By W. R. Reed, Y. Zheng

A recent study conducted by the National Institute for Occupational Safety and Health (NIOSH) evaluated the roof bolter canopy air curtain (CAC) systemin a blowing face ventilation system, demonstrating its effectiveness and illustrating the CAC protection zones. This study evaluates the roof bolter machine CAC while operating in an exhausting face ventilation system. This study considers two similar locations to allow comparison with the previous blowing face ventilation (Zheng et al., Min Metal Explor 36(6):1115–1126, (2019)) study: (1) a roof bolter machine bolting the roof at 20 ft (6.1 m) from the face and (2) a roof bolting machine bolting at 4 ft (1.2 m) from the face. The environment introduces 6.0 mg/m3 of respirable dust to represent the roof boltingmachine operating downstreamof the continuous miner. However, the exhausting face ventilation uses an exhaust curtain with 9000 cfm (4.25 m3/s) of air. Two roof bolter machine working positions are simulated with the use of dual drill heads in the inward position for two inside bolts and in the outward position for two outside bolts. The influence of the CAC on airflows and dust dispersion is evaluated with the CAC operating at 250 cfm (0.12 m3/s) with dust reductions ranging from 39.5 to 82.8%. When the roof bolter machine operated close to the face, increasing CAC airflow was required for adequate protection since the dust reductions can be as low as 39.5%. Additional CAC airflows of 350 cfm(0.17 m3/s) and 450 cfm(0.21 m3/s) were evaluated and demonstrated that dust reductions increased to 59.7% (350 cfm) and 72.0% (450 cfm) for the worst location where the roof bolter operators located.

Aug 26, 2020

By James Noll

Total carbon (TC) is sometimes used to measure or characterize diesel particulate matter (DPM) in occupational settings such as underground mines. DPM samples are collected on quartz fiber filters. When using quartz fiber ?lters, adsorption of gas phase organic carbon (OC) has been reported, causing a positive bias in the particulate TC results (adsorption artifact). Most of the data on the sampling artifacts and corrections apply to environmental air sampling, where samples are collected at a much higher filter face velocity and the OC concentrations are generally much lower relative to occupational sampling. In this study, we investigated the effects of adsorption artifact on samples from occupational settings. Samples were collected with and without denuders to determine the amount of gas phase OC collected and the accuracy of certain corrections. In underground stone mines, the adsorption artifact was found to positively bias the particulate TC by greater than 20% for filter loadings below 25 µg/cm2 TC (8-h time weighted average) 262 µg/m3). The tandem ?lter correction reduced the effect of the artifact, as high as 60% of the TC value, to less than 11% for laboratory data. It also significantly reduced the effect of the artifact obtained for field samples.

Jan 1, 2008

By A. Arik

Reliable ore reserve estimates for deposits with highly skewed grade disributions are difficult tasks to perform. Although some recent geostatistical techniques are available to handle problems with these estimations, ordinary kriging or conventional interpolation methods are still widely used to estimate the ore reserves for such deposits. The estimation results can be very sensitive to the search parameters used during the interpolation of grades with these methods. This paper compares the ore reserve estimates from ordinary kriging using several cases in which certain search parameters are varied. The comparisons are extended to different mineralizations to show the changing effects of these parameters.

Jan 1, 1990

By R. L. Setsepu, S. O. Bada, J. Abdulsalam

The utilization of biomass as a solid fuel for co-firing has received great attention from boiler manufacturers as a clean coal technology (CCT) option. This research aimed to produce biocoal pellets, as a clean energy fuel, using hydrochar from trees planted to rehabilitate acid mine drainage (AMD) water and fine coal discards. The hydrochar was synthesized by hydrothermal carbonization of Searsia lancea harvested from AMD-contaminated land at a temperature of 280°C and a residence time of 90 minutes. It was blended with discard coal (–1 mm) at ratios of 25% and 50% hydrochar to produce different forms of solid pelletized biocoal (BC). The physicochemical and mechanical properties of each of the biocoal pellet blends were determined. The 100% hydrochar had the highest calorific value of 29.99 MJ/kg, while the raw discard coal had a calorific value of 16.73 MJ/kg. The ash content decreased from 42% in the discard coal to 25% in the blend of 50% coal and 50% hydrochar biocoal pellets. Biocoal pellets comprising 25% hydrochar and 75% discard coal (BC25 HC/75 COAL) displayed the best mechanical properties (compressive strength 3.06 MPa) of all the fuels, but the physicochemical properties were inferior to the BC50 HC/50 COAL pellets. This research has demonstrated that hydrochar synthesized from a tree species planted for hydraulic control of AMD has the capability to act as a binder for improving the mechanical properties and energy characteristics of fine discard coal.

Dec 1, 2021

By Arash Saeidi Rashk Olia, Dunja Perić

The increasing demand for renewable energy has attracted attention to energy geostructures as means of extracting clean geothermal energy from the ground. To further advance the understanding of soilstructure interaction in energy piles analytical solutions considering the self-weight of the pile were derived. These solutions were then incorporated in recently-derived thermomechanical weightless solutions to provide comprehensive analytical solutions for axial displacement, strain and stress in single energy piles. This was accomplished by comparing responses of energy pile under different loading scenarios that reflect presence and absence of the self-weight. Results of mechanics-based analysis revealed that the self-weight of energy piles embedded in stiff soils has no significant contribution to displacement, strain and stress that develop under thermo-mechanical loads. Overall, the significance of the self-weight contribution depends on the magnitude of thermal load as well as the soil-pile interface stiffness. The stiffness of end restraints imposed to the pile head and tip were also found to play an important role in contribution of self-weight in induced thermomechanical stresses in energy piles.

Oct 1, 2022

By D Reid, A Fourie

The in-pipe treatment of slurries with polymer addition shortly prior to deposition is a noteworthy emerging technology of increasing popularity. Although polymer treatment has been shown to substantially modify and improve depositional and dewatering behaviour in a significant number of cases, the impacts of polymer treatment on geotechnical performance of tailings are less well understood. For example, certain combinations of polymer and slurry type have been shown to result in lower final densities at a given vertical effective stress. Despite these lower densities, polymer-treated tailings often exhibit peak undrained shear strengths consistent with untreated material. However, the sensitivity and/or brittleness of the material may be negatively influenced by the looser state created. Although these changes have been studied, most testing available in the literature was undertaken on relatively ‘fresh’ samples of polymer-treated material. However, significant shear may occur following treatment and prior to the commencement of settling and self-weight consolidation as the material moves down the beach.To study the effects of shearing on the subsequent performance of polymer-treated tailings, a test program consisting of consolidation, triaxial and direct simple shear tests was undertaken on presheared polymer-treated material. Materials used were identical to those used in previously published studies on the impacts of polymer treatment in a ‘fresh’ condition. Shearing of the polymer-treated material generally appeared to lessen the impacts of the polymer treatment process. However, the behaviour of the material when sheared indicated that the polymer was still impacting the behaviour of the material in some respects. The results indicate the importance of the consideration of shearing on material behaviour when planning and designing a tailings deposit where polymer treatment is to be implemented.CITATION:Reid, D and Fourie, A, 2015. Effects of shear on the behaviour of polymer-treated slurries, in Proceedings Tailings and Mine Waste Management for the 21st Century , pp 215–224 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Jul 27, 2015

By Eugene F. Casey, William H. Hansmire, J. Ghaboussi, Randall L. Lentell, Harvey W. Parker

INTRODUCTION Construction of a major intercepting sewer in Brooklyn, New York involved tunneling in soil over several subway lines. In two instances the clearance between the subway and sewer was sufficiently close that concern was raised about the influence of the new construction. Prior to each critical crossing, analytical studies were performed which characterized the tunneling influence. It was demonstrated that with adjustments in construction procedures the crossings could be made without affecting the integrity of the subway linings. A comprehensive program of instrumentation and full-time monitoring was undertaken to ensure that any unforeseen adverse developments during crossing would be recognized. The successful crossings were subsequently made with minimal influence. Reported herein are the special construction conditions for the two crossings, the analytical simulation of behavior, and the results of monitoring on the subway linings. SEWER TUNNEL CONSTRUCTION AND EXISTING SUBWAYS The Red Hook Intercepting Sewer is a 2600 m (8600 ft) long tunnel which is part of a major water pollution control project in New York City. For clarity of nomenclature, the sewer is termed a 'tunnel' while the rapid transit structures are termed 'subways'. For routine construction, the tunnel was mined by hand with a 3.2 m (10 ft-5 in.)

Jan 1, 1981

By Hideo Ando, Yuka Satou, Tatsuya Ishitake

Whole-body vibration occurs when the body is supported on a surface which is vibrating. Occupational exposures to whole-body vibration mainly occurs in the transportation industry, but also in association with other industrial process. Epidemiological studies have frequently indicated an elevated health risk for the spine in workers exposed to whole-body vibration. With regarding to train or bus operators, a fall of drivers’ wakefulness level because of fatigue is often pointed out. This decrease in wakefulness results in an increase of the occurrence of accidents. However, a study of how whole-body vibration affects people's level of wakefulness has not been done. To test the hypothesis that exposure to whole-body vibration has a certain effects on level of wakefulness, the change of a subjective wakefulness level and changes of electroencephalogram (EEG) were observed under experimental exposure to short-term whole-body vibration. Methods Subjects are ten healthy male university students, with an average age of 20.7 ± 1.8 years old, and they are all nonsmokers. Using the equipment (CV-300, AKASHI) of whole-body vibration generator, we consider an exposure environment of actual driver work, so that set the frequency and the acceleration level as 10 Hz and 0.6ms-2 r.m.s.. The subjects were exposed to whole-body vibration in the seated position and exposure time was fixed for 12 minutes. Subjective wakefulness level was evaluated using the questionnaire of VASS (Visual Analog Sleepiness Scale) and KSS (The Kwansei Gakuin Sleepiness Scale). For the electroencephalogram (EEG) measurement, it was equipped with the electrodes based on the International ten-twenty electrode system (C3-A2, O1-A2, O2-A1). EEG activity in the alpha frequency band (8 – 12 Hz) is one of the most typical physiological indicator which represent the transition from wakefulness to sleepiness. AAT (Alpha Attenuation Test) which repeats three times each opened and closed eye for 1 minute was performed in a seating position with directions of the researcher in the beginning, in the middle and in the end of exposure to whole-body vibration. For analysis, power spectral analysis was conducted over the last 6 min of EEG, and wakefulness levels were defined as the ratio of mean alpha power during eyes closed versus eyes opened. The laboratory was kept at room temperature (21 ± 1.0 degrees C), humidity was 50 ± 5%, noise level was 63.6 dB (A) eq, and illumination 510 lx. Each experiment was started around 10:00 am to minimize the effect of biorhythm.

Jan 6, 2006

By P. N. Anyalebechi

The effects of Si (0.19-0.52 wI. %), Fe (0.20 wI. %-0.44 wI. %), and Cr (0-0.10 wI.%) on the response of ingots of aluminum alloy 3004 solidified at different rates (O.IO°C/s to 30°C/s), to homogenization heat treatment have been investigated. Response to homogenization was determined by quantifying the following microstructural parameters: (i) amount of Mn retained in solid solution; (ii) types, relative amounts, sizes, size distributions, shapes, and chemical compositions of second phases; (iii) extent of the alpha-transformation (i.e., AI6(Fe,Mn) --7 (XAI12( Fe,MnhSi) reaction; (iv) dispersoid formation; and (v) alleviation of dendritic microsegregation. Of the three alloying elements investigated, Si had the greatest effect on the response of aluminum alloy 3004 to heat treatment. Increase in Si content, fineness of cast microstructure, and homogenization temperature facilitated alpha-transformation reaction, dissolution of Mg2Si, loss of Mn supersaturation, and formation of AldFe,Mn)3Si and Mg2Si dispersoids.

Jan 1, 2008

This study was conducted to establish the effects of a diesel particulate filter (DPF) system with sintered metal substrate on the concentrations and size distributions of nano and ultrafine aerosols and concentrations of nitric oxides in underground mine air. The study focused on the formation and transformation of nucleation mode particles in mine air under prevailing test conditions. Experimental work was conducted in the NIOSH Diesel Laboratory at the Lake Lynn Laboratory experimental mine, a facility developed to allow evaluation of control technologies directly in underground conditions. The DPF system was examined for four repeatable steady-state engine modes using a naturally aspirated mechanically controlled Isuzu C240 diesel engine fueled with ultralow sulfur fuel. The engine coupled to an eddy-current dynamometer was operated in the underground drift with tightly controlled ventilation. Measurements upwind and downwind of the exhaust system discharge were used to quantify the effects of the DPF system on the mine air. A baseline was established using a standard muffler. The study showed that sintered metal DPF systems reduced the total mass of aerosols in the mine air by more than ten-fold when compared to a muffler. The nucleation mode aerosols (50dem<40 nm) in mine air were found to be strongly influenced by engine operating mode. The concentration of nucleation mode aerosols was found to be significantly higher for high-load modes than for low-load modes. The muffler and DPF system resulted in comparable total nitrogen oxides (NOx) concentrations. However, the nitrogen dioxide (NO2) fraction of the total NOx was found to be substantially higher for both systems for low-load modes than for high-load modes.

Jan 1, 2009

By D. Xie

An in situ gravimetric technique based on wetting and capillary action principles has been used to investigate the wetting and penetration of synthesized alumina samples and commercial magnesia spinel refractories by CaO-SiO2-Al2O3-Fe2O3slags. Synthetic slags of 40CaO-40SiO2-20Al2O3 (in weight per cent) with 0 to 9 weight per cent Fe2O3were used and the experiments were conducted at temperatures 1370 to 1470ºC under argon. The contact time between the sample and the slag was 30 minutes. The results show that the wetting and penetration are enhanced by the iron oxide addition in the slags. Addition of Fe2O3from 0 to 9 weight per cent resulted in a significant increase in the slag penetration into the magnesia spinel refractory by a factor of about 7 and a moderate increase in the synthesized alumina by about 60 per cent. The addition of Fe2O3enhanced the wetting (??cos?, where ? is the surface tension of the slag and the contact angle between the slag and the refractory) by 5 to 18 per cent. An increase in temperature from 1370ºC to 1470ºC resulted in a significant increase in the penetration of a 6 weight per cent Fe2O3slag in the alumina and magnesia samples by a factor of4 to 5 and a decrease in wetting by approximately 30 per cent. Keywords: refractories, slag penetration, wetting.

Jan 1, 2004

By Li Qihou

Mono-disperse ZnS and CdS nano-particles were prepared by the homogenous precipitation method and the effects of SO42-,NO3- and Cl-ions on crystalline of particles were investigated experimentally. The results showed that these anions had no influence on the crystalline of ZnS, but different crystalline CdS ultrafine particles were produced in different anion systems, where the blend-type CdS was obtained from natrate or sulphate solution, and wurtzite-type CdS from chloride solution. It was ascribed to the coordination of Cl- and Cd2+ that altered the supersaturation of precipitate ions in the solution, the existing growth units and their connecting patterns, thereby producing wurtzite-type CdS with a more stable structure.

Jan 1, 2006

By Shaojun Bai

Siderite ore with high phosphorus content was reduced isothermally at 1,050° C with pulverized coal and different dosages of sodium carbonate. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energydispersive analysis of X-rays (EDAX) were used to characterize the samples. The influence of sodium carbonate on the carbothermic reduction process was investigated. Sodium carbonate and its dosage played a considerable role in the carbothermic reduction. The iron particle size in the reduced ore was below 20 µm, and fayalite was abundant without sodium carbonate additive. With a mass ratio of Na2CO3-to-ore of 5% additive, the iron particle size in the reduced ore was generally above 50 µm, and the diffraction intensity associated with metallic iron in the XRD pattern increased. The effect of sodium carbonate on the phase transformation of fluorapatite during carbothermic reduction was also addressed via thermodynamic calculations and aqueous leaching experiments. The results showed that the fluorapatite was not reduced to P2 at 1,050° C, and a portion of the fluorapatite was converted to soluble phosphate. The reduction of siderite can be catalyzed by adding an appropriate amount of sodium carbonate. This catalytic activity was caused by an increase in the reducing reaction activity of FeO and the acceleration of the carbon gasification reactions. The decrease in phosphorous content in the iron concentrate was attributed to an improvement in the separation of the iron phase from the slag phase when sodium carbonate was added and with the formation of soluble phosphate.

By Honggang Zhong, Wei Du, Qijie Zhai, Junjie Sun, Jingzheng Ye

"Effects of pouring temperature and cooling water flux on solidification structure of ferritic stainless steel are investigated with a thermal simulation setup. The results show that with pouring temperatures 1518° C, 1528° C, 1538° C and 1548° C, both Lmean (the mean length between columnar to equiaxed transition(CET) position and chill surface of the samples) and the mean dimension of equiaxed grains increase. On the other hand, with cooling water flux 400, 800, 1200 and 1600mL/min, Lmean gradually increases, and the mean dimension of equiaxed grains decreases. In addition, low pouring temperature and cooling water flux enlarge the ratio of fine equiaxed grains.IntroductionFerritic stainless steel plays an important role in industry products nowadays. Compared with austenitic stainless steel which contains both chromium and nickel, ferritic stainless steel can obtain good corrosion resistance despite the absence of nickel [ 1]. F erritic stainless steel has been widely applied in automotive exhaust systems [2], electrical equipment, construction and chemical industries and also has broad development prospects. At present, continuous casting technique has developed into an important technology applied in iron and steel making. The solidification structure of continuous casting slab has significant influence on the final properties of stainless steel. The developed columnar grains of ferritic stainless steel would result in negative effects on mechanical property [3]. However, fine and homogeneou& equiaxed grains can improve the comprehensive properties of ferritic stainless steel [4] Therefore, it makes great sense to promote the columnar to equiaxed grain transition (CET). Recently Baosteel has developed a new type of Cr-saved ferritic stainless steel, but the effect of continuous casting conditions on its solidification structure is unknown. It is important to investigate the effects of solidification conditions on solidification structure of this new ferritic stainless steel, which can give guidance for optimizing the production process."

Jan 1, 2014

By P. N. Anyalebechi

The effects of solidification rate (0.4-26.1 K/s) and alloying elements on the cast microstructures of aluminum alloy 5182 have been investigated with directionally cooled laboratory-size ingots. The alloying elements examined included Mg (3.6-4.7 wt.%), Mn (0.35-0.75 wt.%), Fe (0.11- 0.42 wt.%), Cu (0.03-0.25 wt.%), and Si (0.11-0.28 wt.%). These reflect the chemical compositions of AA 5182 end stocks with high recycled used beverage container (UBC) content. For a given chemical composition, the average dendrite cell and constituent phase particle size decreased with increase in average solidification rate. In general, within the level investigated, Mg did not have a significant effect on the types, volume fractions, and average sizes of the constituent phase particles. However, increase in Mn, Si, Fe, and Cu increased average sizes and volume fractions of the constituent phase particles.

Jan 1, 2010

By Ralph Harris, Qi Xia

"Gold cyanidation rates are known to be limited by the rate of oxygen dissolution in the cyanidation tanks. The effect of solids loading on the oxygen dissolution rates is not obvious and the results of previous studies are ambiguous. The present paper presents an analysis of oxygen dissolution rates using a ""spent"" commercial gold slurry diluted to various levels of solids loading. It was found, in an 170 litre stirred tank reactor using an inverted cone sparger, that under certain high loading conditions, there was a decrease of as much as 50 %, i.e., there was a halving of the rate of oxygen dissolution as compared to that in clean water. In particular, it was observed that, due to gas flooding of the impeller, there was a drop in kLa even with an increase of gas velocity. Gas holdup reached a maximum value of only 1.7 %. The total power consumption was between 0.06- 0 .10 kw/m3 within the range of gas velocity before flooding occurred. The decrease in oxygen dissolution rate with increased solids loadings is believed to be mainly due to the increase in the apparent viscosity which reduced the turbulence and shearing effect and resulted in larger bubbles and hence reduced the reaction area a. The interrelations between solids loading, gas holdup, flow pattern, power consumption, and liquid mass transfer coefficient are discussed.IntroductionThe reactors generally used in gold cyanidation are Stirred Tank Reactors (STR). Compared with other types of reactors like fluidized bed reactor and column reactor, STR is of particular importance due to its wide application in industry. It is reported that the stirred tank reactor is used for more than 50 % of the world's chemical production (Xu and McGrath, 1996)."

Jan 1, 1997

By M. A. Wei

Effects due to some metal cations, such as Ca2+, Mg2+,Fe2+, Fe3+, Cu+, Cu2+, Zn2+ and Al3+ etc., which are produced in the pulp when the complicated ore is dipped in the deioned water, on the flotation of chalcopyrite and galena with the isopropyl thionocarbamate as collector have been studied. It is found that chalcopyrite floatability is not influenced by these cations, and the cations can be di-vided into three types according to their effects on the purified galena?s floatability with the same conditions, as activator such as Cu+; as depressant such as Al3+, Fe3+, Fe2+, Zn2+ and Cu2+ , unaffective such as Mg2+ and Ca2+.

Jan 1, 2014

By M Olsson, U Nyberg, K Widenberg, P Svedensten, F Ouchterlony

During 2007 and 2008, the project Optimal Fragmentation in Blasting II was conducted at the L&#229;ng&#229;sen quarry of NCC Roads AB near Arlanda. The main goals were:an evaluation of the effect of using electronic delay detonators (EDDs) in quarry blastinga validation of the design curve concept introduced at the V&#228;ndle quarry.Five production blasts were monitored. After a first trial round, the remaining four rounds each had about 100 &#216;89 mm holes in a 14–19 m high bench charged with site mixed emulsions. In rounds 1 and 2, a tighter pattern than normal was used in one half of the rounds, raising the specific charge there from 0.7 to 1.0 kg/m3. Non-electric initiation was used with two holes per 25 ms delay in-row and 67 ms between rows. In rounds 3 and 4, electronic delay detonators were used instead, with 10 and 5 ms in-row delays respectively.The monitoring encompassed drill hole collaring and alignment, in-hole deviations, the rock structure in the bench faces from 3D imaging, first row burdens, etc. Eleven 400 t samples were taken from the muck piles and sorted in the quarry and sieved in the laboratory (lab). The lab data made up a fines tail that was grafted onto the in-pit sorting data to form sieving curves for the test piles. These curves were then compensated for the absence of boulders to construct the sieving curves for the blasted muck pile.These have been used to derive fragmentation model formulas for the non-electric rounds, also called design formulas. They are based on blast geometry, charging data and the properties of the rock mass. The formulas may be used to estimate the effect of changing blasthole pattern, borehole diameter and stemming length for example.The use of EDDs gave several unexpected results. In comparison with non-electric initiated rounds with a somewhat lower specific charge the fragmentation was much coarser; x50 increased from 160 to 200 mm. The effect of raising the specific charge in the non-electric initiated rounds from 0.72 to 0.99 kg/m3 was a much finer fragmentation; x50 decreased from 160 to 120 mm.CITATION:Ouchterlony, F, Nyberg, U, Olsson, M, Widenberg, K and Svedensten, P, 2015. Effects of specific charge and electronic delay detonators on fragmentation in an aggregate quarry – building fragmentation model design curves, in Proceedings 11th International Symposium on Rock Fragmentation by Blasting, pp 727–740 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Aug 24, 2015

By Timothy Barton

The uniaxial compressive strength (UCS) is the most fundamental measurement used in geotechnical rock characterization for mine design. While there are standardized procedures for how to conduct UCS tests, there are no firm guidelines as to when to conduct them. However, it is well known that the strengths of at least some rocks can change during the time between when the core first comes up out of the hole and when it is prepared and tested in the lab. The goal of this NIOSH (National Institute for Occupational Safety and Health) study was to evaluate UCS changes occurring in a broad range of weak coal measure rocks over a one-year time span. The study found the highest moisture contents were measured when the core was fresh, immediately after it was taken from the hole. The specimens then dried rapidly over the next few weeks. Subsequently, sample moisture contents decreased slightly in the winter and increased in the summer in response to the ambient changes in humidity. The measured UCS of the core also changed during the year, apparently in response to changes in the moisture content. The UCS values from the dry, winter months were, on average, 60% higher than the values obtained when the core was fresh, and the summer UCS was approximately 11% lower than the winter UCS. These findings have implications for the use of UCS as an input parameter for both empirical and numerical mine design methods. UCS values of unprotected core tested weeks to months after drilling can be significantly stronger and indicate stronger roof sequences than warranted. In order to obtain the most representative and reliable UCS value, it is necessary to test the core, or wrap and seal it, at the drill site shortly after recovery.

Jan 1, 2008

By Murat Alkan

In this study, a self-propagating high-temperature synthesis (SHS) and following acid leaching techniques were carried out to produce boron carbide (B4C) powder. First, B2O3 was obtained through calcinations of H3BO3 at 1073 K for 2 hours. Then, the glassy B2O3 obtained was crushed and sieved. In the SHS experiments, different amounts of B2O3, Mg and C black were used. The SHS product was obtained in the form of black, spongy solid. In the leaching step, the SHS product was leached in a HCl solution to eliminate the MgO and Mg3B2O6. The effect of acid concentration on the selective leaching was studied at different concentration range, solid/liquid (S/L) ratio, and temperature. The products obtained were characterized by using X-ray diffraction, chemical analysis and SEM techniques.

Jan 1, 2009