By H. L. Hartman

The estimation of the magnitude of pressure changes which occur in mine ventilation circuits is of primary importance to the mining engineer in making changes in an existing mine or in projecting the ventilation requirements of a new mine. It is a formidable task in many cases, because no adequate theory is available and empirical data are unreliable or even lacking. The common practice of increasing one's estimate of the mine static pressure by an arbitrary "safety factor" to compensate for the unknown is a poor substitute for accuracy. Generally little difficulty is encountered in calculating friction losses in mine airways. As long as the friction factor can be reliably estimated, the well-known Atkinson formula gives accurate results. However, it is in the determination of shock losses that the ventilation engineer encounters difficulty and is apt to resort to an arbitrary allowance. Shock losses may constitute as little as five or as much as twenty-five percent or more of the overall pressure drop in the mine, and such allowances are generally completely unsatisfactory. Since other shock losses have been covered by McElroy (1), this paper deals with a long-neglected source of shock and pressure change in ventilation circuits, divergence and convergence of airflows, here referred to by their more common mining terms, splits and junctions. PREVIOUS WORK There is practically no fundamental information available in ventilation literature on the splitting and junction of airflows, either in mining or mechanical engineering periodicals or handbooks. Fluid mechanics textbooks seemingly avoid the subject of divergence and convergence, except for brief empirical treatment. The only investigation reported for mine ventilation systems was by Weeks, et a1 (21), in 1933. Although applicable to the case of line brattices in coal mines, it cannot be applied to the general case of mine splitting and junctions involving change of direction with little or no area change. In dealing briefly with the subject of shock losses at splits and junctions, McElroy (1) suggests only that they be considered comparable to bends, with losses at junctions being increased 50 pct to allow for interference of merging streams. He recognizes the importance of quantity ratio but concludes that exact quantitative data are lacking to compute losses at splits and junctions. A very capable summary and analysis of the state of knowledge in industrial ventilation and fluid mechanics regarding losses due to divergence has recently been reported by Gilman (3). In considering all earlier work dealing with both air and water as fluids, he compares results on a common basis and obtains good empirical agreement. For divergent flow, the controlling variable in each branch is the quantity ratio, although the deflection angle is of secondary importance. Empirical equations are presented for straight and 90-deg branches with varying velocity ratios, assuming branches smaller than the main duct. These formulas are modifications of the Borda equation for abrupt contraction and expansion. The only information available on shock losses in convergent flow are approximate experimental data presented by Alden (4) and the Manual of Recommended Practice for Industrial Ventilation of the American Conference of Governmental Industrial Hygienists. Alden considers the effects of both quantity ratio and deflection angle. The data indicate an effect opposite to that observed in divergence, the shock loss varying directly with quantity ratio. SHOCK LOSS THEORY Because pressure losses due to shock have been found to bear a constant relation to the mean velocity of flow in a given conduit, they are frequently expressed as a dimensionless function of the velocity head, termed the shock loss factor. For airflow in ducts and mine airways, the shock loss may be represented by the formula (1): Hx - XHv, (1)

Jan 1, 1961

By T. A. Rickard

The purposes of composition are various; one purpose, for instance, is to make a record for the writer's own use, as in a diary. That does not involve responsibility to others. There is also the writing meant to influence opinion-to be persuasive, and pleasing. With such writing we need not concern ourselves at this stage of our study. The prime purpose of technical writing is to be informative-to convey information; therefore it must" be clear beyond the chance of misunderstanding. Such clearness is impossible if meaningless or ill chosen, words are sprinkled through the text. Discard the trivial phrases that are constantly at your elbow. Brush aside a host of vapid superlatives. Metternich exclaimed:' "The superla¬tive is the mark of fools". It is a false emphasis, like the underlining in a school-girl's letter. For example, the little word `very' can be deleted nine times out of ten; it is an impediment to terse and perspicuous writing, as 'the multitudinous hand-baggage of the British tourist is to his travel. 'Very' supposes comparison. A mine with a 1000-ft. shaft is very deep to the scribe who writes from the Joplin district', in Missouri, but it seems a shallow hole to a man living at Calumet, Michigan. A vein that is 10 feet across may be considered very wide at Cripple Creek, Colorado, but it is only a `stringer' to the miner at the Homestake, in South Dakota. Ore assaying $20 in gold is very rich at Juneau, Alaska, where .10,000 tons of $1 ore is crushed daily, but it is relatively low-grade to the pocket-miner at Alleghany, in California. It is all a matter of comparison; unless the reader knows your standards of depth, width, or richness, your `very' has no significance. "Where erosion was very rapid or oxidation very shallow"

Jan 1, 1931

By C. H. Mathewson

COPPER and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.1 It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of. the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By G. Donald Emigh

Nothing is more important to life-plant and animal-than phosphate. Its compounds are essential to the energy functions of all living systems and for the formation of bones and teeth. Animals get their phosphate from eating plants and other animals, or domestically from feed supplements. Plants get their phosphate from the soil. Man's most important use of phosphate is for fertilizer; however, he is also a heavy user of many industrial phosphate chemicals. Phosphate occurs in all igneous and sedimentary rocks, and in all fresh and saltwater. The average content in rocks is 0.1 to 0.2% P2O5, as documented recently by McKelvey (1973). About 200 minerals contain more than 1 % P,O,. However, the important one in igneous rocks is fluorapatite, (Ca,(PO,) ,F) containing about 42% P,O, and 3.8% F,; in sedimentary rocks the one important mineral is francolite, a carbonate fluorapatite containing up to 2% molecular CO,. Both are in the apatite family of minerals. The mineralogy of phosphate minerals was reviewed recently by Altschuler (1973). Although phosphate occurs in nearly all rocks, economic recovery is limited to deposits where natural concentration of the phosphate mineral has occurred. Occasionally natural concentration is great enough that the material can be used as mined; generally, however, the ore is low grade and must be concentrated.

Jan 1, 1975

By H. L. Lovell, L. H. E. Weyher

Cyclones have been used successfully in the mineral industries to solve solid-liquid as well as solid-solid separation problems in the processing of fine particles. Substantial information is available about the operation of cyclones as thickeners, classifiers, and concentrators using a dense medium. However, very little is known about the operation of the cyclone as a fine coal concentrator not using dense medium. This application of the cyclone, namely to wash fine coal in water, requires that classification phenomena be minimized in order to arrive at an effective separation of the high density ash and sulfur-bearing mineral particles from the low density coal particles over a wide particle size range. The authors have investigated the role of feed pressure, orifice diameters, and vortex-finder length in the cyclone washing of fine coal (--1/4 in.) in water. The results of this investigation show that cyclone washing of fine coal in water is an effective unit operation particularly capable of reducing the inorganic pyritic sulfur content. The combination of hydrocyclones with complimentary equipment such as Sieve bends, shaking tables, and flotation units appears to be especially promising and may ultimately yield fine coal processing systems that could approximate the high recovery efficiencies of today's coarse coal cleaning circuits. In the future, fine coal beneficiation can be expected to receive even greater research emphasis as a result of increasing sulfur restrictions on all major coal markets. In a previous paper, work, conducted at the Pennsylvania State University, on the hydrocyclone washing of fine coal was discussed.' The initial evaluation based on that wo-rk demonstrated the feasibility of hydrocyclones as fine-coal cleaning devices, and in that previous paper selected test data were presented that showed in principle how product yield and assay respond to variations of the major cyclone operating variables. The present paper reports in greater detail on the findings and presents a comprehensive evaluation of the data as follows: (1) Hydrocyclone throughput rates were related to feed pressure and other variables by regression equations. These equations are compared with other capacity-vs.-pressure drop expressions taken from the literature on classification cyclones. (2) The flow ratio was found to be the most important variable for the separation of the solids. Control of this ratio through various cyclone operating parameters is discussed. (3) The data on the product yield as well as the ash and sulfur assays from the tests were evaluated by means of correlation and multiple regression analyses. Because size-classification phenomena cannot be suppressed completely in hydrocyclone washers, product yield and assay data are regressed against cyclone operating variables separately for different size classes. These equations then reveal how the interactions of the cyclone operating variables vary in terms of the separation for different size classes. (4) Density partitions from additional tests were analyzed by supplementing product-size analyses with sink-float analyses of the separated product size classes. The evaluation of these data show how classification phenomena affect separation by density. The results demonstrate in particular the feasibility of the hydrocyclone washer for removing pyritic sulfur from fine coal. In addition to these specific findings, the investigation points up the value, in general, of using hydrocyclone washers in combination with unit operations such as screening, table concentration, and flotation. In order to make optimum use of the hydrocyclone washers and work out the most effective combination of unit operations, it is important to have careful flowsheet analyses corresponding to the given feed and product requirements. Analyses of this kind are now possible by means of computer simulation of flowsheets and other operation research tools. INTRODUCTION Before proceeding with the detailed treatment and evaluation of our results, it will be useful to review the fundamental aspects of cyclone separators and also restate the experimental procedures and data handling employed in these studies. Review of Cyclone Fundamentals: AS shown in Fig. 1, the basic components of cyclones commonly used

Jan 1, 1970

By K. T. Koone, R. J. Blackwell

One of the more important problems to be solved in designing a miscible flood is related to the size of the solvent bank used. Size of the bank may be critical to economic success. Too large a bank loses money; too small a bank may deteriorate and fail to maintain the miscibility needed for high recovery. An important factor in deterioration of a small bank is permeability channeling. In a highly stratified reservoir, solvent speeds ahead in the more permeable zones and mixes laterally with fluids bypassed in adjacent, low-permeability strata. Numerical solutions have been obtained .for the differential equations that describe the movement of a slug through a two-layer system in which mixing occurs both in the direction of flow and transversely. The solvent slug is assumed to have the same density and viscosity as the resident fluid and the pushing fluid. These solutions have been verified by comparing them with similar concentration profiles obtained in the laboratory in a 36-ft stratified model packed with glass beads. The theoretical study revealed that when the dominant mechanism causing a bank to fail is lateral mixing the bank size needed for a given recovery may increase with length rather than decreasing as the square root of reservoir length, as suggested by one-dimensional mixing theory. From a comprehensive examination of the variables, a generalized correlation is developed that relates strata thicknesses, bank size, fluid velocity, mixing coefficients, system length and simple solvent-resident fluid phase behavior to the area miscibly swept. INTRODUCTION Miscible displacement, or solvent flooding, continues to receive widespread attention as a method for increasing oil recovery over that possible in conventional gas-drive or waterdrive projects. A basic economic requirement in the application of such processes is the use of as little solvent as possible. A basic physical requirement is that enough solvent be used to maintain miscibility. Economics places an upper limit on the size of a solvent slug, and physical considerations establish a lower limit. Consequently, the practicality of any given miscible process requires that the economic limit be greater than the lower limit imposed by physical requirements. Procedures exist for determining the economic limit; however, procedures for determining realistic minimum bank sizes exist for only special reservoir situations. In the past, bank size has usually been selected on the assumption of a piston-like displacement for which only longitudinal mixing is important. This assumption leads to the favorable conclusion that bank size, expressed as per cent of pore volume, is inversely proportional to the square root of length. Collins considered the problem of transverse mixing of solvent with fluids in bypassed zones with the assumptions that no forward mixing occurs and that the concentration is uniform in the permeable stratum of interest. 1 Lauwerier considered a mathematically similar problem in thermal recovery operations.2 Their work suggests the much less favorable conclusion that bank size could be directly proportional to the length or even higher powers of the length. This paper considers the physical behavior of a small solvent bank as it moves through a real reservoir, without imposing many of the restrictive assumptions of past treatments. To facilitate mathematical description, an idealized, two-layer model that permits mixing both laterally and in the direction of flow will be considered. A calculation procedure for solving the descriptive equations will be developed for a displacement involving fluids of equal density and viscosity. In addition, laboratory experiments designed to check the computational results will be described, and the coincidence of calculated and observed results will be discussed. The use of many solutions for a variety of bank sizes, strata thicknesses and characteristic system lengths to develop a usable correlation between

Jan 1, 1966

By F. V. Lenel, G. S. Ansell

The creep behavior of an aluminum -aluminum oxide alloy, A T 400, fabricated by compacting an atomized aluminum powder, extruding the compact, cold working, and recrystallizing the extrusion, was investigated. This alloy has a dispersion spacing of 1 . Previously Ansell and Weertman determined the steady-state creep rate of a recrystallized aluminum-aluminum oxide SAP-type alloy, MD 2100, with a 0.48-p dispersion. This alloy was found to have a steady-state creep rate of less than 10-6 min-1, too small to be measured accurately. By employing a more sensitive method of measuring creep rate, it was possible to determine the steady-state creep rate of AT 400 alloy, which is somewhat faster than that of MD 2100, at a series of temperature and applied stresses. Above a stress of Burger's vector, A = dispersion spacing, u = is a shear modulus) the rate follms an equation of the type: Steady-state creep rate K = A exp. where A is a constant, Q is the activation energy for sey-diffusion, and is the applied stress. At stresses lower than the steady-state creep rate drops off sharply and is no longer in agreement with this equation. This behavior is in good agreement with that predicted by the model for dispersion strengthened alloys in the stress and temperature range investigated. The absolute value of the creep rate is, however, four orders of magnitude lower than that predicted if the normal number of active dislocation sources are assumed to be present. It is concluded that in this SAP-type alloy the usual three-dimensional dislocation network is not present. Instead, short dislocation segments extending from one dispersed particle and terminating at a neighboring particle may act as dislocation sources. With this provision the creep model proposed by Ansell and Weertman reasonably accounts for the creep behavior which was observed. RECENTLY, Ansell and Weertman1 proposed a dislocation model from which they derived creep equations to describe the steady-state creep behavior of dispersion - strengthened alloys. Following Schoeck,2 they assumed that the rate controlling process for steady-state creep is the climb of dislocations over the dispersed particles. In order to verify their creep model, Ansell and Weertman determined the steady-state creep behavior of an aluminum-aluminum oxide SAP-type alloy, MD-2100, in both the fine-grained as-extruded, and coarse-grained recrystallized conditions. Since the grain size was the order of the dispersion-spacing, their model was not applicable for the as-ex- truded alloy. It should, however, be applicable to the coarse-grained recrystallized alloy. The results they obtained were rather unexpected. No meas-ureable steady-state creep was observed for the recrystallized MD-2100 alloy. If their model is correct, and if the second-phase particles act solely to hinder dislocation motion, then some measureable steady-state creep would have been expected. On this basis, they postulated that, in this SAP-type alloy, the main effect of the fine dispersion was to inactivate dislocation sources rather than to hinder the movement of dislocations. In order to understand more fully this unusual creep behavior, and to determine the validity of the model proposed,' the steady-state creep behavior of an aluminum-aluminum oxide recrystallized SAP-type alloy, with a somewhat coarser dispersion spacing, was investigated. The results of this study are presented in this paper.

Jan 1, 1962

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By AIME AIME

At the Annual Meeting of the Institute, February, 1908, the following amendments to the Constitution were proposed for action at a future business meeting (see Trans., XXXIX, xxvii) To Art. II. After the first sentence of this Article, add the following sentence « These classes may be subdivided by the Council, according to profession, length of membership, nationality, or other conditions not inconsistent with the provisions of this article." To Art. III. In the first line, substitute " fifteen " for "ten " dollars. At the Annual Meeting of February, 1909, action upon these amendments was postponed to the next business meeting (see Bulletin No. 27, March, 1909, p. xiv). Of these two amendments, the first has been withdrawn, as unnecessary-the subdivision thereby authorized being already practicable without such amendment. The second amendment will be acted upon at the next Annual Meeting, February 15, 1910, and the Secretary has been instructed to call the attention of members to the subject in such a way as to secure a general vote upon it. A special circular, now being prepared by the Secretary, will shortly be sent to all members. Year Book of the Institute. The Year Book of the Institute for 1910 is sent to all members and associates with this issue of the Bulletin. In addition to the lists of members enrolled Jan. 1, 1910, and arranged both alphabetically and geographically, this annual contains lists of officers, council, corporation, past officers, meetings, and notices concerning publications; also the constitution and by-laws of the Institute, and blank forms for proposal of mem-

Jan 1, 1910

By L. L. Swift

.It the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows ill sorne types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing tuetal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cicnt of friction. Under most operating conditions the friction depends on the unit, pressure of the bcaring, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.' The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual canstituents was developed to fill this need. MICROCHARACTER The Bierbaum MicroCharacter~,~ measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground so that it is the corner of a cube, and Mounted

Jan 1, 1939

By L. L. Swift

.It the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows ill sorne types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing tuetal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cicnt of friction. Under most operating conditions the friction depends on the unit, pressure of the bcaring, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.' The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual canstituents was developed to fill this need. MICROCHARACTER The Bierbaum MicroCharacter~,~ measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground so that it is the corner of a cube, and Mounted

Jan 1, 1939

By Eugene S. Meieran

The effects of methods of crystal growing, wafer sawing, polishing, routine handling, diffusion, and epitaxial growth on the defects in GaAs are reviewed and studied using reflection and transmission X-ray topographic techniques. In general, it was found that boat-grown crystals exhibited fewer defects than Czochralski crystals, although all crystals showed large numbers of precipitates visible when examined in the electron microscope. Mechanical surface treatments such as sawing and mechanical polishing introduce damage to a depth of about 5 µ, most of which can be removed by suitable chemical or chem-mechanical polishing. In addition, defects can be introduced through routine handling of wafers, for example with metallic tweezers. These defects can be quite severe, and have been observed 20 µ below the wafer surface. Defects can also be introduced through diffusion and epitaxial growth. These defects, which include precipitates, growth pyramids, stacking faults, dislocations, and so forth, can be detrimental to device fabrication. It is shown that wafers or films which appear defect-free optically can contain defects visible in the X-ray topographs. WHILE the use of GaAs in the semiconductor industry has increased very rapidly in the last few years, due mainly to the recent development of many important GaAs devices,1,2 the major limit to the production of commercial quantities of many GaAs devices remains a severe lack of suitable materials technology. This lack is apparent in two critical areas. First, production quantities of high-quality GaAs crystals, reproducibly doped and precipitate-free, simply are not available commercially, although some reasonable quality material is available on a limited first-come, first-serve basis. Second, in comparison to silicon technology, little is known about the effects of processing variables on the defects either present in as-grown GaAs or introduced through processing and handling of wafers. These areas are now receiving some attention from semiconductor device manufacturers, who are studying defects in GaAs in order to better understand how either to prevent their occurrence or to cope with their existence. Most investigations of the defects in GaAs have been made by optical microscopy3-5 or transmission electron microscopy techniques.'-' Recently, however, the imaging techniques of X-ray topography, electron mi-croprobe analysis, and scanning electron microscopy are being applied to the study of GaAs.9-14 In the case of X-ray topography, a one-to-one image is obtained that must be photographically enlarged. In compensa- tion, the defects within entire wafers may be imaged by simple scanning (Lang technique15) if the wafer is reasonably perfect, or by using the scan oscillation technique developed by Schwuttke16 if the wafer is warped or distorted. The purpose of this paper is to both review and extend the general application of X-ray topographic techniques to GaAs. Emphasis will be placed on the effects of growth and process variables on the quality and perfection of both bulk and epitaxial GaAs. Reference to optical or electron microscopy results will be made when useful. Since the effects on defects of a wide variety of processing variables such as crystal growing, sawing, polishing, diffusion, and epitaxial growth will be somewhat superficially reviewed, a fairly extensive bibliography of the most important recent results in these areas is included. However, for completeness, important defects will be illustrated here, although such defects have been previously shown by others. While this paper is concerned with defects rather than with the physics of X-ray scattering, the mechanisms of contrast formation in the topographs will of necessity be briefly mentioned. EXPERIMENTAL GaAs crystals, both boat-grown18 and Czochralski-grown,'8 containing a variety of dopants of various concentrations, were purchased from outside vendors. Wafers were sliced from the crystals using a Hamco ID saw and were mechanically polished using 1 µ diamond paste. Chem-mechanical polishing was done in bromine-methanol as described by Sullivan and Kolb.18 Chemical polishing was done using a modified sulfuric-peroxide solution, 11 parts H2SO4, 1 part 30 pct H2O2, 1 part DI water.5 Zinc diffusion was carried out in a closed tube, using a 10 pct Zn-In source at 825°C for 1 hr. Oxide masking techniques were used to select the area to be diffused. Epitaxial wafers were either purchased or prepared here. All epitaxial runs prepared here were carried out using a Ga-GaAs-AsC13 source in a closed tube at a substrate temperature of 750°C. Wafers were chem-mechanically polished and gas-etched prior to deposition. The X-ray topographs were taken on a Krystallos Lang camera, operating in the transmission scanning geometry (Lang technique15) or in the reflection scanning geometry (modified Berg-Barrett technique20,21). MoKa, radiation was used for all transmission topographs using a Jarrell-Ash 100-µ spot focus. CuKal radiation was used for all reflection topographs using a General Electric CA-7 1-mm spot focus X- ray tube. Topographs were printed from an intermediate contrast inversion film, so the contrast shown in all figures here is the same as that of the original 50-µ-thick emulsion L4 Iiford nuclear plate used to record the topograph.

Jan 1, 1969

By Jonas Svensson

A new method is described for the production of cold-bonded pellets using a hydraulic binder, such as portland cement. Large-scale pilot-plant tests have proved that self-fluxing pellets of high reducibility and good handling strength can be made by the method. Blast-furnace trials have shown that the pellets are an acceptable burden material, comparable with self-fluxing sinter or heat-hardened pellets. Economic factors of commercial-scale production are discussed. The Grangcold Pellet Process—for which patents have been applied or already granted in a number of coun-tries—uses a hydraulic adhesive such as portland cement, slag cements, pozzolanic cements, etc., for the production of cold-bonded pellets. The idea of using a hydraulic binder for the agglomeration of iron-ore fines is not new. Portland cement was proposed as an adhesive for cold-bonded iron-ore briquettes in patents granted more than 50 years ago.' In a report on the briquetting of iron-ore fines, published in Stahl und Eisen in 1959; it is stated that briquettes bonded with portland cement are used on a small scale at an ironwork in Germany. According to the report, the briquettes showed excellent strength in the blast furnace although their general use was made impossible because they required a long hardening time, during which they are sticky, soft, and difficult to store and handle. The Grangcold Pellet Process has overcome this particular disadvantage by mixing the balls with a suitable amount of the balling concentrate before storing them. The pellets are embedded in the concentrated during storing in such a way that they are isolated from each other and thus prevented from sticking together to form clusters. Thanks to the embedding concentrate, the pellets are subjected to a more or less uniform pressure from all sides which does not deform them. Thus, the mixture can be stored in a stockpile or in a bin until the pellets have hardened sufficiently. The concentrate is separated from the pellets by means of screening. The concentrate is returned to the balling operation and the pellets are either shipped to the blast furnace or stored for final hardening. The binder preferred for the Grangcold Pellett Process is portland-cement clinker, ground without the admixture of gypsum in order to avoid sulfur in the pellets as far as possible. Usually a 10% binder content is used. Two-thirds of the portland-cement clinker consist of lime and the rest is silica, alumina, and ferric oxide. Thus, self-fluxing or overbasic pellets are produced with this binder if the amount of silica in the concentrate used does not exceed 4%. The Grangcold Pellet Process was developed by the mineral Processing Laboratory of the Granges Co. Work started in 1963 with batch-scale tests. In 1966, a small pilot plant was put into operation in which 1800 tons of pellets were produced using 10% of rapid-hardening portland cement as a binder. Favorable results from a blast-furnace test with this batch led to the decision to erect a larger pilot plant which went into production in the summer of 1967. Since then, approximately 100,000 tons of cold-bonded pellets have been produced, mostly with 10% gypsum-free portland cement as a binder. Several full-scale blast-furnace trials have been performed with the pellets. The results of the trials indicate that the Grangcold pellets constitute a satisfactory blast-furnace feed. An industrial plant for the production of Grangcold pellets with a rated capacity of 1.5 million tpy is now under construction at the Granges Co.'s mine at Grangesberg. The plant will come into operation in the summer of 1970. Results from Laboratory Work Pellets made from iron-ore concentrate bonded with portland cement harden slowly and their handling is very critical until they have hardened enough to loose their stickiness. It is therefore especially important to study the progress of the hardening action and the factors influencing it. This is best achieved by investigating the relationship between the compressive strength of the cement-bonded pellets and the curing time under varied conditions. The general course of this relation-

Jan 1, 1971

By H. S. Rawdon

One of the most vital problems in the manufacture of steel at present is the occurrence of the defects that have been popularly termed "snow flakes," "flakes," or "scabs." Particularly is this the problem of many manufacturers who, during the past 2 yr., have undertaken large-scale production for the first time. A study of the microstructure of such defective material throws considerable light upon the nature of these defects and is essential before measurcs may be taken for the elimination of the defects. Flakes do not appear to be found in the plain carbon steels; they have been found. however, in abundance in some of the simple alloy steels that are being used in such vast quantities; vie., nickel steel of the approximate composition, 0.40 carbon and 3.5 per cent. nickel, and in the chrome-nickel type. The present article summarizes the characteristic features of defective steel of the flaky type as they have been found by laboratory study of numerous specimens, and it aims to show the conditions within the metal that are favorable to the occurrence of this type of defect without entering into the details of mill practice (size of ingot, design of molds, rate of cooling, distribution of cooling stresses, etc.), all of which conditions appear to play a role in the production of these defects. MacrostrUctURe To one familar with flaky steel, the appearance of "snow-flakes" is unmistakable and is not to be confused with other types of defects. Figs. 1 to 6 show the appearance of fractures of steel showing this type of defect; the white silvery area, which always has the appearance of being of a very coarsely crystalline structure, in the specimen stands out in bold contrast to the darker background and readily justifies the use of the term "snow-flakes." Fig. 1 shows the appearance of the faces of the two halves of a nickel-steel forging that has been split to show the interior flakes. Fig. 2 is a nickel-steel bar (carbon 0.40 per cent.,

Jan 1, 1920

By R. P. Dolan, W. M. Shedd, B. L. Buchanan

Analytical expressions are derived from empirical data relating the basic physical device parameters to the radiation dose. To put in perspective and justify the approach taken, the overall problem and methods of attempted solution of radiation damage to transistors in a missile or satellite environment is briefly examined. The main emphasis is on a new criteria for neutron radiation hardness and the device design implications resulting from using this criteria. Contrary to other derived criteria, the derived bipolar hardness relation depends mainly on the initial lifetime rather than the base transit time. It is shown, that contrary to previously accepted beliefs, the inherent attainable radiation tolerance of JFET's is at least a factor of ten greater than the radiation tolerance ofbipolars. Experimental results on JFET's designed for maximum neutron radiation tolerance are presented. The accuracy, utility, and range of possible validity of various published lifetime and carrier removal damage constants are discussed. It is well known that transistors are subject to damage due to radiation at much lower radiation levels than those which would cause structural damage to a missile or satellite. The three principal categories of radiation damage to transistors are displacement, ionization, and thermomechanical. The main cause of displacement damage is fast neutrons, and the main effects which permanently degrade transistor operation are minority carrier lifetime reduction and carrier removal. A second-order effect is mobility reduction. The main cause of ionization damage is gamma radiation which results in permanent effects due to charge build-up in the oxide and transient effects due to photo-current generation. The transient effects are usually handled by using circumvention techniques in the electronics system. The extent of the transistor degradation due to displacement and ionization damage depends strongly on the transistor type, whereas the extent of thermomechanical damage does not depend on the transistor type, but depends mainly on packaging and metallization which are common to all transistor types. The standard transistor types are categorized in Fig. 1 and typical cross-sections are shown in Fig. 2. The original reason for the designation of the two classes of transistors was that the unipolar operation depends on only one carrier (majority) and the bipolar operation depends on both minority and majority car- riers. The bipolar is then seriously degraded by minority carrier lifetime reduction, whereas the unipolar or field effect transistor is not. One of the two principle classes of field effect transistors, the junction field effect transistor (JFET), depends strongly on carrier removal. However, the insulated gate (MIS) is little affected by either carrier removal or lifetime changes, but is virtually eliminated as a radiation resistant device because of permanent charge build-up in the insulator caused by ionizing radiation. The bipolar and JFET suffer only minor effects due to charge build-up in the oxide passivation when compared1 to the MOS. This is because the active region of the MOS is adjacent to or part of the oxide layer. It is then the bipolar and JFET which are potentially resistant to permanent radiation damage. DERIVATION OF RADIATION TOLERANCE RELATIONS Criteria. The bipolar is by far the most widely used transistor type. The usual criteria for hardening bipo-

Jan 1, 1970

By Charles H. Fulton

Experimental work on the process was begun on a laboratory scale at Cleveland, Ohio, in 1914, and transferred to East St. Louis, Ill. in 1916, where a commercial sized furnace was in technical operation until January, 1918. The essential steps of the process are as follows: Oxidized zinc ore or roasted zinc concentrate is mixed with crushed coke and coal-tar pitch and formed into briquets 9.25 in. (23.5 cm.) in diameter and 21 in. (53 cm.) long in a manner similar to that used in the manufacture of graphite or carbon electrodes, except that much less care and time are required. The composition varies with the nature of the ore; in one case, the composition was 100 parts ore, 70 parts coke, and 18 to 20 parts pitch. These briquets maintain their form and volume during and after the distillation of the zinc. This object is gained by using coke as the matrix and coal-tar pitch as the binder; this pitch becomes coke on heating and unites the ore particle and the original coke particle into a continuous mass. The briquet is an electrical conductor but only to such a degree that it can be used as a resistor. The size of the ore, as in the present practice of zinc metallurgy, ranges from fine material, such as flotation concentrate, to coarse table and fine jig concentrate. The process is not restricted to any particular kind of ore, but is applicable to pure high-grade ores, ores high in iron, and complex zinc-lead ores, since the residue from the distillation IS held immovably in place within the briquet. In the case of complex zinc-lead ores, the distillation is conducted with a carefully regulated temperature so that a high percentage of lead is retained in the distilled briquet, which may then be smelted for its lead content. In present zinc smelting practice, the reduction fuel is from 40 to 50 per cent. of the weight of the ore. In the briquet, it is from 60 to 85 per cent. of the ore; but unless the ore is exceptionally high in residue, the distilled briquet may be used over again as coke, or as a high ash coke for fuel purposes in power production. Baked briquets are hard and tough and may be handled roughly

Jan 1, 1921

By AIME AIME

The following changes of address of members have been received at the Secretary's office during the period of Mar. 1 to May 1, 1908. This list, together with the list in Bi-Monthly Bulletin, No. 20, March, 1908, therefore, supplements the annual list of members corrected to Jan. 1, 1908, and brings it up to the date of May 1, 1908. The names of Members who have accepted election during March and April, 1908 (new members), are printed in italics., By a simple method of cutting out these names and addresses, and pasting them directly over the corresponding names in the annual list of members, the record can be kept practically up to date and the value of the list correspondingly increased. For this purpose the changes of address have been printed only on one side of the page. The names of new members, being in italics, are readily distinguished from the others, and can be pasted in approximate alphabetical order on the margins of the pages of the list.

Jan 5, 1908

By H. C. George

CAREFUL- sampling and good judgment as to probable recoveries are important factors in estimates of ore reserves, based on prospecting drilling results, but other factors are equally as important and may be more misleading and perhaps disastrous if not properly interpreted. Some of these are: 1. The case where no, ore is shown in the "sludgings," when, as a matter of fact, the drill has passed through a thick sheet of ore which has been broken up and washed away into open crevices. In numerous cases, later mining operations have shown that this has happened. This condition may be discovered by shooting the drill .hole at the point where the open crevices occur, but shooting should not be done until after the drill hole is completed, because the resulting shattered formation may salt the drill hole at lower levels. 2. The case where rich cuttings are shown for a thickness of 20 or 30 ft., when ore was encountered in only the first sludging. Owing to soft or loose formation, the ore from the first sludging has salted the lower sludgings. The presence of large pieces of ore and a similar ratio between zinc and iron assays in the lower sludgings frequently indicate this condition. In the lower sludgings, the presence of oxidized ore in unaltered limestone sometimes shows this condition. 3. The case where the drill hole shows a considerable thickness of ore; but owing to the presence of a vertical sheet of ore, perhaps not more than 1 in. thick, at the place where the drill hole is located, the good assays resulting might be misleading. If this condition is suspected, the drilling of several more holes within a distance of 10 or 15, ft. will usually show it.

Jan 1, 1921

By H. H. Kellogg

Available high-fernperatzwe equilibrium measurements and other thermochernical data have been critically reciewed for sulfation reactions of the type: Recommended values for log K and ?Fo as junctions of temperature are given for thirty-six suck reactions involving twenty-six different metals. Methods of calculation and choice between conflict-ing data are discussed. SELECTIVE sulfation now enjoys a considerable renaissance as a metallurgical unit process due, in large part, to the available of the fluid-bed re- actor—a device capable of the close control of temperature and gas composition necessary for a successful sulfation process. An additional need, however, if sulfation chemistry is to be approached in a scientific manner, is a reliable body of data on the equilibrium and kinetics of sulfation reactions in simple and complex systems. This paper offers a critical review and compilation of equilibrium data on pure sulfates (simple systems). The last such review, by K. K. Kelley in 1935:30 has proven itself most useful, but the existence of many new data makes necessary a re-evaluation of the available information. METHODS OF CALCULATION For a simple sulfation reaction such as MS04(c) = MO(c) + SO3 [1] there are two approaches one may take toward establishing the value of ?Fo or K as a function of

Jan 1, 1964