By D. W. Smith, Robert F. Mehl

It has been shown by numerous studies that the orientations of new metal crystals are determined by the orientations of the crystals in the original matrix, whether these new crystals are formed by recrystalliza-tion, by precipitation from solid solutions, or by transitions in the solid state. The orientations of crystals formed by recrystallization of cold-worked metals that bear preferred orientations are occasionally simply related to the initial preferred orientation; often, however, the relationship is not simple, but complicated and obscure in origin.1 The orientations of crystals formed by precipitation from solid solutions have been shown by many studies in this and other countries to be determined by the orientation of the crystals of the solid solution stable at the higher temperatures, though here again complicated cases have been found and no general theory is available.2 Related to this latter class are the relationships found in crystals formed by suppressed transforma-

Jan 1, 1935

By D. W. Smith, Robert F. Mehl

It has been shown by numerous studies that the orientations of new metal crystals are determined by the orientations of the crystals in the original matrix, whether these new crystals are formed by recrystalliza-tion, by precipitation from solid solutions, or by transitions in the solid state. The orientations of crystals formed by recrystallization of cold-worked metals that bear preferred orientations are occasionally simply related to the initial preferred orientation; often, however, the relationship is not simple, but complicated and obscure in origin.1 The orientations of crystals formed by precipitation from solid solutions have been shown by many studies in this and other countries to be determined by the orientation of the crystals of the solid solution stable at the higher temperatures, though here again complicated cases have been found and no general theory is available.2 Related to this latter class are the relationships found in crystals formed by suppressed transforma-

Jan 1, 1935

By Robert F. Mehl, Edward L. McCandless

Oriented overgrowths and intergrowths among both metallic and nonmetallic substances have been recognized and studied for well over a century. The work of Widmanstätten in 1808 on the geometrical structure in meteorites, a structure known by his name, demonstrated that oriented intergrowths can occur in purely metallic systems. This fact led to much of the early microscopic study of alloys, contributing greatly to the advance of physical metallurgy. The problem has been attacked again in recent years in a comprehensive fashion, with the object of discovering what atomic movements may occur during phase changes in alloy systems. Much of this work has appeared in the A.I.M.E. Transactions in a series of papers published by Mehl and coworkers beginning in 19311. Although many aspects of this general problem remain unsolved, it may be said that the orientation of a new phase forming by precipitation from solid solution or by transformation invariably bears a unique relationship to the orientation of the phase from which it formed, and that similarity in atomic patterns on atomic planes in the two phases play an important part in determining the orientation relationship. Analogous orientation relationships exist in oriented intergrowths in nonmetallic systems—mineral or inorganic. In 1827 Haidinger2 discovered natural intergrowths of hematite and magnetite, and demonstrated that the rough form of the magnetite octahedrons was delineated by small crystals of hematite, of which the basal (00.1) planes lay parallel to the octahedral cleavage planes of the magnetite. The description of this orientation relationship was later completed by von Rath3, who showed that the edge (00.1): (10.1) in hematite lies normal to the [Ill]

Jan 1, 1937

By T. L. Joseph

The extent to which hot metal from the blast furnace affects open-hearth practice and the quality of steel produced has been discussed widely. Open-hearth operators have attributed difficulties experienced in making satisfactory steel to characteristics of the pig iron not disclosed by ordinary analysis. The commonest criticism of the iron has been that it is "physically cold" or "dirty." Often when the blast furnaces are working irregularly the quality of the iron is questioned. A cold hearth, slipping and hanging, the use in the past of unsintered flue dust, and the use of ores difficult to smelt have been associated with the production of iron of poor quality. The difficulty of the situation is that we have no proven yardstick for quality aside from ordinary analysis. Uniformity in analysis is recognized as being important, but the difficulty of changing the open-hearth practice when the iron analysis varies widely may not always be fully appreciated. Although the problem of correlating the characteristics of steel with those of pig iron is admittedly obscure, the effort of producers of quality steel to investigate all factors that may have a bearing on the final product is justified. This report contains data on the oxides in several hundred casts of basic iron produced in a furnace during the course of normal operation on Lake ores. Incidental to the study of the oxides in the iron, it was desirable to follow closely the temperature of the iron. The effect of temperature of the iron upon the silicon and sulphur present is discussed. A general relation between the basicity of the slag and the sulphur in the metal was developed. The amount and composition of oxides in the hot metal and in the steel bath during various intervals between melt-down and tap are discussed. Heats of rimmed steel, killed steel, and semikilled steel were investigated. The hot metal on individual heats was either all taken from a mixer or consisted partly of direct metal and partly of metal from the mixer. Samples of the iron for oxide determinations were

Jan 1, 1937

By J. Elmer Thomas

The evolution of the oil business is one of the great industrial romances of modern times. First used as a medicine, then as a lubricant, then as an illuminant, and finally as a motor fuel, each change in its principal usage caused large increases in consumption. Producing Successes The producing branch of the industry responded ably to the demands made upon it. Never was there a famine, rarely any threat of scarcity, and stored inventories were gradually accumulated to form comfortable working stocks. Originally an erratic and hazardous undertaking, the discovery and development of oil fields has made such strides as to classify now as a science. When storage stocks were low, production in close balance with consumption, and demand trending sharply upward, considerable concern was expressed over future needs. Price was very responsive to fluctuations in supply under those conditions, and quotations for crude and refined oils exhibited wide swings. A very different situation exists today. Consideration of the statistics only since the war will show how recent has been this change. In the 10-year period from 1918 to 1927 inclusive, we produced in the United States 6,100,000,000 bbl. of crude and imported 900,000,000 bbl., our total supply being 7,000,000,000 bbl. The consumption was 6,600,000,000 bbl., thus adding to stocks 400,000,000 bbl., an accumulation of somewhat less than 6 per cent. of the total supply. During that period virtually every field was promptly developed as soon as discovered and nearly every well in the country was producing at full capacity. With the maximum production of the wells required to take care of the rapid increases in consumption, with storage stocks moderate and proven reserves very slight, the producing division of the industry acquired a tempo not needed now. Potential Surplus Today the situation is vastly different. The economic consumption is about 2,700,000 bbl., with current production slightly in excess of that.

Jan 1, 1930

By O. W. Ellis

The question of the influence of gases upon the properties of copper has received the attention of a number of investigators, among whom Sieverts,' Iwase,2 Lobley and Jepson3 stand preeminent. Solubility of Gases in Copper Sieverts and Iwasé concerned themselves with the solubility of a variety of gases in the metal in the solid and liquid states. They determined the absorption coefficients of these gases and in all cases found a sharp change in solubility at the melting point of the metal. In this respect they disagree with Lobley and Jepson, who have based their opinions upon the appearance of small ingots of the metal which had been fused in an atmosphere of one or other of three gases and had then been rapidly cooled, while surrounded by gas, to the freezing point (rate—possibly 30" to 60" C. per sec.). The ingots that had been fused and cooled under nitrogen and carbon monoxide were free from blowholes and it was assumed that these gases were not absorbed in amounts much in excess of those which would dissolve in the solid metal; the ingots similarly treated under hydrogen were full of blowholes and it was assumed in this case that gas was ejected on solidification of the copper. The effect of varying the rate of freezing upon the character of the test ingots was not examined by these investigators; otherwise, it is felt, their views might have been subject to modification. Sieverts' most important contribution is that the solubility of a gas in any metal is proportional to the square root of its pressure or concentration. Knowing then the absorption coefficients of the various gases in copper, it should be possible to determine the analysis of the

Jan 1, 1929

By O. W. Ellis

The question of the influence of gases upon the properties of copper has received the attention of a number of investigators, among whom Sieverts,' Iwase,2 Lobley and Jepson3 stand preeminent. Solubility of Gases in Copper Sieverts and Iwasé concerned themselves with the solubility of a variety of gases in the metal in the solid and liquid states. They determined the absorption coefficients of these gases and in all cases found a sharp change in solubility at the melting point of the metal. In this respect they disagree with Lobley and Jepson, who have based their opinions upon the appearance of small ingots of the metal which had been fused in an atmosphere of one or other of three gases and had then been rapidly cooled, while surrounded by gas, to the freezing point (rate—possibly 30" to 60" C. per sec.). The ingots that had been fused and cooled under nitrogen and carbon monoxide were free from blowholes and it was assumed that these gases were not absorbed in amounts much in excess of those which would dissolve in the solid metal; the ingots similarly treated under hydrogen were full of blowholes and it was assumed in this case that gas was ejected on solidification of the copper. The effect of varying the rate of freezing upon the character of the test ingots was not examined by these investigators; otherwise, it is felt, their views might have been subject to modification. Sieverts' most important contribution is that the solubility of a gas in any metal is proportional to the square root of its pressure or concentration. Knowing then the absorption coefficients of the various gases in copper, it should be possible to determine the analysis of the

Jan 1, 1929

By B. Egeberg, H. B. Smith

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929

By H. B. Smith, B. Egeberg

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

By David Sinclair, Philip B. Bucky

The dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests. § None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their application in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I The Photoelastic Method The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution. General Explanation The stress at any point 0 in a structure (Fig. I), may be resolved into two components, P and Q, each a pure tension or compression, at right angles to each other, called principal stresses.' To fully identify the stress, the values of P and Q and their directions or angle F must be known.

Jan 1, 1940

By David Sinclair, Philip B. Bucky

The dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests. § None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their application in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I The Photoelastic Method The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution. General Explanation The stress at any point 0 in a structure (Fig. I), may be resolved into two components, P and Q, each a pure tension or compression, at right angles to each other, called principal stresses.' To fully identify the stress, the values of P and Q and their directions or angle F must be known.

Jan 1, 1940

By R. E. Head

Under existing economic conditions, the treatment of gold ores occupies an outstanding position in metallurgical activity. The increased price of gold has automatically brought about a reclassification of old dumps and low-grade orebodies, and many that formerly were considered valueless are now being vigorously investigated and worked. This situation has developed problems that have taxed the ingenuity and ability of metallurgists to the utmost. Some gold ores give a high extraction of gold by standardized methods of treatment; other ores of apparently similar character yield but a relatively small percentage of their gold when treated by the same processes. Surface Contamination The experience gained by microscopic study of numerous gold ores and tailings has shown that there are pronounced differences in the physical characteristics of the minerals composing them, more especially of the gold. Repeated studies of tailings from flotation and cyanidation of gold ores has established the fact that surface contaminations on gold particles are often directly responsible for high gold losses; comparison of gold particles isolated from flotation concentrates and the resulting tailings have showed that the clean gold has been recovered and the tarnished or contaminated gold invariably lost in the tailing. Obviously, it is not possible to make such a comparison of gold ores treated by cyanidation, as the clean gold has been taken into solution; but when the gold found in cyanide tailing has a tarnished or coated surface, one may infer, with a reasonable degree of certainty, that the clean gold has been extracted. This premise is supported by experimental evidence obtained by isolating particles of tarnished gold and exposing them to cyanide solution in small parting cups. In one such experiment, tarnished gold particles picked from a cyanide tailing showed but slight evidence 01 dissolving at the end of 27 days. In this test, a cyanide solution of 1.6 11). per ton was used and the leach solution was decanted arid renewed every

Jan 1, 1939

By R. E. Head

Under existing economic conditions, the treatment of gold ores occupies an outstanding position in metallurgical activity. The increased price of gold has automatically brought about a reclassification of old dumps and low-grade orebodies, and many that formerly were considered valueless are now being vigorously investigated and worked. This situation has developed problems that have taxed the ingenuity and ability of metallurgists to the utmost. Some gold ores give a high extraction of gold by standardized methods of treatment; other ores of apparently similar character yield but a relatively small percentage of their gold when treated by the same processes. Surface Contamination The experience gained by microscopic study of numerous gold ores and tailings has shown that there are pronounced differences in the physical characteristics of the minerals composing them, more especially of the gold. Repeated studies of tailings from flotation and cyanidation of gold ores has established the fact that surface contaminations on gold particles are often directly responsible for high gold losses; comparison of gold particles isolated from flotation concentrates and the resulting tailings have showed that the clean gold has been recovered and the tarnished or contaminated gold invariably lost in the tailing. Obviously, it is not possible to make such a comparison of gold ores treated by cyanidation, as the clean gold has been taken into solution; but when the gold found in cyanide tailing has a tarnished or coated surface, one may infer, with a reasonable degree of certainty, that the clean gold has been extracted. This premise is supported by experimental evidence obtained by isolating particles of tarnished gold and exposing them to cyanide solution in small parting cups. In one such experiment, tarnished gold particles picked from a cyanide tailing showed but slight evidence 01 dissolving at the end of 27 days. In this test, a cyanide solution of 1.6 11). per ton was used and the leach solution was decanted arid renewed every

Jan 1, 1939

By Eric R. Jette, Earl S. Greiner

Although the mechanical and chemical characteristics of certain iron-nickel-silicon alloys have been investigated,1 the available literature shows no results of a systematic investigation of the constitution of this system. 'This paper describes the results of an X-ray investigation of the constitution of the iron-rich iron-nickel-silicon alloys at 600°C. Data 011 the constitution of the included binary systems obtained in other investigations have been correlated with the structure of the ternary alloys. Jette and Foote2 have presented a tentative constitutional diagram of the iron-nickel system. following X-ray studies on quenched specimens. This diagram shows that the alloys at 600°C. containing from zero to approximately 4 atomic per cent nickel consist of a body-centered cubic (alpha) phase, the alloys containing 4 to 24 atomic per cent nickel consist of body-centered cubic (alpha) and face-centered cubic (gamma) phases, and the alloys containing from 24 to Ioo atomic per cent nickel consist of a face-centered cubic (gamma) phase. These investigators recognized that it was not possible to retain the gamma phase in equilibrium by quenching alloys containing less than approximately 25 atomic per cent nickel and that high-temperature X-ray methods were desirable to determine the gamma-phase solubility limit. In a later investigation of the iron-nickel alloys, Owen and Sulley3 determined the alpha-phase solid solubility limit to be 3.5 atomic per cent nickel at 600°C. High-temperature X-ray methods showed the solid solubility limit of the gamma phase to be 14 atomic per cent nickel at 600°C. Since the high-temperature X-ray method should reveal equilibrium conditions in these alloys better than the quench method of other investigators, the results of Owen and Sulley pertaining to the gamma-phase boundary are to be preferred. As the result of an X-ray investigation of quenched iron-silicon alloys, Greiner and Jette4 have shown these materials to consist of a body-centered cubic (alpha) phase containing from o to 26.4 atomic per cent silicon at 600°C. The alloys containing from 26.4 to approximately 50 atomic per cent silicon consist of two phases at 600°C.; namely, alpha and eta. The eta phase corresponds to the stoichiometrical formula FeSi (33.4 wt per cent Si)." The literature pertaining to the constitution of the nickel-silicon alloys has been reviewed by Ackerman,' who found disagreements in the results of various investigators on several parts of the system. Subsequent data on the constitution of the nickel-silicon alloys were reported by oSawa and okamoto.6

Jan 1, 1943

By Earl S. Greiner, Eric R. Jette

Although the mechanical and chemical characteristics of certain iron-nickel-silicon alloys have been investigated,1 the available literature shows no results of a systematic investigation of the constitution of this system. 'This paper describes the results of an X-ray investigation of the constitution of the iron-rich iron-nickel-silicon alloys at 600°C. Data 011 the constitution of the included binary systems obtained in other investigations have been correlated with the structure of the ternary alloys. Jette and Foote2 have presented a tentative constitutional diagram of the iron-nickel system. following X-ray studies on quenched specimens. This diagram shows that the alloys at 600°C. containing from zero to approximately 4 atomic per cent nickel consist of a body-centered cubic (alpha) phase, the alloys containing 4 to 24 atomic per cent nickel consist of body-centered cubic (alpha) and face-centered cubic (gamma) phases, and the alloys containing from 24 to Ioo atomic per cent nickel consist of a face-centered cubic (gamma) phase. These investigators recognized that it was not possible to retain the gamma phase in equilibrium by quenching alloys containing less than approximately 25 atomic per cent nickel and that high-temperature X-ray methods were desirable to determine the gamma-phase solubility limit. In a later investigation of the iron-nickel alloys, Owen and Sulley3 determined the alpha-phase solid solubility limit to be 3.5 atomic per cent nickel at 600°C. High-temperature X-ray methods showed the solid solubility limit of the gamma phase to be 14 atomic per cent nickel at 600°C. Since the high-temperature X-ray method should reveal equilibrium conditions in these alloys better than the quench method of other investigators, the results of Owen and Sulley pertaining to the gamma-phase boundary are to be preferred. As the result of an X-ray investigation of quenched iron-silicon alloys, Greiner and Jette4 have shown these materials to consist of a body-centered cubic (alpha) phase containing from o to 26.4 atomic per cent silicon at 600°C. The alloys containing from 26.4 to approximately 50 atomic per cent silicon consist of two phases at 600°C.; namely, alpha and eta. The eta phase corresponds to the stoichiometrical formula FeSi (33.4 wt per cent Si)." The literature pertaining to the constitution of the nickel-silicon alloys has been reviewed by Ackerman,' who found disagreements in the results of various investigators on several parts of the system. Subsequent data on the constitution of the nickel-silicon alloys were reported by oSawa and okamoto.6

Jan 1, 1943

By Charles T. Holland

In connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. It is generally agreed that one of the necessary conditions for bumps is a strong coal.' Therefore, since the strength of coal is an important factor, a study of this property should be made. several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semihituminous (Pocahontas No 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the Same coal.

Jan 1, 1942