By Warren J. Bruckard, Mark I. Pownceby, Sazzad Ahmad, M. Akbar Rhamdhani

Rutile is the preferred feedstock for producing high-grade TiO2 pigment but due to decreasing resources, alternative materials such as ilmenite is now used to produce a synthetic rutile (SR) feedstock. This requires removal of impurities (e.g. Fe, Mg, Mn) which, for a primary ilmenite is straightforward process. Processing of weathered ilmenite however, is complex, especially when chrome-bearing impurities are present since minor chromium downgrades the SR market value as it imparts color to the final TiO2 pigment, Chrome-bearing spinels are a problem in weathered ilmenites from the Murray Basin, Australia as their physical and chemical properties overlap with ilmenite making separation difficult. In this paper, different sulfidation process routes for weathered ilmenites are analyzed for their applicability to Murray Basin deposits as a mean of remove chrome spinel impurities. Thermodynamic and experimental studies indicated that selective sulfidation of chrome-bearing spinel can be achieved under controlled pO2 and pS2 processing conditions thereby making them amenable to separation.

Jan 1, 2015

By Katia Vutova, Vania Vassileva

Investigations and results on the refining of tungsten scrap applying electron beam melting (EBM) in vacuum are presented and discussed. In this work EB melting experiments were performed in single or double-melt operations with different power inputs and refining times for tungsten purification and recovery of multiple metals (including refractory and other metals such as Mo, Nb, Cu, Zn, etc.), which are alloyed elements or impurities with high concentrations in the initial materials. Evaluations for extraction of some valuable metals, generated in the condensate at their removal from the liquid metal during the refining process are provided. Efficient technological regimes for e-beam melting and refining that enable the simultaneous production of pure metal ingots and condensates that can be used directly or can be used for subsequent extraction of expensive and valuable metals are presented.

Jan 1, 2016

By Jinjing Dua, Jun Zhua, Kuiren Liub, Bin Wang, Xiaolei Wua

V-Ti-Fe as hydrogen storage alloy was prepared by reducing metal oxides with a metallothermic reduction method. The deoxidation process of the V-Ti-Fe alloy was performed by electro-deoxidation and vacuum induction melting method, respectively. The results showed that the content of oxygen impurity can be controlled at about 0.2wt% after electrolyzing for 240min. Both the maximum values of hydrogen absorption capacity and the effective hydrogen desorption capacity are 2.65wt% and 1.01wt%, respectively. The deoxidization effect of vacuum induction melting process is more remarkable, with Ce as the reducing agent. It is found that Ce addition is beneficial for reducing the componential segregation, promoting the hydrogen absorption activation of V-Ti-Fe alloy. When m(Ce)/m(alloy) is up to 5%, the oxygen content has been reduced to 0.05wt% and the maximum hydrogen absorption capacity and the effective hydrogen desorption capacity are up to 3.36wt% and 1.85wt%, respectively.

Jan 1, 2015

By Ernest D. Mast

Noranda's Altonorte custom smelter, located in the 2nd region of Chile, 20 kilometres southeast of the city of Antofagasta, started operations in 1993. Presently, 1150 tonnes per day of new feed are smelted with an 85% sulphur capture. An oxy-fuel reverberatory furnace produces a 48%-55% copper matte that is treated in 13 ft. x 36 ft. (3..96m x 10.97m) Peirce-Smith converters (two hot and one blowing). Up to thirty percent of the new concentrate is smelted via dry concentrate injection into the converters. This paper reviews the development of the concentrate drying and injection system, and oxygen enrichment at Altonorte from start-up in 1995 to the present time. The relationship between oxygen enrichment and concentrate injection is reviewed from a theoretical and practical standpoint. Concentrate injection has improved the smelter's productivity and added flexibility to the operations. Due to the relatively high matte grades and the subsequent short converting times, maintaining consistent operations was difficult at times and the smelter has gone through a learning curve. Plant operating results and experiences are presented on the impact of concentrate injection in relation to: feed treatment, blowing times, revert generation, slag quality and refractory wear.

Jan 1, 1999

By Donggen Fang, Liu Xuan, Jilai Xue

SiO2 and Al2O3 in the metallurgical slag of nickel laterite ore have great recycling values. In this work, Si and Al were extracted from the slag in NaOH based molten salts through alkali roasting and water leaching process for preparing zeolite materials. The extraction ratio of SiO2 increases with increased temperature and appropriately prolonged time, and more than 80% SiO2 can be recycled from the slag after roasting at 550°C. Si and Al from the slag are in the filtered liquor for producing zeolite materials, while Mg, Ca, Fe and other impurities remain in the leached residues. Adding Na2CO3 into the alkalin-slag roasting process can reduce the amount of pure NaOH used with minor decrease in extraction ratio of SiO2, while make better separation of Ca to avoid it getting into the filtered liquor. Adding Al2O3 into the alkalin roasting process can replace part of more expensive NaAlO2 addition that is required for preparing zeotite material, which may bring out a minor decrease in extraction ratio of SiO2 due to formation of NaAlSiO 4 in the filtered residues. Quality X zeolite and 4A zeolite materials can be made from the starting liquor containing Si and Al recycled from the laterite nickel slag through alkali roasting and water leaching process.

Mar 1, 2018

By Mansoor Barati, Yindong Yang, Yonggang Wei, Bo Li, Alexander McLean

Reduction roasting followed by magnetic separation is an important method for treating laterite nickel ores. In this work, garnierite type laterite ore from Yunnan province in China was reduced by methane under different conditions followed by magnetic separation to obtain the ferronickel concentrate. The phase and microstructure transformations of garnierite in the reduction process were investigated using XRD and SEM-EDS. The experimental results showed that reduction temperature from 873 to 1173 K had only a small effect on content and recovery of nickel and iron. The content and recovery of nickel and iron in the concentrates increased slightly with prolonging reduction time. In addition, the nickel and iron content decreased with increasing methane concentration, but the recovery of nickel and iron increases. A decrease in the iron content and recovery were observed when the dosage of sodium sulfate varied from 5 to 20% at a temperature of 1073 K and reducing time of 90 min, while the nickel content and recovery gradually increased.

Mar 1, 2018

By Wen-long Zhan, Chun-en Zhu, Xiao-dong Du, Yong Zhao, Keng Wu

In view of the traditional evaluation index of sintering basic character- istics ignoring process information, several high temperature characteristic num- bers, which contain process information, were used to evaluate the sintering basic characteristics more comprehensively in this paper. The evaluation model of iron ore properties was established based on the high temperature characteristic numbers with employing fuzzy mathematics. Then, with the constraint of sinter properties and the raw materials, the ore blending model was built, whose target was to obtain the lowest cost and the best sinter properties. A multi-objective fuzzy linear pro- gramming was used to solve the model in order to get the best ore matching schemes. The ore blending model was then applied to the practical production, which was proved to be dependable.

Mar 1, 2018

By Shangshu Li, Xionggang Lu, Xingli Zou, Zhongya Pang, Kai Zheng, Yinshuai Wang

Metal carbides (MCs), especially transition metal carbides have attracted a lot of attention due to their unique properties, such as high strength and hardness, good chemical and thermal stability. In this paper, a new route was proposed for preparing TiC nanoparticles directly from TiO 2/C precursor by using solid oxide membrane (SOM) technology in molten CaCl2. The TiO2/C pellet pressed under 8 MPa was used as the cathode, and a yttria-stabilized zirconia (YSZ) tube filled with carbon-saturated liquid tin was served as the anode. This process employs an inert SOM to separate the anodic reaction area from the molten electrolyte to control the electrolysis process. The electrochemical process was carried out in molten CaCl2 at 1000°C and 4.0 V from 0.5 to 4 h. The characteristics of the phase composition and morphology of the electrolysis products were investigated. The product electrolyzed was examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy dispersive spectrometer (EDS). The results show that TiC nanoparticles can be obtained directly from TiO2/C mixture at 1000 °C, 4.0 V and for 4 h in molten CaCl 2 and the current efficiency is calculated to be 74.1%. In conclusion, we suggest that the SOM process is a promising environmentally friendly and low energy costs electrochemical method for the facile and controllable electrodeoxidation of MO x/C precursors to micro/ nanostructured MCs.

Mar 1, 2018

By Bin Xu, Qian Li, Xishan Li, Yongbin Yang, Hongwei Li, Tao Jiang, Yan Zhang

The cyanide leaching rate of gold from a multi-refractory gold concentrate (18.05 g/t Au) containing 1.62% As, 20.76% S, 6.95% C and 1.31% Sb was only 1.33%. The enhancement of gold leaching was studied mainly by the pretreatment of oxidative roasting and alkaline sulfide washing. Results showed that after the two-stage roasting (i.e., I stage of 500 °C, 1 h and II stage of 700 °C, 2 h) most of sulfur (93.84%) and carbon (98.27%) were removed, but the gold leaching rate of calcine just reached 71.33% because the residual arsenic (0.63%) and antimony (1.15%) were still high. After alkaline sulfide (i.e., NaOH and Na2S) washing, the residual arsenic and antimony was further decreased to 0.21 and 0.65%, respectively. The gold leaching rate of the treated calcine by cyanidation could increase to 93.52% substantially. Also, the optimized particle size, NaCN concentration and leaching time were −0.045 mm over 85%, 0.1% and 36 h, respectively.

Mar 1, 2017

By Maria S. Gudjonsdottir, Miao Yu, Gudrun Saevarsdottir, Pall Valdimarsson

Around half of the energy consumed in aluminum production is lost as waste heat. Approximately 30–45% of the total waste heat is carried away by the exhaust gas from the smelter and is the most easily accessible waste heat stream. Alcoa Fjarðaál in east Iceland produces 350 000 tons annually, emitting the 110 °C exhaust gas with 88.1 MW of heat, which contains 13.39 MW exergy. In this study, three scenarios, including organic Rankine cycle (ORC) system, heat supply system and combined heat and power (CHP) system, were proposed to recover waste heat from the exhaust gas. The electric power generation potential is estimated by ORC models. The maximum power output was found to be 2.57 MW for an evaporation temperature of 61.22 °C and R-123 as working fluid. 42.34 MW can be produced by the heat supply system with the same temperature drop of the exhaust gas in the ORC system. The heat requirement for local district heating can be fulfilled by the heat supply system, and there is a potential opportunity for agriculture, snow melting and other industrial applications. The CHP system is more comprehensive. 1.156 MW power and 23.55 MW heating capacity can be produced by CHP system. The highest energy efficiency is achieved by the heat supply system and the maximum power output can be obtained with the ORC system. The efficiency of energy utilization in aluminum production can be effectively improved by waste heat recovery as studied in this paper.

Mar 1, 2018

By Xu Weimin

The existing copper electrorefining tankhouse of Jinchuan Nonferrous Metals Complex (JNC) was commissioned in 1986 for refining blister copper anodes. Blister copper is produced by reverberating chalcocite separated from converter high grade nickel-copper matter by means of flotation. Special chemical analysis of the anodes shows, a composition of 93.02 - 95.72 % copper, 3.0 - 4.96 % nickel and 0.5 - 1.23 % sulfur. The wide range of composition makes the electrorefining process fairly different from others throughout the world. The initial nickel content of 20 ppm and sulfur 40 ppm or more in copper cathodes are reduced to 8.5 ppm and 11 ppm respectively. Since 1986 the tankhouse has undergone significant evolutionary modifications and implementations to ameliorate cathodes quality desirably. The important fact is that the N-additive was utilized through many studies and pilot and field trials successfully. While our primary purpose is to improve chemical quality of the cathodes, tankhouse capacity is increased considerably and the process is perfected satisfactorily. The tankhouse is described with special emphasis on JINCHUAN PROCESS. The upgrading of our product by the utilization of the N-additive is highlighted. The other aspects of the tankhouse including spent electrolyte treatment and by product nickel sulfate manufacturing are briefed as well. Key words: JINCHUAN PROCESS, anode, cathode, electrolyte, electrorefining, N-additive.

Jan 1, 1993

By Filippos Patsiogiannis

Laboratory size (4.5 kg) low carbon steel melts were deoxidized using Al and FeAl (33% Al), with and without synthetic fluxes, in alumina and zirconia crucibles. The dissolved oxygen, total oxygen, soluble aluminum, insoluble aluminum, silicon and carbon contents in the melt were determined as a function of refining time and temperature. It was observed that the reaction between aluminum and oxygen in solution closely follows thermodynamic equilibrium. Silica present in the alumina crucibles was found to be a source of oxygen for the melt, while this was not the case for zirconia crucibles. Reoxidation of the melt occurred through oxygen pick-up from the atmosphere. The extent of this reoxidation was found to be a function of oxygen content of the bath and the slag cover on the surface of the melt. The effectiveness of calcium-aluminate based fluxes in protecting the melt from the reoxidation and in increasing the rate of removal of inclusions was evaluated.

Jan 1, 1992

By R. G. Reddy

Industrial copper reverberatory furnace slags were treated by high temperature techniques (sulfide and carbothermic reduction) to recover copper in alloy or matte phase at 1473K. Recovery was investigated for the condi¬tions of varying amounts of metallic sulfide, carbon and CaO additions. The results showed that recovery of copper increased with increasing amounts of carbon addition, and also is strongly dependent on the initial concentration of copper in the slags. Copper recovery for both carbothermic reduction and sulfide treatment were modeled with linear relationships as follows: for carbothermic reduction (%Cu recovery) = 9.0 (%Cu in slag)initial 73.8 and for sulfide (%Cu recovery) = 7.1 (%Cu in slag)initial 82.2 Higher copper recovery was obtained with sulfide treatment than with carbothermic reduction of slags.

Jan 1, 1983

By Keiji Okumura, Jiayi Shan, Jian Yang, Masamichi Sano

"A new method of deoxidation and desulfurization of molten iron with magnesium vapor has been developed. An immersion tube, which was filled with pellets of the mixture of magnesia and carbon powders, was put into the molten iron. Magnesium vapor produced by carbothermic reduction of magnesia inside the tube was injected directly into the molten iron with argon carrier gas. The effects of temperature and carrier gas flow rate on deoxidation and desulfurization were investigated. A mathematical model of the reactions was developed. The rates of deoxidation and desulfurization were controlled by mass transfers of magnesium vapor in the gas-phase and oxygen and sulfur in the liquid-phase. This method may offer high efficiency for magnesium deoxidation and desulfurization of molten iron.IntroductionMagnesium is a strong refining agent in steel-making processes1 • At steelmaking temperatures, magnesium has a very low solubility in liquid iron, and a very high vapour pressure2 • Deoxidation and desulfurization with magnesium take place essentially through the interaction of magnesium vapor with oxygen and sulfur dissolved in molten iron, and magnesium can change chemical composition of nonmetallic inclusions3 • However, addition of magnesium to the steel bath is dangerous and does not give high efficiency in the refining process4 • Furthermore, as a refining agent, the price of magnesium is higher than aluminium and CaO fluxes. In the present study, a new method of the deoxidation and desulfurization of molten iron was developed using magnesium vapour in-situ produced by carbothermic reduction of magnesium oxide. Pellets made of mixture of magnesia and carbon powders were charged into an immersion tube, which was made of alumina or graphite. The magnesium vapor was injected directly into the melt. The effects of pellet mass, experimental temperature and carrier gas flow rate were studied on the refining rate. A mathematical model of the refining reaction was proposed on the basis of the experimental results."

Jan 1, 2000

By Nourreddine Menad

Plastic materials have been associated with electric and electronic applications since the early days of the electrical industry. Plastics can amount to 30 percents of the scrap mass. Generally, they are treated with flame retardants such as halogenated ones and they can result in different toxic chemical compounds. These plastics can be used as combustibles in the recovery of copper and precious metals. However, during their combustion, halogenated flame retardants can produce dibenzo-p-dioxins and dibenzo-furans. The estimated thermodynamic data of several organic compounds resulting from combustion of electric and electronic scrap, have been used in conjunction with the program HSC to calculate the conditions for dioxin and furan formation. The results show that the formation of the dioxins is dependent on the quantities of carbon, hydrogen, chlorine and oxygen reacting in a given system, as well as on parameters such as temperature and pressure.

Jan 1, 1998

By Xiaojian Zuo, Yihua Han, Qingguo Xue, Jingsong Wang, Lintao Wang, Rongzong Lan

"Using the facility of reduction experiment, the low temperature reduction pulverization and reduction behavior of sinter in oxygen blast furnace (OBF) were studied. Through analyzing the results, the difference of pulverization and reduction behavior of sinter in OBF and conventional blast furnace (BF) were discussed. Furthermore, the effect laws of reduction temperature and the content of CO and H2 on reduction behavior of sinter were studied. Also the controlling step of iron oxide reduction was discussed. Compared with BF, the low temperature reduction pulverization of sinter became serious at 773 K; reduction rate became faster at 1173 K; reduction time became less and final reduction degree was increased in OBF. With increasing of H2 and CO contents, the reduction of sinter was promoted. The reduction process was controlled by interface chemical reaction at the earlier stage and by interface chemical reaction and internal diffusion at the final stage.IntroductionThe new ironmaking technology of Oxygen Blast Furnace (OBF) is most likely to be used in large-scale application process. The concept relies on the removal of the CO2 contained in the top gas of the blast furnace. Therefore the useful components, i.e. CO+H2, can be recycled back into the furnace and reused as reducing agents. In addition, injecting oxygen (O2) into the furnace instead of preheated air, removes unwanted nitrogen (N2) from the gas. Under the pressure of CO2 emissions in iron and steel making, the growing international shortage of coking coal resources and the rising price of coke, OBF has attracted attentions of both domestic and foreign researchers, because it has so many advantages such as high productivity, high PCI rate, low coke rate, high gas reducing capability and high top gas calorific value, etc [1-7]. As a result of recycling most of the top gas after CO2 removal and injecting oxygen into the furnace, the reduction capacity of blast furnace gas will be increased, so the metallurgical behavior of OBF's iron burden is different from traditional blast furnace. Therefore, it is one of the keys to develop this technology, which studies the metallurgical behavior of sinter in OBF. The purpose of this paper is to study the low temperature reduction pulverization and reduction behavior of sinter at the atmosphere of OBF, which includes the difference of low temperature reduction pulverization and reduction behavior of sinter in oxygen blast furnace and conventional Blast Furnace (BF). It will provide theoretical basis for the development of OBF."

Jan 1, 2012

By Vladimir I. Skorohodov

The technology for copper utilization from circuit boards etching is proposed. The technology is based on combination of electrochemical and sorption methods. The conditions of copper electroextraction from ammonia-chloride solutions with obtaining of cathode copper are defined. The stage of electrolysis is destined for copper recuperation from etching process. Due to the electrochemical processes are unacceptable for cathode precipitation of the copper from diluted solutions such as rinse waters, the concentration on the strong-based cationites are used. After filtration throw the sorption columns solution is directed to the stage of circuit boards washing. It allows organizing close loop water recirculation. After saturation. resin is 'regenerated by chloride ammonium solutions. Obtained eluate directed to the etching stage, Generally. the technology provides copper recuperation and minimize wastes amount.

Jan 1, 2001

By J. S. Becker

Technology developed and first implemented in the United Kingdom enables very low grade aluminum scraps containing oils, organics, plastics and ferrous metals to be directly charged, without pretreatment, into a unique melting furnace. The system has been in full scale production for four years. The oxy-fuel-based furnace design incorporates internal afterburning in the furnace's hot zone, producing excellent thermal efficiency and very low emissions. The furnace is inherently low in NOx. This paper will provide both theoretical background and extensive operating results for this new melting concept. Applications describing both purpose built new furnaces and retrofits of existing reverberatory furnaces will be presented. Extensive operating emissions data will be presented.

Jan 1, 1997

By J. H. Puffer

The copper mineralization of the Mesozoic Passaic Formation of New Jersey is typical of copper deposits in eastern North American Mesozoic sediments. Most such deposits are located at the base of the first of several basalt flows that are interbedded with continental, red-bed sediments. The copper mineralization is similar in most respects to that of the Keweenawan Basalts of the Lake Superior area. The first basaltic flow units of the eastern North American Mesozoic basins, and the Keweenawan Basalts, are continental quartz tholeiites of similar chemical composition and copper contents. The copper minerals and associated zeolite facies metamorphic mineral assemblages of these two rock units are also approximately the same. Stoiber and Davidson (1959) suggested that Keweenawan copper was mobilized and concentrated during metamorphism. The evidence pertaining to the Mesozoic copper deposits of New Jersey is consistent with such an interpretation and also with DeVore's (1955) suggestion that ore fluids commonly arise as a result of the mobility of metals under metamorphic conditions. There is additional evidence that final metamorphic concentration of Mesozoic copper was preceded by an initial stage of hydrothermal precipitation related to fluids emitted by basaltic magma.

Jan 1, 1987

By James W. Evans, Brian R. Wildey

"Carbon has been the principal reducing agent in producing metals for centuries. Carbon is an inexpensive reducing agent, but also an effective one, as any undergraduate who knows her Ellingham diagrams is aware. Even in the production of aluminum, an electrolytic process, carbon consumed at the anodes serves to reduce the voltage of the Hall-Héroult cell. The interest in reducing the amount of anthropogenic CO2 has led to this examination of whether a switch to hydrogen as a major reductant is feasible and economic. The main source of hydrogen is natural gas and its production entails the generation of CO2; however, that CO2 is more easily captured than, say, the CO2 leaving an iron blast furnace. Calculations and speculations lead to conclusions about whether there is significant benefit to be obtained from such a radical change in our way of producing metals and the approximate cost of such change.IntroductionThe 1991 paper by Forrest and Szekely1 was one of the first to examine the impact of CO2 emissions from the primary metals industries on global climate change. These authors compared data from 1968 and 1985 and reported a drop in carbon emissions from 115.8 million tons to 65.6Mt over this period, the latter figure representing approximately 1% of the world’s greenhouse gas emissions. Much of this reduction was due to a drop in steel output (with carbon emissions increasing within the aluminum and copper industries in this period) but some were due to technological changes such as increased use of continuous casting. A more recent paper on CO2 emissions, focused on the steel industry in Japan, is that of Ariyama and Sato2. These authors report CO2 emissions of 182.4Mt from the Japanese steel, industry in 2003, down from 194.8Mt in 1990. The former represents 14% of the GHG emissions for Japan in 2003. Much of this emission is from ironmaking and the authors break these emissions down into"

Jan 1, 2008