By Maurice Cook

A procedure of obtaining specimens of lead, tin, and cadmium with a moderately equiaxed structure and a smooth surface suitable for etching without grinding and polishing is described; the advantages of general oblique illumination (as opposed to vertical illumination) in the photomicrography of pure metals .are stated. Using these methods, a statistical study of the changes brought about in deformed lead, on annealing, has been made. The common mode of structural change was found to be recrystallization. Cases of growth of one original grain into another were rare; but if a totally recrystallized specimen was annealed above 200° C., a few large grains appeared and spread over the whole area, except for a certain number of small grains which remain unabsorbed. The temperature needed to produce structural change in lead was found to be lower, the greater the degree of deformation. With tin, an extension of 28 per cent. caused practically no recrystallization at ordinary temperatures, but recrystallization occurred if the specimen was heated to 100° C. In cadmium at low temperatures, the grain size decreased in marked manner as the deformation increased; but at high annealing temperatures, the grain size was comparatively independent of the degree of deformation. THE structural changes in metals brought about by annealing following a deformation at a low temperature has been the subject of many investigations. No less than eleven metals and alloys have been studied in some detail; namely, aluminum,1 tungsten,2 iron,3 copper,4 gold,5

Jan 11, 1924

By P. A. Fisher, J. B. Wilson, D. J. Whitehead, C. J. P. Ball, A. C. Jessup

The properties of a new magnesium alloy ZT1 containing 3.0 pct Th, 2.5 pct Zn, 0.7 pct Zr are described. The alloy possesses good creep and fatigue resistance up to 650°F, is free from microporosity, and is readily sand-cast. ZT1 is shown to be superior to zinc-free Mg-Th-Zr alloys. THE advent of the jet engine created a demand for a light sand-casting alloy capable of being cast into large complex shapes and capable of resisting creep at temperatures up to 500°F. This demand has been largely met by alloys of the magnesium-cerium mischmetal-zirconium types, containing about 3 pct Ce mischmetal and 0.7 pct Zr, typified by Elektron magnesium alloys MCZ and ZREI, the latter alloy also having a zinc addition of 2.5 pct. These alloys utilize the valuable properties at elevated temperatures conferred by the addition of rare earth metals to magnesium, a fact which has been known for many years and discussed by several investigators.1-1 Murphy and Payne8 showed that the addition of the powerful grain-refining element zirconium to Mg-Ce mischmetal alloys produced alloys with attractive room temperature properties combined with good creep properties and castability. With the increasing power of modern jet engines the temperatures to which some of the magnesium parts are subject are likely to exceed the safe working range of the cerium-mischmetal-containing alloys, and at the beginning of the research considerable interest had been shown by aeroplane engine designers in a magnesium sand-casting alloy suitable for service at higher temperatures, e.g., 600°F and above. At an early stage in the development of this type of alloy a check on the fatigue properties at elevated temperatures indicated that, since the fatigue limit even at 108 eversals was appreciably higher than any permissible creep stress, the main emphasis of the research could be concentrated on creep behavior. The primary aim in developing the new alloy has therefore been to attain maximum creep resistance; but due consideration has also been given to other important properties such as castability, tensile strength, and cost. It is by now well established that it is not possible to correlate creep strength with other short time mechanical properties such as are obtained in tensile

Jan 1, 1954

By Franklyn W. Oatman

In order that the conditions which obtain in an oil well may be readily understood, a brief description of a typical California well and a number of the phenomena accompanying same will be given. That the necessity for the exclusion of water be realized, the effects of water intrusion, a description of methods of prevention, .and a discussion of causes of failure will be presented, followed by a summary and recommendations. Fig. 1 shows a section of a typical well which illustrates the relation of oil sands to overlying strata. It indicates a deep water sand separated from the oil sand by shale, and the proper place for the final shutting off of water. In this well a comparatively thick stratum of compact shale protected the oil from overlying water so that the operation of landing the water string was a simple matter. In some wells the protecting stratum may be only from 3 to 5 ft. thick and very careful operation is necessary in order to land the water string of casing properly and not puncture through to the oil sand. The cases just cited are common, but occasionally, after excluding overlying water, productive oil sands are drilled through in the expectation of finding more productive underlying sand, and a water-bearing stratum is tapped. In this case the problem is the reverse of the normal; water must be prevented from ascending rather than descending. A discussion of well-drilling methods is not within the scope of this paper, except such operations as pertain to shutting off of water. A brief outline of the several conditions which may accompany drilling follows. Some or all may be present in any particular case. The direct relation of these to prevention of intrusion will be discussed in detail further on. In drilling, the hole becomes more or less irregular in shape, and rough, and as the casing follows the bit into the well it does not fit snugly against the walls. As a result, water may descend between the casing and walls of the well. If a circulation pump is not used during drilling, the hole is simply punched through and the pulverized material removed from the well by means of a bailer. If circulation is maintained there is a continual flow of water down inside the casing and up around the outside between the pipe and the walls of hole. This keeps an open space around the pipe.

Jan 1, 1915

By R. F. Mehl, M. Gensamer

Although a large number of X-ray photograms of cold-rolled steel have been published, two circumstances have led to the experimental work reported in this paper. The first is that no complete study, making use of the pole-figure method of Weverl, has been made of cold-rolled low-carbon steel. Wever has published pole figures of mild steel subjected to plane parallel deformation1, 2 and undoubtedly he has applied the method to cold-rolled mild steel, but the authors have not found these data published. Kurdjumow and Sachs3 have applied the method to the study of rolling and recrystallization textures in electrolytic iron; their results will be referred to later. The reason for this dearth of papers using the pole-figure method is obvious; a greater number of photograms and more analytical work (although this work is quite simple and straightforward) are required to construct a pole figure than most investigators have felt worth while, despite the fact that no other method of which the authors are aware will satisfactorily depict the orientations of the crystallites in a polycrystalline aggregate. The second circumstance that led to the work reported in this paper was the appearance of a paper by Wayne A. Sisson4 on the same subject. In his valuable study of the factors influencing the development of preferred orientations in cold-rolled mild steel, Sisson made one observation that required confirmation; that is, that at some stage of the rolling process the type of preferred orientation changed from the type that gives a photogram characterized as a "six-point" X-ray pattern to that known as a "four-point" pattern. A similar observation had been made by Tam-mann and Heinzel5, who studied the orientations developed in the rolling of steel by the specular reflection of light from the etched surface of rolled samples. These workers also found that the type of preferred orientation changed during the rolling process. The authors had some difficulty in seeing how this behavior could be consistent with modern views on the genesis of preferred orientations, particularly with those of Wever2

Jan 1, 1936

By R. F. Mehl, M. Gensamer

Although a large number of X-ray photograms of cold-rolled steel have been published, two circumstances have led to the experimental work reported in this paper. The first is that no complete study, making use of the pole-figure method of Weverl, has been made of cold-rolled low-carbon steel. Wever has published pole figures of mild steel subjected to plane parallel deformation1, 2 and undoubtedly he has applied the method to cold-rolled mild steel, but the authors have not found these data published. Kurdjumow and Sachs3 have applied the method to the study of rolling and recrystallization textures in electrolytic iron; their results will be referred to later. The reason for this dearth of papers using the pole-figure method is obvious; a greater number of photograms and more analytical work (although this work is quite simple and straightforward) are required to construct a pole figure than most investigators have felt worth while, despite the fact that no other method of which the authors are aware will satisfactorily depict the orientations of the crystallites in a polycrystalline aggregate. The second circumstance that led to the work reported in this paper was the appearance of a paper by Wayne A. Sisson4 on the same subject. In his valuable study of the factors influencing the development of preferred orientations in cold-rolled mild steel, Sisson made one observation that required confirmation; that is, that at some stage of the rolling process the type of preferred orientation changed from the type that gives a photogram characterized as a "six-point" X-ray pattern to that known as a "four-point" pattern. A similar observation had been made by Tam-mann and Heinzel5, who studied the orientations developed in the rolling of steel by the specular reflection of light from the etched surface of rolled samples. These workers also found that the type of preferred orientation changed during the rolling process. The authors had some difficulty in seeing how this behavior could be consistent with modern views on the genesis of preferred orientations, particularly with those of Wever2

Jan 1, 1936

By E. F. Miller

The subject " Safe Timbering of Working Places in Mobile Loading" is one that requires an analytical study of the strata both above and below the coal seam as well as the characteristics of the coal seam itself. The projection or mining plan must be based on economic roof control in which the application of timber can be minimized without incurring cost increases in other phases of production. The several types of loading machines in common use today are not adaptable to the same projections or timbering systems. Consequently the type of equipment to be used must also be considered. For these reasons the writer does not believe that the problems of timbering in working places can be discussed without simultaneously considering economic production as well as the safety of men and the conservation of equipment. Prior to the introduction of loading machines as a substitute for the pick and shovel system of loading coal, the care and maintenance of the individual working places were generally the responsibility of the coal loaders who worked in them. Up to that time very few coal companies had developed and applied fixed and definite standards for timbering the working places in the mines they operated. It is common knowledge that mechanical loading of coal has had several false starts in the last twenty-five years and it is only in the last decade that it has developed to the stage at which we now find it. During this twenty-five year period the management of the more responsible companies have come to realize the tremendous importance of roof control in coal mining. From a safety viewpoint, the lack of roof control has been and still is responsible for more than a third of the industry's annual fatality experience. In recent years workmen's compensation and insurance rates have steadily increased while the profit margin has decreased almost to the point of elimination. From an economic operating viewpoint, the failure to properly control roof is quite often the most costly single phase of coal mining. Since the manufacturers of loading machine equipment have so improved their machines that normal care and maintenance can reduce to a minimum the time lost because of mechanical failure the production delays from other causes have assumed a far greater importance. Roof control in the broad sense and in the light of concentrated mining plans or projections that are adapted to mobile loading should be regarded as one of the major problems in the inseparable phases of production and safety of the workman and equipment at the working face. The subject of this paper cannot be treated properly unless what is said here is based upon the broad and fundamental problem of genera' roof control. The suc-cessful solution of a problem arising in any industry must have its origin in a complete analysis of the known facts or factors that pertain to it. The several illustrations

Jan 1, 1949

By P. W. George

This paper presents geological data regarding deposits of over 7,500,000 tons of fine-grained sulphide ore in barite gangue. A series of pyroclastics and arkoses was intruded by sills of quartz porphyry in connection with batholithic intrusions of granite 3 miles from Buchans. Gentle folding, with fracturing and shearing of tuff beds and intruded quartz porphyry, accompanied and followed the intrusion of granite and porphyry. The sulphide-barite mineralization is localized primarily in fractured and sheared tuff beds, but also in the sheared quartz porphyry. Two structures have proved particularly favorable for mineralization—one, the center of an anticline; the other, a series of weak, incompetent tuff beds intruded by thin sills of quartz porphyry and located between strong beds of arkose. During the folding the weak tuff with intruded quartz porphyry was intensely sheared and contorted and subsequently mineralized by sulphides and barite. Introduction Buchans is 5 miles north of Red Indian Lake, in Central Newfoundland, at an elevation of 900 ft. above sea level and 400 ft. above Red Indian Lake, and is reached by a 37-mile private railway from Miller-town Junction. The first ore body found at Buchans was discovered some 30 years ago in the bed of Buchans River, by Matty Mitchell, an Indian woodsman employed by the Anglo-Newfoundland Development Co. Ltd. In the years following the discovery the ore was developed by shaft-sinking and drifting, with results indicating a lenticular ore body in a shear zone, containing about 100,000 tons of extremely fine-grained sulphide ore in barite gangue averaging about 0.05 oz. Au, 4 oz. Ag, 1.5 per cent Cu, 10 per cent Pb, 18 per cent Zn. Because a profitable metallurgical treatment for the ore was not found, the mine was closed down in 1911. In 1915, Mr. H. A. Guess, Vice President of the American Smelting & Refining Co., learned of the Buchans River ore body, and after metallurgical tests had been carried on from time to time in his company's testing plant a satisfactory separation of the sulphides by selective flotation was finally effected in 1925. Prospecting for additional ore bodies was begun in 1926, utilizing geophysical methods under the direction of Hans Lund-

Jan 1, 1937

By M. W. Fabjanczyk, E. G. Alexander

INTRODUCTION The purpose of this paper is to summarise development of design processes used in the 1100 oreoody as a result of experience encountered. Design methods have been developed as a result of the history of ground behaviour, free-standing qualities of cemented back fill and mass blasting techniques. This paper contains an historical review of design methods previously described by Matthews ( 1972 ) , Hornsby and Sullivan (1977 and 19781, Kirkby, Blair and Hutton (19781, and Stewart (1980). The reasoning behind design philosphy changes are discussed and placed into context with methods now adopted. The 1100 orebody is Mount Isa's main producer of copper ore (5 million tonnes per year ) . Proven reserves are 120 million tonnes at 3.2% Cu. Location of the 1100 orebody in relation to overall mine geometry was well described by Dayton (1976). Geology The orebody is located in a series of massive brecciated shale lenses, in either a siliceous or dolomitic matrix, surrounded and separated by a uniform shale sequence. The whole formation is truncated at depth by a faulted contact with a greenschist facies metamorphic sequence below (Figure 1 and Figure 2) Mathias and Clark (1976). The breccia is known locally as silica dolomite and contains nearly all the economic mineralisation. Interfingering of shale and breccia often results in irregular boundaries to the silica dolomite and the ore limits. Geometry The geometry of the orebodies is shown by Figures 1, 2 and 3. Figure 3 also shows the location of the copper orebodies in relation to the lead orebodies. Structure Although the orebody is contained within the massive breccia (u.c.s. 150-250 MPa), it is cut by shear zones sub-parallel to the regional bedding (north-south striking, dipping approximately 60o to the west), and diagonally by major transverse faults (Figure A). These major faults have continuity in excess of 300 metres, with varying amounts of displacement up to 200 metres, and are zones of potential movement.

Jan 1, 1981

By Lawrence K. Jetter, Robert F. Mehl

SOME advances have been made recently in the theory of the kinetics of precipitation from metallic solid solution despite the complexities of the problem, but there is surprisingly little quantitative information available on rates of precipitation with which to test present theory or upon which to build new theory.‡ Attempts to measure rates of precipitation have been beset with difficulties which originate both in the anomalies that attend the changes in the properties selected for measurement, as, for example, in electrical conductivity or mechanical properties, and also in the complexities in the structural changes in some systems, as in the aluminum-copper system. If the functional relationship between the quantity of precipitate and the value of the selected property is uncertain, measurements of that property are obviously of uncertain utility in determining absolute rates of precipitation. If the precipitating system passes through one or more transition stages, the interpretation of measured rates lacks definiteness; in such cases, it is necessary to measure the rate of reaction in each separate stage, if the rate measurements are to have any significance from the kinetic point of view.* These difficulties cannot be wholly avoided, for at least in some measure they are characteristic of the process of precipitation from solid solution, but they can be minimized both by the selection of a simple system and by the use of a method of measurement relatively free from anomalous behavior. The present paper reports dilatometric measurements on the rate of precipitation of silicon from the aluminum-rich solid solution in the aluminum-silicon system-a study that approaches the desiderata of simplicity. The aluminum-silicon system offers advantages from these points of view: there are no known anomalies in the property changes accompanying precipitation; 2.3,4 there are no known transition stages; the precipitate is an element, not a compound, and both matrix and precipitate are cubic, and while the structures are not identical (the solid solution is face-centered cubic and the precipitate is diamond cubic), the system at least approaches the ideal case of a crystal precipitating from a matrix of the same crystal type-the ideal case which Becker5 assumed in treating the precipitation process theoretically. The dilatometric method, while not free from disturbing effects, as the subsequent dis-

Jan 1, 1942

By E. Houdremont

THE different influences exerted by the various alloying elements in iron and iron-carbon alloys give rise to a great number of complexities, which are difficult to grasp. It is important therefore to study any sys-tematic relations that may exist between the effects exerted by the various alloying elements, in order to obtain a general classification and thus a clearer conception of the nature of alloy steels. A systematic survey of the alloys of iron, based on an investigation of the binary equilibrium diagrams, was recently published by Wever. Although his work deals little with properties of importance in works practice, its purpose being rather to point out the theoretical agreement among the types of binary equilibrium diagrams and the position of the alloying elements in the periodic system (atomic radii, etc.), the classifica-tion proposed nevertheless also suggests relationships among the proper-ties of the alloys in question, even though the alloys may contain carbon in addition to iron and the alloying element. Wever divided the alloys of iron into one group exhibiting an open or enlarged gamma field and another exhibiting a closed or restricted gamma field, with both groups capable of further subdivision depending upon whether a continuous series of solid solutions is formed, or, owing to the separation of compounds, etc., only a limited series. Thus all alloying elements which with iron form a closed gamma field, a "gamma loop," produce alloys that beyond the composition correspond-ing to the greatest extent of the gamma loop are composed of ferrite alone at all temperatures. Alloys of this composition accordingly are not susceptible to ordinary heat treatment because of the lack of tran-formations. Steels. of this class may thus be divided into steels that contain less than the critical amount of alloying element, and are subject

Jan 1, 1934

By George H. Gilman

THE campaign now being waged to improve the quality of the rock-drill bit is the natural outcome f the scientific development of the drilling machine during the past twenty years. In this development there has been a great increase of power output per unit of weight of machine. But the development of the rock drilling engine has been seriously hampered by the need of a drill bit that would withstand, without undue wear or breakage, the heavy rapid blows of the improved pneumatic hammer. This problem was difficult to solve because an increase in the weight or section of the drill-steel bar resulted in decreased cutting speed and higher operating costs of both the bit and its actuating engine. The solution, therefore, is to make the bit of steel that, for a given weight or section, will be more shock and wear resisting. In the attempt to meet these requirements, many of the drill-steel manufacturers alloyed the steel with vanadium, chromium, nickel, etc., on the assumption that such elements would improve the rock-drill bit but due to the sensitiveness of such steel to forging and heat treatment, higher cost, and lack f continuity of effort on the part of the steel manufacturer to perfect this product, but little progress has been made in the adoption of these steels and the so-called straight carbon steel is today recognized as the standard material for all rock-drill bits. The first step in improving drill-bit efficiency is the determination f the cause of breakage and wear. For this reason, in 1917, certain rock-drill manufacturers, in conjunction with some of the larger mining interests, conducted exhaustive tests in both the field and laboratory. It was then found that, in the main, the cause of drill-steel troubles is not attributable to the duty imposed upon it by the normal operation of the drilling engine, but to improper forging and heat treating of the bit and to the subjecting of the bit to improper use. The fact that it is possible to minimize the troubles attributable to improper heat treatment of the drill steel has been demonstrated and it is recommended that such knowledge be made available by teaching those interested in the production, use, and up-keep of drill bits the principles on which success in this direction may be achieved.

Jan 6, 1921

By Reno H. Sales

Jan 1, 1914

By J. B. Clark

The oil industry has long recognized the need for increasing well productivity. To meet this need, a process is being developed whereby the producing formation permeability is increased by hydraulically fracturing the formation. The "Hydrafrac" process, as it is now being used, consists of two steps: (1) injecting a viscous liquid containing a granular material, such as sand for a propping agent, under high hydraulic pressure to fracture the formation; (2) causing the viscous liquid to change from a high to a low viscosity so that it may be readily displaced from the formation. To date the process has been used in 32 jobs on 23 wells in 7 fields, resulting in a sustained increase in production in 11 wells. INTRODUCTION Need For Process Although explosives, acidizing, and other methods have long been used, there still exists a need for artificial means of improving the productive ability of oil and gas wells, particularly for wells which produce from formations which do not react readily with acids. This paper discusses the development of a hydraulic fracturing process, "Hydrafrac", which shows distinct promise of increasing production rates from wells producing from any type of formation. The method is also considered applicable to gas and water injection wells, wells used for solution mining of salts and, with some modification, to water wells and sulphur wells. Requirements of Process In considering such a possible process, it appeared that certain requirements must be met. Some of these are as follows: A. The hydraulic fluid selected must be sufficiently viscous that it can be injected into the well at pressure high enough to cause fracturing. B. The hydraulic fluid should carry in suspension a propping agent, such as sand, so that once a fracture is formed, it will be prevented from closing off and the fracture created will remain to serve as a flow channel for oil and gas. C. The fluid should be an oily one rather than a water-base fluid, because the latter would be harmful to many formations. D. After the fracture is made, it is essential that the fracturing fluid be thin enough to flow hack out of the well and not stay in place and plug the crack which it has formed. E. Sufficient pump capacity must be available to inject the fluid faster than it will leak away into the porous rock formation. F. In many instances, formation packers must be used to confine the fracture to the desired level, and to obtain the advantages of multiple fracturing. Development of Process As a necessary step in the development of this process, it was deemed advisable to determine if the Hydrafrac fluids were actually fracturing the formation or whether these special fluids were merely leaking away into the surrounding formation. To determine this, a shallow well, 15 feet deep, was drilled into a hard sandstone. Casing was set, the plug drilled, and the well deepened in the conventional manner. A fracturing fluid dyed a bright red was used to break down the formation. Sand mixed with distinctively colored solids was injected into the well with the fracturing fluid to prop open any fracture made in the formation. A simulated gel breaker solution dyed a bright blue was then pumped into the well to determine if the gel breaker would follow the first solution. The results are shown in Figure 1. It was noted that a fracture was formed about the well bore, that the propping agent was transported back into the break, and that the breaker solution did actually follow the fracturing gel out into the fracture. While it is realized that this shallow well test is probably not exactly equivalent to a deep test, the results were interpreted as being a definite indication of what happens down the hole during a Hydrafrac job. Of interest in this connection is an investigation reported by S. T. Yuster and J. C. Calhoun, Jr.' This study, re~orted after the Hydrafrac work was under way, presents some excellent field data supporting the theory of fracturing a formation with hydraulic pressure. METHOD Steps of Hydrafrcu: Process Figure 2 shows a simplified cross-sectional view of a well treated by one version of the process. The first step, formation breakdown, is done with a viscous fluid, usually consisting of an oil such as crude oil or gasoline, to which has been added a bodying agent. Due to availability and price, war-surplus Napalm has been used in the majority of experiments to date. Napalm is the soap which was used in the war to make "jellied gasoline". The next step consists of breaking down the viscosity of the gel by injecting a gel-breaker solution and then after several hours, putting the well back on production. Figure 3 shows diagram-matically, a typical field hookup. The oil or gasoline is unloaded into the 10 bbl. tank shown on the left rear of the truck. This base fluid is picked up by the mixing pump and pumped through the jet mixer, where the granular soap is added. Next it goes into a small mixing tub, from which the high-pressure pump takes suction. The solution is then pumped into the well. The breaker solution is then taken from an extra tank and is displaced into the well immediately following the gel. When required, additional trucks may

Jan 1, 1949

By J. B. Clark

The oil industry has long recognized the need for increasing well productivity. To meet this need, a process is being developed whereby the producing formation permeability is increased by hydraulically fracturing the formation. The "Hydrafrac" process, as it is now being used, consists of two steps: (1) injecting a viscous liquid containing a granular material, such as sand for a propping agent, under high hydraulic pressure to fracture the formation; (2) causing the viscous liquid to change from a high to a low viscosity so that it may be readily displaced from the formation. To date the process has been used in 32 jobs on 23 wells in 7 fields, resulting in a sustained increase in production in 11 wells. INTRODUCTION Need For Process Although explosives, acidizing, and other methods have long been used, there still exists a need for artificial means of improving the productive ability of oil and gas wells, particularly for wells which produce from formations which do not react readily with acids. This paper discusses the development of a hydraulic fracturing process, "Hydrafrac", which shows distinct promise of increasing production rates from wells producing from any type of formation. The method is also considered applicable to gas and water injection wells, wells used for solution mining of salts and, with some modification, to water wells and sulphur wells. Requirements of Process In considering such a possible process, it appeared that certain requirements must be met. Some of these are as follows: A. The hydraulic fluid selected must be sufficiently viscous that it can be injected into the well at pressure high enough to cause fracturing. B. The hydraulic fluid should carry in suspension a propping agent, such as sand, so that once a fracture is formed, it will be prevented from closing off and the fracture created will remain to serve as a flow channel for oil and gas. C. The fluid should be an oily one rather than a water-base fluid, because the latter would be harmful to many formations. D. After the fracture is made, it is essential that the fracturing fluid be thin enough to flow hack out of the well and not stay in place and plug the crack which it has formed. E. Sufficient pump capacity must be available to inject the fluid faster than it will leak away into the porous rock formation. F. In many instances, formation packers must be used to confine the fracture to the desired level, and to obtain the advantages of multiple fracturing. Development of Process As a necessary step in the development of this process, it was deemed advisable to determine if the Hydrafrac fluids were actually fracturing the formation or whether these special fluids were merely leaking away into the surrounding formation. To determine this, a shallow well, 15 feet deep, was drilled into a hard sandstone. Casing was set, the plug drilled, and the well deepened in the conventional manner. A fracturing fluid dyed a bright red was used to break down the formation. Sand mixed with distinctively colored solids was injected into the well with the fracturing fluid to prop open any fracture made in the formation. A simulated gel breaker solution dyed a bright blue was then pumped into the well to determine if the gel breaker would follow the first solution. The results are shown in Figure 1. It was noted that a fracture was formed about the well bore, that the propping agent was transported back into the break, and that the breaker solution did actually follow the fracturing gel out into the fracture. While it is realized that this shallow well test is probably not exactly equivalent to a deep test, the results were interpreted as being a definite indication of what happens down the hole during a Hydrafrac job. Of interest in this connection is an investigation reported by S. T. Yuster and J. C. Calhoun, Jr.' This study, re~orted after the Hydrafrac work was under way, presents some excellent field data supporting the theory of fracturing a formation with hydraulic pressure. METHOD Steps of Hydrafrcu: Process Figure 2 shows a simplified cross-sectional view of a well treated by one version of the process. The first step, formation breakdown, is done with a viscous fluid, usually consisting of an oil such as crude oil or gasoline, to which has been added a bodying agent. Due to availability and price, war-surplus Napalm has been used in the majority of experiments to date. Napalm is the soap which was used in the war to make "jellied gasoline". The next step consists of breaking down the viscosity of the gel by injecting a gel-breaker solution and then after several hours, putting the well back on production. Figure 3 shows diagram-matically, a typical field hookup. The oil or gasoline is unloaded into the 10 bbl. tank shown on the left rear of the truck. This base fluid is picked up by the mixing pump and pumped through the jet mixer, where the granular soap is added. Next it goes into a small mixing tub, from which the high-pressure pump takes suction. The solution is then pumped into the well. The breaker solution is then taken from an extra tank and is displaced into the well immediately following the gel. When required, additional trucks may

Jan 1, 1949

By Donald E. Ackerman, Norman B. Pilling

The solubilities of a series of experimental alloys covering the range 0 to 100 per cent. Ni, 0 to 30 per cent. Cr have been studied under conditions of complete submersion in several fully aerated acid solutions, and in solutions containing sulfurous acid. In nonoxidizing, hydrogen-discharging acids, if the nickel content is below a certain critical amount, chromium increases the rate of solution and nickel decreases this rate; this critical content of nickel is about 13 per cent. Alloys containing more than this corrode at a constant minimum rate independent of iron, nickel or chromium contents. Austenitic chrome-nickel steels may thus have a resistance to these acids equal to that of nickel-chromium alloys. In nitric acid and in unaerated sulfurous acid rather sharp limits of attack occur which are principally dependent on chromium content. In the former the limit of attack is not related to a particular chromium content but varies continuously with acid concentration. The action of sulfurous acid on these alloys is highly dependent on the presence of small amounts of other substances in solution, and many sulfurous acid mixtures rapidly attack alloys to which the pure acid is wholly inert. The observed effects are not compatible with Tammann's theory relating corrosion resistance to lattice structure but are believed to be concordant with current views of the electrochemical nature of corrosion. Introduction The discovery, development and engineering application of iron alloys resistant to corrosion may well claim a place among the important developments in metallurgy of the past two decades. The varied demands of industry coupled with the skill of the metallurgist have resulted in the production of an extensive group of steels and alloys ranging from the now familiar "stainless " chromium steels of the kitchen to special alloys of great chemical complexity for particular, exacting needs. Any adequate description of the important properties of these-— physical, chemical and economic—would be a formidable undertaking.

Jan 1, 1929

By Donald E. Ackerman, Norman B. Pilling

The solubilities of a series of experimental alloys covering the range 0 to 100 per cent. Ni, 0 to 30 per cent. Cr have been studied under conditions of complete submersion in several fully aerated acid solutions, and in solutions containing sulfurous acid. In nonoxidizing, hydrogen-discharging acids, if the nickel content is below a certain critical amount, chromium increases the rate of solution and nickel decreases this rate; this critical content of nickel is about 13 per cent. Alloys containing more than this corrode at a constant minimum rate independent of iron, nickel or chromium contents. Austenitic chrome-nickel steels may thus have a resistance to these acids equal to that of nickel-chromium alloys. In nitric acid and in unaerated sulfurous acid rather sharp limits of attack occur which are principally dependent on chromium content. In the former the limit of attack is not related to a particular chromium content but varies continuously with acid concentration. The action of sulfurous acid on these alloys is highly dependent on the presence of small amounts of other substances in solution, and many sulfurous acid mixtures rapidly attack alloys to which the pure acid is wholly inert. The observed effects are not compatible with Tammann's theory relating corrosion resistance to lattice structure but are believed to be concordant with current views of the electrochemical nature of corrosion. Introduction The discovery, development and engineering application of iron alloys resistant to corrosion may well claim a place among the important developments in metallurgy of the past two decades. The varied demands of industry coupled with the skill of the metallurgist have resulted in the production of an extensive group of steels and alloys ranging from the now familiar "stainless " chromium steels of the kitchen to special alloys of great chemical complexity for particular, exacting needs. Any adequate description of the important properties of these-— physical, chemical and economic—would be a formidable undertaking.

Jan 1, 1929

By M. W. Hayward

THE object of this paper is to record and tabulate the data and field observations obtained by the writers and their associates during 10 years of intensive study of lead-zinc deposits in the Cretaceous limestone areas in Northern Mexico, particularly in mines owned by the Cia Minera de Peñoles, S. A. At the El Paso meeting of the Institute in October, 1930, J. G. Barry made the suggestion that a committee be appointed to correlate the ideas and theories which have been put forth by the numerous engineers and geologists who, during recent years, have made a study of the ore deposits in the area under consideration. The first step in a work of this nature would be to record all of the observed facts, and these facts would have to be accepted by those who attempted to formulate a theory of ore deposition. It is with this idea in mind that the writers have described as accurately as possible the actual, observed facts pertaining to the occurrence of the lead-zinc ores in dolomites or dolomitic horizons. By most writers the term "dolomite" is loosely used to designate magnesium-bearing limestones, regardless of the percentage of MgO present. Since no true dolomites exist in the areas to be described, we shall also loosely use the terms dolomite or dolomitic limestone to desig-nate those beds having a magnesia content of 5 per cent MgO or more. For a number of years the writers have been impressed with the fact that in areas where dolomite beds occur a large percentage of the lead ore is found in these beds, in spite of the fact that such beds may be overlain or underlain by pure limestone, which one would assume to be just as favorable for replacement as the dolomite, if not more so on account of its being more soluble in acid solutions than the dolomite. It is true that in some limestone areas, such as the Erupcion-Ahumada districts, Chihuahua, and Providencia, Zacatecas, where no dolomite beds have been found, large tonnages of lead ores have been mined. We venture to predict, however, that had there been dolomitic beds in these areas, the

Jan 1, 1932

By S. A. Swensrud

REPORTS from smelters show that all were so occupied with the in- creased production called for during the first half of the year that little time was devoted to metallurgical developments. Improvements which have been made such as gas-firing and other alterations ill the reconstructed Hayden smelter, will require time for reporting. The labor situation at all plants held the most prominent place and put all other problems in the background. Coming events of considerable importance concerti the construction of two new smelters. The Chino unit of Nevada Consolidated which has long had its concentrate smelted at the El Paso plant of the American Smelting and Refining Co. is constructing its own smelter at the property in New Mexico. The newest Phelps Dodge development of the Clay ore body at Morenci, Ariz., will call for another new smelter.

Jan 1, 1938

By William Grady

FACTORS entering into the market value of coal are its grade, and the cost of labor, material, and capital. Reduction in these costs cannot be expected in the future, and it therefore follows that greater economy in their use must be accomplished if it is desired to hold the present markets; more tons of product per unit must be obtained in a given time from both men and material, and means devised for increasing the percentage of lump and domestic sizes. This paper is presented for the purpose of inviting discussion and stimulating thought in regard to the influence of methods of procedure and plans of mining, upon the quality of coal, the economical use of labor, material, and capital, and the cost of production. Even the better methods of the. present day leave much to be desired, and a review of the reasons and necessities for their use may be of value in pointing the way to more economical mining. The writer does not attempt to discuss untried methods of mining, but rather to state clearly and concisely a summary of the results obtained under the several methods of procedure that have been adopted. In some instances a high degree of concentration has been effected, and comparisons of the results obtained with the results of lesser degrees of concentration form an interesting study. It is believed that much may be accomplished in improving the quality, and in the more economical use of labor, material, and capital, by concentration, and it is to concentration in particular that your study is invited. The writer, who .has occasion to visit many mines, most of which ire under different management, has been inclined to the opinion that improvement has been retarded in many ways and that mining has not as yet been entirely freed from the early-day practices which were forced upon it.

Jan 5, 1915

By C. B. Foraker

THE Magma mine, of the Magma Copper Co., at Superior, Pinal County, Arizona, is 68 miles east of Phoenix and 21 miles west of Miami, Arizona, on highway U. S. 180. Temperatures and Underground Waters Surface Temperatures.—The average surface dry-bulb temperature at Superior is 72.4°; wet-bulb, 57.4°; with an indicated relative humidity of 38 per cent. The average yearly rainfall from 1921 to 1936, inclusive, was 18.74 in. The maximum condition of the atmosphere is in June, July and August, and the minimum is in January and February. The surface temperatures, of course, influence the temperatures of the downcast shafts; however, the variation between winter and summer causes a difference of only 2" to 3" in the stopes and working places that are not close to the intake shafts. Average atmospheric conditions are shown in Fig. 1. Rock Temperatures.—Rock temperatures on the deeper levels of the mine are as follows:

Jan 1, 1940