Jan 1, 1942

By J. J. Gilman

THEORIES of fracture in metals have been based primarily on the dependence of fracture strength on grain size. This dependence was first observed by Masing and Polanyi.l These workers, as well as 0rowan12 and Davidenkov and Wittman,' thought the grain size could be equated with the crack size in the Griffith condition for crack propagation.4 In this way they could account for the observed proportionality between fracture stress and the reciprocal square root of the grain size. The chief results of recent investigations of the fracture strength of polycrystals are summarized in Fig. 1. Low for iron,5 Petch for iron,' Greenwood and Quarrel for zinc, Petch and Zein for zinc,' and Hauser, Landon, and Dorn for magnesium'' have all found that the fracture stress of a polycrystal is proportional to the reciprocal square root of the grain size. Also, they find that, for large grain sizes, the fracture stress lies near the extrapolation of the yield-stress curve determined at small grain sizes; where measurable plastic strain precedes fracture. Low9 has gone a step further and shown that, in Range 1, the fracture stress in tension is almost identical to the yield stress in compression for a given grain size. Homes and Gouzou, 10 and Low also have shown that, in Range 2 of Fig. 1, microcracks form when the yield stress is reached, but they do not cause failure until the stress reaches a much higher value. The fact that yielding always precedes fracture suggests that fracture is induced by plastic flow. A mechanism by which this might occur was first proposed by Zener.11 He pointed out that blocked dislocations would cause stress concentrations which might cause fracture. The blocking would be caused by grain boundaries. This idea has been developed by Eshelby, Frank, and Nabarro,12 by Koehler,13 and by Stroh.14 By means of etchpits blocked dislocations have been observed in brass by Jacquet,15 in zinc by Gilman,16 and in lithium fluoride by Gilman and johnston. The blocked-dislocation theory and the experiments that bear on it have been summarized by Mott.18 One of the strong points of the blocked-dislocation theory is that it can explain the grain-size dependence of the fracture stress in a natural way. However, Low9 has pointed out that the theory is not satisfying when it is considered quantitatively. Gilman10 also has criticized the theory and presented an alternative interpretation of the relation between fracture stress and grain size. Since the blocked-dislocation theory is not the only theory that can explain in the grain-size effect, it is necessary to find other evidence either to support or deny it. In this investigation the following points were studied: 1) If blocked dislocations normally cause fracture, then the fracture stress ought to be very high in the absence of plastic glide. Is it? 2) If dislocations must be blocked in order for metals to fracture, then certain types of grain

Jan 1, 1959

71 BROADWAY, NEW YORK, Sept. 22, 1913. CHARLES W. GOODALE, Chairman, . DARSIE C. BARD, ESQ., Secretary. Committee on Precious and Base Metals, Butte, Montana. Gentlemen The wonderful success of the meeting of the Institute held in Montana makes it necessary that some public acknowledgment should be made to those to whom this success is due. We are conscious that the securing of the great number of technical papers of lasting value and the carrying to success of most complete detailed arrangements for holding the meeting have called for several months of skilled effort on your part. The benefit of the meeting is very great and extends not only to those who were fortunate enough to be present, but to our four thousand absent members and their friends as well. To you and your associates on the Committee whose efforts have made this never-to-be-forgotten meeting possible we owe far more than can be expressed in votes of thanks. Very respectfully, CHARLES F. RAND, President.

Jan 10, 1913

Jan 1, 1948

By R. A. Corley, W. R. Wilcox, J. R. Teviotdale

Chemical vapor deposition of hafnium carbide yielded whiskers, needles, dendrites, faceted crystals, and adherent coatings. The gas stream compositiom and the mass transfer conditions determined the habit of the deposit. The deposits were obtained at temperatures ranging from 1100" to 1800°C. HAFNIUM carbide has the highest melting point of any binary compound; therefore, its various potential applications are a subject of vital interest to the aerospace industry. The experiments described herein were performed to investigate the chemical vapor deposition of hafnium carbide with particular interest being placed upon the possible production of high-strength single-crystal whiskers for composite materials. In 1931 Moers 1 used a gaseous mixture of HfC14, Hz, and toluene to vapor deposit crystalline hafnium carbide on a tungsten filament heated to 2400°to 2800°C. More recently Lepie 2 deposited hafnium carbide on graphite using HfC14 and methane in a helium gas carrier. The pyrolytic depositions described here were accomplished in graphite tubes by using various gas mixtures and dopants. The resulting crystal habits included whiskers, needles, needle dendrites, bulbous dendrites, faceted crystals, and smooth, adherent poly-crystalline layers. EXPERIMENTAL The depositions were carried out in an induction-heated graphite tube, 1.2 cm ID, which was contained in a vertical 9-cm-ID quartz tube. (A more detailed account of the experimental procedures and results is given in Ref. 3.) Refractory oxide fiber and tubes and graphite felt were utilized jointly and singly for therma1 insulation. A typical temperature distribution is shown in Fig. 1. The reactant gases were introduced at the top and removed at the bottom of the tube. Table I summarizes the experimental conditions and results. Many deposition habits were obtained. X-ray analyses showed that they possessed the hafnium carbide structure. Almost invariably these formed well above the point of maximum temperature in the graphite tube. The habit depended strongly on the gas composition. In a series of runs (e.g., run A) using HfC14 and toluene in H 2, hafnium carbide coatings, Fig. 2, were reproducibly obtained at the position where the tube wall was 1400°C, and bulbous dendrites, Fig. 3, were

Jan 1, 1969

By Frederick M. Becket, Russell Franks

WideSpread experimentation has been conducted in recent years to devise a means of preventing intergranular corrosion in austenitic chromium-nickel steels of the 18 per cent chromium-8 per cent nickel type. Additions of titanium to these steels have been used commercially to overcome this dificulty, as advocated by Krupp of Germany, and the latest literature reference concerning improved details of this method is the article by Bain, Aborn and Rutherford.' Extensive work by the present authors has shown columbium also to be a particularly valuable agent for inhibiting intergranular corrosion. This paper does not deal with steels that are largely or wholly austenitic; it is limited to a discussion of the results obtained through the use of titanium and columbium in plain high-chromium steels. For many years titanium has been used commercially by some steelmakers as a cleanser, and to a lesser extent as a hardener, but then in greater percentages. The results of the work to be described disclose that titanium and columbium in proper Proportions act as effective softeners in the high-chromium steels. It is well known that chromium intensifies the hardening effect of carbon in steel; it imparts pronounced air-hardening properties within a rather wide range of chromium content; it provides increased ductility in steels of given strength and hardness; and it enhances resistance to corrosion and oxidation at elevated temperatures to a marked degree. However, in applications requiring a combination of some of these valuable properties great hardness is frequently a detriment rather than a merit. When the objective is a soft and ductile steel having optimurn corrosion resistance, the producer strives for a carbon content as low as commercially practicable. Despite these efforts some of the commercial high-chromium steels low in carbon present considerable difficulties during production, owing to their air-hardening properties, and in consequence the economic result is not favorable. A good example is found in the 5 to 6 per cent chromium steels employed chiefly in the oil-cracking industry. Sleels

Jan 1, 1934

By L. H. Cadoff, L. M. Adelsberg

The layer growth method has been used to investigate the reaction kinetics of liquid titanium and hafnium with carbon and the [liq] - [liq + TiC] and [liq] - [liq + HfC] phase boundaries at temperatures above 1800°C. The equipment and experimental procedures used in this investigation are basically identical to those described in an earlier paper' on the Zr-C reaction. Temperature control, however, was improved significantly by connecting a Latronics Colo-Ratio automatic pyrometer and a controller to the power source. The subsequent temperature variations were ±10°C; previously ±20°C was obtained using manual controls. The absolute accuracy of the pyrometer, however, must be considered to be only ±40°C.* The spectrographic analyses of the materials used in this study are listed in Table I. The isothermal reactions of titanium (1800° to 2700°C) and hafnium (2300" to 3000°C) with carbon (graphite crucibles) resulted in the formation of carbon-saturated liquid metal and layers of Tic and HfC, respectively. The thicknesses of the carbide layers, determined from metallographic measurements at 100 times, as a function of carburization time and temperature are given in Figs. 1 and 2. At each temperature, parabolic growth behavior for these reactions was observed and could be expressed as x2 =Kpt, where X is scale thickness (corrected for heating and coolingL), Kp the parabolic growth constant, and t the isothermal carburization time. Values of Kp as a function of temperature for the carbides are shown in Fig. 3 and listed in Table 11. The growth constants are expressible as: kpTiC = 0.2 exp(-61,800/RT) sq cm per sec for Tic and Kp HfC = 2.62 exp(-95,300/RT) sq cm per sec for HfC. The liquidus phase boundaries were determined from metal samples treated in graphite crucibles for different times ranging from 4 to 100 min at each of the temperatures indicated in Table 11. Metallographic examination revealed that the carbide precipitates were distributed uniformly throughout the frozen metal matrices. This is attributed to the rapid cooling rates (800°C per min) and the small difference in density between the precipitated carbide and the liquid metal.

Jan 1, 1968

By H. Rush Spedden

Antoine M. Gaudin was a vigorously creative man and throughout his career an internationally respected leader of his chosen profession of mineral engineering. To his professional colleagues and clients and to his former students he was both "Professor Gaudin," their wise, inspiring, and enthusiastic teacher, and "Tony," their, warm and beloved personal friend. Thus, his teachings and his unique inquisitive-creative approach to problems live on and grow in the accomplishments of his students. Antoine Gaudin was born at the turn of the century in Smyrna, Turkey, where his father was general manager of a French-owned railroad. It was there that he spent his earliest years, literally in the shadow of classic marbles from diggings at the site of Aphrodesias, which his father had rediscovered. From this, Tony developed an appreciation of the arts. He eventually surrounded himself with art treasures; he reveled in the beauties of nature, and he cherished his choice collection of rhododendron and azaleas. His artistic traits led him to take up painting when his daughter, Elinor, sought his help in blending her tints for a water color. In typical fashion he was not satisfied until he had become adept with pastels in capturing the muted tones of distant landscapes and the technical properties of light and color. Unfortunately not many paintings were produced. His paternal grandfather was Marc-Antoine Gaudin, for many years secretary of the Academie des Sciences in Paris, and a well known chemist and mineralogist whose primary interests included the synthesis of precious stones. In an autobiographical sketch written in 1939, Dr. Gaudin recalled: "As a child I saw many of the original synthetic sapphires and rubies which my father had inherited. This, coupled with my father's avocation of mining ventures and archaeology, early decided that I would become connected with the mineral industry." One can speculate that the archeological activities of his father, the mineral systhesis experiments of his grandfather, and his own early studies of mineralogy and geology formed a base from which his special talents as an experimentalist were to develop. Laboratory research under Professor Gaudin's personal guidance was often an intensive, fast-moving, and exciting experience--especially to a new graduate student. First of all, Professor Gaudin was a highly skilled observer with seem-

Jan 1, 1976

By P More

US 4,132,621-In the electrowinning of aluminum, the cells are aligned in a lengthwise direction so as to lessen the harmful influence of the induced magnetic fields Each cell is supplied with current from the preceding cell both via the head arid at least one side riser The output of the cathode bars is divided into two separate groups, the upstream group supplying the head of the subsequent cell arid the downstream group supplying the side risers of the subsequent cell This produces a substantial improvement in cell efficiency arid a greater regularity P Morel, J P Dugois, arid B Langon, assigned to Aluminium Pechiney. Jan 2, 1979 12 pp. (204¬243M) Filed 1-12-78 (868,861) Priority: France, 1-19-77 (77/2,213) US 4,134,806-Cells, anodes, arid methods for use in the electrowinning of nickel, cobalt, copper, zinc, or other metals from an acid ore leach solution or the like The cell is provided with vertically immersed stationary cathodes and stationary rod anodes which are noncorrodible by the electrolyte arid are electrocatalytic to the anode reaction. The spaced parallel anode rods are connected to electric current supply bars The anode rods have an electroconductive core made of a metal alloy arid a surface coating of an oxide of platinum or a platinum group metal The ratio of active cathode surface area to active anode surface area is preferably at least 3 0. De Nora arid C Traini, assigned to Diamond Shamrock Tech¬nologies, SA Jan 16, 1979 13 pp. (204-105R) Filed 9-15-77 (833,661) Priority Italy, 1-29-73 (19738 A/73). Same British 1,434,334-5, dated May 5, 1976 US 4,135,994-In the electrowinning of aluminum at a high current efficiency, the electrolytic bath is a mixed molten salt consisting of 2-15% by weight of aluminum trichloride, 15-83% of sodium chloride, 15-70% of combined calcium chloride arid magnesium chloride but riot more than 40% of calcium chloride, arid optionally up to 10% of barium chloride Preferably, plate-shaped graphite electrodes used for both cathodes and anodes are arranged in parallel inclined relation so that the axis in the lengthwise direction makes an angle of from 10° to 45° to the horizontal. T Ishikawa arid H Ichikawa, assigned to Nippon Light Metal Co Ltd Jan 23, 1979 4 pp (204-67) Filed 11-15-77(851,632) Same British 1,550,502, dated Aug 15, 1979

Jan 1, 1980

By Edward H. Robie

AT a recent meeting of the AIME Board there was considerable discussion of a suggestion that companies should be more interested in promoting AIME membership among their employes. The advocate of this idea argued that companies benefit greatly if their employes are active AIME members, so even on purely a selfish basis they should use various means to encourage membership. Also he argued that companies in general make no contribution to the support of the AIMS although benefiting from its work, so should not object to making more of a contribution, financial or otherwise, than they do. One Director stated that an investigation had developed the fact that a large majority of members felt it unwise for employers to pay the initiation fees or dues of employes. They felt that AIMS membership should be on a purely personal basis; that the rewards of active membership were sufficient so that it is a good investment for a man in developing his own professional stature, presumably resulting in an increase in salary sooner, or in greater amount, than would otherwise be the case. If an employer paid a member's dues or initiation fee the member would take less interest in the Institute. But this Director felt that an employer should otherwise encourage his employes to join the Institute, attend its meetings, and write papers based on company work for presentation and publication. Another Director reported that his company pays the expenses of AIME members in its employ to meetings; the company also encourages nonmembers to attend AIME meetings but does not pay their expenses unless they present papers of interest to the company. Another Director, representing a supplier, stated that his company's policy was to send some of its staff to all AIME meetings at which papers of interest were to be presented or at which valuable contacts could be made.

Jan 1, 1952

By W. J. Keep

Manganese is a nearly white metal, having about the same appearance when fractured as white cast-iron. Its specific gravity is about 8, while that of white cast-iron, reasonably free from impurities, is but a little above 7.5. As produced commercially, it is combined with iron, and with small percentages of silicon, phosphorus, and sulphur. It is generally produced in the blast-furnace. If the silicon is under 0.50 per cent., the product will be white. If the manganese is under 40 per cent., with the remainder mostly iron, and silicon not high enough to make the product gray, the alloy is called spiegeleisen, and the fracture will show flat reflecting surfaces, from which it takes its name. With manganese above 50 per cent., the iron alloy is called ferromanganese. As manganese increases beyond 50 per cent., the mass cracks in cooling, and when it approaches 98 per cent. the mass crumbles or falls in small pieces. When the percentage of manganese is high, the planes of the fracture are not so bright as when it is lower. The ferro-manganese which we have used in the experiments reported in this paper, contains Mn, 81.62; Si, 0.256 ; and combined carbon, 6.153 per cent. We have not been able to make test-bars from this, because the alloy cracks in small pieces in cooling. Manganese combines with iron in almost any proportion, but if an iron containing manganese is remelted, more or less of the manganese will escape by volatilization, and by oxidation with other elements present in the iron. If sulphur be present, some of the manganese will be likely to unite with it and escape, thus reducing the amount of both elements in the casting. Hence, in remelting irons, some of the sulphur which has entered from the fuel with which the iron is melted will very likely unite with some of the manganese in irons which make up the mixture and escape. Remelting, therefore,' reduces the percentage of manganese in cast-iron.

Jan 1, 1892

New Products Equipment

Jan 8, 1951

FOLLOWING the passage of resolutions by a num-ber of the western local sections, which have beer printed in previous issues, the Board of Directors appointed a committee consisting of Messrs. Reynders, DeGolyer, Taylor and Merica, to call on the Director of the Budget, and to bring these resolutions to his attention. In response to a request to the committee Mr. Reynders has addressed the following letter to General Lord. In response to a suggestion made in the course of the conference held between you and President DeGolyer of this Institute at Washington on Oct. 6, I present herewith a brief statement of the reasons that have led the mining engineers and metallurgists of this country to urge upon the Government a policy of increasing support from year to year to the United States Geological Survey and the Bureau of Mines. While these are not the only technical bureaus to which we look for data and guidance in our work of winning and rendering useful the mineral re-sources of the country, they are the ones on which we chiefly rely and the usefulness of which extends over all the industries which are based on mines and mining. In calling this matter to your attention and to that of the departments in which these bureaus are situated, I am acting on behalf of a special committee appointed by the Board of Directors and which includes men in close and intimate contact with the iron, coal, petroleum, metals and metallurgical industries; men well qualified by experience and position to voice the real feeling of these industries. The subject is not a new one to our Board, which has long kept a watchful eye on the work of the two bureaus as would be natural in that the American Institute of Mining Engineers, represents the largest group of technical men and executives and the one of most wide-spread interest in the American mineral industries. With 9000 members and. 27 local chapters scattered among the mining states, the Institute is in a peculiarly favorable position to know and to set out the feeling among mining men and metal-lurgists as to the proper scope of activities of these Federal bureaus, the quality of their work, and the gaps in knowl-edge that most need filling.

Jan 11, 1927

By Mark A. Ammon

The two most widely used methods of measuring hardness are the Brinell and the scleroscope. In the Brinell method a hardened steel ball is pressed into the steel under a definite load and the area of the resulting depression is measured. The load in kg. per sq. mm. of the area of the depression is taken as a measure of the hardness. Within certain limits the hardness number so determined is independent of the load or the size of the ball. In the scleroscope method a small weight carrying a diamond point is dropped through a glass tube upon the steel and the amount of rebound is taken as proportional to the hard-' ness. In both methods the scale of hardness is an arbitrary one; however, they agree in a comparative may, that is, a steel showing 50 per cent. increase in hardness by the Brinell test mill show approximately 50 per cent. increase in hardness by the scleroscope test. Yet upon consideration of the two methods it appears that, upon a steel which has been carbonized, this should not be the case ; for the scleroscope method gives almost exclusively the surface-hardness, and the condition of the material below the surface has but a slight bearing upon the hardness number. The results given by the Brinell method should, however, be the exact opposite; for the depth of penetration 'of a ball pressed into the steel would be dependent to a large extent upon the condition of the material below the surface. This is particularly obvious when it is considered that the size of the ball ordinarily used in the Brinell method is 1 cm. (about 8 in.) in diameter under a load of 3,000 kg., while the diamond point of the scleroscope is in the neighborhood of 0.01 in. across, fitted in a hammer of about 0.5 oz. weight and dropping from a height of 10 inches.

Jan 1, 1913

By B. J. Scheiner, A. G. Smelley

The Bureau of Mines, US Department of the Interior, is conducting research on a dewatering technique for fine particles generated during the mineral beneficiation process that will recover a portion of the water now being lost using conventional waste disposal methods and significantly reduce the time required for land reclamation. The technique utilizes a flocculant, polyethylene oxide (PEO), that forms strong stable flocs that can be dewatered rapidly on static and/or rotary screens. Infield tests, phosphate clay waste has been dewatered from a nominal 2.5% solids to greater than 20% solids. In other field tests, coal-clay waste has been dewatered from a nominal 3% solids to greater than 55% solids. In addition, small-scale continuous tests have shown that bentonitic clays can be dewatered from 12% solids to 40% solids.

Jan 1, 1985

By C. W. Arnold, H. L. Stone, D. L. Luffel

The purpose of this research is to determine (I) the efficiency of small banks of enriched gar driven by methane in displacing oil from a porous medium and (2) the effects of variation in bank size and composition of that efficiency. Most of the experiments were conducted in a sand-packed tube 20-ft long and 1/2-in. in diameter. The hydrocarbon system generally used was methane, butane and decane at 2,500 psia and 160°F. The results of these experiments indicate that, in the regions contacted by the gas, a small bank of an oil-miscible gas driven by methane can displace all of the oil in a piston-like manner. If the enriched gas is of such composition as to remain immiscible with the oil, displacement of oil is less efficient than for the miscible case, and the gas bank travels through the sand with a velocity less than that of the driving gas. These data along with theories discussed imply that smaller banks and less total gas are required when the enriched gas and oil are miscible. INTRODUCTION Widespread application of enriched-gas drive to the recovery of oil rests upon a key factor — the use of limited quantities, or "banks", of enriched gas. At the present time, the value of liquefied petroleum gas or other enriching agents discourages their use in a continuous injection technique, or even in a large bank, except in a few isolated reservoirs. If small banks of enriched gas driven by methane were as effective in displacing oil as is continuous injection, the enriched-gas drive process might be applied to a larger number of reservoirs. Previous research on the mechanics of the enriched-gas drive process reported by Stone and Crurnpl and by Kehn, Pyndus and Gaskell has utilized continuous injection of enriched gas. This work has shown that two types of displacements occur. With gases containing sufficient intermediates. the oil is displaced misciblv and complete recovery is obtained from the regions swept. When gases are used which contain insufficient intermediate hydrocarbon for miscible displacement, oil is displaced immiscibly. In the latter type, selective solution of the intermediate hydrocarbons causes a swelling and reduction in viscosity of the oil and leads to an increased recovery over that obtained by dry-gas (methane) drive. The size of the enriched-gas bank necessary for efficient displacement of oil is determined by those factors which cause deterioration of the bank. A differentiation may be made between those factors which operate on a microscopic scale and those which act on a macroscopic scale. On the smaller scale, the enriched gas mixes in the direction of flow by diffusion and convection with the fluids immediately preceding and following it. On the larger scale, the gas may by-pass the oil by flowing through permeable streaks, by overriding the oil because of density difference, or by fingering because of unfavorable viscosity ratios. In such cases, the enriching material tends to mix with the oil both laterally and in the direction of flow. The increase in effective area available for diffusion and dispersion of the enriching components leads to a faster degradation of the bank and a need for a larger bank than is necessary for those cases in which no by-passing occurs. The effects of such macroscopic factors in the deterioration of enriched-gas banks have been reported in a separate paper by Blackwell, Terry and Rayne. The present study was confined to the factors which operate on the smaller scale, in particular to the behavior of banks of enriched gas in sands uniformly swept by the gas. Experiments were designed to answer the following questions. 1. Can small banks of enriched gas driven by methane be used to secure oil recoveries comparable to those obtained by continuous injection of enriched gas? 2. What is the optimum bank size (the minimum bank size necessary to obtain a recovery comparable to that obtained by continuous injection of the same enriched gas)? 3. How many total pore volumes of gas must be injected to obtain the maximum recovery when the optimum bank size is used? 4. What is the effect of varying the number of enriching components in a gas bank? This report describes the experimental investigations and discusses the results in terms of their significance to reservoir behavior.

By D. C. Buffum, L. D. Jaffee

THAT the path of brittle fracture in temper brit-tle steel differs from the path in unembrittled steel has been known for some years1 More recently it has been recognized that alloy steels, at least, display two forms of temper brittleness1 which may be called upper-nose and lower-nose. No experimental evidence has been published, however, to show that the two forms can be distinguished by simple inspection of brittle fractures. Fig. 1 is a photograph of the fractured surface of a V-notch Charpy specimen of SAE 3140 steel in which temper brittleness developed during heat treatment in the lower-nose temperature range.' The steel was austenitized 1 hr at 900°, tempered 1 hr at 675", and embrittled 48 hr at 500°C, with water-quenching after each treatment. The temperature of transition from ductile to brittle fracture in the Charpy test was + 2°C (criterion of transition: 100 pet fibrous). The hardness was Re 25; the austenite grain size ASTM 8. This specimen was broken at 150°C in the standard Charpy test and absorbed 6.6 ft-lb; its fracture was rated 0 pet fibrous. Fig. 1 shows that the fracture appeared rough to the naked eye. At the side of the specimen away from the notch (the side which was in compression during the test), the surface as a whole deviated sharply from a plane. At higher magnification, X60, the surface gave

Jan 1, 1959

By A. N. Holden, J. H. Hollomon

Inhomogeneous yielding during the early stages of plastic flow has been observed in many metals and has long been a subject of controversy. Low carbon steel, when strained at room temperature, exhibits a distinct yield point at which the metal ceases to behave elastically and begins to flow plastically without further increase in stress,† often with an actual decrease in stress from that existing at the yield point. One manifestation of this behavior is the familiar Lüders lines. The extent of the yield point elongation (the plastic strain which results without raising the stress above that at the initial yield point) may be several percent. Several explanations of this type of yielding in steels have appeared in the literature:1-3}; 1. The segregation of carbides or other constituents at the grain boundaries of ferrite forms cell-like blocks which break down at a higher stress than that at which the ferrite alone will flow. 2. The precipitation of various constituents within the ferrite itself in some way blocks initial flow until a higher stress is reached, after which a great deal of flow occurs without further increase in stress. 3. The restraining influence of neighboring, less favorably oriented grains in a polycrystal results in a storing up of energy, which on yielding is sufficient to cause the continued propagation of slip bands on the multiplicity of slip systems available in adjacent iron crystals without increase in stress. 4. Local segregation of carbon atoms increases the stress required for the initial propagation of dislocations. The stress required for further deformation is lower.3 Such an explanation would require the presence of upper and lower yield points in single crystals. Low and Gensamer2 have shown that heterogeneous yielding can be eliminated by removal of carbon and nitrogen from polycrystalline steels by wet-hydrogen treatment. They also demonstrated that the re-introduction of minute amounts of carbon or nitrogen caused a return of the yield point. Observations of the initial flow of single crystals containing small amounts of carbon and nitrogen- should provide a clue to the explanation of inhomogeneous yielding. Previous tests of iron crystals4-6 can not be considered conclusive because it is uncertain whether the carbon and nitrogen were satisfactorily removed by the decarburization technique employed. The purpose of the experiments described herein was to determine whether single iron crystals containing either carbon or nitrogen would exhibit in-homogeneous yielding. Experimental Procedures THE PREPARATION OF SINGLE CRYSTALS All crvstals were formed in the following way. Aluminum killed sheet material 80 mils thick was machined into specimens of the outer contour shown in Fig 1. These mildly tapered specimens were decarburized at 730°C for 16 hr in hydrogen that had been bubbled rapidly through water maintained at 70°. The resultant grain size after decarburizing was approximately ASTM 5. Several stress-strain curves were made of the decarburized niate-

Jan 1, 1950

GENERAL Broken Hill lies at latitude 31º58'S longitude 141º27'E on the semi-arid western plains of New South Wales. From discovery in 1883 until the end of 1969 the lead-silver-zinc orebody has yielded 107,570,000 tons of ore for an overall grade of 13.1% Pb, 6.9 oz Ag/ton and 9.4% Zn.* The orebody currently supports the activities of four mines which are, from north to south, North Broken Hill Limited, Broken Hill South Limited, The Zinc Corporation, Limited and New Broken Hill Consolidated Limited. It is estimated that in 1969 these mines produced about 8 ½ % of world lead production and about 6% of world zinc production. In 1905 The Zinc Corporation, Limited was founded to recover zinc from tailings dumps and moved into mining in 1911 on leases purchased from Broken Hill South Limited at the then southern extremity of the "line of lode". New Broken Hill Consolidated Limited was formed in 1936 to explore and mine for deep ore in the leases to the south of The Zinc Corporation which were purchased from Barrier South Limited. The Zinc Corporation, Limited and New Broken Hill Consolidated Limited mines are both managed by Conzinc Riotinto of Australia Limited, which wholly owns The Zinc Corporation, Limited and has a 32% interest in New Broken Hill Consolidated Limited. * Throughout this paper tons referred to are long tons of 2,240 lbs.

Jan 1, 1970

By J. A. Putnam, A. D. K. Laird

In laboratory research on the behavior of oil, gas and water in porous materials, no direct method has been devised to measure saturation without disturbing the flow. Indirect methods involving various forms of radiation have been developed for measuring one or two components. The X-ray absorption method for two components has been described previously1-3. The possibility of three component measurement has also been mentioned1. Since two component measurement still requires considerable care to insure accuracy, the fact that three components can be measured satisfactorily is not generally appreciated. The fraction of the energy of an X-ray beam of one wavelength transmitted through a material is given by the transmission factor. in which 1 is the beam's path length through the fluid. p is the fluid density, and 1,. is its mass absorption coefficient. Eq. 1 implies that all parts of the beam pass through equal amounts of the fluid. Practical applications are, therefore, limited to systems in which the fluid is distributed so that I varies negligibly over the cross-section of the beam. Typical variations of the transmission factor with X-ray tube potential arc shown in Fig. 2 from which experimental points have been omitted for clarity. The X-ray absorption of low pressure gases in a core is practically zero so it cannot he distinguished from that a vacuum by instruments that will differentiate between liquids. The transmission factor of a gas in a core is. therefore, unity. Consequently, the saturation of only one gaseous component can be found. If two fluids completely fill a core, their two saturations add to unity and, therefore, only one value of the transmission factor, T, is needed to determine both of them. When two liquids do not completely fill the core, their saturations do not add to unity and transmission factors at two wavelengths must be measured. At one of these wavelengths, 7 for one liquid must be different from T or the other liquid. The change of T for one liquid us the wavelength is changed between the two values must be different from the corresponding change of T in the other liquid. The two values of fluid saturation will also give that of the gas because the three saturations must add to unity. In Fig. 2 it can be seen that there are many large differences of T between various oil solutions and water solutions at any one potential, and between potentials for any one solution. Consequently, conditions for optimum accuracy of measurement of the saturations of a gas and two liquids can be chosen. Once the operating potentials have been selected, however. it is more convenient to cross plot the data from Fig. 2 on transmission factor-solution concentration coordinates for the chosen potentials, as shown in Fig. 3. Fig. 3 was used to plan the experimental procedure for Core N-38-1. Since the voltage control at 45 kv was good, the slopes of the curves in Fig. 2 at this potential would cause little error. At low potentials, however, the voltage control was not good, so 33 kv was chosen because the small slopes of the curves made voltage control less critical. The lowest strength beam that could be measured reasonably at 33 kv corresponded to a minimum T factor of 0.385. Fig. 3 shows that both 4.80 weight per cent of cadmium chloride in water and 24.0 per cent of iodobenzene in crystal oil had this T value, and, consequently, were indistinguishable to the X-rays at 33 kv. Thus, at 33 kv, the liquid saturation was given by the same curve regardless of the relative amounts of oil and water solutions present. This simple calibration curve from which the gas and liquid saturation can be read, is shown in Fig. 4. Fig. 3 also shows that at 45 kv, T for the aqueous solution is 0.610. and that T for the oil solution is 0.220. These values were transferred to Fig. 4 to give the triangular calibration plot from which the brine and oil saturations can be found, after the gas saturation has been determined at 33 kv.