By Takeo Fujino, Nobuaki Sato, Yarong Wang, Kohta Yamada

"Ternary mixed sulfides of some transition metals MTS3 (M=Ba, ·Pb, T=Ti, Zr) were synthesized by a relatively low temperature process using sulfur melt. The mixture of starting materials, such as, metals and/or binary sulfides and a large excess of sulfur was reacted in a vacuum-sealed Pyrex or quartz ampoule at 350- 600 °C for one to three weeks. After the reaction, the remaining sulfur was completely removed by a process composed of filtration of sulfur melt and followed dissolution in CS2• The binary sulfides impurities coexisted in the products were removed by rinsing the products in water and acetone. By using the above method, BaTiS3, PbTiS3 and BaZrS3 'Were obtained in pure form. The effect of addition of halides on the yields of these ternary sulfides were also discussed.IntroductionThere have been a vast number of studies on the preparation and physical and /or chemical properties of mixed metal oxides. As is well known, some of such compounds exhibit excellent materials properties, causing them for use in mechanical, electronic, magnetic and chemical devices. Not a few mixed metal sulfides show similar physico-chemical properties to those of the corresponding mixed metal oxides. However, the study of the mixed sulfide crystals is rather sparse mainly due to difficulties in preparing these compounds. In various methods which have been adopted for preparing mixed sulfides, the simplest method would be the solid-solid reaction of the component binary sulfides or elements. However, there are always diffusional constraints with regard to the reactions in solid phases causing it necessary to heat the reactants at sufficiently high temperatures, viz. 800-1200°C. On the other hand, some mixed sulfides are unstable at high temperatures or to change their materials properties due to sulfur nonstoichiometry and structural modification depending on temperature, i.e., synthesis of such compounds needs to be made at lower temperatures. Processing in alkali halide melts is hopeful to overcome the above problems but to obtain the halide melts the temperatures above ~ 600 °C is needed. Low temperature reaction has been carried out for the preparation of Hg1.24TiS4, which was formed by the ·combination of TiS2 and molten Hg metal at 320°C[l]. Reaction of WS2 with LiBH4 melt at 350°C yielded LixWS2[2]. These sophisticated methods, however, can be applied only to the vary special cases."

Jan 1, 2000

By R. C. Hubli

A panial equilibrium model? to simulate the dissolution of millerite (NiS) in aqueous solutions containing copper(II) chloride as the oxidizing species has been developed. The predominant copper(I) and copper(II) species are CuQ3 and CUO2 respectively. The model computes the initial concentrations of the species present in the aqueous phase under the specified input conditions, prior to the simulation of dissolution. During the dissolution of millerite, nickel enters the leach liquor as NiH and it has been found that the H+ decreases as a function of NiS dissolution. The simulation has been accomplished under conditions prevailing during actual dissolution, with only one mineral undergoing dissolution. The model can be applied for the simulation of co-dissolution of two or more sulfides. Under the given conditions, the precipitation of Cu1(OH»)O is negligible but loss of Cu(1l) could be significant if the initial H+ is lower than 0.03 M. The results of the simulation compare favorably with experimental observations.

Jan 1, 1996

By Freddy Syvertsen

"During the past two years the Association of Norwegian Foundries in Norway has been running a project in evaluation of CAD/CAM systems for foundries.In this work we have had a closer look to the various steps from drawings to the finished castings. On this background we have made a specification of the special needs in the foundry process. The main content of this paper is a presentation of this specification.Some CAD/CAM sytems have been compared with the specification and a summary of the result is presented.In the project we have also had a closer look at some systems where we actually have tried the user interface and some of the possibilities in the systems. In this way we have gained a more detailed knowledge of the systems and we have also got some experience in NC-machining from the systems.IntroductionThe development of CAD/CAM systems has taken place with almost no interaction with the foundry business. This becomes clear when you are having a closer look at the systems. Most of them have not the possibility to describe the complex sculptured surfaces that is often found on castings. The people developing the software, have paid little or no attention to the problems arising when a geometry is going to be transformed for the casting process. Among the problems are the decision of where to place the parting line and to adjust the draft angle. These problems must be solved properly to be able to withdraw the model from the sandmould. In die casting the problems must be solved to be able to get the casting out of the die.In Norway some companies have been developing CAD/CAM systems for several years, with limited interest in foundry problems till 1983. To present the special foundry problems to them a specification of the needs was made that year. Another reason for making this specification, was to compare it with the CAD/CAM systems on the market (1).Design of castingsGeometry transferThe foundries in Norway are small units with almost no design of their own casting products. They are subcontractors receiving paper drawings and limited informations about the product from the mechanical industry both in Norway and in other European countries. This is going to change, and in the future the geometry will be transferred by magnetic tape or by a network of computers."

Jan 1, 1986

By Khandaker M. Anwar Hossain

This paper presents the development of lightweight concrete (LWC) incorporating pumice aggregate and volcanic ash (VA) based ASTM Type I blended cement (PVAC). Fresh and mechanical properties of LWC mixtures such as slump, air content, compressive strength, tensile strength, density and modulus of elasticity are described. The durability characteristics are investigated by drying shrinkage (DS) and water permeability. The investigation suggests the production of LWCs incorporating blended PVAC and VPA having satisfactory strength/durability characteristics for structural applications. The use of PVAC induces the beneficial effect of reducing drying shrinkage and water permeability. Development of such non- expensive and environmentally friendly LWCs with acceptable strength and durability characteristics is extremely helpful for the sustainable development and rehabilitation of volcanic disaster areas around the world.

Jan 1, 2010

By Xi Dai

The LiFe1-xNixPO4(x=0, 0.05, 0.10) cathode materials for Li-ion battery were synthesized with Fe1xNixC2O4?2H2O(x=0, 0.05, 0.10) as Fe sources by high temperature solid-state reaction method. The Fe1xNixC2O4?2H2O(x=0, 0.05, 0.10) materials were produced by liquid co-precipitation method and crystal structure and morphology of cathode materials were characterized by X-ray diffraction and scanning electron microscopy. The composition contents and charge-discharge performances were measured by chemistry analysis and charge-discharge apparatus. The XRD patterns showed that LiFe1-xNixPO4(x=0, 0.05, 0.10) cathode material samples were well-crystallized homogeneous olivine-type phase, with only tiny trivalent iron impurities according to chemistry analysis results. Charge-discharge test showed that cathode materials possessed excellent charge/discharge capacities, about 150mAh/g at 0.1C rate and more than 120mAh/g at 0.4C rate. The polarization of cathode in charge-discharge process can be restrained effectively, for the potential offset between oxidative peak and reductive peak of doped LiFePO4 material was only 0.079V, lower than pure LiFePO4 markedly.

Jan 1, 2006

By Vinay Kumar

The present investigation describes R & D studies carried out for recovery of copper from the sulfate solution expected from the leaching of e-wastes in presence of minor constituents such as cadmium, zinc and nickel using solvent extraction process. In order to extract copper in continuous mode in mixer settler unit (MSU), basic studies have been made to optimize the experimental condition using 5%LIX84 in kerosene. Subsequently, the solvent extraction of copper was made in MSU maintaining leach solution flow rate 4.0 L/h and A/O ratio 1. The results showed complete extraction (~97%) of copper in three stages at A/O ratio 1 from the aqueous solution containing 1.98g/L Cu at pH 1.91 in presence of impurities. Loaded metal was completely stripped after scrubbing with 10% sulfuric acid in two stages. The stripped solution could be used for metal/ salt recovery by electrolysis/ crystallization.

Jan 1, 2010

By S. Ozbilen, B. Erdogan, M. Erdogan

To study by thermal analyses the response of precipitation hardenable alloys of Al-Cu-Mg and Al-Li-Cu-Mg system to natural and artificial ageing, a series of ternary and quaternary Al-alloys with nominal compositions of Al-l.13wt%Cu-0:65wt%Mg (alloy-I), Al-1.15wt%Cu-0.57wt%Mg-0.07wt%Li (alloy-2), Al-l.19wt%Cu-0.56wt%Mg-0.75wt%Li (alloy-3), Al-2.0lwt%Cu-0.89wt%Mg (alloy-4), Al-2.14wt%Cu"0.56wt%Mg-0.07wt%Li (alloy-5) were used in the present investigation. Samples in the form of rolled sheets are subjected to water quenching at 25EC after solution treatment at 530EC for 20 min. Alloys were aged naturally at room temperature (25EC) up to 2 months and artificially at 190EC up to 2 days. By using differential scanning calorimetry (DSC) in the temperature range of25-300EC, differential thermal analysis (DTA) in the temperature range of25-600EC together with Vicker's hardness measurements, the response to natural and artificial ageing of the alloys used in the present study were investigated. It was observed that in these alloys, GPB(Cu, Mg) zones [Guinier-Preston zones with Cu and Mg] do form during water quenching at 20EC following solutionizing heat treatment. Natural ageing of the same alloys causes formation of more GPB(Cu, Mg) zones, which results in hardening in the alloys. Artificial ageing at 190EC up to l day results in GPB zone dissolution causing preliminary decrease in hardness values while two days of artificial ageing in the alloys cause S' (Al2CuMg) precipitation confirmed by DSC/DTA analyses resulting in an increase in hardness values. Li addition up to 0.75wt% helps T1 (Al2CuLi) and T 2 (Al6CuLi3) phase formation together with S' precipitation as DSC/DTA analyses show after the same heat treatment.

Jan 1, 1998

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By Gary A. Wickham

In the zinc industry, this past decade has seen both prosperity and depression. Significant changes have occurred throughout the world in mining, smelting, refining, and marketing. This paper will review many of the industrywide changes of recent years and the potential impact for 1990s. In addition to an historical review of supply and demand are discussion of technology considerations for zinc and zinc based products, effects of geographical shifting of markets, and projections for the 1990s.

Jan 1, 1990

By Atsushi Shibayama

The aim of this research was to develop a copper recovery process from mine tailings (0.34%Cu) using flotation followed by high-pressure oxidative leaching (HPOL) and solvent extraction. The results of HPOL using the concentrate of mine tailings obtained by flotation under the optimal conditions of the previous study shown that an efficient copper dissolution of 94.4% was achieved in an H2O media, while the copper concentration of PLS reached to be 2.9 g/L. The solvent extraction of PLS obtained from the optimal HPOL showed that 91.3% copper was recovered in stripped solution under the determined optimum conditions, in which the copper concentration achieved to be 44.8 g/L. Finally, a proposed copper recovery process from the concentrate of mine tailings was developed by combination of HPOL and solvent extraction, while a total copper recovery of 86% was achieved.

By María Cristina Ruiz

Enargite rich copper concentrates can not be treated by conventional smelting/converting technology and thus nonconventional methods such as leaching must be used. Since enargite (Cu3AsS4) is a hard to dissolve mineral in acidic solutions, pyrite, a common impurity in copper concentrates, could be used to increase the enargite dissolution rate. On this matter, we present in this work experimental data on the pressure leaching of a mixed enargite-pyrite concentrate in H2SO4-O2. The results show that the dissolution of enargite from the mixed concentrate is considerably faster than the dissolution of pure enargite mineral. The leaching rate increases significantly with temperature. Over 98% of enargite was dissolved in leaching 64 micron size particles at 200 ºC and 100 psi of partial pressure of oxygen in just 30 minutes. A change in the partial pressure of oxygen from 50 to 150 psi showed also a large influence in the leaching rate.

Jan 1, 2010

By M. Potesser

One of the main targets in the automotive mass industry and supplying industry is the weight reduction of the vehicle for decrease of the fuel consumption. For that reason combinations of different kinds of materials and connections of, for example, steel and aluminium are developed or are already successfully field-tested. A determining factor concerning the quality assessment of the welded joint during hybrid welding is the characterization of the intermetallic Fe-Al layer regarding strength, hardness, morphology and mainly the different phases in which Fe occurs together with the Aluminum (FeAl, Fe2Al5, FeAl3.). A combination of conventional light microscopy, SEM - EDX - analysis, the usage of an atomic force microscope including a Nanoindenter and theoretical thermodynamic calculations turned out to be highly effective. Based on the attained results, the constitution of the intermetallic FeAl layer, influenced by silicon, manganese and zinc, can be predicted.

Jan 1, 2006

By A. W. Worcester

The plant is designed to produce 60,000+ tons of refined lead per year from a nominal feed consisting of 110,000 tons of SLI and industrial batteries, and 10,000 tons of lead contained in drosses and scrap. The plant will also produce as by-products polypropylene chips and detergent grade sodium sulfate, using the Engitec Impianti CX Technology. The battery separation circuit will consist of a battery breaking hammermill and a vibrating screen with water sprays to separate the battery paste from the grid metal and other battery components. The battery components, consisting of ebonite, and separator materials, will be separated' from the grid metal and classified with the use of hydrodynamic water separators. The battery paste will be treated with sodium carbonate to produce a lead carbonate paste for smelting in a reverberatory furnace. The slag from the reverberatory furnace will be campaigned through a traditional primary blast furnace to produce hard lead. The sodium sulfate liquor from the lead carbonate filtration step will be crystallized to produce anhydrous sodium sulfate. The metallic grid metal will be treated through a small rotary smelter of the Engitec design to produce a hard antimonial lead. The plant's scheduled to be commissioned 12 months after receipt of all of the Federal and state permits. The plant will be integrated into the Buick Primary Lead Smelter, located in the center of Missouri's New Lead Belt, at Boss, Missouri. This will allow The Doe Run company to fully utilize all of its existing assets.

Jan 1, 1990

By Ana E. Bohé, Fabiola J. Alvarez

"The separation of nickel from the aluminum present in spent catalysts and different metallic industrial residues, is proposed in the following systems: alloy Al2Ni and the mixtures 50 wt% Ni + 50 wt% Al, 10 wt% Ni + 90 wt% Al2O3 and 12 wt% NiO + 88 wt% Al2O3. The experiments were carried out in a tubular reactor with a flow of 2 l/h of gaseous chlorine and from 200 ° to 800 °C. The final products of the reaction, extracted from the hottest zones of the reactor where characterized by XRD, SEM, EDS, AA and XRF, as NiCl2 y NiCl2.6H2O while in the coldest regions AlCl3 was deposited in the first two cases and in the other there was a residue of ?, a- Al2O3, sometimes mixed with some remainder of Ni and NiO. The procedure attained different separation factors which showed the optimun conditions for the recovery of both metals. Introduction Some studies of nickel corrosion were carried out in chlorine gas at temperatures above 950ºC, and suggested that nickel is not corroded below 538ºC. [1] However, in a previous work it was shown that the chlorination allows the separation of nickel from aluminum and the formation of NiCl2 was detected from 200ºC in binary mixtures Ni-Al 50 wt%, for isothermal conditions in chlorine flux. [2] Other researchers obtained selective chlorination above 650ºC of a fly ash containing 1.4 wt% of Ni and other metals (V, Mg, Al and Fe). The Ni was separated from the Mg and NiCl2 started to vaporize at 550ºC and was after condensed in a zone of the reactor above 380ºC with 90% of purity. [3]"

Jan 1, 2008

By Dirk van Zyl

As part of the North American regional activities during the Mining, Minerals and Sustainable Development Project (MMSD) one project focused on the development of sustainability evaluations at the operations level. Engagement was identified as one of the seven important questions to be addressed. Engineers and scientists employed in the mining, minerals and materials production arenas must understand the importance of stakeholder engagement, both within and outside the operations as it is essential in the ongoing activities required to contribute to sustainable development. After developing the awareness that a social license can only be contemplated if engagement is in place, they also have to develop skills in engagement processes. This presentation will present the business case for engagement as well as an approach to motivate undergraduate mining engineers to embrace it. The presentation will also review some recent and ongoing research to improve the engagement process.

Jan 1, 2010

By F. Ajersch, P: Tsantrizos, K: Shanker

"TiN films have been deposited on various substrates by a novel reactive plasma technology. In this process, a nitrogen source (NH3 or N2) and TiCl4 are reacted in the jet of a plasma torch, and are deposited onto a substrate forming TiN films at a high growth rate ( > 2µm/min). It was found that the process parameters strongly affect the microstructure, thickness, density, and growth rate of the TiN films. These parameters include source of nitrogen (NH3 or N2, N/Ti ratio, temperature of substrate, and spray distance. In general, it was found that thick and dense coatings were deposited when the N:Ti ratio was kept low, and the substrate temperature was high. Also, for the series of conditions investigated, NH3 was found to give much better results than N2•. The limitations and advantages of this technique are also discussed in this paper.IntroductionTiN is an extremely hard material and is used in many wear applications, particularly as a protective coating on cutting tools to extend their Iife(1.2). Owing to its excellent chemical stability, TiN is also frequently used as a diffusion barrier in the electronics industry for sub-micron Al/TiN/Si ohmic contact systems (3) or as a coating on high-temperature resistant alloys in gas turbine applications (4), based on its good resistance to oxidation. Other applications include decorative coatings in the jewelry industry, and specialized applications such as solar energy absorbers and transparent heat mirrors(5).TiN films can be deposited/formed using various techniques. The main techniques of deposition are CVD (Chemical Vapour Deposition) and PVD (Physical Vapour Deposition). Each of these techniques can have many variations in equipment characteristics, reactants as well as a range of process parameters (pressure and temperature). In the CVD process, TiN is generally deposited onto a heated substrate where a chemical reaction takes place. The reaction can be one of reduction(6) (e.g.: TiCI4 + 0.5N2 + 2H2 --> TiN + 4HCI), of thermal decomposition(7) (e.g. decomposition of titanium dialkylamide), or of displacement (e.g. TiCI4 + NH3 --> TiN + 3HCI + 0.5CI2)' The displacement and reduction reactions are the most common."

Jan 1, 1994

By Svetlana Nikitina

While many question "sustainability" as an intellectual field on the grounds that it is too broad and "undisciplined," we are able to achieve a good balance between breadth of coverage and depth of inquiry in our team-taught seminar "The Grand Challenges: Sustainable Development for the 21st Century" offered to first year students at Worcester Polytechnic Institute. We strike this balance between breadth and depth by a) problematizing key sustainability issues in class discussions; b) by explicitly exploring the lenses of different disciplines (the historical context, the scientific facts, the engineering interventions and the philosophical foundations of unsustainable behaviors); and c) by offering our students opportunities to pursue a targeted project on specific sustainability issues (vertical gardening, metals recycling on college campus) through which they gain depth of understanding as well as practical exposure to all components of the problem, which puts them on the path of seeking effective solutions.

Jan 1, 2010

By E. Gutierrez-Miravete

Hot pressing processes are widely used to shape metallic, ceramic, and glass components. The process is an essential step in manufacturing ceramic fibre-glass matrix composites. The paper describes the use of computer simulation by the particle method, to the analysis of the deformation and flow of glass during hot pressing. The hot glass is represented by an assembly of interacting particles which deform in response to the applied pressure. The results, which should be regarded as complementary to continuum-based studies, provide useful insight about the hot pressing process.

Jan 1, 1990

By A. René Silva

The separation of Fe(III) from simulated Ni(II) solutions using different ion exchange resins was studied. The resins tested included cation exchangers with sulfonic and carboxylic groups and chelating resins with iminodiacetic, aminophosphonic, and mixed sulfonic and phosphonic groups. The dosage of resins was varied from 0.1 to 0.5 g/mL to study the impact of resin type and dosage on iron separation from simulated nickel leach solution containing 25 g/L Ni(II) and 25 g/L Fe(III) at pH 1.5. Also, the effects of different metal ion concentrations, Fe (III):Ni(II) ratios in solution, pH, and adsorption times were investigated. Experimental results demonstrate that all the chelating resins selected favored the adsorption of Fe(III) over Ni(II) with high Fe(III) loading. Soft cation exchange resins also favored the adsorption of Fe(III) over Ni(II), but no significant Fe(III) loading was observed. In contrast, strong cation exchange resins did not show adsorption preferences. The most efficient separation was observed using resin with aminophosphonic groups at resin dosage of 0.2 g/mL, having a Fe(III) adsorption over 94% and Ni(II) adsorption below 5%.

By Jeong-Soo Sohn

Physical treatment and chemical treatment of spent lithium-ion battery were studied in our research team. Especially we developed two types of acidic leaching for crushed powders containing LiCoO2 of spent lithium ion battery. One of them is sulfuric acid leaching with H2O2 as a reducing agent. The leaching rates of cobalt, lithium and the other metals were above 99 % at the condition of 2 M H2SO4, 10 vol. % H2O2, 75 °C, 300 rpm agitation speed, 250 g/5L solid liquid ratio and 75 minutes reaction time. And the other leaching process is the oxalic acid leaching. In this process more than 99% of Li and less than 1% of Co were dissolved at the condition of 3M oxalic acid, 80°C reaction temperature, 300rpm agitation speed, 50g/L initial solid/liquid ratio and 90min extraction time. Each process has its advantage and disadvantage. In sulfuric acid leaching, leaching reagent is very cheap and cobalt could be recovered into cobalt hydroxide. On the other hand, oxalic acid is more expensive than sulfuric acid but lithium could be dissolved selectively. Also cobalt could be recovered into cobalt oxalate and it could be changed into cobalt oxide after heat treatment. In order to select the effective recycling process, recovery rate and purity of cobalt hydroxide and cobalt oxalate were compared and it was investigated which process was more environment-friendly and economical.

Jan 1, 2006