By Kenneth N. Han

Ammonia has been found to be an effective leaching reagent for gold, silver and platinum group metals in the presence of appropriate oxidants. Electrochemical and kinetic aspects of the dissolution of elemental gold in ammoniacal solutions have been investigated. The cathodic reaction of aurous di-ammine on the gold cathode has been investigated first. From this investigation, the standard electro-potential of the cathodic reaction .and hence. the Gibbs free energy of formation of the aurous di-ammine were established. The solubility of gold in ammoniacal solutions was also examined in relation to ammonia concentration, temperature and concentration of various oxidants. The anodic reaction of the gold disk in ammonia? in the presence? of various oxidants including oxygen, ozon, hypochlorite, hydrogen peroxide, cupric and cobaltic ammine, and iodine was also examined and the results have been discussed. Excellent dissolution yielding of gold and many other metals, typically better than 95% recovery in 1'-2 'hours of leaching at a temperature ranging 80°C to 190°C has been observed. Test results of the dissolution of gold from elemental state as well as other sources including sulfidic ores and scrap are presented.

Jan 1, 1998

By Hao Rang

The article Is specially to Introduce the recovery process of Nb, Mn, P from slags and reutilization techniques of the remaining slags. Nb-Mn-Fe alloys which contain 14-16% Nb, 40-60% Mn can be obtained after using fire refining process of " Blast Furnace-Revolving Furnace-Electric Furnace -Electric Furnace, "meanwhile, phosphorous slags which the content of phosphorus pentoxide Is 29.21%. Further going through wet metallurgical processing and electrowinning technics to recover grading 99°o metallic manganese. Finally, phosphorous slags are grinded finely to be as phosporous fertilizers to be directly used for farmlands. Small particle size (0-8mm) rich slags are mixed with slight solid additions for balling directly, and taken Into blast furnace with blocky slags all together. The remaining tall slags are fully used as constructional materials, slags cement as well as a serial of wall materials, road materials, ground ornamental materials without burning operation and steam curing. The compressive strength range of those materials is up to 15-30 MPa. There is no more solid waste slags effluent In the full technical process.

Jan 1, 1994

By Andrew Case

The Port Nickel facility in Braithwaite, Louisiana, is known for pioneering hydrometallurgical processes for the 'separation and recovery of nickel, cobalt and copper. Ten years ago, in 1985, a new CRI-MET process for the recovery of molybdenum, vanadium, nickel, cobalt and alumina from spent catalysts was developed and implemented. Spent- catalysts from the petroleum industry consietute the majority of feed. These are not only a valuable-source of metals, but due to EPA regulations are frequently classified as hazardous under RCRA. Molybdenum and vanadium are selectively leached in an oxidative hydrothermal step. Alumina is then extracted in a caustic digestive leach. The unique technology produces four primary commercial products l molybdenum trioxide, vanadium oxide, aluminum trihydrate and nickel-cobalt concentrate. This paper discusses the process, modifications. during ten years of operation, and the relationship of these modifications to the future of the catalyst recycling business.

Jan 1, 1995

By Florian Kongoli

"Lime ferrite" slag with limited silica content has proven to be a valuable choice in the modem processes of copper smelting and converting due to several advantages that this slag offers compared to classical silicate slags. Nevertheless the liquidus surface of this slag has been experimentally measured only at low oxygen potentials such as in equilibrium with iron or near it and in air. Although most of the smelting and converting processes that use this slag occur at intermediate oxygen potentials, the liquidus surface of this slag is not known at these conditions and the effect of oxygen potential and silica has not been correctly understood. This has brought some confusion in literature as well as in the industrial practice. In this work the liquidus surface of the calcium ferrite slags has been quantified by the means of a new thermophysicochemical model and a new type of liquidus surface diagrams which are very convenient for any industrial process that uses calcium ferrite slags. These diagrams can be easily used to select the lowest liquidus temperature of calcium ferrite slags at a minimum cost and can help design several fluxing strategies in copper smelting and converting processes. The effect of the oxygen potential and silica is also quantified and important industrially related conclusions are drawn.

Jan 1, 2003

By Zenjiro Asaki, Teruo Tanabe

"To clarify the formation of light rare earth (R =Ce, Pr, Nd or Sm) -Fe compounds in the reduction-diffusion (RD) process, two kinds of experiments were carried out: (a) RD experiment in which briquettes composed of R oxide powder, Fe (particles or wire) and CaH2 were reacted, and (b) immersion experiment, where an Fe plate was immersed into R-Fe melt having the composition of Fe-side liquidus line in Fe crucible. The compound formation was examined by using XRD, SEM and EPMA. The formation rates of RzFe17 measured by the RD experiment were compared with those obtained by the immersion experiment. The growth rates of compounds obtained in the RD experiment for Pr-Fe and Nd-Fe systems were much lower than those obtained in the immersion experiment. This result was explained by the difference of the reduction rates of R oxides by Ca. The parabolic rate constants for the formation of RzFe17 were separated in two groups of (a) Pr-Fe and Nd-Fe systems and (b) Ce-Fe and Sm-Fe systems. This was discussed in connection with the difference of their crystal structures and the driving force of diffusion. The parabolic rate constants for the formation of compounds in Ce-Fe and Sm-Fe systems decreased in the order of RFez, RFe3 and RzFe17.IntroductionTo understand reaction behaviors in the production of rare earth (R) -iron intermetallic compounds, which have excellent magnetic properties, is very important from engineering point of view. And the reduction-diffusion (RD) process<O has recently attracted attention as one of the promising processes to economically produce R-related materials. A few fundamental studies on the compounds formation in the RD process have previously been reported. Qi, Hino and Yazawa(2) observed the formation of R(Nd, Sm)-Fe and R-Co compounds in the process from various view points. Song and Ogawa(3) measured the growth rates of Nd-Fe and Sm-Fe compounds by using Nd or Sm vapor supplied from Nd-Ca or Sm-Ca melts. The authors have also carried out fundamental studies (4)-(8) to clarify the rate and mechanism in the production of R-Fe intermetallic compounds."

Jan 1, 1998

By Florian Kongoli

"Lime ferrite" slag with limited silica content has proven to be a valuable choice in the modem processes of copper smelting and converting due to several advantages that this slag offers compared to classical silicate slags. Nevertheless the liquidus surface of this slag has been experimentally measured only at low oxygen potentials such as in equilibrium with iron or hear it and in air. Although most of the smelting and converting processes that use this slag occur at intermediate oxygen potentials, the liquidus surface of this slag is not known at these conditions and the effect of oxygen potential and silica has not been correctly understood. This has brought some confusion in literature as well as in the industrial practice. In this work the liquidus surface of the calcium ferrite slags has been quantified by the means of a new thermophysicochemical model and a new type of liquidus surface diagrams which are very convenient for any industrial process that uses calcium ferrite slags. These diagrams can be easily used to select the lowest liquidus temperature of calcium ferrite slags at a minimum cost and can help design several fluxing strategies in copper smelting and converting processes. The effect of the oxygen potential and silica is also quantified and important industrially related conclusions are drawn.

Jan 1, 2003

By F. Patisson

During exothermic gas-solid reactions, heat generation makes temperature rise and modifies the rate of the various mass transfer processes, namely the chemical reaction itself, the pore diffusion and the external transfer. We have investigated this thermal effect during the oxidation of zinc sulfide porous pellets in a thermo balance furnace, between 550 and 900°C-and under O2-N2 atmosphere. The results have been&apos; analyzed by using, firstly, the law of additive reaction times derived from the isothermal Grainy Pellet Model, and, secondly, a new numerical model taking into account non-isothermal conditions. Both the models can satisfactorily simulate conversion versus time, but the numerical model also depicts the temperature evolution within the pellet. Finally it is shown that owing to the heat generation the zinc sulfide oxidation takes place under diffusion control (3/4 internal, 114 external) in all the cases studied. During the course of reaction, the. pellet undergoes strong temperature variations, with thermal gradients confined to a shell oxide layer.

Jan 1, 1996

By Jiechao Liu, Lijian Luo, Yubao Ma, Bo Zhang, Yanfeng Yang, Xin Hong, Luming Liu, Jienan Liu

Reduction kinetics of stainless steel slag in iron bath smelting reduction was studied at the temperature of 1500℃ ~ 1650℃. It was concluded that the reduction process consisted of two parts. That is to say smelting reduction was controlled by stainless steel slag melting initially and by interface reaction later. In order to increase smelting reaction rate, the melting point of slag should be decreased at the first stage and adjust the liquidity of slag at later stage. Smelting reaction rate will be accelerated by means of optimize the slag content. The optimal reduction result that all most all of the chromium in slag been recovered was obtained in temperature was 1500℃, basicity of slag was 1.0~1.2, the value of Al2O3+MgO was 25%.

Jan 1, 2015

By Yotamu Hara, Animesh Jha

"High Curie temperature and large magnetic anisotropy make cobalt an important magnetic material for power engineering applications of magnets operating above ambient. It is also an essential constituent of modem lithium - cobalt oxide batteries, without which modem electronic gadgets will be functionless. Both these applications of cobalt save energy and reduce C02 emission. Ironically, however the production of cobalt from copper and nickel smelting in the world remains one of the least energy efficient process. The paper analyzes the energy balance, material and process chemistry of overall cobalt recovery and the waste generated, which entail the process limitations. We discuss a novel approach for the reduction of sulphide minerals with CaS04, permitting better separation of metals from slag and generating higher concentrations of S02. Such an approach may seem to be an alternative energy efficient option for processing and further purification of cobalt in metallic form. The results are discussed in the context of process thermodynamics and reaction kinetics for Coalloy production.IntroductionCopper sulphides bearing minerals are predominantly associated with iron and cobalt sulphides minerals. Carrollite (CuC02S4) is a mineral that has both copper and cobalt sulphides [1,2], which may also contain FeS, by substituting either Cu2+ or Co2+ ions in mineral lattice. On smelting copper - cobalt - iron sulphide concentrates, some parts of the cobalt often partition to matte at preferentially low oxygen potential by forming eventually an alloy phase with copper, however a significant fraction is often lost into an oxide slag rich in iron and silica. The slag heaps accumulated in the Copperbelt region in Zambia from last 60 years of mineral processing and metal extraction is reported to be 0.3 to 2.6 wt% of cobalt element, which is high [3]. Cobalt is also available in smaller concentrations in the copper smelting and converter slag, as reported in the investigations on the recycling of such slag materials using leaching with ammonium salt [4], iron chloride [5], and sulphuric acid [6], and solvent extraction [7].The recovery of cobalt from slag, irrespective of the techniques researched so far, does not seem energy efficient because the molten slag at 1300°C is quenched by losing thermal and chemical energy. The quenched slag is again reheated to above room temperature for leaching and above liquidus for carbothermic reduction of residual cobalt oxide. For example, in Mintek DC arc smelting [3], 80% of cobalt and 95% nickel are recovered by expending 600 kW per tonne. Assuming that the mineral carrollite is the starting phase, the univariant calculations for the Co-Ca-Si-S-0, Fe-Ca-Si-S-0, and Co-C-Si-S-0 systems are shown in Figure la, lb, and le, respectively at 1573 K."

Jan 1, 2012

By James R. Craig

Petroleum coke is becoming an increasingly important source of light hydrocarbon products as product crudes become heavier and of poorer quality. The use of petroleum coke to generate synthesis gas results in the formation of residual slags that are enriched in silica, alumina, sulfides, oxides, and free metals. The characterization of these slags and their con? stituent phases is an essential step in considering the ultimate use or disposal of such slags and in understanding how to alter the properties of the slags to optimize the efficiency of gasifiers. Depending upon temperatures and bulk compositions, quenched slags typically consist of silicate glasses, calcium silicates, iron-nickel oxide-sulfide masses, aluminate spinels and free metals. Whereas the glasses contain relatively uniformly dispersed metals and sulfur, the iron-nickel oxide-sulfide masses highly concentrate nickel and sulfur. The aluminate spinels very effectively concentrate vanadium and chromium, thus depleting glasses or other adjacent phases. The abundance as well as the make up of the slags strongly affects the physical behavior of the slags within the gasifiers

Jan 1, 1989

By Yan Wen

For the impurities in the copper smelting waste acid, SO3, Cu, As, Pb, Zn, Re and other elements enter the waste acid and generate a lot of arsenic residue, gypsum and neutralized residue, in which Cu, Zn and Re metals have not been recycled. Cu, Re and As are separated by step-wise vulcanization. The valuable metals of Cu, Zn and Re are recovered by separating zinc through pH adjustment. Calcium injection is conducted for boiler for reducing the amount of SO3. The residues generated in the form of arsenate and hydroxide will be returned together with arsenic filter cake for smelting treatment so as to achieve the purpose of valuable metal recycling and solid waste reduction and harmless treatment.

By LuisW. Pommier

The industrial wastes generated by the plating industry, the circuit board manufacturing industries and other related industries normally contain high concentrations of metals, which make them hazardous. The extraction of the contained metals and their separation may be achieved by both pyro and hydro metallurgical processes. Some of the industrial wastes, those rich in some metals like nickel for instance, are being treated like mine ore concentrates and are being fed to smelting furnaces. The slags from these smelter operations are hazardous. They have, however, special environmental dispensations issued by the regulatory authorities. Hydro-metallurflcal processes have been reported. They also generate a residue which is hazardous because not all the valuable metals are leached out and also, because "non valuable" components, like chromium, are less readily leached. Residues from the plating industry, containing nickel, copper. zinc, iron and chromium as the major constituents and also sodium and calcium, together with cadmium, cobalt, lead. manganese, magnesium, molybdenum, and potassium, have been processed for the extraction of the valuable components. The generation of electrolytic nickel, copper and zinc and also of ferric chloride and chromium oxide is reported. The operation is achieved by a caustic leach for the extraction of zinc, followed by a sulfuric acid leach for the extraction of nickel and copper. This acid leach also extracts the iron and some chromium. The nickel copper and zinc are rendered pure by electrolysis, the iron is oxidized for the production of ferric chloride and the chromium is recovered as an oxide. The leaching operation is performed in two stages, first at a pH of 2.5 to generate an electrolyte for the partial recovery of the metals and then at a pH of 0.5 for the complete extraction of the metals. This leaching operation generates a residue, which although small in volume compared to the initial feed, still contains traces of the valuable metals and a portion of the chromium which makes it hazardous. Additional leaching with hydrochloric acid or nitric acid is required for its complete dissolution. The other minor constituents mentioned are present in concentrations each of less than 0.1% and are handled as impurities in the process. The metals which are soluble at a pH 0.5 and precipitate between 0.5 and 2.0 are bled off. Other impurities will concentrate on the raffinate from the solvent extraction operations from whence they are bled off. These bleeding streams are hazardous and the "impurity metals" are now present in concentrations which would make them valuable, however, the size of these streams is so small that they do not warrant their processing, however they could be marketed to specialized smelters. The extraction of the valuable metals, of the hazardous constituents, the generation of a marketable mixture of minor constituents and the production of a non-hazardous residue for declassification is profitably achieved.

Jan 1, 1998

By Carlos Maurício Fontes Vieira, Sergio Neves Monteiro, Diogo Neves Henriques

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850 to 1100oC. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at temperatures above 1000 ° C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antônio de Pádua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antônio de Pádua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption and low mechanical strength [3,4]. To avoid these problems, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2008

By G. R. Waters

NMR360 is developing a suite of chloride-based metals extraction processes, with the first commercial operation scheduled for commissioning late in 2018. It is critical, therefore, that with the introduction of any new technology, that the circuits do not suffer from mechanical failures which will compromise the operation. Although chloride leaching is at atmospheric pressure and relatively low temperature, the main challenge is preventing corrosion, since the high proton activity makes even a small amount of acid behaves as though it were concentrated. An additional challenge in concentrated chloride circuits is the potential for solids precipitation. In this context, therefore, correct valve selection is crucial, and NMR360 has partnered with CGIS to ensure that the Severe Service Valves (SSVs) needed will perform over and above the definitions of the Manufacturers Standardization Society (MSS) of the Valve and Fittings Industry. This paper outlines what the minimum requirements are for SSVs in chloride leaching applications, drawing on five decades of industry experience from one of Canada’s leading valve experts.

By ZHANG Ting

In view of the high consumption and contamination of traditional vanadium extraction technology, a new process of leaching the converter vanadium slag without roasting with titanium dioxide waste was proposed. Extraction mechanism of P204 in the leaching solution had been researched and single factor experiments show that after a prereduction of Fe, and under conditions: ambient temperature，leaching solution original pH=2.5, phase ratio (A/O)=1:3, shaking time 8min, the extraction rate of V is more than 98.62% meanwhile the separation rate between V and Fe is up to 135.3 in the 20%P204-10%TBP-Sulfonated kerosene extraction system.

Jan 1, 2015

By R. E. Moore

The lining systems currently in use in BOF furnaces, certain steel ladles, and the slag line of electric are furnaces were developed during the late seventies through the mid-eighties using a trial and error method of combining aggregate, carbon sources, additives and binders. They are currently based on magnesia, graphite, metal additives and resin binders, the selections of each being tied to the anticipated intensity of the use conditions. The general functions of the respective constituents are well appreciated, however, there is still a great deal that is not known about how the socalled antioxidants protect the graphite nor how impurities from the graphite and the aggregate enter into the wear processes. In a simplified assessment of wear processes, it appears that if the deoxidized layer can be kept very thin, less than 810 mm in depth, and if the viscosity and quantity of the matrix glassy phases can be controlled to resist erosion of the deoxidized layer, lining life can be maximized for the various applications. This paper will discuss the characteristics of the starting materials systems currently being employed for applications requiring a deoxidation function to realize extended wear. It will not attempt to explain all the complex interrelationships between the respective constituents but will point to the potential for improvements through the use of improved constituents.

Jan 1, 1991

By Chao Li, Qian Li, Yong-bin Yang, Kai Li, Qiang Xie, Yuan-yuan Zhu, Dong-ye Li, Qi-bing Tan

"The permeability of sintering mix is a vital technological property in sintering process. However, it can only be measured by off-line method on samples picked from the production. In order to acquire the properties of sintering mix accurately, on-line measuring of permeability is urgently required. Based on the reflection characteristics of bed permeability on pipe flowing parameters, a new method is presented in this paper for on-line measuring of sintering mix permeability. The measurement can be performed by blowing gas flow in the bed with the measuring pipe. Measuring results are obtained by picking the data on flowing rate and pressure in the pipe. The function of flowing rate to pressure may be certain for samples with the same permeability. Thus, the permeability was determined by contrasting this function to the result of off-line measuring, and the relative coefficient or R2 value was more than 99%.IntroductionThe permeability of sintering mix is a vital technological property in sintering process, which directly determines production and quality of sinter, or even determines whether the sinter production is carried out smoothly [1,3].The permeability have more obvious influence on vertical sintering speed, which is mainly related to air quantity passing through material bed. Under certain inducing capacity and negative pressure, the vertical sintering speed mainly depends on the permeability of sintering mix. Low permeability may make burning through point of sintering move back, and the sinter mix cannot be burnt through. High permeability may make burning through point of sintering move forward, improving production efficiency by increasing the speed of sintering machine [4] Good permeability means a small resistance of fan ,reduction of negative pressure of sintering machine, and full contact between air and sulfide, which can strengthen physical-chemical reaction during sintering process and increase desulphurization rate. In gas well through material layer process, gas-solid desulfurization reaction and gas-solid-liquid heat exchange are completed and hot gas through the combustion zone supplies the sintering process with heat. Finally uniform sintering of the material layer in height and width direction is achieved [5] While high permeability index leads to weak sinter strength, fast sintering speed, short residence time of high temperature region and little liquid phase. Moreover, liquid phase in the fast cooling process is too late to fully crystallize but forming glass phase which is harmful to sinter strength as well. Bad permeability means a big fan resistance and increase of negative pressure of sintering machine, which make the air pass through material layer difficultly. When air and mix contact difficultly, removal of sulfide reduces so that desulfurization is incomplete. Meanwhile, low caking efficiency, slow sintering speed and easily burnt sinter , reduce sinter output. Therefore appropriate permeability of sintering mix is the premise of stable burning through point and satisfactory sinter output and quality."

Jan 1, 2013

By A. D. Damodaran

Batch scale and continuous rotary kiln carbothermic metallisation of ilmenite followed by different down-stream treatments such as catalytic rusting, acidic chloride leaching, oxidation-leaching etc. has given rise to a high grade synthetic rutile (98% TiO2). Rotary reactor metallisation experiments had concurrently given important information with respect to mean residence time, dispersion number, hold-up and axial velocity profiles of the solids bed. A mathematical model based on law of additive reaction times has indicated that Boudouard reaction becomes faster than reduction reaction at higher conversions. A possible use of high grade synthetic rutile in paint industry and metallised ilmenite as welding electrode flux material are discussed.

Jan 1, 1992

By Huimin Lu, Min Li, Jinghua Zou

"Zeolitic imidazolate frameworks (ZIFs) are new type of porous materials, form inerratic polyhedral in three-dimensional with large cages and small apertures, and appear structural diversity. Their hole size can be adjusted. These materials have high selective adsorption capacity to carbon dioxide. In this paper, zeolitic imidazolate frameworks were synthesized by solvothermal synthesis method with dimethylformamide (DMF) as solvent and structuredirecting agent, divalent metallic ions as cation, and imidazole as ligand. The crystals were characterized with XRD, SEM for their crystal structures and physical properties, the adsorption of the crystals for carbon dioxide was also tested, and the result suggests that these porous materials have a capacity of 1.35ml/g for storing carbon dioxide at 273 Kelvin under ambient pressure.IntroductionGlobal warming caused by the increase of carbon dioxide in the atmosphere has become one of the main environment problems, contemporary research has focused on ways to slow or stop this trend. CO2 capture has attracted attention due to the potential to trap and sequester large amounts of CO2 from concentrated sources such as power plants [1]. Traditional technologies in capturing CO2 include absorption by aqueous amines [2]. However, utilization of this process is energy intensive and expensive. Carbon dioxide storage materials investigated so far can be divided into two categories: chemical storage adsorbents and physical storage media [3]. The first kind of materials can chemically adsorb carbon dioxide within their structures and need thermal energy to release the adsorbed carbon dioxide. The examples of the chemical adsorbents include aqueous amines, gas-hyperbranched aminosilicas [4]. The physical adsorbents store carbon dioxide by physical adsorption of carbon dioxide at elevated pressure and release the adsorbed carbon dioxide at low pressure. The physical adsorbents that have been investigated for carbon dioxide storage include zeolites, carbonaceous materials and other porous materials. Until recently, a new type of microporous material, known as zeolitic imidazolate frameworks (ZIFs), has been reported as promising adsorbents for carbon dioxide storage [5 ~ 10]."

Jan 1, 2010

By Mariane Costalonga de Aguiar, Carlos Mauricio Fontes Vieira, Sergio Neves Monteiro

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850, 950 and 1050°C. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at 1050°C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antonio de Padua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antonio de Padua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption [3,4]. To avoid this problem, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2011