By Shan He, Qiang Wang, Xuling Chen, Min Gan, Lishun Yuan, Xiaohui Fan

"The sintering properties of vanadium-titanium magnetite concentrate(VTC) was studied in this paper. Through the optimizing the sintering process of VTC, the suitable granulation moisture and coke proportion were determined. The sintering velocity decreased from 23.05 mm/min to 18.22 mm/min. With the increase of VTC proportion from 0 to 46%, the specific productivity and tumbler index were respectively decreased from 1.55 t/(m2·h) to 1.21 t/(m2·h), and 62.93% to 57.73%. The temperature of liquid phase formations of mixtures increased, the amount of liquid lowered, and the content and sharp of sintering mineral gradually changed with the increase of VTC ,these lead that sinter quality became worse.IntroductionIn recent years, the steel industry of China is developing rapidly. And the steel production was 627 million tons in 2010. At present, the resources of vanadium-titanium magnetite concentrate(VTC) was about 14.4% of the total national iron reserves of China[1]. VTC has been used as sintering material by Magang, Chenggang and Pangang. The amount of VTC in Pangang is maximum. However, there exist many problems in VTC sintering, which involve in high specific productivity, bad sintering tumbler strength and high energy consumption[2~5]. That’s why the proportion of VTC is limited in sintering.The high quality of iron ore resources is worse in China. Therefore, it’s necessary to study the properties of VTC sintering, and to find out the reason how the VTC ratio affect the sinter performance. Purpose and significance of the research is to get high-quality sinter with the proportion of VTC greatly raised."

Jan 1, 2012

By Jitka Jandová

In this study, hydrometallurgical processing of waste ZnO flue dust arising during zinc removal from galvanized low-alloy steel sheets was investigated on a laboratory-scale to obtain electrolytic zinc. The flue dust was separated from flue gases, generated during heating waste galvanized steel sheets in an electric furnace under air atmosphere at temperatures of about 1000oC. The dust, comprising tetragonal ZnO and insignificant amounts of SiO2, was contaminated by Fe, Mn, Pb, Al, Mg, Pb, Cu and Ca. The dust was leached in 0.5 and 1.0M H2SO4 and/or in 20 and 30% NaOH at different temperatures and different liquid-to-solid ratios to determine the optimum conditions leading to the highest possible selectivity of leaching and efficiency of Zn extraction in minimum time. The subsequent electrowinning process was performed with refined zinc sulphate leach liquors and/or with untreated zinc caustic solutions. Zinc sulphate leach liquors were purified using a combination of a hydrolytic pH-controlled precipitation, cementation and carbon refining. Effects of operational variables on Zn electrowinning have been studied for both sulphate and caustic electrolytes. The conventional plate-plate electrowinning cell has been explored in this study. Comparison of results obtained for both zinc electrowinning from acid sulphate and alkaline solutions is presented contribution.

Jan 1, 2003

By F. Mucciardi

With the increasing trend to continuous smelting and converting, granulation of copper matte is gaining prominence as a means of decoupling the smelting and converting operations. Moreover, granulation is also being seen as a possible avenue to using higher grade oxygen in converters. By feeding cold solid matte, the oxygen concentration can be increased to compensate for the lower enthalpy feed. This leads to a higher grade of SO2 in the off gas and a lower total flow rate. Current granulation technology relies on the cooling of a falling matte film by water jets. This technology while effective has several drawbacks including those related to safety. Noranda and McGill University have developed a new process (patent pending) for solidifying copper matte (or slag). It overcomes many of the negatives of current technology. The system is based on an air cooled twin roll caster. This: new system uses no water and instead incorporates heat pipe technology to transfer the heat from the solidifying matte to the cooling air to produce a thin strip of 1 to 2 mm in thickness. Testing of a prototype unit demonstrated its viability. This paper describes this newly developed, twin roll casting system that is completely waterless. The advantages of this process as well as the findings from several tests are also detailed.

Jan 1, 1999

By Tetsuya Uda, Sakae Shirayama

"With the aim of producing nickel (Ni) metal directly from acidic aqueous solution containing cobalt (Co) and other impurities, selective reduction of Ni was examined. As a preliminary experiment, sodium hypophosphite monohydrate (NaH2PO2·H2O) was selected as a reductant, and reacted with aqueous solution containing 0.1 mol L-1 nickel sulfate (NiSO4·6H2O) and 0 ~ 0.05 mol L-1 cobalt sulfate (CoSO4·7H2O) for 3 hours at 90 °C. As a result, it was revealed that Ni was selectively reduced and separated from Co in the acidic region (pH= 4.8). In this study, differences of reduction behavior between Ni and Co were investigated, and the feasibility of Ni I Co separation by the selective reduction of Ni was discussed.IntroductionEfficient Ni condensation and separation from Co are essential in nickel hydrometallurgical processes. Currently, the hydrometallurgical production of Ni from oxide ore is mainly carried out by acid leaching at elevated temperature, followed by the removal of impurities using neutralization, and condensation of Ni and Co into intermediate products such as hydroxides and sulfides. Then, the intermediate product is dissolved in acid aqueous solutions, and Ni I Co separation is conducted by solvent extraction. Finally, Ni and Co are recovered by electro-winning. This complicated process consumes large amounts of alkali, hydrogen sulfide (H2S), and organic solution in a multiple-staged process'. To reduce the consumption of these chemicals, it is important to recover Ni more efficiently from acidic aqueous solution containing impurities."

Jan 1, 2014

By Mingming Zhang, Ramana G. Reddy

"Carbon dioxide (CO2) is one of the most common by-products produced during light metals production. It is considered to be the cause of greenhouse effects. Efficient reduction of CO2 can help minimize the rate of global warming and improving energy sufficiency. In this paper, a novel light metal production process was developed using ionic liquid electrolytes. This process has significant advantages compared to the traditional high temperature processes such as zero CO2 and CF4 emission, low energy consumption due to the low temperature operation and nonconsumable electrodes. Two types of anode materials (graphite, extruded carbon) were tested in electrolysis experiment. The results showed that both anode materials were stable (negligible weight loss). However, the extruded carbon was found to be superior to graphite in terms of current density and current efficiency. The calculated energy consumption for aluminum production was less than 10 kWh/kg at current densities up to 300 A/m2.IntroductionGlobal demand for ultra-light, ultra-strong, recyclable metals is growing as the world switches to low-emission vehicles, energy-saving devices and sustainable products. Aluminum demand is forecast to climb by 30 percent; magnesium demand by 200 percent, while for the emerging industrial light metal, titanium, the demand is expected to be at least double in the next decade. However smelting of light metals is the most energy intensive among all the steps of light metals production. For example, on an average it takes about 15.7 kWh of electricity to produce one kilogram of aluminum from alumina [1, 2, 3]. Advancements in energy efficiency have been steady, but slow, and most U.S. aluminum smelting production operates at 95% current efficiency. Besides high energy consumption, another major concern of the light metals smelting process is the emissions of greenhouse gases (GHG). Electrolysis green house gas emissions in the Hall-Héroult process can be split into three groups: 1) reduction reaction emissions, carbon dioxide (CO2) and carbon monoxide (CO); 2) process upset perfluorocarbons emissions; and 3) hydrogen fluoride (HF) formed from the moisture (H2O) present in the raw materials [2, 3]. Hydrogen fluoride gas can be captured and returned to the cells by the alumina dry scrubbing system used in modern facilities. A total of 5.31 kilograms of CO2 is generated from the reduction process for each kilogram of aluminum produced in the average U.S. primary facility. The perfluorocarbon emissions are related to the “anode effect.” If the concentration of alumina in the bath becomes too low, other reactions between the carbon anode and the bath occur and tetrafluoromethane (CF4) and hexafluoroethane (C2F6) are generated. These gases have high global warming potentials (GWP), which is a ratio developed to compare the ability of each greenhouse gas to trap heat in the atmosphere relative to carbon dioxide"

Jan 1, 2008

By Kanchan Mondal

"Methanol, lower hydrocarbons, CO, and HCOOH formation have been by the reduction of CO2 with H2. Un-catalyzed electro-reduction requires a significant overvoltage. An alternate route has been conceptualized. Production of hydrogen from water can be achieved by chemical oxidation of a metal in water followed by oxidation of the hydronium ion by the released electrons to form hydrogen radical. It is hypothesized that circumventing the problem of the formation of hydrogen molecule is essential while having the hydrogen radical to react with CO2 forming methanol, etc. This may be possible by a bimetallic catalyst acting as a galvanic couple, wherein one metal acts as the electron donor for the production of hydrogen radical while the other acts as a catalyst for the reduction of CO2. This may enhance the reaction rates. The current concept circumvents the need for an external electric field unlike the electrochemical process.IntroductionUtilization of carbon dioxide as a raw material, not only as carbon sources but also as useful chemical feedstock is a more holistic approach to reduce air pollution by flue gases (1-3). Several methods have been proposed to maintain the concentration of atmospheric CO2 or to reduce and recycle it. One of these is the chemical fixations using catalysts. The conversion of CO2 to methanol by hydrogenation over copper containing catalysts is one of the most widely studied subjects in this area. The limitation in this reaction is the low conversion of CO2."

Jan 1, 2008

By K. P. V. Lei

The U.S. Bureau of Mines investigated a hydrothermal sulfidation procedure to recover lead and silver from plumbojarosite. The plumbojarosite, generated during pressure-oxidative leaching of zinc concentrate in a commercial operation, contained, in percent, 25.4 pb, 18.8 Fe, 1.4 Zn, 29.5 SO,2-, 3.2 s?, 13.4 total sulfur, and 7.4 oz/ton Ag. The sulfidation was conducted in an autoclave and converted the plumbojarosite to amorphous iron oxide and liberated the lead and silver as sulfides. The best operating conditions were using 50 9 of plumbojarosite and 7 pct s? (2.04 9 S? added) in 500 mL of 2.0 mol/L NH3, 150? C, and 1 h. The sulfidation product contained, in percent, 37 Pb, 28 Fe, 6 S2-, 2 SO,2-, and 11.2 oz/st Ag. Ferric chloride leaching extracted 98 pct Pb and 97 pct Ag from the sulfidation product.

Jan 1, 1990

By Dong Hoon Han

The simultaneous sulfation by sulhr dioxide and oxygen of CaO and MgO in calcined CMA (calcium magnesium acetate) were investigated. he experiments were carried out in the temperature range from 700 to 830 "C and at the SO2 concentrations of 0.3 to 1 mol %. The oxygen concentration was kept at 5 %. Each sample was calcined completely before the temperature was lowered to the sulfation temperature. According to the ranges of partial pressure of sulhr dioxide and temperature, there exist three regions for the sulfation reaction: region I in which neither oxide is sulfated, region I1 in which only CaO is sulfated, and region 111 in which both oxides are sulfated. It was shown that the MgO in calcined CMA is sulfated at a rate comparable to that of CaO by forming a mixed sulfate phase. Thus, unlike MgO contained in other desulhrization materials, the MgO content in calcined CMA can be fully utilized for flue gas desulhrization.

Jan 1, 1999

By M. E. Ramos Rada

Mexicana de Cobre, which is part of Grupo Mexico, carried out studies for the construction of a copper refinery in the La Caridad Metallurgical Complex located in Nacozari, in the state of Sonora, Mexico. After the studies were concluded, the decision was made to construct a 180,000 t/y refinery using the state of the art permanent cathode Kidd Process. The basic engineering was developed by Fluor Daniel and the detail engineering and the construction were carried out in record time by the Mexican company Bufete Industrial. During the construction phase, Grupo Mexico decided to expand the refinery, and actions were taken to increase its capacity by an additional 120,000 t/y; the final result was a refinery capable of producing 300,000 tonnes of grade A cathode per year. Construction began in January 1996, and the operation of the first stage began on July 1, 1997. The operation of the second stage commenced on January 7, 1998. The capacity of the first stage was reached in November, 1997 and the total capacity of the refinery was achieved in May, 1998. This presentation describes the process and equipment installed in the refinery, the steps leading to the start-up, the operation and the results obtained during the first two years, the handling of anodes with high impurity contents, and the problems confronted and the way they have been solved. It also includes personnel productivity, the control parameters and the most relevant data on the operation of the process.

Jan 1, 1999

By Sunil Jayasekera

This paper describes the results of a study carried out to examine the feasibility of electrolytic recovery of silver from cyanide leach liquor generated from a Western Australian silver mine tailings using a novel high mass transfer electrowinning cell. The proposed circuit involves heap leaching and electrowinning in a closed loop. The filter-press-like closed electrode arrangement of the cell allowed much improved mass transfer of metal ions to the cathode surface, making direct electrowinning of metals from dilute solutions feasible. The tests were conducted both in the laboratory and at large scale using a prototype with ~1.0 m2 cathode area. The results showed that the recovery of silver from as low as 250 mg L-1tenor was feasible. The silver deposit produced with the prototype cell was non-adherent and powdery and could be readily removed from the closed cell. A system was developed so that silver powder was discharged continuously during the run.

Jan 1, 2003

By Corby Anderson

The efficient separation of palladium from the transition metals copper, nickel and iron can be effected by passing a leach solution of these metals through a column of the silica polyamine composite material, WP-1, patented by Purity Systems Inc (PSI), Assignee, University of Montana with exclusive license to PSI. The separation can be done at the intrinsic pH of a nitrogen species catalyzed (NSC) oxidative pressure leach solution (~0) and stripping of the palladium from the composite can be effected with hydrochloric acid/ammonium chloride solutions at 50oC. Batch capacities of the composite for palladium are ~ 1.8 mmol/g resin. The possibilities for isolating the metal from the strip are discussed. Given the proven longevity and rapid capture kinetics of the polyamine composites, this new approach should prove to be an economically viable alternative to the multi-step concentration processes practiced in the PGM industry to date.

Jan 1, 2003

By G. Roy Chaudhury

Adsorption techniques are comparatively low cost and effective for treatment of arsenic contaminated drinking water. Various adsorbents such as alumina, ferrihydrite and manganese ores have been used, but there has been little investigation of modifying the structure of ferrihydrite to improve its adsorptive efficiency of As(III) and As(V). In the present study the incorporation of manganese oxide into the ferrihydrite structure was carried out and the prepared materials used in arsenic adsorption experiments. The compounds were X-ray amorphous, but TGA/DTA and FTIR analysis showed some structural characteristics. Sorption studies reported in this paper indicate the excellent arsenic removal properties of the manganese/iron compounds with a loading capacity of 0.3 mmol/g. Adsorption follows first order kinetics and the results fitted to adsorption and mass transfer models. Arsenic levels in water containing 1 mg/L As(V) were reduced by 50% in 20 minutes and 90% in 60 minutes using 1 g/L manganic ferric oxyhydroxide.

Jan 1, 2003

By Ralph P. Hackl

Bacterial leaching of the Doe Run Company?s cobalt/nickel-containing copper concentrate at low pH (pH 1.0-1.2) and high redox potential (>750 mV vs. SHE) enabled the cobalt and nickel to be preferentially dissolved over copper and iron due to the rapid passivation of the chalcopyrite component. Selective leaching of the cobalt and nickel was achieved with a mesophilic culture comprised mainly of Leptospirillum-like bacteria and Acidithiobacillus thiooxidans. This finding led to the conception of a novel hydrometallurgical process for passivating chalcopyrite and recovering the cobalt and nickel. The bacterial leaching process was tested extensively at the bench and pilot plant scales during 1997-1998. A pilot plant containing four leaching stages processed 30-40 kg/day of chalcopyrite concentrate continuously for 87 days. The cobalt extraction ranged from 75% to 86% during 6- and 8-day retention times respectively, whereas the copper extraction was limited to about 9%

Jan 1, 2003

By Arvind Thekdi, Cynthia Belt2

"Waste heat from industrial operations in metals industry represents 20% to 50% of the total energy used in most manufacturing plants. Reduction and recovery of waste heat offers the most attractive and cost effective method of reducing energy intensity for an industrial plant to meet corporate energy saving goals. It is possible to reduce or recover 30% to 60% of the available waste heat by using conventional and readily available technologies. Projects to reduce or recovery waste heat may offer less than 3 years payback to as short as a few months. This paper presents information on most commonly used methods for waste heat reduction and recovery in the metals industry operations. It describes the methods and use of analysis tools that would allow a user to estimate energy savings, CO2 or GHG reduction potential, and economic benefit and includes appropriate case histories.Waste Heat SourcesSources of waste heat abound with the metals industry. While the overall quantity of energy is high, the sources are distributed throughout a plant. The largest source within the metals industry is within furnace exhaust / flue gases. This includes the high temperature gases from burners in process heating such melting, calcining, and sintering operations. It also includes lower temperature gases from heat treat, dryers, and heaters. Lower temperatures are also found after post processed hot gases. This could include heat left after heat exchangers, regenerative systems, thermal oxidizers, and emission control systems. Other hot gases include air used in direct and indirect cooling.While waste heat in form of exhaust gases is readily recognized, waste heat can also be found within liquids and solids. Waste heat within liquids includes things such as cooling water, heated wash water, and blow down water. Solids can be hot product at discharge after processing or reactions are complete. Indeed, not only is energy wasted in the hot metal that slowly air-cools, but additional energy may be used in providing air or water-cooling to increase the speed of cooling. Other waste heat sources are not as apparent and include things like hot surfaces, steam leaks, boiler blow down water, etc. Table 1 and Figure 1 show several major sources along with the temperature range and characteristics of the source."

Jan 1, 2011

By M. Rockandel

"Universal Dynamics Ltd. of Vancouver, Canada has developed, patented and commercialized the ""REMERC"" process for the treatment of mercury contaminated sludges and soils. Mercury is extracted into an acidified and oxidizing, sodium chloride brine solution. REMERC was initially developed to treat mercury contaminated EPA listed wastes (K106) generated by the chlor-alkali industry. More recent work has expanded the capability;' of REMERC to include remediation of mercury contaminated sites, equipment and building materials.In the process mercury is currently recovered from solution by cementation on iron powder in an agitated reactor. The process recovers high purity elemental mercury (99.9% purity). Cementation typically recovers about 90-95% of the mercury in 30 minutes. Higher recovery is not necessary because of the recirculation of the leach solution. When treating highly contaminated chloralkali wastes (5-13% mercury content), REMERC will reduce the mercury laden solutions from 400-1,000 mg/L mercury to 50-100 mg/L. In the treatment of less concentrated wastes «1,000 mg/kg mercury) such as those encountered in site remediation, the treated solutions will generally contain 10-20 mg/L mercury. Cementation while being simple and able to achieve the required recovery has the. undesirable properties of; requiring a solid-liquid separation and adding iron to solution which must be precipitated, ultimately increasing the weight of residue to landfill. .The potential advantages of electrolysis were recognized early in the development of REMERC. Mercury electrolysis is well known in gold and chloralkali processing. Initial testwork utilized a liquid mercury cathode and a coated titanium anode both common to chloralkali producers. The mercury cathode appeared susceptible to polarization and solution impurities significantly affected performance. Agitation of the mercury pool improved performance but it was still not possible to achieve the reduction objectives. Current efficiencies were low, near 10%, and it was apparent that a relatively large cathode pool would be required to limit the current density. A number of electrode combinations with and without a membrane were then tested in a vertical electrode' configuration but the desired performance was not obtained."

Jan 1, 1997

By K. A. Lewandowski

Agglomeration of ore can be used to immobilize fine particles during heap leaching by agglomerating them into granules. Without agglomeration, the fine ore particles can migrate within the heap, clogging flow channels and producing large areas where access of solution to the ore is very poor. The benefits of agglomeration are well-known in gold heap leaching operations, which can be effectively agglomerated using binders such as Portland cement due to the alkaline leaching solutions used. However, agglomeration has not been very effective in the heap leaching of copper ores, because these ores require an acidic leaching solution. Acid destroys the effectiveness of most binders, causing the agglomerates to disintegrate as soon as the leaching solution is applied. In order to gain the benefits of agglomeration in copper heap leaching, an economical, acid-resistant binder is needed. The two issues that needed to be addressed were: 1) Lack of effective methods for evaluating binder acid resistance before performing expensive, time-consuming, full-scale heap leaching tests, and 2) The vast majority of known binders react poorly to acid conditions, and so a basis was needed for determining which binders are most likely to be acid-resistant. In this paper, the development of two new tests for evaluating binder acid resistance in the laboratory are described. The ?soak test? determines the degree to which agglomerates disintegrate and release fines on contact with acidic solution, measuring the relative quantities of fines released by agglomerates made with different binders under controlled conditions, and serves as a rapid means for comparing large numbers of binders. The ?percolation test? measures several different parameters to determine how a binder is likely to perform in heap leaching: 1) the degree of ?slump? and compaction of agglomerates as they are wetted by acidic solutions; 2) the hydraulic conductivity of the agglomerate bed; 3) the migration of fines through the bed as the solution flows through it; and 4) the quantity of liquid retained in the agglomerates after they are drained. Using these tests, a broad spectrum of binders were examined. Soak testing determined that the most acid-resistant binders were nonionic polymers. Five of these binders were further evaluated using percolation testing.

Jan 1, 2006

By P. Chris Pistorius

"Use of coke in blast furnace ironmaking is the main origin of carbon dioxide emissions from integrated steelmaking. Use of pre-reduced iron feedstocks would reduce the coke rate and, if pre-reduction were carried out with natural gas, would decrease the overall carbon intensity of ironmaking. Blast furnace productivity would also increase, because the blast volume per unit of hot metal would decrease. This paper shows that these trends can be predicted quantitatively, by using a conceptually simple Rist-style blast furnace mass and energy balance, assuming furnace productivity to be limited by the tuyere gas flow rate. Such predictions would assist in optimizing the choice of the degree of reduction and relative amount of pre-reduced blast furnace feed.IntroductionSteelmaking is responsible for some 5% of world CO2 emissions, at a rate of approximately 1.9 tonnes of CO2 per tonne of cast steel [1]. In integrated steelmaking, the ultimate source of most of the CO2 emissions is coke, the indispensible (and expensive) fuel and reductant for blast furnaces. There are several research programs underway worldwide which seek to lower the carbon intensity of ironmaking; one of the largest is the European ULCOS program [2], in which the main proposed change to blast furnace ironmaking is to scrub CO2 from the furnace off-gas (for possible sequestration), recycling the remaining gas to the furnace. To limit the recycling nitrogen load, oxygen rather than air is used to combust coke.A conceptually simpler approach is to charge prereduced feed (direct-reduced iron) to the blast furnace. This approach has been used for some two decades at the AK Steel Middletown plant, where some 200 kg of direct-reduced iron (DRI) is charged per tonne of hot metal [3]. The Middletown blast furnace has exceptionally high productivity (rate of iron production relative to the furnace hearth area), simply because less coke is required per ton of hot metal if part of the feed is already metallic. Midrex [4] has provided some quantitative predictions of the implications of DRI use in the blast furnace, stating that for every 10% of Fe in the feedstock that is in metallic form, the fuel requirement decreases by 7% and the productivity increases by 8%."

Jan 1, 2012

By G. P. Chaudhari, F. Warchomicka, M. Dikovits, V. Pancholi, C. Poletti

"The hot formability of a microalloyed steel with 0.16 wt-%C modified with N is studied by using processing maps. Compression tests of cylindrical samples are carried out using a Gleeble®3800 simulator in the range of temperature between 750 -1000°C and strain rates between 0.01-100 S-1. For this alloy, an Ar3-temperature about 740°C is determined by means of dilatometry. Processing maps are calculated using the modified dynamic material model developed by Murty and Rao for different logarithmic strains. For the instability map, the parameter Kj developed by the authors in previous works is used and compared with other instability values. Softening in the flow curves provoked by induced ferrite during deformation at low temperatures and low strain rates is reflected in the n-value. Light optical microscopy (LOM) and electron back scattered diffraction (EBSD) measurements are used to study the microstructure of the hot deformed samples to determine the deformation mechanisms active and to verify the processing maps.IntroductionProcessing maps offer a good possibility to optimize thermomechanical process parameters and to avoid defects in the products. Prasad et al. [1] developed the processing maps using the dynamic material model (DMM) and Murty & Rao [2] modified it. Processing maps consist of two superimposed maps: the dissipation efficiency and the instability map. The processing maps can be used to detect areas with a good hot formability, which are normally related to restoration of the material by dynamic recovery/recrystallization. For a high dissipation efficiency value and no instabilities, a good hot formability is predicted. In the DMM no storage of energy takes place and so the material is considered essentially dissipative, this is only true for high temperatures and high strain rates [1]."

Jan 1, 2012

By Artur Camposo, Rômulo. L. Loiola, Frederico M. Margem

"The growing interest for natural materials as an environmentally friendly alternative for the substitution of energy intensive and non-sustainable synthetic materials, has motivated the use of lignocellulosic fibers as reinforcement of biocomposites. The sisal fiber, a relatively unknown lignocellulosic fiber with potential for composite reinforcement, still needs to characterize for possible engineer applications. Therefore, the present work analyzed the sisal fiber by means of Fourier Transform Infra-red (FTIR) spectroscopy. The sisal fiber FTIR spectrum revealed main absorption bands typical of any lignocellulosic fiber. However, some specific bands as well as bands broadening and intensity suggested particular activities for functional molecular groups in the sisal fiber.IntroductionIn recent decades, environmental issues related to worldwide pollution and climate changes, mainly the global warming, are motivating new paradigms for the development of our society. Among these, the use of natural materials in substitution for non-sustainable synthetic materials, obtained from non-renewable ores and petroleum, is increasingly being considered. In particular, natural fibers extracted from plants are, in this 21st century, experiencing a surge as composite reinforcement [1-11 ], following their replacement by synthetic fibers, specially the glass fiber, during the second half of the 20th century [1-2-8].In addition to environmental benefits [12-13] the lignocellulosic fibers present economical advantages, such as worldwide abundance and comparatively low costs as well as some technical properties associated with flexibility and toughness[ll], which contribute to the performance of automobile components fabricated with natural fibers composites[14-16].Among the less common lignocellulosic fibers that only recently have been investigated[l 7], the fibers extracted from the stem of the sisal plant, shows in Fig 1, reveals a potential for polymer composite reinforcement."

Jan 1, 2013

By Yves Fautrelle, Kader Zaidat, Hervé Combeau, Miha Zaloznik, Mohammed M'Hamdi, Bachir Saadi, Xiaodong Wang, Knut Omdal Tveito

"Numerical simulations of macrosegregation formation during horizontal solidification of a hypoeutectic Sn-Pb alloy in a rectangular cavity is presented and compared to experimental results. The experiment involves a melting phase, a holding stage at constant temperature with/without application of electromagnetic stirring, and finally solidification. We simulate all stages of the experiment and study the segregation of Pb throughout the experiment. A twophase volume averaged model is used for the numerical simulations, accounting for thermosolutal convection and assuming perfect microscopic mixing (lever rule). The influence of the melting phase and the electromagnetic stirring is studied with different cases to illustrate the consequences on the flow pattern and Pb segregation. The numerical simulations are compared to the experimental data and the impact of chemical inhomogeneities prior to solidification on macrosegregation formation is discussed.IntroductionMany extensive investigations have been performed so far on the solidification of metallic alloys. However, the melting process of metallic alloy has not attracted attention in a same manner. Nevertheless, melting of alloy may put forth peculiar effects as described in the present paper. It has been observed from a benchmark experiment [1, 2] that significant stratification might arise during the melting process of Sn-Pb alloy. That effect was put forth thanks to the analysis of the experimental temperature distribution which indicated that the convective fluid flow was almost zero. The effect was enhanced when the lead composition was higher (above 6wt.%). The present paper is aimed at confirming that the melting of an alloy containing a heavier solute may be accompanied with a stratification of the solute which exerts a stabilizing effect on the convective fluid flow. Results obtained from numerical modeling are compared with experimental data obtained from the benchmark facility."

Jan 1, 2012