By Gordon M. Yocom

A PROPER consideration of the subject of this paper should include economic aspects as well as the technical phases of the metallurgy, production, and properties of the product. The metallurgical phases of the processing and properties of the product will be considered only from practical aspects and within the scope of the writer's experience with tonnage production. The Bessemer process was invented 85 years ago and became important because it put steel manufacture upon a larger and less costly basis. In America the Bessemer production has declined for many years and has not maintained its proportionate place with the rapid advances of the open hearth. The achievements in the open-hearth field were attained by the greater number of technical people attracted to that branch of the industry. The antipathy of technical students for the older and less popular Bessemer field gradually weakened the forces defending it and retarded the development of new and better methods. In Europe the economic advantage of the basic Bessemer process has not been overlooked and the tonnage usually is greater than that of the open hearth. The acid process has been the subject of renewed attention in America during the past few years and those who are more familiar with it are striving to show that the method is too valuable to abandon. A considerable tonnage of Bessemer-blown metal, in both molten and ingot forms, used in connection with the open-hearth practice makes it an important auxiliary unit to the industry. This practice aids in modifying the price level of heavy remelting scrap in addition to speeding up the open-hearth operation. The use of Bessemer steel has continued not only because of periodic economic advantages but also because of certain inherent qualities of machinability, weldability and stiffness, which are valuable for many applications. The properties of stiffness and rather high reaction to cold-work require some modification in order to meet the demands of modern methods of processing, which involve cold-reduction and cold-forming. At least one factor contributing to the stiffness of this steel is the relatively high phosphorus content of the acid product. The phosphorus content of the Thomas or basic Bessemer steel of Europe is considerably lower than the normal acid product in America. The American industry has continued the use of the acid process chiefly for the reason that the available ores are more easily adapted to this process from both metallurgical and economic standpoints. In European practice the basic process is necessary with the highly phosphoric ores available and it is sustained to some degree by the sale of the rich phosphate slag as a by-product. The basic process was used in this country at several plants many years ago, but was abandoned for economic reasons. A part of the past history of these trials is given here because the author believes it has not been published and it has some bearing on the subject of this paper. The information is authentic to the extent that

Jan 1, 1941

GENERAL COMMITTEE GERALD F. G. SHERMAN, Chairman. ARTHUR NOTMAN, Secretary. NORMAN CARMICHAEL, JOHN C. GREENWAY, W. L. CLARK, W. G. McBRIDE, B. BRITTON GOTTSBERGER, FOREST RUTHERFORD. General Committee on Transportation WALTER DOUGLAS, Chairman. CLEVELAND E. DODGE, Secretary. ARTHUR S. DWIGHT, JOHN C. GREENWAY, JULIUS KRUTTSCHNITT, JR. Committee at El Paso W. D. GORDON, ROBERT McCART, JR., W. W. ROSE. Committee at Santa Rita JOHN M. SULLY, Chairman.

Jan 12, 1916

By O. W. Ellis

Recently there has been a considerable revival of interest in the effects of the various elements commonly added to brass for the purpose of increasing its strength. For many years the work of Guillet2 alone gave reliable information in this regard. Even today his determinations of the coefficients of equivalence of the various elements relative to zinc in brass are those universally employed in industry. This is so because these coefficients have stood the test of time—their substantial correctness has been proved in almost universal practice. It is not our intention to discuss here these coefficients or their use. Rather do we wish to emphasize the need for further systernatic studies of the mechanical properties of the ternary systems of copper, zinc, and other individual elements. Since Guillet published the results of his first investigations Millington, 16 Smalley33 and Thiband 45 have added somewhat to our information. In general they have confirmed the findings of Guillet, which may be stated in the following rather general terms: 1. The addition of aluminum to the 70:30 and 60:40 brasses progressively increases their hardness and strength and reduces their ductility and resistance to shock. 2. The addition of small amounts of iron to a 60:40 brass improves its strength without affecting its ductility. 3. The addition of small amounts of manganese to a 60:40 brass causes a progressive increase in its strength and reduction in its ductility. A considerable amount of information has been amassed in regard to the effect of nickel on brass (9, 22, 41) which it is unnecessary to refer to here, in view of the scope of this paper. The situation in regard to these alloys in 1926 was very clearly stated by an anonymous writer,47 in The Metallurgist of February of that year, whose remarks were so to the point that they are well worth quoting: It will he seen that there are still large fields remaining to be studied in each of these systems (those of the aluminum, iron, nickel and manganese brasses) before our knowledge is adequate. When we come to the more complicated systems the position is even less satisfactory, and on account of the very incomplete nature of the work which has been

Jan 1, 1929

By Yves Dardel

INTRODUCTION SINCE the first determination of Dumas1 in 1880, many authors have tried to measure the solubility of hydrogen in solid aluminum, or at least the amount of dissolved gas in it. However, the interpretation of the results which have been obtained is still difficult. Sieverts,2 then Baukloh and Oesterlen,3 during their gassing experiments could not determine any solubility of hydrogen in solid aluminum. On the other hand, Portevin, Chaudron and Moreau,4 leaving the determination of the hydrogen solubility beyond the scope of their experiments, measured only the amount of gas that they could extract by high voltage positive ion bombardment and found up to 151 cm3 of gas per 100 g of metal. Winterhager,5 by repeated vacuum extraction during severe cold rolling, extracted up to 161 cm3 per 100 g. In both series of experiments, the extracted gas contained chiefly hydrogen with a small amount of nitrogen, carbon monoxide, carbon dioxide and methan. Later, Schmidt and von Schweinitz6 as well as Chaudron and Moreau7 showed the importance of the adsorbed layer of hydrogen, the extracted quantities being proportional to the surface and not to the weight of the sample, when its cleaning was not perfect. In earlier experiments, Steinhauser8 extracted from more massive samples nothing but a little amount (< 0. 5 cm3 per 100 g) of hydrogen, carbon monoxide and methane. Thus, according to these experiments the quantity of dissolved gas is probably very small and the effect of the surface could falsify the results of the extraction. However, owing to the care taken by Chaudron and his coworkers, it was clear that all the hydrogen extracted could not come from the superficial layer, or that the links which bound hydrogen to the surface were so strong that the usual method of cleaning could not destroy them. After the main parts of the experiments reported here had already been carried out, Eborall and Ransley9 published the results which they obtained with an analysor having an accuracy of 0.03 cm3 per 100 g, while that of the usual apparatus was only about 0.2 cm3 per 100 g. During all their experiments the adsorbed layer would have been a difficulty, for the value of the adsorbed hydrogen was approximately equal to that of the dissolved amount. [ ] Since always keeping the same adsorbed layer is very difficult, an error in the correction for the adsorption can be made when using the apparatus of Eborall and Ransley, as well as the earlier apparatus,

Jan 1, 1948

By Reinhardt Thiessen

UNDER sulfur in coal, is usually understood that form of sulfur which is combined with iron and known as pyrite. It occurs in the form of halls, lenses, nodules, continuous layers, thin sheets, or flakes, both in horizontal planes and vertical cleavage fissures. But pyrites also occur as very fine microscopic particles, or nodules, disseminated through the compact coal. This form has had but very little consideration. Finally, there is sulfur in coal in an amicroscopic form (not visible with an ordinary microscope), probably combined with the organic matter that exists -in tile coal. This form has had considerable attention from a scientific standpoint, but has probably not been recognized enough on the economic side. One or the other, or both, of these two latter forms may comprise the larger part of the sulfur content of coal, especially after it has been washed or otherwise prepared for use.

Jan 9, 1919

By R. M. Sellwood

The No. 4 I.S.F. Smelter Complex at the Avonmouth Works of Imperial Smelting Corporation (N.S.C.) Limited commenced operation at the beginning of 1968. The furnace rating is 120,000 tons zinc and 40,000 tons lead per annum. Zinc and lead concentrates are unloaded onto a 1,000 tons per hour capacity conveyor belt and automatically weighed and sampled before receipt into a 48,000 ton capacity raw material store. Distribution is by a reversible boom stacker into 16 x 3,000 ton bays and recovery is by a front end loader. Materials are fed to 16 proportioning bins for feeding via continuous weigh feeders to a 132 square metre effective updraught area sinter machine with a material flow rate of 240 tons per hour over the machine. The required quantity of output lump sinter at up to 800ºC is fed to 2 x 600 ton storage bins on the I.S.F. plant. By-product SO2 rich gas is fed to a conventional wet gas single stream acid plant rated at 600 tons per day utilizing a dry N.T.P. gas volume of 100,000 cubic metres per hour. The hot sinter and preheated coke (800ºC) are automatically neighed and charged to a 27.3m2 shaft area I.S.F. fitted with 2 x 5.5 m. wide lead splash condensers. Grade 4 zinc is tapped and transferred to the zinc refinery. Conventional type lead bullion and slag are tapped from the bottom of the furnace through a separation forehearth. The refinery consists of 6 lead and 3 cadmium columns to produce some 52,000 tons per annum of S.H.G. metal. S.H.G. metal and Grade 4 metal is cast into various shapes as required.

Jan 1, 1970

By John J. Gilman

F many years it has been suspected that a correlation existed between pits produced by etching and the density of dislocations in crystals. In 1953, the interest in this correlation was greatly stimulated when Vogel et al&apos; demonstrated a 1:l correlation between etch pits and dislocations in low angle grain boundaries of germanium. About two years ago, the author began attempts to produce etch pits at dislocation sites in zinc mono-crystals. These attempts met with success a year or so ago,&apos; and since that time a survey has been made of the etch pit patterns that are associated with various modes of deformation in zinc monocrystals. Unfortunately, the etching technique that will be described is too delicate for use as an accurate quantitative tool. Nevertheless, it has been of considerable assistance in clarifying the structure of plastically deformed crystals. Technique Many attempts were made to produce etch pits in high purity zinc crystals. It was found that several techniques would produce surface grooves at grain boundaries that had misorientation angles greater than about l°, but no technique was successful for boundaries with smaller angles. Among the things that were tried were: electrolytic CrO, (both etching and polishing concentrations), HNO, in various water and alcohol solutions, dilute HC1, many 0-0,-Na,SO, solutions, Cr0,-HC1 solutions, picral, electrolytic Na,S,O,, and electrolytic NaOH and KOH. A few attempts to use cathodic sputtering and thermal etching were also made.

Jan 1, 1957

By Gunnar Thaning, Borje Bjorkvall

At LKAB Central Division for Metallurgical Research at Malmberget, Sweden, fired pellets are examined in respect to mechanical and reduction properties. The paper deals with descriptions of the test methods. It also involves the rationale for the choice of these tests. Their correlation to the blast furnace operation will be examined. The mechanical tests used are the ISO-tumbler test and the cold compression strength test. Concerning the metallurgical properties, experiments have shown that some superbasic pellets in particular have different disintegration properties in different temperature ranges. Pellets which have favorable reduction properties when tested under isothermal reduction at high temperature may disintegrate to a large extent under low temperature reduction. This is also valid for some types of acid pellets. Consequently, it was found to be necessary to determine the reduction strength both at high and low temperatures. In the low temperature range, the disintegration is measured by tumbling the pellets in soft reducing conditions at 600°C in a modified Linder test equipment. The high temperature reduction strength is determined under load in the Burghardt-Grebe equipment. However, in order to get more information of the high temperature strength, LKAB intends to introduce a softening test. The tendency of high temperature disintegration will also turn up in the swelling test. The swelling properties are examined according to a procedure developed at LKAB. In this test the pellets are subjected to free swelling without mutual contact. The reducibility of the pellets is recorded in the swelling test.

Jan 1, 1974

By A. N. Mitinsky

Discussion of the paper of A. N. MITINSKY, presented at the San Francisco meeting, September, 1915, and printed in Bulletin No. 104, August, 1915, pp. 1697 to 1705. LAWFORD H. FRY, Burnham, Pa. (communication to the Secretary*). -The author assumes that the proportional limit and the elastic limit are coincident or very nearly so, and then further assumes that the stress corresponding to these two points is the least stress which if repeated will cause failure. The point is extremely interesting and it is to be regretted that the author did not quote experimental data to show the relation between the limit of repeated stress and the other properties of the material. The author&apos;s suggestion that a steel of poor quality may have a normal value for the yield point and tensile strength (see Fig. 2) and an abnormally low elastic limit, and that this will correspond to a low resistance to repeated stress, may account for a number of failures of axles in which the tensile tests show normal physical properties. If so and if a determination of the proportional limit would have eliminated the material before it was put into service, this determination will merit most earnest attention. It appears, however, that considerable further research is necessary before any definite conclusion as to the quality of a steel can be drawn from its proportional limit. Mr. Mitinsky&apos;s paper is extremely interesting and if it stimulates thought and work along the lines indicated, it may prove of considerable practical benefit. H. V. WILLE, Philadelphia, Pa.-The paper discusses the difference between the proportional limit, or elastic limit, and the yield point, and refers to the fact that much harm results from confusion of the terms yield point and elastic limit. Similar confusion has arisen in this country; the American-Society for Testing Materials does not even consider the elastic limit and proportional limit to be identical and recently adopted the following definitions:

Jan 12, 1915

By R. H. Winn

In this paper a heterogeneous carbonate reservoir is considered as a succession of layers of formations of radically different porosities, permeabilities, water saturations, and rock matrix types; i.e., the heterogeneity is vertical rather than radial to the wellbore. Presumably each layer is more or less homogeneous. To determine the "net oil in place" in this reservoir it is desirable to know the porosity and water saturation of each layer. In addition, the section must be subdivided into that which will produce oil, that which will produce water, and that which will produce little or nothing. In numerous wells drilled in these reservoirs radioactivity surveys, guard electrode surveys, and caliper surveys have been made. These logs have been compared with core analysis data, when available, and the analysis of the surveys compared with production data. This study, still in progress, is intended to provide improved analytical techniques if such are possible. This paper is a progress report on the work. DETERMINATION OF POROSITY The neutron-gamma log has long been recognized as a measure of hydrogen concentration.1,2,3 In reservoirs that are free of clay, shale, or other hydrogen containing matrices, it has been accepted as a measure of porosity.4,5 Empirical methods to relate relative neu-tron-gamma intensity to porosity are often employed." To provide a more precise determination of porosity from the neutron-gamma log each instrument is calibrated immediately prior to each survey by a method which refers all tools to a hydrogenous cylinder. To insure stability a calibration check is made after each survey. These calibration records are printed as an integral part of the log that is recorded in standard counts per second. A detailed description of the calibration procedure is available in the literature.&apos; The procedure employed insures that each Survey is numerically reproducible within the limits of statistical variation. To relate the standard neutron counts per second to porosity and hole size, records were made in test wells constructed of blocks of limestone. The porosities of the blocks were accurately measured and the blocks completely saturated with fresh water. Fig. 1 presents some of the results obtained in these test wells.&apos; The lines shown in Fig. 1 were obtained by deriving an empirical equation relating the 11 points shown so that the relationship may be projected to larger and smaller hole sizes. A detailed description of the tool is available in the literature.&apos; Field tests indicate that the tool is adjacent to the wall of the hole most of the time when the surveys are made in uncased holes drilled with saline muds. In this circumstance porosity may be calculated from Fig. 1 if the hole size is known. When fresh muds that form thick mud cakes are employed, the centralizing effect of the mud cake must be considered and the porosity determination is less reliable. In cased holes the combined effect of variations in hole diameter and the unknown eccentricity of the casing in the hole may make porosity determinations extremely unreliable. In any event, an accurate knowledge of hole size is essen-

Jan 1, 1958

By Richard W. Smith

KYANITE, long known to occur in Georgia, did not excite commercial interest until about 1930. Investigations revealed two main types of deposits: (1) separate kyanite crystals embedded in mica schist; and (2) crystal aggregates of kyanite associated with quartz in small and very irregular veins. The second kind at first sight appeared to be the best source of supply. Large boulders or dornicks of kyanite with more or less quartz were found on the surface at many places throughout the Piedmont and Highland sections of the state, but prospecting failed to disclose a sizable vein. These dornicks seem to be a surface accumula-tion from small veins or lens-shaped masses not more than one or two feet thick, and with a horizontal extent of not&apos; more than a few feet. The larger surface accumulation of kyanite dornicks, where not too badly stained by iron oxide, may prove to be marketable, but it is extremely doubtful whether a vein large enough to mine will ever be found. In 1932 deposits of the kyanite-mica schist were known to occur in two places northwest of Clarkesville, in Habersham County. In 1934, at the request of and in cooperation with the Georgia Geological Survey, the United States Geological Survey made a thorough investigation2 of the deposits and found that the two known areas of kyanite-mica schist in Habersham County were but a part of an unsymmetrical, U-shaped belt (Fig. 1) with a western limb extending into Rabun County and somewhat longer than the eastern limb. The total length of the belt is about 30 miles. The width of outcrop ranges from 100 ft. to 1/4 mile or more. Deposits of kyanite-mica schist of very doubtful commercial importance were found in several other counties. Only the deposits of this kyanite-mica schist belt in Habersham and Rabun counties will be discussed in this paper.

Jan 1, 1936

By B. G. Klugh

In a paper before the Institute at Wilkes-Barre, Pa., June, 1911,&apos; Mr. James Gayley discussed the application of this process to iron-bearing materials. The same author² described the results of operations at the plant at Birdsboro, Pa. The purpose of the present paper is to present further discussion of some techuical details involved in the operation of this plant, and of the theoretical and practical relations of this product to blast-furnace practice. Since Oct. 1, 1911, the Birdsboro plant has been in operation at the blast-furnace of the E. & G. Brooke Iron Co. The results have been highly satisfactory, although the material treated, being chiefly the flue-dust currently made by the furnace or taker] from the accumulated stock-pile, was excessively high, and yet not uniform, in carbon, so that the desirable control or regularity of the amount of fuel in the mixture treated could not be maintained. Nothing could more forcibly demonstrate the flexibility of the process than the fact that, under these conditions, the sinter produced was, in all cases, of excellent quality. The Dwight & Lloyd process, as such, slid its present highly-developed mechanical appliances were described by Mr. Gayley in the paper above mentioned. While the repetition of some particulars will be unavoidable in this paper, it will be confined to features bearing upon the metallurgical principles involved. According to the principle of the process, the finely-divided iron-bearing material to be sinterecl is intimately nlixed with

Jan 1, 1913

By A. E. J. Engel

INDUSTRIAL talcs and ground soapstones both include earth materials of different chemical and mineral compositions. In general, the industrial talcs are composed of silicates that contain appreciable amounts of magnesia. Generally talc, the mineral, is a predominant or at least common constituent. Talc, the mineral, is a hydrous magnesium silicate, with a suggested theoretical formula H2Mg3 (SiO3)4 or H2O.3MgO.4SiO2, which postulates 63.5 pct SiO2, 31.7 pct MgO, and 4.8 pct H20.11 Actually different single grains or leaves of pure talc have variations in water content ranging from 3.5 pct to more than 7 pct, as well as slight differences in the proportions of MgO and Si02.16 Only a very small percentage of the ground industrial talcs produced in the United States approaches the composition given above (see Table 1). The purer talcs invariably occur as alteration products of magnesium carbonate rocks. Some of these relatively pure talcs include compact, massive types largely mined in California, which are designated as steatite.38,58 In general, steatites cannot contain in excess of 1.5 pct CaO, 1.5 pct combined FeO and Fe203, and 4 pct A1203. The less pure varieties of massive talc and mixtures of magnesian silicates are commonly called soapstones, or merely talc. Many industrial earth products classified as talc or as soapstone contain a variety of minerals, especially serpentine (H4Mg,Si2O9), chlorites (hydrous magnesium, iron, aluminum silicates), tremolite (Ca2Mg5H2[SiO3]8), anthophyllite ([MgCa]SiO3), diopside (CaMg[SiO3]2), and quartz (SiO2). The carbonates calcite (CaC03), dolomite (CaMg[CO3]2), and magnesite (MgCO3) are also present in some industrial talcs and soapstones. Some of these minerals, as well as sulphides, sulphates, and iron and manganese oxides, if present at all or in excess of minute amounts, may alter the composition of the industrial talc sufficiently to restrict materially its use or to lower or destroy its value. These factors are discussed in a subsequent section of this chapter.

Jan 1, 1949

By C. Altstetter, Y. Huang, E. de Lamotte

Nitrogen was introduced into pure niobium (colutn-bium) and dilute Nb- Zr alloy wires by equilibration with pure nitrogen gas at high temperatures. Room-temperature hardness was correlated with the alloy composition, heat treatment, and microstructure. Hardness was found to be most sensitive to the amount of nitrogen in solution; however, a significant hardening up to 500 Dph look place upon aging of quenched alloys. A coarse dispersion of nitride did not significantly increase the hardness of the material though the nitride was found to have a hardness of 1400 Khn. BY now the marked effect of nitrogen on the properties of bcc refractorv metals is we ll-documented. There are few studies, however, in which the state of the solute has been carefully controlled. Indeed, the composition-temperature-pressure relationships in nitrogen-refractory metal systems have been determined precisely for only niobium and tantalum.&apos;-4 Most investigations on niobium have dealt with alloys High-nitrogen alloys cleaved on (100) planes and had negligible ductility. Precipitation was found to occur in either a discontinuous or a continuous fashion, depending on the composition and cooling rates. Upon cooling, the precipitation first proceeded discontinu-ously by the nucleation of nilride needles at subbound-aries and subsequent growth of a two-phase microcon-stituent. At lower temperatures continuous precipitation occurred in the subgrain interior ahead of the discontinuous precipitation interface. containing nitrogen, carbon, and oxygen in significant but uncontrolled and, in several instances, undetermined amounts. Thus, there has been some uncertainty regarding the presence and the distribution of precipitates. This paper presents results which relate the hardness and microstructure to the heat treatment and nitrogen content of niobium and Nb-Zr alloys. Niobium rod* produced by the Wah Chang Corp.

Jan 1, 1968

By W. Chubb

By measuring the hardness of metals at temperatures just above and just below their allotropic change point, it has been established that crystal structure has a real effect upon the strength of metals. The DPH of cobalt, iron, titanium, uranium, and zirconium have been measured at temperatures up to 1000°C. It was found that the body-centered-cubic crystal structure is always the softer structure when it is involved in an allotropic transformation. The close-packed and more complex structures are inherently harder, and may be expected, therefore, to be better base materials for high strength alloys. IT has been observed that for metals with nearly the same melting point (i.e., tin and lead, magnesium and aluminum) the metal with the more complex crystal structure has a higher tensile strength and hardness. It might be asked whether this effect is really caused by the difference in crystal structure; and, if so, just what is the contribution of crystal structure to the strength of these metals. A qualitative answer to these questions can be obtained by measuring the change in hardness produced by the change in structure in metals exhibiting allotropic forms. The evidence for changes in mechanical properties during allotropic transformations is rather meager. In 1909, Rosenhain and Humfrey&apos; observed that "ß" iron showed much less deformation at the transformation temperature than a iron. By means of a torsion test, Lee found that iron bars were "critically plastic" at the a-7 transformation temperature. Sauerwald and Knehans have shown that the dynamic hardness of iron increases between 900" and 1000°C. In 1930, Albert Sauveur&apos; presented data on the hardness, tensile strength, and torsional strength of pui-e iron up to 1000°C. He concluded, "At 900°C, the a iron transforms into y iron, and this is accompanied by increased strength and stiffness and decreased ductility." The same year, Schischokin" obtained data on the hardness of thallium at temperatures above and below its transformation temperature. His data are replotted on semilogarithmic coordinates as Fig. 1. The fact that his data fall on straight lines in this type of plot is believed to attest to the purity of his metal and the accuracy of his results. In 1941, Nadai and Manjoine" obtained tensile data on pure iron with an indicated increase in strength at about 900°C. These experiments make it quite evident that changes in mechanical properties occur when a metal transforms from one crystal structure to another; but, except for Schischokin&apos;s data on thallium, none of the measurements seem accurate enough to determine the relative magnitude of the mechanical property change. Materials The metals that have been examined for changes in hardness during transformation include l—as- deposited commercial electrolytic cobalt about 99.7 pct pure, 2—Armco ingot iron, 3—are-melted iodide titanium of a purity in excess of 99.8 pct, 4—uranium of a purity in excess of 99.5 pct, 5—are-melted iodide zirconium of a purity in excess of 99.8 pct, 6—annealed, 0.08 pct C, rimmed steel, and 7—commercially pure RC55 titanium. While the purity of the first five of these materials leaves something to be desired, it will be noted that the observed hardness discontinuities occurred at the accepted transformation temperatures. (These temperatures are indicated by vertical arrows in Figs. 1 and 3 through 7.) The last two materials are commercial alloys introduced to show the effect of minor alloying elements upon the hot hardness curve. Apparatus Hardnesses at elevated temperatures were determined by means of a vacuum hot hardness machine. A diagram showing the basic features of this machine appears as Fig. 2. This machine is essentially a deadweight hardness .machine in a furnace within a vacuum chamber. The sapphire-tipped indentor

Jan 1, 1956

By P. G. Beckett

THE problem of handling the large quantities of water encountered in the Old Dominion mine presents many features of interest. In the present paper are discussed the probable sources of water, the pumping equipment, the increased flow into the mine in the early part of 1915, culminating in the flooding of the 18th and 16th levels in March of that year, and the difficulties that were met with during the high-water period. I. PRELIMINARY The Old Dominion mine, situated 1 mile north of the town of Globe, Ariz., has long been one of the prominent copper producers of the State, and until the opening up of the copper schist deposits in the neighboring mines of Miami, was responsible for the greater part of the copper output from the Globe district. As the gradual exhaustion of its orebodies near the surface led to the downward development of the mine, more water was encountered in the western portions directly underlying the dacite formation until the drainage problem became a serious factor in the operation of the mine and in the economical extraction of the ore. A heavy inrush of water on the 10th level of the mine in 1906, preceded by still earlier water difficulties, rendered imperative the immediate installation of a pumping equipment capable of handling large flows of water. While the Old Dominion has been recognized as a wet mine since its early clays and one in which the complete control of the water situation was of paramount importance in the development of the lower levels, it is chiefly in the last nine years, since the installation of the increased pumping equipment, that the mine has developed and handled large quantities of water.

Jan 4, 1916

By J. T. McGrath, G. B. Craig

Tensile tests on aluminum single crystals, grown from the melt, revealed that the yield stress of these crystals was raised as the amount of striation substructure was increased. The number of striation-type boundaries was varied by changing the rate of growth of the crystals. The results are interpreted in terns of a blockage of dislocation movement by striation boundaries. IMPERFECTIONS are known to have a large effect on the mechanical properties of metals. Teghtsoonian and Chalmers 1 studied a block or striation-type substructure in tin and found that the formation of the striations depended upon rate of crystal growth and orientation. They found that the angular misorienta-tion between neighboring striations varied between 15 min and 5 deg. Atwater and chalmers2 investigated striations in tin and lead, and found that purity was another factor which influenced their formation. There was a limiting purity above which the striations were straight and regular. There is little information in the literature concerning how substructures in melt-grown crystals affect strength. washburn3 introduced small-angle boundaries into zinc by a shear process and found a subsequent increase in yield stress which he attributed to the presence of these boundaries. Lauriente and pond4 found the critical resolved shear stress in aluminium crystals grown from the melt, to increase with etch pit density. The etch pits were used as an indication of growth imperfections. In Hibbard&apos;s5 work on lineage structure in copper crystals grown from the melt, he tested one crystal containing interlineage boundaries, and found a 50 pct increase in the critical resolved shear stress. Fleischer and Chalmers6, in a recent paper, mention briefly that, in the production of aluminium crystals from the melt when the growth rate was raised from 1.2 to 18 cm per hr, the yield stress increased 50 pct. They felt that the increase in yield stress with rate of growth might be attributed to a higher concentration of impurities in the gage length and also might be affected by the increased number of small-angle boundaries (striations). The present investigation was undertaken to determine the effect of the striation substructure on the strength of aluminum single crystals. EXPERIMENTAL PROCEDURE Aluminum single crystals of 99.9992 purity were grown from the melt using a technique described by Chalmers.7 The growth rate was varied from 0.6 to 20 mm per min, thus producing crystals with varying numbers of striation boundaries. To avoid prior deformation, the crystals were chemically cut to the desired length with a saturated solution of cupric chloride. They were then annealed at 580°C for 24 hr and allowed to cool slowly in the furnace. Finally, the specimens were electropolished using an electrolyte of 5 parts ethyl alcohol and 1 part perchloric acid. Each specimen was approximately 5 in. in length and 0.125 sq in. in cross section. The average orientations of the 5 series of crystals studied are shown on the stereographic projection of Fig. 1. The crystals were strained approximately 2 pct in a soft tensile machine. The strain sensitivity was 3.6 x 10-4 cm over a 5-cm gage length.

Jan 1, 1960

By J. D. Hunt, R. J. McDonald

It is proposed that extensive fluid motion occurs between the dendrites of a Partially solid casting and it is suggested the A segregates in steel castings are a direct result of this motion. The fluid flow arises because of density differences between liquid ahead of the dendrites and the interdendritic liquid. Experiments are described on a model system investigating this fluid motion. The importance of interdendritic fluid flow is discussed with reference to longitudinal segregation. SERIOUS macro segregation is often found in large killed steel ingots. Among the most common segregates are those known as A and V, Fig. 1. The A segregates are arranged over the surface of cones, the wide parts being at the base of the ingot. The A segregates are pencil like in shape and extend from the columnar into the equiaxed region. The V segregates are distributed over inverted cones but have a less well defined shape. They occur at the center of the ingot. Because of the commercial importance of macro inhomogenities these segregates have attracted wide-scale attention. The segregates contain alloying elements and impurities which depress the freezing temperature and are thus the last liquid to freeze. A number of explanations have been proposed to explain their presence. It has been suggested1&apos;&apos; that the segregates are the result of the equiaxed zone growing towards the columnar region together with the interaction of convection within the bulk liquid. It has also been proposed that the segregates are the result of nucleation and rapid growth ahead of the dendritic front.3 Neither of these explanations is completely satisfactory because A segregates are pencil shaped and are not found as continuous cones. In this paper an alternative mechanism is proposed, and experiments are described on a model system to determine whether the mechanism occurs in practice. It is thought that A and V segregates are not peculiar to steels but should occur in many other large castings. Fluid motion within the bulk liquid region of a casting has been extensively discussed. Little attention has been paid to fluid motion within the partially solid regions. The work415 that has been done has been mainly concerned with the fluid motion which results from the volume contraction on freezing. The volume contraction is used to explain various types of macro segregation. The present authors suggest that in many cases the fluid flow resulting from volume contraction will be small compared with that due to other causes. When the columnar region is growing, the liquid still remaining between the dendrites has a much lower temperature near the ingot walls than at the dendrite tips. The composition of the liquid in contact with solid will vary with temperature. The density of the liquid will thus vary both because of changes in temperature and composition. The layers of different density liquid will give rise to a slow but steady liquid flow through the interdendritic regions. If there is no density change with composition, the temperature gradient within the dendritic region should give rise to a downward flow between the dendrites, shown schematically in Fig. 2. When the liquid density changes appreciably with alloy concentration this motion could either be en-

Jan 1, 1970

By L. E. Wemple

Previous to 1915, zinc refining had not become a general practice among the zinc smelters in the United States. Such refining as had been carried on was confined chiefly to remelting very high-leaded zinc, such as third-draw metal from the retort furnaces, and slab dross, and hard spelter from galvanizing pots. In this remelting operation, the lead and iron were settled out and the refined spelter obtained graded fifth class, ie., Prime Western. Owing to the presence of lead in most zinc ores, the bulk of the spelter produced by direct smelting is of this Prime Western grade. Careful selection of ores of low lead content gave purer grades of spelter, z.e., Brass Special and Intermediate; and smelters which could secure ores carrying practically no lead produced high-grade spelter. Thus, in general, the grade of spelter produced by any smelter was predetermined by the purity of the ore it could obtain. The needs of the warring nations of Europe for enormous quantities of cartridge and other high-grade brass resulted in such a demand for the purer grades of spelter that the available supply of lead-free and low-lead ores could not produce the quantity required. Prime Western grades went begging, so to speak, while high grades sold at times from 5 to 15 c. per pound over the Prime Western market. The great demand, coupled with the wide market margin, which permitted the inherent costs and losses, resulted in the conversion of the lower grades into higher grades by processes of refining. These conditions also accentuated the development and size of the electrolytic plants, which were being worked out at the time this increased demand for pure grade of metal occurred. The electrolytic process, where available, produces a higher grade of spelter from impure ores than does the fire process; a large portion of those impurities in the ore, which by the distillation process would be carried into the spelter, are removed in the leaching of the ores and the purification of the solutions. The refining process, adopted at a number of smelters for the purpose of converting low-grade spelter into grades suitable for bras4 was that of redistillation.

Jan 1, 1918

Schedule of Events

Jan 1, 1977