By Ming-Feng Ye, Guang-liang Wu

The investigations on chemical composition, mineral composition, embedded figures, texture and microstructure of chrome ores were conducted systematically byvariousanalysismethodssuch aschemical analysis, XRF, SEM, and MLA 650 system. The results showed that there are 92.66% chromite and a small amount of chlorite and forsterite as the main mineral compositions, the content of quartz is very low. Elements as Cr and Fe are almost all present in chromite. The content of Cr O is 41.84% and Cr O /FeO is 2.1. The main ele- 2 3 2 3 ments in the chromite are Cr, Fe, Mg, Al, O; the main elements in the chlorite are Mg,Al,Si,OandasmallamountofFe;themainelementsintheforsteriteareMg, Si and O. On the basis of clarifying the mineralogical characteristics, to produce high-grade alloy, this ore should not be separately put into the submerged arc furnace without pretreating. However, it also seems to be difficult to separate the gangue compositions by the conventional physical upgrading methods, such as magneticseparationandgravityseparation.So,chemicalmineralprocessingshould be taken into account. (cid:1) (cid:1) (cid:1)

Mar 1, 2018

By HeeDong Lee, Owen Reedy, Lawrence Matson, Naidu Seetala, Thomas Key

Spark Plasma Sintering (SPS) consolidated ZrB2+SiC composites using nano-powders (around 40 nm) showed smaller grains compared to those using micron size powders and segregation of SiC into islands is minimal but with higher oxidation of ZrB2 to form ZrO2 in nano-composites. Argon-gas purging prior to SPS consolidation at around 2000 °C and 40 MPa of ZrB2+20vol.%SiC nano-powders was used to minimize the oxidation and obtain fine granules with high densification. The densification of the Argon-gas purged nano-composites is higher compared to those consolidated without Argon gas purging. The EDX analysis showed a strong reduction in the oxygen peak for the Argon gas purged composites. The XRD spectra also support this observation with less ZrO2 phase composition in Argon gas purged composites. The Vickers micro-hardness showed slightly lower values for Argon gas purged composites though they have higher densification.

Mar 1, 2017

By Juárez T. Julio Cesar, Mendez R. Eliecer, Reyes P. Martín, Flores G. Mizraim Uriel, Teja R. Aislinn Michelle, Hernández C. Leticia, Reyes D. Iván Alejandro

The present study shows the characterization of a zinc concentrate collected at Hidalgo, Mexico, in order to identify its mineralogical species and to propose a leaching methodology for silver recovery. The results obtained by X-Ray Diffraction (XRD) show Sphalerite (ZnS) as the mineralogical matrix and silver into the specie proustite (Ag3AsS3). The techniques of Scanning Electron Microscopy-Energy Dispersive Microanalysis (SEM-EDS) and Polarized Optical Microscopy (POM) identified the presence of sulfides of Fe, Cu, Pb and Zn, in addition to silicates and feldspar. The proposed dissolution method of Ag(I) was carried out with [S2O3 2−] = 0.5 M and [NaOH] = 0.1 M to regulate the medium at pH = 9 for 12 h at 298 K. Oxidation of the concentrate was favored by injection of O2 to a partial pressure of 1 atm. Monitoring of the reaction was carried out by reading the [Ag] and [As] by AAS.

Mar 1, 2017

By S. Jolivet, A. Klöfverskjöld, P. Latostenmaa, B. P. Wilson, M. Lundström, P. Halli

Doré slag is secondary product of copper electrore fining anode slime treatment. The slag consists mainly of different slag formers, such as borax and silica based minerals together with soda and traces of sealing materials. However, Doré slag also contains metals present in the anode slime, such as Ag, Cu, Bi, Sb and Te. At some plants, slag cleaning has been conducted utilizing conventional grinding and flotation circuits in order to enrich the content of precious metals in the slag [1]. Nevertheless, the routine consideration of the slag as a secondary raw material has so far not been adopted on an industrial scale. The current study presents the preliminary results of the nitric acid and chloride leaching of antimony from Doré slag. Chemical and mineralogical analyses (SEM-EDS, AAS, XRD) were performed for the raw material, leaching residue, and leaching solution in order to ascertain the metal recovery and kinetics during leaching.

Mar 1, 2017

By Chao Li, Shi Sun, Hongxu Li, Jiaqi Fan, Qi Liu

With the great demand of consumer electronics (CE) and electric vehicles (EV), cobalt has become one of the more scarce energy metals.The recovery of cobalt from a copper converter slag, which contained over 2.4% Co and was accumulated as industrial waste, by reduction-sulfurization smelting was explored. Quantitative analysis of treated slag showed that activated carbon and ferrous sulfide can be used to settle cobalt into matte as Co–Fe alloy. The experiment was carried out at 1673 K with a reducing atmosphere of burning electrode graphite crucible. It was found that the recovery of Co would increase within creased added activated carbon, was unaffected at higher carbon additions, and for low additions of carbon increased at higher FeS additions. Over 95% Co, 99% Cu and 62% Fe could be settled into matte. Preliminary separation of Co from converter slag by pyrometallurgical smelting is proposed.

Mar 1, 2017

By Fuming Wang, Xi Chen, Shuai Liu, Changrong Li, Dan Wu, Yaxu Zheng

The effects of B content and austenitizing temperature on hardenability and toughness of Cr–Mo alloy steel have been studied. The results show that the hardenability is deteriorated with increasing B content and austenitizing temperature. With increasing temperature, more and more B containing particles were dissolved in austenite and increase the amount of B atoms segregating at grain boundaries. Moreover, the coarsening grains reduce area of grain boundaries and also increase the amount of B atoms at unit grain boundary, excessive B atoms segregating at grain boundaries promotes precipitation of M2B, which accelerates ferrite nucleation and reduces hardenability. The main elements in M2B phase are Fe, Cr, Mo and B. The B atoms segregating at grain boundaries during austenitizing promote precipitation of M2B during tempering which deteriorate toughness significantly.

Mar 1, 2018

By M. A. Kader, W. D. Hutchison, M. A. Islam, P. J. Hazell, J. P. Escobedo, A. D. Brown

The effects of post-foaming thermal processing on the quasi-static compressive strength of closed-cell aluminium foam with an average relative density of 0.56 g/cc have been investigated. Samples were subject to one of four material conditions: as-received (AR), warm aged (WA), solution treated (ST), and annealed (AT). X-ray diffraction (XRD) was performed to determine a relationship between each material condition and macro-crystallographic texture of the dendritic α-Al phase. It was found that all heat treated samples contained clear deviations from random texture towards the exterior regions of the samples, indicating non-uniform recrystallization kinetics. The ST and WA samples exhibited the highest yield stresses and energy absorption, with the AT samples exhibiting the lowest. Additionally, it was found that the AR and WA conditions lost 12.8 and 15.6% of their total mass from brittle cell wall crumbling, whereas the AT and ST conditions lost 2.5 and 3.0% of their total mass.

Mar 1, 2017

By Guihong Han, Duo Zhang, Yanfang Huang

Ni2SiO4 was prepared by chemical precipitation process as a novel anode material for lithium-ion batteries. The structure and morphology of further annealed Ni2SiO4 samples were characterized by XRD and SEM analysis. The electrochemical performance including cyclic voltammetric curves (CV), electrochemical impedance spectra (EIS), charge/discharge curves and cycling performances were also determined. The results demonstrated that the crystal structure of the samples is orthorhombic having space group Pmn21. The morphological structure of materials exhibited cubic particles with sizes in the range of 50–80 nm. The first cycle charge capacity of the pure Ni2SiO4 particles reached to 753 mAh g−1 with the coulombic efficiency of 63.8%. The charge capacity remained 305 mAh g−1 at a current density of 100 mA g−1 even after 50 cycles, which is nearly 208% higher than those of the Ni2SiO4 with SiO2 impurity. Ni2SiO4 can be a promising alternative anode material.

Mar 1, 2018

By Tiejun Chun, Gutian Mu, Jiaxin Li, Hongming Long, Zhengwei Yu, Ning Li

The basic characteristics of iron ore, including assimilation, fluidity, cohesive phase strength and the ability to produce calcium ferrite, are often used to evaluate the sintering properties of iron ore and guide the optimization of iron ore blending. Six kinds of common iron ore used in a steel company in China were selected in this work. The basic characteristics of the single iron ore and blended iron ores were studied, as well as the difference between weighted averages of basic characteristic index of single iron ores and the real value of basic characteristic index of blended iron ore under different ore blending ratios. The results shew that the liquid phase liquidity, cohesive phase strength and calcium ferrite formation ability had a significant linear positive correlation with SiO2 content. The weighted average of basic characteristic index of single iron ore cannot fully reflect the actual blended iron ore properties. The optimization of the blending ratio can be achieved through the detection of the basic characteristics of the mixed iron ore, combined with the basic characteristics of iron ores.

Mar 1, 2018

By Ari Jokilaakso, Dmitry Sukhomlinov, Keiran Holland, Pekka Taskinen, Ville Naakka

This study is focused on distribution of Co, Ni, Ag, Au, and Pd between molten copper and molten copper sulfide (‘white metal’) phases in copper converting conditions. The behavior of the elements selected was studied experimentally at 1300 °C and at various sulfur dioxide partial pressures (0.01, 0.05, 0.1, 0.5, and 1 atm). The experimental technique employed involves a high temperature equilibration followed by rapid quenching in ice water, with subsequent quantitative elemental analysis of the equilibrium phases with an electron micro probe analyzer. The distribution coefficients LCu=wm Me determined in this work can be arranged in the following sequence: Co < Ag < Ni < (Au, Pd).

Mar 1, 2018

By Xudong Liu, Ganghua Fu, Yufeng Guo, Wei Chen, Yujia Tan, Tao Jiang

Willemite is usually found in high-silicon oxide zinc ore and zinc metallurgical secondary resources but without effective extraction method yet. In this study, zinc was extracted from willemite by sodium salt roasting and ammonia-leaching process based on the idea of zinc phase reconstruction. The effects of Na2CO3 dosage, roasting temperature and roasting time on phase transformation and zinc leaching rate were studied, respectively. The results show that Zn2SiO4 was transformed into ZnO or Na2ZnSiO4 during roasting process. After roasting at 800 °C for 2.5 h at ratio of n(Na2CO3)/n(Zn2SiO4) = 2.5:1, willemite was thoroughly transformed into ZnO. The zinc leaching rate of the roasted sample was 97.62% in NH4Cl–NH3–H2O leaching system, which increased by 91.57% compared with zinc leaching rate of 6.05% when willemite was directly leached in NH4Cl–NH3–H2O system.

Mar 1, 2017

By Xiaolong Lin, Yuanbo Zhang, Guanghui Li, Zhizhong Li, Zhiwei Peng, Tao Jiang, Yan Zhang, Yutian Ma

Pyrometallurgical processes for recovering platinum group metals (PGMs) from spent catalyst have been the focus of current research for many years. They suffer from high energy consumption, large trapping agent consumption and huge slag production. Because of versatility of PGMs-containing spent catalysts, comprehensive recovery of valuable metals from these catalysts from an experimental point of view remains a challenge. In this study, thermodynamic analysis of pyrometallurgical smelting process in the presence of various additives for ef ficient recovery of PGMs was performed. It showed that addition of sodium salts would promote the migration and separation of the precious metals from carrier of the spent catalyst. By replacing calcium oxide with sodium carbonate and sodium borate, the smelting temperature could be reduced by more than 200 °C, which agreed well with the experimental findings.

Mar 1, 2018

By Paul Laforest, Michael Moats, Daniel Majuste

The interaction of anode and electrolyte chemistry in copper electrorefining is complex. This is especially true with regard to the behavior of Group 15 elements (As, Sb, and Bi). To better understand this system, laboratory electrorefining experiments were conducted using commercial anodes with As/(Sb + Bi) molar ratios of 0.54 and 3.8 and an electrolyte collected from a commercial refinery. The effect of adding thiourea during plating was also examined. Twenty-one hour copper deposits were produced in the laboratory to simulate starter sheet production. The mechanical properties of the electrodeposited copper as measured by an industrially relevant empirical bend test and a one-point bend test developed by UFMG are reported. The crystal structures of the samples were also examined.

Mar 1, 2017

By Minh H. Pham

This paper presents a technique for imaging the extent of solidification of molten metal flowing in a cooled pipe based on the concept of eddy currents. A 3D mathematical model, which relates the geometry of solidification to the scattered field induced in a solenoid external to the pipe, is derived. The model is described by a set of integral equations which are solved numerically using the moments method. An iterative algorithm is developed to reconstruct the solidification distribution image. Experimental measurements have shown that the eddy current technique is sufficiently sensitive for practical purposes.

Jan 1, 2001

By Hsing Kuang Lin

Extraction of zinc from chloride solution with dibutyl butylphosphonate (DBBP) in Escaid 110 has been investigated. The distribution coefficient of zinc was found to be independent of equilibrium pH. This independence indicates that the mechanism of the extraction may be solvation. Slope analysis for the system of dilute zinc chloride solution reveals that two moles of DBBP react with one mole of zinc. A series of tests were conducted to bring DBBP to its full loading capacity and the analysis of the results confirms this stoichiometric factor of 2. Extraction isotherms were established by varying either the AIO ratio or the concentration of zinc in the aqueous feed. Both curves were found to be identical.

Jan 1, 1990

By A. Rawat

The removal of oxyanions of arsenic present in mine process water and drinking water to a regulatory level is a challenging problem. Recently a patented adsorbent lanthanum oxide has been developed which has shown strong specificity for the anions of arsenic. In this paper the kinetic and thermodynamic aspects of arsenic adsorption on to lanthanum oxide are discussed. Adsorption tests were performed at different temperatures using synthetic solutions of arsenic of varying concentrations. From the kinetic data and adsorption isotherms thermodynamic properties such as Gibb&apos;s free energy, standard enthalpy of adsorption, standard entropy, isosteric heat of adsorption and activation energy were determined. The results showed that temperature had a positive effect on the rate and degree of adsorption:The activation energy decreased with increase in the initial concentration thus indicating solute-solute interactions in the system. Also, the isosteric heat was found to decrease with increase in the adsorption density implying a heterogeneous adsorbent surface.

Jan 1, 1998

By D. de la Villa

From 1989 to 1992 Rio Tinto Minera has developed and implemented a productivity program in its Huelva Plant, including Smelter, Acid Plant and Electrorefinery. This Plan was designed in order to increase productivity, reduce emissions and produce a better quality of cathodes. This paper describes investments and operating improvements involved in this project, focusing on Smelter and Acid Plants, and comments the results obtained so far.

Jan 1, 1993

By Mikko Loponen

Outotec has developed an operator training simulator (OTS) platformsuitable for various hydrometallurgical processes. The complete solution is run in the cloud, where virtual client instances can be managed on-demand. The aim is to build a generalizable model that produces coherent results even when operating outside of ideal parameters, allowing the operator to train in unsteady state conditions such as start-up and shutdown. Complex software products are commonly associated with significant development time and cost. Utilizing modular software architecture, only the control system and processmodel are tailored for theOTS,whereas modules such as user administration and cloud-based client machine spawning can be imported, shortening development time. A generic acidic pressure oxidation process (POX) operator training simulation consisting of feed preparation, autoclave, dual-stage flash evaporation and off-gas scrubbing is described. Process is simulated using Outotec HSC Sim 9 process simulator and controlled by Siemens Simatic PCS7 control system.

By S. K. Utimurd, D. C. R. Espinosa, J. A. S. Tenório

"Waste Electrical and Electronic Equipment (WEEE) has become an environmental issue due to technological advance and waste plastic is one of the main polluters. The excessive discard of these plastics result in a difficult to dispose it to landfill and need further separation with technique in order to produce high added value plastics. There are many kinds of plastics in extensive use at the present time and the co=on are the acrylonitrile-butadiene-styrene (ABS) and high impact polystyrene (HIPS) used in the production of electric appliances. These plastics are difficult to separate because they have similar densities. Flotation of plastics is one possible separation technique and using selective wetting agents. The separation may be possible given close control at particle size and the concentration of the reagent. The process was able to produce a concentrate of HIPS with at least of 93% purity and a concentrate of ABS with 99% purity.IntroductionThe current situation of municipal solid waste (MSW) management especially in emerging economies like Brazil, the growing population and economic activity will result in a significant increase in the generation of waste in the coming decades. It is worthwhile to review and update the sources, amounts and recovery technologies of specific materials from waste, particularly from municipal solid waste (MSW).The growing impact of the current waste management practices stresses the need for a change in how waste is handled. The 2012 survey and the Brazilian Association of Public Cleaning and Special Waste Disposal Companies (ABRELPE) reports the generation of 62 Mt urban MSW in that year, which is an increase of 13% compared to 2011. It has been reported that in Brazil about 90.17% of the generated MSW is currently collected, which indicates an increase in the coverage of collection services compared to 2011 [ l]."

Jan 1, 2014

By G. L. Fredrickson, T. A. Johnson, B. R. Westphal, J. C. Wass, S. X. Li, D. Vaden

"Recovery of uranium from the Mk-IV and Mk-V electrorefiner vessels containing a LiCl/KCl eutectic salt has been on-going during the pyrometallurgical processing of used nuclear fuel for 14 and 12 years, respectively. Although austenitic stainless steels are typically utilized for LiCl/KCl salt systems, the presence of cadmium in the Mk-IV electrorefiner dictates an alternate material. A 2.25Cr-1Mo alloy (ASME SA-387) was chosen due to the absence of nickel in the alloy which has a considerable solubility in cadmium. Using the transition metal impurities (iron, chromium, nickel, molybdenum, and manganese) in the electrorefined uranium products, an algorithm was developed to derive values for the contribution of the transition metals from the various input sources. Weight loss and corrosion rate data for the Mk-V electrorefiner vessel were then generated based on the transition metal impurities in the uranium products. To date, the corrosion rate of the 2.25Cr-1Mo alloy in LiCl/KCl eutectic is ""outstanding"" assuming uniform (i.e. non-localized) conditions.IntroductionLow-enriched uranium products are being recovered from the Experimental Breeder Reactor-II (EBR-II) and Fast Flux Test Facility (FFTF) used nuclear fuels by a pyrometallurgical treatment process at the Idaho National Laboratory (INL). The treatment process comprises a set of operations designed to neutralize bond sodium, recover uranium from radioactive fission products, and place the fission products into acceptable waste forms [1-2]. Reactive sodium metal, essential for heat transfer purposes during reactor operations, is readily converted to chloride during the process. Electrorefined uranium products are currently being stored pending a final disposition decision. Treatment of the EBR-II used driver fuel was initiated in June 1996 while blanket fuel processing started in September 1998. These treatment processes continue on the balance of the used fuels."

Jan 1, 2011