Search Documents

By H. I. Aaronson, H. A. Domian

The self-diffusivity of Ag10 has been measured as a function of temperature and composition in AgMg. a CsCl-type intermetallic compound with a substitutional defect structure on both sides of the stoichiometric (50 at. pct Mg) composition. These measurements show that In D increases linearly, and both In Do and Q decrease linearly with deviation from stoichiometry. The slopes of these lines are significantly steeper in magnesium-rich alloys. Equations for the variation of Q with composition have been derived by application of the theory of random walk processes on the assumption that diffusion in compounds of this type takes place by the six-jump cycle mechanism of Huntington, Elcock, and McCombie. The favorable agreement obtained with experiment furnishes fresh support for the correctness of this assumption. A principal result of this treatment is that. although the concentration of vacancies is considerably higher in the silver sublattice than in the magnesium sublattice, the acfivation energies for movement of the magnesium sublattice vacancies are so much lower that these vacancies are responsible for effectively all diffusion of silver in this compound. A tendency for vacancies of both types to be kinetically bound to wrong atoms is also noted. THIS study was undertaken to examine the influence of substitutional defects upon self-diffusion in an intermetallic compound, AgMg, with a CsCl-type crystal structure. The CsCl structure is exception- ally simple. At the equiatomic or stoichiometric composition in a binary alloy, it consists of two interpenetrating simple cubic sublattices, each of which is exclusively populated by the atoms of one species. When atomic size and other factors are favorable, deviations from stoichiometry can be entirely accommodated by the substitution of atoms of the species present in excess of 50 at. pct on the sublattice of the other species on a one-for-one basis. Under this condition, the only vacancies present are those formed by thermal activation. The excess atoms thus incorporated into the sublattice of the minority species may be considered as substitutional defects in this sublattice. Several X-ray studies have shown that the defect structure of AgMg is entirely of the substitutional type on both sides of the stoichiometric composition.1"3 The thermodynamic investigation of Kachi indicates that, aside from a low level of thermal disorder and these constitutional defects, order is maintained to the solidus temperature. This compound is therefore a particularly useful vehicle for a study of the influence of substitutional defects upon diffusion kinetics. Other advantages of AgMg for this purpose include: the broad composition region, as much as approximately 10 at. pct on either side of the stoichiometric (50 at. pct Mg), in which the compound is stable; the comparatively low temperature range of the solidus (820°C and below),5 making diffusion anneals near this range experimentally convenient; the reasonably good machinability of the compound, permitting utilization of the standard sectioning method of radiotracer analysis; and the availability of a good tracer, A for one of the constituent species. While this investigation was in progress, Hagel and westbrooks reported data on the self-diffusion

Jan 1, 1964

By M. E. Wadsworth, G. W. Warren

INTRODUCTION Hydrometallurgical processes for the extraction of metal values can be divided into two broad categories: (a) Processes involving the treatment of high grade material (e.g. finely divided mineral concentrates); and (b) processes which treat lower grade material (ores, waste dumps, etc.). This discussion will be directed primarily toward the first category, but in either case a fundamental knowledge of the intrinsic kinetics and thermodynamics is necessary to understand the behavior of the system. The bulk of research efforts in the last decade along these lines has been aimed at the recovery of copper (1-8). However much information has also been reported on uranium (9, 10) , zinc (11) , cobalt and nickel (12, 13). More comprehensive reviews on these areas are also available (14). As discussed by Sepulveda and Herbst (15, 16) one of the most difficult problems facing process designers is the acquisition and scale-up of reliable information concerning the intrinsic kinetics of leaching systems. The scale-up or modeling of these multiparticle systems is far more complex than that of homogeneous ones. This is due to the numerous rate determining steps which are possible with heterogeneous reactions and the broad distribution of properties of a multiparticle feed such as particle size and mineralogical composition (16). In addition, other factors must also be considered such as interactions between particles, the anisotropic nature of individual particles, the effect of solution chemistry, and electrochemical phenomena. All of these factors must be taken into account, often simultaneously. The thrust of this paper will be to more closely examine how the factors mentioned above can be treated. Some elementary examples of

Jan 1, 1980

Jan 1, 1879

By J. M. Callow

THE results obtained by pneumatic flotation throughout the country on all classes of ore, and. the tonnage now being treated by this particular method, speak for themselves. Its advantages over the so-called agitation process are now established by facts and data from practice. The comparative efficiency of a rapidly revolving paddle, as a means for aerating an ore pulp, and of a cycloidal or turbine blower for the same purpose, would seem to be so obvious as to leave no room for discussion. Practitioners in this art are to be congratulated on the acquisition of the valuable literary contributions that have recently been made on the theory of. flotation by Messrs. Ralston, Van Arsdale, Taggart and Beach, and others, and the very valuable and able articles, by Messrs. Laist and Wiggin on "Flotation Concentration at Anaconda, Mont.," by, Dr. Rudolf Gahl- on the "History of Flotation at Inspiration," and by David Cole on "The Advent of Flotation in the Morenci District." It is not within the province of this article to attempt an answer to the various issues raised in regard to the theory, or to defend the one advanced by me a year ago. But since discussion usually benefits the profession, a reply will be made to some of the statements made by the last-named writers. COMPARATIVE SENSITIVENESS AND ATTENDANCE Concerning 'the article, "Flotation Concentration at Anaconda, Mont.," by Laist and Wiggin, a little explanation is in order. It should be stated that; with the exception of about 24 days at the end of the testing 'period, the Callow experimental plant at Anaconda was not run under my direction. This perhaps accounts for some of the conclusions drawn on page 562 of the descriptive paper. The conclusion that the use of acid seems to be of considerable advantage, calls, for some comment. While the tests conducted by the Anaconda Copper Co. do show acid to be, of considerable benefit, this is a consequence of using acid sludge as a flotation agent. My belief has always been that the Anaconda

Jan 2, 1917

By Edward W. Parker

THE agreement of September, 1922, between the anthracite operators and the United Mine Workers of America, which followed the 54.5 months strike during the summer of that year, contained the following provision : The parties unite in a recommendation to Congress that legislation be forthwith enacted creating a separate anthracite coal commission with authority to investigate and report promptly on every phase of the industry and the parties hereby ask the President to request the enactment by Congress of the recommended legislation. The continuance of production after Aug. 31, 1923, shall be upon such terms as the parties may agree-upon in the light of the report of the Commission.

Jan 1, 1924

By James W. Malcolmson

This paper treats of the history and development of the Sierra Mojada mines in the north of Mexico, the character and extent of the ore-deposits, and the methods of mining the ore. The growth of the smelting industry in Mexico in recent years is, to a large degree, due directly to the output of the lead-bearing ores from the Sierra Mojada mines, and at the present time (1901) new smelters are being built, looking to this district for their supply of lead-ores. These mines are located in the southern part of the State of Coahuila, in the Republic of Mexico, in latitude 27 24' N. and longitude 103O 43' W. of Greenwich. The last account of the Sierra Mojada published in our transactions was contributed by Mr. Richard E. Chism, in October, 1886.* Since that time some 3,000,000 tons of ore have been extracted from the mines, and much additional information has been developed regarding the mineral deposits. Since 1886, the Mexican Northern railroad, 78 miles in length, has been built from Escalon, connecting the camp with the Mexican Central railway, a trunk-line from El Paso, Texas, to Mexico City. The distances by rail from Sierra Mojada to the principal smelting-centers are as follows : To Torreon, Coahuila, Mex., 179 miles; to Monterey, Nuevo Leon, Mex., 422 miles; to El Paso, Tex., U. S., 494 miles; to Aguas Calientes, A. C., Mex., 522 miles; to San Luis Potosi, 8. L. P., Mex., 644 miles; to Pueblo, Colorado, U. S., 1158 miles; to Argentine, Kans., U. S.,

Jan 1, 1902

By P. D. Zemany, G. W. Sear, B. W. Roberts

Vanadium metal is embrittled by hydrogen at a temperature as low as 250°C when held in the presence of manganese metal and water vapor in a rough vacuum. It is established that the property changes are caused by the catalytic decomposition of water vapor at the vanadium surface and the diffusion into and solution in the vanadium of the resultant hydrogen. It is found that manganese is a necessary component of the catalyst. The manganese is transported in the vapor phase by an unknown molecule. A deuterium tracer experiment demonstates the role of water vapor in the embrittle-ment process. VANADIUM metal foils were observed to become embrittled' at a temperature of about 300 °C when held in the presence of manganese metal and a small amount of moist air, This paper describes the investigation to find the embrittling agent and an understanding of the relatively low temperature reactions that are involved. Experimental The vanadium metal foil used was prepared by cold-rolling and pack-rolling 32 mil sheet" in a series of steps down to 1 mil foil. The original observation was confirmed by sealing vanadium foils of 3 x 10 sq cm into individual Pyrex tubes with manganese powder† and a con- trol tube containing only the vanadium foil. These tubes were evacuated to 10 -5 mm Hg without baking and sealed. After heat treatment for 200 hr at 300°C, the control foil showed no change in duetility, whereas the foil contained in the manganese— containing tube was embrittled. The visual appearance of each was unchanged. A series of Pyrex sample tubes, about 2.5 cm diam and 25 cm long, were prepared, each containing a 3 x 10 sq cm piece of foil and 5 g manganese powder at the lower end of the tube. By reducing the time of anneal and the temperature of these samples, it was found that embrittlement could be created at 250°C in a time as short as 1 hr. Since the vanadium metal used here has been drastically cold-worked by rolling, it is assumed that it contains a maximum number of dislocations. To check the possible necessity of dislocations in this low temperature reaction, a vanadium foil sample was annealed in Vycor for 2 hr at 800°C to re crystallize and reduce the dislocation concentration. Metallographic examination showed grains which were not visible before annealing. The embrittlement procedure was carried out at 300°C and 3 hr. Upon checking the foil no embrittlement was observed. Further experiments demonstrated that about 6 hr at 300°C are required to create embrittlement in the foil. This delay in the onset of embrittlement in the vanadium foil suggests but does not prove that dislocation channels play a role in the embrittlement phenomena. If manganese metal is necessary for this low temperature embrittlement, do other elements in the transition metals group yield the same result? To check this qualitatively, a group of elements of similar atomic radii were obtained and sealed as before into Pyrex tubes with a sheet of vanadium foil. These tubes were annealed at 250°C for 6 hr and included (with radii)-2 A1 (1.4A), As (1.25A), Be (1.2A), Co (1.25A), Cr (1.45A), Cu (1.25A), Fe (1.25A), Ga (1.2A), Ge (1.25L%), Mn (1.3A), Ni (1.25A), Si (1.2A), Ti (1.45A), Zn (1.3A), air, H,O, 10 cm Hg of dry hydrogen, and MnO, powder. Upon testing the above sample foils for brittleness, only the manganese-containing tube yielded a brittle foil. Manganese Transport—To eliminate contact of manganese metal powder and vanadium foil, sample tubes were prepared with fritted glass barriers. The embrittlement reaction was still found to occur. Thus, the mode of transfer of manganese is certainly vapor transport. A vanadium foil was embrittled by this mechanism in an evacuated Pyrex tube for 8 hr at 300°C. By means of X-ray fluorescence analysis,' the amount of manganese added to the surface was established at 5 ±2 x 10 -6 g per sq cm. Since the average rate of manganese deposition is known, an effective average pressure of an assumed carrier compound can be computed. ___ P = M/T v2p mkT

Jan 1, 1959

By Eugene McAuliffe

TWO years ago the American Institute of Mining and Metallurgical Engineers made a memorable contribution toward a better understanding of the problems that have for many years confronted the coal industry. Specific suggestions toward betterment were then advanced, certain of which were taken up, amplified and endorsed by men who were conscien-tiously interested in the work of lifting this great industry out of the morass it has lain in for years. Two certain suggestions then made-provision for seasonal variations in railroad freight rates that would tend to encourage the purchase and movement of coal during the low summer production period, and provi-sion for the collection by the United States Government of all the facts surrounding the industry-were intro-duced in the form of legislation in the United States Senate by a member of that body, a man whose personal character, antecedents and business training put him above and beyond all suspicion of demagoguery; however, as the result of the insistent, vindictive opposition of the industry itself, these two bills, con-structive in their nature, were buried under an ava-lanche of misrepresentation. Today, with all mines that employ union labor at a stand still, the work of stabilizing the industry is yet before us. As aptly stated by Herbert Hoover, in March, 1920, when he was president of the Institute; An engineering organization is particularly the body to under-take this work. It is an economic problem, an engineering pro-blem within the ken of our experience; it is a problem that requires not only constructive thought but quantitative thought and wise social thought. The engineers of the United States occupy a position midway between capital and labor. They enter upon problems of this kind without prejudice either way, and they have that faculty of mind for quantitative thought, as distinguished from qualitative thought, that takes such problems as this out of the region of politics into the region of matter-of-fact solution.

Jan 5, 1922

By G. F. Comstock

The subject of transverse fissures in steel rails has been discussed very thoroughly in recent years from various points of view and the final opinions expressed may be roughly classified into two groups: That these fissures are the result merely of fatigue of the steel and are independent of the quality of the metal. That the quality of the metal and the mill practice must have something to do with them. The first point of view was most ably and logically presented by J. E. Howard,' and in the discussion of this paper, as well as in several other preceding publications, Dr. P. H. Dudley, Consulting Engineer of the New York Central Lines, has strongly defended the other opinion.2 The steel makers of the country have naturally rallied under Mr. Howard's banner, hoping to place the entire blame for these failures upon the railroads with their high wheel-loads, hard steel, heavy traffic, and sometimes inferior road-bed; while the railroad men, on the other hand, have been busy accumulating statistics and records in the effort to find an actual reason in the rails themselves that would account for the seemingly haphazard occurrence of transverse fissures under varying conditions and at widely separated points. The view that these fissures were due merely to normal fatigue under alternating stresses seemed most reasonable to the writer until quite recently, because from work done in this laboratory, as well as the work of other investigators, of the problem, no structural differences, in the vast majority of cases, were found between metal at the nuclei of transverse fissures and metal at similar positions in the same rails or in other rails that had not developed fissures. Within the last year or two, however, since the method of etching polished sections for the microscope with a oupric chloride solution has been tried systematically on lengthwise sections, passing through the nuclei of transverse fissures, evidence

Jan 1, 1920

By E. Keller

Some years ago the writer's attention was called to the fact that rolling-mill scales from auriferous copper do not have the gold content proportional to the gold contained in the copper from which they are derived.' So, later, he made a few simple experiments, which are described herewith. In order to test the gold movement on the changing surface of a copper plate under the influence of oxidation, plates 6 in. by 8 in. by 1 in. (15.2 cm. by 20.3 cm. by 2.5 cm.) of converter copper, refined, of 99.29 per cent. purity, and leaded copper with a content of 95.65 per cent, copper, were obtained. Ten cuts were made through the thickness of the plates along the longitudinal center and the silver and gold content ascertained in each of the 10 samples in both plates, as shown in the accompanying illustration. The assay results, recorded in Tables 1 and 2, show that the gold distribution is relatively uniform in both plates, while silver has greater variations, especially in the leaded plate. The plates subjected to oxidation were placed in a red-hot muffle for about 2 hr., two small scarifiers being used as supports. Arranged alongside each other, they nearly filled the width of the muffle, and so were practically under equal conditions of heat and draft. The accurate observance of the time was not possible, however, because of other work, but the time of the exposure of each plate in a pair was identical. At the end of each period, each plate was plunged into water and completely freed of scale, which was carefully collected, dried, weighed, and analyzed. Samples of the plates had also been taken of the molten metal and duly analyzed. Table 3 contains the analytical data for the two plates and their several sheets, or layers, of oxide scales. These figures show that in the oxidations of the converter copper the silver is fairly uniform, while the gold is highly irregular and especially low in the first layer. In the oxidations of the leaded copper plate, the silver and gold contents are variable; however, this irregularity is due to two different causes. The

Jan 1, 1919

A. W. TRACY' AND D. H. THOMPSON (presented in written form).-Messrs. Ed¬munds, Anderson and Waring are to be commended for their excellent work in so painstakingly reducing to constants, the variables believed to be associated with these types of stress corrosion. An ammonia stress-cracking apparatus similar in many respects to the one described has been assembled. Certain aspects of its construction may be of interest. Tensile loading of the specimens, which are usually Y8-in. diameter wires, is accomplished by springs acting in compression in compact, portable, tubular assemblies weighing less than 10 lb. The lower end of each assembly contains the test specimen and is passed into the test chamber for exposure to the moist ammoniacal atmosphere. There is considerable convenience in being able to load the specimens in a portable unit, which may be warmed to prevent condensation, and then thrust instantaneously into the test chamber. Spring loading obviates the use of weights, but it has the disadvantage of allowing some relaxation of the load if the specimen elongates during corrosion. The maximum loss in load found so far was 20 per cent. The air supplied to the test chamber is humidified by passing it through thermo¬statically controlled water. The air is dispersed into fine bubbles by being forced through a porous ceramic filter at the bottom of a tank containing about 10 liters of water. The temperature of the water is controlled independently of the tempera¬ture of the test chamber. Thus, with the

Jan 1, 1945

By P. R. Sahm, T. V. Pruss

Mixtures of fine GaSb and Gds as well as preal-loyed GaSbl,As, powders were hot-pressed at 690°C and 25,000 psi. Dense alloys with compositional gradients of less than 5 pct were obtained from mixtures containing about 20 mol pct GaAs. For x < 0.2, there were increasing compositional gradients, and for x > 0.2 a GaAs-rich second phase appeared in the microstructure. Densification as well as alloying wlechanisms were enhanced by dissociation and, possibly, oxidation reactions of the powders. Densification of coarse prealloyed material, however, primarily depended on plastic flow phenomena and required temperatures just below solidus and pressures of 50,000 psi Thermal and electrical properties were measured. Although in no case was the figure of merit of melt growth materials approached closer than to within 25 pct, the better overall thermoelectric properties were found in coarse-grained, prealloyed materzals which had been compacted to near theoretical density and where grain regrowth had been induced. Similar results are believed to hold in other binary 111-V compound systems if processed under similar conditions. The densification of unalloyed GaSb powders during pressure sintering (= hot pressing) was shown to depend strongly on powder particle size.&apos; Fine powders displayed a "liquid skin effect" that enhanced compaction through the presence of liquid gallium, whereas coarse powders compacted predominantly by plastic flow. The liquid skin effect, in particular, appeared attractive for alloying GaSb with other, higher-melting, III-V compounds, and to densify these in a one-step operation. This is of special interest in the case of III-V compound alloys as the conventional techniques of melt growth or long-time annealing of powders2 is very time-consuming, especially in cases where a large separation of liquidus and solidus can be expected, such as in GaSbl alloys.2 It was felt that experimentation with this system, a particularly unfavorable example, would allow us to extrapolate to several other, more favorable, cases. Uses of Ill-V alloys are most evident in thermoelectric energy conversion devices.&apos; For this reason certain thermal and electrical properties were measured and compared to those of melt-grown material and to hot-pressed prealloyed powders. EXPERIMENTAL PROCEDURE The pressure-sintering apparatus has been previously described.&apos; Using this equipment, both powder mixtures of GaSb with GaAs and prealloyed GaSbl-,As, powders were hot-pressed. The mixtures were pre- pared from cast GaSb and melt-grown GaAs. The prealloyed material was obtained from stoichiometric melts, initially heated to 1200°C in an evacuated quartz ampoule, and then annealed in the solidus-liquidus interval. A typical annealing cycle consisted of a heating to 850°C (1 hr), extended successive annealing at 750°C (65 hr), and slow stepwise cooling (25 hr) to below solidus. The GaSb, GaAs, and GaSbl-,As, materials were ground in a vibrational mill to particle sizes below 500 . A jet mill reduced these further where necessary. Fine powders were analyzed by Coulter counting for their size distribution. Average sizes by volume were calculated from the data. Mixing of the powders, where necessary, was carried out through rapid vibrational motion. The hot-pressing operation consisted of a degassing period of 15 hr, in most cases at 690°C, followed by several hours of compression, normally 25,000 psi at 690°C for powder mixtures and 50,000 psi at 710°C for prealloyed powders. The chemical compositions were confirmed by X-ray fluorescence analysis. To estimate the degree of solid solution achieved, lattice parameters were determined and interpreted according to Vegard&apos;s rule. In addition, optical microscopy helped to correlate the relative amounts of the phases present as well as the degree of porosity to the measured density. To reveal grain boundaries, polished surfaces were etched4 with H 2 O:H 2 O:HCl = 2:l:l. In several cases microscopic concentration gradients were monitored by electron-probe analysis-. RESULTS AND DISCUSSION Alloying and Densification of GaSn-GaAs Powder Mixtures. After preliminary experiments showed that no appreciable alloying took place in mixtures of coarse GaSb (22.5 p) and fine GaAs (2.5 p) powders, hot pressing of mixtures was confined to fine powders only (3.1 and 2.4 p, respectively). Alloying and densification apparently occurred simultaneously with a grain regrowth mechanism which depended on the presence of a liquid phase.&apos; The liquid phase was provided by the dissociation of GasbS particles into liquid gallium and antimony above 555°C. This not only enhanced grain regrowth and densification, as in unalloyed GaSb,&apos; but took on additional importance here for the alloying process. Alloying was speeded up by the resulting liquid-solid interaction as compared to the very slow solid-state diffusion process normally expected at these temperatures.&apos; The results obtained with a series of powder mixtures have been compiled in Table I. It is seen that for mixtures with less than 20 mol pct GaAs, x < 0.2, the compositional ranges increased and for x > 0.2 a GaAs-rich phase and free antimony appeared in the microstructure in sizable amounts.

Jan 1, 1968

THE paper on "Specific Efficiency of the Blast Furnace" by Richard Franchot, which was pub-lished in the September issue of MINING AND METALLURGY, was presented for discussion at the Pitts-burgh meeting. The session opened with a discussion among S. P. Kinney, Mr. Franchot, and J. N. Reese as to the methods and results in sampling for cyanides in the blast furnace. This is covered in detail in writ-ten discussion below. T. T. Read objected to the use of the term specific efficiency as likely to be confusing. The blast furnace has to perform the function of reducing Fe, 03 to Fe as well as that of fusing the metal and, since the reduc-tion of Fe, 0? involves a CO equilibrium, it seems mis-leading to calculate efficiency on the basis of burning the , all carbon to CO? since it is not possible. Mr. Franchot replied that he used the term in the sense defined by Richards in his "Metallurgical Calculations;" but a subsequent search failed to reveal the term in Richards, who says (page 245, 1st edition): The practical conclusion is that a blast furnace generates in itself not much over 40 per cent of the calorific power of the fuel used, and rejects nearly 60 per cent; by using part of the waste gases to heat the blast, however, some of this rejected heat, to an amount representing net 5 to 10 per cent of the calorific power of the fuel used, is returned to and injected bodily into the furnace, thus rendering available for the purpose of running the furnace about 50 per cent of the calorific power of the fuel as a maximum. The efficiency with which the furnace applies this 50 per cent usefully to the objects of the reducing and smelting is another question for investigation.

Jan 2, 1927

By Clyde E. Williams

DESPITE the confusion resulting from the depression and the beginnings of recovery, important progress in all branches of iron and steel metallurgy has been accomplished during the year 1933. Research work has been intensive and highly technical, with increasing attention paid to fundamentals. Plant application of research developments has been rapid. Highly specialized laboratory methods were used for the study of iron-ore concentration methods. More attention has been given by the blast-furnace operator to the sizing of ore and the elimination of fines from the charge by the use of sinter. Combustion in the open-hearth has been placed under better control and the insulation of open-hearth furnaces has spread rapidly, with resultant higher fuel efficiency and better control of the melting and refining operations. Control of iron oxide content in the slag and the determination of iron oxide and other inclusions in steel received great attention during the year.

Jan 1, 1934

By R. I. Jaffee, J. G. Dunleavy, W. Hodge, H. R. Ogden

IN a search for an improved conductor for use in field wire for the L. S. Army Signal Corps, an alloy of copper and silver was developed from which it was possible to obtain 29 B & S ga. strands with tensile strengths in excess of 160,000 psi combined with an electrical conductivity of over 70 pct IACS. Such a favorable combination of strength and electrical conductivity has not been reported previously in the rather extensive literature covering this subject. The properties obtained from various binary alloys of copper and silver, together with the method of fabrication of these alloys which has been developed to obtain the properties desired in fine wire strands, are discussed in this paper. LITERATURE The effect on the electrical conductivity of copper of the various elements in solid solution is shown in Fig I, taken from published data by J. O. Linde and others.&apos; It will be noted that silver in solid solution depresses the electrical conductivity to a lesser extent than any other element for which data are given, and is followed rather closely by cadmium, and then by chromium. Zinc, which lies between cadmium and chromium, has so high a solid solubility in copper that the data for zinc are scarcely comparable to the data for the other two in the range covered. Not many data are available on the strain hardening of copper-rich Cu-Ag alloys. Corson2 reports a 3 pct Ag alloy properly cold worked and annealed to have 100,000 psi tensile strength and 90 pct IACS conductivity. On straight cold working, Hessenbruch3 reports 101.000 psi for a 5 pct Ag, 0.3 pct Be alloy, and 129,000 psi for a 30 pct Ag, 0.5 pct Be alloy. Here it would he expected that much of the strain hardening came from the silver content of the alloys. The copper-rich side of the Cu-Ag diagram, according to Stockdale,4 is shown in the upper part of Fig 2. The electrical conductivities for copper-silver alloys annealed at 750 and 350°C, taken from the work of Johansson and Linde,5 are shown in the lower part of Fig 2. The sloping line corresponds to the conductivity of solid solutions of silver in copper, and the horizontal offshoots correspond to the conductivity of the two-phase alloys in equilibrium at the two temperatures shown. The electrical conductivities are very high, even for the 750°C anneal. The potentiality for age hardening from supersaturated alpha copper solutions appears to be excellent from the solubility line, but Smith and Lindlief6 have shown that the response to age hardening of solution-annealed alpha alloys is not good. They found that the tensile strength of a 5 pct Ag alloy aged at various temperatures was not as great as in the quenched condition, even though, anomalously, the hardness increased from RB68 to RB78 by annealing for 4 hr at 400°C after a 750°C quench. Weist7 also found that the alloys increased in hardness

Jan 1, 1948

By AIME AIME

MEXICO embraces one of the great metal and petroleum producing provinces of the world. In this respect its history dates back to the overthrow of the Aztec empire by a Spanish force under Hernando Cortes between 1519 and 1.521. Even before then, its richness in silver and other minerals was not unknown. But it was a treasure house for the Spanish conquerors until the country became independent in 1821. It has been computed that in the 400 years following 1521, Mexico yielded 1.55,000 metric tons of silver, worth $3,000,000,000, two-thirds of the entire world production. In 1935 the country accounted for 36 per cent of the world&apos;s silver output, 14 per cent of its antimony (in 1934), 13 per cent of its lead, 3 per cent of its zinc and copper, and 21/2 per cent of its petroleum. Contrary to the impression of some, its gold output is now comparatively small, though important in the past. Its oil, as well, formerly hulked much larger than now, in 1921 being one-fourth of the world output.

Jan 1, 1936

By R. D. Reiswig, J. M. Dickinson

The 0s-Ir equilibrium diagram was determined. The diagram is of the simple peritectic type, with a peritectic temperature of about 2660°C. The solid miscibility gap is narrower than previously reported, the nearly vertical solvus lines occurring at about 42 and 63 wt pct 0s. Widmanstaetten figures resembling martensite in some of the two-phase alloys account for a previously suspected transformation. In view of the long history of use of such alloys, it is surprising that the 0s-Ir equilibrium diagram has not yet been completely determined. The boundaries of the miscibility gap in this system have been estimated to be between 24 and 39 wt pct 0s and 79 and 100 wt pct OS. It has been predicted3 that alloys of ruthenium, osmium, and rhenium with the fcc platinum metals should solidify peritectically in their two-phase regions. The metallographic examination of natural osmiridium alloys has been said4 to indicate, by the presence of a martensitic structure, the existence of a transformation or a phase separation. On the basis of superconducting transition temperature measurements, a 70 at. pct 0s alloy was found5 to be two-phase prior to annealing. EXPERIMENTAL The elemental components used in this work were obtained from several suppliers as sponge. The purities, stated by each supplier to be in excess of 99.8 pct, were confirmed in each case by a semiquantitative spectrographic analysis. The pure components were premelted in an inert-gas tungsten arc furnace with the evolution of some fume, crushed, and pickled for use as alloy melting stock. Upon arc melting to the final compositions, no fume evolution was observed. Because weight losses of the order of 15 mg or less were observed in preparing alloy buttons weighing 15 g, "synthetic analyses" were used in determining the compositions of the alloys. Alloys used in this investigation contained 15, 20, 33, 40, 42, 43, 45, 50, 55, 60, 63, 64, 66, 70, 79, and 80 wt pct 0s. Heat treatments of the alloy buttons and pieces thereof were performed in a previously described6 tungsten tube furnace under pressures of 105 torr or less. It was found that homogenization treatments on the specimens were essential to remove the severe coring which was present, a 3-hr treatment above 2300°C removing all the metallographi-cally visible evidence of coring. Following the various heat treatments, the specimens were "vacuum-quenched" by melting a tungsten fuse wire and allowing them to drop onto a water-cooled copper plate. In a few instances, specimens were quenched into molten tin for comparison, but no difference was apparent. Vacuum-quenched specimens cooled from 2400°C to below a red heat in less than 60 sec. Typical equilibration times varied from 3 hr above 2300°C to 88 hr near 1100°C. The utilization of successively longer equilibration times and the approach to equilibrium from both directions indicated that the times used were sufficient to give a close approach to true equilibrium. Heat-treatment temperatures were measured with a calibrated Leeds and Northrup optical pyrometer through a 0.120-in. lateral sight hole in the tungsten heater tube. It was known that the assumption of black-body conditions inside the 1-in.-diam by 10-in.-long tube was unwarranted. The empirical results of work with thermocouples and melting

Jan 1, 1964

Secondary minerals are the result of a process of concentration and enrichment and are commonly richer than the primary minerals of the same deposit. Secondary ores that contain abundant sulphides are commonly distinguishable in the field from primary ores; this distinction is more difficult with ores that carry a small quantity only of sulphide minerals, and microscopical examination of the ore in thin section is advisable in all doubtful cases. It is frequently difficult, and in some cases impossible, to determine the primary or secondary character of quartzose gold ores. The safest guide is the presence or absence of gaseous or fluid inclusions in association with the ore minerals; such primary association coupled with a lack of traces of oxidation is indicative of primary origin. Any ore that carries traces of oxidation, such as iron stains, endritic oxides of manganese, kaolin and so forth must be considered to have been acted upon by surface agencies, and secondary enrichment must be suspected. Further examination, however, may indicate that the contained value is primary, and, therefore, persistent in its vertical distribution. The manner of occurrence of secondary minerals is frequently characteristic; secondary minerals, being due to the action of surface waters, are commonly found in cracks through earlier minerals, or as crusts lining vugs or surrounding nucleal masses, or in general, in some distribution later than and not conforming to the arrangement of the primary minerals. Secondary sulphides are often found as soft black pulverulent masses or coatings, although they frequently occur well crystallized or as

Jan 1, 1932

Sec. 1. This Division shall be known as the Institute of Metals Division of the American Institute of Mining and Metallurgical Engineers. Sec. 2. The object of the Division shall be to furnish a medium of cooperation between those interested in the metallurgy, fabrication and uses of the nonferrous metals and their alloys; to represent the A. I. M. E. in so far as nonferrous metallurgy is concerned, within the rights given in A. I. M. E. By-law XI., Sec. 1, and not inconsistent with the Constitution and By-laws of the A. I. M. E.; to hold meetings for social intercourse and the discussion of nonferrous metallurgy; to stimulate the writing, presentation and discussion of papers of high quality on nonferrous metallurgy; to reject or accept such papers for presentation before meetings of the Division. Article II—MembeRs Sec. 1. Any Member, Associate, or Junior Associate of the A. I. M. E. in good standing may become a Member, Associate or Junior Associate of this Division upon registering in writing a desire so to do, but without additional dues. Sec. 2. But no one who has been continuously indebted to the A. I. M. E. or to this Division for more than three months shall be entitled to vote or to receive publications to which, as a member of the Division, he would be entitled. Article III—Funds Sec. 1. The expenditure of the funds reccived by the Division shall be authorized by the Executive Committee of the Division. Article IV—Meetings Sec. 1. The Division shall meet at the same time and place as the annual meeting of the A. I. M. E., and at such other times and places as may be determined by the Executive Committee subject to the approval of the Board of Directors of the A. I. M. E. Sec. 2. The annual business meeting for election of officers shall be held within a few days before or after the annual business meeting of the A. I. M. E. Sec. 3. At any meeting of the Division for which notice has been sent to the members of the Division through the regular mail at least one month in advance, a business meeting may be convened by order of the Executive Committee, and any routine business transacted not inconsistent with these By-laws or with the Constitution or By-laws of the A. I. M. E. Sec. 4. For the transaction of business, the presence of a quorum of not less than 25 members of the Division shall be necessary. Article V—Officers and Government Sec. 1. The officers of the Division shall consist of a Chairman, two Vice-chairInen, Secretary and Treasurer. The office of Secretary and Treasurer may be combined in one person, if desired by the Executive Committee. Sec. 2. The government of the affairs of the Division shall rest in an Executive Committee, in so far as is consistent with the By-laws of the Division and the Constitution and By-laws of the A. I. M. E. Institute of Metals Divisiori

Jan 1, 1931

By R. Schuhmann Jr., P. J. Ensio

As a first step in a study of the physical chemistry of copper-smelting slags, experimental measurements were made of the oxygen pressure of simple iron-silicate slags in equilibrium with solid iron. The experiments consisted in bubbling CO2-CO mixtures through the slags in iron crucibles and in finding the equilibrium ratios of CO2 to CO. From the data, activities and partial molal heats of solution FeO and SiO2 in the slags were calculated. THE ternary system FeO-Fe,O,-SiO, is the simplest system which can represent adequately the important chemical properties of the slags formed in matte smelting and converting. Accordingly, the experimental study of slags in this system was started as the first step in a general research program on the thermodynamics of copper smelting. A recent paper by one of the authors&apos; outlines this general research program and shows in some detail how information on thermodynamic properties of iron-silicate slags, especially information on oxygen activities, is essential to a full understanding of the chemistry of copper smelting. The FeO-Fe,O,-SiO, system also is the basis of slags produced in other processes, such as acid steelmak-ing processes, and is important in relation to the behavior of silicious refractories. In addition, data on the physicochemical properties of iron-silicate slags should contribute to a general understanding of the nature of slags, since at present such data for all kinds of slags are relatively meager. The principal quantitative information already available on iron-silicate slags consists in Bowen and Schairer&apos;s constitution diagram for slags in equilibrium with metallic iron,&apos; Darken and Gurry&apos;s complete and precise thermodynamic study of the Fe-0 system,",&apos; and Darken&apos;s study of the phase equilibria in the Fe-Si-o system. From the results of this previous work, it was clear that a complete thermodynamic study of ternary iron-silicate melts was a major undertaking which would have to be broken down into parts, including the working out of the ternary equilibrium diagram as well as extensive activity measurements on slags. The experimental measurement of oxygen activity, using CO-CO, and other gas mixtures as yardsticks of oxygen activity, was the basis of Darken and Gurry&apos;s study of the Fe-0 system. From the experimental measurements of oxygen activities over a large range of temperatures and compositions, they were able to calculate the activities of other species such as Fe, FeO, Fe,O,, etc., and also the other important thermodynamic properties in the Fe-0 system. At the start of the present investigation, it appeared that the same approach would be fruitful for the study of iron-silicate melts. Also, the experimental measurement of oxygen activities seemed particularly attractive because oxygen activity itself is a quantitative measure of oxidizing or reducing power, which is an important variable in copper-smelting slags. The slag compositions in equilibrium with yFe appeared most suitable for the first investigation of this kind, for the following reasons: 1—Good constitution data2 were available. 2—An iron crucible could be used, thus affording a simple solution to the refractory problem without introducing contarnination. 3—With Fe activity fixed, at unity with respect to a standard state of solid Fe, measurements of 0 activity could be followed by simple calculations of activities of FeO and other Fe-0 complexes and of SiO,. 4—This starting point afforded several possibilities for cross-checking with previous work,

Jan 1, 1952