Cutter roof failure, a ground control problem that frequently results in massive roof failure, is common in coal mines of the Northern Appala-chian Coal Basin, causing delays in production and posing a safety hazard to mine personnel. The Bureau of Mines is conducting research on the causes of cutter roof failure to gain a basis from which to predict and prevent its occurrence, and to support such roof when failure occurs or is imminent. Research conducted at the Greenwich Collieries North and South Mines, in central Pennsylvania revealed a correlation between the presence of clastic dikes and formation of cutter roof failure. The research con-sisted of in-mine mapping of geologic and deformational features, rock pressure monitoring, core recovery and evaluation, and in situ stress measurement. It was found that roof failure increased in areas where the occurrence of clastic dikes was most frequent, especially where two or more clastic dikes intersect. Staggering of crosscuts prevented the extension of cutters and deterred the occurrence of large falls extending over several break-throughs. In addition, trusses and cribbing were effective in stabilizing clastic dikes and inhibiting the development of cutter roof failure when employed immediately or shortly after mining.

Jan 1, 1987

By G. W. Reimers

Conditions in the underground mine environment can cause self-heating of sulfide ores as a result of exothermic oxidation reactions, which may result in mine fires. This Bureau of Mines report describes thermal analyses of finely ground chalcopyrite, chalcocite, galena, pyrrhotite, marcasite, and arsenopyrite, to characterize their responses under oxidizing conditions. Thermal gravimetric analysis (TGA) and differential thermal analysis (DTA) were used, in the temperature range 1000 to 5000 C. Chalcopyrite showed an initial weight gain, due to formation of sul-fates, a weight loss, caused by ignition of iron sulfide to iron oxide, and a final weight gain, indicating the conversion of copper sulfide to sulfate. Chalcocite did not ignite in the temperature range studied but exhibited a rapid weight gain, because of the rapid conversion of copper sulfide to sulfate. Likewise, galena failed to ignite but underwent a steady weight gain when oxidized in a moist atmosphere, showing conver-sion of lead sulfide to sulfate below the ignition point. Marcasite underwent a rapid weight loss, indicating ignition, at 2000 C. Moisture in the oxidizing atmosphere lowered the ignition point of marcasite and arsenopyrite but not that of pyrrhotite. All the sulfides exhibited exothermic behavior at temperatures below the ignition point.

Jan 1, 1987

By C. W. Smith

The Bureau of Mines conducted laboratory-scale beneficiation tests on a sample of corundum gneiss from Montana to devise a method for beneficiating corundum for use as a substitute for refractory-grade bauxite. A flotation process utilizing petroleum sulfonate as the collector in an acid circuit was devised. Results showed that two flotation schemes each produced a concentrate exceeding the national stockpile specifications for calcined bauxite. From a feed containing 28 pct corundum concentrates containing up to 92.5 pct alumina (A1203) were produced with a corundum recovery of 78.5 pct.

Jan 1, 1987

By K. S. Gritton

The Bureau of Mines investigated the feasibility of numerlcally modeling the sorption of cobalt, a vulnerable strategic and critical metal, from spent copper leach solutions in a multiple-compartment ion-exchange (MCIX) column. Equilibrium resin loadings, cobalt-sorption kinetics, and resin-fluidization characteristics were determined in simple laboratory tests, and a numerical model was developed to predict cobalt extraction and the MCIX-column resin inventory based upon the test results. The model was implemented on a microcomputer to approximate the solution to the set of differential equations that govern model performance. Results compared very well with data from 12 pilot-scale MCIX-column experiments. The average difference between predicted and actual cobalt extractions was 3.2 pct; the maximum difference was 9.3 pet. The actual and predicted resin inventories differed by an average of 5.8 pet, and the maximum difference was 12.0 pct.

Jan 1, 1987

By W. C. Smith

This Bureau of Mines report discusses how pull-test data can help establish polyester resin column length criteria for roof bolts in evaporite minerals. The study evaluates the effectiveness of partial to full columns of resin in anchoring 4-ft, No.6, grade 40 rebar roof bolts in potash, salt, trona, gypsum, and borate mine roofs. Pull tests were performed on over 600 roof bolts in 11 evaporite mines. Column lengths ranging from 6 to 48 in (fully grouted) were evaluated for each test site. In general, comparative results among all test sites indicate that pull-out loads in excess of 10 tons (force) were attained with resin-grouted bolts having 13 to 75 pet less than a full column of polyester resin. Ten tons (force) of load-carrying capability compared favorably, in terms of strength, with the calculated yield strength of the rebar used in the tests, which was 8.8 tons (force). The site-specific nature of each test site, due to the unique combinations of geology, mine-induced stresses, and other unknown parameters, prevented the establishment of valid generic column-length criteria. For these reasons, data to evaluate resin-column-length effectiveness are best obtained on a mine-specific basis.

Jan 1, 1987

By D. A. Larson

This is the second in a series of Bureau of Mines reports which de-scribe experiments designed to devise an efficient, economic mechanical fragmentation technique for hard rock. The previous study described the development of the ripper cutting technique to successfully cut hard rock with 3-to 6-in-wide drag cutters. This study was conducted to test the ripper cutting technique at full scale using 9-in-wide drag cutters. The experiments were conducted with a special test device that cut shallow, 6-by 6-ft openings in 9,200-lbf/in2 compressive-strength concrete blocks. The tests showed that ripper cutting can excavate large-scale openings of the type required by the mining industry at a production rate that outperforms the conventional drill-blast technique. Moreover, the system can produce openings of various sizes and shapes, is simple to oper-ate and maintain, and produces very little dust or noise during operation. The system appears to meet all of the criteria for a successful hard-rock mining machine.

Jan 1, 1987

By J. E. Fraley

This report describes the preliminary results of a Bureau program to develop and test an inexpensive grout for full-column support of roof bolts. Various inorganic grouts were tested in both cartridge and slurry form. Tests were also performed on methods of water packaging and on the effect of fillers on the grout strength. Results showed that some grouts had poor early strength and exceptional mid-to long-term strength. Laboratory tests have shown that rapid-setting inorganic grout could be an economical replacement for resin bolts if the short-term strength could be increased. Further development to improve its early strength would need to be tested in the laboratory and underground to prove its potential for the mining industry.

Jan 1, 1987

By James C. Church

The Bureau of Mines devised and demonstrated a portable linear cutting tester that directly measures and records the in situ cutting forces required of continuous-mining machine picks to it coal in underground mines. It requires only two operators to transport and operate the tester, which can be assembled and operated through a complete test cycle within a single mine work shift. This report reviews the factors considered in the design and development of the tester and the results of its system verification testing at coal mine sites.

Jan 1, 1985

By E. R. Cole

One objective of Bureau of Mines recycling research is to devise technology that enables recovery of metals and minerals from wastes. From October 1982 through September 1985, researchers at the Bureau and at the University of Missouri Rolla (contract H0222002) investigated the use of nonferrous flue dust with varying Zn contents (11 to 66 pct) as a source of Zn for electrogalvanizing steel wire. The waste dusts used were from a secondary Cu smelter, a brass smelter, a Pb smelter, and a water treatment plant. The dusts were leached in H2S04, and the leach solutions were treated to make electrolyte for electrogalvanizing steel wire using soluble Zn anodes. Cyclic voltammetry was used in an inno-vative method to evaluate the quality of the electrolytes used for elec-rogalvanizing. After electrogalvanizing, the wire was drawn on a labo-ratory draw bench to simulate industrial practice. Corrosion resistance was measured by a number of electrochemical techniques and by the stan-dard ASTM salt-spray tests. After successful bench-scale tests, the process was demonstrated in an industrial pilot plant. Results indicate that nonferrous flue dusts can be used as a source of Zn for electro-galvanizing if certain impurities are either partially or completely removed from the starting electrolyte.

Jan 1, 1987

By John E. Pahlman

The Bureau of Mines has conducted research on a dual leaching method that offers the potential for the economic recovery of the silver, as well as of the manganese, contained in some domestic manganiferous silver deposits. The method consists of an initial leach of manganese with aqueous sulfur dioxide (S02) followed first by a neutralization rinse, and then by a second leach with cyanide solution for the extraction of silver. Refractory silver in these ores was either (1) intimately associated with the manganese, (2) chemically resistant to cyanide leaching, or (3) rendered inaccessible to cyanide leach solution by the surrounding manganese mineralization. Less than 10 pct of the silver was extracted when minus 2.5-plus 1.3-cm ore pieces were leached directly with cyanide. However, extractions of 25 to 82 pct of the silver and 65 to 96 pet of the manganese were attained in laboratory column-leach tests using the dual leaching method on equivalent-sized ore pieces from seven domestic deposits.

Jan 1, 1987

By L. S. Sundae

The Bureau of Mines conducted a series of tests to compare the cutting forces required by radial and point-attack bits when making similar cuts. Three radial and four point-attack bits were tested in two coal mines using the Bureau's in-seam tester to measure coal-cutting forces in situ. Tests were also conducted to investigate the effects of weathering and cleating. The test results show that in each case, at a specific clearance angle, the radial bits required less tangential and much less normal force than the point-attack bits. The resultant of the cutting forces for some types of cut was 50 pct less at mine 1 for radial cuts compared to cuts with the best point-attack bit, and 40 pct less at mine 2. There was some difference between three types of radial bits, but it was not as significant as the difference between each type of point-attack bit. Cutting coal perpendicular to the cleat planes required less cutting and normal force than the same type of cuts parallel to the cleat planes. Test results showed no effect due to weathering on cutting force data. Cutting parallel increased forces only because cuts were made in the rock band.

Jan 1, 1987

By D. A. Larson

The Bureau of Mines conducted research to develop preliminary engineering data necessary if the cobalt-rich manganese crusts that occur in the Exclusive Economic Zone (EEZ) of the Hawaiian Archipelago are to be mined. The research was divided into the following sections: (1) physical, mineralogical, and chemical descriptions; (2) mechanical property testing, such as compressive strength, tensile strength, and a rippability index; and (3) mechanical cutting characteristics, including average and peak cutter forces, the specific energy, and cuttings size distribution. Section 1 utilized microscope, X-ray powder diffractometer, and electron microprobe analyses. Section 2 utilized standard mechanical property testing techniques. Section 3 utilized a converted planer mill with full-size coal cutters to fragment the crust and substrate samples. The manganese crust samples were mainly manganese and iron oxides and hydroxides with an average cobalt content of 1 pct and had a nucleus or substrate of rock or sediment. The significant results shown by the mechanical property and cutting tests are that the crust and all but two types of substrates (basalt and trachyte) are weak materials and easily cut with standard drag cutters. The crusts are generally comparable to medium hard coal in strength and in their resistance to cutting.

Jan 1, 1987

By Howard C. Pettibone

Mine safety personnel reported occurrences of excessive "glove-fingering" and other problems with resin-grouted roof bolt installa tions. To study these problems, the Bureau of Mines designed a test plan to (1) obtain baseline information on several resin cartridges and (2) investigate the variables involved in the installation of a resin bolt. Three brands of resin representative of the industry in January 1983 were selected for cartridge evaluation. The installation variables selected for study were the method of installation, the hole depth, and the hole annulus. These variables were studied by installing a series of bolts in concrete blocks using different values for each variable. Results of the research show overspinning the resin may cause problems, but they can be avoided by using the spin times recommended by manufac-turers. Excessive glove-fingering is not a problem if the manufacturer-recommended installation procedures are followed.

Jan 1, 1987

By Elger. G. W.

The Bureau of Mines investigated preheating of continuously fed, fragmented ferrous scrap charges by furnace offgases and utilizing substitutes for imported fluorspar to condition electric steelmaking slags. Three types of continuous scrap charging procedures were investigated to determine electrical energy consumption in a I-st (short ton) electric arc furnace. Cold and preheated scrap charges were continuously fed at rates averaging 37.5 and 43.7lb/min, respectively. The feed rate varied appreciably from test to test owing to hangup of the scrap in the charge bin. Approximately 7 pct less electrical energy was consumed in melting scrap preheated to 8400 to 1,1100 F by furnace off-gases than in melting cold scrap. Overall energy consumptions were 888 kW'h/st for cold scrap, 829 kW'h/st for preheated scrap" and 637 kW'h/st for conventional backcharged scrap. Stack gases from scrap preheating averaged 1200 F and a flow rate of 1,615 scfm compared with 2200 F and 1,302 sefm for cold-charged scrap. Slag conditioners tested included synthetic fluorspar, boric acid, hydroboracite, used aluminum potlining wastes and aluminum anode tailing wastes, and Sorelflux B. The boron-containing conditioners fluidized the slags the best, followed in order by the conditioners containing fluorine and titanium.

Jan 1, 1987

By J. C. Edwards

The Bureau of Mines developed a mathematical model for analysis of the impact of scrubber bed length, porosity, and gas flow rate on the absorption of C02 in a breathing apparatus. The model accounts for the decrease in available absorbent through chemical conversion. The pre-dicted efflux of C02 from a canister containing LiOR compared favorably with measured values reported elsewhere. It was determined from a com-putational study that the time for breakthrough of C02 at a prescribed level is nearly directly proportional to bed length and inversely pro-portional to gas flow and porosity.

Jan 1, 1987

By Davis E. Traut

TiC14, AIC13, and VC14 were coreduced simultaneously via a Kroll-type magnesium reduction to form an alloy sponge as part of a research effort by the Bureau of Mines to produce titanium alloy powder. Reduction tem-peratures of 750°, 850°, and 950° C, a range of chloride feed rates from 34 to 152 Ib/(ft2·h), and crucible diameters of 7-3/4 and 10-1/4 in were tested. Microprobe analyses using a 40-um-diam spot showed no effect on alloy microhomogeneity (distribution of Al and V in the Ti, considered critical as a powder property), due to changes in process variables within these ranges. Statistical analysis of these data for alloy sponge indicated greater variation in the chemical composition (AI and V) than that found in commercial Ti-6Al-4V plate or Plasma Rotating Electrode Process (PREP) powder. Therefore, a one-step approach to pow-der, such as grinding the Ti alloy sponge, would not produce a powder product of acceptable chemical homogeneity. An approach that homoge-nized the sponge, such as with a melting step, would produce an accept-able powder product with respect to chemical homogeneity.

Jan 1, 1987

By Lung Cheng

The Bureau of Mines conducted laboratory tests to investigate the ease of frictional ingition with frozen (nonrotating) conical bits cutting into sandstone. The number of strikes with a new bit to obtain ignition of a combustible methane-air environment was measured. Tests were made with bits tipped with both tungsten carbide and steel at several bit attack angles (angle between bit axis and sandstone surface) and initial tip angles (included angle at the tip of the new bit). Carbide-tipped bits required more strikes for ingition than steel-tipped bits, by a factor of 7 to 10. With a carbide-tipped bit, the number of strikes for ingition increased by a factor of about 3 if the bit attack angle increased by 10° or if the initial tip angle decreased by 10°. During use, abrasive wear of the frozen bit caused a flat surface to form at the tip of the bit, thereby decreasing the tip angle. As the attack angle increased, however, the new bit involved a smaller wear-flat area whereby, abrasive wear was decreased.

Jan 1, 1987

By M. O. Serbousek

The load-transfer mechanics of fully grouted roof bolts in coal mines have been investigated in laboratory and analytical studies. The purpose of this Bureau of Mines research is to increase understanding and better interpret data from routine field pull tests and to develop a numerical model of a grouted bolt that can be used in a global computer model of a mine roof. Analytical studies using closed-form solutions and finite-element techniques were compared to experimental results. Laboratory work includes variation of bolt length, hole diameter, and grouL type. Pull tests were pel'fol·med on 4-, 2-, and I-ft bolts in holes of 1-and I-3IB-in diameters. Both polyester resin and inorganic grouts were used as the anchorage medium. Strain gauges were installed on the bolts at several locations to observe the rate of load transfer from the bolt through the grout to the rock mass when a force was applied at the bolt end using standard jack pull testing procedures and equipment. The average anchorage length of 4-and 2-ft bolts was 22 in. Grout type and hole size variations did not produce a significant effect on the rate of load transfer from the bolt to the rock.

Jan 1, 1987

By R. H. Sprute

The Bureau of Mines conducted a feasibility study and designed an operational system for consolidating waste coal sludge in a 110-acre pond by applying direct current between buried and floating electrodes. Consolidation would reduce the sludge to half its present volume, there-by extending the working life of the pond as well as creating a safe, stable impoundment. The project was conducted by the Bureau under an agreement with the Washington Irrigation and Development Co. (WIDCO), located near Centralia, WA. Part 1 of this report, published as Report of Investigation 8666 in 1982, covers the results of laboratory tests at the Bureau's Spokane Research Center and of a small-scale field test at WIDeO's coal preparation plant. Test results show the process is efficient and cost-effective when power is applied at low current density. Part 2 (this paper) describes a detailed design for an electrokinetic system to dewater WIDCO's 110-acre pond with a 27.4-acre electrode array. Densification of the inactive sludge pond will require 3.6 yr of treatment for a total cost of $1,450,000. The study and design are site specific, but design procedures and analyses are sufficiently detailed to serve as a guide for applying the process to any sludge pond.

Jan 1, 1988

By R. O. Dannenberg

The Bureau of Mines conducted laboratory investigations with the objective of developing an alternative process for recovering cobalt and copper from complex sulfide concentrates. Processes currently used depend largely upon precipitation techniques to remove impurities and recover cobalt from sulfate liquors prepared by oxidative pressure leaching of the sulfide concentrates. The Bureau conducted bench-scale research on a process for treating cobaltite concentrates, comprising (1) oxidative pressure leaching, (2) jarosite precipitation followed by H202 oxidation and pH control to remove iron and arsenic, (3) copper solvent extraction with a mixed hydroxyoxime-amine extractant, (4) copper electrowinning from recirculating acidic strip liquor, (5) selective cobalt extraction from copper solvent extraction raffinate with a phosphinic acid extractant, and (6) electrowinning of cobalt from a recirculating weak acid strip liquor. Overall cobalt and copper recoveries were 91.7 and 84.1 pct, respectively. Electrowon products assayed 99.8 pct Co and 99.89 pct Cu.

Jan 1, 1987