Search Documents

By C. S. Samis, J. C. Mitchell

Sodion activity data have been obtained for the Na-A1 system for sodium concentrations in aluminum between NN, = 25 . 10-and 300 x 10'. This concentration intert-a2 encompasses those sodium concentrations nor1)zally encountered in aluminum reduction cell operation. The sodium activity data were measured by a two-phase equilibration of sodium between a lead and an aluminam rich phase. The Na-Pb system was emplojed as a reference for the determination of the actiz7itj 0.f sodium. The activity of sodiin in aluminuwz exhibits large positi2.e deviations frorn ideality and a strong dependence, on concentration below NN, = 100 x 1K6. The inteated data indicate that the activity of aluminium is equal to its mole fraction over the range of miscibility of the Na-A1 sgstem. The data on the Na-A1 binary have been combined with experimental data on the cryolite-A1 system at 1025°C to obtain the activities of Na F and AlF, in liquid cryolite oz2er the cornposition 1-ange encountered in aluminum cell operation. The results are in agreement with activities calculated from the NaF-AlF, phase diagram. ALUMINUM is produced commercially by the electrolytic reduction of aluminum oxide dissolved in molten cryolite. There is considerable controversy over the actual mechanism of the discharge processes, but sodium potentials in the systems appear to play an important role in the reduction mechanism. The metal-salt reaction involving NaF and aluminum to produce A1F3 and sodium is responsible for the presence of sodium in the aluminum metal phase. Additional sodium may be produced from the simultaneous deposition of sodium and aluminum at the cathode as a result of a cathodic overvoltage. runert' has suggested that sodium gas at atmospheric pressure would be the result of reaction between cryolite and aluminum at 1000°C. Subsequent investigations have shown that production of sodium at atmospheric pressure does not occur. These later investigations can be conveniently separated into two categories. The first involves sodium, aluminum, and cryolite, in which the sodium activity was measured. The second includes a lead phase for sodium activity measurement. Jander and errmann,' studied the reaction: at 1090°C in alumina crucibles under an atmosphere of dry, oxygen-free nitrogen. The equilibrium constant for the reaction was expressed in terms of concentration. Their results in Fig. 1 show an increase in sodium content of the aluminum with increasing NaF/A1F3 weight ratio. Pearson and waddington3 performed similar experiments at 1000°C. Their results are included in Fig. 1. Dewing and ollinshead have measured the sodium content of aluminum as a function of the NF/AF, ratio at 1025"C, Fig. 1, and ewin' measured the sodium content of the aluminum in a system involving the solid reactants NaF, cryolite, and liquid aluminum. This reaction is different from those discussed above. Two solid phases, NaF and Na3A1F6, and a liquid aluminum phase were present. The sodium concentration in the aluminum was determined by the temperature. Dewing's measurements covered the temperature range 679" to 896°C. Omo, Matsushima, and 1t02" investigated the equilibrium 6NaF ential thermal analysis. Stokes and Frank6 determined sodium activities by

Jan 1, 1970

By Thomas C. Wilder, Walter E. Galin

Measurements of the electromotive force of the cell at 995°C have shown that the cell may be used to detennine the zinc content of molten Cu-Zn alloys to the nearest 0.05 wt pct. The cell is used for brass melts to which no ZnO is added intentionally, because essentially all oxygen in the Cu-Zn-O system is present in the form of ZnO. The cell is also used to detev,nine the thernodynamic activity of zinc for Cu-Zn al1oys of the brass composition range, from which the equilibrium partial pressure of zinc for such alloy may also be calculated. The electrochemical measurement of the concentration of the most active metal in other engneering- alloy systems by a similar technique is also considered. IN recent years there have been many studies concerning the direct electrochemical measurement of oxygen content in molten engineering metals.' These investigations employ galvanic cells in which the electrolytes are various solid mixed-oxides which conduct current by movement of oxide ion vacancies under the influence of an oxygen potential gradient. Similar cells have also been used to measure the thermodynamic properties of mixing of solid alloys,' one component of which has a much greater affinity for oxygen than the other component(s). One alloy system of obvious engineering importance comprised of two metals of greatly differing affinity for oxygen is copper-zinc. At the casting temperature of molten brasses, the zinc concentration is very difficult to control not only because its vapor pressure is very high, but also because of its high affinity for oxygen to form ZnO. Inasmuch as brass castings may be required to have a zinc concentration within very narrow limits, it would be advantageous for the brass industry to have a means for quickly measuring the zinc content in the molten alloy just prior to pouring. A calculation based on earlier thermodynamic studies of oxygen and zinc in dilute solution in binary Cu-O and CU-Z' alloys indicates that the oxygen concentration of molten 70 wt pct Cu-30 wt pct Zn brass must be much less than 1 ppm for the separate phase ZnO not to exist in the ternary Cu-Zn-O system. Thus it can be assumed that all molten brasses, both in the laboratory and in the foundry, are sufficiently saturated with oxygen for the separate phase ZnO to be present. In view of the foregoing reasons, the cell investigated at 995°C for the purpose of measuring the zinc concentration in molten copper-zinc alloys, particularly those of brass compositions. In this cell the left hand electrode is a reference electrode comprised of a mixture of the pure powders of nickel and nickel oxide, to which a platinum contact is made. The electrode of interest is a molten Cu-Zn alloy of unknown zinc concentration with a tantalum wire contact. The electrolyte is the commercially available (Zircoa) calcia stabilized zirconia. The ZnO in the Cu-Zn electrode compartment is not intentionally added, but is naturally present as a result of the infinitesimal amount of oxygen required for its formation in this alloy system. In cell [A] nickel oxide is reduced at the cathode where O= represents the electrolyte. At the anode dissolved zinc of the Cu-Zn alloy is oxidized to form ZnO(s) in its standard state Thus the overall reaction is for which the molar free energy change is where 5 is the Faraday equivalent (23,063 cal per v equivalent), is the electromotive force of the cell in volts after correction for the Pt-Ta thermocouple, FOf (ZO) and AFF (NO) are the standard molar free energies of formation of the respective oxides, and a2n is the thermodynamic activity of zinc in the molten Cu-Zn alloy. The reference state of zinc in this case is taken to be the pure liquid. At constant temperature all the terms of Eq. [I] are constant except and azn Thus since all other participants in the electrochemical reaction are in their standard states, the change in the electromotive force of Cell [A] is represented only by a change of the thermodynamic activity of zinc at constant temperature. The zinc concentration is related to the activity by sampling the alloy for chemical analysis after cell measurements are taken. EXPERIMENTAL A typical cell construction is shown in Fig. 1. This and other experimental details were similar to that described earlier with the exception of some minor modifications which are detailed below.

Jan 1, 1970

By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.' Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

By J. Szekely, V. Stanek

Heat and gas flow interactions in nonisothermal packed beds were examined in the paper. A study was made of the response of the system to a step or pulse change in the inlet gas temperature, with a fixed value of the overall pressure drop across the bed. Under these conditions the heat flow and fluid flow transients are coupled because the convective heat transfer rate is alfected by the mass flow rate of the gas which, in turn, for a fixed pressure drop will depend on the temperature profile in the system. The Problem was stated in terms of differential equations, which were integrated numerically. The parameters used in the computation were so chosen to reflect the operation of the stack region of blast furnaces and sinterbeds. The computed results showed that the pressure drop-flou1 relationships and the rate of progress of the temperature fronts (waves) were strongly interrelated and were also markedly affected by variations in particle size and in void fraction. MANY metallurgical processes involve the contact of solid particles with a gas stream in a packed bed arrangement under nonisothermal conditions. Examples are shaft furnaces, regenerators, pebble heaters, and the sinter process. Although the heat and mass transfer aspects of packed bed processing have been extensively studied, the associated flow phenomena and in particular the effects of nonisothermality on the flow, have received little attention to date. :In fact, most of the previous workers considered the flow rate of the carrier gas time invariant and independent of the heat or mass transfer processSzekely and carr2 have shown that the pressure drop-flow relationships in nonisothermal packed beds may be strongly affected by the temperature profile within the system. These authors have devised a method for relating the pressure drop to flow for a given temperature profile. thus providing an extension of the Ergun equation to steady nonisothermal systems. Finally, in a recent paper willmot3 examined the response of regenerators to externally imposed changes in the gas flow rate. Both these investigations were somewhat specialized since, in general, neither the temperature distribution nor the gas flow rate may be regarded as truly independent variables, thus the heat transfer and the fluid flow problems have to be solved simultaneously. The work reported here is divided into two parts: in Part 1 the general formulation is given and a detailed discussion is presented of fixed bed systems. Part is devoted to systems in which a gas and particulate solids are contacted in a counter flow arrangement. FORMULATION Consider a nonisothermal fixed packed bed, extending from through which a gas is flowing. The problem is to develop a relationship between pressure drop and gas flow (with the gas flow being the dependent variable) and to evaluate the rate at which a change in the gas temperature, imposed at the inlet, travels through the system. Let us consider an infinitesimal section of the bed and establish differential heat, mass, and mechanical energy balances over this region. In addition, relationships are needed describing the temperature dependence of gas density (equation of state) and the temperature dependence of viscosity. These may be written as: where c, and are constants. It is noted that in this formulation we neglected any temperature gradients within the solid particles, thus assuming these to be either sufficiently small or of sufficiently high thermal conductivity to meet this condition. The justification and consequences of this assumption will be mentioned in the discussion.

Jan 1, 1970

By M. Marciano, K. Kreider

Silicon carbide coated boron fiber (Borsic) reinforced aluminum composites were made which exhibit strength and modulus values predicted by the rule of mixtures. A successful technique for fabricating these composites consists of plasma spraying of monolayer filament reinforced tapes and subsequent diffusion bonding of these tapes into composites. The elastic properties of the composites were given by the rule of mixtures in reinforced directions. (The modulus parallel to the fibers was 32 x 106 psi for a composite with 50 pct by volume fibers. The other elastic properties for a composite with 50 pct fiber were transverse modulus = 14 to 16 X 10 psi, G = 9.5 x 106psi, and v,, = 0.23. Tensile strengths of over 190,000 psi were measured for the composites with 50 pct fiber and the average strength for these composites was 162,000 psi. These same composites had interlaminar shear strengths of 12 to 15,000 psi. Multidirectionally reinforced composites demonstrated the same reinforcement efficiency in strength and modulus as the uni-directimlly reinforced composites. Comrpessive strengths of composites with 50 pct by volume fiber were found to be greater than 250,000 psi. STRUCTURAL filamentary composite materials are being considered for use where high strength, high modulus, and lightweight materials are required. Metal matrix composites have been considered for use at temperatures ranging from cryogenic (aluminum stainless steel) to 6000°F (plasma sprayed tungsten plus tungsten fiber) and other requirements have been similarly diverse. Metal matrix composites offer high modulus and high strength in unreinforced directions, the ability to be joined by brazing or welding, and greater fracture toughness compared with the more easily fabricated resin matrix composites. This paper deals with the mechanical properties of aluminum boron composites, a system which is being considered for applications where lightweight, high modulus, and high strength are required at temperatures including those above the normal operating temperatures of resin composites. The boron fiber used in this investigation had an average room temperature strength of greater than 400,000 psi, a modulus of 58 x 106 psi, and a density of 0.09 lb per cu in. (2.6 g per cu cm).' The fiber used in the composites had a coating of silicon carbide to retard degrading reactions with the matrix at elevated temperatures. The coated fiber, which is sold commercially as Borsic: has been reported to have excellent resistance to degradation at temperatures up to 600°C in air and in aluminum2 and the same mechanical properties as the standard bare boron fiber. Fabrication of Composites. The composites were diffusion bonded from plasma sprayed monolayer tapes. These tapes were fabricated on a substrate of aluminum alloy foil which is incorporated in the composite matrix. The technique consists of winding a layer of fiber on the foil, and plasma spraying the balance of the matrix alloy over the windings which bonds all of the components together. Advantages of this process include the ability to achieve good fiber spacing, Fig. 1, the formation of a good bond between fiber and matrix (achieved during the plasma spraying), and the adaptability of the process for forming large and complex parts. This is particularly true when used with brazing foil backing which alloys low pressure bonding of the structural shape. PROPERTY EVALUATION TECHNIQUES Tensile test specimens, 5 to 7 in. long with a reduced gage section and ,030 to ,040 in. thick, were cut from composite sheets with a diamond saw. The gage section was .200 in. wide, while the gripped section was .240 in. wide and over 2 in. long in each grip. The standard gage length used was 1 in., however, transverse specimens (i.e., specimens with the fibers oriented 90 deg to the loading axis) were tested without a reduced section. Twelve specimens were also made with a 3-in. gage length but no significant effect of gage length was measured. The tensile test specimens were mounted in a fixture and aligned in friction grips using a 10X microscope. Unbonded foil doublers (0.010-in.-thick aluminum) were used to insure firm gripping with a minimum of damage to the fibers. The test specimens were transferred to the testing machine in a rigid fixture and mounted in the self aligning loading train. Testing was performed using a Tinius Olsen four screw testing machine with a torsion bar LVDT load

Jan 1, 1970

By B. J. Shaw, R. Kossowsky, W. C. Johnston

High purity (99,95) Ni-51 wt pct cr eutectic alloy was unidirectionalty solidified at rates of 0.1 to 8 in. per hr. The resulting material was characterized by large grains, approximately 0.5 mm in cross section and extending through almost the entire length of the specimen, parallel to the growth axis. The eutectic structure of specimens the growth at -1/3 The per hr consisted of a continuous nickel-rich phase and chrome -rich lamellae approximately 2 thick, spaced about apart. Specimens were tested in compression at temperatures ranging from —196 to 850"C over which range the 0.2 pet yield strength dp -creased from 160,000 p si to 35,000psi, respectively. Swaging to 40 pet reduction in area, followed by a 30-min anneal at 1000c to remove residual cold work, increased the 0.2 pet yield to 260,000 psi at -196°C, dropping to 35,000 psi at 850°C. The increase in strength was attributed to a residual cell structure. The strength of the alloy could be rationalized by the simple rule of mixtures if one assumed that additional strength is derived front a size effect characterized by is petch equation IN recent years there has been increasing interest in dispersion and second phase strengthening in materials needed for high-temperature applications. inm role of structure on the mechanical The of such alloys has been well established of such some extent accounted for theoretically. and to of how the strengthening mechanisms due to fibers and lamellae operate has been reduced to its fibers form by the fabrication of composites of strong rods unidirectionally aligned in a From work on tungsten-fiber-reinforced copper, for example, it was established that the "Rule of Mixtures" could explain the strengthening.12 " some what more sophisticated technique for introducing strong fibers into copper matrix was used by Hertzberg strong Kraft3 who unidirectionally solidified the copper-chromium eutectic. The use of unidirectionally fied eutectics has advantages in that there are no matrix-fiber wetting problems and fine fibers are automatically aligned and uniformly fiber However, one Is restricted to a specific volume fraction of the second phase. Nevertheless, even though the volume fraction is fixed, the rod or lamella thickness, , can be varied by controlling the freezing interface velocity. Alternatively, the grown material may be worked down by swaging or rolling. Embury and Fisher, " using this approach, drew down pear lite in iron and studied the mechanical properties iron and that the yield strength, oy, was properties.proportional They that d was the wire diameter. It could be inferred that was also proportional to but the work hardening had to be taken into consideration at the same time. By varying the growth rate of the cadmium-zinc lamellar eutectic, Shaw'1 showed that was proportional to without the introduction of work hardening and suggested that the lamellar interface itself contributed to the strengthening of the composite. In this investigation we have evaluated the mechanical properties of the unidirectionally solidified fec-bec eutectic Ni-Cr. This eutectic was selected because it presented the possibility was selected beca temperature, and high corrosion resistant alloy, and also represented a hard-soft phase combination with two completely different slip systems. Specimens were tested in compression and tension up to 850°C and a detailed study of the micro structure as a function of plastic strain and temperature was carried out by light and electron microscopy. It was shown that the composite strength tested in compression can be accounted for by the simple rule of mixtures if one allows for an additional term representing the effect of Intereprese EXPERIMENTAL PROCEDURE 1) Unidirectional Solidification. Fig. 1 is a schematic drawing of the apparatus used to produce 0.2 in. diam by 12 in. long alloy ingots. The crucible tube is alumina, containing the charge which has been is swaged, or machined to 0.195 in. diam. The lower end of the tube is immersed to 0 .195in in.d iam. The upper end is supported by a 10 mil nichrome wire which lowers the crucible mil nic hr the] wire at a prescribed rate. Surrounding the furnace is a graphite susceptor into which a control thermocouple is inserted. The furnace is insulated with fiberfrax and enclosed in a quartz tube. There is a sliding seal at the bottom around the crucible and one on the top so that an atmosphere may be used for the sample and suscep tor. The power for the furnace is supplied from a 10-kw, 450 kc generator. The skin depth (the skin depth at which the field falls to l/e of its value at the outer surface) for graphite (p = 10 (j-ohm-cm) is 0.1 in. at this fre-

Jan 1, 1970

By Yuri D. Tretyakov, Robert A. Rapp

The stoichiometry ranges ofNiOl+y and LiFe,O,-d were established by high-temperatwe electrochemical meas7rements in a stabilized-zirconia electrolyte cell. The results were consistent with doubly ionized cation vacancies in NiO,+y and interstitial lithium or iron ions in . The defect structure of the ternary ferrite was derived from the consideration of equilibration with respect to oxygen between the solid and the gas phase. The absolute magnitudes of defect concentrations were calculated. Pavtial molar enthalpies of oxygen in the compounds were calculated and interpreted in terms of the enthalpy of defect formation in these crystals. NICKEL oxide (NiO,,?) is a metal-deficient, p-type, extrinsic semiconductor whose properties are consistent with a structural model based on the presence of cation vacancies as the predominant ionic defect at sufficiently high temperatures and oxygen activities. A survey of previously reported conductivity studies and the presentation of some more recent conductivity measurements will be given in a later paper.' The absolute magnitude of the equilibrium vacancy concentration in NiO has been reported from combined conductivity and thermogravimetric data of ' However, disagreement exists concerning the state of ionization of the nickel vacancies in NiO. Some authors3-' have proposed that the predominant defects in NiO are singly ionized nickel vacancies and positive holes (h') formed by the reaction where, accorhng to the notation of Kroger and Vink,6'7 Oq represents an oxygen ion on its normal lattice site. Other authors"27E have proposed that doubly ionized nickel vacancies (V{i ) and positive holes are predominant and are formed by the reaction One purpose of the present investigation was to establish the nature of the predominant defect in NiO,+? as well as its equilibrium concentration and thermo-dynamic properties at elevated temperatures and known oxygen activities. To accomplish this purpose, the coulometric titration of oxygen into and out of NiO was accomplished using a galvanic cell involving the calcia-stabilized zirconia electrolyte. The ternary oxide, lithium ferrite (LiFe50,-6) is ferromagnetic and has the inverse spinel structure LiFe,O,-d Thus, in the ideal stoichiometric XY204 lattice, Fe3 ions occupy one-eighth of the tetrahedral (A) sites, and i' and Fe3' ions share at random one-half of the octahedral (B) sites within the fcc sublattice of oxygen ions.g The structure and thermodynamics of the spinel structures have been comprehensively decribed.'-' A recent compilation of literature for lithium ferrite is also available. 15 Oxygen-excess LiFe50sis not expected to exist because both i' and 17e3& ions are in their highest normal valency states (positive hole formation is not favorable). As will be discussed, equilibration of the ferrite crystal with oxygen of a surrounding gaseous phase will result in the introduction of equilibrium concentrations of ionic and electronic defects. In the Results and Discussion section a defect model for LiFe50,-d is proposed. This defect model is tested by high-temperature coulometric titration experiments. EXPERIMENT The oxygen activities in nonstoichiometric NiOl+, (and also LiFe,O,-d) were measured by means of coulometric titration with the high-temperature galvanic cell The critical characteristic of a suitable experimental cell is the complete isolation of the phase to be investigated in a minimum sized chamber which is free from extraneous sources and sinks for oxygen (leakage). Then oxygen is only admitted to the chamber or removed from it in known amounts by coulometric titration, which involves the passage of oxygen ions through the solid electrolyte with electrochemical oxidation and reduction reactions at the platinum contacts to the electrolyte. The experimental cell is shown in Fig. 1. The cap of the cell was the tip from a closed-end alumina tube, which was found to be leak-free from a helium leak-detector test. This alumina cap was about 1.2 cm OD and about 1.5 cm high. A Zircoa calcia-stabilized zirconia tablet (crucible lid) of 1.5 cm diam and 0.3 cm thickness served as the solid electrolyte. A Pyrex ring of about 0.1 cm thickness was placed between the electrolyte and the cap. The electrolyte tablet was painted with platinum paste on the entire outer face and on that part of the inner face which would be within the enclosure; these electrodes were further prepared by heating in air at 1000°C for 2 hr. Nickel oxide powder, listed as 99.999 pct pure, was purchased from Leico Industries, Inc. Pills of the NiO were cold-pressed and sintered at 1050°C for 3 hr in a platinum crucible. This poorly sintered NiO was crushed, and chunks were wrapped in 52-mesh Pt gauze (to catalyze the solid-gas exchange) for place-

Jan 1, 1970

By B. S. Hickman

Using primarily quantitative single crystal X-ray techniques studies have been made of the precipitation of the metastable w phase in alloys of titanium with Mo, Mn, Fe, Cr, and Nb. It is shown that, in agreement with earlier work on the Ti-V system, the composition of the w phase during aging approaches a constant; the value varies from one system to another in a systematic manner with the electron concentmtion. Results relevant to the mechanism of w precipitation during quenching and during aging are presented and discussed. Results are presented to confirm that the w phase is coherent and the nzorphology of the Necipitates is described and discussed. PRECIPITATION of the metastable w phase in alloys of titanium is of interest because of its severe embrittling effect and also because of the enhancement of the superconducting properties which accompanies precipitation.1 The general features of w phase precipitation have been discussed by cuillan and by Bagaratskii et d3 The work described in this paper forms part of a general study of w phase precipitation which was undertaken to elucidate various unknown or controversial features of the process, namely: i) What is the mechanism of formation of the phase ii) How does its composition, morphology, volume fraction, and particle size vary with the type and content of the alloying element and with the heat treatment conditions? iii) What is the relation between the w phase and the equilibrium a phase? In a previous paper4 the results of a detailed study of w phase in Ti-V alloys were presented. It was shown that: U During aging the composition of the w phase approached a saturation value of 13.5 to 14.0 at. pct V. ii) w precipitated as cube shaped particles and once precipitation was complete, particle coarsening did not occur. iii) a phase formed initially by direct conversion of w-phase precipitates. In this paper similar measurements are reported on Ti-Mo alloys and some more limited data given on the Ti-Cr, Ti-Fe, Ti-Mn, and Ti-Nb systems. The results i.1 the six systems are then compared. It has been shown previously by electron microscopy that the w precipitates as ellipsoids in both the Ti-Nb system,&apos; and in i-o.&apos; Blackburn and williamsz3 have reported the precipitates in Ti-Fe, Ti-Cr, and Ti-Mn are cubic, i.e., similar to the Ti-V system.476 EXPERIMENTAL METHODS 1) Specimen Preparation. Samples of the compositions shown in Table I were prepared by arc melting. High purity electron beam zone refined titanium (Materials Research Corporation Grade I—total impurity content =250 ppm) was used; the other source materials are given in the table. A commercial Ti-8 wt pct Mn alloy was used for studies of this system. After homogenization the materials were rolled or cut into strip approximately 1/4 in. by 2 in.; the strip was then heated at temperatures of 1200" to 1300°C for several hours by passage of a direct current through the strip in an ultra high vacuum system (<10-torr) and then quenched by admitting high purity helium and switching off the current. This treatment resulted in crystals up to 2 in. by 2 in. by A in., almost all of which had a [100] direction nearly perpendicular to the plane of the strip. The crystals were cut from the strip by spark machining and their composition checked by lattice parameter measurements supported by chemical analysis. 2) X-Ray Diffraction Methods. Lattice parameter measurements were made using a modification of the single crystal spectrometer described by ond. In this technique the crystal angles for reflection on either side of a highly collimated primary beam are measured. Generally the 400 CuK, or the 400 CuKp reflections of the bcc lattice were used. In the as-quenched crystals a precision of 1 in 105 was obtained, but due to line broadening the parameters in aged materials could only be measured to 1 in lo4. This accuracy was, however, quite adequate for the purposes of these experiments and enabled the composition of the p phase to be obtained to 10.1 pct in all systems except Ti-Nb where the lattice parameter change with composition is very small. The precipitation and growth of the w phase was examined using a single crystal goniometer attached to a Phillips diffractometer. The relative intensities and line shapes of b-phase and w-phase reflections

Jan 1, 1970

By J. Szekely, J. W. Evans

A formulation is given for radiant heat loss from the surface of molten steel held in a ladle and numerical solutions are presented for the resultant integrodif-ferential equations. The results are shown on plots of the net rate of heat loss against time, with the geometlry, emissivities, thermal properties of the walls, and Preheat as parameters. It was found that the rate of the vadiant heat loss from the exposed metal surface was comparable to the conductive losses from the Portion of the metal in direct contact with the walls. The radiant heat loss was markedly affected by the geometry and by the thermal properties of the walls the net radiant heat loss from the steel could be drastically reduced by providing a top cover and also by the provision of preheat. The results of this work are thought to be relevant to heat loss calculatious concerned with vacuum degassing and with operatzons in which molten metals are held in ladles. WhEN molten steel is held or transferred in ladles heat losses inevitably occur. The accurate assessment of these heat losses is of importance in process design considerations, as the temperature of the metal may have to meet rigid specifications in certain stages of the processing sequence. As shown in Fig. 1, the principal mechanisms responsible for heat loss are: i) Conduction into the walls and ii) Thermal radation from the top metal surface (possibly augmented by natural convection) The conductive heat loss may be readily calculated as much information is available in the literature on both the general theory1&apos;&apos; and on its particular applications to ladle heat loss calculations. Evaluation of the radiant component of the heat loss is less straight-forward. In two recent papers it has been shown that the presence of a slag layer 2 to 3 in. thick would prevent any significant heat loss for periods up to an hour,5&apos;" however, should bare metal be exposed, constituting the radiant surface, substantial heat losses could occur. This latter case is of considerable practical interest in various degassing operations and in the vacuum processing of certain specialty steels, where the top surface of the metal is not covered by a protective slag layer. Under these conditions a substantial radiant flux is emitted by the top metal surface; part of this flux leaves the system, part of it falls in the ladle walls. The radiant flux incident on the ladle walls is in part absorbed and conducted away, and in part reflected and re radiated. The purpose of the paper is to present a general formulation of the problem, the resultant solution of which should enable computation of the net radiant heat loss from the metal surface. The principal variables, the effect of which will be investigated, include initial metal temperature, geometry, thermal and radiative properties of the wall, and various modes of preheat. FORMULATION Consider a cylindrical enclosure, shown in Fig. 2, with a diameter D, height H, and wall thickness W, the cover at the top of the cylinder having a wall thickness L. If the temperature of the base (representing the top surface of the metal) is kept constant, say, Tb, the problem is to calculate the net rate of heat loss from the base as a function of time, geometry, the initial temperature distribution, and the thermal properties of the system. As customary, the formulation will consist of the mathematical statement of the conservation of thermal energy within the system.

Jan 1, 1970

Jan 1, 1970

By K. M. Kolobova, E. Z. Kurmayev, A. Z. Menshikov, S. A. Nemnonov, V. A. Trapeznikov

The present work represents a review of our intestigations into the X-ray spectra of solids, which have been carried out by us along two lines of upproach: 1) St@ of the electronic structure of high -rnelting compounds of transition metals; 2) stzddy of the interatomic binding forces by the fine structure of absorption spectra under varying temperature and concentration conditions. With this in mind, int>estigations hare been made into the emission and absorption spectra of the K-series of atoms of transition elements in alloys and compounds. In the problem concerned with the electronic structure of high-melting compounds of transition metals, considerable importance is attached to the question of ascertaining the role played by 3d4sp electrons of metal and 2p electrons of metalloid in the formation of chemical bonds and of giving, on the strength of this data, an explanation of the properties which seem to be contradictory at first sight: good conductivity inherent in metals and high brittleness and high-melting characteristics typical of covalent compounds. Over the last few decades this question has attracted the attention of many investigators whose studies were devoted to this type of compound. Many works, both of theoretical1-3 and experimental4- l5 nature , have contributed much to the elucidation of the physical character of the phenomenon referred to. Alongside the investigations in the field of electric resistance, Hall effect, paramagnetic susceptibility, electronic heat capacity, and the temperature of transformation into a superconducting state, we should particularly emphasize the studies on X-ray spectra, which have played a significant role in the development of the zonal theory for high-melting compounds. This fact has become highly evident after the theoretical calculation of the energy spectrum has been made and the density of states curve in Tic, TiN, and Ti0 has been plotted by Ern and Switendick3 who used the method of augmented plane waves. Correlation of the results of the theoretical calculation of the band structure in the compounds listed above with the data obtained by X-ray spectroscopy studies showed that X-ray spectra can be a source of valuable information on the electronic structure of high-melting compounds within a wide range of ener- gies. It is well known that X-ray emission spectra basically give a direct picture of the occupied excited states above the Fermi level of a solid (valence band, conduction band) and that the absorption spectra (region of initial absorption) give a similar picture of states corresponding to the unoccupied levels near the Fermi surface. Full information on the density distribution of electronic states by energies can be obtained by combining the emission and absorption spectra. Such an opportunity arises from investigation

Jan 1, 1970

By S. Leber, R. F. Hehemann

Diffusion coefficients for the Cb-W system were measured using couples prepared from poly crystalline, commercially pure metals. The diffusion coefficients, measured in the temperature range between 1700° and 2300°C, decreased exponentially as the tungsten concentration was increased from 0 to 50 at. pct, then decreased abruptly at higher concentrations. A decrease of two orders of magnitude was observed over the entin? compositional range. The diffusion coefficients were in the range defined by the self-difiusion coefficients of the individual elements, indicating their general validity. An activation energy of 60,500 cal per mole was measured for the 20 pct W composition. Such low values, when compared with energies over 100,000 cal per mole for the pure constituent elements, indicated that transport mechanisnzs more rapid than volume diffusion were contributing substantially to inter dijfusion. Difference should, therefore, be expected between these data and the intrinsic diffusion coefficients. These differences should be significant in the kinetics of &apos;transport phenomena in practical systems. CONSIDERABLE attention has been devoted in recent years to the mechanical behavior and other properties of the refractory metals and their alloys. The Cb-W system has been of special interest as a base for the development of more complex compositions of commercial interest. In spite of the importance of mass transport to all aspects of elevated-temperature behavior, and especially to the production of alloys by powder-metallurgy techniques, little attention has been paid to diffusion in the Cb-W system. Results from a previous study of this system1 appeared to be anomalously high. The present investigation is, therefore, an attempt to obtain more accurate diffusion coefficients in this system. Intrinsic diffusion coefficients, of primary importance from the theoretical viewpoint, can only be obtained accurately from studies utilizing compositional gradients approaching zero. However, many practical problems involve diffusion under significant concentration gradients. The diffusion coefficients determined in this investigation were, therefore, obtained from couples prepared from elemental metals. The data obtained should be of value in the analysis of problems such as homogenization during powder-metallurgy alloying or reactions between base and clad in coated structures. In this vein, the investigation was conducted on poly crystalline materials of commercial purity. PROCEDURE Diffusion couples were prepared by sandwiching a columbium sheet between two sheets of tungsten. The composite was welded around all edges, the tungsten forming a protective can for the columbium. The composite was soaked for 4 min at 1600°C in a hydrogen-atmosphere furnace, quickly forged to 40 pct reduction in thickness, and then rapidly cooled to room tempera-

Jan 1, 1967

By G. Y. Chin, M. T. Dolan, W. L. Mammel

In the case of plastic deformation by slip, von Mises&apos; showed that an arbitrary shape change of a crystal generally requires the activation of five independent slip systems. The selection of the five active systems was worked out by Taylor ,&apos; who hypothesized that, among all combinations of equivalent slip systems which are capable of accommodating a given imposed strain, the active combination is that one for which the sum of the absolute values of the glide shears is a minimum. Taylor analyzed the case of {lll}( 110) slip for fcc metals and applied the analysis to crystals undergoing axisymmetric flow, which approximates the shape change of an embedded grain in a polycrystalline aggregate deformed in tension (or compression). For the twelve equivalent (111) (110) slip systems, there are 384 independent combinations of five slip systems that satisfy the imposed strain.&apos; Taylor laboriously calculated the value of M = ZjIyj /E for each combination (although some were missed) and obtained the minimum M, hence the active combination, for a number of axial orientations distributed throughout the stereographic triangle. (yj is shear from slip on the th system and e is the tensile strain). Detailed contours of constant minimum M were recently obtained by Hosford and Backofen using a simplified but equivalent Bishop and ill&apos; analysis. Due to the numerous combinations of slip systems involved in the calculations, however, the full potential of the powerful Taylor analysis has not been exploited. For this reason, we have recently utilized techniques of linear programming to obtain solutions of the Taylor analysis for axisymmetric flow, for slip on {110)(< 111), {112)(111), and {123)(111) systems as well as mixed slip composed of these three systems. These slip modes are of obvious importance in the deformation of bcc crystals. Some of the salient results are summarized below. 1) Stress-Strain Data for Polycrystal. The value of M averaged over all axial orientations is the ratio of the tensile flow strength of a randomly oriented aggregate to the critical resolved shear stress for slip. This value enters importantly in theoretical deductions of the polycrystalline stress-strain curve from single-crystal data.2&apos;3&apos;5 Table I lists the values of Ma,, for the several cases of slip, as obtained by the present computer work. 2) Texture Hardening. Since the value of M depends on the axial orientation, the (tensile) flow strength of a specimen may be increased through texture control.&apos; An example of the computer results is shown in Fig. 1, where contours of minimum M have been computer-plotted for the case of mixed slip on {110}(111), {112)(111),and {123}(11 1) systems. It may be seen that, under axisymmetric flow, wires of (111) and (110) axial orientations are 50 pct stronger than those oriented at (100) .

Jan 1, 1968

By D. G. Westlake

Levine has concluded that prismatic slip in titanium is controlled by two distinct thermally activated processes in the temperature ranges O° to 220°K and 220" to 300°K. We feel that his evidence is not convincing. He has drawn a curve through the plot of activation volume u* vs temperature T with a break at 22WK, Fig. 2. We believe that considering the possible experimental error apd the fact that there are only four points between 4° and 196°K, one could be justified to represent these points by the smooth curve we show as a solid line in Fig. 12. Levine believes that (8rf/aT)+ is discontinuous at 220°K, but he hints that he recognizes the possible doubt. We doubt seriously that the results shown in Fig. 1 indicate a discontinuity at 220°K. Certainly if he were justified in drawing a straight line through only four points on Fig. 2, we are even more justified in drawing straight lines through the seven points between 77" and 297°K on Figs. 1 and 3, because a straight line touches all seven of his circles. If his measurements of t were so precise that his decision to draw two curves in Fig. 3 is valid, then the experimental technique is deserving of further mention. We have drawn a smooth curve through the results in Fig. 3 and used this and the curve in Fig. 12 to obtain the values of shown in Fig. 13. Finding continuous is a contradiction of Fig. 4, which deserves comment itself. Levine obtained the solid circles in Fig. 4 using Fig. 2 and a smooth curve through the points shown in Fig. 3. We have replotted these solid circles in Fig. 14. We submit that there is no basis for his two straight lines (dashed in Fig. 14), and therefore have superimposed the curve that we believe is indicated. Certainly, there is reasonable doubt that a discontinuity in dH/dT exists at 220°K, even when one accepts Fig, 2. Furthermore, if one draws the straight lines indicated by least-squares treatments of the results presented as open circles in Fig. 4, their intersection is at about 196°K, not at 220°K as shown. Thus the alleged agreement between Figs. 3 and 4 with respect to "break" temperatures is not apparent. In Fig. 9, Levine has drawn a straight line very much different from the one indicated by a least-squares treatment. Obviously, he has done this because he recognized that H = 0 when T = 0. He is consistent in drawing the low-temperature curves in

Jan 1, 1968

By P. Marier, T. R. Ingraham

When cylindrical powder compacts of nickelous oxide (NiO) are heated in an equilibrated stream of SO3, SO,, and 02, in the temperature range 500°to 800°c, tlickelous suljate (NiSO4) is formed as an adherent layer on the oxide. The reaction is diffusion-controlled, with an activation energy of 13 ± 3 kcal per mole. When cylindrical powder compacts of NiSO4 are heated in a stream of dry nitrogen in the temperature range 1000 0to 11500C, NiO is formed at a well-defined interface between the sulfate and oxide. The interjhce migrates into the sulfate at a constant rate at a constant temperature and gas flow. The reaction rate increases with increasing gas flow and decreases with increasing partial pressure of SO3 in the gas stream. Resolution of the partial-pressure data with a Lang-itzliir Adsorption Isothern suggests that about 80 pct of the NiO interface is covered with SO3. The heat of adsovption is about 68 kcal per mole. The activation energy of the decomposition process is 61 ± 3 kcal per mole. MOST of the work reported on the formation and decomposition of nickel sulfate is related to thermodynamics.1-3 No quantitative work has been reported on the decomposition process. The only kinetic work reported on the formation is that by Fletcher and shelef.4-6 whose main purpose was to study the effects of alkali metal sulfate additions on increasing the rate of nickel sulfate formation. They found that, in the absence of an additive, only small amounts of sulfate were formed and the kinetic data were difficult to interpret. However, they suggested that the sulfa-tion of nickel oxide is a diffusion-controlled process for which the activation energy is approximately 17 kcal per mole.6 In this paper, both the formation and decomposition reactions will be examined; and based on the effects of temperature, flow rate, interfacial area, and partial-pressure of sulfur trioxide, mechanisms and activation energies will be suggested for both processes. EXPERIMENTAL Material. The nickel source material used in all experiments was Baker and Adamson Reagent Grade NiSO4. 6H2O, for which the following analysis was supplied by the manufacturer: C1, 0.001 pct; NO3, 0.005 pct; Co, 0.02 pct; Cu, 0.005 pct; Pb, 0.002 pct; Fe, 0.001 pct: insol, 0.005 pct. The anhydrous sulfate was prepared by heating the hydrate at 420°C in a muffle furnace for 5 hr. Nickel oxide was prepared by decomposing the sulfate at 950°C over a period of 10 hr. Method. The technique used for measuring the rates of formation and decomposition was developed earlier in these laboratories.7-8 The method is based on the observation that the kinetic parameters of a reaction can be established in a flow system, with specimens prepared by compacting powder to a uniform pellet shape. The results are identical with those established with solid polycrystalline specimens or single

Jan 1, 1967

By B. W. Roberts, V. A. Phillips

A copper alloy containing- 25.5 at, pct Zn and 19.0 at. pct Ni, which was previously found to show an anoma1old.s hardening effect on quenching- from 600 "C and aging- at 400oc, has now been examined by neutron diffraction. No evidence of long-range order was found. The aged sample showed diffuse scattering- consistent with clustering. The anomalous hardening effect is now attributed to lattice strains caused by clustering rather than (long-range) order hardening. SOLID-solution Cu-Ni-Zn alloys (the commercial &apos;nickel silvers") have been reported to show anomalies in: change of resistivity on cold working,1-6 temperature coefficient of resistance,2-12 resistivity at low temperatures,13,14 parameter (vs temperature),2"4 calorimetric data,2,4 specific heat,15,16 dilation,2-4 and elastic modulus.17 The structure responsible for the anomalies is produced by annealing typically near 400°C and is rather loosely referred to as the (&apos;K-Zustands" (K state), a term coined by Thomas1&apos; who apparently meant simply that the arrangement of atoms on the sites deviated from that expected statistically. Thomas proposed that the K state occurred in a variety of (solid-solution) alloys such as Cu-Ni-Zn, Ni-Cr, Ni-A1, Ni-Cu, Fe-A1, and Fe-Si and is recognized because its formation is strongly temperature-dependent and results in an increase in electrical resistance which can then be decreased by cold working. Later workers on (&apos;nickel silver" have interpreted the K state variously as short-range order, long-range order. or a combination. The present work was prompted by the discovery by Phillips and Jones19 of a substantial hardening effect when an 18 pct "nickel silver" alloy which is fairly close to the Cu2NiZn composition, was reheated in the range 150" to 450 C after previously quenching from 600°C or, alternatively. was slow-cooled from 600°C or above. The phenomenon was attributed to (long-range) order hardening. Due to the similarity in the atomic scattering factors of copper. nickel, and zinc atoms, the &apos;&apos;nickel silvers" are unfavorable for X-ray diffraction studies aimed at detecting ordering. Nevertheless Bialas et a1.,20 using a powder sample containing 47.96 wt pct Cu, 24.03 wt pct Ni, and 27.98 wt pct Zn, slow-cooled from 400" to 200°C taking 500 hr, observed weak super lattice lines. Further unpublished work" using an anomalous dispersion X-ray technique indicates that zinc atoms are regularly ordered at the corner points of the lattice cell, while the nickel and copper atoms are statistically distributed on the remaining sites. Köster 17 also observed X-ray superlattice lines, for example, in an alloy containing 43.5 wt pct Cu, 28.6 wt pct Ni, and 27.9 wt pct Zn superimposed on the basic fcc cell with a = 3.62 kX. He proposed a Cu3Au-type superlattice with the Ll2 structure in which the A sites were statistically occupied by copper and nickel atoms and the B sites by zinc. He adds that substitution must be possible so that zinc atoms partly occupy A sites. Below about 35 pct Cu, Koster had some evidence for a CuAu-type superlattice with the Llo tetragonal fcc structure with a = 3.82 kX, c/a = 0.88 which could be preserved by quenching. This is suggested17722 to correspond to CuNiZn. While the present work was in progress Hirabaya-shi et a1.23 made an independent comprehensive neutron-diffraction study of a single crystal containing 50.05 at. pct Cu, 26.57 at. pct Ni, 0.25 at. pct Mn, 0.13 at. pct Fe, balance zinc. The presence of manganese and iron is surprising since the crystal was supposedly grown from high-purity metals. The homogenized crystal showed evidence of long-range ordering after an anneal of 5 months at about 300°C. Three possible crystal models were proposed. A curious feature of their results23 is that they could not find any neutron-diffraction evidence of ordering in a powdered polycrystalline near-stoichiometric Cu2NiZn alloy. There appears to be some essential difference between a near-stoichiometric Cu2NiZn alloy and one somewhat further off stoichiometry as used by the present authors. Thus Sato14 was able to reproduce the low-temperature resistivity anomaly reported by one of the authors13 on the present alloy if he used a similar composition, but found the normal behavior of the residual resistivity in a near-stoichiometric alloy. satol2 found that the resistivity of a cold-drawn slightly off-stoichiometric alloy increased to a maximum on isothermally annealing at 300°C and then decreased ("over-aged"). Since he could not explain this on the basis of ordering phenomenon, he proposed that zinc atoms were segregating to stacking faults (Suzuki effect) and found etching bands on the surface by replication which were attributed to the widening of faults. Sato suggested14 that the hardening effect observed by Phillips and Jones19 is partly due to the Suzuki effect. EXPERIMENTAL The starting material was 1/4-in.-diam hard-drawn rod of a commercial 18 pct "nickel silver" alloy identical with that used in a previous study by Phillips

Jan 1, 1967

By Y. H. Liu, G. W. Powell

Thin foils made from the gold-rich region of- short (0.15 mm)Au-Ag diffusion couples annealed at 880°C for 1 hr were examined in ax electron microscope and the structures were compared with that of pure gold subjected to identical heat treatments. The couples underwent Plastic deformation (bending) during the diffusional anneal. The foils prepared from the diffusion zone have a higher dislocation density and incidence of subboundaries than pure gold. The plastic bending of the couple can be interpreted in terms of the climb of edge dislocations, which are pavallel to the bend axis, along the direction of diffusion. THE interaction of lattice defects during interdiffu-sion between two metals has been considered by several investigators. In particular, da Silva and Mehl,1 Barnes,&apos; and Bardeen and Herring3 have proposed models based on interactions between point and line defects to account for the Kirkendall effect (marker movement). Each of these models is based on dislocation climb, which can either add or remove lattice planes, induced by an under- or supersaturation of vacancies. A theoretical treatment of the nucleation and growth of voids by the condensation of vacancies has been presented by Seitz.4 Stresses can arise in a binary diffusion couple as a result of the vacancy flux and the gradient in the lattice parameter. rinkmman&apos; has investigated the effects of diffusion-induced stresses on void formation; the results of his analysis suggest that voids can form and grow under the influence of these stresses in the absence of an excess vacancy concentration. The relationships between vacancy supersaturation and diffusion-induced stresses and void formation have been elucidated also by Balluffi and seigle6 who concluded that the stress generated by a vacancy supersaturation aids the growth of voids. Experimental evidence which indirectly shows that stresses are produced by chemical diffusion has been obtained by several researchers.2,7-9 This evidence consists in part of the observation by light microscopy of the formation of subgrains, a process characteristic of the high-temperature deformation of some metals during creep.&apos;0 More striking, however, is the plastic bending of short (0.2 mm) Cu-Ni couples observed by Barnes2 and of boron-doped silicon crystals reported by Queisser.9 Diffusion-induced dislocations in iron and silicon have been investigated by Ainslie et a1.11and Schwutte and Queisser,12 respectively, the former using transmission electron microscopy and the latter an X-ray transmission technique. Matthews and Crawford13 observed the formation of boundaries by the climb of interfacial misfit dislocations in thin, vapor-deposited Au-Pd couples diffused in situ in an electron microscope. In order to obtain additional information on the phenomena associated with defect interaction and diffusion-induced stresses in binary couples, an electron transmission study of foils prepared from the diffusion zone of short Au-Ag couples was undertaken. The initial objective was to investigate the processes occurring at various points of the diffusion zone. Subsequent research demonstrated that foils could be prepared only from the gold-rich region of the diffusion zone using the technique described herein. EXPERIMENTAL PROCEDURE Preparation and Annealing of the Diffusion Couples. The couples were made from annealed, high-purity (99.999 pct). polycrvstalline gold and silver sheets (0.075 mm thick). Shall (0.075 by 5 by 17 mm) elec-tropolished coupons of gold and silver were pressure-bonded by heating the two metals in a graphite device to 770°C and holding at this temperature for approximately 30 min. The quality of the bond was ascertained by metallographic examination at 150 times. Each couple subsequently was annealed at 880°C for 1hr; under these conditions, the extreme portions of the

Jan 1, 1968

By A. Hellawell

Specitlrens of the Al-Ge eutectic alloy have been frozen unidivectionally at rates between 2.5 x 10-6 and 2.5 x 10-4 cm per sec and the structure examined by optical and X-ray methods. There is no epitaxial relationship between phases, the aluminum having random orientation and the germanium a preferred (011) fiber textuve. Lamellar colonies which are BINARY eutectic alloys occur between either silicon or germanium with the metals aluminum or silver. common in this alloy are constructed from axial and nonaxial (111) plates of germanium which are related by a variety of twin configurations. Irregular or globular regions of the microstructure are composed of continuous single crystals of each phase, the germanium being heavily twinned. There is limited solid solubility in these systems, and the eutectic phases all involve diamond cubic with fcc crystal structures. In the microstructures of these eutectic mixtures the silicon and germanium crystals exhibit an almost infinite variety of shapes which are notably sensitive to

Jan 1, 1968

By B. C. Allen

The solubility of chromium in liquid silver and that of molybdenum and tungsten in liquid tin have been determined by equilibrating Ike Liquid in a crucible of the solule metal. Generally the weight of solute in solulion was delermined both chemically and from crucible weight losses. The resulting weight percent solubilily of chromium in silver as a function of absolule temperature T is given by log w = -6660/T + 4.02 in the range 960° to 1445°C, and that of molybdenlttrl in tin by log w = —5050/T + 1. 79 in the range 1200° to 2200°C. The values appear unaffected by minor changes in solute composition. Calculations aye made of the parlial molar heal and excess entropy of mixing. The estimated solubility of tungsten in tin is 0.001 pct at 2000°C. Evidence is presented that molybdenwm dissolves in tin without compound for mation and that tungsten and tin form W10Sn. RECENT developments in coatings, heat transfer, and brazing require a knowledge of equilibrium solubilities in a variety of systems at elevated temperatures. Of particular interest are solid-liquid interactions in metal systems involving dilute solutions. This investigation was undertaken since little is known about the phase relations or solubility of chromium in liquid silver or of molybdenum and tungsten in liquid tin.1,2 EXPERIMENTAL WORK As indicated in Table I, high-purity metals or those of known impurity levels were used. Crucibles were machined from chromium, molybdenum, and tungsten bar stock 1.3 cm diam and 2.2 cm long. Chromium rod was prepared by arc melting and extruding iodide process crystals.3 The five chromium impurity alloys were in the form of 0.6-cm-diam swaged rod. A Cr-0.06N* alloy was prepared by exposure to NH3 at 1150°C in a closed quartz capsule for 24 hr. Because significant nitrogen was lost during annealing in argon at 1600°C,4 the estimated level was 0.01 pct N. Chromium and Mo,W crucibles were outgassed at 1200" and 1600°C, respectively, at 3 X 10-5 mm. The solvent was placed In crucibles of the solute metal- 6 g Ag in chromium, 0.4 g Ag in the five chromium impurity alloys, and 4 g Sn in Mo,W crucibles. The silver and tin series were outgassed at 900" and 110O°C, respectively, and held at the desired solution temperature in a tantalum resistance furnace under 1.05 atm 99.995 pct Ar. An equilibration time of 0.5 to 1 hr was chosen since 0.3-, I-, and 4-hr anneals at 1235°C for Cr-Ag yielded similar results. Temperatures were measured optically to +10°C under essentially black body conditions which were checked against the melting point of silver. The Cr-Ag and Mo-Sn,W-Sn series were respectively equilibrated at 990° to 1400°C and 1200" to 2000°C. Vaporization losses were generally held to <1 pct by the argon. In the 1800" and 2000°C anneals for 0.5 hr, the crucibles were placed in tightly sealed tantalum cans which kept tin losses to <5 pct. After the anneals, the specimens were furnace-cooled. One anneal was made on small Mo-0.02 C, Mo-0.5Ti-0.lZr, and tungsten crucibles containing tin at 2200°C. The metals were sealed in an electron-beam-welded tantalum can of minimum volume. After the anneal, tin was still present in each crucible, none of which was severely attacked. After equilibration, the saturated solvent metal was selectively removed from the crucible by acid leaching. Weight losses sustained by the crucibles were determined from the initial weight minus the final blank-corrected weight after acid leaching. Chemical analyses were performed on some of the samples. Hot 1:l HNO3-H2O removed silver from chromium with the blank running <0.1 mg or <0.002 pct on measured solubility. Tin was removed from molybdenum and tungsten by hot concentrated HC1 with the respective blanks amounting to -0.004 and -0.0004 pct in the presence of tin. The insoluble residues were weighed and checked for composition. The leaching solutions contained traces of the solute metals which were analyzed by colorimetric methods, Diphenyl Carbazide for chromium, Thiocyanate for molybdenum, and Dithiol for tungsten. The total of the two percentages found from the residue and leaching solution minus the blank gave the desired solubility values. On the basis of annealing empty molybdenum and tungsten crucibles, weight losses due to MoO3 or WO3 volatilization were found to be generally 10.4 mg and affect measured solubilities by <0.01pct. RESULTS AND DISCUSSION Chromium-Silver . Since no intermediate compounds are reported to form in the Cr-An system,&apos; crucible weight losses and chemical analysis of the entire melt should provide reliable measures of the chromium in solution. Values obtained by the two methods are in agreement as shown by the results for unalloyed chromium in Table II and plotted in Fig. 1. Furthermore, the results are consistent with those previously determined by melting equilibrated silver out of the crucible and analyzing calorimetrically for chromium.&apos; On the basis of limited thermal analysis data, the solubility of chromium in silver has been quoted as 8 pct at the monotectic temperature of -1445°C.1 This investigation indicates an extrapolated solubility of 1.38 pct which is believed to be more reliable. At the eu-

Jan 1, 1968

Jan 1, 1967