By Guangshi Li, Xionggang Lu, Xueliang Xie, Xingli Zou, Yuyang Bian, Hongwei Cheng, Kai Zheng, Changyuan Lu

The corrosion resistance and corroded microstructure of MgO-C refractory in molten slag are investigated by immersion test in muffle furnace at 1600 °C . The microstructure and chemical compositions of the specimens after erosion experiment are characterized by scanning electron microscope (SEM) and energy dispersive X-ray (EDX). The results confirm that the oxidation of graphite is the most important degradation mode of MgO-C refractory. The structure of the refractory material is damaged due to the decrease of graphite, as a result, the periclase substrate reacts with the molten slag directly. The corrosion process is controlled by the dissolution of the refractory materials into slag, low melting point oxides are therefore generated which lead to the damage of MgO-C refractory finally.

Jan 1, 2015

By Patricia A. Wells

In the remelting of scrap, the ultimate goal is to produce clean aluminum while minimizing metal losses. Recently, it has become more difficult to make significant recovery improvements in Reynolds' Reclamation Plants since metal recoveries were nearing the theoretical maximum. In an effort to gain a better understanding of the factors impacting Reynolds remelting process, a series of experiments using a Taguchi-type design was performed. Specifically, the critical variables and interactions affecting metal recovery of shredded, delacquered Used Beverage Containers (UBC) melted in a side-well reverbatory furnace were examined. This furnace was equipped with plunger-style puddlers and metal circulation. Both delacquecing and melting processes operated continuously with downtime only for necessary mechanical repairs. The experimental design consisted of an orthogonal array with eight trials, each using nominal 500;000 lb shred charge volumes. Final recovery results included molten output and metal easily recovered from dross generated during the test.

Jan 1, 1995

By P. M. Tait, N. A. Warner

"The refining of thermally produced zinc is currently performed using a highly energy intensive and arguably outmoded process, distilling zinc under atmospheric pressure at temperatures of 900°C to 1000°C. In order to produce refined zinc more profitably and with less environmental impact a new process has been proposed. This process is generic to all thermal zinc smelters and aims to match the purity of zinc from current technology (99.99%-99.999%). The objective is to perform all separation processes using only the heat contained in the smelter product stream. Vacuum conditions are extensively used lowering operating temperatures and enhancing separations. As part of this process zinc is distilled under vacuum from high concentration obtaining a refined product with respect to lead content. A mathematical model has been developed from fundamental principles to describe this stage, the distillation of zinc across a temperature difference between two circulating zinc streams in open channels under vacuum. Heat for the distillation is supplied by the liquid phase, necessitating a large recycle to maintain high operating temperatures, and keep zinc concentrations high. In determining this model and the operating conditions required, relationships between temperature, pressure and composition are considered.IntroductionCurrent technology (the Refluxer) used to refine thermally produced zinc is both expensive and highly inefficient. At present 80% of the worlds zinc is produced via the electrolytic process reflecting the poorer performance of the thermal route, the zinc-lead blast furnace and Refluxer. A new process is proposed to overcome the drawbacks of current processes. These drawbacks are both economic and environmental. The Refluxer requires 6.6 GJ of energy to refine one tonne of SHG zinc 1, other disadvantages of the Refluxer stem from high operating temperature, around 900°C, and liquid zinc being highly corrosive towards ferrous metals. The Refluxer is constructed from silicon carbide sections which join together by means of flat machined faces making liquid metal leaks inevitable. The Refluxer columns are very sensitive to thermal cycling, thermal shock and mechanical vibration, which easily lead to structural failure. To avoid thermal stress on the columns the feed rate and feed temperature need to be kept constant which means the feed baths to the columns must be able to accept solid and liquid feed as the Refluxer has to operate when the smelter is shut down."

Jan 1, 1998

By Tam Tran

Most new gold mines in Australia are required to treat tailings to reduce cyanide levels before they are discharged to storage ponds to meet the stringent environmental management guidelines set by government statutory authorities. In New South Wales, the average level of weak acid dissociable cyanide allowed in open tailings dams is now limited to 20 ppm, As stringent environmental guidelines continue to be enforced in Australia as well as in other parts of the world, the management of cyanide wastes has emerged as a key issue for the gold mining industry. This paper provides a critical evaluation on technical aspects related to the use of ion exchange resins and affiliated processes in cyanide management and tailing treatment. Particular attention is given to the use of ion exchange resin technologies in the processing of mixed gold-copper ores, where cyanide usage is the highest. Information presented in this paper is heavily drawn from the experience on the application of ion exchange resin processes at May Day mine, in New South Wales, Australia and associated pilot plant test programs. Issues related to the management of thiocyanate, especially with respect to the recovery of cyanide from thiocyanate are also discussed.

Jan 1, 1998

By A. F. Giamei, F. Landis, M. O. Duffy, R. J. Mador

"The directional solidification of complex advanced gas turbine airfoils must be carried out without the nucleation of undesirable grains and with minimal shrinkage. Such problems are typically eliminated by using a number of mold design and process iterations. A more efficient approach is envisioned where a solidification model is generated and utilized to accelerate process development. Towards this end, the directional solidification (DS) of simple geometrical shapes in a crystal grower apparatus has been simulated with MARC finite element nonlinear thermal analyses.The finite element models of cylindrical (2D) and rectangular (3D) cross-section bars in the DS environment are presented. Temperature dependent properties, the impact of latent heat of fusion and a time-dependent radiation boundary condition constitute the more salient features of the MARC models. Solidification zone thermal behavior is predicted during the withdrawal transient for the specific case of nickel based superalloys grown in ceramic shell molds. Comparisons of analytical results with experiments demonstrate notable prediction accuracy. INTRODUCTIONSingle crystal and uni-directional crystal turbine blades require tightly controlled conditions if metallurgically and mechanically acceptable parts are to be produced. Gated blade geometry and process parameters must be precisely determined if incorrect grain structure, orientation and shrinkage are to be avoided. Since purely experimental development programs designed to evaluate these parameters can be excessively costly and time-consuming, an effort combining engineering analysis and verification by experiment has been initiated at Pratt & Whitney. Comparison of analytical predictions and measured data for geometries simpler than a turbine blade, namely cylindrical and rectangular bars, comprised the initial stage of this effort. Subsequent tasks involve modeling geometries of increasing complexity and ultimately the simulation of the directional solidification of the turbine blade, shown schematically in Figure 1. This paper summarizes the results of the initial stage of the effort."

Jan 1, 1986

By Dale W. Collins

The disposal of arsenic from copper operations possess various health, environmental and processing problems. There are basically two areas of concern. The first being the disposal or treatment of smelter flue dusts and the second the removal of arsenic from refinery electrolytes. A number of treatment options have been proposed including the addition of soluble arsenic wastes to copper heap and dump leaching solutions. This approach will allow arsenic to be reintroduced to the ore via Solvent Extraction (SX) raffinate associated with hydrometallurgical operations. Knowledge of the attenuation behavior and mechanism during leaching is important in determining the long term stability of arsenic and the success of this approach. Parameters, such as uptake capacity, pH, particle size and solution chemistry have been investigated. Arsenic attenuation has been examined using column leaching with experiments employing both continuous flow and pulsed additions of As(V). In the initial stages of leaching, the attenuation of arsenic appears to depend on the pH and iron concentration in the effluent. Arsenic stability in the copper oxide ore has been examined with rinses of progressively lower pH.

Jan 1, 1994

By Milorad Cirkovic

Kinetics of copper concentrate oxidation in roasting processes in a fluidized bed reactor has been studied at temperatures between 600°C and 720°C using particles of 0.038 to 2.5 mm in average size. The analysis of composition of samples has been done by chemical methods. Phase composition has been determined by Siemens X-ray equipment with Cu anticathode and Ni filters at a voltage of 40 kV and a current of 18 mA. The content of sulphur has decreased from 33.23 to 19.02 mass percent with the increase of temperature, but the content of Fe304 has increased from 0.15 to 17.14 mass percent. The new mechanism of copper concentrate oxidation in a fluidized bed reactor is proposed in this study. It has been shown from the mathematical model that the velocity of oxidation of copper concentrate between 600°C and 720°C is virtually controlled by the rate of diffusion of 02 through the layer of reaction product.

Jan 1, 1999

By M. A. Neri

A lead-free solder alloy Sn-57.5Bi-0.5Ag has been developed by mechanical alloying and foundry processes, and has great potential as a lead-free solder system, to low temperature applications. The mechanical alloying powders show a microstructure different to the microstructure obtained by the foundry process for the same alloy. Its melting point of 142°C is slightly higher than that of eutectic tin- bismuth solder. Examination of the microstructure revealed that eutectic microstructure is refined by the mechanical alloying process Ag additions. The lamellar structure of tin-bismuth gradually disappeared with the process of mechanical alloying, while intermetallic compounds AgaSn phase was formed. The Cu-Sn intermetallic compound layer formed at solder-copper interface is the Cu6Sn5 phase. Keywords: Lead-free solder, Microstructure. Mechanical alloying

Jan 1, 2003

By Z. Smieszek, J. Botor, Z. Miczkowski, S. Sobierajski

"From 1978, the direct process for the smelting of chalcocite concentrates in a flash furnace by the Outokumpu method has been applied at the Glogów II copper smelter. The chemical composition of these concentrates make it necessary to control the process very strictly. In this paper, the method for controlling and measuring the main technological parameters of the copper production by flash smelting is being presented. It includes the determination of the chemical composition of the concentrate, its grain structure, the temperature of liquid products of the process, oxygen content in process gases, as well as lead concentration in copper and copper concentration in slag.The main process parameters are determined from the mass and energy balances. The relations between parameters, such as an effect of grain structure of a concentrate on oxygen and oil consumption, and dependence of chemical composition of a concentrate on capacity and products quality are discussed. 1. IntroductionThe Polish copper concentrates, as most concentrates occurring worldwide, contain from 18% to 30% Cu, and less sulphur (7-11%) and iron (2-5%). The main copper-bearing mineral contained in the concentrates is chalcocite, while bornite and chalcopyrite are present in smaller quantities. Moreover, the organic carbon (5-7.5%), arsenic (0.05-0.3%) and lead (1.2-3.0%) are also contained in the concentrates. The gangue consists mainly of silica, aluminosilicates, calcium carbonate and magnesium carbonate. Their proportions make the addition of slag-forming agents unnecessary.The composition of Polish concentrates, especially their low iron content, allows their application in the direct flash smelting process for blister copper production. Low sulphur content is the factor which determines the necessity of oxygen application in this process."

Jan 1, 1989

By T. T. Nguyen, D. R. Gunasegaram, D. Celentano

"Heat transfer rates at the casting-mold interface are believed to be substantially reduced by the formation of an interfacial gap during the course of solidification of aluminum alloys in permanent molds. In the current work, the effect of force-cooling a permanent composite mold on (i) the initiation and growth characteristics of the gap and (ii) interfacial heat transfer rates are studied. Interesting comparisons are made with the case where no cooling is employed. Casting and mold displacements are measured using L VDTs, and the mold is force-cooled by air jets.IntroductionIn a gravity casting situation where an aluminum alloy solidifies in a permanent mold, a gap initiates and grows between the shrinking casting and the expanding mold (1). It is widely believed that the formation of this gap, customarily referred to as an 'air gap', results in a substantial reduction in the heat transfer coefficient at the casting-mold interface (2), and hence is an important factor in solidification studies.The nature of the air gap formation process is thermo-mechanical. The rate of heat loss from the casting first determines the rate of solidification, which, in turn, decides when the gap initiates. The reason for this is the requirement for the solidified casting surface 'skin' to gain sufficient thickness, and hence strength, to be self-supporting. Once the gap initiates, the gap width controls the rate of heat loss from the casting, which, again, determines the rate at which the gap expands."

Jan 1, 1997

By David R. Sadedin

The highly negative Gibbs free energies of hydrogen atom reactions suggest that refractory oxides such as titanium dioxide should be easily reduced by hydrogen atoms. These reactions appear to be most favourable at low temperatures; oxides should be reducible even at room temperature. Since hydrogen atoms are produced in plasmas containing hydrogen a number of investigators have used hydrogen plasmas of various sorts to test these possibilities for reducing refractory oxides, in particular TiO2. None of these attempts has succeeded, a small degree of reduction being achieved in only a thin layer near the surface. A deeper consideration shows that several factors complicate the reactions expected on the basis of the negative Gibbs free energy. One factor is that the back reaction by water molecules produces molecular hydrogen, not hydrogen atoms, and the metal atoms that have been reduced may be immediately re-oxidised. In plasmas there are complications due to diffusion, thermal and charge boundary layers and charged particle reactions. Interpreting the results of hydrogen atom reactions is difficult. Hydrogen is not detectable by electron dispersive spectroscopy and amorphous products are not determinable by x-ray diffraction. Another consideration is economics. The cost of producing hydrogen atoms has a large bearing on the metals for which hydrogen atom reduction may be competitive. In this paper these factors are discussed, some necessary basic studies are highlighted and the general principles of a laboratory reactor are given, together with the results of tests using ZnFe2O4, ZnO and TiO2 as test oxides.

Jan 1, 2006

By T. Mutoh

Tellurium in raw slime has recently been recovered as copper telluride in Onahama Smelter & Refinery. The slime is decopperized with sulfuric acid solution in conventional leaching tanks. The pregnant leach solution containing 45 g/l of copper and 1 g/l of tellurium is introduced to a copper telluride recovering reactor. The tail solution from the reactor containing less than 20 mg/l of tellurium is recycled directly to circulation tanks of copper electrolysis. The impurities of the product copper telluride is kept below 1% without any purification.

Jan 1, 1990

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004

By Hiroyuki Sano

A closed recycling process for the low-grade scrap of Al-based composite materials was developed. In this process flux treatment with water-soluble halide is a key technique. In the present work, flux treatment conditions were discussed from the viewpoint of the separation and the recovery of the base material, reinforcement and flux. Optimum separation condition was obtained for the NaCl-KCI-KF flux treatment. The recovered aluminum alloy can be recycled for various usages. The recovered SiC particles cannot be reused as reinforcement because of the coexistence of the contamination, therefore it is necessary to eliminate these contaminates or to find another use. The recovered flux is reusable with supplemental addition of fluoride.

Jan 1, 2003

By X. K. Lan

The greater demand for high-quality large-diameter crystals has led to the robust idea of a free- flying solar-powered furnace satellite, whereby the buoyancy-driven convection effects are almost nonexistent, and diffusion-controlled crystal growth with minimal radial segregation is promoted. In the proposed solar furnace, a paraboloid of revolution imaging concentrator is used to focus the sun's radiation onto an-ampoule which holds the solid charge to be processed. The charge will start melting in the vicinity of the focal point, after which it is translated in order for the melt to resolidify as a single crystal. A ray-trace method has been developed to determine the incident concentrated solar heat flux on the ampoule surface for a perfectly-aligned configuration with an incoming columnated beam. A transient 2- dimensional conduction problem with phase change is formulated, which is solved using the commercial code FIDAP. Results highlighting the feasibility of growing GaAs, Ge and Si crystals with diameters of the order of 20 cm using the solar furnace satellite concept are presented. The transient temperature fields within various charge materials are quantified.

Jan 1, 1994

By Peter V. Barr

Despite the advent of modem firing control systems reheating furnace operations frequently allow significant thermal excursions in the discharged slabs or billets after furnace delays. Although HSM furnaces are not immune to this and other related problems, mini-mill operations are most vulnerable due to their more frequent delays and (often) less sophisticated control systems. In order to reduce these problems control systems will commonly include a thermal model, operating either on-line (interacting directly with the controller logic) or in an advisory, off-line mode. Using a new 'fast' thermal model, the paper examines the thermal response of a typical mini-mill furnace during both delays and the subsequent recovery period. A variety of firing strategies are explored and compared on the basis of maintaining thermal excursions within allowable limits for rolling. Other factors, such as the potential for overheating of billets within the furnace during delays and the overall thermal state of the furnace, are also considered in some detail. Although common practice, the use of conventional thermocouple zone temperatures for furnace control during and after delays is shown to be a dubious proposition. Keywords: Reheat Furnace, Modeling, Process Control

Jan 1, 2003

By M. Kobashi, T. Choh, N. Kanetake

"A new processing route, which enables the cost-effective and energy- saving fabrication of metal matrix composites, have been proposed. The pressureless infiltration of the reactive powder blend with molten aluminum was investigated in this work. The molten aluminum infiltrated into the [Ti + C] powder blend spontaneously, whereas the spontaneous infiltration into the TIC powder phase did not occur under the same experimental condition. The processing time was shortened and· the processing temperature was .lowered by adding the aluminum powder in the [Ti + C] powder. The differential thermal analysis revealed that the aluminum powder in the powder blend melted at 933K and then ignited the reaction between titanium and ·carbon. However there was an .optimum additional amount of aluminum in the powder blend. The TiC formed in situ had three-dimensionally continuous morphologyIntroductionThe squeeze casting process has been used as one of the processing routes for aluminum matrix composites. [1, 2]. Non-reactive metal-ceramic systems have been, generally, used in this technique in order to prevent the degradation of the ceramic phase. Materials obtained by this process basically consist of a continuous metal matrix and discontinuously dispersed ceramic particles. Reactive systems have begun to be introduced into the infiltration process· recently [3A]. Since the ceramics are synthesized in-situ, this process can provide a continuous ceramic matrix [5]. This is one of the outstanding features of this technique in that a bulk ceramic-can be synthesized at relatively lower temperatures in a short time. Another advantage is that the highly reactive combination of a ceramic with a molten metal is in many cases wettable [6], which enables a spontaneous infiltration."

Jan 1, 2000

By Olexandr Gydin

The evolution of grain and dislocation structures during cold deformation of the new steel LH800 of Salzgitter AG is investigated in the frame of this work. The main feature of this material is its ability to air-harden by carbon content of about 0.1%. The initial ferrite structure of the metal provides high plasticity at cold deformation and subsequent heat treatment increases tensile strength approximately two times. Described are results of in-situ tensile tests in the SEM. SEM and TEM analysis of grain and dislocation structures evolution in samples, which have been uniaxially deformed to certain strains, are carried out. After statistical evaluation of results the grain elongation against strain is determined. A microstructure of a deep drawn cup is analyzed by means of SEM. A quantitative evaluation of grain elongation on the different cup zones and comparison of these data with prediction results based on tensile tests are carried out.

Jan 1, 2009

By Hans Jürgen Maier, Hans-Bernward Besserer, Gregory Gerstein, Florian Nürnberger

The formation and development of voids in both the single-phase ferritic steel DC04 and the dual-phase ferritic-martensitic steel DP600 are discussed. Various mechanisms and kinetics of void formation are considered regarding the influence of dislocation glide, precipitates and other parameters. Different characteristic locations in the microstructure are investigated at which strain concentrations during plastic deformation can occur and cause the formation of voids and microcracks. For the specimen preparation ion slope cutting is applied. Voids and cracks revealing ductile damage are analyzed by Scanning Electron Microscopy (SEM). Stress concentrations in consequence of plastic deformation could be shown by extinction contours on images recorded by Transmission Electron Microscopy (TEM).

Jan 1, 2015

By D. L. Jones

The leaching of natural chalcopyrite was studied in both ferric sulfate and ferric chloride solutions. The chemistry of the two reactions is quite different, with substantial sulfur oxidation occurring only in sulfate solutions. Ferric chloride is a more effective reagent, for the leaching rate is greatly increased with finer particles and higher (Fe+++), and unaffected by high (Fe++); none of these advantages are found with ferric sulfate. In addition, the morphology of leaching appears to be different, with ferric sulfate leaching preferentially along fissures or grain boundaries. The kinetics were found to be linear over an extended period, rather than parabolic as reported elsewhere. An explanation of the observed phenanena is proposed using the electrochemical theory of leaching, and experimental measurement of the mixed potential of the mineral during leaching.

Jan 1, 1976