By L. F. Mondolfo, B. E. Sundquist

The crystallographic orientation relationships resulting when lead is nucleated from the liquid by Ni, Cu, Ag, and Ge were determined. For each nucleating agent several definite orientatioz relationships were found. These relationships seemed to be controlled by good symmetry relations and low crystallographic disregistry between mating planes. For any given nucleating agent the under colling for nucleation was found fairly constant and independent of the orientation relationship and consequent disregistry. It was also found that, upon re melting and refreezing the Pb, the orientation relationship was changed. These findings prove that crystallographic disregistry is not the controlling factor in heterogeneous nucleation from the liquid. The results of this investigation tend to confirm the theory presented in a preceding paper that heterogeneous nucleation starts with the formation of an adsorbed layer of nucleated metal on the nucleat-ing impurity. Evidence is given that cavities in the nucleating agent act as centers of nucleation. IT has long been known' that solid extraneous particles are active in catalyzing phase transformations that occur in a system, particularly condensation and crystallization. It is well established that these heterogeneities act as catalysts by providing surfaces upon which nuclei of the precipitating phase can form with activation energies smaller than those required for homogeneous nucleation. Numerous investigations have shown that in this process of heterogeneous nucleation: a) the nucleus forms with one, or several, definite crystallographic orientation relationships with the nucleating phase2-4 and b) that there is a small range of undercoolings or super saturations characteristic of the nucleation of a given solid on a given Substrate.5-10 Turnbull and vonnegut11 have developed a theory based on theories developed by Volmer12 and Turn-bull and Fisher1= for heterogeneous nucleation from gases and liquids, that relates the super saturation or undercooling required for nucleation to the dis-registry between the lattices of the nucleus and the nucleating agent. This theory predicts that nucleation should occur with the orientation relationship between the nucleus and nucleating agent that minimizes the disregistry. Further, it predicts that the undercooling or super saturation necessary for nucleation should be a function of the disregistry. Numerous investigations have dealt with the orientation relationships resulting from the condensation of vapors onto crystalline solid substrates2,3 and a few with the nucleation of one phase by a second phase in solidification4,14. Others have dealt with the supersaturation8-10 and undercooling5-7 associated with nucleation in condensation and solidification respectively. However, there is virtually no report that gives both of these factors for the same system. In this investigation a study was made of the undercoolings and orientation relationships resulting when Pb is nucleated from the liquid by Ni, Cu, Ag, and Ge. It was the purpose of this investigation to check the Turnbull-Vonnegut theory, i.e., the importance of crystallographic disregistry between nucleating catalyst and nucleated metal. The results indicate that disregistry is not an important factor in nucleation and that the nucleation process is probably somewhat more complex than current theories suggest. EXPERMENTAL PROCEDURE Small single crystals of nickel, copper, silver, and germanium were prepared from materials of four to five nines purity, and the Pb used was also 99.999+ pet pure. Cu and Ag single crystals were prepared by sealing small chips of Cu or Ag in an evacuated quartz capsule and heating the capsule at 2000°F for 1 hr before cooling. Nickel crystals of 200 diam were also prepared in evacuated quartz capsules, but melting was done by heating the capsules in an oxy-acetylene flame for a few minutes. These spheres were invariably polycrystalline so

Jan 1, 1962

By J. J. Kanter

The choice of a nonferrous metal or alloy for a given Application is frequently predicated upon a consideration of properties other than merely the capacity to withstand stress. When ability to withstand stress is the dominant engineering requisite of the material to be used, economic considerations seldom lead to the choice of nonferrous metals and alloys. In most instances where a nonferrous metal is used it is because of some special quality of either corrosion resistance, electrical properties, thermal properties, antifriction, or fabrication advantage that commends its application. The mechanical properties, as a rule, present an incidental engineering consideration entirely secondary to the special quality deciding its use. Indeed, great ingenuity has often been exhibited by engineers and metallurgists in overcoming the mechanical shortcomings of a nonferrous base material. in order to take advantage of some outstanding property. . With this thought in mind, we might better appreciate some of the problems in stress design. encountered with nonferrous metals and alloys pertinent to a symposium on their creep characteristics. Our considerations must necessarily be far from complete because of the broad range of materials in the nonferrous category for which creep properties assume a technical interest. Creep deformation of these metals can be subject for study at temperatures ranging from ambient to incandescent, depending upon which one is under consideration. Whereas the steel metallurgist thinks of creep as an essentially high-temperature engineering consideration, the same is not necessarily true in the field at hand. The diversity of the creep problems in the nonferrous field is perhaps accountable to some extent for its virginity as a symposium subject. Each research has necessarily been sponsored by some organization or group interested either in promoting the use of a certain nonferrous base or in obtaining data toward the solution of a mechanical difficulty encountered in applying a material indispensable for its special attributes. Perhaps as many techniques of creep testing have been used as there are base metals implied under "nonferrous." Some of the creep problems that have occasioned researches are associated with steam-pressure vessels such as tubes, drums, castings, and forgings of copper-base and nickel-base alloys, cable sheathings of lead and lead-base alloys, electrical transmission lines of copper and aluminum, engine parts die-cast from alloys based on zinc, aluminum, copper— soldered and brazed joints-—as well as numerous duties at extremely high temperatures met with alloys based on cobalt, nickel, tungsten, molybdenum, platinum, and other precious or semiprecious metals. Postwar technology will have the benefit of much creep research on nonferrous metals, which for reasons of security cannot be discussed on this occasion. Suitability OF Metals As already intimated, the bulk of the constructional metal that ordinarily is

Jan 1, 1945

Executive ARTHUR S DWIGHT, Chairman B THAYER CHARLES F RAND P MATHEWSON J V W REYNDERS Membership WILLIAM H BASSETT, Chairman W Y WESTERVELT Vice-chairman P MATHEWSON H G MOULTON F T RUBIDGE Finance WALTER H ALDRIDGE, Chairman GEORGE D BARRON GALEN H CLEVENGER

Jan 1, 1923

By Peter N. Calder, G. H. Blackwell

The development of an open pit slope monitoring system, from equipment selection and justification to complete computer data storage and analysts, Is described. Methods of overcoming the Limitations of the electronic transit/distance measuring device and survey system selected are discussed. Results of the monitoring program showed that blasting was a major cause of Instability, and, after much experimentation, suitable blast patterns for mine production and pit wall integrity were designed. The experiences gained with double benching 'and wall cleanup procedures are discussed . The monitoring program also indicated that water was a contributor to instability, and methods of dealing with water In a rock with a low storage coefficient and transmissibility are described. Because of the danger of falling rock, photogrammetric methods are used for joint mapping and analysis, this work being contracted out. Joint strengths are measured on-site using a portable shear tester. Finally, a discussion of a complex failure is given.

Jan 1, 1983

By R. S. Rickard, H. D. Peterson, J. D. Miller, M. C. Fuerstenan

Pure chrysocolla is floated with chelating agents that form insoluble complexes with copper at ambient temperature. Complete flotation is obtained with potassium octyl hydroxamate as collector at pH 6. Flotation response is enhanced with increased temperature when low additions of hydroxamate are involved. A natural ore was floated with 0.4 1b per ton octyl hydroxamate at pH 6.5 and 58°C, and a flotation recovery of 76% was obtained with a concentrate grade of 31.6% copper. The flotation characteristics of the oxide copper minerals, malachite, azurite, and cuprite, have not presented the difficulty for concentration as have those of the copper silicate, chrysocolla. The copper carbonates and oxides respond reasonably well to flotation with conventional collectors, whereas chrysocolla will not respond to flotation with fatty acids or xanthates under normal flotation conditions. In this view then, other reagents will have to be devised to function as collectors for chrysocolla. The most obvious general class of reagents for this purpose would seem to be the organic copper chelating compounds. The utility of chelating agents as collectors in flotation systems has already been demonstrated. For example Vivian1 has floated cassiterite using ammonium nitrosophenylhydroxylamine. Holman2 studied the flotation of nickel oxide ores with dimethylglyoxime and also suggested the use of taurine on oxidized lead ores. A rather detailed study on the application of certain chelating agents to some flotation systems was presented by Gutzeit.3 This work indicated that the formation of surface insoluble chelates is probably responsible for flotation in many cases. The role that soluble chelating agents assume was also presented, that is with effective removal of polyvalent cations by complex formation, effective depression of quartz can be obtained. DeWitt and Batchelder4,5 have shown that oximes function well as collectors for chalcocite, malachite, azurite, and cuprite. Ludt and DeWitt6 have presented the possibility of using dyes, such as octyl malachite green, as a collector for chrysocolla. These works presented by DeWitt et al suggest that organic copper chelating compounds offer considerable promise for concentrating chrysocolla, but that the most suitable chelating reagent from the standpoint of cost and flotation response has yet to be determined. The present investigation was undertaken to study the flotation response of chrysocolla to selected copper chelating compounds, that is ethylenediamine, hexamethylenetetramine, potassium octyl hydroxamate, dimethylglyoxime, and benzoin a-oxime. EXPERIMENTAL MATERIALS Chrysocolla: The chrysocolla used in the microflo-tation studies was from New Mexico and analyzed 20.8% copper. X-ray diffraction showed this material to be amorphous in character, but some faint lines of quartz were noted. A natural oxide copper ore from Utah was also used in the investigation. This ore contains malachite principally but also contains chrysocolla and tenorite together with some sulfide copper. The sulfide copper comprises from 15 to 20% of the total copper content of the ore. Water: Conductivity water was used in the microflo-tation experiments, while Golden tap water was used in the experiments with the natural ore. Reagents: Reagent grade n-amyl alcohol was used as frother in the experiments with pure mineral, while MIBC was used in the work with the ore. Ethylenediamine, hexamethylenetetramine, dimethylglyoxime and benzoin a-oxime were reagent grade in quality. Pure potassium octyl hydroxamate was prepared as follows: 1) 1.0 mole of KOH in 140 cc of methanol was combined with 0.6 mole of hydroxyl-amine hydrochloride in 240 cc of methanol at 40°C (KC1 precipitates under these conditions and to effect complete removal of KCl, the system was cooled to 10°C and filtered), 2) a light methanol wash was then given the KC1 cake, 3) the filtrate was agitated at room temperature and 0.33 mole of the methyl ester of the organic acid (i.e. methyl octanoate) was

Jan 1, 1965

PAGE Problems of American Railroads Early in 1936, by J. J. Pelley 3 The Heavier Nonferrous Metals in Transportation, by C. H. Mathewson... 9 Light-weight Metals in the Transportation Industry, by Zay Jeffries 21 Trends in the Metallurgy of Low-alloy, High-yield-strength Structural Steels, by H. W. Gillett 40 Structural Steels and Light-weight Metals in the Transportation Industry, by Horace C. Knerr 62 Proposed Use of Alloys in Merchant Shipbuilding, by Edgar P. Trask 66 Mutual Effects of Metallurgy and Speed in the Automotive Industry, by Merrill C. Horine 84 The Railroads and Light-weight Equipment, by W. W. Colpitts 93

Jan 1, 1936

By W. K. Godfrey

The highest compressive strength cement has the highest bond strength in tests in which the cement is subjected to a confining pressure. After perforating, the bond strength is reduced to nearly zero when the pipe is supported by weak cement. Perforating does not affect the bond strength, however, when the pipe is supported by strong cement. Pipe supported by weak cement is damaged by perforating with expendable capsule jets, but is not damaged by perforating with the hollow carrier gun. High strength cements are recommended for oil wells that are to be perforated. Introduction The purpose of this work is to determine the effect of jet perforating on the bonding strength of oilwell cement at simulated down-hole conditions. Bond strength is a good criterion for determining the effectiveness of cement in performing its main function, i.e., that of isolating zones. According to the literature on the subject, the optimum cement strength for perforating is low and should not exceed 2,000 psi compressive strength. This conclusion was based on the appearance of bullet and jet perforations in neat and gel cements largely done in the absence of a confining pressure more than 15 years ago. Discussion Literature A relatively weak cement has been recommended in the literature as having optimum properties for perforating. In 1947, Oliphant and Farris tested bullet perforating of neat cements at various curing times.' Some of the tests were made at down-hole conditions. They reported that the optimum cement strength for perforating was about 2,000 psi compressive strength. Enlarged holes occurred when strength was too low, and the cement shattered and cracked when the strength was too high. In 1951, Morgan and Dumbauld tested bullet and jet perforating of neat and gel cements at surface conditions.' They reported that optimum cement has a compressive strength less than 2,000 psi. In their tests at atmospheric pressure, high strength cement shattered and cracked when perforated. Thus, the optimum cement strength was based on the appearance of neat and gel cement after perforating. In 1953, Clark showed a relation between cement strength and fluid shutoff.' He concluded that a 500 psi compressive strength is required for good fluid shutoff and that maximum bonding ability is developed at approximately 1,000 psi compressive strength. In 1964, Bell and Shore invalidated most of the conclu sions by the previous authors when they demonstrated that atmospheric pressure tests cannot be used to determine casing deformation and damage that will result from perforating under down-hole conditions.' They showed that the higher the hydrostatic pressure, the more restricted will be the expansion of gases generated by the charge. Less casing deformation and damage occurs under down-hole conditions than at atmospheric pressure. In recent work, Bearden et al. reported that jet perforating at surface pressure with the hollow carrier gun caused the cement sheath to shatter and crack.' The perforating, however, did not seriously affect the pressure required to leak past the casing cement bond. Only three cementing mixtures were tested, and presumably they had strengths in excess of 2.000 psi. Bearden et al. also reported that the hydraulic bonding strength increased as the compressive strength increased. Their hydraulic test showed that approximately 1,000 psi pressure is sufficient to break the casing cement bond for a well aged neat Portland cement sheath. Unfortunately, the tests were not run with a confining pressure, so Bearden et al. were merely measuring the strength of their outer 8%-in. casing. In our investigation, we measured the hydraulic bond strength of cement to pipe under a confining pressure and found that the bond strength was not limited to 1,000 psi. Cement Bond The bond strength is a good criterion for measuring the effectiveness of cement in performing its main function, that of preventing interzonal communication of fluids behind the casing. Measuring bond strength after perforating should be a good quantitative method of determining optimum cement properties, and should be a better method than that used by previous investigators,11 ' who simply observed the appearance of the cement after perforating.

Jan 1, 1969

By M. R. Louthan, C. L. Angerman

In polycrystalline Zircaloy-2 the orientation of zirconium hydride precipitates is influenced by an applied stress during hydride precipitation; hydride platelets are oriented nearly parallel to a compres-sive stress and perpendicular to a tensile tress. 1,2 A similar effect has been observed in the Ti-H system, where precipitation of the low-density hydride platelets occurred on habit planes made energetically favorable by the application of stress. 3 Recently, stress activation of hydride habit planes in zirconium and Zircaloy-4 was also demonstrated. The hydrides precipitated on {101l), {112l} and (2131) planes in both zirconium and Zircaloy-4; however, no platelets were found near the prism-plane positions in the Zircaloy-4 samples. Investigations at the Savannah River Laboratory, using polycrystalline Zirc_aloy-2 samples, have confirmed the (101l) and (1121) habit planes but also showed that the prism planes were active hydride habit planes. Using single-surface stereographic analysis and back-reflection Laue techniques, most of the previously reported habit planes for a zirconium were observed.4"1 and one additional plane, the (1013) plane, was noted, Table I. All the habit planes observed had the form (101l) or { 112l) indicating that these planes are the habit planes for hydride precipitation in poly-crystalline Zircaloy-2. The specimens used in these studies were cut from large-grained weld areas of seam-welded tubing and were hydrided in either a static steam autoclave at 400°C and 1500 psig or in a modified Sieverts apparatus at 400°C.

Jan 1, 1967

By Lawrence P. Bonicatto

The steel industry's increased demand for higher grade pellets has caused the pellet producers to investigate methods of upgrading their product and the Hanna Mining Co.'s Groveland plant on the Upper Peninsula of Michigan is no exception. The low grade iron deposit is a complex mixture of magnetite and hematite with chert, quartz, jasper and various iron silicates.1 Beneficiation is by Humphrey spirals and anionic flotation of the iron minerals.2 Flotation of the spiral tailings makes up about 75% of the concentrate, while a minor amount of concentrate (less than 3%) is produced in magnetic circuits. The concentrate is pelletized at the rate of 1.6 million tpy. The initial concentrating facilities were constructed in 1958 and the concentrate was marketed as sinter feed until a pelletizing plant was added early in 1963. Grade improvement soon became a high priority research project, and several methods of concentration were investigated.

Jan 3, 1968

By W. O. Philbrook, H. W. Hosking, N. B. Melcher

A simple and inexpensive mercury-tracer method has been develohed to study rates and Patterns of gas flow in blast furnaces. A Pulse of mercury is injected into the hot blast, and its arrival at the sampling Point is recorded by an electronic circuit that measures resonant absorbtion of ultraviolet light by mercury vapor in the gas aspirated .through the detecting. cell. A rapidly developing interest in blast-furnace technology in recent years has created a strong demand for precise knowledge of the rates and patterns of gas movement through the stock column. Classical fluid-flow theory cannot supply the desired information because the complexity of the blast-furnace situation precludes the accurate determination of many of the parameters required for solution of the equations. In fact some of the terms employed in fluid-flow treatments become almost meaningless under blast-furnace conditions. The void fraction of the stock column, for example, varies widely from place to place and is affected by the segregation of charge materials, attrition of lumps during descent, and channeling. Gas density varies with changes in local pressure, temperature, and composition, while viscosity varies with temperature and composition. Even if mean values for these functions were acceptable, they would be either impossible or extremely difficult to determine with a high degree of accuracy since the value of the mean for all gas properties would depend upon the flow distribution itself. Attempts to study gas movement by the pitot-tube determination of kinetic pressures have met with little acceptance. Reproducibility of results is extremely difficult to achieve in a situation where alignment of the tube orifice with respect to the flow direction in tortuous channels cannot be guaranteed. Because of these difficulties it would appear that progress can be achieved only with a direct method of measuring gas velocities and determining the shape of flow paths through the stock. The establishment of such a method is described in this paper. SELECTION OF METHOD Direct measurement suggests the use of a tracer by means of which the progress of a "parcel" of gas can be followed through the furnace. Several requirements must be met before any selected material can be considered a suitable tracer. First of all, it must be a substance not normally present in blastfurnace gas or dust; otherwise its presence in a gas sample will have little significance. It should be volatile at temperatures normally existing within the furnace, to ensure that it will travel with the gas, as a gas. It should possess special properties enabling its presence in the gas to be detected readily, and it should not undergo exchange reactions with any material normally present within the furnace, including refractories and coke as well as all components of the metal and slag. Radioactive materials naturally are considered because their radioactivity renders them susceptible to detection. However, of the many radioactive materials available, almost all are eliminated from final consideration by their unsuitability in terms of other properties. Radioactive silicon, carbon, calcium, phosphorus, and many others have been considered and discarded, either because they are not volatile over the whole range of significant temperatures, or because they could be expected to undergo exchange reactions with burden or refractory materials. Others which might be suitable in terms of these properties are eliminated because of a low activity, short half life, or the necessity for fragile counting apparatus. Of the many elements available in radioactive form, perhaps radon is the only one suitable for blast-furnace gas-flow studies. This has been used in several investigations1-4 with considerable success. The use of radiotracers has certain inherent disadvantages. One is the cost. An appreciable sum must be allowed for materials each time a test is made. Also, special methods of handling must be employed, and very often the progress of an investigation must be governed by the availability of isotopes and the delivery arrangements that can be made for them. An advantage is immediately gained if the tracer material can be a substance which can

Jan 1, 1960

By J. R. Hornaday, A. E. Morris, N. A. Parlee, D. C. Carmichael

Rates of absorption and effusion of hydrogen in solid iron were measurede by a Sieverts type of apparatus. With clean a iron these rates are diffusion controlled down to 420°C and are represented by the equation D = 6.70 x e-'100' crn2 sec-I Certain surface impurities can affect these rates at all temper-atuves. Thin oxide films lower, the apparent diffusivity of annealed iron markedly. Cold-worked iron (75 pct) annealed at 430°C has practically the same solubility and diffusivity as anealed iron. THE mechanism of absorption and evolution of hydrogen in solid iron alloys is not fully understood despite the large number of investigations on the subject. While there appear to be many instances of simple solid-state diffusion control of rate, there are many cases where investigators have either concluded that surface reactions are rate controlling or that some "nondiffusible" hydrogen resides in discontinuities. The purposes of this research were 1) to develop a sound method for studying this absorption and evolution behavior, 2) to examine it in pure annealed iron, and 3) to determine the effects of important variables, such as cold work, surface condition, and composition. This paper relates the progress toward these objectives. Much of the present knowledge of the movement of hydrogen through iron alloys comes from permeability studies which involve the measurement of the rate of passage (under steady state conditions) through membranes of the order of 1 mm in thickness. This method is open to question on various grounds. If surface reactions are involved, two different surfaces operating under two different conditions must be considered. The presence of defects in the membrane even of microscopic dimensions may lead to erroneous results. A few people have studied evolution of hydrogen into vacuum, under carefully controlled (unsteady state) conditions, and some of the best diffusivity data come from these sources. Most of these methods measure rates of evolution only and thus do not make a rigorous test for reversibility of behavior. It appeared that an "unsteady state" method that would permit the measurement of both rates of evolution and absorption under controlled temperature, pressure, and other conditions would offer several advantages. Accordingly the modified Sieverts apparatus described below was designed and built. APPARATUS This apparatus is shown in Fig. 1. The sample bulb is detailed in Fig. 2. Hydrogen of 99.5 pct purity and argon of 99.99 pct purity were used. The hydrogen was deoxidized and dried by means of a Deoxo unit followed by a "Dri-erite" tower. The argon was only dried. The gas burette was graduated in tenths of a cubic centimeter, and, with the aid of a travelling magnifier, readings could be estimated to the nearest 0.01 cc. The level of mercury in the burette was adjusted by means of a leveling bulb operated by a fine screw adjustment. An electrical system, consisting of two slightly separated platinum electrodes inserted in one leg of the manometer and a small light bulb was used to obtain rapid accurate adjustment of the pressure. The capillary tubing of the Vycor sample bulb was 3 mm bore as was all tubing back to the gas burette. The samples were discs made from vacuum-melted Ferrovac-E iron of greater than

Jan 1, 1961

By J. R. Cain

In every process for making steel there are one or more stages where the metal is exposed to gas of one kind or another. Thus, in the open-hearth furnace, the carbon dioxide and water vapor in the products of combustion are oxidizing toward the ferrous and manganous oxides in the slag, tending to convert these to higher oxides; the higher oxides then , oxidize the steel, so that indirectly the products of combustion are oxidizing toward the steel. In the Bessemer process, there is direct contact of air and steel; also, the water vapor in the air blown into the converter is continually decomposed by the molten steel, yielding hydrogen and ferrous oxide, both of which are in part taken up by the metal. In the electric-furnace processes, there is always more or less air in contact with the slag covering the metal, and this air and the gaseous reaction products from it are dissolved in the slag to some extent and thus transmitted in part to the steel. In the crucible processes, there is always entrapped air in the charges and the crucibles are more or less permeable to the gaseous products of combustion from the furnace. In all the processes of manufacture, the molten metal is exposed to air while tapping into ladles and ingot molds and has an opportunity to saturate itself with air or with gaseous or solid products generated by chemical reactions between air and steel. Sievertsl has shown that molten metals requirc but a few seconds to saturate themselves with a surrounding gas. No one familiar with the operations at a steel plant needs to be reminded of the important role that gases play at all stages. The familiar "boil" of open-hearth furnaces, due to evolution of carbon monoxide when iron ore is added to the molten steel; the spectacular operation of the Bessemer converter brought about entirely by a gaseous reagent; the almost magic effect of small quantities of silicon, manganese, or aluminum added to the molten metal in ladle or furnace in quickly preventing bubbling and evolution of gases; the unwelcome phenomena of blowholes in ingots that have not been properly manufactured—these

Jan 1, 1920

THE discussion of this topic at the Open-hearth Conference at Detroit on Nov. 3, 1927, was opened by statements of the general principles involved, made by manufacturers of molds. Because of their general interest they are printed below. WILLIAM HAIL RAMAGE,* Hubbard, Ohio.-I did not come prepared to read a paper, thinking. the most I would be called upon to do would be to make a few, remarks by way of discussion. A number of our friends have pre-viously asked questions. similar to this which really does not permit a direct "yes" or "no" answer. If I may he pardoned for so doing, I believe it advisable to discuss rather what we consider the principal factors which in-fluence mold life. I think possibly a little undue weight has been given to the subject of the analysis of the metal. For the last eight years we have spent a lot of time, effort, and money investigating this very problem from a chemical, physical and microscopic standpoint. We have had the benefit of complete records and history of over 100,000 molds in service at a variety of plants and over long periods of time. Obviously, I cannot be so specific that I should divulge information that is really a trade secret. In our opinion the principal factors influencing mold life are: (1) design of the mold; (2) process of manu-facture, including workmanship; (3) care in the steel plant or what might be termed "the use or abuse" in the steel plant; (4) the analysis of the iron and the physical con-dition of it. Under normal conditions these factors are of importance in the order named, although in specific cases they might be rearranged in any order you choose. For instance, the best mold made can be destroyed in one or two pours by subjecting it to certain conditions which are occasion-ally met in steel plant practice. Obviously, in that case, nothing else matters but that one item. On the other hand, I have seen molds made of such a terrible design that it was a foregone conclusion it would have to be broken after the second pour of the ingot to get it out. In that case, nothing but design mattered. As to the effect of process of manufacture, let me cite a case. Some years ago there were two batches of molds sent to a certain company. They were the same sized molds, used under the same conditions and in the same kind of service. There were, 20 molds in each batch. The second batch sent gave ten times the life of the first batch. It is true that the design was changed a little, but not very much, and it was not. a bad mold to begin with. It is possible that the iron may have been better in the second consignment but not very much. In my opinion, it is con-servative to say that of the 900 per cent improvement in life, 5 per cent was probably due to better iron, 25 per cent to better design and the remaining 870 per cent to process of manufacture and workmanship.

Jan 2, 1928

By J. M. Camp

In conforniity with the design of the oficials of the United States Steel Corporation for the standardization of the methods employed in the sampling and analysis of all materials encountered in their various lines of manufacture, the Chemists' Committee presents this compilatioti of standard methods for the sampling and subsequent analysis of molten pig-iron. In selecting the methods, the Committee employed the same line of procedure as in former cases, viz., the careful consideration of all the methods employed in each laboratory of the Corporation, evolving therefrom the several methods herein described, the immediate adoption of which is desired. The services of Messrs. W. B. N. Hawk, William Brady, and C. H. Rich, a sub-committee appointed for the preparation of the present paper, are gratefully acknowledged. II. Introduction. A quite obvious cause of nonconformity of results of comparative analyses in the various laboratories of the Corporation has been an apparent lack of uniformity of method in the sampling and analysis of molten iron. This condition is particularly apparent with regard to the determination of the sulphur, numerous discrepancies in which would appear t.o indicate the absence of, and the necessity for, some uniform method of procedure. The estimation of the

Jan 1, 1913

By C. H. Mathewson, Kent R. Van Horn

Copper and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.' It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

It is known that stoichiometric NiTi transforms to a structure of lower symmetry near room temperature. The present investigation deals primarily with the changes in the electrical and magnetic properties which occur at the transformation. The effects of composition and various heat treatments on electrical properties are also discussed. In recent investigations by Purdy and Parr,' Wang et a1.,2 Dautovich and Purdy,~ Dautovich et a1.,4 and the authors, ~,' NiTi has been observed to undergo a martensitic phase transformation from the ordered CsCl (B2) structure to one of lower symmetry. The crystal structure of the low-temperature modification is still not completely worked out. This transformation occurs near room temperature for the stoichiometric composition. The thermodynamic, elastic, crystallographic, and microstructural characteristics of this transformation for some compositions have been previously reported.'-= In the present investigation, the changes in the electrical transport properties and magnetic susceptibility of NiTi when it undergoes the martensitic phase transformation have been measured. The approximate composition range covered is 48 to 52 pct Ti.* *All compositions are given in atomic percent._____________________ EXPERIMENTAL PROCEDURES AND RESULTS 1) Sample Preparation. The NiTi alloys were prepared from iodide titanium (>99.92 pct Ti) and vacuum-premelted carbonyl nickel (>99.95 pct Ni) by repeated arc melting under gettered argon and casting in a water-cooled copper mold. After the cast buttons were hot-forged at 800" to 950°C, the oxidized surface was removed by grinding and etching. Samples were cut from the worked polycrystalline buttons. After fabrication, the samples were annealed 1 hr at 900°C and water-quenched. The composition of the alloys was assumed to be the same as in the initial feed. This assumption was supported by material balance checks on 100-g arc-melted buttons which demonstrated quantitative recovery to within k0.02 pct. The oxygen content of the alloys was '150 ppma (weight) and the carbon content was 30 to 50 ppm. 2) Electrical Resistivity and Hall Effect. The electrical resistivity was measured over the composition range 48 to 52 pct Ti for temperatures varying from 4.2"K to 900°C. The high-temperature and many of the low-temperature experiments were carried out using conventional 4-probe dc techniques.7 The Hall coefficient and ac resistivity were measured at 20 cps using the apparatus shown schematically in Fig. 1. The equipment is basically an ac potentiometer: The resistive or Hall voltage of the sample is balanced by a comparison voltage provided by a dividing network across a standard series resistance. The off-balance signal is amplified by a Tektronix 122 amplifier and detected by a Princeton Applied Research (PAR) phase-sensitive detector. The precision of the resistivity and Hall coefficient measurements is i0.1 and i3 pct, respectively. The uncertainty in the data is increased by i2 pct from the precision limits because of uncertainty in dimensions and possible end effects. The temperature dependence of the electrical resistivity and Hall effect for a stoichiometric (50.0 pct Ti) NiTi sample are illustrated in Fig. 2. Above 75"C, this sample has essentially the B2 structure, while below about 0°C it is completely in the low-tempera-

Jan 1, 1968

By E. W. Davis

ABOUT a year ago several carloads of magnetite ore from New York state were sent to the Mines Experiment Station at the University of Minnesota for grinding and concentration tests. The flowsheet used minus ½ -in. ore as feed to a 3 by 3-ft. overflow cylindrical ball mill operating at 37 r.p.m. in closed ciruit with a vibrating screen. The screen oversize was returned to the mill for further grinding and the screen undersize was concentrated magnetically. Several different screens, between 8 and 35 mesh, were used and it was desired to determine the capacity of the ball mill operating in closed circuit with each screen. From earlier tests using this flowsheet and equipment, it was known that when comparatively coarse screens were used it was necessary to increase the grinding dilution in the mill beyond that ordinarily used when grinding in closed circuit with classifiers. It was also known that after the circulating load had passed about zoo per cent of the original feed it tended to increase rapidly in amount, and grinding conditions appeared to become unstable. These conditions may be peculiar to this small ball mill but they were very marked in this series of tests. If conditions were not right, the mill would suddenly "go dead," and it was found desirable to operate so that the occasional rattle of balls against the lining of the mill could be detected. As the test proceeded, it was found that the cure for almost any difficulty that developed in the grinding circuit was to add more water to the mill feed. To begin with, the mill was operated at pulp densities of from 60 to 65 per cent solids but gradually it was found that with higher dilutions grinding conditions were more stable and the ball-mill power per ton of screen undersize decreased. Actually, the most satisfactory operating conditions were secured with a pulp density of about 40 per cent solids. The ore was hard but it was possible to grind ½ in. feed so that all would pass an 8-mesh screen with a power expenditure in the ball mill of less than 2 1/2 kw-hr. per ton and with a circulating load of less than 50 per cent. With so high a dilution in the feed to the mill, it was feared that steel wear would be very high. However, the mill was not noisy, and in order to find exactly the grinding conditions, a special test was made at the end of the main series of tests. After the mill had been in operation for several hours and grinding conditions had become balanced, the power to all the equipment was shut off at a given signal. The ball mill made about one revolution after the power was turned off, and just as soon as the mill stopped, a spout was placed at the discharge trunnion and all of the pulp that flowed out of the mill was caught in tanks. The manhole in the mill was then opened and the whole mill charge dumped into other tanks. Both of these products were weighed, dried, and weighed again. The balls were screened out and weighed, and the dry solids were sized. In this way it was possible to determine the nature of the pulp and the ore within the mill under actual grinding conditions.

Jan 1, 1945

By L. R. Weisberg, E. A. Miller

Single-crystalline films of silicon of good quality were vacuum-deposited on sapphire. The improved crystallinity was achieved by the strict exclusion of oxygen from the evaporation system, including the use of a "oxygen-free" silicon source. To minimize possible contamination of the source, the silicon was sublimed from the solid at about 1390° C. using a simple electron bombardment system to heat the silicon. This resulted in deposition rates of about 5 to 7 µ per hr and film thicknesses of 4 to 20 µ. The vacuum during deposition was ordinarily about 5x 10-8 Torr, DESPITE the success achieved in the chemical vapor deposition of silicon on sapphire using Silane,1-4 vacuum deposition has not provided comparable properties. For example, Chu et a1.5 vacuum-deposited silicon on single-crystalline substrates of A12O3, Sic, ThO2, and other compounds, and, although some epi- but the use of ultrahigh vacuum (about 1 to 3 x10-9 Torr) during deposition did not significantly improve the results in the oxygen-free system. The crystalline quality of films deposited on (0001) sapphire was found to be considerably superior to (1102) sapphire surfaces. Using (0001) sapphire, single-crystalline films were deposited at temperatures as low as 780° C and as high as 1075°C, with the best crystalline quality obtained at about 1000°C. At this temperature, hole mobilities over 250 sq cm per v-sec were achieved. taxy was indicated, single-crystalline films were not produced. More recently, Salama, Tucker, and young6 evaporated silicon on single-crystalline sapphire, but only poor crystallinity was observed, and low carrier mobilities were measured. In the present experiments, good-quality single-crystalline films of silicon on sapphire have been achieved by specifically excluding oxygen from the evaporation. This included not only the use of a "clean" vacuum system but, of special importance, the use of an oxygen-free silicon source. This has also been shown to provide a dramatic improvement in silicon homoepi-taxy.7 As a result, silicon-on-sapphire films with hole mobilities over 250 sq cm per v-set were achieved, and single-crystal films were grown as low as 780°C and as

Jan 1, 1969

By Reinhardt Thiessen

In the general study of coal, all evidence points in the one direction —that coals had their origin in a manner analogous to that of peat. The best method of studying coal, whether it concerns its chemistry, composition, or physical condition, is to study peat. The essentials in a study of peat are a knowledge of the chemistry of plants, knowledge of decay and of the transformation process of plant-substances into peat. A number of facts must be emphasized, namely, (1) peat is formed under wet conditions only; (2) plants grow in the place where peat is formed; (3) all the plant substances go into the bog; and (4) all the plant substances are subjected to a series of phases of decay which are (a) in the air completely above the water level but in relatively moist conditions; (b) above the water level, but covered by debris; and (c) completely submerged by both water and debris. Plant Chemistry Plant chemistry as a whole is remarkably well understood. The number of compounds composing plants is large, and it is not possible here to give even a comprehensive outline, but a classification into definite groups is possible; this is as follows: Carbohydrates; glucosides; pigments; tannins; acids, alcohols and ketones, etc., and their salts; essential oils; resins; vegetable bases; proteins; enzymes. Plant substances may also be grouped according to the role they play in the life of the plant, such as: Framework materials, living materials, food materials, protecting materials, waste materials. While this classification groups them well for. certain purposes, it does not group them exactly chemically; but in a consideration of the composition of coal, this is an excellent classification for our purpose here.

Jan 1, 1925

By H. S. Bell

IT SEEMS unnecessary to dwell upon the advantages of the modern pipe still as compared with the older type of distillation equipment used by oil refiners. The relatively low installation cost, coupled with remarkable operating efficiencies of pipe stills, precludes the consideration of other types except in rare instances where some peculiarity of product or plant may have an influence. The question of the actual heat required to distil petroleum is quite involved. We have extensive data on the latent heats of the various hydrocarbons under different conditions of pressure. We also have information regarding the specific heats of various oils and the effect of temperature thereon. Because of the complexity of petroleum and of each fraction, it seems impossible to theoretically analyze the partial-pressure effect of the great number of hydrocarbons upon one another during distillation. If a distillation curve and percentage analysis of any crude or product are available, it is possible to construct a curve with ordinates representing per cent. distilled and B. t. u. per pound or per gallon, or other desired unit. To do so the crude is split into fractions, of 5 or 10 per cent. The boiling point and gravity of each fraction being determined, it is possible to evaluate the heat required. As each fraction is removed, the residue must be raised to a higher temperature and latent heat supplied for the successive fraction. As the calculations progress, the latent heats decrease while the specific heats increase. Such a curve is illustrated by Fig. 1 for a typical 39.9 B° North Texas crude.

Jan 1, 1928