By F. D. Rosi, F. C. Perkins, L. L. Seigle

An investigation was made of the mechanism of plastic flow in coarse grained specimens of both sponge and iodide titanium at low (-196°C) and high (500° and 800°C) temperatures. Deformation by slip occurs predominantly on a {1011} plane and in a <1120> direction over this entire temperature range, and secondary slip on {101-1} planes becomes more prevalent with overthisentireincreasing temperature.range, The crystallographic habit of the predominant twin planes becomes more prevalent with type is temperature-dependent, and deformation by twinning increases as the temperature of testing is lowered. Kink bands were not observed at -196OC and rarely at the high temperatures. A LTHOUGH the deform a tional mechanisms in . -titanium at atmospheric temperature have been extensively investigated," there is little information regarding the influence of testing temperature on these mechanisms. The only available data come from the recent work by McHargue and Hammond, who extended single crystals of iodide titanium at a temperature of 815°C. No significant changes in the types of slip and twinning planes were observed, but increased activity on the type I, order 1 pyramidal slip planes and on the type 11, order 2 twinning planes was reported. These planes contribute very little to the deformation process at room temperature.&apos;&apos; &apos; Since there is interest in titanium as a material for use at both low and high temperatures, the present investigation was undertaken to examine the slip and twinning behavior in coarse grained specimens of titanium at -—196", 500°, and 800°C in order to determine the general effect of temperature on the mechanism of plastic deformation. Experimental Material Used and Specimen Preparation—Both sponge and iodide titanium were used in the present investigation; chemical analyses appear in Table I. These materials were arc-melted under argon into 25 g slugs, which were then cold-rolled approximately 90 pct to a sheet thickness of 0.05 in. Since the strain-anneal technique was used for obtaining coarse grains, the cold-rolled sheets were made into tensile specimens which were then annealed to produce a relatively coarse uniform grain structure prior to critical straining. The details of the strain-anneal treatment. size of grains, and the method for preparing the specimen surface for optical microscopy have been described in a previous report.&apos; In order to obtain a wider spread in crystal orientation for the present work, it was necessary to vary the rolling schedule to reduce the degree of preferred orientation in the annealed sheets prior to critical straining. Methods for Tensile Testing—The apparatus for experiments at the temperature of liquid nitrogen (—196°C) consisted of two concentric stainless steel

Jan 1, 1957

By C. R. Taylor, John Chipman

THE study of chemical reactions of liquid steel and basic open-hearth slag involves a complex slag system of at least eight important components, and often a number of others. In initiating an experimental program on the equilibrium relationship of slag and metal, it became evident that but little progress could be expected in the interpretation of the complex slags until an understanding had been gained of the simpler liquid systems composed of a limited number of slag constituents. The simplest system that in any way resembles open-hearth slag must contain lime, silica and iron oxide. Attempts to produce in an induction furnace slags containing only these constituents have met with serious limitations because of the solubility of refractories in the slag. Thus in acid-lined furnaces the slag is always saturated with silica and consequently contains between 48 and 63 per cent of this component. In basic-lined furnaces an undesired additional component, magnesia, is introduced to the extent of some 3 to 15 per cent, depending upon the acidity, sometimes with disastrous results to the furnace. Thus in a magnesia-lined furnace, Fetters and Chipman1 found it impossible to prepare slags in which the ratio (CaO + MgO)/SiO2 was less than that corresponding to the metasilicate (approximately 0.8: I). Between this composition and that of the true acid slags lies a field of composition about which very little is known and which cannot be explored by any ordinary means. This circumstance, as well as the desire to study the more basic slags in the absence of magnesia, calls for the development of a method by which slags may be brought into equilibrium with molten metal without coming in contact with refractory. Such a technic has been provided by the rotating induction furnace developed by Barrett, Holbrook and Wood.2 Three modifications of the rotating furnace were described by these authors. The first was essentially a rotating refractory cylinder containing the magnesia crucible, which was itself heated by a graphite crucible. In the second, only the magnesia crucible rotated, the cylindrical graphite heater being stationary. In the third, the coil and crucible revolved, and the metal was heated directly by induction. EXPERIMENTAL METHOD Furnace The furnace used in this investigation differed from previous designs and may be considered a fourth modification of the original rotating furnace. Its essential features are shown in Fig. I. The outer case A is a fire-clay flue liner for control of the atmosphere. The top B and base C are alberene stone. The coil supports D are of "Formica," a material formed from phe-

Jan 1, 1942

By H. R. Barnhurst

It would be a difficult matter to trace from the beginning the very few improvements made in the burning of fuels prior to 1860. Donbtless the crossing of the sticks of wood in building a mood fire early appealed to our savage ancestry as a means of expediting its effectiveness for their crude culinary purposes. Stones and andirons came later in assisting the admission of air to the under part of the fuel bed, while beacons and cressets, utilized metal bars as supports for the same purpose. It is probable that Tuba1 Cain owed his success to the use of bellows making possible the use of mixed fuel and charge upon a hearth. With the development of working in cast iron, grate bars came in, and they are still with us doing duty in every household and almost every art where heat is a factor. Little was done beyond these crude methods prior to 1860. With the advancement of knowledge came the fuel-gas producer, a natural child of the retorts employed in supplying illuminating gas. It is only within the last 15 years that the conclusion became general that complicated systems for saving heat would not remedy deli-. ciencies in its primary development, and within that time there has been great advancement in the means of producing initially a fire of high effciency, so that to-day we are moving rapidly toward both high development and high absorption, with the resultant of high efficiencies. In studying the subject of the availability of pulverized coal as a fuel, it may occur to ask, why has this not come up earlier? This, question would be naturally prompted by recalling the fact that Thomas Crompton&apos;s English patents upon his methods were issued to him nearly 40 years ago. A conclusive answer to this, however, is that Crompton at that time had very crude facilities for making what was at best a very imperfect pulverization of the coal, arid the expense of preparation mas very great. He does not seem to have been aware of the advantage of a thorough drying of the coal in the

Jan 1, 1914

By George A. Moore

A recent survey of existing analytical results, and an attempt to correlate them with each other and with the known history and behavior of the samples, indicated that none of the commonly applied methods could be considered established as intrinsically reliable. It was. therefore, desired to attempt to establish the reliahility of some one method by external evidence. If this were to be accomplished, other methods could then be evaluated in terms of the method establibhed. The correct method was accordingly to be chosen without regard for cost, speed, or convenience; with the requirements for routine application to be reserved for 1ater consideration. The method of total combustion was chosen and submitted to a limited number of tests against primary standard samples. Considerable experimental difficulty was encountered, indicating that additional work on the experimental arrangements is desirable. While the work to (late by no means represents a completed investigation, it is helieved that the combustion method is basically sound and that its development should be continued. Choice of Method Of the several available methods, mechanical disintegration. electrochemical methods&apos;2&apos;3 modifications of the Sieverts experiment,% and vacuum fusion, were all judged to contain one or more factors of un- certainty not at present completely cvaluated or suhject to complete control. These methods, therefore, were considered currently unsuitable for referee purposes. Solid evolution was considered to be of doubtful significance when conducted in the alpha range. A reasonable chance for a true analysis was found for evolution in the gamma range. Preliminary tests have indicated a very slow rate for evolutioll from gamma iron. indicating a running time of possibly 100 hr. for a one-centimeter sample. Difliculty in distinguishing such slow. evolution from blank gas was anticipated, hence the method was not consitlerctl the most suitable for the present purpose. The combustion method was evaluated as being most sound on fundamental principles. The only important unknown would be to determine that the iron oxide formed did not occlude water at the tcmperaturv of the combustion.with the odvious precautions of using a sound and clean specimen, providing a system sufficiently tight to give acceptable blanks in longtime runs, and providing a suficicntly sensitive measuring system, reasonable, precise, and truthful analytical results could be logically expected. Apparatus The equipment as originally operated is shown in Fig. I, and the glassw-are in its latest modification in Fig. 2. The sulphuric acid drier and small safety tube in the upper right of Fig. I were replaced by a KOH drier and combined manometer safety tube, to permit operation at reduced

Jan 1, 1945

By Richard M. Foose

FIVE miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. GEOLOGY Lower Cambrian Antietam quartzite and the Montalto quartzite, stratigraphically older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65° to vertical. The clay crops out at an elevation of about 1000 feet. ORIGIN AND CHARACTER The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about l00 ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: Si02, 67.05 per cent; A1203, 22.27; Fe203, 0.40; CaO, 0.00; Ti02, 1.05; MgO, 0.52; Na20, 0.04; K20, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1944

By J. A. Herbst, K. Rajamani, M. Siddique

This paper presents an investigation of the accuracy of population balance model predictions for ball mill scale-up. Experiments performed in 25.4 x 29.2 cm (10 x 11.5) batch mill are used to estimate linear grinding rate parameters that, in turn are scaled according to specific power draft to predict performance in 381 x 292 mm (15 x 11.5 in.) and 762 x 457 mm (30 x 18 in.) batch and continuous ball mills, respectively. Results are presented for wet and dry grinding of two homogeneous solids, limestone (soft) and quartz (hard), and one heterogeneous solid, a complex molybdenite ore. In all cases good agreement between predicted and experimental product size distributions was obtained.

Jan 1, 1983

By Richard A. Walker, John P. Hager

The thermodynamic properties of the Pb-Au system have been determined between 750" and 1075°C by means of the cell Mo, Pb(1) |(PbO-SiO2){l) , SiO2(s) |Pb-Au(1), Mo The activities of lead and gold exhibit negative deviations from ideal behavior; the values of ? pb and ? the raoultain activity coefficients at infinite dilution, being 0.24 and 0.25, respectively, at 1200°K. The liquidus curve for the gold-rich region of the Pb-Au phase diagram has been determined from measure-ments on seven alloy compositions in the two phase region (liquid + Au(s)). The standard free energies of formation of Au2O(l) and Ag2O (1) have been estimated from cell measurements obtained by replacing the alloy electrode with pure liquid gold and silver. A new integral molar heat of mixing curve for the liquid Pb-Au system is presented and the results of previous studies discussed. The contribution of HM to FE was found to be small relative to TSE. THE use of galvanic cells of the type A(l) |A+Za|A - B(l) [I] provides an accurate means for the thermodynamic study of liquid alloy systems. In Part 1&apos; it was shown that cells of type [I] may be extended to higher temperatures and to a wider range of alloy systems if the ion A+Za is incorporated in an appropriate molten oxide phase, rather than in the classical fused salt electrolyte. In the following investigation the experimental method is extended to an investigation of the thermo-dynamic properties of the Pb-Au system by use of the cell: Mo, Pb(l) | (PbO-SiO2)(l), SiO2(S) |Pb-Au(l), Mo [] Previous measurements on liquid Pb-Au alloys were obtained by Kleppa2 by electromotive force measurements on a galvanic cell involving a molten chloride electrolyte. These measurements were confined to temperatures less than 830°C and compositions with X Pb > 0.2 because of the instability of the cell at higher temperatures. Later measurements by Kleppa3 on the heats of formation in the composition range 0.67 < Xpb < 0.98 were not consistent with the results by electromotive force measurement. The purpose of the present study is to extend the temperature and composition range of the thermodynamic properties and to obtain an independent measure of the integral molar heat of mixing over the entire composition range.

Jan 1, 1970

By C. M. Means

Considering the hazard involved in mining operations, statistics show that a very small percentage of accidents is chargeable to electricity. These accidents do represent quite a large percentage of those that are preventable and they are the direct result of the introduction, for purely economical reasons, of a dangerous element. The introduction of electricity in mines should decrease the hazard, and in no case should electricity be applied to the mechanical operation of equipment if by so doing the dangers incidental to mining are increased. The greater number of accidents are the result of persons coming in contact with exposed conductors at potentials varying from 258 to 508 volts direct current. The use of alternating current at higher potentials than these is quite common in large mines, but it is very rare that an accident happens from this source. This is explained by the fact that where these high voltages are warranted, proper precautions are taken, and the installations are directed by those who fully appreciate the dangers incidental to the work. Direct current is in much more general use than alternating current because of its adaptability to haulage locomotives and the low cost of installation in small operations. We are, however, coming to a more extended application of alternating current for the operation of mechanical devices used in connection with mining. Our underground direct-current wiring system is an evolution from the surface trolley and feeder systems. This is probably due to the fact that our earlier successful applications were electric locomotives, which required the use of a trolley wire. The trolley current has been almost banished from industrial establishments on the surface because of the hazard involved, yet we use it indiscriminately underground, where the dangers from accidental contact or fire are infinitely greater., This does not mean that the underground trolley systems should be eliminated, but it does imply the proper safeguarding of such equipment as is necessarily a part of the trolley systems. It is a fact that the men now employed in the installation and maintenance of mining equipment may be in many cases incompetent or not thoroughly familiar with the work, but they are the men who must do the work and, in order to do it properly, it is necessary that they be educated

Jan 1, 1915

By C.R. Taylor, John Chipman

The study of chemical reactions of liquid steel and basic open-hearth slag involves a complex slag system of at least eight important components, and often a number of others. In initiating an experimental program on the equilibrium relationship of slag and metal, it became evident that but little progress could be expected in the interpretation of the complex slags until an understanding had been gained of the simpler liquid systems composed of a limited number of slag constituents. The simplest system that in any way resembles open-hearth slag must contain lime, silica and iron oxide. Attempts to produce in an induction furnace slags containing only these constituents have met with serious limitations because of the solubility of refractories in the slag. Thus in acid-lined furnaces the slag is always saturated with silica and consequently contains between 48 and 63 per cent of this component. In basic-lined furnaces an undesired additional component, magnesia, is introduced to the extent of some 3 to 15 per cent, depending upon the acidity, sometimes with disastrous results to the furnace. Thus in a magnesia-lined furnace, Fetters and Chipman1 found it impossible to prepare slags in which the ratio (CaO + MgO)/SiO2 was less than that corresponding to the metasilicate (approximately 0.8:I). Between this composition and that of the true acid slags lies a field of composition about which very little is known and which cannot be explored by any ordinary means. This circumstance, as well as the desire to study the more basic slags in the absence of magnesia, calls for the development of a method by which slags may be brought into equilibrium with molten metal without coming in contact with refractory. Such a technic has been provided by the rotating induction furnace developed by Barrett, Holbrook and Wood.2 Three modifications of the rotating furnace were described by these authors. The first was essentially a rotating refractory cylinder containing the magnesia crucible, which was itself heated by a graphite crucible. In the second, only the magnesia crucible rotated, the cylindrical graphite heater being stationary. In the third, the coil and crucible revolved, and the metal was heated directly by induction. Experimental Method Furnace The furnace used in this investigation differed from previous designs and may be Sci- a fourth modification of the original rotating furnace. Its essential fea tures are shown in Fig. I&apos; The Outer case A is a fire-clay flue liner for control of the atmosphere. The top B and base 6 are alberene stone. The coil supports D are of ""Formica," a material formed from phe-

Jan 1, 1943

By C. R. Taylor, John Chipman

The study of chemical reactions of liquid steel and basic open-hearth slag involves a complex slag system of at least eight important components, and often a number of others. In initiating an experimental program on the equilibrium relationship of slag and metal, it became evident that but little progress could be expected in the interpretation of the complex slags until an understanding had been gained of the simpler liquid systems composed of a limited number of slag constituents. The simplest system that in any way resembles open-hearth slag must contain lime, silica and iron oxide. Attempts to produce in an induction furnace slags containing only these constituents have met with serious limitations because of the solubility of refractories in the slag. Thus in acid-lined furnaces the slag is always saturated with silica and consequently contains between 48 and 63 per cent of this component. In basic-lined furnaces an undesired additional component, magnesia, is introduced to the extent of some 3 to 15 per cent, depending upon the acidity, sometimes with disastrous results to the furnace. Thus in a magnesia-lined furnace, Fetters and Chipman1 found it impossible to prepare slags in which the ratio (CaO + MgO)/SiO2 was less than that corresponding to the metasilicate (approximately 0.8:I). Between this composition and that of the true acid slags lies a field of composition about which very little is known and which cannot be explored by any ordinary means. This circumstance, as well as the desire to study the more basic slags in the absence of magnesia, calls for the development of a method by which slags may be brought into equilibrium with molten metal without coming in contact with refractory. Such a technic has been provided by the rotating induction furnace developed by Barrett, Holbrook and Wood.2 Three modifications of the rotating furnace were described by these authors. The first was essentially a rotating refractory cylinder containing the magnesia crucible, which was itself heated by a graphite crucible. In the second, only the magnesia crucible rotated, the cylindrical graphite heater being stationary. In the third, the coil and crucible revolved, and the metal was heated directly by induction. Experimental Method Furnace The furnace used in this investigation differed from previous designs and may be Sci- a fourth modification of the original rotating furnace. Its essential fea tures are shown in Fig. I&apos; The Outer case A is a fire-clay flue liner for control of the atmosphere. The top B and base 6 are alberene stone. The coil supports D are of ""Formica," a material formed from phe-

Jan 1, 1943

By R. S. Wagner, C. E. Miller, H. Brown

A dc field was applied to liquid BI-Sx or Au-Ge alloys of eutectic composition. The liquid alloys were kept at a temperature slightly above the eutectic. The concentration changes due to electrodijfusion are large enough to cause nuclcation and growth of the primary phases at the respective electrodes. Nearly complete separation of Bi-Sn eutectic was obtained as well as substantial separation of Au-Ge eutectic. The effect of an electric field on the solute distrihn-tion was itluestignted itt tlirectiortally solidified rods of a dilute Bi-Sn (0.5 al. pc,t Bi) alloy. Field-freezing was carried out in small-diameter cupillay tubes to avoid cotuectice mixing -of the liquid. The relative sollcte corzcentratioi, Cs/Co , was rneusred by n radioac1il.e tracer netlod. Cs/Co can be made both largev than unity or srialler than the equilibiuwz distvibrrlion c.oejyicienl, k, , oiler a substattiul portion of the soliclifi&apos;erl rocls. A direct current, passed through a liquid-metal solution, can cause substantial concentration changes by electrodiffusion. The magnitude of the change depends on the difference in ionic mobilities of the atomic species in solution. Electrodiffusion has been studied in many binary and ternary liquid alloys.&apos;y2 It was found that the rate of material transport decreases with time for a constant applied field, as a concentration gradient is established in the solution. A steady-state concentration profile is achieved when electro-diffusion is compensated by chemical diffusion. This may seem to limit the use of electrodif fusion for metallurgical application. However, a way of utilizing the effect of electrodiffusion is to combine it with crystallization or controlled freezing. rakin was first to propose this as a new method of separating metal alloys of eutectic composition at temperatures slightly above the eutectic temperature. It was possible by this method to separate Bi-Sn and Bi-Cd eutectics into their component phases. Angus et al discussed the possibility that the effective distribution coefficient, keff, could be varied by proper application of an electric field during solidification. The combination of electrodiffusion and solidification, called field-freezing, was discussed in detail by Pfann and aner. It was shown that field-freezing can be used as a crystal-growth process, an efficient method for eutectic separation, and a new means of changing the effective distribution coefficient. k,ff, beyond the usual range of ko < k,ff < 1. The liquid layer adjacent to the solid-liquid interface can be either increased or depleted in solute due to

Jan 1, 1967

By W. G. Pfann

In zone-melting, a small molten zone or zones traverse a long charge of alloy or impure metal. Consequences of this manner of freezing are examined with impurerespect to solute distribution in the ingot, with particular reference to purification and to prevention of segregation. Results are expressed in terms of the number, size, and direction of travel of the zones, the initial intermsofsolute distribution, and the distribution coefficient. IF a charge of binary solid-solution alloy is melted and then frozen slowly from one end, as for example in the Bridgman method of making single crystals,&apos; coring usually occurs, with a resulting end-to-end variation in concentration. Such coring, or normal segregation, is undesirable where uniformity is an object. On the other hand, for certain systems, it can be utilized to refine a material by concentrating impurities at one end of the ingot.&apos;. &apos; In the present paper a different manner of freezing will be examined with respect to the distribution of solute in the ingot. A number of procedures will be indicated which have in common the traversal of a relatively long charge of solid alloy by a small molten zone. Such methods will be denoted by the general term zone-,melting, while the process described in the preceding paragraph will be called normal freezing. It will be shown that, in contrast to normal freezing, zone-melting affords wide latitude in possible distributions of solute. Segregation can either be almost entirely eliminated or it can be enhanced so as to provide a high degree of sttparation of solute and solvent. A number of simplifying assumptions will be invoked which, while not entirely realizable in practice, nevertheless provide a suitable point of departure for more refined treatments. Moreover, our own experience with zone-melting has shown that, for certain systems at least, the analysis holds quite well. The present paper will be confined to a discussion of principles and a general description of procedures. Comparison with experiment is planned for later publication. Normal Freezing Before considering zone-melting, segregation during normal freezing will be reviewed briefly. If a cylinder of molten binary alloy is made to freeze from one end as in Fig. 1, there usually will be a segregating action which will concentrate the solute in one or the other end of the ingot. If the constitutional diagram for the system is like that of Fig. 2, then the distribution coefficient k, defined as the ratio of the concentration in the solid to that in the liquid at equilibrium, will be less than one and the solute will be concentrated in the last regions to freeze. If the solute raises the freezing point, then k will be greater than one and the solute will be concentrated in the first regions to freeze. The concentration in the solid as a function of g, the fraction which has solidified, can be expressed by the relation: C = kC0 (1-g)k-1 [I] where C, is the initial solute concentration in the melt. Eq 1 is based on the following assumptions: 1—Diffusion in the solid is negligible. 2—Diffusion in the liquid is complete (i.e., concentration in the liquid is uniform). 3—k is constant. Concentration curves representing eq 1 for k&apos;s from 0.01 to 5.0 are plotted in Fig. 3. This equation, in one form or another, has been treated by Gulliver,³ Scheuer,4 Hayes and Chipman5 for alloys and by McFee2 for NaCl crystals. It is derived in Appendix I. It should be pointed out that the k which is calculated from the phase diagram will be valid only in the ideal case for which the stated assumptions are correct. In all actual cases, the effective k will be larger than this value for solutes which lower the melting point, smaller for solutes which raise the melting point, and will probably vary during the beginning of the freezing process. For simplification it will be assumed that the ideal k is valid. Zone-Leveling Processes The processes of this part are designed to produce a uniform, or level, distribution of solute in the ingot. Single Pass: Consider a rod or charge of alloy whose cross-section is constant and whose composition, C2, is constant, although permissibly varying on a microscopic scale." Such a charge might be a rapidly frozen casting or a mixture of crushed or powdered constituents. Cause a molten zone of

Jan 1, 1953

By Otto F. Pfordte

Although the subject has no practical bearing on the metallurgy of the present day, it may not be entirely uninteresting to note how the art of silver-lead smelting has been, and in a few remote districts of Peru is still practiced by an old method, and under conditions widely different from our own. The subject will be considered under the following subdivisions,. viz.: The general conditions; construction and plan of furnaces;, fuels and ores; method of working; furnace products and slags. The mineral region of Peru varies in altitude from 10,000 to 16,000 feet above sea-level, comparatively few mines being locatedh above or below these limits. The timber-line in the valleys is at about 12,000 feet altitude on the western slope of the mountains, and even there the supply of wood is not sufficient to be utilized as fuel for furnaces. The sides of the mountains are either bare or covered with a hard bushy grass, which is most luxuriant during the latter part of the rainy season, from February to April. Agriculture on the western slope rarely reaches above 12,000 feet, while on the eastern slope its limit is at 14,000 feet; and in either case the height named is reached only in sheltered places. Transportation is slow, being carried on mainly by llamas, donkeys and mules; the former (taking 100 pounds at a load) are almost

Jan 1, 1893

In accordance with the requirements of our By-Laws I beg leave to submit herewith the report of the Library Committee for the year 1915. The activity shown by the sale of the institute publications during the year continues satisfactory, although not as large as last year. The total sales amount to $6,666.81, distributed as follows: Sale of Transactions...:: :. $4,585.42 Sale of Special Editions 553.17 Sale of Pamphlets and Bulletins 2,028.22 It should-be borne in mind that the sale of special editions was only begun last year,, and most of the members who did not have the special editions immediately bought them for their libraries. This year only a little less than half of the same number have been disposed of, and it is more than probable that from now-on the number will be considerably lessened.

Jan 2, 1916

By D. Moskowitz

IN the course of a general investigation of boride systems, sponsored by the Office of Naval Research, various vanadium boride powders of relatively good purity were prepared which could be used for a determination of the phases present. The X-ray pattern of one of these lots showed, in addition to the known VB1 and VB22 phases, an additional phase, almost certainly of composition V3B4, isomorphous with Cr3B4, Cb3B4, Ta3B4, and Mn3B,. Its pattern fitted in well with the indices worked out by Kiessling for Mr3B4.3 The unit cell for this new compound is orthorhombic, with the dimensions a = 3.030A, b = 13.18A, c = 2.986A7 V=119.2A.&apos; Table I lists the X-ray diffraction data for V.3,.

Jan 1, 1957

By D. D. Pollock, G. P. Conard II

Equations of the form of the Mott and Jones equations for the absolute thermoelectric powers of metals are derived primarily from a thermodynamic approach. The behaviors of transition thermoelements in common use are then examined and compared with this simple theory. MOTT and ones&apos; derived a general expression for the absolute thermoelectric behavior of metals and alloys using the approach of the solid state physicist. This expression was then applied to specific cases.1,2 The present work develops equations of the same form principally by a thermodynamic approach. These relationships are then employed to gain some insight to the behavior of the transition thermoelements in common use. I) DERIVATION OF AN EXPRESSION FOR ABSOLUTE THERMOELECTRIC POWER First consider a metallic conductor which is maintained in a temperature gradient with no current flowing. At constant pressure, there will be a gradient of the free energy (F,) given by:

Jan 1, 1963

By R. A. Vandermeer, Paul Gordon

On the basis of a unified concept, theoretical erPressions for grain boundary migration in recrys-tallization are derzved for impurity-controlled and impurity-independent migration. The expression in the former case is analogous to that Previously derived by Lucke and Detert, and in the latter is shown to be equivalent to that usually obtained on the basis of absolute reaction rate theory. The equations are tested with quantitative experimental data for boundary migration obtained for the recrystallization of poly crystalline zone-refined alumimnz and for binary "alloys" of this aluminum with 0.00021, 0.00043, 0.0017, 0.0034, 0.0068, 0.0124, and 0.0256 at. pct Cu, respectively. All the essential characteristics of the e@erimentally determined boundary migration rates check both qualitatively ard quantitatively with the predictions of the theoretical equations. THE rates of transformations are customarily analyzed phenomenologically in terms of the two component rates—N, the rate of nucleation and, G, the rate of growth of the nuclei. The scientific aim of both theory and experiment is to describe the fundamental atomic phemmena involved in these two component processes with the hope that parameters calculated from theoretical equations will check those found experimentally. In solid state transformations, the theoretical and experimental problems are both generally of almost prohibitive complexity, for in addition to changes in composition and in such properties as density which may accompany transformations in amorphous, nonrigid materials, transformations in crystalline substances also involve structural changes, crystal reorientations, and the development of stresses. In studying such transformations it thus becomes; highly desirable, if not essential, to focus on a transformation and a set of conditions which minimize the number of active variables. This principle has been applied with considerable success by Cohen and his associates&apos; in their evaluation of nucleation theories using the martensite transformation as the basis of study. A similar possibility exists for the evaluation of growth theories by the use of recrystallization after cold-deforming. If an unalloyed metal is employed as the subject of investigation, the recrystallization transformation involves basically only a change in strain-conditions and orientations. In spite of this possible simplilfication, however, until recently little quantitative success has attended attempts to correlate recrystal1ization parameters measured experimentally with those calculated theoretically. It seems highly probable that this lack of success may be attributed, both in the experimental and theoretical treatments, to one or more of the following factors: a) conditions have usually been studied under which apparently* both nucleation and growth are active;

Jan 1, 1962

ALFRED C. LANE, Tufts College, Mass. (written discussion*).-The attention of members may well be called by Allen to his discoveries, which affect not only correlations in Michigan but, as I have pointed out,1 the use of names like "Animikie" which are widely applied. It shows that one disadvantage of the wide use of locality names is that local discoveries may show that they are inappropriate. The Wewe hills were found not to contain the Wewe slate! So we note that Allen, in his correlation, drops the term Animikie, which his researches indicate covers both middle and upper Huronian: It would seem well, then, in dividing the Huronian or Proterozoic, to use, as Allen does, terms like upper, middle, and lower Huronian, or newer, middle, and early, which may be shortened into eo-, mio-, and neo-Huronian rather than to carry local terms far away; or we shall soon be

Jan 12, 1919

Rossiter Worthington Raymond, Ph.D., LL. D-1840 to 1918.-Dr. Rossiter W. Raymond, Past President, Honorary Member and Secretary Emeritus, died suddenly of heart failure at his home, 123 Henry&apos;St., Brooklyn, N. Y., on the evening of Tuesday, Dec. 31, 1918. He was one of the founders of the Institute and its second President. A Memorial &apos;Service will be held on Monday afternoon, Feb. 17. James Douglas.- The Institute suffered a second very severe loss by the death of Dr. James Douglas, Honorary Member, Past President (having served as President for two years), and in three separate respects the greatest benefactor of the Institute: first, in raising funds by volun¬tary subscription and his own personal gifts to pay the Institute&apos;s share of the money owed on the land on which the Engineering Societies Build¬ing now stands; second, as original donor to Engineering Societies Library; and third, by his bequest of $100,000 for the maintenance of the library of the American Institute of Mining Engineers. A resolution regarding the death of Dr. Douglas was passed by the Board of Directors and at the meeting of the Institute on Sept. 4, 1918, in Colorado, at which time a memorial service was held in the thea¬ter of the Hotel Broadmoor, attended by about 400 members and guests. A copy of the resolution was prepared and sent to the family. A bronze tablet is now being prepared and will be placed in the Members&apos; Room and unveiled at the February meeting. A biography and portrait of Dr. Douglas was published in the September, 1918, Bulletin. There is also placed in the Engineering Societies Library an oil portrait of Dr. Douglas which had his own approval and was presented by him. American Institute of Metals.--During the Spring of the year, plans were completed with the American Institute of Metals whereby this society became the Institute of Metals Division of the American Insti¬tute of Mining Engineers. This body was a dignified aggregation of metallurgists which had been in existence for about 11 years. A bronze tablet commemorating the American Institute of Metals is now being placed in the Members&apos; Room of the Institute, and during the year 1919 the Bulletin will bear the following title: "Bulletin of the American Institute of Mining Engineers, with which is consolidated the American Institute of Metals." Visits to Local Sections.-During the year President Jennings made visits to six of the Local Sections, on three of which occasions he was accompanied by the First Vice-president and the Secretary. First Vice-president Goodale made five visitations and the Secretary made eight.

Jan 1, 1923

By M. C. Flemings, R. Mehrabian, G. E. Nereo

Analytical expressions derived previously are used to describe quantitatively effects on macrosegregation of some solidification and mold design variables. Al-4.5 pct Cu alloy is used as example. It is shown that abrupt changes in heat transfer rate result in solute-rich or solute-poor "bands". Severe solute-rich bands accowzpany "reheating" that can result, for example, from abrupt formation of an air gap at a mold-metal interface. With planar isotherms, solute-poor regions also result from reduction in cross section through which fluid flow to feed shrinkage takes place. It is suggested that the negative "cone" of segregation often found at the base of large ingots results from this reduction in cross section for feeding. Consideration is given to the positive and negative segregation to be expected in laboratory ingots in association with changes in ingot cross section. Under-riser positive segregation is considered and it is concluded this segregation results when vertical temperature gradient is low in the region of the riser; the segregation is accentuated by the temperature gradient reversal which can occur in inadequately insulated risers ("&apos;hot tops"). Finally it is shown for Al-4.5 pct Cu alloy that the assumption of constant k and p in analytic solutions gives calculated results close to those obtained for the case of ziariable k and 0. A basic "local solute redistribution equation" was derived earlier&apos; for calculation of macrosegregation resulting from flow of solute-rich liquid to feed solidification shrinkage, thermal contraction, and/or other contractions occurring during solidification. This expression relates fraction liquid, g~, to liquid composition, CL, at a given position x, y, z, in a solidifying Eq. [I] is for the general case of three-dimensional heat and fluid flow assuming constant solid (but not necessarily liquid) density during solidification, negligible net solute change from diffusion, and no pore formation. In this paper we first demonstrate application of this equation for calculation of macrosegregation in several examples involving one-dimensional heat and fluid flow. Specifically considered are examples in which segregation results from sudden changes in heat flow conditions. Next, Eq. [I] is used to describe segregation in examples where isotherms remain planar but where fluid flow is no longer one-dimensional. Application of this expression illustrates the type of segregation to be expected in unidirectionally solidified ingots of gradually or abruptly varying cross section. For segregation calculations, A1-4.5 pct Cu alloy is employed with constant k and p Vz = 0.172, 4 = 0.055), eutectic composition (CE = 33 pct Cu). In all examples, fraction eutectic is neglected in velocity calculations; this was previously shown to introduce little error.&apos; A linear distribution of fraction liquid in the liquid-solid zone is assumed. In a concluding section it is shown that the assumption employed of constant k and /3 gives results close to those obtained when the actual (variable) values of k and 0 are employed.

Jan 1, 1969