By George Oprea, Tom Troczynski, Joe A. Rigby, Waiman Lo

The refractory lining of the tuyere line in Peirce Smith converters have usually much shorter life in service than the rest of the lining, above or below it. There are already recognized chemical, thermal and mechanical factors which contribute to the wear of the lining. Our study presents the experimental results on microstructural changes occurring on these tuyere line bricks in a nickelcopper converter. The experimental bricks, after use at the tuyere line, were investigated using SEM/EDS and XRD techniques, to identify the mineralogical changes due to interactions with the nickel-copper matte or fayalite type slag at the process temperatures. The microstructural changes were correlated with physical and mechanical properties of the brick before and after use and a wear mechanism was suggested. Although the matte does not theoretically react with the mineralogical components of the brick, a partial oxidation of the Ni-Cu sulphides was identified using a line analysis by SEM/EDS in the densified layer at the hot face, which allows for mineralogical changes at the matte-refractory interfaces, with a high probability of microcrack formation due to the thermal cycling during use. These microcracks were also identified to open through inter-granular fractures parallel to the hot face, which appeared to be the main cause of lost lining during use. The reactions between the fayalite slag and refractory brick could eventually play a role in chemical dissolution of the brick only in the superficial layer at the hot face, as no slag components were identified deep into the brick.

Jan 1, 2009

By Marcelo B. Mourao

Interactions of carbonaceous materials with liquid Fe-C melts have been investigated experimentally by determining the volatile yield due to rapid devolatilization (Flash Pyrolysis) and rates of dissolution at temperatures ranging from 1623 to 1873 K. The volatile yield increased with increasing the temperature. The comparison of results of different types of carbonaceous materials was possible by expressing the volatile yield in terms of Enhancement Factor, fE. The rates of dissolution of spectroscopic graphite and an industrial coke seemed to obey the correlation for natural convection under turbulent conditions. The experimental data for the graphite suggested that the rate of dissolution was controlled by the mass-transfer in the liquid boundary layer adjacent to the solid sample. The value for the empirical parameter correlating the dissolution coefficient and the operating variables was found to be 0.19 which was close to that reported in the literature. The comparison of the results obtained for the coke samples with those for the graphite revealed that the impurities and the porosity of the samples can effect the dissolution rates.

Jan 1, 1992

By K. Mansfield

Spent Pot Lining (SPL) is an unavoidable waste product of the electrolytic process in the smelting of aluminium. SPL is considered to be a hazardous waste in various countries because it contains significant quantities of absorbed fluorides along with traces of cyanide. In 1995, Portland Aluminium undertook the investment of AUD$26,400,000 to construct a Research and Development processing facility at Portland, Victoria, Australia, to treat SPL. Extensive research, development and design were carried out over 5 years prior to the investment decision. This study led Portland Aluminium to install an Ausmelt pyrometallurgical furnace to combust and melt the SPL producing a hydrogen fluoride (HF) laden gas, which was cooled and then converted to aluminium fluoride (AlF3). Both the cooling and AIF3 manufacture were processes developed by Portland Aluminium. Many commissioning, equipment reliability and process problems have been encountered that had not been experienced in the trials at Ausmelt or in the developmental process for the treatment of the furnace offgases to form AlF3. Designs based on anticipated process expectations have had to be re-engineered by the SPL team to ensure plant and operational success. In June 2001, the installation of the final major component - a slag granulation process - was completed. This has produced a vitrified (glassy) slag that is expected to have leachability qualities acceptable to the Victorian Environment Protection Authority (EPA) to allow commercial end uses of the slag material to be developed. Today (September 2001), the smelter has successfully used the fluoride product, namely 65- 70% AIF3, in aluminium production and the SPL plant has significantly increased throughput with expectations to be at annual design rates of 12,000 tonne of SPL in early 2002. "The Alcoa Portland SPL Process" has been technically developed and is a proven process for the treatment and recovery of valuable components from SPL materials.

Jan 1, 2002

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015

By Lucas Nana Wiredu Damoah, Lifeng Zhang

"The use of electromagnetic field to remove suspended particles from metals such as aluminum by pushing to the boundary has been well studied. However, the potential of this method is yet to be exploited for the removal of inclusions from silicon. Considering the increasing amount of Top-cut SoG-Si scraps year upon year, there is the need to harness all the potentials of technologies to recycle this materials to ensure sustainability. This study investigates, and discusses new results on the effect of processing parameters such as composition, coil current, and frequency on the removal of inclusions from silicon under high frequency AC electromagnetic field.IntroductionThe solar cell silicon making industry requires pure and clean silicon in order to maximize the conversion potential of the solar cell material. The conversion efficiency of solar cells is limited by minority carrier recombination at dislocations and those intra-granular defects such as impurities, small clusters of atoms, or precipitates [1]. Recent global developments in the energy sector with a drive for the production of clean, reliable, and affordable energy have stirred a rapid growth in the production of photovoltaic (PV) cells.[2] Thus over the years, silicon based PV cells has seen a lot of growth as it has a PV market share of over 90 % [3] either as single-crystalline silicon, or multi-crystalline Si (MC-Si), or amorphous Si [4]. MC-Si produced by directional solidification of solar grade silicon melt dominates the silicon PV market. During the directional solidification process, SiC and Si3N4 particles within the melt are pushed by the solidification front to the top of the ingot which is the last to solidify. Therefore the top of the ingot is cut generating what is known as top-cut solar silicon scraps. The Si3N4 particles are mainly from the coating material at the inside surface of the silica crucible and from the air absorption during solidification process. The SiC particles mainly stem from the carbon reduction process of the primary production of silicon [5]. For sustainability the silicon in the top-cut silicon scraps must be recovered. Therefore methods for removing non-metallic particles, such as SiC and Si3N4, from the silicon are important in order to recycle the top-cut scraps to a useful feedstock for the silicon solar cells manufacturing."

Jan 1, 2012

By Rodney Hundermark, July Ndlovu, Lloyd Nelson, Phillimon Mukumbe, Paul van Manen, Whitey Seyanund, Bart Pieterse, Bertus de Villiers, Diale Mokwena

The 2003 redoubling in power to 68MW on the Polokwane Smelter furnace represented a significant intensification in platinum group metal (PGM) smelting. Combined with onerous ‘green’ PGM concentrate smelting requirements, this yielded conditions unusually corrosive to copper coolers and refractories. This presented unexpected operational and design challenges to reliable crucible operation and maintenance. Combined with specific operational control intervention, development of protective coatings has led to the life of water-cooled copper components improving from 9 to 40 months. The furnace matte endwall was extended in 2010 to address accelerated wear of refractories and the potential risk for contact of copper components by superheated matte. An 18 month planned endwall rebuild cycle has been demonstrated (versus catastrophic failure within 9 months). Finally, benefits including lower energy consumption, improved metal recoveries and higher productivity resulting from operational and in-house design developments will be described, that justify “Celebrating the Mega-scale” in PGM smelting.

Jan 1, 2014

By Christoph Sagadin

Corrosion mechanisms between high melting synthetic ferronickel slags and refractory were investigated. The used slags were prepared by mixing and melting of specific oxides. Substrates of the applied refractory material and specimens of FeNi slags were heated in a hot stage microscope up to 1650 °C. The experiments were performed under a defined gas atmosphere of 60% CO and 40% CO2. A further examination of the formed phases between slag and refractory occurred by scanning electron microscope. The investigations indicate that the slag penetrates between magnesia grains and partly dissolves magnesia. Spot analyses show that iron diffuses into the magnesia grains, which transform to magnesiawustite, meanwhile SiO2 forms different types of olivine like forsterite and monticellite. Thermodynamic calculations confirm the formation of these phases. The combination of practical lab scale experiments and thermodynamic calculations should finally contribute to an improvement of the refractory lifetime and performance.

MODELLING FOR DESIGN AND CONTROL AT KALGOORLIE NICKEL SMELTER Modelling at KNS has been driven by a need to have better tools to answer questions about control, design and optimisation of the plant. This paper describes a number of modelling tools developed for use at KNS and how the development of modelling tools fits with a design and control strategy. In the area of control, a thermodynamic model has been developed to allow process parameters to be calculated. The model allows for the automatic selection of data from a laboratory data base, desired operating set points are input and the operating parameters are calculated. The model has the ability to adjust the burner efficiency and the furnace heat loss depending upon conditions. To assist with the testing of proposed furnace design changes, various mathematical models of the burner and shaft have been created using PHOENICS. These models are particularly well suited to combustion heat transfer and flow aspects of both the burners and shaft. Validation of these models have been based on novel sampling and measuring techniques in the shaft and also by using scale and cold models. Overall plant energy and cost structures can be analysed using a flowsheet simulation, developed to evaluate potential alterations to the plant flowsheet. This model system allows the global evaluation of process changes.

Jan 1, 1993

By H. Doostmohammadi

During the tapping of liquid steel from Electric Arc Furnace (EAF), some slag is carried over into the ladle. High levels of FeO and MnO in slag carryover increase the oxygen activity in steel melt leading to oxide inclusion formation during the ladle treatment. The demand on cleaner steels requires minimization of carryover slag. In this work, the effect of EAF slag carryover on ladle slag-steel equilibrium calculations for a hot working tool steel was studied. Steel and slag sampling were done in Uddeholm Tooling AB in Sweden. XRF and OES techniques were used to determine chemical composition of samples. The quantity of slag carryover was calculated based on a mass balance followed by thermodynamic calculations on metal-slag equilibrium using Thermo-Calc software. The agreement between predictions and experimentally determined compositions was good. This leads to the development of a prediction method for optimizing the production of other tool steel grades.

Jan 1, 2009

By J. L. Watson

The composite nature of titanomagnetites found on the west coast of the north island of New Zealand is an important parameter in the beneficiation of the black beach sands for export to Japan. To investigate this composite nature, borehole and plant samples from the Waipipi Ironsands Ltd property were subjected to a series of separations in heated Clerici solutions at densities varying from 3.2 to 4.6 g/cc. The resulting density fractons were analyzed magnetically and a set of distribution curves for composite grains proposed. In addition the experi¬mental data was plotted to produce titanomagnetite sand 'washability curves" which illustrate the possible problem areas in beneficiation that may arise due to composite titanomagnetite grains. From this data a set of guidelines are suggested for interpreting the curves in terms of ease of gravity concentration. The composite nature or liberation of titanomagnetite grains is shown to favor high and low grade composites with few intermediate compositions being isolated. The relationships between grain size, borehole depth and liberation are examined and related to beneficiation procedures for the black sand deposit.

Jan 1, 1982

By Jilai Xue, Jun Zhu, Baisong Li

"TiB2-C/C Function Gradient Materials (FGM) is used in cathode materials to improve aluminum wettability and melt penetration in aluminum electrolysis. In this investigation, FGM was tested for use as part of the cathode materials, where a 10 mm thick TiB2-rich layer was on the top as an Al-wettable surface, the TiB2-C layers in the middle as a gradient layer and the carbon on the bottom as a base. Electrical resistances ofFGM were determined in the temperature range of25- 9600C in argon atmosphere. The results show that the present of TiB2-C gradient layer can reduce the open porosity and the electrical resistance of the cathodes materials at elevated temperatures. The cathode samples after aluminum electrolysis usually demonstrates an increase in electrical resistance, but the application of FGM layer can compensate such an increase for certain extend due to less variation in porosity and lower the level of melts penetration.IntroductionCarbon is still used for aluminum reduction cathodes dominantly, but it has a poor wetting properties by liquid aluminum and the anode-cathode distance has to be kept about 4-5cm with an additional 1.3-2.0 V voltage drop [l]. TiB2 has better wettability by liquid aluminum with higher electrical conductivity and stronger chemical resistance to the electrolyte attack. And the wettability ofTiB2-C composites cathode on liquid aluminum can be also improved, while liquid aluminum can completely wet the cathode surface ifTiB2 content exceeds 27% [2-4]. However, during the process of TiB2-C composites cathodes preparation and aluminum electrolysis, the deformation by temperature variation or sodium penetration are great disparity between TiB2 and carbon due to their physical properties difference. This will accelerate the cathodes cracking and deterioration."

Jan 1, 2013

By Noel A. Warner

Modern steelmaking is based on direct use of oxygen in high intensity batch reactors. A totally new approach is proposed in this paper, based on the view that pursuit of high intensity is unlikely to lead to successful coal-based continuous steelmaking. By substituting carbon dioxide and water vapor as the oxidants rather than using oxygen directly, the intensity is greatly reduced. Accordingly. subsurface formation of carbon monoxide bubbles can be avoided by careful manipulation of the three participating rate processes, gaseous diffusion, interfacial chemical kinetics and liquid phase mass transfer. Steelmaking can then be carried out without explosive ejection of molten droplets and the generation of micro-spray but rather in a controlled and fumeless fashion. The vital component is the introduction of generic melt circulation technology. Three melt circulation loops in series are envisaged. Starting with a composite feed of iron ore fines, pulverized coal and lime flux, a metallized solid raft floating on molten iron is propelled out of the ironmaking loop onto the first of two downstream steelmaking loops. In the first, a liquid slag is formed, primary decarburization is undertaken not with oxygen but rather with CO2 and H2O and the melt is desulfurized. The semi-product stream enters the third melt circulation loop, where open-channel decarburization is effected along with dephosphorization to yield a low carbon steel product. Alternatively, the melt leaves the last loop to irrigate a packed tower countercurrent to argon at around 100 mbar to continuously produce ultra-low carbon (ULC) steel.

Jan 1, 2003

By O. Durand

The Cerro Verde Hydrometallurgical Plant, located at Arequipa in the southern part of Peru, started its operation in 1977 with a design capacity of 33,000 MT/year of copper cathodes. The plant has treated 61,055,000 MT of ore mainly oxides with a content of 1.01% total copper and 0.67% of soluble copper. The leaching plant has three pads that produce 4.0 gpl copper solution. The solvent extraction plant has four trains with three extraction stages, two stripping stages with a single mixer in all stages. The mixer-settlers are 316 stainless steel and the pumps are vertical turbines. The flowrates of 1,300 gal/mil of aqueous and 1,300 gal/min of organic at a 1/1 ratio. The electrowinning plant contains 208 commercial cells and 18 starting sheet cells. Each cell has 47 anodes and 46 cathodes. In addition to describing the hydrometallurgical plant, this paper also mentions efforts directed at reducing costs and improving operations. The initial results from leaching secondary sulfides, which started October 1985, are also discussed.

Jan 1, 1987

By Hadi Fanisalek

"Most industries attempted to conduct their energy consumptions in an optimized way for a few decades. This is because policymakers and top managements in industries have felt the critical situation of a possible energy shortage that could happen for them in the near future, even in countries with significant fossil fuel resources. Decisions related to energy consumption in any industry will have a long-term effect on different parts of the industry structure. In this way, energy decisions should be categorized as part of any industry's main strategic and long-term decisions, which should be made by top strategists. On the other hand, strategic management has many powerful tools to help the policymakers in industries to establish a long-term strategy for energy consumption and reducing or preferably eliminating the energy loss. This will be more important for industries in the Middle East, where they have just started to make an applicable strategy for their energy consumption and to design a long-term procedure for their energy management. Based on strategic management and by comparison we designed and offered a new model for establishing the main structure of energy management strategy in primary aluminum industry, which is a high consuming energy industry. This strategy, which we will call ESM (Energy Strategic Model) and has been applied for a typical primary aluminum industry in this paper, is similar to the practical models in the field of strategic management, which were developed for designing the overall company strategy.IntroductionThe elementary goal for introducing strategic management in any organization was to establish a successful plan helping the company to survive and to gain competitive advantage over its competitors in a rough business environment. Strategic management is an ongoing process that evaluates and controls the business and industries in which the company is involved; assesses its competitors and sets goals and strategies to meet all existing and potential competitors; and then reassesses each strategy annually to determine how it has been implemented and whether it has succeeded or needs replacement by a new strategy to meet changed circumstances, new technology, new competitors, and a new economic environment[!]."

Jan 1, 2013

By Xiangjun Zuo

This paper firstly reviewed the state of the art in the recycling of used Printed Wiring Boards (PWB), and then presented part of the authors study on the combustion of PWB powders with and without the addition of catalyst. During the combustion of PWB powders without catalyst addition, there were two obvious exothermic reactions, one at 300-380oC, the other at 450-500oC. With the addition of catalyst during PWB combustion, there were no obvious exothermic reactions, indicating that dehalogenation reactions are not exothermic: The results showed that NaHCO3 and CaCO3 were very efficient to control the emission of Br2 and C6H6, lowering 80% compared to the case without catalyst, Na2CO3 can slightly control the emission of Br2 gas but not for C6H6 gas mission, and NaOH has no any effect of the control of both gases.

Jan 1, 2009

By Thomas E. Weyand

Prior to 1975, lead-based paints were commonly used in protecting steel structures. Because of the toxic effects of lead on human health and the environment, their use has been significantly reduced. However, problems with these paints persist when they are removed during normal maintenance by pneumatic blasting with mineral abrasives. Technologies are developed to contain the spent abrasive and paint during blasting operations. This paper reports on A study to identify beneficial reuses for the spent blasting material. Nine samples were gathered from different projects within Pennsylvania. The samples were thoroughly characterized with regard to composition, morphology, and EP and TCLP leach test performance. Potential reuse applications will be reviewed with regard to technical adequacy, economics, and environmental constraints.

Jan 1, 1992

By Shengli Wu, Feng Chang, Hua Lu, Jianliang Zhang

Kinetic studies of the blast furnace dust (BFD) reduction process have been carried out under non-isothermal conditions. BFD pellets were made with bentonite as the binder. A Comprehensive Thermal Analyzer (TG-DSC) was used to determine the mass loss of pellets, which were heated at three heating rates of 10, 20, 30 K/min up to 1493 K. Furthermore, the metallization rate and mineral composition of BFD pellets heated to several different temperatures were analyzed by chemical analysis and X-ray diffraction (XRD). It was found that, with its inherent carbon resources as the reducing agent, the metallization rate of BFD pellets could reach 88% at most. The reduction and weight loss process of iron oxides mainly happens above 1273 K. In addition, from application of the Coats-Redfern equation the apparent activation energy of the reduction from wustite to Fe was 443 kJ/mol and the mechanism was interface reaction R..

Mar 1, 2017

By Mototsugu Matsuno

A new process has been developed to treat fly ash generated from municipal incinerators, which contains not only toxic metals such as lead and cadmium, but also dioxins. The process includes the following steps; fly ash is formed into green pellets with some additives and the pellets are then roasted to eliminate or stabilize the toxic metals and to decompose dioxins. A pilot plant with a capacity of approximately 100 kg/hr was used to test the process. The tests verified that heavy metals were either volatilized or stabilized and dioxins were decomposed by high-temperature roasting. The pelletized ash was found to be non-toxic, so that it can be recycled as artificial lightweight aggregate. It was also found that volatilized metals collected as secondary ash can be recycled as smelting resources.

Jan 1, 2003

By Ricardo A. Valls

The Sechol Nickel-Cobalt Laterite Project is located in East-Central Guatemala, 140 km northeast from Guatemala City. In-situ resources in the immediate Sechol area, including those on other mining concessions contain 133 million tonnes of mineralization, grading 1.5 1% nickel. Considering the ever-increasing market for these metals, and the potential quick return on the initial investment, Jaguar Nickel Inc. is confident that by late 2006, it will be producing the first nickeltcobalt hydroxides from Guatemala. The path from now until the production stage passes through a pre-feasibility study, scheduled for completion by mid 2004, and bankable feasibility by mid 2005. Jaguar's objective, however, is not only to have a producing nickel-cobalt mine by late 2006, but also to continue with the exploration work in order to make Guatemala one of the world's leading nickel-cobalt producers. The Sechol group of deposits is conformed of several lateritic pockets, delimited by tectonic faults, and hosted by ultramafic rocks of the Sierra de Santa CW. ophiolitic belt that intruded the Maya Continental Block during the Early Tertiary age. The intrusive is mainly represented by a layered sequence of dunites, peridotites, and pyroxenites, usually strongly serpentinized. Existing data indicate that these rocks underwent fractional crystallization, and probably some degree of magma mixing and contamination previous to their main tectonic event. The most complete profiles are usually present over weathered dunites and serpentinites, while on top of the less altered pyroxenites, there is usually the formation of only a limonitic zone. The relative complexity of the ophiolitic belt explains the variety of mineral resources in the area, which include Ni-Co-Fe laterite, chromite, bauxite, magnesia, and also has the potential for gold, PGMs, and precious and semi-precious stones such as jade, nephrite, and chrysoprase. Metal recovery from the Sechol deposit will be based on an atmospheric chloride process, followed by solution purification, production of an intermediate nickellcobalt hydroxide suitable for sale, and finally acid and magnesia recovery by standard spray roasting technology. The chloride process will allow exploitation of the whole lateritic profile to produce 20,000 Mt of nickel hydroxide and 800 Mt of cobalt hydroxide per year. The exploration work completed to date has concentrated mostly on the Sechol group of deposits, representing less than 5% of the current land position of Jaguar in Guatemala. Within Sechol, the company has identified a large pocket of more than 5 Mt of laterites grading 2.1% nickel and 0.08 % cobalt as a startup pit "El Inicio". Including the work previously completed Keywords: Laterite deposits, Ophiolitic Belts, Central Guatemala, Nickel, Cobalt

Jan 1, 2004

By Hiroyuki T. Takeshita

Ca-Ni based alloys were investigated on structures, hydrogenation properties and the effect of additive elements on hydrogenation properties. CaNi, samples were decomposed to form a new hydride with a CsCl-type structure on the constituent metal atoms at high temperatures such as 673K in a hydrogen atmosphere. The candidate of the third element which was added to stabilize the original compound was investigated by using the Miedema's semi- empirical model and, as a result, Pd was chosen. The hydrogenation of CaPd was conducted with a Sieverts' type apparatus and the synthesis of Ca-Ni-Pd ternary alloys was performed by high frequency heating.

Jan 1, 2002