1968

By C. G. Goetzel

E. V. Crane.*—I want to ask Dr. Goetzel concerning the control of atmosphere in heating and pressing. Was the heating and pressing done in the die, or were the two kept separate there? C. G. Goetzel.—The setup used for this investigation implied heating the die to the temperature at which the work was to proceed, introducing a preformed compact into the hot die. The atmosphere was supplied through an annular chamber from which it passed through two holes into the die cavity. E. V. CRane.—The compact was not preheated? C. G. Goetzel.—The compact was not preheated. Tee Chairman.—In the course of recent studies on the effect of time of heating upon the tensile strength and hardness, I have observed that there is often a maximum in tensile strength and hardness reached before complete homogenization has been attained. The magnitude of each mechanical Property changes rapidly with time in the early stages of sintering, the more so as temperature increases. For these reasons it seems that the comparison of values obtained by heating for the same time at a series of temperatures may be deceptive. Not only may those heated at higher temperatures give higher tensile readings, but the reverse may be true if the maximum in the tensile strength versus time curve has been passed. A better basis for comparison would be that of equal degree of diffusion. C' " Goetzel.—Thank you, Professor Rhines, for this interesting contribution. I would like to add here that I have noticed a similar effect with straight copper. There is, of course, the possibility that this maximum in hardness and tensile strength may be caused by work-hardening.

Jan 1, 1945

By R. L., Fullman

During the past year there have been a number of significant investigations that have furnished evidence on the driving forces governing grain growth and on the role played by boundary impurities. Thus Burke has shown that in high purity alpha brass the rate of grain growth in the earliest stages is approximately inversely proportional to the existing grain size. This relation agrees with one derived by Zener assuming that surface energy was the driving force in grain growth. Also in confirmation of the surface energy hypothesis, Burke found that growth virtually stopped when the grain boundaries or even only the grain corners were melted.

Jan 1, 1949