By P. Beardmore, A. H. Holtzman, M. B. Bever

Specimens of the alloy CU3AU in the ordered and disordered states were subjected to explosive loading at shock pressures in the range from 160 to 475 kbars. The resulting changes in the resistivity, stored energy, microhardness, and microstructure were determined. By comparing the effects of explosive loading on ordered and disordered specimens a separation of structura1 and configurational changes has been made. In the pressure range from 290 to 370 kbars, representing a small increment of strain, the degree of long-range order in the ordered alloy decreased sharply. This change is attributed to the generation of shear stresses in excess of the theoretical shear strength of the alloy. Disordered CU3AU under explosive loading behaves in a manner considered to be characteristic of fee solid-solution alloys generally. The response of metals to high-velocity deformation and, in particular, to explosive loading has attracted much interest in recent years.' In general, metals are substantially strengthened by the passage of shock waves although the permanent strains are small. Explosive loading induces this strengthening by causing the metal to undergo rapidly a transient strain in a narrow region, first in the shock front and then in the rarefaction wave, which releases the pressure. The transient strain is given by e = 4/3 In V/Vo, where Vo and v are the specific volumes in the uncompressed and compressed states.2 The process produces many defects, which account for the strengthening. For the investigation reported here, an ordered alloy was chosen because it was expected to give sensitive indications of the near-neighbor effects produced by shock waves. The ordered alloy CU3AU was of special interest because of past work on the effects of conventional deformation on this alloy.314 The disordered alloy was included as a standard for comparison and as an alloy typical of a solid solution containing short-range order. The effects of explosive loading were followed by measurements of the resistivity, stored energy, and microhardness, and by metallographic examination. EXPERIMENTAL PROCEDURES Preparation of Specimens. Part of an ingot of the alloy Cu3Au prepared previously4 was cold-rolled with several intermediate anneals in vacuum to a final thickness of 0.042 in. Specimens of dimensions 2.0 by 1.0 by 0.042 in. were machined from this strip. After a recrystallization treatment of 1 hr at 565oC, half of the specimens were disordered by heating in evacuated Pyrex capsules for 1 hr at 460°C and quenching into water. Although they contained short-range order, they will be referred to as 'disordered" to indicate the absence of long-range order. The rest of the specimens were cooled slowly from 380°C to induce long-range order. The grain size of the ordered and disordered specimens was 0.012 mm. Explosive Loading. This was carried out at the Eastern Laboratory, Explosives Department, E. I. du Pont de Nemours & Co., by a driver-plate procedure described elsewhere.2 Two ordered specimens were stacked alongside two disordered speci-

Jan 1, 1964

By E. W. Hart, W. R. Hibbard

The room temperature flow characteristics of a series of Cu-Cr alloys are found to be related to the amount and characteristics of the chromium-rich precipitate. The results are consistent with the theory of Fisher, Hart, and Pry, which considers the trapping to dislocation loops around precipitate particles. THE use of dispersed phases for hardening metals, particularly high temperature alloys, has been practiced for several years. Current theories describing the effects of dispersions on the basis of dislocation theory have been proposed by Mott and Nabarro.l-4 rowan," and Fisher, Hart, and Pry.8 These theories recently have been discussed by Hart,' who pointed out that the experimental data available for comparison with theoretical calculations for overaged alloys are confined to studies by Gensamer, Pearsall, Pellini, and Low,8 Shaw, Sher-by, Starr, and Dorn,9 and some hitherto unpublished data on Cu-Cr alloys which will be described herein. Certain difficulties were associated with the interpretation of the first two studies. Gensamer, Pearsall, Pellini, and Low were concerned principally with interparticle spacing and did not document particle sizes. Shaw, Sherby, Starr, and Dorn included all the data in their report which was necessary for the theoretical evaluation, but their study is subject to some question1" due to difference in prior history of various specimens and due to systematic differences in particle characteristics" which appeared to be associated with differences in the magnification of their microscopic examination. The current study was undertaken to obtain critical data in a manner which avoids some of these limitations. Specimens of eight Cu-Cr alloys remaining from a previous investigation'' were available in the form of 100 mil sheet of the compositions shown in Table I. At 200 mil this material had been previously an- nealed ½ hr at 1000°C, water quenched, and cold rolled 50 pct. Samples were further cold rolled to a thickness of 20 mil for a total reduction of 90 pct. Sheet tensile specimens of standard geometry with a gage length 2½ in. long and 0.20 in. wide were machined from this sheet. These specimens were then annealed in a dried N2-H2 atmosphere for the times and temperatures indicated in Table I. This anneal served two purposes: 1—to obtain a fairly uniform and nearly constant grain size of 0.015 to 0.022 mm average diameter, and 2—to precipitate a fairly uniform, nearly spherical over-aged dispersion of essentially pure chromium. A typical microstructure illustrating the grain size and the uniformity of the dispersion is shown in Fig. 1. A typical dispersion illustrating the range of sizes and shapes of the particles is shown in Fig. 2. The tensile specimens were tested in the Instron equipment described in ref. 11 at room temperature at a strain rate of 0.04 in. per in. per min. Three tests were run on each alloy with sufficient repro-ducibility that a single true stress-true plastic strain curve could be drawn through the three sets of data for each alloy. Typical curves are shown in Fig. 3.

Jan 1, 1956

By Robert C. Linares

Cubic zinc sulfide has been grown from molten salt solutions substantially below the hexagonal-cubic phase transition of 1020°C. Crystals free of birefringence have been grown from molten lead chloride at temperatures from 500° to 800°C. Factors affecting the optical transmission and the birefringence are discussed. CUBIC zinc sulfide is of interest for electrooptic devices and as an optical coating material. However, it cannot readily be produced as large crystals which are free of birefringence. The birefringence arises from the fact that the cubic ZnS is usually grown as the high-temperature hexagonal phase and is transformed to the lower cubic phase by annealing.' This results in stacking faults, stress, and birefringence. A requirement for the growth of cubic ZnS is that it be grown below the phase transition of 1020°C.2 Crystals of cubic ZnS have been grown below 1020°C by the hydrothermal,3 flux,4 and vapor transport5 techniques. However, these all appear to have limitations in size or quality of material produced. It was felt that a new flux method might have a good chance of overcoming some of the previous problems. Mita6 reported the growth of hexagonal ZnS from molten NaCl and wilke7 reported the growth of iron sulfides from molten lead chloride solution, indicating that molten chlorides make good solvents for sulfides. An investigation of a number of possible molten chlorides as solvents showed that molten PbCl2 has an appreciable solubility for zinc sulfide and that crystals can be grown at temperatures from 500° to 800°C. EXPERIMENTAL Crystal growth was performed in open or sealed Vycor or fused silica tubes, in an argon atmosphere or vacuum. There were no deleterious effects due to using vacuum; however, a sealed essentially isothermal system must be used to prevent vapor transport mechanisms from dominating. This will be discussed later in detail. Noble metal containers were not usable as they were severely attacked by these melts. The materials used were: reagent-grade PbC12, reagent-grade ZnS, optical-coating-grade ZnS, and Irtran 2 (ZnS). Crystal growth was accomplished by both slow cooling techniques and gradient growth techniques. In the slow cooling techniques, 15 g of ZnS and 100 g of PbCl2 were used. The components were placed in the silica tube, heated at 800°C for 2 hr, and then slowly cooled (l° to 10° C per hr) to 500°C. The furnace was constructed so that the tube could be inverted, thus allowing the liquid to drain off the crystals at the end of the run. The gradient runs were made by placing the above mixtures in a silica tube at 550° to 600°c, Fig. 1. A temperature gradient was maintained such that the floating mass of undissolved sulfide was 10° to 50°C warmer than the bottom of the tube. Growth occurred on spontaneously nucleated sites at the cooler bottom. RESULTS When using high cooling rates (5° to 10°C per hr), crystals form in thin sheets perpendicular to the {111} face. Crystals 5 by 5 by 1.2 mm, Fig. 2, have been ob-

Jan 1, 1969

By R. M. Brick, J. T. Richards

Tests have been conducted to determine the mechanical properties of several beryllium copper alloys down to liquid air temperatures. The materials investigated include beryllium copper, beryl-lium-cobalt-copper, and beryllium-zinc-copper in the wrought and cast conditions. As a means of evaluation, the influence of cold work and age hardening treatment upon subzero behavior has been observed. The effects of temperature upon both elastic and plastic deformation are also considered. THE low temperature mechanical properties of beryllium copper are of current interest in view of the increasing number of subzero applications. At extremely low temperatures, beryllium copper components are employed in temperature control and gas liquefaction equipment. At more moderate temperatures, such as those encountered in arctic regions, these alloys find use in a wide range of civilian and military applications. Although several previous subzero investigations have included beryllium copper,'-' none have been complete with respect to test temperatures or materials employed. As indicated in Table I, the alloy: used by Colbeck and MacGillivray,1 Walle,2 and Kostenets' were nonstandard and were not representative of present commercial practice. In addition, Kostenets4 did not test age hardened specimens, while the temperature in the other investigations", "-' were not carried below —100°F. These tests, however, indicate that beryllium copper offers interesting possibilities in subzero atmospheres, since the increase in strength with decreasing temperature is not accompanied by a reduction in ductility or impact resistance. As a means of checking and extending this earlier work at subzero temperatures, an investigation was undertaken at the University of Pennsylvania. In addition to testing the standard 2 pct beryllium copper, other alloys were also considered in wrought and cast forms. Charpy impact and tension tests were included with particular emphasis on the elastic characteristics, since beryllium copper is frequently selected for its spring qualities. Nominal test temperatures were +80°, —75", —200°, and —300°F. Test Materials Wrought beryllium copper, beryllium-cobalt-copper, and beryllium-zinc-copper specimens were machined from 0.560 in. diameter rod. These alloys were tested in the solution treated, cold drawn, or age hardened conditions. In the case of solution treated beryllium copper, some specimens were aged (3 hr at 600°F) for maximum hardness and others were overaged (1 1/2 hr at 750°F) to determine the effect of heat treatment. The compositions and average room temperature properties of these wrought alloys are presented in Table 11. The casting alloy versions of beryllium copper and beryllium-cobalt-copper were prepared as sand-cast cylinders, roughly 3/4 in. diameter x 6 in. long. Test specimens were machined from these cylinders. Conditions tested included as cast as well as solution treated and age hardened. Table 111 lists compositional and room temperature property data for the cast alloys. Test Methods Tension tests were conducted on specimens having a 0.25 in. diameter reduced section over a 1 in. gage length. To insure axiality, specimens were loaded by means of hardened chains. The yield strength at 0.2 pct offset was obtained from autographically recorded stress-strain curves resulting from a spe-

Jan 1, 1955

By C. H. Mathewson, H. l. Burghoff

The study of the creep of metals under conditions of prolonged loading has received the attention of many investigators for several years and almost innumerable papers have been published on the various aspects of the subject. As it appeared that much could still be learned from a study of single crystals, the present work was carried out to study the effects of temperature and conditions of loading upon the properties and deformation in tension of single crystals of alpha brass containing about 70 per cent copper and go per cent zinc. In particular, it was hoped to obtain information from tests below and above the recrys-tallization temperature of the material, so that properties such as elastic limit, yield point or critical stress, and manner of deformation might be compared for tensile tests at an ordinary loading rate and for prolonged loading. Accordingly, short-time tensile tests and creep tests were made at room temperature, 300°, 500° and 700°F. The two latter temperatures are above the lowest possible recrystallization temperature of polycrys-talline 70-30 brass. Previous Work Clarke and White1 have made creep tests of some copper-zinc alloys, including 70-30 brass, and copper-zinc-tin alloys at temperatures both below and above the recrystallization temperature of the materials considered. Hanson and Wheeler2 have studied the flow and fracture of single crystals of aluminum for short-time and prolonged tensile loading over a range of temperature extending from room temperature to 400°F., their experiments being made without consideration of the orientations of the test specimens. Extensive creep and fracture tests on single crystals of lead at room temperature have been made by Betty3 and by Baker, Betty and Moore." Results of the last-named investigation were published while the present work was in progress. Miller5 examined the elastic limit of zinc single crystals at and above room temperature by means of creep tests, while Miller and Milligan6 reported the results of tests designed to show the influence of temperature on elastic limit of single crystals of aluminum, silver and zinc. The behavior of iron crystals under static tensile loading at room temperature was reported by Gensamer and Meh17 while the present investigation was in progress. Their specimens exhibited a well-defined yield point, below which no appreciable creep could be detected. The manner of yielding proved interesting, as the shape of the creep-time curve for the iron crystals differed from the common type of crcep curves. Elongation did not begin immediately, or at least was initially very slow. The rate of elongation then increased continuously and finally decreased to zero. This S-shaped type of elongation-time

Jan 1, 1941

By James K. Stanley

Preferred orientation, particularly in irons and low-carbon steel, is a phenomenon that is both of considerable importance and theoretical interest. At times it is a liability and at other times an asset. In deep-drawing operations, preferred orientation is extremely undesirable because it necessitates trimming operations and increases scrap loss. Furthermore, oriented metals are likely to crack more easily than randomly oriented material because the forming of symmetrical and unsymmetrical shapes out of preferentially oriented metals and alloys increases the probability of rupture in regions of high stress, owing to differential ductility.' In the electrical industry, on the other hand, preferentially oriented silicon irons are in demand for transformer application because of the improved magnetic permeabilities in the rolling direction.2 This phenomenon of preferred orientation in soft magnetic materials has been responsible for the tremendous improvement in transformer design and construction in recent years. Directional properties in metals have received a great deal of attention in the metallurnical -literature,3-9 in which much of the information reported about orientation has been obtained by conventional methods, mechanicai properties and X-rays. A wealth of data has been obtained and often at a great expenditure of time. The recent introduction of the magnetic torque measurements on ferromagnetic materials provides a very simple and rapid method of evaluating orientation. The judicious use of the method can supply important information, but it should be borne in mind that such studies must be supplemented by X-rays, optical methods,10 and etch and pressure figures" to get a rational understanding of the orientation phenomena. No claims are made that the magnetic torque of evaluating orientation will reveal the behavior of the metal in deep drawing. For this purpose the accepted tests for deep-drawing quality must be used. For a good drawing stock, which must have low impurities, desirable grain size, ductility, strength, hardness, good surface, random orientation, and good recrystallization behavior, it cannot be expected that any simple test will be satisfactory for appraising all the factors. The only factor on which the magnetic method can be used is orientation, which is, of course, of considerable importance. When directionality can cause a 10 to 15 per cent change in tensile strength and a IOO to 300 per cent change in tear length,12 it goes without saying that a reliable as well as rapid method for detecting these changes would be desirable. There are certain inherent advantages in testing orientation by the torque method: The method is rapid with the proper type of equipment; no elaborate preparation of specimens is required—it is only necessary to punch or machine a I-in. disk of the sheet material and insert it into the testing device.

Jan 1, 1944

By W. R. Hibbard

Although extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110) , [111] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampton5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr in a standard mer-curous nitrate test. Edmunds12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wasserman11 reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. Preparation OF Specimens Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5, 10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. Determination of Pole Figures A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pet nitric acid to 0.0015 in. thickness and (111) pole figures were determined using copper K-alpha radiation in the manner described by Brick.' The three general types of pole figures

Jan 1, 1949

By W. R. Hibbard

Although extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110) , [111] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampton5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr in a standard mer-curous nitrate test. Edmunds12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wasserman11 reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. Preparation OF Specimens Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5, 10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. Determination of Pole Figures A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pet nitric acid to 0.0015 in. thickness and (111) pole figures were determined using copper K-alpha radiation in the manner described by Brick.' The three general types of pole figures

Jan 1, 1949

By H. l. Burghoff, C. H. Mathewson

The study of the creep of metals under conditions of prolonged loading has received the attention of many investigators for several years and almost innumerable papers have been published on the various aspects of the subject. As it appeared that much could still be learned from a study of single crystals, the present work was carried out to study the effects of temperature and conditions of loading upon the properties and deformation in tension of single crystals of alpha brass containing about 70 per cent copper and go per cent zinc. In particular, it was hoped to obtain information from tests below and above the recrys-tallization temperature of the material, so that properties such as elastic limit, yield point or critical stress, and manner of deformation might be compared for tensile tests at an ordinary loading rate and for prolonged loading. Accordingly, short-time tensile tests and creep tests were made at room temperature, 300°, 500° and 700°F. The two latter temperatures are above the lowest possible recrystallization temperature of polycrys-talline 70-30 brass. Previous Work Clarke and White1 have made creep tests of some copper-zinc alloys, including 70-30 brass, and copper-zinc-tin alloys at temperatures both below and above the recrystallization temperature of the materials considered. Hanson and Wheeler2 have studied the flow and fracture of single crystals of aluminum for short-time and prolonged tensile loading over a range of temperature extending from room temperature to 400°F., their experiments being made without consideration of the orientations of the test specimens. Extensive creep and fracture tests on single crystals of lead at room temperature have been made by Betty3 and by Baker, Betty and Moore." Results of the last-named investigation were published while the present work was in progress. Miller5 examined the elastic limit of zinc single crystals at and above room temperature by means of creep tests, while Miller and Milligan6 reported the results of tests designed to show the influence of temperature on elastic limit of single crystals of aluminum, silver and zinc. The behavior of iron crystals under static tensile loading at room temperature was reported by Gensamer and Meh17 while the present investigation was in progress. Their specimens exhibited a well-defined yield point, below which no appreciable creep could be detected. The manner of yielding proved interesting, as the shape of the creep-time curve for the iron crystals differed from the common type of crcep curves. Elongation did not begin immediately, or at least was initially very slow. The rate of elongation then increased continuously and finally decreased to zero. This S-shaped type of elongation-time

Jan 1, 1941

By C. Burton Clark, J. Spotts McDowell

Refractories are defined as "materials having the ability to retain their physical shapes and chemical identities when subjected to high temperatures," or as "nonmetallic materials suitable for the construction or lining of furnaces operated at high temperatures." While resistance to "high" temperatures is thus the primary requirement for refractory materials, it is by no means the sole requirement. They must be able to withstand thermal shock resulting from rapid heating or cooling; other stresses induced by temperature change; pressures from the weights of furnace parts or contents; mechanical wear (abrasion) resulting from movement of furnace contents; and chemical attack by heated solids, liquids, or gases. Refractories of many kinds are needed for the many and widely diversified industrial applications. Those in greatest demand are classified on the basis of composition or properties into a few main groups, known as alumina-silica, silica, basic and insulating refractories. In each of these groups there are several classes. In addition to those included in the main groups, there are various special refractories, including silicon carbide, carbon, zircon, zirconia, alumina, and several others. Alumina-silica refractories comprise two main divisions: fire clay and high-alumina. The alumina content of fire-clay refractories covers the range from about 45 pct to 18 pct, and the silica content from 50 pct to 80 pct. The alumina content of fired high-alumina refractories ranges from about 99 pct to 45 pct, and the silica content from about 0.5 pct to 50 pct. Silica refractories of the different classes contain 94 pct to 97 pct silica. Basic refractories include periclase (magnesite), chrome spinel, forsterite, and dolomite. Refractory materials, including insulating firebrick, are supplied mainly as preformed shapes. Other products include bonding mortars and high temperature cements, ramming mixtures, plastic firebrick, hydraulic setting castables, dead-burned grain magnesite, and dead-burned dolomite. Refractory brick are classified on the basis of their physical form as Standard Sizes and Special Shapes. The Standard Sizes are brick of certain definite sizes and relatively simple design which are used in sufficient amounts to permit quantity production. The brick most widely used are the standard 9 in. X 4 ½ in. X 2 ½in. and 9 in. X 4½in. X 3 in. straights and corresponding series of sizes. All brick of nonstandard dimensions are regarded as "special shapes." They include a wide variety of brick regularly used for specific services, such as baffle tile for boilers, checker brick for regenerators, and others; together with shapes of special design manufactured on particular orders from designs submitted by the user. Not included in the broad classifications of Standard Sizes and Special Shapes are several specific-service refractory products, usually made by companies which specialize in their manufacture, or in some cases by the consumers themselves. These products include

Jan 1, 1960

By J. M. Seeman, R. A. Dodd

If some solution-quenched supersaturated aluminum solid solutions, e.g.., Al(Cu), are plastically deformed at room temperature and then aged at 200oC, the hardness may first decrease before increasing in the usual manner ' A similar transient softening is observed, even in the absence of plastic deformation, when a thin foil or small-diameter wire Al(Cu) specimen is rapidly quenched from the solution-treatment temperature and then aged.' Also, some solution-quenched and neutron-irradiated alloys undergo an initial hardness decrease during subsequent aging.3 The usual explanation of the transient softening in the above examples involves the effect of vacancies introduced by plastic deformation, rapid quenching, and neutron irradiation, respectively However, the mechanism of softening is not unequivo-cably established. In the first-noted case, Gane and parkins' observed that the softening was approximately proportional to the difference in the atomic diameters of solute and solvent, and it was argued that, if a large relative difference in atomic diameter promoted vacancy-assisted room-temperature solute diffusion to dislocations, dislocation climb occurring during subsequent aging at 200°C could cause transient softening. Some substantiation of this theory was offered by the additional observation that discontinuous yielding of solution-quenched polycrystalline Al(Cu) tensile specimens was suppressed by interrupting the test for a short aging treatment at 200°C. Of course, reversion (resolution of GPI) at 200°C would also cause softening, and Sil-cock4 expressed the opinion that the softening in the case of Al(Cu) must be partly associated with reversion. Also, Hirsch5 commented on the possibility that, if jogs cause hardening, an anneal at 200°C should straighten the jogged dislocations and result in softening. However, parkins' has re-expressed his belief that these mechanisms are not entirely consistent with the observed serrated stress-strain curves. Experimental. New data has now been obtained for Al(Cu), Al(Ge), Al(Mg), and Al(Zn) primary solid-solution alloys. These alloys were prepared from metals exceeding 99.99 pct purity, and specimens 4 by 4 in. diam were solution-treated, quenched, deformed 10 pct in compression at room temperature, and aged at 200'C in a cottonseed oil bath for various times. Generally, these operations could not be carried out in rapid succession, so the alloys were stored in a freezer between treatments to minimize aging. The variation in hardness with aging time, Figs. 1 to 4, was determined by microhardness testing with a 3.0-kg load. At least five readings were averaged to obtain each data point, and all measurements were taken about the center circumference of each cylinder (region of maximum deformation). Each specimen was used to obtain only one data point, i.e., specimens were not replaced in the aging bath after measurements were made. In

Jan 1, 1968

By James K. Stanley

Preferred orientation, particularly in irons and low-carbon steel, is a phenomenon that is both of considerable importance and theoretical interest. At times it is a liability and at other times an asset. In deep-drawing operations, preferred orientation is extremely undesirable because it necessitates trimming operations and increases scrap loss. Furthermore, oriented metals are likely to crack more easily than randomly oriented material because the forming of symmetrical and unsymmetrical shapes out of preferentially oriented metals and alloys increases the probability of rupture in regions of high stress, owing to differential ductility.' In the electrical industry, on the other hand, preferentially oriented silicon irons are in demand for transformer application because of the improved magnetic permeabilities in the rolling direction.2 This phenomenon of preferred orientation in soft magnetic materials has been responsible for the tremendous improvement in transformer design and construction in recent years. Directional properties in metals have received a great deal of attention in the metallurnical -literature,3-9 in which much of the information reported about orientation has been obtained by conventional methods, mechanicai properties and X-rays. A wealth of data has been obtained and often at a great expenditure of time. The recent introduction of the magnetic torque measurements on ferromagnetic materials provides a very simple and rapid method of evaluating orientation. The judicious use of the method can supply important information, but it should be borne in mind that such studies must be supplemented by X-rays, optical methods,10 and etch and pressure figures" to get a rational understanding of the orientation phenomena. No claims are made that the magnetic torque of evaluating orientation will reveal the behavior of the metal in deep drawing. For this purpose the accepted tests for deep-drawing quality must be used. For a good drawing stock, which must have low impurities, desirable grain size, ductility, strength, hardness, good surface, random orientation, and good recrystallization behavior, it cannot be expected that any simple test will be satisfactory for appraising all the factors. The only factor on which the magnetic method can be used is orientation, which is, of course, of considerable importance. When directionality can cause a 10 to 15 per cent change in tensile strength and a IOO to 300 per cent change in tear length,12 it goes without saying that a reliable as well as rapid method for detecting these changes would be desirable. There are certain inherent advantages in testing orientation by the torque method: The method is rapid with the proper type of equipment; no elaborate preparation of specimens is required—it is only necessary to punch or machine a I-in. disk of the sheet material and insert it into the testing device.

Jan 1, 1944

By A. I. Blank, S. E. Maddigan

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,' the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White's range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940

By S. E. Maddigan, A. I. Blank

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,' the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White's range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940

The papers discussed in the following pages were presented during two sessions of the Geophysics Education Committee of the Mineral Industry Education Division on Feb. 17 and 18, 1941. At the first meeting, to consider the "Influence of Geophysics upon Geology Curricula," this Committee was joined by the Geophysics and Mining Geology Committees of the A.I.M.E., the Society of Economic Geologists, representatives of the American Geophysical Union, and delegates from the Committees on College Curricula and on Applications of Geology of the American Association of Petroleum Geologists. Quentin D. Singewald and Sherwin F. Kelly presided. At the ensuing session, especially emphasizing the integration of geology, physics and chemistry for the solution of earth problems, the joint participants with the Geophysics Education Committee were the Geophysics Committee, and representatives of the American Geophysical Union and of the Committee on College Curricula of the American Association of Petroleum Geologists. Richard M. Field and W. R. Chedsey presided. In the following summary of the discussion at the two meetings, written discussion submitted subsequently is not differentiated from that offered orally at the session. A provisional report of the Geophysics Education Committee was presented at the second session, and some of the following discussion refers to it. This report has not been printed (it is anticipated that a more comprehensive, final one will be rendered at the 1942 annual meeting), but a few mimeographed copies of this provisional report are at the A.I.M.E. headquarters and will be mailed on request. . Dr. W. P. HAYNES presented some notes prepared by Dr. F. H. LAHEE, Chairman of the American Association of Petroleum Geologists' Committee on College Curricula. This Committee's inquiries reveal the general opinion that a four-year academic preparation is inadequate, five or six being advisable. The fundamentals, mathematics, physics, chemistry, and English composition, should be stressed in the first three years, with specialization in the last two or three years. Some companies provide an apprenticeship period, and themselves give additional training.. During academic years more attention needs to be given to engineering training, to field mapping, and in geology to stratigraphy and sedimentation. The amount of mere memory work should be cut, and men trained to observe and reason. Dr. Lahee emphasized the need of more adequate preparation in English composition, because of the inability of many graduates to compose acceptable reports. SHERWIN F. KELLY pointed out that much time in university training, which ought to be devoted to technical subjects, was taken up with English courses. He emphasized that it is the part of the universities to demand of the high schools that the students they send to the university be properly trained to speak and write English. Prof. W. T. THOM protested against the crowding of high-school material into already overcrowded college curricula. C. E. DOBBIN, chairman of the Committee on Applications of Geology of the American Association of Petroleum Geologists, described briefly the work of his committee in publicizing geology, and said that it found a widespread popular interest in the subject but a lack of appreciation of its importance. He recommended that attempts to coordinate the works of geologists and geophysicists be expanded somewhat, toward the further developing and encouraging of a "species of geopolitician" capable of assisting the progress of geology and geophysics by more vigorous advertising of

Jan 1, 1941

By R. Stefanko

The use of strain gauges and compression pads for an underground bolt installation in a central Pennsylvania coal mine revealed that satisfactory anchorage could not be maintained in the shale stratum that constituted the immediate roof. Comprehensive laboratory tests resulted in a new shell designed with an increased area of contact and smaller surface serrations. Retightening of the bolt was also found to be beneficial for maintenance of high load values. Roof bolting in coal mines has progressed very rapidly in the last decade, and today this method of support is in general use. There are many theories concerning the functions of roof bolts, but the importance of beam building is indisputable. Proper tension in the bolts minimizes shearing along bedding planes and creates a thick, competent beam from individually weak layers. Bolting must be accomplished immediately upon exposure of the roof, and bolt tension must be maintained if roof failure is to be prevented. Seams are being mined today with roof bolt support where conventional timbering was not effective.' The widespread use of continuous mining equipment was made possible by roof bolts which permit long supported spans free of obstructions. Since adequate anchorage is the key to successful bolting, better methods for determining the efficiency of anchorage are continually being sought. Attempts have been made to measure bolt loads, thus assessing anchorage efficiency by employing sensing devices between the bolt head and roof. 3-s None of the techniques appears to be very accurate, and all have at least one serious deficiency. The greatest efforts are being directed toward the standardization of the pull test.6" Nevertheless, the author believes that the pull test is only one criterion for establishing the efficiency of anchorage and not necessarily the most important one. The conventional pull test involves the short-term application of forces, whereas the success of roof bolt installations is dependent upon the ability of anchorage to sustain relatively long-term forces. Therefore, it would appear that the time-dependent function of the anchor is the single most important parameter for the success of roof bolting in many types of rocks. UNDERGROUND TESTS Strain gauges and compression pads were employed to measure bolt loads in a central Pennsylvania coal mine.8 Bolting had been employed only sporadically in the shale top since dubious benefits were obtained with this type of support. Table I shows some typical results from this investigation. Anchorage losses were extremely variable among the bolts, but all showed a considerable degree of bleed-off. The tests indicated that anchorage efficiency was extremely low in this type of shale. The results confirmed that bolting under these conditions was practically worthless, and thus a waste of material and labor. Probably even more important, bolting constituted a hazard when reliance was placed upon it for support. Certainly the complete lack of confidence in roof bolting, which was apparent in the mine personnel, was justifiable since the bolts did not accomplish their purpose. PRELIMINARY LABORATORY BOLT TESTS The extreme losses in bolt tension that were detected in underground installations prompted a comprehensive study to assess the causes. However, preliminary studies were first made to determine the combined stresses in a roof bolt and to prove conclusively that the observed bleed-off phenomena were due to anchorage: slippage and not to some other physical manifestation. In all of the ensuing tests

Jan 1, 1962

By W. L. Worrell

R. C. Gifkins (CSIRO)—In this paper evidence is put forward to support the idea of grain boundary shearing in aluminum at 4.2°K and the phenomenon is explained in terms of a low-temperature "equicohesive temperature". It is stated that these findings show that grain boundary shear cannot be ruled out in any situation by temperature arguments alone. We believe, from our own recent study of "apparent grain boundary sliding'' at temperatures below 0.45 Tm, that it can be ruled out on temperature arguments alone.45 Our experiments were made principally with magnesium and a Ms-A1 alloy ("Magnox A12"). Careful examination of offsets of marker lines or steps at grain boundaries produced by deformation at room temperature (-0.3 Tm) showed many of these to result from curvature over narrow zones along the grain boundaries. A significant residuum did, however, appear as a sharp offset or step. It was found that the mean value of this step rose to a small value during the first 0.5 to 1 pct strain and then remained at this level with further strain. Moreover, exactly the same values were obtained (at the same stress) at 75°C instead of 21°C. That is, in this range of temperature the "apparent sliding" was not temperature-sensitive. At 125°C and above there was sliding which increased with strain and which was temperature-dependent. When this temperature-dependent sliding was used to calculate the sliding to be expected at room temperature, this underestimated the "apparent sliding" by a factor of 104. The conclusion drawn is that the "apparent sliding" consists of shear localized in a zone of a width measured perhaps in microns, whereas it seems that true sliding occurs on the boundary surface.46 A model for such localized shear has been developed in general terms, following a similar model of Urie and Wain.47 Other strong evidence for low-temper- ature sliding has been based on the offsets of marker lines consisting of a substructure seen using the electron microscope to resolve these.48 We have repeated this work and found that the effects can be accounted for in terms of cracks in an oxide film which is produced when the substructure is etched up; these cracks form over zones of shear rather than at actual interfaces. However, in aluminum at room temperature (-0.3 Tm) there is no "apparent sliding" which is optically detectable. We suggest that, when the temperature is much lower (and possibly the rate of strain higher, too), as in the experiments of Chin et al., then aluminum behaves like magnesium at room temperature, and a narrow zone of shear develops to accommodate differences in strain across the grain boundary. Such a zone could well give rise to triple-point cracks. It is hoped to investigate these suggestions further. B. Y. Chin, W. F. Hosford, Jr., and W. A. Backofen (authors' reply)—It is interesting to have Dr. Gif-kin's comments, although it is somewhat difficult to reply in detail without the reference containing the work that he describes. Apparently though, he does find a low-temperature temperature-independent sliding that would seem to be related to the observations reported here. Perhaps some of the difficulty has semantic origins, growing out of the distinction between ('true sliding" and "apparent sliding".

Jan 1, 1965

By Clarence W. Dunham

BECAUSE of the earthquakes that occur at Chuquicamata, the design of the smelter stacks constituted the most difficult structural problem of the entire sulphide ore project. Slight tremors occur almost daily and shocks of moderate magnitude are not uncommon. Naturally, the operation of the smelter depends upon the safety of these stacks, and their resistance to earthquakes was the critical feature of their design. Adequate data of the magnitudes of past shocks at Chuquicamata were not available. However, considering the information that was obtained from experiences in other parts of Chile, a period of one to two seconds was adopted as a basis for the design. To complicate the problem further, the stacks had to provide for operations under a wide variety of conditions ranging from the possibility of running one reverberatory furnace and two converters initially to perhaps five or six furnaces and eight or ten converters simultaneously in the completed plant. No one could tell for certain just what the ultimate capacity might have to be because the plans permitted a large extension beyond the first installation if this became necessary. Studies of the stacks were made for many conditions. At first it was thought that one stack 600 or 650 ft high should be used initially for both the furnaces and converters, with a second similar stack to be built for the future extension. This height would provide adequate draft in the rarified atmosphere at the plant's elevation of 10,000 ft. It would also disperse the gases high in the air. Preliminary studies of this large stack showed that such a structure was possible if made of steel but it would be exceedingly costly. Furthermore, the effects of the tendency for the top to whip under the action of earthquakes might be serious, and the design had to be based upon assumptions which might not be trustworthy. Such a tall stack was finally abandoned in favor of a larger number of smaller ones. Initially, one stack will service the first three or four furnaces. Another will handle the gases from four or five converters. The smelter has been located in such a position that the prevailing winds carry the fumes away from the remainder of the plant. A height of 300 ft for the stacks was finally selected. The top diameter is approximately 24 ft 9 in. clear inside of the lining. The converter stack is located upon a hill alongside the smelter. This provides an effective increase in height because its base is approximately 66 ft above the yard level. The base of the reverberatory stack is at the latter elevation. Stacks made of reinforced concrete or of steel were investigated, and so were many shapes for them. As these studies progressed, the lightness of a steel structure, and the ductility of the metal itself, led to the decision to use steel for the main part of the stacks. The fact that serious damage to one of the stacks would cause the plant to shut down, caused special studies to be made of the stress conditions that might exist around the breeching which had to be nearly 15 ft wide and 40 ft or more high where it joined the stack. This height was necessary in order to provide adequate transition from the horizontal flow of the gases to the vertical direction without undue eddies. This opening constituted a serious source of weakness in the structure. If made with sufficiently strong reinforcement around its edges, there would be a hard spot in the structure that might cause trouble because of shaft vibrations.

Jan 1, 1952

By F. H. Ellinger

TI HE crystal structure of neodymium has been re-A ported by Quill1 and by Klemm and Bommer"s to be hexagonal-close-packed, Strukturbericht-type A3, with a, = 3.650.4, c, = 5.890.4, c/a = 1.614. Klemm and Bommer,% owever, pointed out that the observed intensities of the lines of the neodymium powder pattern agreed only in part with the intensities calculated for the type A3 structure, and that the neodymium powder pattern showed extra lines which could not be traced to impurities. They found that these extra lines could be accounted for by doubling the c-axis, but apparently they did not consider their evidence to be sufficiently conclusive to justify reporting the doubled c-axis. In the present work, the structure of neodymium was found to be double hexagonal-close-packed. The neodymium metal used in the present investigation was obtained through the courtesy of F. H. Spedding of the Ames Laboratory. Its major impurity was stated to be 0.03 pct Ca. The author's spectrographic analysis indicated high purity and carbon was determined to be less than 30 ppm. X-ray powder specimens were prepared from filings stress relieved in vacuum at 200°C for 50 hr. Powder photographs were taken in an 114.6 mm diam camera (Straumanis film mounting) at room temperature and in a 19 cm diam Unicam high temperature camera at elevated temperatures. Copper x-radia-tion was used for all the photographs. The powder pattern of neodymium was found to index to a hexagonal unit cell with dimensions, as determined from the high angle Ka doublets, of: a.= 3.655+0.001.4; c, = 11.796+0.004.4; and c/a = 3.227 at room temperature. The measured density of neodymium shows that this cell contains 4 atoms, the calculated density is accordingly D, = 7.02 g per cu cm. The diffraction data for the first 15 lines of the powder pattern are listed in Table I. In a double hexagonal-close-packed unit cell, the 4 atoms would be in the positions (0,0,0), (0,0,%), (1/3, 2/3, 1/4), and (2/3,1/3,%) of space group P 6,/mmc. On the basis of these positions, the relative intensities of the reflections were calculated using the expression: 1+cos2 20 I oc \Frp 1 ' sin2 0 cos 0 where F is the structure factor and p is the multi- plicity factor. Since absorption was not taken into consideration, comparison of observed and calculated intensities should be made only for neighboring reflections. Each atom has 12 neighbors, 6 in the basal plane at a distance of 3.655.4 and 3 above and 3 below at the closer distance of 3.626.4. These distances correspond to an average radius of the neodymium atom of 1.820.4. The description of this structure in terms of A, B, and C close-packed layers of atoms is ABAC ABAC. ...... The structure repeats every fourth layer and the stacking sequence of the second, third, and fourth layers corresponds to cubic-close-packing of atoms. A series of powder photographs taken at successively increasing temperatures up to 680a10"C revealed that the double hexagonal-close-packed structure is stable up to this temperature. Acknowledgments The authw wishes to thank W. H. Zachariasen and A. S. Coffinberry for their helpful comments on this work and also Marion Gibbs for measuring the diffraction films. This work was sponsored by the United States Atomic Energy Commission.

Jan 1, 1956

By U. F. Kocks

SINGLE slip and a single parallel array of edge dislocations have been obtained in silicon single crystals by homogeneously bending them in a four-point dead-loading device at 1000°C around the [211] axis with [253.] as the tensile axis which encloses an angle of 40° with the glide plane. Other orientations or lower temperatures proved unsuitable. The homogeneity of the bending was checked by the method shown in Fig. 1. The chemically polished specimen was exposed to parallel light from a microscope-stage lamp. The sharpness of the focus of the reflected light is an approximate measure of the circularity of the sample. This method permitted the determination of the actual radius of bent specimens within 10 pct accuracy. The etching solution developed to show up dislocations consisted of the following volume parts: 2 HF, 1 HNO,, 2 CH,COOH, 1 a solution of 5 wt pct of CuNO, in water (Rosi'). The acetic-acid content was adjusted to produce fine well-defined etch-pits in about 2 min at room temperature. The effectiveness of the etch did not depend on the crystal-lographic orientation of the face etched. The number of etch pits produced after a given deformation was checked in the usual way against the Cahn formula' and showed good agreement. As it is to be expected from the orientation of the primary system there are slip steps on the top and bottom faces but not on the side faces (perpendicular to the bending axis), whereas etch pits appear on the side faces but not on the top and bottom faces. This is different only for occasional dislocations of a secondary glide system. All the micrographs included have been taken in places where the most of secondary glide could be seen. From this it is evident that in the homegeneously deformed region the number of secondary dislocations was less than 1 in 1000 of the primary type. Dislocation Distribution—A series of tests with varying amounts of deformation is shown in Figs. 2(a-c). An observation that can readily be made from these pictures is that the linear density of dislocations within slip lines is relatively constant and independent of the amount of deformation. "Slip line" in this context is understood to mean a line that is a straight connection of individual etch pits. The heavily pitted bands which can be seen in each of these three pictures may be resolved fairly definitely, at higher magnifications, into many "slip lines" the distance between them being of the order of 0.5p The distance between dislocations in slip lines is of the order of 2p and it is also fairly constant in going from the neutral zone outward. The higher over-all dislocation density in the outer regions of any sample and the higher total number in a more heavily deformed sample, are effected by a larger number of "slip lines." The relative constancy of the dislocation distance within an individual slip line is surprising. The absence of pile-ups" may imply, if there is no rear- rangement on unloading," that there are no substantial obstacles to slip in this case. It seems that the equilibrium distribution of the dislocations in each active slip plane under the higher external stress on

Jan 1, 1959