By Yotamu Stephen Rainford Hara, Animesh Jha

The investigation focuses on a low temperature recovery of Cu and Co from a 40 wt% SiO2-(30 wt%Fe,6 wt%Al)2O3-10wt% CaO-7wt%CuO-7wt%CoO slag over a temperature range of 1173K to 1323K. The alloy phases containing Cu-Co and Fe-Co alloy formed via the carbothermic reduction of oxides: MO + C = M + CO(g), where M represents metallic copper, cobalt or iron. In the direct reduction of oxides, the recovery of metallic phase was well below 90% at 1323K, due to the kinetic barrier which was analysed and attributed to oxygen and metal-ion transport in the slag. This barrier was overcome by adding CaSO4 and carbon, which yields a matte (MS) phase via MO + CaSO4 + 4C = MS + CaO + 4CO reaction. Lime thus produced in situ participates in metal oxide/metal sulphide reduction reactions, which are analysed with the help of X-ray powder diffraction, scanning electron microscopy, and thermogravimetric analysis.

Jan 1, 2014

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In tungsten ion-exchange process, excessive sodium impurity enters into ammonium tungstate solution. However, the Na content of the final ammonium paratungstate (APT) product must be strictly controlled. Consequently, it is necessary to remove Na from the ammonium tungstate solution during processing in order to obtain the required purity of APT. In this study, porous Na specific absorbent, Na1+xAlxTi2−x(PO4)3, is used to remove Na from the ammonium tungstate solution. Through experiments, the effect of reagent concentration of Na1+xAlxTi2−x(PO4)3, reaction time, reaction temperature and Na concentration on the Na removal were investigated. The results showed that under optimal reaction conditions of reagent amount of NATP 1.0 times of theoretical amount, reaction temperature 25 °C and reaction time 15 min, the Na removal from commercial (NH4)2WO4 solution can reach 98%. Na1+xAlxTi2−x(PO4)3 has a good applicability to different Na+ concentrations. The obtained APT product reaches the national standard purity of zero level.

Jan 1, 2014

By Dian Adisty, Leiv Kolbeinsen, Eli Ringdalen

In Si and FeSi production, the main Si source is SiO2, in the form of quartz. Reactions with SiO2 generate SiO-gas that further reacts with SiC to Si. During heating, quartz will transform to other SiO2 modifications with cristobalite as the stable high temperature phase. Transformation to cristobalite has been investigated and shown to be a slow process where the rate varies between the investigated quartz types. The effect of quartz versus cristobalite as SiO2 source has been studied for reaction (1) 2SiO2 + SiC = 3SiO + CO, by heating of pellets with SiO2 + SiC in Ar-gas. The reaction was faster with cristobalite than with quartz. Initial experiments indicates that this is the case only in Ar and not in CO-atmosphere The higher specific surface area of cristobalite is believed to contribute to the higher rate. The industrial consequences of the observed difference between quartz types are discussed.

Jan 1, 2014

By Alessandro Blasi, Massimo Morgana, Corradino Sposato, Pietro Garzone, Giuseppe Devincenzis

The rare earth elements are essential for a diverse and expanding array of high-technology applications, which constitute an important part of the industrial economy of the 21st century. As a matter of fact, rare earth has been listed in the category of strategic elements in many countries becoming a core business for international research. Experimental tests have been carried out on a bench scale battery of mixer settler composed of 24 stages, each one with a volume of 150 ml. These trials have been performed at room temperature checked by a micro-climatic control system. The battery was setted in two sections: extraction and scrubbing section. Rare earths concentrations were obtained by ICP-OES analysis made on aqueous phase and on the stripped from organic phase. We obtained a complete separation of light rare earth (La, Ce, Pr, Nd) in two sub-groups: La/Ce and Pr/Nd.

Jan 1, 2014

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In order to produce good quality ammonium paratungstate, Sn needs be removed efficiently from the tungstate processing solution. The nascent hydrous ferric oxide has excellent adsorption ability and is often used as an adsorbent to remove metal ions from aqueous solution. In this paper, nascent hydrous ferric oxide is used to remove Sn from tungstate solution. Through experimental, the effects of pH value, reagent amount of adsorbent, reaction temperature and reaction time on the Sn removal are investigated. The study shows that 98% of Sn can be removed effectively from sodium tungstate solution and only 2% of W is lost during process under the conditions of pH 9~12, reagent amount of Fe addition 40 times Sn amount, reaction time 30min and room temperature. As the Fe addition reaches 90 times of Sn concentration in the ammonium tungstate solution, 99% of Sn is removed and APT with zero level purity national standard is obtained.

Jan 1, 2014

By Hu Meilong, Liu Lu, Bai Chenguang

Extracting perovskite from high titanium-bearing blast furnace (BF) slag is a green and potential method to recover the second titanium resource. The non-isothermal crystallization process of perovskite in synthesized high titanium-bearing slag was studied in situ by confocal scanning laser microscope (CSLM) with cooling rate of 20 K/min. The results showed that perovskite was the primary phase formed during cooling process in the titanium-bearing synthesized slag (TiO2=23%). Perovskite started to precipitate at 1719 K and finally presented an orthogonal straight lines morphology.

Jan 1, 2014

By E. Bélisle, Christopher W. Bale, S. Petersen, C. Robelin, K. Hack, J. Melançon, G. Eriksson, A. D. Pelton, P. Chartrand, S. A. Decterov, I. H. Jung, A. Gheribi

The FactSage® package consists of a series of information, database and calculation modules that enable one to access pure substances and solution databases and perform thermochemical equilibrium calculations. FactSage was originally founded by process pyrometallurgists and has since expanded its applications to include hydrometallurgy, electrometallurgy, corrosion, glass technology, combustion, ceramics, geology, environmental studies, etc. With the various modules one can perform a wide variety of thermochemical calculations and generate tables and graphs of complex chemical equilibria and phase diagrams for multicomponent systems. This paper presents examples of recent and current developments in FactSage in areas of particular interest to Dr. David Robertson. These include both ferrous and non-ferrous processing, as well as solidification and refining simulation. The paper also includes reference to the Internet Fact-Web education package.

Jan 1, 2014

By Dong Joon Min, Joo Hyun Park, Mi Sun Choi, Jae Hong Shin

Sublimation of ZrCl4 is important for the production of nuclear grade metallic Zr in Kroll’s process. The sublimation kinetics of ZrCl4 was investigated by TGA under both isothermal and non-isothermal conditions. The sublimation rate of ZrCl4 increased with increasing temperature under isothermal conditions. ZrCl4 sublimation was confirmed to be a zero-order process under isothermal conditions, whereas it was first-order kinetics under non-isothermal conditions. The activation energy of ZrCl4 sublimation under isothermal conditions was 21.7 kJ/mol. The activation energy for non-isothermal sublimation was 101.4 kJ/mol and 108.1 kJ/mol with the Kissinger method and Flynn- Wall-Ozawa method, respectively. These non-isothermal activation energies were very close to the heat of sublimation (103.3 kJ/mol). Sublimation occurs by two elementary steps: surface reaction and desorption. Therefore, the overall activation energy of ZrCl4 sublimation is 104.8(±3.4) kJ/mol. The activation energy of the surface reaction and desorption steps are proposed to be 83.1 kJ/mol and 21.7 kJ/mol, respectively.

Jan 1, 2014

By P. J. Mackey

Over the course of Dr. Robertson’s career, the ferrous and non-ferrous plants have seen enormous changes in technology and increases in plant capacity, essentially amounting to a “technological revolution”. In iron and steel, the “mega” blast furnace of some 6,000 m3 working volume is now standard (~10,000 tonnes (mt) of pig iron/day). Similar huge changes in process technology and plant size have occurred in the non-ferrous industry. As an example, the fuelfired reverberatory furnace, once the mainstay of the copper industry, has disappeared - replaced by large capacity flash and bath smelting technologies. The energy consumption per unit mass of metal produced has also been reduced considerably. Our understanding of the thermodynamics and mechanisms of metallurgical reactions, a field to which Dr. Robertson has significantly contributed, has made great strides. This paper reviews these changes with particular reference to the copper smelting industry, providing also comments on expected future trends.

Jan 1, 2014

By Michele L. Bustamante, Gabrielle Gaustad

In recent years, t h e future supply of tellurium has been called into question due to the anticipated rapidly increasing demand from thin film cadmium telluride photovoltaics. Since tellurium is produced as a byproduct of other extractive processes – principally, the electrolytic refining of primary copper sulfide ore – it is important to explore the dynamics of the parent metal extraction and processing – in this case copper – when attempting to answer this question. This research explores the changing landscape of global copper production; introducing system diagramming and the concept of byproduct intensity (BPI) to illustrate concerning downward trends in tellurium supply potential. Upon closer inspection, it is concluding that, while a likely contributor to these downward trends, the increased use of non- traditional copper production techniques alone are not responsible; other factors include market substitution and incomplete data reporting. Additionally, a review of literature on tellurium recovery processing reveals a promising outlook for future supplies; highlighting potential for improvements in yield, which allow producers to make better use of what is available, even in the face of suppressed BPI.

Jan 1, 2014

By Baozhong Ma, Yonglu Zhang, Yongqiang Yang, Chengyan Wang, Yongqiang Chen

During the past decades, slurry electrolysis (SE) has been implemented commercially for the processing of bismuthinite and complex Pb-Cu bearing gold concentrates. Recently, SE was proven effective for the treatment of As-rich antimonic gold concentrates. Laboratory test results suggest over 98% of the antimony was extracted, while the extraction of arsenic and gold was less than 0.5%, and that of iron was less than 6%. Moreover, the cathode antimony contained over 98% antimony and less than 0.3% arsenic. Considering the disadvantages of traditional 3 kA slurry electrolysis baths, such as smaller electrode area, reduced capacity, and greater electrode deterioration, the authors have developed an innovative 12 kA slurry electrolysis bath equipped with mesh and fence type titanium alloy electrodes. Furthermore, the technique was successfully used within a pilot scale plant yielding results similar to those observed in the laboratory. The technique yielded ametallic antimony ingot of 99.9% purity after arsenic removal via the addition of Na2CO3.

Jan 1, 2014

By Mansoor Barati

The present paper is based on a term project for final year undergraduate students, requiring them to evaluate a process for producing silicon from rice husk. The traditional method for production of silicon involves carbothermal reduction of quartz in electric arc furnaces at temperatures exceeding 2000 °C. The technology consumes a considerable amount of electrical energy as well as fossil fuels, resulting in significant CO2 emissions. A flowsheet for production of silicon metal from rice husk is laid out in this paper. The technology will consist of combustors, which will generate steam using the rice husk biomass, power generator, and electric furnace for reduction of the rice husk. Materials and energy balance calculations presented here indicate that such process can be operated independent of external electricity.

Jan 1, 2014

By Xin Li, Hai-Xing Fang, Bing Xie, Hong-Yi Li

Chromium-containing vanadium slag (V-Cr slag) was obtained by an industrial smelting process of Hongge Ore, which is valuable vanadium-titanium magnetite to extract V and Cr in China. Sodium roasting thermodynamics of V-Cr slag in presence of oxygen were calculated to evaluate the reactivity of chemical compounds. Results showed that the oxidation of FeV2O4 was intensified in presence of Na2CO3 while the oxidation tendency of FeCr2O4 was far lower than that of FeV2O4. It was probably that reactions of impurities including Al2O3, SiO2 and Fe2O3 with Na2CO3 happened and the products can promote the oxidation of vanadium or chromium compounds in lower valence. Based on thermodynamic analysis, a two-step selective extraction process of vanadium and chromium was proposed. Extraction rate of vanadium was 88.6% while 7.0% for chromium in the first extraction step; extraction rate of 90.7% and 95.4% for vanadium and chromium, respectively, were obtained in the second step.

Jan 1, 2014

By Do-Hyeong Kim, Tae-Jung Kim, Seung-Yeon Won, Jong-Jin Pak, Min-Kyu Paek

Liquid iron alloys containing V, Mo, and Ni can be produced by the carbothermic reduction of spent catalysts used in petrochemical industry. Thermodynamics of carbon in these alloy melts is important for refining these alloys. In the present study, the carbon solubility in Fe-V, Fe-Mo, Fe-Ni, Fe-V-Mo, Fe-V-Ni, Fe-Mo-Ni and Fe-V-Mo-Ni alloy melts of various compositions was measured at 1873 K. The temperature dependency of vanadium effect on carbon solubility in liquid iron was also measured in the temperature range from 1823K to 1923K. The additions of vanadium and molybdenum significantly increased the carbon solubility in liquid iron alloys while nickel decreased the solubility. The experimental results were thermodynamically analyzed using Lupis’ relation at constant activity to determine the first- and the second-order interaction parameters of vanadium, nickel and molybdenum on carbon at carbon saturated condition. Using thermodynamic parameters determined in the present study, the carbon solubility in Fe-V-Mo-Ni alloy melts of various composition were accurately predicted and verified experimentally at 1873 K.

Jan 1, 2014

By P. Chris Pistorius

An example is presented to illustrate the joint effect of local reaction equilibria and mass transfer limitations, for reactions during ladle refining of steel. The example relies on some of the kinetic principles that David Robertson has employed to quantify many metallurgical processes. In calcium treatment of alumina inclusions in aluminum-killed steels, solid CaS forms as an intermediate reaction product. During subsequent reaction, CaS disappears and calcium aluminate forms; at the same time, aluminum and sulfur dissolve in the steel. Kinetic analysis shows that the rate of this reaction is not limited by mass transfer of dissolved aluminum and sulfur away from the reacting inclusions. The reaction rate is likely limited by transport of dissolved calcium. This example also illustrates the use of FactSage macros for kinetic modeling.

Jan 1, 2014

By Mark E. Schlesinger

Engineering design follows a six–step sequence. Demonstration of this sequence in materials engineering is less common. A case study is presented, using the 1989 paper by Gafner on the development of 990 gold-titanium alloy. This paper identifies a need, develops the problem, identifies alternatives, demonstrates the use of metallurgical principles to identify alternative responses, and shows how more favorable options are selected. The paper can also be used to illustrate engineering design as an iterative process. The paper is also useful as a starting point for more in-depth examination of specific elements of the design process, and lends itself to the creation of student exercises.

Jan 1, 2014

By Peng Jianping, Feng Naixiang, Di Yuezhong, Wang Yaowu, Pan Xijuan

A vacuum silicon thermal reduction lithium process is developed in present work which used lithium hydroxide, alumina and calcium oxide as raw materials. The process contains two steps, which are that Li5AlO4 clinker is prepared in ambient environment, and that metal lithium is extracted from Li5AlO4 clinker with ferro-silicon alloy as reductant in vacuum. On the basis of thermodynamic analysis and investigative experiments, feasibility of this process is proved. The results show that Li5AlO4 can be generated by calcination lithium hydroxide and alumina, the burning loss is above 31% under the conditions of calicination temperature above 750℃ and time more than 90min. The main phases of calcination product are Li5AlO4 and CaO. When the calcination product is reduced by ferro-silicon alloy in vacuum, the lithium reduction ratio can be over 80% under the conditions of reduction temperature 1200℃ and reduction time 60min.

Jan 1, 2014

By P. J. Mackey, J. B. See, D. G. C. Robertson

The production of iron and steel and non-ferrous metals by pyrometallurgical processes will remain a critical element in meeting the demand for materials in both developed and developing nations. Given the important need to reduce and minimise greenhouse gas emissions the technological focus of future pyrometallurgical R&D by universities and industry alike must concentrate on sustainability issues such as improved energy efficiency, recycling and waste minimization. Continued efforts are also needed on process optimization and new process development with a view to reducing capital and operating costs of the new large “mega” plants. Using the academic and industrial backgrounds of the authors, the present paper reviews the current status of R&D in pyrometallurgy in university departments with a particular emphasis on sustainability issues. The role of industry and government laboratories is also reviewed although primarily for developed countries. The paper also includes comments and suggestions on the future requirements for education and R&D in pyrometallurgy in developed countries to maximise sustainability. It is also suggested that future R&D in pyrometallurgy will be even more concentrated in developing countries – most notably China.

Jan 1, 2014

By Hassan Saalman, Mahmoud Mahmoud, Omneya El Hussaini

The Ferruginous sandstone ore was obtained from Ramlet Hemeyir area, Southwestern Sinai, Egypt, was found to contain 10% rare earth elements (REE). A representative sample has been subjected to sulfuric acid agitation leaching. About 93% of the REE content was released by mixing the ground sample to -100 mesh with concentrated H2SO4 at solid/liquid (S/L) ratio of 1/2 for 5h at a temperature ranged from 250 to 300o C. The REE was precipitated from the prepared sulfate leach liquor of pH 1.0 by adding 35% oxalic acid at 25o C. The precipitation yielded 98% REE. For selective separation of yttrium, the rare earth cake was leached with 31.5% nitric acid. Next, the aqueous solution was contacted with di-(2-ethylhexyl) phosphoric acid (D2EHPA) where 98% yttrium extraction was achieved. Stripping was done with hot H2O (80o C). Finally, a precipitation with oxalic acid was done followed by ignition at 950o C. A yield of 95% yttrium oxide was produced.

Jan 1, 2014

By Xiaofei Guan, Adam C. Powell, Uday B. Pal, Srikanth Gopalan

This paper reports a solid oxide membrane (SOM) electrolysis experiment using an LSM– Inconel inert anode current collector for production of Mg and O2 at 1423K. The electrochemical performance of the SOM cell was evaluated by using various electrochemical techniques including electrochemical impedance spectroscopy, potentiodynamic scans, and potentiostatic electrolysis. The effects of Mg solubility in the flux on the current efficiency and the YSZ membrane stability during SOM electrolysis were discussed and examined through experiment and modeling. The electronic transference number of the flux were measured to assess the Mg dissolution in the flux during SOM electrolysis. A negative correlation between the electronic transference number of the flux and the current efficiency of the SOM electrolysis was observed.

Jan 1, 2014