F. G. SMITH.-Probably someone will ask whether I discovered why the bottoms of the large shells broke out. I did not, as a result of this investigation. An experiment was made along the lines indicated in this paper, to determine whether abnormal grains greatly affected the physical properties of brass. Two ordinary test bars were annealed for 1/2 hr. at 750° C. and physical properties determined on one. The other was covered with indentations made with a peen hammer and then reannealed. for 5 hr. at 750° C. It was found in the tensile test to be made up of large grains 1/4 to 1/2 in. in diameter. The physical properties, however, differed from those of the first bar only as much as might be expected after a 5 hr. anneal under normal conditions. It appears then that the large grains produced in this manner do not ruin the physical qualities of the brass.

Jan 12, 1919

By Walter Fuchs

IT is now generally conceded that coal is the product of deposition and transformation of debris of forests and swamps.29 Ample data are available to illustrate the metamorphosis of biochemical substances through biological action; other data show the progressive regional metamorphism existing in coal beds ;25 and numerous examples of change effected by intrusion of igneous dikes into coal deposits have been established.23 However, often the relative importance of the biological and the geological factor in determining the character of the various natural coals is a debatable question. Since both biological and geological factors are ever present in nature, the problem, at first glance, would appear to resemble certain probability problems: specifically the simultaneous toss of two coins, with the biological factor as heads and the geological as tails. The probability is 2 : I for the combined effect of both factors, as compared to the exclusive effect of either one, if the a priori probability is the same for each factor. This condition can be analyzed by a thermodynamic treatment of data, which may be obtained from a consideration of pertinent biological, chemical, geophysical and geological facts. SYNOPSIS OF BIOLOGICAL AND CHEMICAL FACTS The biosphere is not sterile; i.e., microorganisms are always present. Microorganisms have been established in the ocean deep, under the ice of the polar regions, in the sand of the deserts, and in swamps far below the surface. The various biological media may be acid, neutral, or alkaline, and they may or may not be readily accessible to air. Microorganisms are encountered almost everywhere, except where the temperature is not within the range tolerable by microbial life. Of course, with changing conditions, the type of microorganisms will change. All chemical products of life-proteins, fats, carbohydrates, lignins, waxes, resins may serve as a habitat of microorganisms. In the decomposition of a medium. some microorganisms macerate organic matter mechanically and remove certain constituents for their own nutrition; others decompose a large part of the organic matter but may leave certain constituents undecomposed. Some attack only certain specific ingredients of the organic matter. All of them build up cell substance. The nitrogen content of the medium largely determines the degree of decomposition. Below 1.7 per cent nitrogen, growth of microorganisms and hence decomposition of organic material is retarded; consequently organic material will accumulate.17, 32 Such accumulations of organic material may give coal eventually. Coals differ in type and rank. The nature of the original vegetation and the conditions attending the transformation of the accumulated debris determine the type of coal such as bright, splint, cannel, and algal or boghead coals. Chemical analysis of representative samples of a given type of

Jan 1, 1941

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300' to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By Raymond M. Howe

Additional data have been secured on the disintegration of furnace linings and the spalling of stove brick. The first article on the disintegration of furnace linings appears to have been written by John Pattinson in 1876.l The furnace involved was 85 ft. (25.0 m.) higher and 27 ft. (8.2 m.) in diameter at the boshes; after being in blast five years, the top brick became contaminated with carbon and disintegrated. An examination of the lining showed that the discolored, disintegrated brick were in a zone found from 35 to 67 ft. (10.6 to 20.4 m.) above the hearth; immediately below, in a zone extending from 22 to 40 ft. (6.7 to 12.1 m.) above the hearth, the brick were hard and porcelain-like in appearance. Analyses of samples taken from the different sections are given in Table I. The water-soluble portion found in the sample taken 39 ft. (11.8 m.) above the hearth had a composition approximately as follows: silica, 0.50 per cent.; lime, 0.04 per cent.; potash, 0.78 per cent.; soda, 0.20 per cent.; potassium chloride, 6.19 per cent.; moisture, 1.03 per cent.; total, 8.74 per cent. The carbon Table 1.—-Analyses of Samples Taken from Diferent Sections of Furnace . I ii In Iv v Section 67 Section 45 Seotion 39 Section of Original ft Above ft above ft above vitrified Lining Hearth Hearth Hearth Portion Per Cent. per Cent per Cent per cent. per Cent Silica........................... 55.70 55.60 55.67 47.60 37.07, Alumina........................ 35.50 35.40 30.00 26.47 23.18 Ferric oxide..................... 3.00 1.32 0.96 Lime........................... 0.23 0.06 0.17 Magnesia....................... 1.22 0.95 0.86 0.00 Potash......................... 2.60 2.10 5.30 7.54 21.59 Soda.........,.................. 0.45 0.42 1.67 0-76 6.28 Ca1bon ......................... 2.05 3.24 5.97 Carbon dioxide.................................. 2.. 17 Water...................................... 7.70 Water-soluble........................... 8.74

Jan 1, 1920

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

ONLY a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about I per cent of copper, with or without additions of elements such as magnesium,1 and die-casting alloys containing about 4 per cent of aluminum with small amounts of magnesium and sometimes copper.2 A number of elements are capable of forming alloys with zinc, which do not enter into solid solution except in limited degree. The present paper considers one such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. ZINC-TITANIUM SYSTEM The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor of the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. ALLOY PREPARATION All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C. until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount of this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidation. HOT-ROLLING TESTS Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections revealed a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By Lawrence H. Van Vlack, Alfred S. Keh

The distribution of sulfur in iron was found to be dependent upon the time and temperature of the treatment as well as the chemical composition of the sulfide. With higher temperatures, the sulfide phase spreads more extensively between the iron grains. A complete network, however, does not form until approximately 1300°C (2372°F), ot which temperature the dihedral angle approaches zero. Silicon has little effect on this change. Aluminum, oxygen, and manganese all modify the temperature of sulfide network formation to a higher value. The microstructures which result and have significance in relation to hot-shortness are discussed. SULFIDE inclusions in steel were recognized by metallurgists before the turn of the century. Considerable attention has been paid to them, and numerous studies have been made on the working properties of steel as affected by them. It has been suggested that ho t-shortness of steel is due to the presence of an enveloping liquid sulfide film at the grain boundaries of the steel in the range of the hot-working temperatures. However, several facts have been observed in commercial steels which do not seem to be completely consistent with this explanation: 1) the frequent absence of continuous films of sulfide as observed under the microscope, 2) the absence of hot-shortness in some high sulfur and resulfurized steels, and 3) the limitation of hot-shortness to a definite temperature range. The role that manganese plays in steel to eliminate hot-shortness is well known, but the theory behind it is still under question. Moreover, the effect of de-oxidizers such as aluminum and silicon, and the effect of oxygen are still not clearly known. In this study, the effect of heat treatments and of additions of manganese, aluminum, silicon, and oxygen upon the distribution of sulfide inclusions in iron was investigated. Both the as-cast and the heat treated structures were studied, using microscopic and autoradiographic techniques. Part of the results were interpreted in terms of Smith's' concept of microstructure. Review of Literature Metallurgists used to consider sulfide inclusions as suspended particles. It was Wohrman' who first pointed out that sulfide inclusions are soluble in liquid iron. Many observed facts may be understood on the basis of this concept of solubility. Wohrman found that small castings contain small inclusions. and larger castings contain larger ones. Also, inclusion sizes are smaller near the chilled surface. For the same size ingot, the average inclusion size in a given heat of steel depends upon the rate of solidification. That is, with slow solidification, enough time for precipitation and agglomeration of these

Jan 1, 1957

NEW MEMBERS. The following list comprises the names of those persons who became members during the month of April, 1913: BARNES, BLAKESLEE, Min. Engr Burrwood, La. BOYLSTON, HERBERT M., Cons. Met. Engr 26 Abbot Bldg., Cambridge, Mass. BUEHLER, HENRY A., State Geol Rolla, Mo. CASTO, WILLIAM H., JR., Mining Bonanza, Idaho. COHEN, MAXWELL B., Mill Operator Miami, Ariz. EVANS, MILTON R., Shop Draftsman 92 Division St., Kingston, Pa. HARPER, WALTER S., Asst. Treas 42 Broadway, New York, N. Y. JAMES. JAMES S.. Min. Engr Telluride. Colo.

Jan 5, 1913

By S. E. Haszko

Fused alumina or silica crucibles were used as the containing vessel. X-ray powder photographs were taken with CrKa radiation and the use of Straumanis type Norelco cameras of 114.6 mm diam. Crystallographic data for these compounds are shown in Table I. These results are in agreement with others of this series reported previousiy by Wernick and Geller.l The abnormally large atomic volume of Eu and Yb metal3 is manifested in EuA12 and YbAl2, when one compares them with the compounds reported in Ref. 1. However, the behavior of Yb in the Ni compound is the same as that observed in Ni5Yb having the Cu5Ca structure.4 Thus, it appears that Yb has a valence closer to 3 only in the Ni compounds; i.e.. the 2s and Id electrons are lost to the conduction band. 1,4 Europium in EuAl2, appears to have a valence closer to 2. In previous work.' X-ray patterns of ingots of NdCo2 indicated a multiphase material with faint indication of the presence of a phase having the MgCu2 structure. It was thought that NdCo2 formed peri-tectically from the melt, resulting in a multiphase system when cooled under nonequilibrium conditions. An X-ray pattern of a sample from a melt cooled more slowly than in past work showed that the major phase was NdCo2. The lattice constant, Table 1, is in excellent agreement with the value one can predict from the data of Ref 1. One of the other phases was identified as Co,Nd. The author wishes to thank J. H. Wernick for his guidance in this work, and D. Dorsi for the preparation of these compounds. 'J. H. Wernick and S. Geller: AIME Trans., in press. 'J. H. Wernick and S. E. Haszko: to be published. 'F. H. Spedding and A. II. Daane: Progress in Nuclear Energy, Series 5, Eds.: H. M. Finniston and J. P. Howe, McGraw-Hill Book Co., 1956. 'S. E. Haszko: to be published. 'J. H. Wernick and S. Geller: unpublished work. 6J. 11. Wernick and S. Geller: Acla Cryst., 1959, vol. 12, p. '162. The Influence of Hydrogen on the Lattice Parameters of Ti-Sn Alloys A. Coucoulas and H. Margolin A reinvestigation of the lattice parameters of Ti-Sn alloys by the present authors has revealed consistently higher c and a values than those obtained by Worrier. The difference is most pronounced in the c-parameters which are, therefore, used as a basis of comparison. This discrepancy was not due to air contamination, since precautions were taken to exclude this possibility. Specimens for Debye-Scherrer photograms were prepared by arc-melting 15-g buttons of Bureau of Mines titanium and 99.99 pct Sn, with compositions of 6, 8, 10, and 12 at. pct Sn. These buttons were forged under an oxygen-acetylene torch to 1/8-in. sq rods to produce relatively fine grained material. Scale and some surface were ground off, and the rods, after wrapping in molybdenum and titanium sheet, were vacuum annealed 15 min at 800 °C to remove hydrogen. Heat treatment of one of the samples at 875°C to produce ß and reveal a at the surface showed no surface contamination. Following the vacuum treatment, the specimens were wrapped in molybdenum and annealed for 1week at 800°C under two atmospheres of argon. After water-quenching, the rods were ground so that the thickness tapered to 0.1 mm at the tips. The ground specimens were then recapsuled as previously and reannealed 1 hr at 800°C to remove cold work. The

Jan 1, 1961

D. M. Riordan has been appointed a member of the Institute Com¬mittee of the Engineers' Reserve Corps movement. Our Committee, therefore, now consists of Henry S. Drinker, Chairman, Messrs. Arthur S. Dwight, Warren A. Wilbur and D. M. Riordan.

Jan 1, 1916

By W. G. Bearden, G. C. Howard, J. W. Spurlock

An investigation of the factors af-fec.ting the inter-zonal flow of fluids in the casing-wellbore annrc1rt.s of an oil or gas ivell is presented Laborntory tests revealed that failure of the caring-cement bond allows communi-cation of fluid at pressure differentials near 1.000 psi. Perforating with a 11011011: carrier gun does not shatter or crack the cement sufficiently to allow communication through these cracks and does not seriously affect the casing-cement bond failure pressure. The pressure to cause communication at the casing-cement bond can he increared to 3,000 psi by. limiting pipe deformation during cementing and subsequent operations. Communication can be prevented, however. up to pressures sufficient to cause the cement to fail or the casing to col-lapse, by attaching to the casing a seal ring of deformable ruhber molded between two steel flanges. When installed, one flange is attached rigidlv to the casing to serve as back-up for the gasket While tile other flange is movable. To date, these gasket seal rings have been field-tested in 27 Wells. Althotrgh communication has been noted in two wells, inter-zonal flow has been prevented in other wells in the same area by installing more seal rings between the communicaring zones. INTRODUCTION The inter-zonal flow of fluids behind casing cemented in oil wells during normal production or stimulation operations is a major operating problem. If it cccurs during production operations. it can seriously limit the pressure to which a reservoir may be depleted without harmful invasion of unwanted fluids. If it occurs during stimulation operations, it may preclude the possibility of stimulating the desired zone. This communication can be caused by failure of the bond between the casing and cement, failure of the bond between the cement and formation, or failure of the cement itself. This paper presents the results of an investigation of factors affecting com-munication at the casing-cement bond and methods which aid in preventing it. LABORATORY INVESTIGATIONS The laboratory tests performed in this study were divided into three phases. The first phase consisted of tests to determine if perforating would shatter and crack the cement sheath so severely that communication would occur through the cement itself. The second phase consisted of tests to determine more precisely the cause for the casing-cement bond failure. The third phase consisted of tests to evaluate the effectiveness of various de-formable seals attached to the casing in preventing communication. EFFECT OF PERFORATING, The effect of perforating was invest~gated in tests performed with apparatus shown on Fig. 1. Cement was poured into the annulur space hetween 5%-in. casing and 8%-in. casing and allowed to cure for 72 hours. The apparatus was then perforated with a hollow carrier gun containing eight duPont 26-A shaped charges. Bull plugs were placed over the perforations in the 8 5/8-in. casing and hydraulic pressure was applied inside the 5 1/2i-in. casing. The pressure to cause fluid communication past the cement sheath was observed and termed the "bond failure pressure". Several different cement compositions were included in these tests, the results of which are shown in Table 1. In Tests 1 through 4 of Table 1, bond failure occurred at- the inter- .

Jan 1, 1966

H. H. Kellogg (Columbia University)—The accurate measurements of the equilibrium gas ratios for the reaction: Pb(1) + H2S = PbS(c) + H2 [I] reported in this paper are a distinct contribution to the literature, and the authors are to be congratulated. I wish to comment, however, on the correlation of the data which is presented. The authors show a straight line correlation of log H2S/H2 vs 1/T, Fig. 1, and are satisfied with this for calculation of ?Fo even when extrapolated to low temperature (427 °C). Heat capacity data for the constituents of this reaction are available (at least to 900°K), however, and ACP for reaction [I] is finite and positive in the temperature range studied. Simplification of the heat capacity equations yields: ?CP= 2.71 + 1.65 x 10-3T (298°-900°K) This positive value of ?CP should result in a small but noticeable curvature of a plot of log K vs 1/T. That the experimental data fail to show such a curvature may be traced to another oversimplification of the author's treatment of their data. They assume that the activity of liquid lead is unity for all temperatures, so that

Jan 1, 1961

By John K. Gustafson

The title of my talk is "The Gold Miner and the Future of Gold." This title might just as accurately have been stated as "Gold and the Future of the Gold Miner." Since prehistoric times gold has been sought by mankind for its beauty and its unusual physical and chemical properties. Early in the dawn of civilization it became the ultimate unit of value and lubricated trade between peoples. For at least 6000 years, gold has been used to barter for other commodities. It has been prospected for, treasured, made into works of art and personal adornment, and from time to time has been the object of conquest. Because of its predominant role in recent centuries as a basis for money, economists began to think of it solely in these terms. Annoyed by the disciplinary pressure of gold on the money manager's desire to manipulate money, the famous economist, John Maynard Keynes, characterized it as a "barbaric relic of the past", a characterization repeated by William McChesney Martin, Jr., when he was head of the Federal Reserve Bank. Gold, however, has physical and chemical properties that make it one of the most useful metals in the modern world.' It is the most ductile metal known. An ounce of gold, for example, can be drawn into a continuous wire over 35 miles long. It also is so malleable that an ounce of gold can be beaten into films ten one-millionths of an inch thick sufficient to cover 68 sq ft of surface. It has a density of 19.3 and is so heavy that 1 cu ft of gold weighs more than half a ton. Gold is nonmagnetic and has a high electric conductivity, only slightly less than silver and copper. Gold is so inert to all the chemicals found in nature that gold coins and jewelry buried beneath the soil or at the bottom of the sea for thousands of years appear to be as bright and perfect as when they were first immersed. Finally, gold has an extremely high reflectivity both to light and infrared rays. Because of these qualities, in addition to its rare beauty, industrial and artistic uses of gold have been growing rapidly. On a world basis, a recent study estimated that in 1960 about 750 tons of gold were used for fabrication, and that the amount had grown to about 1296 tons in 1968. My objective in this talk is to discuss with you the present and future supply of and demand for gold on a worldwide basis and the effect these forces are likely to have on the price the miner can expect to receive for the gold he produces. This is a highly controversial and risky subject to discuss before any audience. Nevertheless, it is a subject that I live with constantly as Chairman of the

Jan 1, 1972

By W. C. Hagel, H. J. Beattle

DURING an earlier examination of high-temperature alloy, A-286, the presence of an unknown intermetallic compound was verified by X-ray diffraction. Owing to its prominent appearance at grain boundaries, the arbitrary name of G phase was assigned.' Low-silicon, vacuum-melted heats were found to contain no G phase, and this investigation was initiated to determine the influence of silicon on G-phase formation; additional work was undertaken to extend existing data on other intermetallic compounds and the aging reactions in this group of alloys. Taylor and Floyd2-4 observed that the Ni3Al phase (y') and the Ni8Ti phase (7)) are the only equilibrium intermetailic compounds in nickel ternary alloys containing up to 25 pct Cr and 10 pct Ti or Al. They found that y' can dissolve considerable nickel, chromium, and titanium, although the stoichio-metric composition of 7 remains fixed. Nordheim and Grant5 confirmed that age hardening of 80 pct Ni-20 pct Cr alloys of the Nimonic-80 type is due to precipitation of y', where aluminum is partially replaced by titanium. They suggest that optimum hardness and ductility result from increasing the titanium to aluminum ratio toward the end of the y' solubility range and from increasing total titanium and aluminum content to the maximum limit permitted by processing. Such information is necessary for those seeking to improve the service-temperature range and long-time structural stability of high-temperature components. Experimental Methods Compositions of materiais studied. are listed in Table I. Alloys D, E, and F possess representative A-286 analyses; silicon increases from less than 0.02 to 1.75 pct in alloys A to H; in alloys I to K, titanium decreases from 2.24 to 0.39 pct, and aluminum increases from 0.1 6 to 240 pct. Alloys A and D were solution heat treated for 4 hr at 1700°F, oil quenched and aged for 0.5, 2, 6, 12, 30, 70, 200, and 1000 hr at 1200°, 1300°, 1400°, and 1500°F. Therefore, a total of 33 specimens was required for each

Jan 1, 1958

CARL A. WENDELL, New York, N. Y. (written discussion*) .-I have never seen in print anything that even remotely has approached this article in clearness and important conclusions in conjunction with work done on the sink-and-float test. I have had many hundreds of these tests made and on different specific gravity solutions and the resultant product analyzed, but I have never grasped nor been able to show what this article sets forth. This article brings out one factor very clearly to my mind; what is to take the place of the solutions of different specific gravities used to obtain the laboratory results, when it comes to washing on a large scale, since water has one constant weight only? The answer is, sizing of coal. And as we know the importance of size versus specific gravity of the material to be washed, perhaps defined (practical) lines can ultimately be gotten up so that the sizing, if any, may be determined at the same time as the laboratory work on the coal is being done. G. R. DELAMATER, ? Steelton, Pa. (written discussion?).-The authors' deductions are well founded and although they disclaim any wide experience in commercial coal washing, practically all of the data presented are applicable to coals of all parts of this country. The paper clearly sets forth the great necessity of careful preliminary investiga-tion of each contemplated washery undertaking and contains the follow-ing very true statements. "It is not safe to assume that any coal which can he successfully washed on coarse coal jigs can be cleaned more com-pletely by washing at a finer size on tables," and "The effect of finer crushing upon the completeness with which impurities may be separated from coal depends upon two opposing tendencies. First, that the more finely a raw coal is crushed, the more completely will the particles of impurities be detached from the particles of clean coal. Second, the finer a coal is crushed the more difficult it becomes to separate the pieces of clean refuse from the pieces of clean coal."

Jan 12, 1919

By Edna A. Dancy, Ronald L. Pastorek, Gerhard J. Derge

In an earlier study1 in this laboratory, it was found that there is a minimum in the specific conductance of Ni-S melts in the region of the stoichiometric composition, Ni3S2. This and similar observations on other sulfide1 and telluride2 systems suggest that short-range order exists in the molten phase for several hundred degrees above the melting point, and a qualitative energy-band model has been proposed, with intrinsic semiconduction at the stoichiometric composition and degenerate electron and hole conduction at metal- and tellurium-rich compositions. This suggestion has been substantiated for the telluride systems by Seebeck coefficient measurements which showed a change in sign from negative on the metal-rich side to positive on the tellurium-rich side. In the present investigation, in order to substantiate still further the proposed model, Seebeck coefficient determinations have been extended to the Ni-S system over a composition range in the vicinity of Ni3S2. The experimental method was essentially the same as that used for the telluride systems, with minor modifications on cells for high sulfur melts to permit the use of tungsten wires and W— W-Re th~rmocouples instead of the chrome1 or alumel wires and chromel-alumel thermocouples originally used. Chrome1 and alumel both deteriorate very rapidly in atmospheres containing sulfur. The Ni-S alloys were prepared as described in the conductivity paper. Initially, a portion of the solidified melt was analyzed at the end of a run, but after this was found to be inaccurate because of segregation during cooling, the whole sample was analyzed. The nickel content, only, was determined, the sulfur content being obtained by difference. The results are summarized graphically in Fig. 1, and clearly show a change in the sign of the Seebeck coefficient in the region of the stoichiometric composition. This change of sign near Ni3S2, coupled with the minimum in the conductivity, is suggestive of an intrinsic semiconductor at the stoichiometric composition, with degenerate electron and hole conduction on either side of this composition, in keeping with the proposed model. The negative temperature coefficient of conductivity, normally indicative of metallic conduction, is not inconsistent with this model. In the completely degenerate region it would be expected, while in the vicinity of Ni3S2 the suggestion originally made by Argyriades, Derge, and pound3 for the Fe-S system can probably be applied. They proposed that the forbidden gap between the valence band and the conduction band is small, and that the increase in the number of the conducting species with increase in temperature is not large enough to compensate for the loss of mobility through thermal scattering. The research was sponsored by the Office of Naval Research under Contract NONR-760(22) Project NR 039-081. 'E. A. Dancy and G. J. Derge: Trans. Met. Soc. Aime, 1963, vol. 227, pp. 1034-38. 'E. A. Dancy: Trans. Vet. soc. AIME. 1964, vol. 233, pp. 270-77. 'D. Argyriades, G. Derge, and G. M. Pound: Trans. Met. Soc. . 1959, vol. 215, pp. 909-12.

Jan 1, 1965

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld' and verified by Opie and Grant' and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957

By Charles Austin

IT has been known for several years1 that certain alloys of the Konal type, containing commercial cobalt (99.32 per cent C0 and 0.42 per cent Ni) and varying amounts of ferrotitanium, exhibit very high tensile strengths at 600°C. However, their pro-portional limits and yield points are rela-tively low. Published data1 for the alloys quenched in water from 950°C. and then tested at 600°C. are summarized in the upper section of Fig. I. Similar specimens that were aged at 650°C. for 72 hr., after quench and prior to testing at 600°C., gave the results shown in the lower section of Fig. I. TABLE I.-Analysis of Material I Percentages Constituent Sample Sample Sample 3125 3124 3123 Si 0.25 0.51 o.6o Fe 4.15 10.70 13.17 Ti I.15 3.58 4.70 Mn 0.30 0.41 0.42 Co (by difference)^ 94.15 84.80 81.71 The cobalt from all three samples, united and tested for nickel, gave 0.54 per cent Ni based on the weight of cobalt. In the present work the investigation of the properties of these materials has been extended by a study of the tensile deforma- tion characteristics in moderately long-time tests at 600°, 700° and 800°C. after quenching from various solution tempera-tures. In addition, some metallographic studies have been made to correlate with the deformation tests, and to obtain in- FIG. 1.-EFFECT OF VARYING AMOUNTS OF FERROTITANIUM (FE2TI) ON PHYSICAL PROPER-TIES OF COMMERCIAL COBALT. (C. R. Austin.1) Upper section. Tested at 600°C. after water-quenching from 950°C. Lower section. Tested at 600°C. after water-quenching from 950°C. and aging 72 hr. at 650°C. FIG. 2.-PORTION OF QUASI-BINARY DIAGRAM COBALT-FE2TI AS DETERMINED METALLOGRAPH-ICALLY. formation on the quasi-binary system Cobalt-Fe2Ti. The material, very kindly furnished by the Westinghouse Electric and Manufac-turing Co. in the form of hot-swaged rods of 3/16-in. diameter, analyzed as shown in Table I. The alloys, when originally made up,1 were based upon an iron-titanium com-pound, Fe3Ti, as indicated by the work of

Jan 1, 1940

By George C. Stone

Since the Troy meeting I have received several additional results of analysis of the same sample of spiegel, which I give below: P. I know only by correspondence. His methods are : for results Nos. 47, 48 (13.03, 13.26) dissolve In hydrochloric acid, evaporate, oxidize with nitric arid, filter from silica, separate iron as basic acetate, precipitate manganese as sulphide, dissolve in hydrochloric acid; and precipitate as carbonate. No. 49 (13.72) was obtained by Eggertz's method. Nos. 50, 51 (13.10, 13.10) were dissolved and oxitfized as before, the iron precipitated by oxide of zinc, filtered and washed four times with cold water; and the manganese titered hot with permanganate. P. regards these two results as low. Nos. 52, 53 (13.75, 13.69) were dissolved and treated like the last two, the precipitated iron was again dissolved, separated, and titered as before; the results are the sum of the manganese joined in both

Jan 1, 1884

By Charles Y. Clayton

A study of the literature shows that the greater part of research work on annealing of cold-worked iron has been for the purpose of studying the effect on grain-size and properties other than hardness. No reference has been found of experimental work of the same nature as that explained in this short paper. The material used throughout was Vismera iron, an iron containing 0.03 carbon and made several years ago by the Inland Steel Co. One-half inch stock was cut into cylinders % in. long. The cylinders were then compressed for 60 sec. in a Reihle testing machine under loads as indicated below: CoMPressiON, Average Length, Series Pounds Inches 1 10,000 0.693 2 15,000 .599 3 20,000 .501 4 25,000 .426 5 30,000 .378 6 35,000 .351 7 40,000 .311 Fig. 1 shows these cylinders after compression. Each series consisted of 17 specimens lettered 0, B, C, D, E, F, G, H, I, J, K, L, M, N, P, Q and R. One specimen of each series was reserved for study of the properties in the cold-worked condition. The other specimens were annealed in a Hump furnace for 1/2 hr. at the following temperatures: TEmpeRa- TempeRa- Letters tuRe,° C. LettERs tuRe °C. B............................... 250 J.............................. 650 C............................... 300 K............................. 700 D............................... 350 L.............................. 750 E............................... 400 M............................. 800 F................................ 450 N............................. 851 G............................... 500 0. . :........................... 900 H............................... 550 P.............................. 950 I................................ 600 Q............................. L000

Jan 1, 1926

By M. R. Pickus, C. H. Mathewson

THE study of the plastic deformation and recrystallization of metals has been the subject of many investigations. In regard to the simple deformational processes, such as tension and compression, the early knowledge gained from studies of polycrystalline material has been supplemented by many significant researches on the behavior of single crystals. Unfortunately, this has not been true for more complicated deformational processes. As far back as 1927, G. I. Taylor1 wrote: It is impossible in the present state of knowledge to do more than give a possible reason why (face-centcred cubic) crystals set themselves with a (110) direction in the plane of rolling, and at right angles to the direction of rolling. The explanation of why the orientation of the crystal axes round the transverse direction is what it is, must be left till the distortion of metals, and particularly single crystals of metals in the process of rolling, has been studied in greater detail. That this gap in the systematic study of deformation and recrystallization has not yet been filled was indicated by C. H. Samans,2 who wrote in 1934 that "only four investigations upon cold-rolled single crystals of any of the face-centered cubic metals have been reported in the literature." Of these four studies, only those of S. Tanaka3 and T. Sakao,4 both of whom worked with aluminum crystals, had quantitative significance. The other two, carried out by F. Wever5 and W. G. Burgers," were of a qualitative nature. It is our hope that the present investigation may contribute something to the knowledge necessary for a rationalization of the origin of rolling textures in terms of the known behavior of single crystals, and may add pertinent information concerning the recrystallization characteristics of deformed single crystals.

Jan 1, 1938