By Seyed Mahdi Abbasi, Adel Sheikhhosseini

"This research was conducted to study the changes of microstructure, chemical composition and mechanical properties ofIN718 superalloy after adding aluminum to the ESR process slag. The experiments were performed in VIM and ESR furnaces. The results showed adding 1.5 percent aluminum to the slag increase lave phase in the IN718 samples from 0.34 percent in the base sample to 3.0 percent. It also indicated that the more increase of aluminum in slag cause decrease in the aluminum absorb yield in the superalloy.it is observed that increasing aluminum from 0.7 to 1.1 and then to 1.5 percent caused a decrease of absorb from 91.4 to 76.3 and 74.6 percent respectively due to increasing of aluminum oxidation. According to the results, tensile strength increased and ductility declined in the IN718 samples mainly because of rising the amount of y' volume fraction.IntroductionIN718 superalloy is an iron-nickel base superalloy with constant mechanical properties at medium at high temperatures. For the past seven years a considerable amount of time and effort has been expended by both suppliers and users in the study of Alloy 718 [ 1]. The interest in this material stems not only from the interesting metallurgy associated with the alloy, but with the large usage of the material in numerous applications In fact many people believe that the projected use of this alloy increase significantly over the next several years, The large use of Alloy 718 is the result of its performance in respect to high strength, good ductility, good repair weld ability and from its versatility of being supplied in various product forms. This superalloy is used in wide ranges of industries such as aerospace and gas turbines [2]. In the past more than 20 years many researchers did a lot of work to improve the structure stability of IN718 at high temperatures and intended to develop a new 718 type alloy to be used beyond 650 °C. One of the methods is to control and phase precipitation behavior by means of adjustment of Al, Ti and Nb contents. The other idea is to strengthen the matrix by altering the content of solid solution elements such as W and Co. The adjustment of these alloying elements can change phase precipitation behavior [3]. If detailed information dealing with phase precipitation behavior can be obtained before experimental work for alloy development, a lot of time can be saved and the development cost can also be reduced. In recent years, computer modeling based on experimental data plays an increasing role in alloy design and development. Adding Al to the Iron and Nickel increas the strength of superalloy by formation of y phase and subsequence formation of n phase. Ti in IN718 superalloy also helps the formation of MC carbides and gamma prime phase. Increasing Al/Ti and (Al + Ti)/Nb will lead to form finer particles of y'. More uniform distribution of the precipitates and enhancing stability of y' in IN718 superalloy [ 4]. Adding Al to slag of ESR process can reduce the oxide inclusions because of the strong tendency of Al to oxidation. In addition, tensile properties of IN718 superalloy improve. The most significant inclusions in IN718 superalloy are Alz03 and TiN that were found in agglomerate forms. Thermodynamic calculation results indicate that the effect of increasing Al shows a strong increase in solvus while phase solvus shows mildly decrease when Al level is less than 2%, after that it dramatically decreases [ 5]. Laves phase precipitation and the appearance of phase are occurred when Al content reaches 2%. In fact, when Al content is beyond 1.5%, phase has already precipitated in a considerable scale. Shows the fraction of increases greatly while the fraction of phase decreases remarkably with the increment of Al content. Based on thermodynamic theory, if these particles were not existed in the melt during cooling agglomeration would not accrue and the superalloy will be cleaned By adding Aluminum to the slag, the metal reacts with oxyge"

Jan 1, 2013

By Gabriel A. Torma

This paper provides infonnation on selected technologies available for remediation of metal contaminated soils and industrial effluent solutions. Because some of the industrial sites are contaminated with organics (solvents, gasolines and oils), an effort has been made to introduce the most frequently used cost-effective cleanup methods, such as "bioventing" and "composting." The microorganisms involved in these processes are capable of degrading organic soil contaminants to environmentally harmless compounds: water and carbon dioxide. Heavy metals and radionuclides contaminated mining and industrial sites can be remediated by using adapted heap and dump leaching technologies, which can be chemical in nature or bio-assisted. The importance of volume reduction by physical separation is discussed. A special attention is devoted to the remediation of soils by leaching (soil washing) to remove heavy metal contaminants, such as chromium, lead, nickel and cadmium. Furthermore, the applicability of biosorption technology in the remediation of heavy metals and radionuclides contaminated industrial waste waters and acidic mining effluent solutions was indicated.

Jan 1, 1996

By Jerome P. Downey

Technologies developed within the field of extractive metallurgy to recover, concentrate, and purify metals and industrial minerals from ores, have served as the foundation for all of the subsequent environmental remediation, materials recycling, and waste management technologies. This paper discusses the application of classical extractive engineering principles to the development of a thermal process for the recovery of mercury from solid wastes. Process development is presented as a series of logical stages, which begin with a thorough characterization of the site-specific waste, move on to bench and pilot scale testing of the process options, and end with a functional process flowsheet. This paper also presents thermodynamic data on many mercury species of interest to the minerals, power, and chemical industries. These data can be used to model the speciation and recovery of the mercury as a function of various process parameters.

Jan 1, 2003

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were examined during the entire growth stage of bacteria (fermentation), The pyrite ?surface invariably drastically changed ' its. properties at the second day of fermentation. Beyond two .. days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The product layer was examined by SEM,. X-ray diffraction and chemical analysis. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became .insensitive to convective diffusion in solution (stirring). The x-r:ay diffraction study confirmed jarosite as a product layer. A mechanism of T. ferrooxidans cells serving as nucleation sites for jiarosite formation is proposed.

Jan 1, 1991

By A. McLean, S. Dawson, N. D. G. Mountford

"IntroductionIn order to predict the accepted industrial practice for the year 2000, it may be helpful to first consider the rate of development of scientific knowledge. If the speed with which man can travel on commercial vehicles is taken as a criterion for determining the rate of progression, then it can be seen from Figure 1 that advancement in our present century is very rapid. Likewise, if computer technology is used as a criterion for the measurement of scientific advancement, it becomes evident that technological evolution can be highly exponential. These two examples are sufficient to demonstrate that engineers and managers cannot afford to regard scientific development as being linear with respect to time if they are to avoid underestimating the needs of society.Within this framework of overall development, the time required for individual ideas to progress from inception to regular application has decreased considerably. For example, X-rays first discovered by Roentgen in the 1890's and now used widely in medicine and engineering, required a developmental period of some eighty years. The motorcar evolved from early beginnings at the turn of the century to a position of great social impact in sixty years. Rectifier materials used in high frequency radar to the present explosion in communications, required forty years. As illustrated in Figure 2, the period is shortening rapidly.The use of sound waves appears to be following a similar path. There is now a considerable body of knowledge concerning their behaviour and exceptional advances have been made. In medicine and engineering the sonic approach to examination is well established, and acoustic testing forms the basis of several diagnostic and quality control applications. With respect to metals engineering, ultrasonic testing has contributed to the understanding of the relationship between the size and number of internal defects and the probability of premature failure. This has allowed the designer to incorporate appropriate safety factors in his designs; but more importantly, the realization of the deleterious effect of inclusions on the performance of the final product has resulted in a continuous pressure on the material suppliers to reduce the number of defects in their products.It is not only the designer who is demanding defect free material but also the fabricator, as material breakdown during manufacture can be prohibitively expensive. Examples of this can be found in both the aluminum and steel industries where ultra clean sheet is required to ensure that rejections are minimized during beverage can manufacture and other deep drawing operations."

Jan 1, 1988

By U. M. Mutnti

In order to meet the stringent market requirements for high purity cobalt, ZCCM commissioned the VIR plant in December 1982. The plant comprises a 4.1 tonne/heat vacuum induction furnace with a rated annual capacity of 2,500 MT of barstock. In the VIR furnace, molten cobalt is held under vacuum at 1600°C resulting in the removal of more volatile impurity elements by distillation. Operations todate have demonstrated that Pb, Zn and Cd have good distillation rates in excess of 95%, leading to cobalt containing 1 ppm or less of the above elements. Removal of other impurities such as Se, Bi is about 65% with the finished product still assaying around 1 ppm of each of these elements. Vacuum refining of cobalt offers an economic route for producing higher grades of cobalt from the type of concentrates and treatment processes available within ZCCM. The consistency of VIR cobalt quality has been confirmed by ZCCM and some of its alloy customers.

Jan 1, 1988

By Miller, Geoffrey W.

The Ravensthorpe Nickel Project (RNP) flow sheet provides for the upgrading of Ni & Co in a size based beneficiation process prior to leaching. The upgrading effect on Ni and Co makes the beneticiation process a powerful addition to the flow sheet. Multiple linear regression (MLR) analysis based on 351 individual batch tests, 52 large scale composites and 21 pilot plant tests has been used to successfully model beneticiation product grade, recovery, upgrade and mass recovery. Statistically, 83% and 96% of the variability in nickel recovery and nickel product grade respectively was accounted for. Algorithms have been developed for Ni, Co, Mg, Al and Fe, which represents the revenue and operating cost factors for the process. The algorithms have subsequently been applied to the resource model, allowing prediction of elemental grade and recovery for the development of the mine schedules based upon these parameters and not head grades alone. This has allowed optimisation of the mine schedule for improvement to the project's NPV. Keywords: Ni Laterite, Prediction, Multiple Linear Regression, Beneficiation

Jan 1, 2004

Gas flow and heat transfer phenomena in two industrial-scale waste-heat boilers of the Outokumpu copper flash smelting process were analyzed with a commercial computational fluid-dynamics (CFD) package Phoenics. Various operating conditions were simulated for the first boiler and particularly for the second boiler. The gas flow pattern was compared qualitatively with the physical laboratory models, and the general flow pattern was consistent with the laboratory visualization. The heat transfer simulation was validated with, temperature measurements for both boilers, and good agreement was reached between the computed temperature profiles and the measured data. The computational results indicate that gas flow in both boilers is of three-dimensional and recirculating nature. The numerical tracer experiments indicate that some dead volume is present in both boilers, and the boiler modification reduced the dead volume from 38% to 15% under basic operating conditions. Radiative heat transfer accounts for 65-90% of the total 'heat transported in the radiation sections of both boilers under different operating conditions. The modified boiler is very efficient for cooling the off-gases at almost doubled volume flow rate. The CFD modeling proved to be a useful tool for numerical experiments and analysis of boiler performance for process: optimization.

Jan 1, 1998

By Kazuteru Tozcwa

The oxidation of several sulfide minerals in aqueous ammoniacal solution is discussed thermodynamically. The region in which Cu(NH3)2 4+ is stable has been estimated as a function of pH and concentration of total ammonia, {[NH3) + [NH4)}. In ammonia leaching when copper in sulfides is assumed to be extracted in the form of Cu(NH3)2 which will be rapidly converted to cupric ammine, thermodynamic data predict that such minerals are oxidized readily in the following order, CuS, Cu2S, CuFeS2, ZnS, NiS, Ag2S. This agrees with investigations on ammonia leaching of sulfide minerals, reported previously. The leaching of copper sulfide concentrate has been examined experimentally. Copper in a copper sulfide concentrate, in which the main constituents were chalcopyrite and pyrite, was effective¬ly extracted. The copper extraction was affected by factors such as (1) agitation intensity, (2) oxygen partial pressure, (3) NH3/Cu molar ratio, (4) leaching temperature and (5) addition of ammonium sulfate. From the results obtained in this work, it is concluded that mass transfer of oxygen plays the most important role in ammonia leaching of copper sulfide minerals.

Jan 1, 1976

By Luis M. González, Guzmánm Guillermo D., Davis Juan C.

"The Teniente converter (CT) of the Ventanas Smelter and Refinery of Codelco-Chile has two tuyeres for dry concentrate injection directly into the melt.The diluted phase injection system can feed 15 to 20 kg of concentrate for 1 kg of air, which creates a very abrasive solid/gas phase. The tuyeres commonly used lasted for about 3.5 days due to the accelerated decay of the shell, and 1.5 hours were necessary for the replacement of new ones in the reactor.Tests were carried out with common shell tuyeres with a tungsten based welding cover, and a life span of 28 days was reached, increasing the Teniente converter operational continuity between 1.5 to 2 %."

Jan 1, 2009

By Aarne Kopanen

In recent years, various renovations have been carried out in the production chain of the Outokumpu copper refinirg process. The anode casting shop, which is the final integral production section at the Harjavalta copper smelter built in its original form in 1945, was fourxl unsuitable for technical and capacity demads during longer periods of operation, and a new casting shop was built in 1974. The electrolytic copper refinery of Outokumpu Oy at Pori was built in 1941, and subsequently expanded in two stages. Even with its present limited scale of production it has been fom important to mechanize the main operations. This work was started in 1967 with the design and construction of the starting sheet machine connected with the cathode washing and unloading machine as a combined unit. Mechanized treatment of anodes has gained advantage particularly from the new design of a highly automated anode casting shop. In the further development of the mechanization a stripping machine for, starting sheets was designed and installed, starting operation in 1974.

Jan 1, 1976

By Roland Loewen

A review of the aqua regia method for the recovery of gold from jewelry shop wastes is given. Also outlined is a specialized procedure for the recovery of the silver that occurs in these wastes. A classic method for the recovery of platinum and palladium is, given. There is a brief review of other gold and silver refining methods. Environmental conditions are discussed and a few perhaps, new and useful processes ,are mentioned. References are by author or editor and are listed alphabetically. Suggestions for further information in the field of precious metals, are given in a final list.

Jan 1, 1989

By K. Morsi, P. Mehra

"Spark plasma sintering has gained a considerable amount of attention over the past decade, due to its rapid sintering rates, and low temperature requirements, but has so far been usually limited to the production of simple geometries. The present paper examines the current-activated production of extended geometries through the process of spark plasma ""extrusion"". Of interest in the present study is exploratory research into the effect of electrical current activation on the reactive consolidation of powder systems to form intermetallic materials.IntroductionSpark Plasma Sintering (SPS) has been the subject of intense research over the past decade [ 1,2, 3,4,5,6]. The process boasts unique advantages which include ultra fast heating rates, shorter sintering times and lower sintering temperatures than needed in conventional sintering. The process is however limited to the generation of predominantly simple geometries. Recently one of the authors investigated the spark plasma extrusion of aluminum, where an aluminum powder compact is directly (Joule) heated through an applied DC electric current. Here extended geometries can be generated under the influence of electric current. A number of heating sources were identified including the heat source from current, i.e. Joule heating, frictional heating and heat from the deformation energy. However in the case of reactive powder systems, an extra ""one-time"" transient heating source can be supplied. By considering combustion synthesis of powders, this heating source is derived from the reaction between elemental powders to exothermically form a product at some ignition temperature [7]. This exothermic energy heats the compact to the maximum ""combustion temperature'', which could be hundreds of degrees higher than the ignition temperature. Hence a high temperature processing window (of short duration due to heat losses to the surroundings) becomes available in which the material is most suitable for stress-induced deformation and consolidation. For reactive spark plasma extrusion, two scenarios can be envisioned. The first is where the reactive powder compact is ignited through the application of current, and extruded within the high temperature processing window (also under the influence of current). The second scenario is to allow the heat of deformation/friction to heat the material during extrusion, to simultaneously force a reaction and consolidation. Here it is expected that the processing window will be very small if feasible."

Jan 1, 2011

By Katsuyoshi Kondoh

The synthesis processing of Mg2Si or Mg2Si/MgO at lower temperature from the elemental magnesium alloy powder/chips and Si or SiO2 powder mixture was established via the repeated plastic working (RPW) based on Powder Metallurgy (P/M) process. RPW is much effective on the mechanical breakage of MgO surface films, which prevent from the solid-state reaction between Mg and Si powder. The solid-state synthesized Mg2Si particle of 200nm-2JIm is extremely fine, compared to that via the conventional casting process, causing the coarse one of 50-100um. This is because of not coarsening during the solid-state synthesis of Mg2Si. By using in-situ forming process of Mg2Si via RPW and pre-heating before hot working such as extrusion and forging, the magnesium composite material with Mg2Si or Mg2Si/MgO dispersions was developed in employing Si or SiO2 particles, respectively. For example, when employing AZ31 chips as raw materials of the matrix, it has low density of 1.85g/cm) and extremely superior mechanical properties, such as tensile strength over 350MPa with 5-10% elongation and Young's modulus of 47-50GPa, to the conventional Mg-Al-Zn alloys. The Mg composite alloy wires and pipes were produced via the hot extrusion process in the manufacturing plant, and also showed excellent mechanical properties.

Jan 1, 2003

By Katsuyoshi Kondoh

The synthesis processing of Mg2Si or Mg2SiIMgO at lower temperature from the elemental magnesium alloy powder/chips and Si or SiO2 powder mixture was established via the repeated plastic working (RPW) based on Powder Metallurgy (PIM) process. RPW is much effective on the mechanical breakage of MgO surface films, which prevent from the solid-state reaction between Mg and Si powder. The solid-state synthesized Mg2Si particle of 200nm-2um is extremely fine, compared to that via the conventional casting process, causing the coarse one of 50-100um. This is because of not coarsening during the solid-state synthesis of Mg2Si. By using in-situ fonning process of Mg2Si via RPW and pre-heating before hot working such as extrusion and forging, the magnesium composite material with Mg2Si or Mg2Si/MgO dispersions was developed in employing Si or SiO2 particles, respectively. For example, when employing AZ31 chips as raw materials of the matrix, it has low density of 1.85g/cm3 and extremely superior mechanical properties, such as tensile strength over 350MPa with 5-10% elongation and Young's modulus of 47-50GPa, to the conventional Mg-Al-Zn alloys. The Mg composite alloy wires and pipes were produced via the hot extrusion process in the manufacturing plant, and also showed excellent mechanical properties.

Jan 1, 2003

By Yutaka Yasuda

The particle dispersion phenomena in a turbulent gas jet of the flash smelting process has been investigated. The particle number density in a non- reacting jet was measured experimentally by taking photographs of the particles in flight and counting them using the image analysis. Numerical computations were also performed using a mathematical model for a turbulent particle laden gas jet The experimental particle number density data were then compared with the predicted results of the model. Good agreement was obtained between the experimental and predicted data. The effects of the parameters such as the injector design, particle loading and air flow rate are discussed. Optimization of the concentrate burner design can be achieved with the help of experimental and theoretical simulation as performed in this work.

Jan 1, 1994

By James Vaughan

Ionic liquids are solvents of interest for applications such as electro- plating, winning and refining of metals. Of particular interest is the possibility of processing reactive metals such as aluminium, magnesium and titanium that cannot be deposited from aqueous solutions. Aluminium has been electro deposited from AlCl3 : ionic liquid mixtures at low temperatures relative to conventional Hall-Héroult smelting. Imidazolium ionic liquids are have been used in the past due to their relatively high ionic conductivity and cation stability. The less studied and less expensive phosphonium ionic liquids systems may provide a viable alternative to imidazolium ionic liquids for certain applications. New information regarding the physical properties and electrochemical behaviour of phosphonium ionic liquid systems is presented.

Jan 1, 2006

By S. G. Kumar, R. G. Reddy

"Niobium aluminides offer the advantage of higher high temperature capability compared to other intermetallic aluminides due to the refractory nature of niobium. However, the reaction sequence in Nb-Al system is sluggish and currently there is a great interest in the processing aspects of these materials. In the present study, a systematic investigation was undertaken to compare the effect of different powder metallurgy processing routes on the phase relations and microstructure of 66Nb-22AH2Ti (in atom percent) alloy. The three different process routes adopted were: (i) cold pressing followed by reaction sintering; (ii) cold pressing and hot pressing followed by sintering; and (iii) arc melting, hydride-dehydride process to make the alloy powder followed by cold pressing and then sintering. The samples are analyzed by XRD, Optical Microscopy, SEM-EDS and EPMA. The analysis showed that alloy pellets made from pre-alloyed powders i.e., arc melting followed by hydride-dehydride process, gave good densification and more Nb3Al formation.1. IntroductionTo improve the performance standards of turbine engines, materials scientists are challenged to develop materials that have· high thrust-to-weight ratio with high specific strength, high specific modulus and good environmental properties at elevated temperatures. The conventional high temperature materials like nickel based superalloys are high in density and hence many of the high temperature materials scientists have focussed their attention on intermetallic aluminides like Fe-AI, Nb-AI, Ni-AI and Ti-AI in recent years. The phase relations and properties of alloys based on Fe-AI, Ni-AI and Ti-AI are fairly well known whereas little is known about the alloys based on niobium aluminides."

Jan 1, 1996

By Magnus Ek, Peter Olsson

The Rönnskär Smelter has been faithful to Peirce Smith Converting during its 79 years of existence. Though a visitor to our smelter museum will easily find out that a lot has happened since the beginning – and development continues. In this paper an up-date on Converting and Casting at the Rönnskär Smelter is presented. Recent developments include an investment into converter process gas handling, but also day-to-day operational aspects such as converter aisle productivity and flexibility, but also minimal EH&S impact. 127

Jan 1, 2009

By Jae-Ho. Lee

Mercury is a toxic contaminant encountered in the extraction of gold from mercury-containing ores. It is found in the leach solution of CIP circuits and in the cathodes of the electrolyte cells used to electrodeposit the gold. The research conducted has examined the potential for selective removal of mercury from synthetic Au-Hg-CN electrolytes containing only gold, only mercury, and both gold and mercury. Cyclic voltammograms were obtained for mercury- coated copper electrodes with these cyanide electrolytes. Exchange current densities were determined from the voltammograms in the low overpotential region. Laboratory scale batch- electrolysis at constant current was also conducted for the electrolytes containing only mercury and both mercury and gold, at 20 and 50°C and from which the kinetic behavior associated with the process was analyzed. The surface of cathode before and after electrolysis was also characterized and a copper mercury intermetallic (CyHg,) was identified. Gold codeposited with mercury during the later stages of electrolysis. The results of this work corroborate that the mercury-amalgam copper electrode offers a viable electrochemical technique for the selective removal of mercury, however a high-surface-area cathode-cell would have to be utilized to provide for the desired selectivity.

Jan 1, 1994