By A. U. Seybolt, J. L. Walter

The effects of the addition of 0.5 pct ThO2 (by volume) on the grain structure and texture of heavily rolled tungsten sheet were studied. Powder metallurgy ingots were rolled to sheet, 0.001 in. thick, and samples were annealed at temperatures from 1200" to 2500°C. The heating rate to the anneal temperature was varied from 3°C per min to 6500°C per min. The orientations of the largest grains were determined by X-ray diffraction. The disposition and loss of the ThO2 particles were determined by electron transmission microscopy and the activation energy for remozlal of the thorium was measured by mass spec-troscopy. Heating rates below about 800 C per min produced large, highly elongated grains. Higher heating rates produced much smaller, less elongated grains. The grain structure and texture of the slowly heated samples were identical to the structures and textures of heavily rolled tungsten foil conventionally doped with aluminum, silicon, and potassium but the recrystallization temperature was about 200°C lower. There was stringer-like dispersion of larger ThO2, particles superimposed on a uniform dispersion of fine particles. The particles increased in size and decreased in number with time at temperature. The loss of particles was accompanied by formation of grain boundary voids and surface pits. The activation energy for removal of the ThO2 was about 40 kcal per mole. THE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of heavily rolled sheet1 or drawn wire."4 Thus, "doped" tungsten sheet, rolled to 0.001 in. and recrystallized, develops a structure consisting of large, highly elongated grains of a specific preferred orientation.' It has been shown that the elongated grain structure was caused by a dispersion of particles, identified as mullite (Al6si2O13),1,4 in strings parallel to the rolling direction in sheet or to the wire axis. Identical results were obtained for iron which was doped with glass and rolled to 99 pct reduction of thickness and recrystallized.5 Again, the glass particles were disposed in strings parallel to the rolling direction. The strings retarded boundary migration in the lateral direction but grain growth was able to proceed relatively unhindered along the direction parallel to the strings.1,5 In both the doped tungsten and the glass-doped iron, the particles were highly plastic during the high-temperature deformation. Since mullite melts at about 1800°C and the glass employed melts at about 810ºC, the particles were probably molten during the recrystallization anneals (above 1800°C for the doped tungsten and 850°C for the glass-doped iron). There are indications in the literature that particles not plastic at hot-working temperatures (up to about 1550°C for tungsten) may also impart elongated grain structures by primary recrystallization of worked alloys. Examples are dispersions of tantalum carbide in chromium,6 and ThO2 in nickel where elongation ratios of recrystallization grains of up to 20:l were obtained.7 Strings of ThO2 particles in W-ThO2 wire have been seen by Rieck.8 In view of the available evidence, it was of interest to extend the previous studies of doped tungsten and glass-doped iron to include W-ThO2 sheet materials. Of specific interest was the grain structure, preferred orientation, recrystallization temperature, and disposition of the thoria particles. EXPERIMENTAL PROCEDURE A) Material Preparation. About 380 g of blue tungsten oxide (approximate composition WO3) was wet with a sufficient amount of aqueous solution of Th(N03)4 to provide 0.5 vol pct ThO2. The wet mixture was stirred to distribute the doping material uniformly throughout the powder. Stirring was continued while the mixture was heated until it was completely dry. The dried, doped mixture was then reduced to tungsten powder by heating at 850°C for 2 hr in a stream of dry hydrogen. The doped tungsten powder was hydropressed in a rubber sack at pressures of 50,000 psi to produce an ingot approximately 2 cm diam by about 5 cm long. Next, the pressed cylinder was heated in hydrogen for 2 hr at 1350°C to render it strong enough for machining. The cylinder was machined to a square cross section of 1.6 by 1.6 cm with rounded corners. Finally, the bar was heated for 2 hr at 2150°C in hydrogen to provide a sufficiently dense mate rial to withstand the hot-rolling operation. Prior to rolling, the ingot was reduced in thickness by about 20 pct by forging at 1550°C. This served to increase the density of the material and to widen it slightly for better rolling characteristics. The forged ingot was then rolled at 1550°C to a reduction of 45 pct of thickness, following which the rolling temperature was reduced to 1300°C and the slab rolled, with several reheats, to 0.050 in. Further reduction was accomplished at 800°C in tungsten sheet packs to a total reduction of about 99.85 pct. B) Annealing Treatment and Observation of Structure. Small samples of the rolled foil were annealed in one of two ways. Some of the samples were suspended in a covered tungsten can and annealed at temperatures from 1200" to 2200°C for various times in vacuum of l0-7 to 10-6 mm Hg. The can was heated by induction and temperatures were determined by optical pyrometry

Jan 1, 1970

By R. F. Lynch, J. D. Wood

The Al-1.0 pct Mg alloy 565 7 was studied using optical microscopy and electron microprobe X-ray analysis. Constituent particles were found to exist inter-dendritically in the as-cast material in a region of precipitate free a -aluminum. Five phases besides a fine precipitate and a-Al were identified in the cast structure: Fel3, Fe2Al7, Mg2Al3, CUMgAl2, and Cu2FeAl7. Thermal treatments conducted for 100 hr at 1180°, 1130°, 1080°, 1030°, 980°, and 880° F revealed a general dissolution and spheroidization of the in-terdendritic constituent network observed in the cast structure. The principal constituents present in the thermally treated structures were FeAl3 and Fe2Al7 with the relative amount of Fe2A17 to FeAl3 increasing with a decrease in the treatment temperature. The phases Present in the wrought structure were identical to those observed after the thermal treatments, with the constituent particles strung out in the direction of rolling. ALLOY 5657 is a nonheat-treatable commercial purity Al-1.0 pct Mg alloy utilized extensively because of its bright finishing characteristics. This investigation was conducted to determine the constituents present in 5657 alloy, and to study the effect of extended thermal treatments on morphology. Numerous studies have been carried out to establish the equilibrium diagrams for various aluminum systems,1-3 with phase identification based on X-ray analysis, morphology, and the etching response of relatively large particles. Phragmen4 conducted a study of the phases in aluminum eutectic systems and compiled a "corrected" table of etching responses, drawing on his work plus that of Schrader,5 Keller and Wilcox,6 and Mondolfo.7 A review of the original work of Keller and Wilcox, and Mondolfo, which was concerned with the constituents found in commercial alloys, reveals that in numerous cases their etching responses differ from those reported by Phragmen and from each other. These inconsistencies may occur because a specific constituent will react to a given etch in a varying manner depending upon its size, the elements dissolved in the phase, the other constituents surrounding a phase, and the solute content of the matrix. Work with a commercial orientation was conducted on alloys 2024 and 3003 by Sperry8,9 and on alloy 3003 by Barker,10 where the relationship between the phase diagram and the nonequilibrium structure of an alloy was examined. Backerud11 investigated the A1-Fe binary system and found that at high cooling rates the equilibrium eutectic reaction forming a-A1 and FeA13 is replaced by another lower temperature eutectic reaction forming a-A1 and metastable FeAl6, a constituent first identified by Hollingsworth et al.12 Most of the above mentioned studies were conducted on materials having a significantly greater alloy content than 5657 alloy, where the relatively small size and sparse distribution of second phase particles hinders the process of identifying constituents. EXPERIMENTAL PROCEDURE Material with a composition as given in Table I was examined in the as-direct chill cast, hot rolled and cold rolled conditions, and after thermal treatment of the cast structure. Thermal treatments were terminated by a water quench. Microscopic examination was conducted under various lighting conditions following the application of standard etchants as specified in Table 11. A semi-quantitative electron microprobe X-ray analysis was conducted for Al, Mg, Fe, Cu, Si, Zn, and Ti. RESULTS AND DISCUSSION Microstructure of the As-Cast Material. Particles of second phase material were found to exist inter-dendritically, principally in regions of precipitate free a-Al, as illustrated in Fig. 1. Adjacent to the ingot edge was a region of inverse segregation, resulting in an increased amount of second phase material containing large sized particles which aided in phase identification. Phase Identification. Cast Structure. Five phases besides a-Al and a fine precipitate were identified using optical microscopy and electron microprobe X-ray analysis, as presented in Tables II and III, respectively. FeA13 and Fe2A17 are often found with Fe2A17 forming a sheath around the core of FeAl3, resulting from an incomplete peritectoid reaction. These phases have a nearly identical appearance under white light, although they are easily differentiated under crossed polarizers, as characteristically illustrated in Figs. 2(a) and 2(b), respectively. Microprobe analysis con-

Jan 1, 1970

By Frank M. Monroe, James R. Cost

The solubility of nitrogen in vanadium is determined from 275" to 575°C by measuring the height of the nitrogen internal friction peak of equilibrated V-N alloys. The proportionality constant at 275°C between the internal friction peak height (Q- 1) and the atom percent nitrogen in solution is found to be 0.095 per at. pct for nitrogen concentrations up to 0.8 at. pct. The heat of solution of the nitride in vanadium is 5500 cal per mole. The solubility of nitrogen in the Group V metals is discussed. LITTLE work has been performed on the vanadium-nitrogen terminal solid solution. Hahn1 found the solubility for nitrogen to be very small and reported the existence of a hexagonal phase of composition near that of V2N at the solubility limit. Rostoker and Yamarnoto2 reported the solubility to be at least 3.5 at. pct at the melting point and to be less than this value at 900°C. In addition, they reported from X-ray diffraction studies that nitrogen in solution produces tetragonality in the vanadium lattice. An X-ray study by Schonberg3 has confirmed the results of Hahn but indicated that the tetragonality observed by Rostoker and Yamamoto was due to the presence of oxygen in their specimens. Beatty4 has performed lattice parameter and hardness measurements on terminal solid solutions and found the upper limit of the solubility to be at least 0.66 at. pct N. No measurements have been made of the pressure-temperature-composition relationships (P-T-X) for the terminal solid solution. As a part of a research program on gas-metal equilibrium, an attempt was made to study the P-T-X relationships in the V-N system using both the internal friction and the gas equilibration methods which have been successful with the Nb(Cb)-N and Ta-N systems (see Ref. 5 for a review of this work). Extensive investigation, using the gas equilibration methods, showed this method not to be applicable with vanadium This was presumably due to the gettering action of vanadium sublimed on the walls of the Sieverts apparatus. Thus, the nitrogen pressure relationships with temperature and composition were not obtained. The internal friction methods were, however, found to be applicable, and the temperature-composition relationships are reported in this paper and compared with similar results for the Nb-N6 and Ta-N7 systems. The existence of a Snoek internal friction peak due to nitrogen in solution in vanadium has been clearly demonstrated. 8-10 Powers and Doyle found the peak to be at approximately 275°C for frequencies near 1 cps.8 In a subsequent paper10 they reported the proportionality constant at 275°C between the internal friction peak height (Q-1) and the concentration of ni- trogen in solution (in atom percent) as 0.06 per at. pct. The studies of Stanley and wert9 indicated qualitatively that the height of the Snoek peak decreased with aging at the peak temperature and thus suggested that internal friction methods were suitable for study of the solubility. EXPERIMENTAL METHOD The vanadium for this investigation was of particularly high purity. It was obtained from the Ames Laboratory of the U.S. Atomic Energy Commission, Ames, Iowa in the form of a 1/2-in. diam, three pass zone-refined ingot. The electrical resistivity ratio (p300ºk/p4ºk) was 160. The initial composition was determined as follows: Carbon 200 ppm Oxygen 150 ppm Chromium <50 pprn Iron 125 ppm Silicon <50 ppm Other metallic 100 pprn The initial vanadium ingot was fabricated to 30-mil wire by swaging and wire drawing without the need of intermediate annealing. Lengths of this wire were then further purified (particularly for oxygen) by outgassing at 10-6 torr at 1400°C for 4 hr. The outgassing treatment resulted in specimens with a bamboo grain structure and a lustrous appearance. Desired amounts of nitrogen were added to the outgassed wires in a Sieverts apparatus in which known amounts of nitrogen were equilibrated with the wire at 1300°C. Nitrogen concentrations were produced in the desired range from less than 1 to 10 at. pct N. Monitoring of the partial pressure of nitrogen in the Sieverts apparatus indicated that at 1300°C equilibrium between the nitrogen gas and the vanadium was obtained within 10 min. Relatively rapid cooling from the nitrogen addition temperature was obtained simply by turning off the specimen heating current and cooling to room temperature in the partial pressure of nitrogen. Internal friction measurements of wire specimens were made under forepump vacuum in a torsional pendulum at frequencies near 1 cps. The torsional pendulum was of low thermal inertia and was designed so that specimens could be heated both by a conventional tube furnace and by the joule heating of a separate current through the wire specimen." Use of a static atmosphere of helium gas as a quenching medium made it possible to cut the specimen current, rapidly cool the specimen to the measurement temperature, and make a measurement of the internal friction in less than 1 min. Because of the large solubility of vanadium for nitrogen, the internal friction peak heights were in some cases greater than Q-1 = 0.1. This high damping resulted in an estimated relative uncertainty in the damping measurements of approximately 10 pct. X-ray analyses made to identify the precipitated ni-

Jan 1, 1970

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InAs and GaAs were measured over the temperature range 400°K to temperatures above the melting points using a di-phenyl ether drop calorimeter. Smoothed values of the thermal properties have been derived and tabulated at even temperature interuals . The heats of fusion of InAs and GaAs were determined as, respectively, 8790 ± 200 and 12,590 ± 300 cal per g-atom at the respective melting points of 1210º ± and 1513º ± 1°K, yielding entropies of fusion of 7.26 * 0.16 and 8.32 ± 0.20 cal perºK per g-atom, respectively. A general discussion of the thermal properties of III-V com-pounds is given. THE low-temperature heat capacities of InAs and GaAs have been determined by Piesbergen.1Using a dynamic temperature modulation technique, Miller2 has determined the heat capacities of the compounds as well as GaSb and Ge between room temperature and 650°K; however, it has been observed that values determined by drop calorimetry for GaSb3 and for germanium4 are consistently about 5 pct lower than Miller&apos;s results. Cox and Pool10 report values for the heat content of InAs and GaAs and the heat of fusion of InAs. No value for the heat of fusion of GaAs appears to have been previously reported. This paper reports results of high-temperature heat content investigations of InAs and GaAs measured in the range 400" to above 1500°K employing a diphenyl ether drop calorimeter. These results, together with our previous results on III-Sb compounds3 as well as heat-content measurements5 of solid InP and Gap, are used in a general discussion of these compounds. EXPERIMENTAL PROCEDURES High-purity samples of the compounds, stoichio-metric to ±0.1 at. pct, were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories. The sample preparation, description of the calorimeter, and details of the heat content measurement have been previously described.3 Samples were sealed in evacuated silica capsules and suspended by a Pt-Rh wire in a Pt-wound vertical tube furnace, heated to temperature

Jan 1, 1970

By E. T. Turkdogan, L. S. Darken, R. J. Fruehan

Further consideration is given to the application of the quadratic formalism to evaluate the thermodynamics of binary metallic solutions from experimental data. The use of the thermodynamic relation, in(r1/r2) dN2= 0, in the evaluation of activity data is discussed. The empirical correlations derived previously for enthalpies and entropies of solutions in Part II are shown to be predicted theoretically for a special case. The applicability of the quadratic formalism to the activity coefficients for binary organic solutions is demonstrated. DARKEN&apos; introduced a quadratic formalism describing the composition dependence of the activity coefficient in the terminal regions of binary metallic solutions. In a subsequent paper (Part II) Turkdogan and Darkeen2 extended this formalism to the enthalpy and excess entropy of binary metallic solutions, and showed that the available data for the activity coefficients and heats of mixing of many solid and liquid binary metallic solutions confirm reasonable applicability of the quadratic formalism. Much variation was noted, however, in the extent of the terminal regions from one system to another, commonly from about 10 to 70 at. pct. For the present purpose, equations derived previously need be given only for one of the terminal regions, e.g. region (I), 0 < N2 < N&apos;2: where subscripts 1 and 2 indicate quantities for components 1 and 2 and superscript ° the values at infinite dilution; other terms are: N = atom fraction, y = activity coefficient, = partial molar enthalpy of solution, ?HM = molar heat of solution, ?Sx = excess partial molar entropy, ?Sx = excess molar entropy. The heat and entropy like terms (constants) el, and S12 are defined in the following expression for the temperature dependence of a12, thus a12 £12 — s12 rnl 2.303RT 2.303 R l J Using this formalism, the thermodynamics of binary systems in the terminal regions may be described over a temperature range of experisental interest in terms of eight quantities: Lº1—Lº2, ?Sx1,?Sxº2 , £12 ,£21,fiai, S12, and S21. In the previous paper, these quantities were evaluated for many solid and liquid binary solutions, and two significant correlations were observed between these thermodynamic quantities pertaining to the terminal regions, thus [10] and [11] Combining Eqs. [9], [l0], and [ll] and rearranging gives a12 -a21 = 1.382R log rº2- 0.08(?S2xº- ?S1xº) [12] Since the second term involving entropies is small and Eqs. 1101 and [ll] are empirical relations, the above equation may be simplified to a12 = 2.74 log rº2 [13] Using the values of a&apos;s and y°&apos;s compiled in Parts I and 11, a12 - a21 is plotted against log(rº2/rº1) in Fig. 1; the line drawn has a slope of 2.74. For Hg-K at 300°C, log(yº2 /yº1)= —5.10, not shown in Fig. 1, and from correlation [13], a12 - a21 = -13.97; this is to be compared with -10.76 derived from the activity data (Part II).

Jan 1, 1970

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.&apos; Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler&apos;s saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.&apos; A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By N. A. Gjostein

The real and apparent dependence of the surface self-diffusion coefficient, Ds, of gold on crystallo-graphic orientation has been investigated by isolated scratch smoothing and grain boundary grooving experiments. No systematic variation of Ds with orientation was found along the [100] zone. In view of the experimental scatter in these results, however, only aniso-tropy ratios, p, greater than -1.3 would be detectable. Anomalously low values of Ds were found on the [0ll] and [110] zones when the diffusion direction lies along (the scratch or grain boundary groove is perpendicular to) these zones. By comparing these results with a previous y plot study of gold, it is hypothesized that this is not an intrinsic diffusivity effect, but rather it results from a decreased driving force for mass transfer at orientations where the y-plot curvature is negative and appreciable in magnitude relative to y. The characteristics of this type of anisotropy do not appear sEVERAL investigations1-7 have dealt with the anisotropy of the surface self-diffusion coefficient, Ds, of metals as measured by the decay of single or multiple to be in agreement with the hypothesis of fast diffusion along ledges in the surface structure. In certain cases the Fourier method of determining Ds, described in Paper I of this series9 was compared with the second moment analysis in order to determine whether or not the method of analysis affects the anisotropy ratio. While the type of analysis does influence the magnitude of the anisotropy ratio, this effect is not associated with the shape of the profile, but rather is connected with the iterative volume diffusion correction used in conjunction with the second moment analysis. It is further demonstrated that the volume diffusion correction can be too large by either method when the y-plot curvature effect is large. Certain orientations exhibit an unusual temperature dependence of Ds ; this is discussed in terms of the y-plot curvature effect and/or the influence of impurities on Ds . scratches in the surface. Depending on the system investigated, both large1"3&apos;6&apos;7 and small4&apos;5 anisotropies in Ds have been found. Although adsorbed impurities undoubtedly play an important role in determining the magnitude of the anisotropy,8 there are other factors that can give rise to an apparent anisotropy in Ds, thus obscuring the true nature of an intrinsic anisotropy in

Jan 1, 1968

By F. R. Brotzen, L. D. Whitmire

Single crystals of high-purity molybdenum were de-formed at temperatures from 195°to 473°K, and the effect of deformation on the electrical resistivily was deler-mined. To separale the resislivity components of point and line defecls some cryslals were annealed at 473°K. The vale of resislivily increase wilh strain was nearly linear and was strongly dependent upon the deformation temperature. Point dejects are annealed out without any effect on the flow stress. At low temperatures the flow stress is a linear function of the square root of the resistivity increase attributable to dislocations. ELECTRICAL-resistivity measurements have been used successfully to gain information on structural changes in metallic materials. During plastic deformation the electrical resistivity rises because of electron scattering from newly created lattice defects. Such measurements lend themselves, therefore, to corroborating results from direct observation of lattice defects and, to a certain extent, to correlating defect densities and distribution with mechanical properties. Published information on research with single crystals of the bcc metals of Group VI, particularly molybdenum, is still limited. Yet, molybdenum single crystals of relatively high purity can be readily prepared by electron-beam-melting techniques. Furthermore, some valuable information on the defect structure of deformed crystals by direct observation is available. Lawley and Gaigher,1 for example, have examined dislocation configurations in deformed molybdenum crystals by means of transmission electron microscopy. Their results revealed that the dislocation density and distribution were strongly dependent upon the deformation temperature. These findings differed from those by Keh and weissmann,2 who found that the average dislocation density in polycrystalline iron deformed between 138° and 298°K depended only on the degree of strain and not on the deformation temperature. Martin3 and peiffer4 showed that point defects introduced in polycrystalline molybdenum by cold work can be eliminated by annealing at a relatively low tempera-ture. In view of their work it became apparent that resistivity measurements of suitably annealed crystals could disclose changes in their dislocation structure and contribute to the understanding of the work hardening of molybdenum crystals. EXPERIMENTAL PROCEDURE Crystals were grown by electron-beam zone melting5,6 of 0.062-in.-diam molybdenum rods (99.99 pct) supplied by General Electric Lamp and Wire Division, Dover, Ohio. The crystals, about 4 in. long, were prepared by using five zone-refining passes at a speed of about 6 mm per min in a vacuum of about 5 X l0-6 Torr. The resistivity ratio of the crystal, p(4.Z°K)/p(273°K), was generally near 10-3. These crystals were used as tensile specimens of uniform diameter in the "as-grown" condition. They were oriented for maximum shear on the (011)[111] slip system (Schmid factor >0.49). The specimens were held in spherically seated Templin-type grips so as to minimize bending. Samples were deformed on an Instron machine at a strain rate of about 5 X 10-5 sec-1 in an isopentane bath with dry ice at 195°K, in ice water at 273°K, and in a vegetable-oil thermostat at 373° and 473°K. The temperature in the latter was maintained constant within +2°K. Resistance measurements were carried out with a Kelvin double bridge. The resistance of the potential leads was kept low by using large-diameter wires outside the low-temperature bath. Many of the resistance data were checked by measurements made with an ac bridge. Current and potential leads were spot-welded to the specimens. The distance between the potential leads, about 3 in., was also considered to be the gage length for the strain measurements. Diameter and gage length of the samples were measured optically with an error of less than 2 pct. These measurements were used also to insure that the deformation had been uniform over the gage length of the specimen. Resistivity changes were then determined from the resistance measurements at 4.2°K assuming constancy of volume. In the course of a test, the crystal diameter, gage length, and resistance at 4.2°K were determined first in the initial state and subsequently for various amounts of elongation.

Jan 1, 1968

By W. D. Robertson, J. -P. Briant, M. Gell

The distribulion of dislocatiorls genevnted during the propagalion of hydrogen-induced cracks in Fe-Si cryslcrls was studied as a funclion of temperature f-110o lo 243°C) and silicorz conlenl (3.1 and 4.2 pct). It zoas found that the clislocntiotl densily and the size of the plctslic zone increased with increasing tempevalnre and decreasing silicon conlent. Furtheruvzove, there was a correlcrtion in the dislocalion patterns formed around cracks that propagated at different tempevattrt-es in cvyslals of diffevent silicon contents such that a 1 pcl itlcverise in silicon content was equivalent to a lemperaluore redziclion of approximately 120°C. The experimenlal YeSnllS were compaved with the results of an elastic-plastic wodel that relates the size of the pluslic .zone to the cvack length, internal pressure, and yield stress. it was found that the clzunges in the dislocctlion cryrays with lemperature and combosition can be e-kplaincd by the lemperatrnre and composilion dependence of the yield stress. An wmtsual feature of this study was the observation of low -temperature noncrystrrllogruphic cracks. PLASTIC relaxation can occur at the edge of a moving crack by the operation of pre-existing dislocation sources or by the creation of new sources in a region of perfect 1attice.l&apos;2 The amount of relaxation in a given crystal depends on the crack velocity and the temperature, and can determine whether a crack propagates in a brittle or a ductile manner.1-3 Tetelman and Robertson4 observed microcracks m Fe-3 pct Si single crystals that formed on (100) planes by the precipitation of hydrogen gas during electrolytic charging at 23°C. The plastic deformation accompanying crack propagation was observed in the form of dislocation etch pits and an extensive analysis has been made of the size, shape, and crystallography of the dislocation arrays5-7 This paper describes the effect of temperature on the plastic deformation generated around hydrogen-induced cracks in Fe-3.1 pct Si and Fe-4.2 pct Si single crystals. The observations are compared with the results of an elastic-plastic model for yielding around a crack containing an internal pressure. 1) EXPERIMENTAL PROCEDURES The composition of the materials used in this study are given in Table I. Single crystals of alloy A and the 4.2 pct Si alloy were grown by the strain-anneal method; crystals of alloy B and the 5.1 pct Si alloy were cut from an ingot grown from the liquid. he ~ingle-cr~stal metallographic specimens had a Cross section of 0.100 by 0.050 in. with a length of at least 3/8 in. Specimens were annealed for 3 hr at

Jan 1, 1968

By David J. Mack, Dennis R. O’Boyle

The mechanical properties of three polycrystalline intermediale Phases that have the y bvass structure were measured in compression between 400° and 900°K. At the lower testing temperatures— termed Region I— no plaslic deformalion occurred prior to brittle fracture. A1 higher temperatuves— lermed Region III—the three phases deformted plaslically for all strain rules from 1.5 to 36.0 x 10-4 sec-1. The homologous temperature for the inilialion of plaslic flow increased in the same order as tile atomic size difference between atoms in each plmse (0.50Tmp for y AgZn, 0.62Tmp for y CuZn, and 0.76 Tmp for y CuCd). The increased flow resistance oj. y CuCd above 0.50Tmp is explaitzed in terms of the more random arrangement of copper and cadmiwn atoms on the laltice sites of&apos; the y bvass slrilctlire. Plaslic deformation of the three intevmiediate phases in the smooth plaslic flow region appears to be controlled by oacancy-induced dislocation climb. RESULTS are reported in this paper on the mechanical properties of three binary intermediate phases having the complex cubic y brass structure (D82, 143m) containing fifty-two atoms in the unit cell. The structure of the prototype y brass phase, y CuZn, was first analyzed by Bradley and Thewlis&apos; based on the X-ray work of Westgren and Phragmen.2 The y brass structure can be visualized as an arrangement of twenty-seven body centered cubes (3 by 3 by 3) into a unit cell containing fifty-four atoms. From this cell the center atom and the four corner atoms are removed and the remaining fifty-two atoms are slightly displaced, resulting in the y brass structure. Approximately thirty-five binary intermediate phases that have an electron to atom ratio of 21:13 have been reported to form the y brass structure. The three y brass intermediate phases selected for this study are formed from elements in groups IB and IIB of the first and second long period. Each compound exists over a composition range that includes the stoi-chiometric composition A5BB (Cu5Zn8, Ag5Zn8, Cu5Cd8). y CuZn (a0 = 9.944A) has solubility limits extending from 57 to 67 at. pct Zn at 500°C apd melts peritecti-cally at 834°C; y AgZn (a0 = 9.326A) has a solubility range from 58 to 63 at. pct Za and melts peritectically at 661°C. y CuCd (a, = 9.596A) melts congruently at 563°C and has a maximum range of solubility extending from 58 to 64 at. pct Cd. In order to minimize coring and microporosity during solidification, the composi- tion of the compounds that form peritectically (y CuZn and y AgZn) was chosen so that the temperature difference between the liquidus and the solidus is only a few degrees centigrade. In selecting y brass compounds for this study, phases were avoided that contained a transition element or that had an electron to atom ratio greater than 1.70. Hume-Rothery et a1.3 has observed that, when the electron to atom ratio of y brass intermediate phases exceeds 1.70, atoms begin to drop out of the unit cell to maintain a constant electron to unit cell ratio. EXPERIMENTAL PROCEDURE Each of the three intermediate phases was prepared from elements having a purity >99.999 pct. Only trace quantities of impurities (<0.0001 pct) were detected by spectrographic analysis of the four elements. A master alloy of each compound weighing approximately 130 g was prepared by melting the elements in evacuated sealed quartz tubes heated in an electric furnace. Specimens having the desired diameter for the mechanical property measurements were obtained by remelting the master alloy in a Vycor tube under argon and drawing specimens from the melt into 4-mm-diam quartz tubes. To obtain a smooth surface on specimens drawn from the melt, the inside of the quartz tube was coated with a thin layer of graphite formed by thermally decompositing acetone. All specimens were imbedded in sealing wax and cut to the proper length with a diamond-impregnated cut-off wheel. The individual specimens (4 mm diam by 8 mm long) were then sealed in evacuated Pyrex tubes and homogenized at 500°C for 72 hr. Chemical composition, variations over the length of the rod (10 cm long) were generally less than 0.2 pct and the analyzed composition differed from the desired composition by less than 0.5 pct.4 Metallographic evaluation of the specimens after homogenization showed no evidence of a second phase in any of the compounds. The average grain size of the specimens after homogenization was 1 to 2 mm. All mechanical property measurements were carried out in an argon atmosphere using a compression apparatus described previously.5 Prior to applying the load to the specimen, the test apparatus was evacuated, back-filled with argon, and heated to the test temperature for 20 min to establish thermal equilibrium. EXPERIMENTAL RESULTS Mechanical properties measured as a function of temperature and strain rate for each of the three y brass phases were similar. From room temperature to the ductile-to-brittle transition temperature, only elastic deformation was observed prior to fracture.

Jan 1, 1968

By R. C. Gifkins, K. U. Snowden

The value of the index n in power ktivs for the stress sensitivity of minimum creep rale at lead is derived front results drawn from lite literature and from previously unpublished nork on commercial (99.99 pel) and high-purity (99.999 pel) lead polycryslalline and hi crystal specimens. In tests al 0.5Tm (22 to 50&apos;C) for slvesses below 250 psi, n fulls to mily for poly-cr,yslullirle specimens, single crystals, and bicrystals, and toy grain boundary sliding in bicrystals. Between 250 and 500 psi there is a tyansilion range and, for the polycrystalline specimens al least, u high-stress regime for 500 to 1500 psi where n is 5 or 6. These results are such that none of the suggested stress taws can he used to extrapolate to very loir stresses. Meclianisms for deformation in Ike grains and toy grain boundary sliding in the low-strcss regime are outlined. In particular, the mechanism for grain boundary sliding involves sliding controlled by diffusion from tensile to compressire Ledges. predictions based on this model give promising numerical agree-nicul with experiment. II is suggested that the mechanism for grain boundary sliding may he important in other circumstances, e.g., in creep of ceramic materials or superplaslicity, because it can operate with lille or no dislocation aclirity. WhEN the stress dependence of secondary creep rate is represented by a power law the values taken by the stress exponent n are found to vary between 1 and 7, see, c.g., Garofalo.&apos; In Eq. 1 11 u is the applied stress and A a constant. The case for accepting values of v = 1 rests principally upon tests at high temperatures (>0.9Tm) and there have only been isolated tests at lower temperatures (rather than plots of creep rate against stress) for which the creep rates are such that some form of Nabarro-Herring creep with n = 1 is applicable. Hanson5 and Greenwood and cole6 plotted creep rate against stress for tests made in the vicinity of 0.5Tw, and found a "creep yield", so that below a certain low stress the creep rate was linearly related to stress: these observations appear to have been subsequently ignored. Various models have been proposed which agree with a large body of experimental results in which n equals -5 at high stresses (e.g., weertman7 and McLean8). Various alternatives to Eq. [1] have been proposed principally as a means of unifying creep data, but sometimes, it seems, in order to obviate the necessity for assuming a series of regimes of deformation associated with the various values of n; further refer- ence to these will be made in the section on stress laws. This paper calls attention to extensive results which show n = 1 for the creep of lead at room temperature (0.5 T,). RESULTS Fig. 1 is a composite diagram based on figures in the literature6,9,10 with additional results obtained by the present authors and their colleagues11,12 in the course of a number of investigations not directly concerned with stress sensitivity. In Fig. 1 In creep rate is plotted against In stress. The curves show results for two kinds of material. Lead I is of commercial purity (99.99 pct Pb) and lead IT a specially refined material, hydrogen-purified to remove oxygen; it contains 99.999 pct Pb. Curve A is for lead I in polycrystalline form (grain diameter 0.02 to 0.05 cm) at room temperature (22&apos; to 26°C). Curve B1 is for lead I, polycrystalline, tested at 50C. Curve B2 is for lead 11, polycrystalline (grain diameter 0.02 cm), tested at room temperature (22 O- Curves C to F relate to tests made of bicrystals of lead 11: all of the same nominal orientation ("Y" in Ref. 12). Curves C and V are for creep within the component crystals of the bi crystals at 22°C (AB and CD in Fig. 2). Curve E is for creep measured in a gage straddling the boundary, approximately 0.15 mm either side (BC in Fig. 2). Curve F shows rates of grain boundary sliding (as distinct from strain rates in the other curves), obtained by averaging the offsets of six marker lines on the bi-crystal boundaries. The principal feature of the results is that the stress sensitivity falls into two distinct regimes, according to whether the stress is below approximately 250 or above 500 psi (there is a transitional range between 250 and 500 psi). The new result is that below -250 psi two of the curves (A and BI) give a value of n 1, and the other curves also drop below n - 2 to -1.5 but do not extend to low enough stresses to show clear evidence of n 1. At very high stresses the curves tend to give values of n - 6, as previously determined in other investigations. Curve R2 for the high-purity lead in polycrystalline form at room tenlperature almost merges with B, and thus gives new significance to the values for stresses of 150 and 200 psi; previously&apos;3 these points had seemed to fall away from the curve of slope -3, but they now can be seen as almost completing a transition to n = 1. It should be noted that there was originally considerable apparent scatter in the results for the high-purity lead. However, this was found to be associated with annealing conditions or variations in residual content of oxygen and curve B2 was constructed using the highest rate (i .e., the rate for the purest lead) determined for each stress during the course of various investigations over the years: altogether, some forty tests were used in constructing curve R2.

Jan 1, 1968

By R. Kossowsky

Structural changes in Be-Cu, Be-Ni. Be - Ag, and Be-Fc alloys pressurized in a solid medium were invesligated by resistivity measurements , X-ray diffrac lion in situ and metallogvaphic examination. Some limited tests in liquid medium were also conducted. Good correlation was oblained between diauges of slope of relative resistance us pressure and changes in diffraction pattern. Metallographic examination rez:ealed that the copper, silver, and nickel alloys lwiu heauily due to the applicalion of pressure at room temperature. Using polarized light technique {1012}, {1011}, and possible {1010} twinning planes were identified. At eleuated temperature twinning was moslly confined to the {1012} planes. Although twin-ning could be promoted by application of hydroslutic pvessure (liquid medium), it was strongly enhanced by the pvesence of a nonhydvostatic shear component due to pressurizalion in a solid medium. It was further obserced that a decrease in grain size inlnibiled twinnitzg activily. A great deal of effort has been expended in recent years to render beryllium useful for structural applications. Efforts were concentrated towards a possible phase change and to promoting other than basal deformation modes. Quenching experiments to obtain the high-temperature bcc phase have failed,&apos; nor were alloying additions successful in improving ductility of the brittle hcp phase.2 Herman et a1.3 have reported a new {1011} twinning mode in a Be-4.4 wt pct Cu alloy oriented for a C axis compression sustaining loads to 440,000 psi. A new approach using high-pressure techniques was undertaken at Curtiss-Wright, Wright Aeronautical Division Laboratories. Marder4 reported a 25 pct decrease in relative resistance of commercially pure beryllium at 92 kbar. He proposed that this discontinuity corresponded to the bcc phase found at high temperature; however, X-ray diffraction in silu did not confirm a phase transition.5 contre6 has recently shown that the bcc transition in pure beryllium is lowered to 800°C at 80 kbar accompanied by a 50 pct increase in relative resistance. The purpose of this paper is to report on one phase of an investigation of the effects of high pressures and temperatures in beryllium alloys, namely, twinning behavior in Be-Ni, Be-Cu, Be-Fe, and Be-Ag alloys pressurized to nearly 100 kbar and temperatures up to 200°C. EXPERIMENTAL METHODS Material was obtained from Nuclear Metals, Inc., in the form of a 1.5-mm-diam wire extruded in stainless-steel cladding at 1600° F. Nominal composition of the alloys is listed in Table I, and the major impurities are are given in Table 11. Pressures to 100 kbar* were ob- tained using a National Bureau of Standards type 100/400 ton tetrahedral unit supplied by Barogenics, Inc. This type of apparatus contains a retaining sleeve with a conically tapered internal surface and four pressure-intensifying anvil assemblies with tungsten carbide tips. The 10-mm-long specimen fits into a pyro-

Jan 1, 1968

By E. Miller, K. L. Komarek

Equatiorzs have been derived which related maximum solid solubilities in semicondcting compounds having retvograde solidus curves with 1iqllidus data. Liquidus curves in Lke Pb-Te, Pb-Se, ard PB-S systetris have been defermined by thertrzal aralyses. Fvotrz expevimental maximum solibilities ia CdTe, PbTe, uxd PbS vetvograde tetrperatures hale beep1 calculated. TIze resllts support the concept that under certaiz conditiots pronounced itjlections in the liquidis curves arc indzcatiz:e of retropade solidus curves and that the tenlperatltre of the lmaximum solid solubility will be close to the temperature of the point of inflection in the liquidus curve. The maximum solid solihility within a gvoup of homologous cottrpoods SeetlLs to increase with increasing flatness ol the liquidus curvres. The phenomenon of retrograde solubility in metals, i.e., maximum solubility in a solid terminal phase in equilibrium with a liquid phase, has been theoretically predicted by Van aar&apos; in his calculations of hypothetical binary phase diagrams. It was not until 1926, however, that retrograde solubility was experimentally verified in the Zn-Cd system.&apos; Since then many sys- tems with retrograde solubility have been found, so that at present approximately fifty binary diagrams with a retrograde solidus curve are known.3 Meijering4 has critically appraised the accumulated data and has presented calculations which alloy predictions as to whether or not a solidus line will be retrograde. Interest in retrograde solubility increased when it was found that the solidus curves of germanium and silicon alloyed with a great many doping elements are retrrade. The problem was treated thermody-namically by odkinson,% d all available data on solid solutions in germanium and silicon were summarized by Trumbore.7 Although it is to be expected that intermetallic compounds will also exhibit retrograde solubility, experimental evidence is much more limited. Until now retrograde solidus curves have been reported for the compounds de,&apos; be, Ps:" ne," SnSe," and SnS.13 All these compounds are semiconductors, and the solidus curves were usually obtained by determining the carrier concentration at room temperature of samples equilibrated at elevated temperatures and then quenched. It has been hown,&apos;&apos; however, that it is not always possible to quench in the equilibrium compositions from above a certain temperature. Theoretical discussions have either explicitly excluded intermetallic compounds4 or not treated them with respect to retrograde slubilit.j In the following a thermodynamic treatment of retrograde solu-

Jan 1, 1967

Jan 1, 1967

By G. L. Fisher, R. Maddin

The rate of self-diffusion in silver single crystals during torsional strain was measured over a wide range of tenperatures and strain rates. The torsional strain was applied in a cyclic manner by reversing the divection of twist aftev a certain fraction of the total strain was reached. Surface roughening was substantially reduced in cyclically strained specimens compared with those strained entirely in one direction. Diffusion coefficients were determined using a special sectioning technique whereby slices could be removed parallel to the surface of a strained torsion specimen. The accuracy of the technique was first determined using roughened specinzens statically diffused to various penetration depths. Simultaneous strain-diffusion experiments were then performed over the temperature range 550&apos; to 800 using strain rates of lo-&apos; to 2.2 x 10&apos; sec-&apos;. The increase in silver self-diffusivity during torsional plastic strain was small. In only one case was the enhancement greater than twice the static value of the diffusion coefficzent. The enhancements increased slightly with decreasing tenzperature and increased with increasing strain rate. A dislocation pipe mechanism of enhancement was found to explain the present results satisfactorily. The magnitude of the enhancements and the tenzperatures at which they were observed suggests that a steady-state dislocation density of 10&apos; to 109 dislocations cm-2 existed during the high-tempevature deformation. The diffusion coefficient in an fcc metal can be increased by 1) an excess concentration of point defects and 2) the rapid movement of diffusing atoms along grain boundaries and dislocations. Plastic deformation may be responsible for enhancements by both of these mechanisms. The results of simultaneous strain-diffusion experiments have caused a controversy over the magnitude of the effect of strain upon diffusion. Experiments reporting large enhancements have been criticized for the manner in which the diffusion coefficient was measured. Several of these experiments have been contradicted by other results obtained in a similar manner. No enhancement was reported by two investigators&apos;&apos;&apos; who performed their experiments at high temperatures where strain is expected to have little effect upon diffusion. A recent theoretical analysis3 indicates that strain enhancement by a vacancy mechanism will be small and exist only at low temperatures and rapid strain rates. It is doubtful whether any experiment has yet proven that strain enhancements can occur by an excess vacancy mechanism. In the present research, experiments were performed at extremes of temperature and strain rate in an attempt to measure enhancement of diffusion by strain. Self-diffusion of silver during torsional deformation was chosen since two separate investigations4j5 indicate that at least a small enhancement exists under these conditions. An accurate method of determining the diffusion coefficient, mechanical sectioning, was employed after a technique was devised to apply it to the roughened surface of a strained torsion specimen. First, the accuracy of the technique was determined for different penetrations (2fi). Then diffusion experiments were performed at temperatures between 550" and 800°C at strain rates of 10"" to 10"" per sec. I) EXPERIMENTAL PROCEDURE Preparation of Specimens. The experimental procedure detailing the growth of crystals, their treatment, and the annealing techniques during straining are contained in earlier publications.496 The dimensions and orientations of the torsion specimens are shown in Figs. 1 and 2. licatiin of Torsional Strain. The torsion procedure was changed from that used previously. The specimens were strained in cycles to reduce the gross distortion and surface roughening inherent in twisting to high strains in one direction. For all strains above 0.30, the total surface strain was obtained as follows: the specimen was twisted to 0.10 strain in a clockwise direction; the direction was reversed; the backlash in the torsion apparatus was taken up; and the specimen was twisted in a counterclockwise direction through the initial starting point to 0.20 surface shear strain in the opposite direction. The strain reversal took no more than 1 min to accomplish. The total accumulated surface shear strain was arbitrarily taken as the sum of the 0.10 strain in the clockwise direction plus 0.20 in the counterclockwise direction. Although cyclic torsional strain was beneficial, surface roughening and specimen distortion were not entirely eliminated. The variation in the diameter at various points on the specimen was often much greater than the depth of the diffusion zone. Since serious errors might result if specimens were sectioned in the usual manner, a technique of lathe sectioning was devised to allow sections to be taken parallel to planes of equal concentration.

Jan 1, 1967

By Robert E. Green, Edmund G. Henneke

The velocities of the three possible modes of elastic wave propagation have been calculated for single-crystal copper at 1-deg intervals throughout the standard stereographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy flux and specimen axes are presented as arrows drawn on stereographic projections. The orientation factors associated with dislocation motion on the primary slip system only and also on all twelve slip systems have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing wave resonant specimen have also been calculated. The results of these calculatians are compared with earlier calculations on aluminum crystals and the relevance of these results to ultrasonic attenuation measurements is discussed. GREEN and inton&apos; have recently outlined a procedure for determining the orientation factors for dislocation damping in single crystals. The stress field associated with a given mode of elastic wave propagation is resolved on the slip systems in which it is assumed the dislocations are vibrating due to this stress field. Since, at room temperature, slip has been observed on a limited number of systems in fcc and hcp metal crystals, it is assumed that these systems are the appropriate ones to use for the resolving process. This procedure has been applied to aluminum crystals by Hinton and hreen&apos; and to zinc crystals by Henneke and Green.3 In the present paper the modes of elastic wave propagation have been calculated for copper crystals possessing orientations at 1-deg intervals throughout the standard stereographic triangle. The deviation of the energy flux vectors from the specimen axis have been calculated for each mode. The stress field associated with each mode has been resolved on the (111)(110) slip systems in order to determine the orientation factors for dislocation damping. MODES OF ELASTIC WAVE PROPAGATION For any direction in a linear homogeneous aniso-tropic material three elastic modes can be propagated. In general, each of these modes has both longitudinal and transverse particle displacements associated with it and thus are not "pure" modes. However, there is always one component which is greatest in either a longitudinal or transverse direction and hence the mode may be referred to as quasi-longitudinal or quasi-transverse, accordingly. For certain axes of high symmetry pure modes may be propagated. The phenomenon of refraction of the energy flux vector is also exhibited by elastic wave propagation in ani-

Jan 1, 1969

By M. J. Duggin

Structural similarities between the E, X, and iron carbides are illustrated. Experimental evidence regarding phase transformations occurring during ternpering reactions in finely divided carbides, thin-film carbides, and carbides which occur in steels is considered and possible mechanisms for the E — x and x — 9 transformations proposed. HOFER1 has shown that within the appropriate temperature ranges carbon monoxide will react with finely divided a iron to form either iron carbide or x iron carbide. He has shown that at an elevated temperature the E iron carbide will transform to the x iron carbide (Hagg carbide) which, upon further elevation of temperature, will transform to 9 iron carbide (cementite). Jack,2,3 using X-ray diffraction methods, has observed that during the tempering reactions occurring in steel the E iron carbide formed in the first stage of tempering passes into two-dimensional platelets of 0 iron carbide during the second stage of tempering. The three-dimensional form of the 0 carbide is formed during the third stage of tempering. Jack suggested2 that the two-dimensional platelets of 0 carbide could be related to the faulted x iron carbide. Okada and Arata4 investigated a Swedish steel containing 1.05 wt pct C and approximately 1.0 wt pct Mn using permeability measurements at low field strength. A Curie point of 360°C was observed in the quenched steel, which indicated the presence of E iron carbide. On tempering at 400°C the specimen developed a Curie point at 230°C, indicating the presence of x iron carbide, and on tempering at 700°C the specimen developed a Curie point at 190°C which was assigned to 0 iron carbide. The carbides were extracted electro-lytically and the use of X-ray diffraction techniques4r5 indicated the carbide with a Curie point of 230°C to be x iron carbide. The Curie points of the carbides are 10 to 22°C lower than the accepted values which is probably due to the presence of manganese in the carbides, since it has often been observed (e.g., Ref, 6) that a partial substitution of manganese for iron in cementite will lower the Curie point of this carbide. Hofer&apos; summarizes additional evidence of the tempering reactions in steel in which E iron carbide, formed during the first stage of tempering, transforms to x iron carbide during the second stage of tempering. During the third stage of tempering, the x carbide disappears as the 0 carbide is formed. By carburizing thin iron films in a CO gas stream, ~a~akura&apos; has been able to produce the E, X, and 0 iron carbides. He found that below 250°C the E iron carbide was formed; between 250" and 350°C the x iron carbide was formed and above 350°C the 0 iron carbide was formed. He has shown that the E iron carbide transforms to form x iron carbide at 380" to 400°C and that the x ir°n carbide transforms to form the 0 iron carbide at approximately 550" C; both of these phase transformations are irreversible. Hofer&apos; presents a review of evidence to show that the sequence of reactions occurring during tempering processes subsequent to the formation of E iron carbide formed by the direct carburization of finely divided a iron is the same as the sequence of reactions which occur during the tempering processes subsequent to the formation of E iron carbide in steel during the first stage of tempering. It is evident from Nagakura&apos;s work that identical tempering reactions are found in thin films of iron which have been carburized to form iron carbide. The purpose of this paper is to discuss the structural similarities between the E, X, and 0 carbides and to suggest a possible mechanism by which regions of the E carbide, formed during the first stage of tempering, may transform to the x carbide during the second stage of tempering. For the finely divided or thin film carbides a mechanism will be proposed for the transformation of the x carbide to the 0 carbide during the third stage of tempering, although it will be suggested that there is evidence that such a transformation may not occur in steels. STRUCTURAL DATA OF THE E, X, AND 0 IRON CARBIDES € Iron Carbide. It is evident from X-ray diffractions and electron diffraction&apos;, investigations that the metal atoms in the E iron carbide form an hcp structure with lattice constants ah = 2.752A, ch = 4.3534, using electron diffraction, reports the lattice paramet$rs of the superlattice cell to be a = 4.767A, c = 4.354, c/a = 0.9134. He finds that the carbon atoms occupy the octahedral voids in the metal atom structure so as to form a hexagonal stacking sequence with its basal plane parallel to that of the metal atoms. Considerable long-range disorder occurs in the positioning of the carbon atoms, however, which is in agreement with the possible range of composition Fe2C-Fe3C discussed by Hofer.&apos; Barton and ale" have made X-ray diffraction measurements on a sample of E iron carbide extracted from a catalyst in an organic process. Although there were few reflections recorded on the obtained X-ray powder diffraction pattern, they have proposed that the structure could belong to one of the three possible space groups p3m1, P63/mmc, or Pbcn if one assumed the composition to be Fe2C. Nagakura, using electron diffraction data, suggests a space group of P 6322 for a specimen of c iron carbide of apparent composition Fez.&. x Iron Carbide. The x iron carbide has been studied by Duggin and Hofer" and by Jack and wild,&apos; who

Jan 1, 1969

By M. H. Richman, W. D. Sproul

THE indexing of a field-ion micrograph is in many cases similar to the indexing of the poles of a stereo-graphic projection.* If one has a standard projection as a guide, the task of indexing is relatively simple. In this way, field-ion micrographs of bcc and fcc wires have been oriented from projections available in most any text on X-ray diffraction. These books always illustrate the projections for the bcc and fcc structures and even for a particular hcp structure. There is no "standard" hcp projection because the angles between planes depend on the c/o ratio of the unit cell. In order to index field-ion micrographs of hcp metals, one must compute the angles between various planes—a rather laborious task. In recent work,, we have had to identify the structure and index the orientation of field-ion micrographs of the compounds WC and W,C. To overcome the problem of computing angles by hand or calculator, a program was written in Fortran lV for use on the IBM 360, Model 50 which will compute all angles between planeswith indices (hlklll) and (17,k,l2) in the range from (447) to (444) for any given c/o ratio. The program, which is more specific than that of Camp and clum, was so written as to take advantage of the multiplicity of the hexagonal system, and, for the limits defined above, only 26,649 values out of a possible 265,721 values had to be computed. This is a 90 pct saving in time (and cost) and was accomplished in the following way. Because the lattice parameters of the hexagonal crystal system are defined such that: a = b * c [1] the I index does not enter into the multiplicity (i.e., it cannot be transposed with the h or k indices), and all possible values of h and I, from 4 to 4 must be used—a total of eighty-one combinations. The index h2 varies the most—it must assume values from - Ill,: to 3Ihl. The indices kl and k2 are always equal and vary

Jan 1, 1969

By P. O. Metz, E. L. Wiehe, J. S. Foster

BASED on their analyses of growth kinetics, ibbs&apos; and Harris et al.&apos; have recently proposed that the rate of subcritical graphitization of steel is controlled by the rate of diffusion of carbon in ferrite. illert has concluded that this is the rate controlling growth mechanism when the growing graphite particles are relatively large. Harris et al.&apos; also propose that the matrix surrounding a growing graphite particle is plastically deformed to make room for the growing particle. If this plastic deformation does occur, then preferred recrystallization may be observed around the larger particles. If diffusion of carbon in ferrite is rate controlling, then a graphite particle growing in a matrix of, say, tempered martensite or pearlite, should be surrounded by a carbide depleted zone. Thus, the simple metallographic experiments reported here are sufficient to determine whether or not diffusion of carbon in ferrite is the dominant mechanism for the growth of graphite in steel. The present investigation considers graphitization in five alloys. The compositions are given in Table I. Graphitization was carried out at three temperatures: 900°K (627"C), 950°K (677"C), and 990°K (&apos;717°C). Samples were reacted in both the martensitic and the pearlitic initial conditions. In the hypoeutectoid steels, Sets 7 and 8, .and in the hypereutectoid Fe-C binary, Set 6, graphitization was very limited after 1000 hr at temperature. In these samples graphite particles observed were less than 10 p in diam. In the hypereutectoid commercial steels, Sets 1 and 3, large graphite particles (100 p) did not appear until after 250 hr at temperature. The limited number of graphite particles observed and the range of sizes obtained prohibited measurement of growth rates in this investigation. However, in all samples showing graphitization, neithe a carbide depleted zone nor recrystallization was observed. illert&apos;s model predicts that diffusion of carbon in ferrite should become dominant for graphite particles larger than about 300 p in diam. The largest graphite particle observed in this investigation was approximately 450 p in diam. No evidence of carbide depletion was noted. Fig. 1 shows a typical graphite particle. This nodule is from an initially pearlitic sample from Set 3 after

Jan 1, 1970

By Shiro Ban-ya, John F. Elliott, John Chipman

The activity of carbon in Fe-C austenite at 1150°C has been determined for concentrations up to about 2.1 pct C using the equilibrium: C + COz = 2CO; equations have been derived expessing the activity as a function of carbon content on the basis of twelve mathematical models. Several of these represent the data satisfactorily. ACCURATE information on the thermodynamic properties of austenite in the binary system Fe-C is needed as a basis for studies of transformation and precipitation in steels of all sorts, alloy as well as plain carbon. The many attempts to approach this problem through statistical thermodynamics require sound and dependable experimental data in order to evaluate the several models which have been suggested. In this paper we are concerned with the experimental determination of the activity-composition relation in austenite at the temperature of its widest range of stability, approximately the eutectic temperature (1153°C). Accurate investigation of the activity of carbon in austenite may be said to have begun with the work of Dunwald and wagner.&apos; A more detailed study was carried out by R. P. smith2 on the two equilibria: More recent work on these two equilibria has been reviewed by Chipman,3 who pointed out the experimental hazards associated with studies of Eq. [I]. Studies of this reaction involve rather small values of the ratio these are susceptible to errors due to traces of moisture in the apparatus according to the reaction: Ellis, Davidson, and Bodsworth4 evaluated K, for their experimental temperatures and used desiccants to control water vapor pressure. While they were able in this way to obtain consistent values for K1 it cannot be said that all of the uncertainties of the method have been overcome. Results by both methods reported by Schurmann, Schmidt, and wagener5 appear to be consistent except at very low carbon content. Reaction [2] was employed in the experimental work reported here. It is to be recognized, however, that it is not applicable to projected studies of certain alloy steel compositions involving stable oxide-formers.

Jan 1, 1970