IN A broad sense, the subject of slag control includes not only the adjustment of the composition of the slag but also of its relative weight in terms of percentage of the metal-bath weight. The slag is made up essentially of (1) oxides formed by oxidation of silicon, manganese, phosphorus, and iron in the charge, (2) SiO2, MnO, and other oxides charged as such, and (3) lime charged or fed to the heat to neutralize the “acidic”: oxides present (Si02 and P2O5). Obviously, if practically perfect control were possible over the composition of the charge as well as over the oxidation process during the melting period, both slag weight and composition would be very nearly predetermined, and the control problem would be solved. Unfortunately, we have only a somewhat. imperfect control over these factors, so that beginning at about the lime-boil period in the heat, and later in the early refining period, it becomes necessary for the first helper, as the heat progresses, to make quick estimates of the composition and physical state of development of the slag (as well as of the amounts of phosphorus, sulphur, and carbon in the metal) from which he can judge how much extra lime, roll scale, fluorspar, and other additions will be needed not only to give the desired final slag composition, but also to hasten the complete fusion or shaping to a desired viscosity in the liquid state. The discussion in this chapter is limited essentially to those more or less practical rapid methods of slag estimation that have been used, or at least tried, for these purposes under actual open-hearth shop conditions. Another aspect of importance here is the extent to which the freedom of choice to the operator is limited by available charge materials, product specifications, and the oxidation and other chemical- reaction effects which inevitably occur under the conditions of this furnace process. For a better understanding of these control limitations and of the chemical and physical background of the subject, the reader is urged to read at least part of the discussion in Chapters XVII and XIX. Charge materials are discussed in Chapter IV, and many of the details of charging, melting, and refining practice closely related to slag control are given in Chapters VI and VII.

Jan 1, 1944

By Nicholas J. Grant, Klaus M. Zwilsky

EVER since the unusual high temperature creep resistance and structure stability of SAP (Sintered Aluminum Powder) and similar aluminum-alumina alloys were reported,'," there has been a need to determine whether other metal-metal oxide (or other hard stable particle) alloys, not so ideal as the Al-Al 2 O 3 system, would show similar high temperature strength and stability. Of the many possible methods of obtaining a metal-metal oxide alloy,a one that offers many practical and theoretical advantages is the simple mechanical blending of metal powders with hard stable particles, followed by pressing, sintering, and hot extruding. With this purpose in mind copper powder and silica and alumina were selected for experimentation because these materials are readily available, cheap, reliable, and lend themseives te the simplest processing and testing. Starting Materials—Two sizes of electrolytically deposited copper powders were used, a —200 mesh powder referred to as A powder in this investigation and a —325 mesh powder referred to as C powder. Silica was added in the form of pure Potter's flint from which a —10µ fraction had been separated. Alumina of the a variety was used in two size ranges. The first was a —10µ fraction separated from a coarser aggregate, the second a commercial product of 0.3µ average diam manufactured by Linde Air Products. Preparation of Powders—Five-hundred gram batches of A copper with 1, 3, and 10 volume pct of each of the three oxides mentioned above were prepared, as well as C copper containing 1, 3, and 10 volume pct of —lop silica. Powders were weighed out carefully and blended by ball milling in air for 24 hr. Since this treatment resulted in surface oxidation of the copper, the charge was hydrogen reduced at 260°C for 5 hr. The next step consisted of hydrostatically compacting the powder into a shape suitable for the required hot working. For this purpose a slug about 11/2 in. in diam and 31/2 in. in length was produced by placing the mixed powders into a rubber sleeve, holding in a perforated steel canister, and rubber stoppering at the ends; the assembly was then subjected to a hydrostatic pressure of 50,000 psi. The air was evacuated from the assembly prior to pressing in order to prevent

Jan 1, 1958

By N. Brown, H. Green

The effect of quenching temperature and of aging temperature and time on compression stress-strain curves of ß brass was investigated. Age softening occurs at a rate which decreases with decrease of quenching temperature below the critical temperature for ordering. The activation energy for softening is 15,400 cal per mol. No matter how rapidly brass is quenched or what the temperature from which it is quenched, practically complete order is obtained at room temperature. It has been demonstrated that with respect to the specific heat,',' electrical resistivity," X-ray diffraction, and microstructure, the slowly cooled and rapidly quenched specimens are the same and that complete long range order exists in both cases. However, Smith" showed that the hardness of ß brass depended upon the cooling rate and the temperature from which brass is quenched. Smith showed that the hardness was a maximum for specimens quenched from about 445 °C and that the as-quenched structure softened at room temperature at a rate depending upon the temperature prior to quenching. This softening after quenching is in this paper referred to as age softening. The results of this investigation are qualitatively the same as the findings of Smith. However, a more detailed analysis of these phenomena has been possible since the stress-strain curve offers a more sensitive index of the state of the metal than hardness. It is the purpose of this paper to show how the mechanical properties are related to the ordering of ß brass. A 200-lb ingot made from electrolytic copper and electrolytic zinc was extruded to 1/2in. rod. Chemical analyses at frequent intervals along the rod showed that the alloy contained 51.5 pct Cu with the greatest impurity being iron, at 0.01 to 0.001 pct. To obtain a constant test material, the 1/2in. extruded rod was warm-rolled to % in. diameter at 200°C and then recrystallized to a grain size of 2.0 mm. The specimens for the compression test were % in. high and % in. in diameter. The specimen ends were polished on 600 metallographic paper and coated with Molykote for a lubricant. The compression rig consisted of an anvil resting on the machined table of the Baldwin Southwark testing machine and a plunger fixed to the movable cross

Jan 1, 1954

By Zay Jeffries

A. G. WORTHING, Nela Park, Cleveland, Ohio (communication to the Secretary*).-The paper by Mr. Jeffries is very interesting. He is to be commended for his pioneer work in the study of equilibrium systems at the very high temperatures which one obtains with tungsten and molybdenum. There is one statement, however, to which I must take exception. On page 1227, a statement is made which would seem to indicate that the Nela Research Laboratory joined Dr. Langmuir in the recommendation of 3,300°C. as the most probable melting point of tungsten. This is not the case. In. the paper referred to by Mr. Jeffries, I have given 3,630°K. or 3,357°C. as the melting-point temperature for tungsten. Confirming observations by other workers in our laboratory justify the belief that this latter value is correct to within a small part of the discrepancy between the two values quoted.

Jan 12, 1916

By Charles Catlett

While the occurrence of phosphorus in coking-coal has assumed less importance with the development of the opeu-hearth method of steel-making, it may not be without interest to note the form in which phosphorus exists in one particular coal-seam. In the examination of what is known as the Big seam, which outcrops a few miles west of Columbiana, Ala., my attention was called to the distribution through the coal, in the form of minute veins and particles, of a resinous-looking substance. A small amount of this was selected, and was provisionally identified as evansite (Al6 Y2 O14, 18 Aq). Subsequently, through the courtesy of Dr. J. Sharshall Grasty, of the Geological Department of the University of Virginia, I was able to secure an additional amount of material, which was purified down to about 0.3 g. This was examined by Prof. John J. Porter, of the University of Cincinnati, and gave the following partial analysis: Per Cent. Loss on ignition,......... 37.43 Phosphoric anhydride,..10.33 Alumina,..........36.33 There was also a trace of silica, and quite a considerable quantity of lime and magnesia. Professor Porter was led to think that the material was not pure, but a mixture of several of the phosphates of aluminum carrying lime and magnesia. The material available did not permit of the convenient determination of the other ingredients. One form in which phosphorus occurs in coal is evidently as a hydrated phosphate of aluminum; and any coal which shows to the eye the occurrence of a light-colored resinous-looking material should be looked on with suspicion as being high in phosphorus.

Jan 1, 1912

By Ralph Arnold

SOUTH of Havana, there is a geanticline that extends from Madruga to Bejucal. The older formations outcrop in the. east and gradually go under until in the Bejucal region the entire geological column lies below the surface, with the Nazareno formation at the top. The well we are now drilling is located at the deepest part of the section. I think there is a good chance to obtain oil, for the conditions are like those in the Santa Maria field in California. In both places asphalt occurs in the upper shales in the form of dikes that break through the older formations. The drilling in the Santa Maria field was brought about by the evidence offered by the asphalt deposit, which overlaid the oilfields. Detailed geologic work in both fields discloses pretty well defined domes with minor faults. Between Madruga and Bejucal, the San Francisco formation has come, to the surface in a dome and still farther east there are other domes near the base of the formation in which the Madruga chalk is the surface rock. The Bejucal dome was selected for drilling because, it gave the greatest evidence of petroleum in the form of asphalt and because it offered three chances of striking oil in the three possible oil horizons below the top of the Nazareno formation. The hole is now 2600 ft. deep and has shown considerable gas and some oil. The lowest gas sand will probably yield from 2,000,000 to 3,000,000 cu. ft. per day. Very heavy mud has been used in drilling this hole and this has held back gas and oil indications.

Jan 3, 1925

By Hollis L. Caswell

The present status of integrated circuits utilizing. superconductive switching. elements is reviewed with special attention given to fabrication techniques, methods for interconnecting completed circuits, and refrigeration requirements. Cryoelectronics has been largely an "inte- grated-circuit" technology since its conception because the switching speed of superconductive devices is attractive only when these devices are fabricated with thin-film techniques. It is true that cryotron circuits can be constructed from wires of appropriate materials (as indeed was done by Dudley Buck 1 in his early investigations) but these circuits will switch in times characteristic of milliseconds whereas similar circuits fabricated by thin-film methods have potential switching times of nanoseconds. Furthermore, cryo-electronic devices such as the cryotron lend themselves readily to fabrication by thin-film techniques since these components may be made from polycrys-talline thin films and are relatively insensitive to the presence of impurities (as measured by semiconductor standards). Therefore, during the past decade considerable effort has been devoted to developing techniques for batch fabricating circuit arrays containing superconductive switching elements. Technology had developed to the point several years ago that fabrication of cryoelectronic arrays containing up to one hundred devices was rather straightforward. However, larger arrays containing between lo4 and 106 components which are required for commercial development of cryoelectronics still pose very severe yield problems. Thus in a sense cryoelectronics found itself in 1962 at the point semiconductor technology finds itself today; namely, individual devices and small groups of integrated devices could be fabricated with acceptable yield and the outlook for building larger integrated-circuit arrays was bright. Unfortunately, problems associated largely with yield have made fabrication of these larger arrays difficult. Unlike semiconductor technology, cryoelectronics had to solve the problems of large-scale integration before it could become economically attractive. This has proven to be a sizable burden to bear. Since several reviews exist on superconductivity,2 superconductive devices,3 and cryoelectronic technology, no attempt will be made in this paper to summarize these areas. Instead a few specific topics will be dealt with in more detail. First, a brief description is given of selected superconducting switching and storage devices with special attention to several metallurgical techniques which improve the performance of these devices. Second, techniques used to fabricate cryoelectronic devices are described with emphasis on problems affecting yield. Third, techniques for interconnecting a number of cryoelectronic planes are described. And last, refrigeration of cryoelectronic components is discussed briefly since the low operating temperature of superconductive devices is an important consideration in this technology. SUPERCONDUCTING STORAGE AND SWITCHING DEVICES The basic superconductive switching device is the thin-film cryotron. The geometry of this device is attractively simple, since it involves only the intersection of two lines that are electrically insulated from each other. The switching element (gate) and control element (control) of a crossed-film cryotron are arranged as illustrated in Fig. 1. The material for the gate is selected to permit the gate to be switched from the superconducting to the normal (resistive) state by the application of a control current. Tin, which has a critical temperature (T,) of 3.7°K, is commonly used for the gate and the cryotron is operated at a temperature just below T, (for example, 3.5°K). The control material (normally lead, with T, = 7.2°K) is chosen so that the control is never driven normal during circuit operation. To improve cryotron operation, a ground plane, also of lead, is placed under all of the circuitry to act as a diamagnetic shield and improve the current-density uniformity across the width of various thin-film elements. Normally, line widths vary from 0.005 to ^ 0.020 in. and film thicknesses from 300 to 10,000A, although new fabrication techniques make narrower lines feasible. In fabricating cryotrons it is important that the edges of the gate elements be geometrically sharp to avoid undesirable switching characteristics associated with a thinner edge region, Fig. 2. One technique which has been used extensively to form patterns consists of placing a physical mask containing the film pattern between the evaporation source and the substrate and depositing through the mask. Film strips formed in this manner possess a penumbra at the film edges due to shadowing of the evapor-ant under the mask. Several techniques have been proposed for minimizing effects due to this penumbra. One of the more promising metallurgical techniques

Jan 1, 1967

By J. E. Stukel, J. Cocubinsky

A CONSIDERABLE amount of information is available on the equilibrium distribution of manganese between slag and metal under oxidizing conditions. These data have increased our knowledge of the manganese reactions in the open hearth, ladle, and ingot mold. In contrast, there is a paucity of data on the slag-metal distribution of manganese under reducing conditions. The purpose of the present investigation was to study the equilibrium distribution of manganese between blast-furnace type slags and iron saturated with carbon. Experimental Method Furnace: The induction furnace used for the experiments is shown in Fig. 1. A 1 in. pipe, attached to the transite cover, was fitted with a window through which the charge could be observed. Material could be introduced into the furnace through a tee and plug without removing the cover. A graph-it cylinder (3 in. ID and 10'/2 in. long), centered within the induction coil, was used as a heating element. During a test, a zircon plug kept the top of the furnace from becoming too hot from heat radiation. At the bottom, a graphite block on the vertical center line of the furnace and extending 1 1/2 in. into the coil, was used as a support for the graphite crucibles containing the melt. The graphite crucibles, machined from regular carbon electrode stock, had a 2% in. OD with 3/16 in. walls and were 5% in. long. The fumes present in the furnace during the early part of a run made optical readings uncertain. A noble metal thermocouple was, therefore, adopted to measure the temperatures. The arrangement used, shown in Fig. 1, allowed the silmanite protection tube to be replaced with a minimum effort. The thermocouple was calibrated against a standard Pt-Pt-Rh thermocouple in a fused quartz protection tube. The latter was inserted in the molten iron by removing the glass window on the cover. The lower couple was found to be very sensitive to temperature changes. To insure accurate temperature readings, the graphite crucibles were made to fit tightly against the silmanite protection tube. Further, to avoid contamination of the thermocouple by carbon, the silmanite tube was changed and the calibration procedure was repeated at frequent intervals. By using this temperature measuring technique, the furnace was easily held within *1O°C of the desired temperature. Because of the small free space in the furnace, no attempt was made to control the atmosphere. It

Jan 1, 1955

By Lawrence Addicks

Some three years ago the smelter connected with the Chrome, N. J., refinery of the United States Metals Refining Co. found itself embarrassed by constantly increasing piles of unsmelted blast-furnace flue dust. The charge was fine and 10 to 15 per cent. of it was blown over into the flue. Sulphur was at that time too scarce to make the sintering of the finer part of the charge attractive, and raw-ore smelting in a reverberatory with a partly oxidized charge was not to be thought of. A great many schemes were considered, including leaching, blowing into the converters, and briquetting, the problem finally narrowing down to blast roasting and nodulizing. It was found by experiment that blast roasting would not yield a satisfactory sinter without the addition of coke dust or sulphide fines to augment the fuel value of the flue dust, and on this account, together with the low first cost of a kiln, the latter was decided upon. A couple of tons of flue dust were tried out in the experimental kiln in the laboratory at Yorktown, Va., of J. H. Payne, who acted as consulting engineer in this connection. This kiln was approximately 2 ft. in diameter and 20 ft. long and was fired with fuel oil. A run of several hours yielded excellent nodules. The ki1n showed no tendency to build in and form "nose rings" and gave a fuel consumption of 50 gal, of oil per ton of flue dust. There was no indication of any stack loss. The roasting was strongly oxidizing. A study of what full-size kilns were doing on cement clinker and on nodulizing pyrites cinder indicated that a 60 by 6 ft. kiln would certainly not consume over half of the oil per ton of flue dust shown on the test and as fuel oil at that time was selling around 2 1/2 c. per gallon it was decided to let it go at that. A 60 by 6 ft. kiln was decided on, as that size is standard in cement practice, although fast being replaced by much larger ones with their greater fuel economy, and as it fitted in the building space available. A 6-in. brick lining brought the net diameter down to 5 ft. The inclination

Jan 1, 1915

By C. W. Sherman, John Chipman

IN the mathematical statement of the law of mass action, the activity of each substance consumed or produced in a reaction is used to obtain a numerical constant which is characteristic of the equilibrium of that reaction at the given temperature. The activity in many cases is equal to, or proportional to, the concentration. If this is the case, any units denoting concentrations, such as weight percentage or mol fraction, may be substituted in the equilibrium expression. It is even permissible to use mixed units provided only that each unit is that used in defining the activity of the corresponding substance. The indiscriminate use of concentration units in writing equilibrium constants sometimes leads to very erroneous results. On the other hand, what appear to be contradictory results from similar investigations often might be resolved if the activity is the quantity that is used to determine the equilibrium constant for the reaction in question. De-sulphurization serves as an important illustration. Sulphur in lron and Steel The control of the sulphur content of the finished product is one of the oldest and broadest problems in the metallurgy of iron and steel. In general, this control must be exercised through the action of a slag, and for this reason experimental studies of the distribution of sulphur between slag and metal have assumed considerable importance. Under slags of the type found in the basic open-hearth furnace the ratio (% S)/[% S] does not in general exceed about 8. Under blast-furnace conditions, however, de-sulphurization ratios of 50 to 100 are readily obtained, and under laboratory conditions using similar slags, the ratio may be as high as 400. The fact that blast-furnace metal is much more readily desulphurized than is molten steel rests upon two distinct phenomena. The first of these is connected with the slag reaction. In the open-hearth furnace, the equilibrium in the following reaction places a definite limit on the sulphur content of the slag: S + 0-- = 0 + S- - where the symbols underlined indicate elements dissolved in the liquid metal, while slag constituents are represented as ions. The high oxygen content of the open-hearth bath prevents this reaction from proceeding far enough to effect good desul-phurization. In the blast-furnace process, however, the oxygen activity is limited by the presence of carbon in the metal and in the coke bed and the controlling reaction becomes: S_+O- + C_=S- + CO(gas) [2] The second phenomenon which contributes to the easier desulphurization of blast-furnace metal is the effect of high concentrations of other elements. These elements, notably carbon, silicon, and phosphorus, increase the thermodynamic activity of sulphur several fold. As a result of this increase, the escaping tendency of sulphur from the metal phase is increased and its removal facilitated. Previous Studies It becomes, therefore, a matter of importance to determine the effects of various elements upon the activity of sulphur in the melt. The experimental approach to this problem has been made through the equilibrium between sulphur in the melt and gaseous atmospheres containing hydrogen and hydrogen sulphide. The reaction and its equilibrium constant are written as follows: S + H2(gas) =H2S(gas);K1 = -- [3] Pn2 • as where the symbol a, represents the activity of the sulphur in solution in the metal. The understanding of the chemical behavior of sulphur in steel and pig iron rests on a firm knowledge of the binary system Fe-S. A number of studies of the equilibrium have given closely agreeing results from which the activity and free energy of the dissolved sulphur may be found. The recent paper by Sherman, Elvander, and Chipman1 includes a discussion and quantitative comparison of the results of several of the significant researchesr-" on dilute solutions of sulphur in iron. The results of this study indicate that the relationship between the ratio Ph,s/p+ and the percentage of sulphur in solution is not a linear one. This

Jan 1, 1953

By S. D. Baumer, P. M. Hulme

IN the late thirties, the National Carbide Co. cooperated with C. E. Wood, of the U. S. Bureau of Mines, in his investigation of the relative merits of various desulphurizers, including soda ash, caustic soda, and calcium carbide. Laboratory tests showed that carbide, when it could be made to react, is an excellent desulphurizing agent for molten iron. Sulphur content can be driven to lower levels and higher extractions obtained with carbide than with actionsany of the more common reagents. Wood's results1 are shown in Table I. Unfortunately, as the Handbook of Cupola Operation puts it, the chemical fact that carbide is a good desulphurizer was of only academic interest because it was found to be extremely difficult to devise a practical means to make it react with molten iron. Calcium carbide is formed in the electric furnace at 4000°F and above, and its softening point is probably at least 500 °F above the usual working temperatures encountered in iron and steel practice. Consequently, carbide does not form a true slag but floats as a dry powder on top of the metal and only a very small portion of it ever comes in actual contact with the iron. Stirring with a rabble, or pouring the metal over the carbide, increases the efficiency only slightly. Extractions of 20 to 30 pct can be obtained in this manner, but conventional soda slag treatment can do better than this and do it more cheaply. All attempts to lower the melting point of carbide in order to obtain a reactive, liquid slag have so far proved fruitless. Directly under the arc in a metallurgical electric furnace, carbide becomes highly reactive. Excellent sulphur removal can be obtained without any slag other than a thin layer of carbide." imilarly, good results are obtained by adding small amounts of carbide to the finishing slag in double-slag arc furnace practice. To react a liquid with a solid, it is axiomatic that the liquid has to wet the solid before anything can happen. If the solid is heavier than the liquid, the problem is easy, but it becomes more difficult when the solid is much lighter than the liquid, as in the case of carbide and liquid iron. Wood recognized this problem and solved it in a unique fashion. The results shown in Table I were obtained by spinning the carbide beneath the surface of the molten iron by means of a refractory centrifuge. This technique allowed each particle of the finely divided carbide to come into intimate contact with the metal and to be wetted thereby. Wood's centrifuge technique was successful in the laboratory where it achieved excellent and consistent results. Some attempts were made to expand this method to commercial practice, but serious difficulty was encountered in obtaining a refractory centrifuge head that would be economically feasible. About this time the war intervened and the project lay dormant for several years. In 1944, it was revived. It was suggested that the carbide could be blown into the metal with a carrier gas in an attempt to eliminate the necessity for the expensive and brittle centrifuge. The idea was first tried out in a fairly large ladle of iron using natural gas as the carrier. Considerable sulphur was removed, but it was quite obvious that the use of natural gas was not practical. Attempts then were made to blow carbide into molten iron using, in turn, nitrogen, argon, carbon dioxide, air, and oxygen. The latter two gases proved unsatisfactory. Calcium evidently prefers oxygen to sulphur because in the tests calcium oxide and carbon dioxide were produced, the sulphur still being untouched in the iron. Nitrogen, argon, and carbon dioxide gave much better results, although the efficiencies and extractions were erratic, and only a few isolated tests approached the results obtained by Wood. Table II shows typical results obtained with these gases. The sulphur removals were interesting, sometimes even encouraging, but it is evident that such erratic behavior could not be tolerated in commercial practice. A number of different types of equipment, such as sand blasting machines, refractory guns, and the like can used to blow the solid into the metal. All types required relatively large quantities of gas in order to maintain the flow of solid carbide through the system and into the metal. It was observed that the bubbles of gas breaking through the surface of the metal contained quantities of unreacted carbide. The liquid metal never came in contact with these particles and if it cannot wet them it cannot react with them. The initial work had shown that carbide had great possibilities as a desulphurizer. In practice

Jan 1, 1952

By Harry C. Swanson

TRANSPORTING concrete from mixer to forms has always been a problem. Twenty-five years ago this task was generally accomplished by means of wheelbarrow or concrete buggy. On large dam jobs, as the number of these projects increased, the gantry crane or highline came into use. Today several methods of handling concrete are employed on smaller surface construction jobs, for example, transit-mix trucks or dumpcrete trucks, which have crawler cranes with buckets for placing concrete into forms. In 1944, during early stages of developing Mather mine A shaft, several large underground concrete jobs were necessary. At this time the Cleveland-Cliffs Iron Co, purchased the first pump-crete machine, introduced by the Chain Belt Co. of Milwaukee. The machine was used to pour approximately 200 cu yd of concrete for a dam, or bulkhead, located 400 ft from the shaft. Concrete was mixed on surface, lowered down the shaft 1000 ft in a 2-cu yd bucket hung under one skip, spouted into the bowl of the pumpcrete machine from the bucket, and pumped directly into the forms. Since the day of the first pipeline concrete in 1944 to the present time, other equipment and other methods have been developed to permit transportation of concrete by pipeline through vertical and horizontal distances totaling 1 mile from mixer to forms. Much of the efficiency in present handling of underground concrete can be credited to the Bethlehem Cornwall mines, where concrete was transported through 6-in. pipe for great distances down an inclined shaft and along levels into forms.' During initial development of Mather mine B shaft, with concrete work under way on two or more levels at one time, the pneumatic concrete placer, Fig. 1, was selected as best adapted for underground concrete transportation. The 3/4-cu yd pneumatic placer is a small machine readily moved from one location in the mine to another. It can be equipped with two sets of mine car wheels, which will permit moving on regular mine tracks. It is therefore possible to send concrete through the pipe at great velocity; the pipeline is clean after each shot except for the film of cement adhering to the inside. With the proper slump in the concrete, it is possible to shoot concrete 2000 ft with this machine, using the mine supply of compressed air at 95 psi. This equipment was first used at Mather mine B shaft to concrete slusher drifts, Figs. 2 and 3, and finger raises located about 2000 ft from the shaft. In several instances there were bends into crosscuts and up vertical distances into the forms. For the first pours two placers were used. The first was located near the shaft where the concrete could be spouted into it from a 2-cu yd concrete bucket on the cage. The second was set on the side of the drift at a point approximately 1500 ft from the shaft. The concrete was shot directly into the second placer from the first unit and from the second machine directly into the forms. After completion of several pours with the two machines, a trial pour with only one placer located at the shaft proved that the second placer could be eliminated. Since then all pours have been successfully completed with only one placer underground. As production of iron ore from the mine increased and the development program expanded, use of the cage for handling mine supplies and concrete became a major problem. This brought about the first attempt at shooting concrete vertically down the shaft for 2600 ft. A 6-in. pipeline with victaulic couplings installed during shaft sinking was used for the trial. One placer was set on surface 250 ft from the collar of the shaft so concrete could be spouted directly into it from the mixer. This machine shot the concrete 250 ft horizontally on surface to the shaft, 2600 ft vertically down the shaft, and 100 ft horizontally into the second placer located near the rib of the shaft station or plat. The second machine shot the batch into the forms, about 2000 ft. Total distance horizontally and vertically was 4800 ft. The entire time cycle for a ¾-cu yd batch of concrete from the mixer on surface to the forms underground totaled about 5 min. During the past two years the two-placer method from the mixer on surface to the forms underground has proved a very efficient means of transporting underground concrete. Advantages of using pipeline concrete are as follows: 1—Interference with normal mining operation is eliminated. When the cage, skips, mine cars, or mine openings are used for transporting concrete and materials used for making concrete, mine operation suffers in one way or another.

Jan 1, 1955

By Werner Schwartz, Wolfgang Haase

Lead sulfide concentrates, which may include other lead concentrates, are sintered on an up-draught sintering machine without the addition of any diluting agents or fluxes. Subsequently they are melted in an oil- or gas-fired rotary furnace. The sintering and melting processes are based upon the following roast-reaction: PbS + 2 PbO = 3 Pb + SO, PbS + PbSO, =2 Pb + 2 SO, For obtaining a lead bullion free from sulfur, the sintering process is carried out in such a way that the sinter product contains a small amount of excess oxygen above that to react with the sulfides. At the end of the melting process, when the reactions are finished, the remaining small amount of oxide residues is reduced with coal to which a certain percentage of soda ash (about 1 pct of the lead bullion) is added. For the lead smelting process described neither coke nor fluxes—except soda ash—are required. This process is being utilized by a European smelter successfully and with a high lead recovery. The consumption figures for the smelting of 100 tons per day of lead concentrates are indicated. The lead content of the lead concentrates from modern ore dressing plants ranges from 65 pct to above 80 pct. In most lead smelters of the world these concentrates are smelted in a blast furnace. For blast-furnace smelting the concentrates have to be desulfurized and agglomerated by sintering. A requirement for the perfect operation of a down-draught sintering machine and of a blast furnace is a maximum lead content in the feed of 40 to 45 pct. For this reason, some lead concentrates have to be diluted by adding return slags, limestone, and possibly iron oxide and sand. As an example, 100 tons of lead concentrate with 72 pct Pb would contain 13.5 tons of gangue (including the zinc). To produce a perfect sinter with 42 pct Pb it would be necessary to add 70 tons of flux and return slag, more than five times the original weight of the gangue, to the sinter mix and blast-furnace charge. A correspondingly large amount of coke would be required in order that all of these materials reach the heat of formation and the melting temperatures of the slag (1200" to 1400°C) inside the blast furnace. The roast-reaction process presents a possibility for lead recovery without dilution of the concentrates. In this process the concentrate mixed with coal is placed upon a Newnam-hearth and air is blown through nozzles into the heated mix. AS a result metalllic lead and a relatively great amount of so-called .'Grey Slag" with a lead content of 25 to 35 pct are formed. The slag is sintered to eliminate sulfur and, after addition of the requisite fluxes, treatt:d in a blast furnace. Owing to the poor recovery of lead from the hearths and to the unavoidable heavy hand-work plus the risk of poisoning this process is utilized in very few 112ad smelters today. Since in mxny countries of the world coke is expensive and difficult to obtain, it appeared feasible to use the principle of the roast-reaction by modern sintering and melting methods with recovery of the lead in electric, or oil, gas, or coal-fired furnaces. Two processes are utilized on an industrial scale: A) Lead smelting in the electric furnace of the Bolidens Gruv A/B in Sweden, as described by S. J. Walldcn, N. E. Lindvall, K.G. Gorling, and S. Lundquist. B) The self-fluxing lead smelting of Lurgi Gesell-schaft fiir Chemie und Huttenwesen m.b. H., Frankfurt a M, Germany, which is described in this paper. In the Boliden process referred to above the sinter mix is pelletized by enveloping return fines with layers of flue dust, limestone powder, and dried galena concentrate. The roasting and agglomeration are carried out on a down-draught machine, and a slight excess of sulfur is left in the sinter product. During the smelting in the electric furnance the roast-reactions occur and a slag poor in lead and a sulfur bearing lead are formed. This latter is subsequently oxidized in a converter to obtain lead bullion and dross. The Lurgi-process achieves the maximum possible extent of the roasting reaction on the sintering machine. The wet flotation concentrates are blended with return fines (lead content 70 to 80 pet), any existing flue dusts and lead slimes—but without the

Jan 1, 1962

By F. W. Jessen, John C. Miller

In many areas where carbonate rocks form important parts of the stratigraphic sequence, stratigraphers have experienced varying degrees of difficulty in differentiating and correlating limestone and dolomite units in both surface and subsurface work. With early Paleozoic rocks of the Mid-Continent, insoluble residues yield a remarkable amount of strati-graphic data and relatively good correlations may be carried over broad distances.' Unfortunately, neither such information nor electric logs and radioactive logs have been particularly helpful in interpreting the limestone sections of the Permian Basin of West Texas. This is because: (1) the variations in the sections may be very slight; (2) no completely satisfactory method of interpretation has been developed; and (3) the measurements themselves are not sensitive enough for small variations. Also, such logs are influenced by the fluid content. Paleontology and micro-paleontology remain the ultimate arbiters. As a routine tool, however, paleontol-ogical examination is slow and tedious. Chemical analysis may be used, but this, too, is extremely slow. Although rocks are not classified according to chemical composition, there is considerable variation with rock types. Correlation by chemical composition has two advantages, first, the characteristics determined are subject to minimum human error and interpretation, and secondly, the lithologic changes are not masked by fluid content as in the case of electric and radioactive logs. Some fossils concentrate certain elements which tentatively might be used to date rock units.' Rapid chemical analysis by spec-trographic means could be used as an adjunct to other means employed in correlation work, or might, in itself, present a suitable method. PURPOSE OF THIS INVESTIGATION Sloss and Cooke' have published data concerning spectrographic analysis of limestone rocks specifically for purposes of direct correlation of a single formation. These authors found satisfactory evidence that differences in percentage of four elements (Mg, Fe, Al, and Sr) in the Mississippian limestones of northern Montana were useful in carrying out correlation of this formation over a distance of approximately 50 miles. It was concluded from the preliminary work that the spectrochemical method offered possibilities of solution of some problems of correlation heretofore not possible. Since the work of Sloss and Cooke' was confined to one particular limestone zone, extension of the use of the method to examine two or more geologic formations would aid materially in the over-all problem of correlation of such rocks. Equipment is now available commercially with which very rapid spectrographic analyses may be made, and hence the problem was to determine whether the variations existing in the minor constituents of limestones were sufficient for use in possible correlation. Qualitative and semi-quantitative investigations were made to determine whether significant changes in the chemical condition occurred. It was a further purpose to investigate the geologic time-boundaries to see whether significant chemical variation could be found corresponding to the paleontological breaks. It was desirable to attempt correlation of a thick section of limestone or dolomite rock and to have as much information as possible on the section. Furthermore, it was felt that examination of formations more difficult to correlate by other means would enhance the value of the method should definite points of correlation be found. Samples were chosen from the Chapman-McFarlin Cogdell No. 25 well in the Cogdell field, Kent County, Tex., and from the General Crude Oil Co., Coleman No. 193-2 well in the Salt Creek field, Kent County, Tex. These fields belong to the famous series of "Canyon" reef fields of West Texas. Cores from the above wells were available from the United States Geological Survey, Austin, Tex. THE SPECTROGRAPHIC METHOD The choice of procedure to be followed in this investigation was based on the anticipated requirements peculiar to the problem. Since the problem was primarily to investigate the possibilities of applying the spec-trograph to problems of correlation in thick carbonate sections, a precise quantitative analysis did not appear necessary. A qualitative analysis to show the possible absence of presence of any element, or a semi-quantitative analysis of the elements present to show the relative changes in magnitude of selected elements was required. Both types of analysis were employed. The two most widely applied methods of semi-quantitative estimates are those of Harvey and of Slavin4,5 though various other procedures have been described.6 while the Harvey method has been modified by Addink,7 this refinement did not seem necessary to the present problem. Essentially, the procedure employed is a variation of the total energy method of Slavin with two exceptions: (1) stressing matrix effect, and (2) using densitometer measurements. As measured by a densito-

Jan 1, 1956

By R. E. Reed-Hill

A simple accurate graphical method for orienting fcc crystals using (111) slip traces on a single surface is described. Solutions placing the pole of the surface in a unit stereographic triangle are obtained using a Wulffnet, a (111) standard projection showing the four (111) planes, and a (111) standard projection ruled into unit stereogmphic triangles. The multiplicity of solutions is described in relation to this method. AN accurate, rapid single-surface technique for orienting fcc crystals, using (111) slip or twin traces, has been a matter of continuing interest, as evidenced by the periodic appearance of papers on this subject.'-4 This note presents a new method possessing some advantages over those previously reported. It is an analog to the technique for hcp metals5 where the solution is based upon a stereographic rotation of the specimen surface on a (0002) standard projection that contains the planes of the possible features that might account for the observed traces. In the hexagonal solution, the axis of rotation is the basal-plane trace in the surface. In the fcc case, the axis of rotation is one of the observed ( 111) slip or twin traces. It has been observed that the solution is greatly facilitated if the indicated movements of the (111) traces during the rotation of the surface are plotted directly on a paper copy of a Wulff net as shown schematically in Fig. 1. The trace selected to represent the axis of rotation is assumed to fall at the north-south poles of the Wulff net. The directions of the other traces are then plotted as points at the proper angles around one-half of the basic circle of the net. The loci of points corresponding to the movements of these traces (directions) during a 90-deg rotation of the surface, about the polar axis of the net, are then easily and accurately drawn by following the appropriate small circles on the Wulff net. The solutions to the problem are obtained with the aid of a (111) standard projection of the (111) planes, see Fig. 2. This is normally a Xerox copy of a carefully drawn master made on high-quality tracing paper. The (111) standard projection is superimposed over the Wulff net and rotated about its center until the points of intersection of the loci of surface traces, drawn on the Wulff net, and the great circles representing the (111) traces, all lie along a common meridian of the Wulff net as demonstrated in Fig. 3. This latter great circle represents a possible position of the surface. The pole of this plane is then plotted on the (111) standard projection. Its location in a unit stereographic triangle may be readily obtained by superimposing (over the standard projection) another tracing paper (111) standard projection subdivided into unit stereographic triangles. The result of this last operation is shown in Fig. 4. MULTIPLICITY OF THE SOLUTIONS The maximum possible number of (111) traces on a single grain surface is four. Any one may be selected as the axis about which the surface is rotated. Corresponding to each such choice are three possible surface-pole orientations, related to each other by a simple 120-deg rotation about the pole of the (111) basic circle. This is a direct result of the threefold symmetry of the (111) standard projection. Since each of the four rotations will normally give a different set of three-pole positions, there are, accordingly, twelve possible solutions. Each of these twelve solutions places the surface pole in the same relative position in a stereographic triangle so that all are crystallo-graphically equivalent. Accordingly, only a single solution is required to obtain a basic orientation of the crystal. It should be noted, however, that the orientations obtained by reflecting* any of these twelve orien- *The reflected orientations may be obtained by a 90-deg rotation of the opposite sense to that shown in Fig. 1. This rotation places the correspond-ing trace loci in the lower hemisphere of the Wulff net rather than in the upper hemisphere. tations through the surface are also possible orientations that could account for the surface traces. Thus, a given set of four traces always corresponds to a pair of basic orientations related by reflection through the specimen surface. This ambiguity can only be re-

Jan 1, 1967

By D. R. Parrish, T. M. Geffen, R. A. Morse, G. W. Haynes

Flow tests on small core plugs have indicated that a large amount of gas is trapped and not recovered by water flooding a gas sand. Instead of I to 15 per cent pore space, as is usually assumed, the residual gas saturation is 15 to 50 per cent pore space, and is thus of the same magnitude as residual oil after water flooding oil sands. A thorough investigation was made to ascertain that large amounts of residual gas actually remain in reservoirs after a water flood and that this condition is not merely a laboratory phenomenon. In field experiments, the amount of gas left in a watered-out gas sand was measured by use of a pressure core barrel and the residual gas saturation of two watered-out gas sands was determined by electric log evaluation. In the laboratory, an investigation was made of factors that could possibly cause the value of residual gas saturation as measured on small core plugs to differ from that in the reservoir, and the effect of these factors on the amount of residual gas saturation was studied. The factors studied include flooding rate, static pressure, temperature, sample size and saturation conditions before flooding All evidence established that a relatively high gas saturation is trapped in water flooded gas sands and that this residual gas saturation can be measured in the laboratory by tests on small core plugs. INTRODUCTION There. has been general agreement among engineers that very high recovery of gas could be obtained from natural reservoirs By water displacement. Gas recoveries of 80 to 95 per cent of the original gas in place have become the normal expectation in water drive fields. The assumption of high recovery has been based on: 1. low density and viscosity of gas compared with water; 2. the erroneous assumption that the flow relationship in a gas-liquid system where gas is the displaced phase will be the same as when it is the displacing phase. It has long been recognized that gas can flow at very low gas saturations (in the range of 1 to 15 per cent pore space) in systems where liquid is being displaced by gas. By assuming the reversibility of this process, the conclusion was reached that the residual gas saturation following water flooding of a gas reservoir would be the qame (1 to 15 per cent) as that at which gas first flowed continuously as a displacing phase. Recent laboratory relative permeability Studies have demonstrated that the flow characteristics are very different in gas-liquid systems, depending on whether gas is displacing or being displaced by, a liquid. Also, it has been shown that there is no difference between the flow characteristics of oil and water or gas and water in water wet porous rocks. The residual gas saturation that can be expected following water flooding of a gas reservoir then would be in the same range as the residual oil saturation normally expected after water flooding an oil reservoir! i.e., in the range of 15 to 50 per cent pore space, depending on the rock characteristics. Obviously, such a difference in residual gas saturation means very important differences in recoverable gas reserves from water drive reservoirs. For example, if the original gas saturation in a field were 70 per cent, and the residual gas following flooding were 35 per cent, only half of the gas in place could be recovered by complete water drive, compared to the previously expected 80 to 95 per cent. This is a situation in which complete pressure maintenance could result in very greatly reduced recovery, since straight pressure depletion recoveries from gas reservoirs can approach 80 to 90 per cent. Such a change in thinking must be based on more complete information than a series of small core tests. Hence the work reported herein was undertaken with the objective of determining whether or not residual gas saturations indicated from small core relative permeability tests at atmospheric pressure and room temperature are representative of the residual gas saturations which could be expected after water flood of natural reservoirs. A study was made both through laboratory and fields tests to determine any differences in residual saturation which might be occasioned by differences in pressure, temperature, rate of flooding, and original saturation conditions. Four separate types of laboratory experiments and two field mesurements were made in this investigation. The apparatus and testing methods of each will he discussed individually. LABORATORY EXPERIMENTS, APPARATUS AND PROCEDURE Relative Permeability Tests Steady state flow experiments Here conducted using the Penn State type apparatus. The equipment used has beer (described in a previous publication? "Irreducible" water satu-ration was established in the core' by imposing ,a capillary pressure of 45 psi before simultaneous flow of air and water

Jan 1, 1952

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,' whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham's work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy' found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By Jasper Whiting

It is well known that there is no better indication of the working of a blast-furnace than is ,given by analyses of its gases; yet although many indiviclual analyses have been made, there is, I think, no

Jan 1, 1892

By L. R. Plitt, M. K. Kim

The collecting properties of the fatty acid type collectors for barite were studied using zeta potential measurements, infrared spectroscopy, and Hallimond tube flotation tests. Based upon the experimental results, an adsorption model has been formulated which emphasizes the predominant role of the hydrocarbon chain in collector adsorption.

Jan 1, 1975

By E. W. Stewart, G. P. Conard, J. F. Libsch

The effects of several additives upon the reduction characteristics of hydrogen-reduced ferrous formate are described. The various additives inhibit sintering of the reduced iron particles by apparently different mechanisms. The magnetic properties of the low density compacts produced from the resulting ultra-fine iron powders were improved markedly. THE permanent magnetic characteristics of ultra-fine iron powder prepared by various means have been a subject of considerable interest and experimentation in the past few years. When such particles are small enough to show single domain behavior, they possess' 1—permanent saturation magnetization, and 2—high coercive force. In the absence of domain boundaries, the only magnetization changes in a particle occur through spin rotation which is opposed by relatively large anisotropy forces. With decreasing particle size, the coercive force tends to increase to a maximum and then decrease because of the instability in magnetization associated with thermal fluctuations. Kittel' has calculated the critical diameter at which a spherical particle of iron can no longer sustain domain boundaries or walls to be approximately 1.5x10-' cm. Stoner and Wohlfarthr in England and Neel4,6 in France have shown from purely theoretical calculations that the high coercive force expected from single domain particles is dependent upon crystal anisotropy, shape anisotropy, or strain anisotropy contributions. Further work by Weil, Bertaut,' and many others has contributed much to the understanding of fine particle theory. Neel and Meikeljohn" have demonstrated that a decrease in particle size below a critical value of approximately 160A leads to a quite rapid decrease in coercive force because of the prevention of stable magnetization by thermal agitation. Lih1, working with powders prepared by the reduction of formate and oxalate salts of iron, has shown the marked influence of powder purity upon magnetic properties. Maximum coercive force was obtained in powders of approximately 65 pct metallic iron content while the maximum energy product, (BxH) occurred in powders of 85 pct metallic iron content. Careful consideration of the preceding theoretical considerations and experimental results has led to the manufacture of permanent magnets from ultra-fine ferromagnetic powders by powder metallurgy techniques. Such work has been done by Dean and Davis," the Ugine Co. of France, and Kopelman." The aforementioned work of Kopelman and the Ugine Co. was concerned somewhat with the effect of various additives upon the properties of hydrogen-reduced ferrous formate. Virtually no work, however, has been published on the effects of additives on the reduction rates of metal formates, although unpublished work by Ananthanarayanan16 howed promise of improved energy product in ultra-fine iron compacts prepared by the hydrogen reduction of a coprecipitated mixture of magnesium and ferrous formate. After consideration of the preceding information, it was hoped that a better balance between the metallic iron content and particle size of the reduced iron powder could be accomplished by a prevention of the attendant sintering of the partially reduced iron powder during the reduction reaction. It appeared possible that magnesium oxide might interpose a mechanical barrier between adjacent iron particles and prevent their sintering together, while metallic cadmium and metallic tin would interpose a liquid barrier which might accomplish the same purpose. The degree to which these materials were effective in accomplishing the foregoing objective and the experimental details associated with the work are reported in the following sections of this paper. Experimental Procedure Preparation of Formate and Oxide Mixtures: To obtain ferrous formate of reproducible reduction characteristics, a slight modification' was made in the technique of Fraioli and Rhoda." A supersaturated solution of ferrous formate was mixed with an equal volume of 95 pct ethyl alcohol and the formate crystals precipitated by stirring and screened to —325 mesh. These crystals were in the shape of elongated hexagons, approximately 4x10 micron in dimension. Various preparations of such ferrous formate, designated as lot 111, were reduced for 2 hr, yielding ultra-fine iron particles of exceedingly reproducible size, metallic iron content, and magnetic properties. The magnesium and cadmium formates were prepared by the reaction of dilute formic acid with their respective carbonates, while the tin formate was prepared by the reaction of dilute formic acid with stannous hydroxide. To evaluate the effect of metallic formate additives in intimate mixture with the ferrous formate, varying amounts of magnesium, cadmium, and tin formates were coprecipitated with the latter. The designations of these materials and their chemical compositions are given in Table I. Due to the differing solubilities of the various formates in aqueous media,

Jan 1, 1956