Search Documents

By W. H. Class

The embrittling effects of oxygen, ozone, nitrogen, air, and surface residues, on NaCl has been investigated. The embrittlement by ozone and oxygen was found to be associated with the formation of a NaClO3 surface compound. In these cases the initial crack that was responsible for fracture (in a bend test) always nucleated at the corners between the tension and side faces. The behavior of air was very erratic and on certain days did not produce enzbrittlement. During these periods, crystals that had become embrittled by the ozone treatment completely recovered their ductility after a short exposure to the ambient atmosphere, It was established many years ago1 that considerable ductility could be obtained in NaCl single-crystal specimens if the crystal surfaces were dissolved in water either during or immediately prior to the test. The original interpretation of this effect by Joffe attributed the enhanced ductility to the removal of surface microcracks by dissolution. Later investigations2'3 have suggested that the exclusion of air from the specimen surface is the criterion for extensive plastic flow prior to fracture. The air em-brittlement in this later work was attributed to the diffusion of gaseous atoms into the surface layers of the crystal, thereby impeding the movement of dislocations. This model satisfactorily accounts for the reembrittlement observed after further air exposure subsequent to the water dissolution treatment. However, the situation has recently become more complex by the observations in several laboratories4-t that under certain conditions air exposure does not impair the ductility of NaC1. It has also been recognized5 that improper drying operations after water dissolution can leave surface precipitates that lead to embrittlement. Cleavage defects on as-cleaved crystals can often be another source of embrittlement. In the present work the effect of the gaseous atmospheres nitrogen, argon, air, oxygen, and ozone, on the ductility of rock salt was studied extensively. The embrittlement resulting from oxygen and ozone exposures was found to be associated with the formation of a NaC1O3 surface film. It is suggested that certain atmospheres, one of which often can be ambient air, which inhibit the formation or favor the decomposition of this compound, can promote ductility. Thus one aspect of the Joffe effect is certainly related to the removal of surface compounds or complexes by water dissolution. The effect of surface precipitates that remain after drying operations and of cleavage defects were also studied. In neither of the latter cases was the embrittlement as severe as that found with a NaClO3 surface layer. PROCEDURE AND SPECIMEN PREPARATION The nature of the embrittlement produced by the agents mentioned above was studied by means of microscopy, mechanical testing, and X-ray diffraction. Specimens were cleaved from large crystals of optical quality sodium chloride obtained from the Harshaw Chemical Co., and, except for those tested in the as-cleaved condition, were given a 15- to 20-sec immersion in distilled water followed by a rinse in absolute methyl alcohol. The specimens were then blotted on a soft, absorbent paper, and dried by a few seconds exposure to a stream of warm, dry air. Such a procedure was found to give a control surface which was microscopically free of residues. (A few crystals were intentionally painted with a concentrated NaCl solution in order to investigate the effect of surface residues). All specimens were of 0.140 sq in. cross-section. Crystals prepared in the above manner were immediately placed in a gas train where they could be exposed to the desired gases for preselected periods of time. For the oxygen and nitrogen exposures, pure reagent-grade gases were employed. The ozone was provided in the form of an ozone-oxygen mixture (approximately 10 pct ozone) prepared by passing commercial grade oxygen over a strong ultraviolet light source. All gases were dried prior to their introduction into the train. Since argon was found to be completely inert in its behavior (i.e., residue-free specimens that were exposed to argon were not embrittled), it was periodically utilized to check the control specimen surfaces as well as the condition of the gas train used for aging the specimens. After exposure to the gaseous media in question, the crystals to be used for the measurement of the strain to fracture were transferred from the gas train to a protective oil bath (without further exposure to the atmosphere) where the tests were conducted in three-point bending. The apparatus was so adjusted that the load could be applied at a constant, continuous rate. Other Snecimens from the gas train were deformed

Jan 1, 1962

By John L. Watson

A conceptual model (MAGSEP) is described to simulate the beneficiation characteristics of a drum magnetic separator in terms of the probability of an individual grain being recovered in the magnetic concentrate. This probability is determined as a function of particle magnetic composition and magnetic field strength and is modified by particle size and the separator operating conditions. The model predicts the size, magnetic grade and distributions of magnetic and gangue minerals in the concentrate and tailings produced by the drum separator. The configuration of the magnetic concentration circuit may be altered to permit single or double drum units in parallel or series operation. The characteristics of the feed material, in terms of a magnetic parameter, are essential in permitting the determination of individual grain recovery probabilities upon which the model is based. Thus the model requires input data relating to the distribution of composite grains in terms of magnetic grade and particle size. To illustrate the use of the conceptual model an example is given for the beneficiation of New Zealand iron sands.

Jan 1, 1984

By J. W. Hickman, E. A. Gulbransen

One of the important factors that determine the resistance of a metal or alloy to further chemical reaction is the structure of the superficial oxide film. A thorough understanding of the physical and chemical structure as well as the stability of the oxide film formed on the surface as a function of time and temperature of the chemical reaction might furnish clues as to the nature of the reaction process and the protective nature of the film. A comprehensive program has been undertaken to study these phenomena. This paper summarizes the structure of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper at temperatures up to 700°C. Before the introduction of the electron diffraction technique, it was necessary to use either direct chemical analyses or X-rav diffraction analyses to determine the nature of the oxide film formed on the metal or alloy. Chemical analyses yields information on the percentages of the several atomic species present in the film while X-ray diffraction analyses yield information on the atomic geometry. In special cases the information obtained may be identical, but in general both viewpoints are necessary. Much of the early work was carried out on the oxidation of bulk samples where thick films were obtained. The products were identified after cooling to room temperature by X-ray diffraction and chemical analyses. Although much useful information has been obtained in this manner. little could be learned about the character of the protective oxides during the period when the films were actually protective. Evidence concerning the chemical structure of thin oxide films has been made possible by the development of the electron diffraction reflection technique. In this method the most fruitful investigations have been made by carrying out the reaction in situ at the temperature at which the film is actually protective. Literature The oxidation of iron has been extensively investigated by X-ray and electron diffraction. Jackson and Quarrelll found that oxide films formed and examined at the same temperature differed considerably from those allowed to cool to room temperature. The results showed that below 400°C the oxide that was stable in intimate contact with iron was Fe³O4; between 515° and 900°C. the stable film was FeO. Above the upper change point of iron the oxide was found to be Fe³O4. From 400' to 515°C., FeO, Fe³O4 or a mixture of the two oxides was found. Recrystallization of the air-formed film below 400' and above 900°C. led to the formation of Fe3O4. In the range where thicker films consisted of FeO, the air-formed film was converted to a new hexagonal oxide not previously described.

Jan 1, 1947

By E. A. Gulbransen, J. W. Hickman

One of the important factors that determine the resistance of a metal or alloy to further chemical reaction is the structure of the superficial oxide film. A thorough understanding of the physical and chemical structure as well as the stability of the oxide film formed on the surface as a function of time and temperature of the chemical reaction might furnish clues as to the nature of the reaction process and the protective nature of the film. A comprehensive program has been undertaken to study these phenomena. This paper summarizes the structure of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper at temperatures up to 700°C. Before the introduction of the electron diffraction technique, it was necessary to use either direct chemical analyses or X-rav diffraction analyses to determine the nature of the oxide film formed on the metal or alloy. Chemical analyses yields information on the percentages of the several atomic species present in the film while X-ray diffraction analyses yield information on the atomic geometry. In special cases the information obtained may be identical, but in general both viewpoints are necessary. Much of the early work was carried out on the oxidation of bulk samples where thick films were obtained. The products were identified after cooling to room temperature by X-ray diffraction and chemical analyses. Although much useful information has been obtained in this manner. little could be learned about the character of the protective oxides during the period when the films were actually protective. Evidence concerning the chemical structure of thin oxide films has been made possible by the development of the electron diffraction reflection technique. In this method the most fruitful investigations have been made by carrying out the reaction in situ at the temperature at which the film is actually protective. Literature The oxidation of iron has been extensively investigated by X-ray and electron diffraction. Jackson and Quarrelll found that oxide films formed and examined at the same temperature differed considerably from those allowed to cool to room temperature. The results showed that below 400°C the oxide that was stable in intimate contact with iron was Fe³O4; between 515° and 900°C. the stable film was FeO. Above the upper change point of iron the oxide was found to be Fe³O4. From 400' to 515°C., FeO, Fe³O4 or a mixture of the two oxides was found. Recrystallization of the air-formed film below 400' and above 900°C. led to the formation of Fe3O4. In the range where thicker films consisted of FeO, the air-formed film was converted to a new hexagonal oxide not previously described.

Jan 1, 1947

By D. F. Kaufman, E. D. Levine, L. R. Aronin

The deformation of' impure beryllium crystals by basal glide at room temperature invariably tevminates by basal cleavage after a few percent strain. It is generally accepted that .fracture of this type is caused by the splitting of low) -angle boundaries, or bend planes, by obstacles that restrict the motion of the bed planes in the deforming crystal. The details of such a process have been developed by Stroh, who showed that the high tensile stress norrnal to the basal plane in the region where the bend plane is split results in the propagation of a basal cleavage crack, provided there is no available dejorvrlatzon mode having a shear component normal to the basal plane It has been postulated that puvification of beryllium might lead to increased basal ductility by the vemoval of barviers to bend plane motion and possibly by the activation of nonbasal defor~rlation systems. Large increases in the amount of basal glide that can he sustained prior to fracture have been observed in crystals purified by zone refining. In each case, eventudal fracture was by sharp basal cleavage, suggesting that the split bend plane model still applies to tile fracture of beryllium of rensonably high purity. In the present work, calculations are made to show to what extent basal duetilits can be increased by purification while the split bend plane .fracture process remains applicable. Experimentally observed ductilities are generally somewhat lower than those predicted by calculation because of premature failure due to defects introd~cced during specimen preparation and testing. SEVERAL investigators1-4 have studied the deformation characteristics of beryllium single crystals of commercial purity, and have related the strong anisotropy of plastic deformation in single crystals to the problem of brittleness in polycrystalline beryllium. For most orientations, the principal deformation mode is basal slip, which, at temperatures between 300" and 900°K, begins at a critical resolved shear stress of approximately 1500 g per sq mm and terminates after 3 to 6 pet glide strain by cleavage on the basal plane in the neighborhood of (1120) bend planes that are formed during the deformation. This type of fracture, which is also observed in zinc at low temperatures, has been interpreted by stroh5 to be caused by the splitting of bend planes by obstacles to their motion. In the Stroh model, a (11.20) dislocation wall, or bend plane, moving along the slip direction under the action of the applied stress, encounters obstacles which cause part of the bend plane to be held up, the other part continuing to move. Stress concentrations are built up in the region where the bend plane is split, with a high tensile component normal to the basal plane, resulting in a microcrack at the end of the split wall. Because no deformation mode having a shear component at an angle to the basal plane is available to relieve the stress at the crack tip, the crack can propagate under a sufficiently high applied stress. The Stroh criterion for crack propagation is given by

Jan 1, 1964

By John J. Secretary Egan

The present list of problems relating to the physical chemistry of steelmaking has been prepared by the Committee on the Physical Chemistry of Steelmaking, from answers to a questionnaire submitted to a number of metallurgists engaged in both industrial and educational work throughout the United States. The purpose of the project is to make available to research laboratories a list of problems, all reduced to their simplest terms, the solution of which would aid in creating a better understanding of the steelmaking process. It is not intended to restrict the problems to practical steelmaking. The list also includes the study of the properties, and their correlation, as well as the physical and chemical reactions, of all substances that occur or that may be in any way associated with steelmaking operations, such as metallic substances, refractories, nonmetallic inclusions, and the constituents of slags. Many of the problems can be carried out in university or other research laboratories. Others may be most successfully attacked by cooperation of the research men with the operating personnel. It is the Committee's earnest wish that this cooperation be fostered. It is requested that investigators who are working on any of the problems listed and who anticipate future publication of their results, notify the Secretary of the Committee that such investigation is in progress. Suggested additions to the present list are also requested. The Committee is undertaking to act as a clearing house for information regarding the topics in this field that are being actually studied. Interested persons are invited to correspond with the Secretary. I. Data involved in the state of equilibrium for the various systems (laboratory work, almost entirely). A. Specific heats, heats of formation, entropies and free energies of various PURE ELEMENTS OR COMPOUNDS; ALSO CERTAIN TYPICAL SLAGS AND REFRACTORIES I. Determination of specific heats and entropies of oxides, sulphides, nitrides, etc, over a wide temperature range. 2. Determination of free energies of oxides, sulphides, nitrides, etc., over a wide temperature range. 3. Determination of the heats of formation of the oxides, sulphides, nitrides, etc. 4. Determination of the thermodynamic properties of the more important mineral-ogical constituents of the basic open-hearth slags such as calcium silicates, calcium phosphates, calcium ferrites, manganese silicates, FeO and Fe2O3. 5. Determination of the specific heats of open-hearth slags, including liquid silicates, if possible.

Jan 1, 1941

By John J. Secretary Egan

The present list of problems relating to the physical chemistry of steelmaking has been prepared by the Committee on the Physical Chemistry of Steelmaking, from answers to a questionnaire submitted to a number of metallurgists engaged in both industrial and educational work throughout the United States. The purpose of the project is to make available to research laboratories a list of problems, all reduced to their simplest terms, the solution of which would aid in creating a better understanding of the steelmaking process. It is not intended to restrict the problems to practical steelmaking. The list also includes the study of the properties, and their correlation, as well as the physical and chemical reactions, of all substances that occur or that may be in any way associated with steelmaking operations, such as metallic substances, refractories, nonmetallic inclusions, and the constituents of slags. Many of the problems can be carried out in university or other research laboratories. Others may be most successfully attacked by cooperation of the research men with the operating personnel. It is the Committee's earnest wish that this cooperation be fostered. It is requested that investigators who are working on any of the problems listed and who anticipate future publication of their results, notify the Secretary of the Committee that such investigation is in progress. Suggested additions to the present list are also requested. The Committee is undertaking to act as a clearing house for information regarding the topics in this field that are being actually studied. Interested persons are invited to correspond with the Secretary. I. Data involved in the state of equilibrium for the various systems (laboratory work, almost entirely). A. Specific heats, heats of formation, entropies and free energies of various PURE ELEMENTS OR COMPOUNDS; ALSO CERTAIN TYPICAL SLAGS AND REFRACTORIES I. Determination of specific heats and entropies of oxides, sulphides, nitrides, etc, over a wide temperature range. 2. Determination of free energies of oxides, sulphides, nitrides, etc., over a wide temperature range. 3. Determination of the heats of formation of the oxides, sulphides, nitrides, etc. 4. Determination of the thermodynamic properties of the more important mineral-ogical constituents of the basic open-hearth slags such as calcium silicates, calcium phosphates, calcium ferrites, manganese silicates, FeO and Fe2O3. 5. Determination of the specific heats of open-hearth slags, including liquid silicates, if possible.

Jan 1, 1941

INCREASING realization that pouring and ingot-mold practices involve many factors of fundamental importance to ingot quality and general steel-mill operations has caused these phases of steelmaking to become major concerns of operators and metallurgists engaged in control of quality and costs. Methods of pouring steel from the ladle into the ingot molds have some direct effects on ingot quality. The mold itself governs solidification and dimensions of the ingot and in so doing exerts some very tangible influences not only on ingot quality but also on product yields and general steel-mill processing. In addition, practices are employed in the handling of molds during daily open-hearth operations that are important to quality and production costs. Therefore, pouring and mold practices must be considered highly specialized and important steps in steel-mill operations. MOLD DESIGN Mold design is difficult to discuss in a precise manner because it varies greatly throughout the industry, both in theoretical concepts and practical application, and few well developed data are available. Most ingot molds are designed to meet conditions peculiar to a given plant wherein quality standards are dictated by end-use requirements, which may differ considerably even for the same grade of steel. The mold designer must also consider the equipment available to process ingots and the product obtained from them. Such equipment, used for stripping, heating, blooming and finishing operations, is seldom, if ever, exactly the same in any two steel plants. Thus, pronounced contrasts in mold designs can be expected to continue, even among plants making strictly comparable types of product, particularly because some producers are just beginning to realize the benefits possible from specialized designs. Certain fundamentals are used in mold design but even these

Jan 1, 1964

By Frank H. Macpherson

Few people realize the tremendously important part that Saline and Pulaski Counties in central Arkansas have played in the winning of the war The present favorable war situation might have been very different if we had not had the bauxite produced during the past two years from these two small areas, a total Of about 15 square miles. As a general statement, it can be said that the Arkansas bauxite deposits are, individually, relatively small, irregular in thickness, somewhat scattered and, therefore, compared with coal or iron-ore or open-pit copper deposits, relatively ill adapted to a rapid and drastic expansion in output. A few years ago it would have seemed an impossibility for these two counties to produce over six million long dry tons of bauxite in one year. However, with the cooperation of the operators, that is what happened in 1943, when the state of Arkansas achieved the seemingly impossible with a production of 6,020,684 1 long tons (dried equivalent) of bauxite ore during the calendar year, compared with an average annual production of 323,7252 tons in the period 1931 to 1941. It became apparent early in the year '94' that the united States soon might be drawn into the war, and, therefore, that an immediate study of the domestic metal situation was necessary. Aluminum is by far the most important metal used in the manufacture of aircraft and many other implements of war and it was evident that there would have to be a tremendous increase in the domestic production of bauxite, which is practically the only present source of this metal. AS more than 95 per cent of the known bauxite reserves of the United states was in Arkansas, careful preliminary studies were made in that state by representatives of the united States Bureau of Mines, the United States Geological survey and the War Production Board in the summer of 1941 Reserves in other states also were studied. The result of these studies was a recommendation by the War Production Board that mining in the bauxite.producing areas of Arkansas be geared for maximum production, in order to supply sufficient ore for this country's war requirements and, if necessary, to supply the war needs of Canada as well. The annual goal of eight million long tons (dry weight) set for Arkansas by the war Production Board was exceeded in 1943, when in August the output reached a rate equivalent to more than 8,300,000 long tons, dry basis. Because of the comparatively small tonnage of bauxite reserves, Congress appropriated funds for an extensive drilling program to be carried out by the Bureau of Mines in cooperation with the Geological Survey. Drilling began in May 1942 but owing to delay in delivery of drills, and trucks upon which the drills were mounted the program did not get into peak operation until early in 1943. By the end of July 1944, the Bureau of Mines records indicated an addition to the Arkansas reserves of 10,000,000 long tons (wet basis) in place,

Jan 1, 1946

By M. E. Wadsworth, G. W. Warren

INTRODUCTION Hydrometallurgical processes for the extraction of metal values can be divided into two broad categories: (a) Processes involving the treatment of high grade material (e.g. finely divided mineral concentrates); and (b) processes which treat lower grade material (ores, waste dumps, etc.). This discussion will be directed primarily toward the first category, but in either case a fundamental knowledge of the intrinsic kinetics and thermodynamics is necessary to understand the behavior of the system. The bulk of research efforts in the last decade along these lines has been aimed at the recovery of copper (1-8). However much information has also been reported on uranium (9, 10) , zinc (11) , cobalt and nickel (12, 13). More comprehensive reviews on these areas are also available (14). As discussed by Sepulveda and Herbst (15, 16) one of the most difficult problems facing process designers is the acquisition and scale-up of reliable information concerning the intrinsic kinetics of leaching systems. The scale-up or modeling of these multiparticle systems is far more complex than that of homogeneous ones. This is due to the numerous rate determining steps which are possible with heterogeneous reactions and the broad distribution of properties of a multiparticle feed such as particle size and mineralogical composition (16). In addition, other factors must also be considered such as interactions between particles, the anisotropic nature of individual particles, the effect of solution chemistry, and electrochemical phenomena. All of these factors must be taken into account, often simultaneously. The thrust of this paper will be to more closely examine how the factors mentioned above can be treated. Some elementary examples of

Jan 1, 1980

By J. D. Hunt, R. J. McDonald

It is proposed that extensive fluid motion occurs between the dendrites of a Partially solid casting and it is suggested the A segregates in steel castings are a direct result of this motion. The fluid flow arises because of density differences between liquid ahead of the dendrites and the interdendritic liquid. Experiments are described on a model system investigating this fluid motion. The importance of interdendritic fluid flow is discussed with reference to longitudinal segregation. SERIOUS macro segregation is often found in large killed steel ingots. Among the most common segregates are those known as A and V, Fig. 1. The A segregates are arranged over the surface of cones, the wide parts being at the base of the ingot. The A segregates are pencil like in shape and extend from the columnar into the equiaxed region. The V segregates are distributed over inverted cones but have a less well defined shape. They occur at the center of the ingot. Because of the commercial importance of macro inhomogenities these segregates have attracted wide-scale attention. The segregates contain alloying elements and impurities which depress the freezing temperature and are thus the last liquid to freeze. A number of explanations have been proposed to explain their presence. It has been suggested1'' that the segregates are the result of the equiaxed zone growing towards the columnar region together with the interaction of convection within the bulk liquid. It has also been proposed that the segregates are the result of nucleation and rapid growth ahead of the dendritic front.3 Neither of these explanations is completely satisfactory because A segregates are pencil shaped and are not found as continuous cones. In this paper an alternative mechanism is proposed, and experiments are described on a model system to determine whether the mechanism occurs in practice. It is thought that A and V segregates are not peculiar to steels but should occur in many other large castings. Fluid motion within the bulk liquid region of a casting has been extensively discussed. Little attention has been paid to fluid motion within the partially solid regions. The work415 that has been done has been mainly concerned with the fluid motion which results from the volume contraction on freezing. The volume contraction is used to explain various types of macro segregation. The present authors suggest that in many cases the fluid flow resulting from volume contraction will be small compared with that due to other causes. When the columnar region is growing, the liquid still remaining between the dendrites has a much lower temperature near the ingot walls than at the dendrite tips. The composition of the liquid in contact with solid will vary with temperature. The density of the liquid will thus vary both because of changes in temperature and composition. The layers of different density liquid will give rise to a slow but steady liquid flow through the interdendritic regions. If there is no density change with composition, the temperature gradient within the dendritic region should give rise to a downward flow between the dendrites, shown schematically in Fig. 2. When the liquid density changes appreciably with alloy concentration this motion could either be en-

Jan 1, 1970

Abel, Charles Edwin, Student, Univ. of California Los Angeles, Cal. '31 Adams, Horace M.5148 Benton Ave., Downers Grove, Ill. '31 Ahlskog, Harold A., Student, Washington State College Pullman, Wash. '30 Aldridge, John, Student, New Mexico School of Mines Sbcorro,, N. M. '30 Allen, Hugo K., The Univ. of Texas 104 W. 33rd St., Austin, Tex. '31 Ames, Marshall B., Student, Washington State College Pullman, Wash. '31 Ancell, Virgil F., Student,. Missouri School of Mines Rolla, Mo. '30 Anderson, Norman John, Student, South Dakota School of Mines Rapid City, S. D. '32 Annett, Norman T., Student, Mackay School of Mines, Univ. of Nevad Reno, Nev. '32 Apablasa, Salvador C., Student, Univ. of California Los Angeles, Cal. '31 Armstrong, James Arthur, Jr., Student, Michigan College of Min. & Tech., Houghton, Mich. '31 Armstrong, John R. Box 274, Neosho, Mo. '31 Armstrong, Robert H., Student, Lafayette College Easton, Pa. '31 Armstrong, Thomas E., Student, Univ. of California Los Angeles, Cal. '31 Arnot,. Paul H 2617 Haste St., Berkeley, Cal. '31 Ashby: Harve I., Willow Creek Mines Wasilla, Alaska. '31 Aud, Robert A., Student, Lafayette College Easton, Pa. '30 Augenthaler, Robert L., Student, New Mexico School of Mines Socorro, N. M. '32 Augustine, Grant, Jr., Instrument man, Min. Dept., Fairbanks Exploration Co., Fairbanks, Alaska. '31

Jan 1, 1932

By John E. Greenawalt

In view of the increasing importance of sintering in the beneficiation of iron ores preparatory to their reduction in the blast furnace, the writer believes the time is opportune for an up-to-date, though brief, discussion of the general principles of sintering, as well as a discussion of some of the recent improvements and mechanical developments that have been achieved in this industry, its present trend and future possibilities. Sintering may be defined as the agglomeration of fine mineral particles into a porous mass by incipient fusion caused by heat produced by combustion within the mass itself. Its first successful application, in connection with the treatment of lead sulphide ores, was known as blast roasting. In this process the lead ore was given a preliminary roasting in a reverber-atory furnace, then the incandescent mass was placed in a pot with a grate and an updraft was applied. It was soon discovered that much better results were obtained by cooling the ore, moistening it, and placing it upon an incandescent layer of fuel previously placed upon a grate, and then applying the updraft blast of air until the charge was converted into a more or less agglomerated mass. The fuel was sulphur and the process one of desulphurization, which was the principal result desired. The application of downdraft to blast roasting brought about tremendous results; the principal one of which was that an air blast of high pressure could be passed through a layer of ore deposited on a grate, or on a grate covered by a layer of coarse porous material, without disturbing the particles of which the layer is composed. The air current is compelled to filter through the pores of the charge, whereas if the same pressure applied to the top surface of the charge with downdraft were applied to the bottom of the charge with updraft, the charge would be completely blow11 off the grate. Another result of reversing the draft was that a flame could readily be applied to the top surface of the charge for igniting purposes. Broadly speaking, sintering is an oxidizing or burning process, therefore the volume of air passing through the charge is the all-important factor. The air must pass through with sufficient rapidity to produce the necessary heat, and if sufficiently rapid the combustiorl will take place

Jan 1, 1938

By John E. Greenawalt

In view of the increasing importance of sintering in the beneficiation of iron ores preparatory to their reduction in the blast furnace, the writer believes the time is opportune for an up-to-date, though brief, discussion of the general principles of sintering, as well as a discussion of some of the recent improvements and mechanical developments that have been achieved in this industry, its present trend and future possibilities. Sintering may be defined as the agglomeration of fine mineral particles into a porous mass by incipient fusion caused by heat produced by combustion within the mass itself. Its first successful application, in connection with the treatment of lead sulphide ores, was known as blast roasting. In this process the lead ore was given a preliminary roasting in a reverber-atory furnace, then the incandescent mass was placed in a pot with a grate and an updraft was applied. It was soon discovered that much better results were obtained by cooling the ore, moistening it, and placing it upon an incandescent layer of fuel previously placed upon a grate, and then applying the updraft blast of air until the charge was converted into a more or less agglomerated mass. The fuel was sulphur and the process one of desulphurization, which was the principal result desired. The application of downdraft to blast roasting brought about tremendous results; the principal one of which was that an air blast of high pressure could be passed through a layer of ore deposited on a grate, or on a grate covered by a layer of coarse porous material, without disturbing the particles of which the layer is composed. The air current is compelled to filter through the pores of the charge, whereas if the same pressure applied to the top surface of the charge with downdraft were applied to the bottom of the charge with updraft, the charge would be completely blow11 off the grate. Another result of reversing the draft was that a flame could readily be applied to the top surface of the charge for igniting purposes. Broadly speaking, sintering is an oxidizing or burning process, therefore the volume of air passing through the charge is the all-important factor. The air must pass through with sufficient rapidity to produce the necessary heat, and if sufficiently rapid the combustiorl will take place

Jan 1, 1938

By William P. Blake

This camp is just now startled by the alarming suggestion that unless there shall speedily be an appreciation in the value of silver, and a decrease in the cost of salt, it will be prudent business policy to close the Alice mines and mills until the conditions of production are more favorable. Such an event would be a great blow to the prosperity of Butte. It would throw some hundreds of men out of employment, and it might lead to the adoption of the same policy by other companies, which, like the Alice, have not been able to pay dividends to their shareholders for a long time. The question arises, and becomes emphatic: If, under the present adverse conditions, the mines and mills cannot be made to pay a proper profit, why should they continue to be worked ? The owners mentally ask: Shall we go on exhausting our mines, pouring out a stream of silver for the maintenance of the community, and the support of the rail ways, or shall we husband our reserves, withdraw the miners from our slopes, and wait for more favorable conditions ? This is the impending question, and all concerned dread to meet and answer it. Let us briefly review the situation and forecast, if possible, what the solution of' the problem will be. It must be understood that the discussion does not include, or refer to, the immense copper-producing interests of the camp, which may or may not be upon a very much more satisfactory basis. It will be confined chiefly to the operations of the Alice company, sta tistics of which are at hand, without involving the other silver com panies in the conclusions beyond those inevitable from well-known facts, patent to all. There are at present in Butte and in its vicinity in the principal mills an aggregate of 290 stamps dropping upon silver-ores: Alice,...........80 stamps. Moulton,. .........40 " Lexington,...50 " Silver Bow,.........30 " Blue Bird,..........90 " The Alice mills at present, with their 80 stamps, devour, in round numbers, from 100 to 120 tons a day. The actual amount

Jan 1, 1888

By F. E. Bash

About three years ago, the writer presented a paper1 on the rate of heating and cooling of a 24-in. round ingot. The present paper deals with work done on larger ingots at the plant of the Allis Chalmers Mfg. Co., Milwaukee, Wis., in August, 1919. Sufficient data on ingots of all sizes were desired to enable one to calculate in advance the rate at which any ingot could be raised to a forging temperature without injury to the steel, determining also the temperature gradient between different sections of the ingot and the length of time necessary to heat to the center. This has now been experimentally determined for 24-in. and 45-in. ignots by the writer and for a 18-in. cube by E. F. Law.2 J. F. Harper has also made tests on heat-treating temperatures on 30-in, ingots; which data are included in this paper. No attempt is made here to work out a formula for the heat penetration of steel, for too many factors are involved concerning which we have not sufficient information, as for instance, the specific heat of steel up to 2300' F. It is hoped that eventually a set of formulas will be developed so that one may calculate maximum allowable temperature differences within an ingot for any particular kind of steel and the rate of absorption of heat and temperature gradient within the ingot for a definite temperature head. EXPEEIMENTAL INGOT The ingot tested was 45 in. in diameter, having been forged into the shape shown in Fig. 1 from 54 in. diameter. Seven -in. holes were

Jan 1, 1923

By F. E. Bash

About three years ago, the writer presented a paper1 on the rate of heating and cooling of a 24-in. round ingot. The present paper deals with work done on larger ingots at the plant of the Allis Chalmers Mfg. Co., Milwaukee, Wis., in August, 1919. Sufficient data on ingots of all sizes were desired to enable one to calculate in advance the rate at which any ingot could be raised to a forging temperature without injury to the steel, determining also the temperature gradient between different sections of the ingot and the length of time necessary to heat to the center. This has now been experimentally determined for 24-in. and 45-in. ignots by the writer and for a 18-in. cube by E. F. Law.2 J. F. Harper has also made tests on heat-treating temperatures on 30-in, ingots; which data are included in this paper. No attempt is made here to work out a formula for the heat penetration of steel, for too many factors are involved concerning which we have not sufficient information, as for instance, the specific heat of steel up to 2300' F. It is hoped that eventually a set of formulas will be developed so that one may calculate maximum allowable temperature differences within an ingot for any particular kind of steel and the rate of absorption of heat and temperature gradient within the ingot for a definite temperature head. EXPEEIMENTAL INGOT The ingot tested was 45 in. in diameter, having been forged into the shape shown in Fig. 1 from 54 in. diameter. Seven -in. holes were

Jan 1, 1923

By O. G. Lellep

IN every country economic circumstances prescribe the method used to produce a commodity at lowest cost. In Pennsylvania a man's wages for working 4 hr buys a ton of coal wholesale; in Germany a laborer must work 40 hr, or ten times as long. In western Europe, therefore, conservation of fuel is of primary importance, and recent practices of burning lime and cement differ from those employed in the United States. This paper presents data collected during a trip through western Europe in 1953. Considered uneconomical, shaft kilns for burning cement disappeared in the United States two generations ago. But because required capital investment is low and operation greatly improved, shaft kilns are still used to some extent in Europe, where fuel costs are high, and are even included in designs for plants under construction. During the last 50 years shaft kilns have been maintained at the same physical size, while their output has been increased at least four times.

Jan 7, 1954

By Edward Keller

About a dozen years ago the art of bessemerizing copper- * matte, brought to these shores from France, was first established at the smelter, in Butte, Montana, of the Parrot Silver and Copper Company, which had bought the process from Mr. Manhks, the inventor. Through the efforts of Mr. J. E. Gaylord, general manager, and Mr. A. J. Schumacher, snperintendent,, assisted by an able staff, the new method rapidly underwent, at the Parrot establishment, an evolution towards higher perfedion, and within a few years its success and its advantages were so marked that all the great works in the west followed in the footsteps of this pioneer. The converter-process has now practically superseded the reverberatory-process in this country. The latter will undoubtedly, in a not very distant future, be relegated to metallurgical history. The writer has availed himself of what was perhaps the last chance to make comparisons of the two methods, working practically on the same material on an extensive scale, the reverberatory process being that of the Baltimore Copper Smelting and Rolling Company,* while the converter-process is that of the Anaconda Copper Company—both using the matte from the latter company's works in Anaconda, Montana. For the greater portion of the material considered in this paper, the writer is indebted to the two companies. In order to understand the difference of behavior of the several elements, and the difference of the copper produced in the two processes, it is best to study and follow those elements

Jan 1, 1899

By Herbert H. Kellogg

IN 1930, Taggart, Taylor and Knoll1found that addition of various electrolytes to suspensions of ground minerals resulted in the stopping or starting of Brownian movement of the suspended particles. On the basis of the many new facts found, they rejected the "classical "[t] theory of Brownian movement and proposed an "ionization" theory. This new theory was further supported in later publications by Taggart.3,4 The acceptance of the ionization theory by men in the field of flotation may be judged by the mention given this theory in Gaudin's "Principles of Mineral Dressing,"5 Wark's "Principles of Flotation,"6 as well as in a recent paper by Fitt, Thomas and Taggart.7 The proponents of the ionization theory have gone further than the mere statement of the new theory. A parallelism between the Brownian movement of mineral particles and their behavior in flotation was reported.1,3,4 Likewise, the correlation between flocculation-dispersion of mineral particles and the Brownian movement of these particles has been investigated.7 Bankoff15 has suggested that "slime-coating" can also be directly correlated with the Brownian movement of the slime particles. In each of the instances mentioned it is the ionization theory of Brownian movement that has been used to "explain" the correlations that were found. The essential conflict between the kinetic theory and the ionization theory can be understood best by a brief description of each. The kinetic theory* proposes that Brownian movement is caused by the impacts of liquid molecules against the solid particles. At any instant of time, the molecular impacts on all sides of the solid particle will not balance, and the particle will receive a push in some direction. According to this theory, all particles suspended in a liquid are in Brownian movement. However, if the particle is very large, the impacts on all sides will very nearly balance and the motion will not be noticeable. Another factor, besides the size of the particle, that affects the magnitude of the Brownian movement is the viscosity of the liquid-the greater the viscosity, the less the displacement of particles by Brownian movement. This theory has been verified experimentally by measurement of the velocity of Brownian movement, and by measurement of the compacting of suspensoid particles under the influence of gravity.2 The originators of the ionization theory found that the addition of various electrolytes to slime pulps caused cessation or commencement of Brownian movement, depending upon the chemical nature of the particle and the electrolyte. The Brownian movement of quartz particles was observed to stop upon the addition of certain electrolytes, where the conditions of the experiment prevented flocculation

Jan 1, 1945