By C. H. Li, J. Washburn, E. R. Parker

Yield stress in single crystals of zinc was shown to be dependent on prior annealing temperature and rate of cooling after annealing. Rate of strain hardening beyond the yield was not sensitive to annealing procedure. A tentative mechanism for the effect was discussed. COMPARATIVE mechanical tests of metal single crystals generally show a large scatter of results. Many factors may contribute to this variation. The present investigation was undertaken to evaluate the influence of two factors not ordinarily considered of major importance—annealing temperature and cooling rate after annealing. Since plastic properties of crystals are thought to depend on the presence of lattice imperfections, it follows that a variation in properties should result from differences in the distribution and density of these imperfections. Furthermore, in the light of current theories of interaction between edge dislocations and lattice vacancies,' it seems possible that annealing temperature and subsequent rate of cooling might play a part in this distribution. Analysis of the effect of these variables on plastic properties may lead to a better understanding of the annealed state. Single crystals of zinc which have been strained in simple shear undergo complete recovery of mechanical properties upon subsequent annealing. This behavior is useful because a single specimen can be used repeatedly, thus eliminating the uncontrollable variables introduced by the use of many crystals. The test section of the crystals used for these experiments was a cylinder 1/8 in. thick with a cross-sectional area of about 1/3 sq in. The specimens were acid-machined from spherical single crystals 1 in. in diameter in such a way that the slip plane (0001) was at right angles to the axis of the cylinder. In testing, a shear stress was applied along one of the slip directions, [2110] in the (0001) plane.' All crystals, unless otherwise noted, were grown in a helium atmosphere from molten 99.99 pct pure Horse Head Special Zinc. Fig. 1 is a family of curves obtained from one crystal. Each curve was obtained by deforming the crystal to 10 pct strain at a rate of 3 pct per min, following an anneal of 1 hr at 260°C. The strain direction was reversed every other time so that no progressive change in shape of the specimen took place during the series of tests. Since the stress-strain curve was reproducible within a fairly narrow range under the same conditions of annealing, it was then possible to determine the effect of changes in annealing conditions. A crystal was tested repeatedly as previously described but the annealing temperature and rate of cooling preceding each test were varied (Fig. 2). Two cooling rates were used, approximately 30°C per min and 3°C per min. Annealing was conducted at three temperatures, 200°, 300°, and 400°C. For a given annealing time and rate of cooling the room temperature flow stress was higher the higher the annealing temperature. The increase in flow stress was small as the annealing temperature was increased from 200° to 300°C but rose rapidly when the annealing temperature was raised from 300" to 400°C. Faster cooling from the high temperature produced an even greater strengthening of the crystal. The curves were obtained in the order indicated by the numbers. The stress level associated with a certain annealing treatment was, within the limits of scatter, always the same regardless of the

Jan 1, 1954

By G. A. Yuko, J. W. Barton, J. G. Parr

ALTHOUGH previous work1 has shown the compo- sition range of the complex face-centered cubic phase,2 Ti2Ni, to be narrow, no precise limits were established. The purpose of this investigation was to prepare homogeneous alloys on either side of the stoichio-

Jan 1, 1959

[Title 1 Contents Page . 3 Officers and Directors 5 Past and Present Officers 6 Standing Committees 9 Professional Divisions 11 Technical Committees 12 Institute Representatives on Boards 17 United Engineering Society 17 Engineering Societies Library Board 17 Engineering Foundation Board 17 Other Committees 17]

Jan 1, 1928

THE second part of the mould for making guns is the core. Without this the space could not be made where the powder is to be and through which the ball, impelled by the fire, can pass and take flight. To make this it is necessary to take two things into consideration, because they are very important. One is what you are to make it on so that it may be supported and kept true. The other is what composition of clay will stand up during casting and yet not be very difficult to extract from the body of the finished gun. For the first, it is found that only an iron spindle of a suitable thickness is able to support the weight of the clay without bending under the heat of the fire or wobbling as it is turned on its journals or when handled. This should be a braccio or more longer than the mould of the gun and worked exactly round, straight, and well tapered like a spindle; above all every one of its joints should be well secured and solid. At the upper end a per-orated heel should be made, and lower down, exactly at the point corresponding to the length of the mould, are one or two other holes through which the little crossbars can be passed that fasten the core to the outer mould and also serve for constructing the disc. Now this iron is to be arranged on two trestles, pivoted so that it may turn truly when rotated. In order that it may not run up and down, make a little iron fork which engages a notch made with a file at the foot, and another at the head. After this, you must prepare clay for the core which is well made and tenacious ,enough not to crack. Fint take care that there are no pebbles in it and that it is composed of a small amount of cloth clippings and much sifted horse dung and some washed and clean wash ashes so that it may be of a tender and crumbly consistency in order that it may later be more easily extracted from the space inside the gun. In the same way, in order that you may be able to take out the iron piece at the same time, first cover it with ashes, and then wrap it all over with a rope of ordinary thickness, leaving a dito of the iron uncovered in every palmo length. [86] Alternatively, you may cover it all very tightly with hemp tow in the same way after it has been covered with ashes. Or heat your iron considerably and then cover it all to the thickness of a good cord with wash ashes or powdered charcoal that has been made into a paste with a little

Jan 1, 1942

By H. Landsberg

The curriculum presented here is an outgrowth of discussions by the Committee on Geophysics Courses of the A.I.M.E. in previous years. It had to be a compromise between the desires voiced by employers of geophysicists, professional geophysicists and the possibilities at an average college. There one has to face the questions of the available teaching staff, the inertia of administrators and teachers set in their ways, and the red tape involved in modernizing antiquated curricula. It is, of course, not ideal to have colleges and universities lag Io years behind the times. Rather, instead of being prodded by industry, they should be ahead of industrial needs. There should also be a certain amount of leeway for the student in any college curriculum. All these points had to be considered in drawing up a curriculum, which, instead of being narrowly termed "geology" or "geophysics" was rather called "earth science." It gives the student a chance to specialize in one of the various branches represented by teachers on the faculty of The Pennsylvania State College, giving as options Geology (with subdivisions of Mineralogy and Paleontology), Geophysics, Geography, and Meteorology. Table iA represents the option of geophysics in the curriculum that envisages that a student may want to make his career in any of the fields encompassed by the American Geophysical Union or in geoexploration. This is, of course, only the start of an education that in most cases will have to be followed by graduate work for complete professional training. The outlined curriculum is definitely of an engineering type and is identical for all of the four options mentioned for the first two years. Specialization will start in the junior year but even thereafter the branches are kept as closely allied as feasible in order to permit a student to change from one tO the other (e.g., because of a different aspect in the mployment situation) with a minimum of additional work. Table IB shows the geophysics option according to subject matter, indicating the considerable amount of work in the fundamentals of mathematics, physics and chemistry with a liberal number of geology courses, and some engineering. The courses in the field of geophysics are limited—just two lecture courses as a general introduction and one field course, to permit the student a visualization of the correlation between mathematically analyzed physical data and the geological realities. Thesis work is considered essential to teach the student, while he is still in college, some things S. F. Kelly has mentioned as desirable: (I) following of instructions for somewhat independent work; (2) organizing of material, and (3) producing a readable report. This, together with the personal contact with the advising faculty member, will help in forming a student's personality. The seminar course attempts to get the student into the habit of reading current literature, so that he can keep abreast of the times.

Jan 1, 1946

By H. Landsberg

The curriculum presented here is an outgrowth of discussions by the Committee on Geophysics Courses of the A.I.M.E. in previous years. It had to be a compromise between the desires voiced by employers of geophysicists, professional geophysicists and the possibilities at an average college. There one has to face the questions of the available teaching staff, the inertia of administrators and teachers set in their ways, and the red tape involved in modernizing antiquated curricula. It is, of course, not ideal to have colleges and universities lag Io years behind the times. Rather, instead of being prodded by industry, they should be ahead of industrial needs. There should also be a certain amount of leeway for the student in any college curriculum. All these points had to be considered in drawing up a curriculum, which, instead of being narrowly termed "geology" or "geophysics" was rather called "earth science." It gives the student a chance to specialize in one of the various branches represented by teachers on the faculty of The Pennsylvania State College, giving as options Geology (with subdivisions of Mineralogy and Paleontology), Geophysics, Geography, and Meteorology. Table iA represents the option of geophysics in the curriculum that envisages that a student may want to make his career in any of the fields encompassed by the American Geophysical Union or in geoexploration. This is, of course, only the start of an education that in most cases will have to be followed by graduate work for complete professional training. The outlined curriculum is definitely of an engineering type and is identical for all of the four options mentioned for the first two years. Specialization will start in the junior year but even thereafter the branches are kept as closely allied as feasible in order to permit a student to change from one tO the other (e.g., because of a different aspect in the mployment situation) with a minimum of additional work. Table IB shows the geophysics option according to subject matter, indicating the considerable amount of work in the fundamentals of mathematics, physics and chemistry with a liberal number of geology courses, and some engineering. The courses in the field of geophysics are limited—just two lecture courses as a general introduction and one field course, to permit the student a visualization of the correlation between mathematically analyzed physical data and the geological realities. Thesis work is considered essential to teach the student, while he is still in college, some things S. F. Kelly has mentioned as desirable: (I) following of instructions for somewhat independent work; (2) organizing of material, and (3) producing a readable report. This, together with the personal contact with the advising faculty member, will help in forming a student's personality. The seminar course attempts to get the student into the habit of reading current literature, so that he can keep abreast of the times.

Jan 1, 1946

By Vsevolod Krivobok

THE re-crystallization of metals has been the subject of much scientific investigation, some of which has resulted in a better understanding of this extremely important and interesting phenomenon. Unfortunately, while many have propounded theories of re-crystallization, but a few have presented experimental evidence as to how it takes place. If this can be determined the question, why re-crystallization occurs, may be answered more definitely. Re-crystallization in single phase metals consists of a complete rearrangement and re-sizing of the grains, of which the structure is composed, while the type of structure remains the same. That is to say, if the structure before re-crystallization is composed of a number of polyhedral grains of different shape and size, a particular spot after re-crystallization will be seen to consist of grains in no way different from the original except in size and shape. The re-crystallized grains may be smaller or larger, depending on the treatment received; and, while the re-crystallization may be brought about by means of heat treatment only in passing through a critical range, yet it is common knowledge that single phase metals subjected to cold working are possessed of a tendency toward re-crystallization, even if the heating does not reach critical range. The study of re-crystallization would, of course, be much easier if we had single crystals of any metal as the original material with which to study the phenomenon of re-crystallization, since it would permit the observation of structural changes at what amounts to enormous magnification, by changing the scale of the specimen. In metals of more normal grain size the crystal boundaries introduce complications, but the process, it may be assumed, is essentially the same. Such an opportunity

Jan 2, 1926

By E. T. Turkdogan, J. H. Swisher

The solubility of oxygen in zone-refined iron was determined in the temperature range.from 881" to 1350°C. The solubility in a iron at 881°C ms found to be about 2 to 3 ppm; in y iron, the solubility was found to increase from about 2 to 3 ppm at 950°C to about 25 ppm at 1350°C. The permeability of oxygen in an iron -0.1 pct Al alloy was determined in the y iron range, using an internal oxidation technique. By combining the permeability and solubility data, the diffzisivity of oxygen in y and a iron was calculated. The oxygen diffusivity in solid iron may be s~immarized as follows: 8820 For 6 iron and IN a recent paper, Hepworth, Smith, and Turkdogan1 reported on the solubility, permeability, and diffusivity of oxygen in 6 iron, together with permeability data for oxygen in a iron. In the present investigation, similar measurements were made in the ? phase region. In addition, a solubility measurement was performed in the a phase region to permit calculation of the diffusivity of oxygen in a, iron. References to early work on this subject are given in the previous publication.' EXPERIMENTAL Solubility Measurements. The oxygen solubility was determined by equilibrating cylindrical samples 0.3 in. diam by 14 in. long of zone-refined iron in water vapor-hydrogen gas mixtures. The zone-refined iron was prepared by B. F. Oliver of this laboratory, using an apparatus and technique described elsewhere.2'3 Six zone-melting passes were used to achieve a total impurity level of about 30 ppm. Of this 30 ppm, the combined nickel and cobalt content was about 20 ppm, oxygen was 4 ppm, and all oxidizable impurities less than 1 pprn each. A vertical resistance furnace wound with molybdenum wire was used for the experiments. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. In the gas train, flow rates of hydrogen and argon were measured with capillary flow meters, and the resulting mixtures were passed through a column containing 90 pct oxalic acid dihydrate and 10 pct anhydrous oxalic acid to obtain predetermined ratios of H2O to H2. The vapor pressure of H2O above this mixture as a function of temperature is well-known.4 The exit gas was ana- lyzed periodically for H2O, and good agreement (+3 pct) with the calculated composition was obtained. The zone-refined iron specimens were held in the furnace for a sufficient length of time for equilibration, e.g., 18 hr at 1350°C and 1 week at 881°C, then quenched in a brine solution. After removing the surface oxide from the samples by machining, duplicate analyses were obtained by a combined vacuum fusion-infrared method; oxygen analysis was reproducible within 2 ppm. Permeability Measurements. The permeability of oxygen in alloys containing about 0.1 pct A1 was determined by internal oxidation and measurement of the subscale thickness as a function of time. The experimental alloys were prepared by adding aluminum to electrolytic iron (grade 104A plastiron) that had previously been vacuum-carbon deoxidized. The resulting ingots contained about 20 ppm O, 100 pprn C, 40 pprn Si, 50 ppm Mo, 20 ppm P, 20 ppm S, and 20 pprn Zr as the principal impurities. After hot rolling the ingots to 1-in.-thick slabs, specimens were machined from the stock in the form of rectangular plates, 4 by 5 by 2 in. The general procedure for the permeability experiments was the same as those for the solubility measurements. The specimens were cooled in a reducing atmosphere rather than quenched, however, in order to maintain a clean surface for measurement of the sub-scale thickness. This measurement was made on a polished cross section of each specimen, using a microscope with a micrometer stage. The inclusions formed at the lowest temperature 1033°C were too small to be seen with an optical microscope. An electron micrograph showing the size and shape of individual particles is shown in Fig. 1. The dark band in the picture is a boundary between two subgrains. The subscale thickness in these samples was measured with an optical microscope after heavily etching in 2 pct nital, which gave contrast between the subscale and the unoxidized zone.

Jan 1, 1968

By H. L. Luo

SYSTEMATIC investigations of the Fe-Ga system have been reported only very recently."' The maximum solid solubility of gallium in a-Fe is nearly 50 at. pet at 900°C. However, from Ref. 1, it was not evident that the a-Fe solid solution could be retained successfully beyond 17.38 at. pet Ga by solid-state quenching. The present investigation reports the retention of a-Fe solid solution at 50 at. pet Ga by quenching from the liquid. An ordered phase of CsC1-type B2) structure was observed between 34 - 50 at. pet Ga. Since it was considered very probable that the CsCl structure would occur at high temperatures, alloy filings were also quenched by the conventional quenching technique. In addition to the CsCl phase, a second ordered phase of BiF3-type (DO3) structure was found in the range 25 - 30 at. pet Ga. Alloys were prepared from elements of 99.99 pet purity or better, induction-melted in alumina crucibles under hydrogen. After reweighing, the alloy ingots were cast into wires under argon. From the weight losses and the reproducibility of the lattice parameters, compositions were estimated to be within ± 0.3 at. pet. The techniques of quenching from the liquid state were reported before.3-5 Prior to quenching, a small section of cast alloy wire (30 - 50 mg) was melted in an alumina insert under an argon flow. The quenched specimens were in the form of flakes, typically 1 sq mm in area. For solid-state quenching, alloy filings passing 200 mesh were sealed under a reduced helium atmosphere in a thin-bottom silica tube. After heating for -30 min at the desired temperature in a vertical furnace, the sealed tube was rapidly dropped into ice water so that the thin bottom of the tube broke on impact. The quenched alloy filings were always ferromagnetic and could be collected by a magnet. X-ray diffraction patterns were taken with iron-filtered cobalt radiation in a 114.6-mm-diam Debye-Scherrer camera. High-angle lines were always resolved and spacings were computed relative to ? (CoKa1) = 1.78890Å. Lattice parameters were obtained from extrapolation against the Nelson-Riley function. The variation of lattice parameter with composition is shown in Fig. 1, together with the data of Dasarathy and Hume-Rothery.1 Uncertainties in the present measurements are within the dimensions of the symbols or indicated by error bars. X-ray diffraction lines indicative of CsC1-type ordering could be clearly identified for alloys of 34 - 50 at. pet Ga quenched from the liquid and alloys of 35 - 41 at. pet Ga quenched from -975°C. Within experimental error, no difference in

Jan 1, 1968

By W. E. Anderson, T. M. Brady

As part of a larger study to identify factors influencing the practical operating life of wire rope used on large draglines in surface coal mining, field trips to operating surface coal mines were made during late 1975. Wire rope performance information was obtained from personnel at 13 mine sites west of the Appalachians. Seventeen pieces of equipment, utilizing bucket sizes ranging from 30 to 220 cu yd (23 to 168 m), were documented. Draglines at large US surface coal mines can be represented as 120 machines having 60-cu yd (46-m3) buckets, moving 1.8 x 10[9] cu yd (1.4 X 10[9] m3) of overburden during 6650 hours of productive availability per year. Based on the limited field study, the calculated downtime resulting from rope-related causes averages 105.6 hours per year for each typical 60-cu yd (43-m3) dragline. The total loss in production from this source alone is thereby estimated at about 25 X 10[6] cu yd (19 X 10[6] m3) annually.

Jan 11, 1979

By O. E. Palasvirta

Close examination of most so-called new processes in mineral dressing reveals that they were conceived and developed a long time ago. High-intensity magnetic separation is no exception. Although its application in iron ore beneficiation seems new, in Germany the process has been commercially successful for almost two decades. High-intensity separators have long been standard equipment in the glass sand industry; they have also been used in concentrating some of the more unusual paramagnetic minerals. The basic features of an induced-rotor, high-intensity magnetic separator were described by Désiré Korda in Paris in 1905,1 and many patents have since been issued for improvements on the original design. Fig. 1 shows the basic design of an induced-rotor separator. Several U. S. manufacturers have been supplying induced-rotor separators for many years, but these are all devices of relatively low capacity, not suitable for treating such low-cost commodities as iron ore. On the other hand, two German manufacturers are offering induced-rotor separators of high capacity, both proven in the field.

Jan 12, 1959

By M. L. Fuller

THE fundamental mechanism of the deformation of zinc has been thoroughly described by several prominent investigators, particularly Mark, Polanyi, and Schmid,1 Mathewson and Phillips,2 and Schmid and Wasserman.3 The deformation of zinc occurs primarily through slip along basal planes {00. 1 }, and secondarily through twinning on pyramidal planes of the form { 10.2). In addition to these basic studies on single crystals, there have been a number of determinations4,5 of preferred orientations developed in rolled, polycrystalline zinc. In no case, to our knowledge, has there been described the development of oriented struc-tures in zinc as a result of a, systematic series of rolling treatments. The work included in the present paper shows the changes in orientation produced in a zinc alloy by successively increasing degrees of cold-rolling reduction. This alloy has the same crystal form, hexagonal close-packed, as zinc, but its susceptibility to hardening for a given degree of working is much greater because of its higher recrystal-lization temperature.

Jan 1, 1934

By R. G. Carlson, F. E. Westermann

HOT pressing of powder particles has gained importance recently, since it affords a method in which high densities are rapidly attained. In a recent study on hot pressing of alumina powders, Mangsen, Lam-bertson, and Best1 have shown within the limits of their experiment, the validity the rate equation for densification in hot pressing, originally proposed by Murray, Livey, and Williams.2 i.e., where D = fraction of theoretical density, t = time, P = pressure and 77 is the viscosity, all in appropriate units. This equation was derived from earlier work of Shuttleworth and Mackenzie3 which is based on the closing of spherical pores under the action of surface tension. The integrated form of this equation yields a straight-line relation between log (1 - D) and t. Such conditions were found by Felten4 to be true only after extended periods of pressing. In an endeavor to quantitatively evaluate the exactitude of this equation in the initial sintering stage, i.e., prior to sealing of the pores, spherical anti-

Jan 1, 1962

By B. S. Hickman

Using primarily quantitative single crystal X-ray techniques studies have been made of the precipitation of the metastable w phase in alloys of titanium with Mo, Mn, Fe, Cr, and Nb. It is shown that, in agreement with earlier work on the Ti-V system, the composition of the w phase during aging approaches a constant; the value varies from one system to another in a systematic manner with the electron concentmtion. Results relevant to the mechanism of w precipitation during quenching and during aging are presented and discussed. Results are presented to confirm that the w phase is coherent and the nzorphology of the Necipitates is described and discussed. PRECIPITATION of the metastable w phase in alloys of titanium is of interest because of its severe embrittling effect and also because of the enhancement of the superconducting properties which accompanies precipitation.1 The general features of w phase precipitation have been discussed by cuillan and by Bagaratskii et d3 The work described in this paper forms part of a general study of w phase precipitation which was undertaken to elucidate various unknown or controversial features of the process, namely: i) What is the mechanism of formation of the phase ii) How does its composition, morphology, volume fraction, and particle size vary with the type and content of the alloying element and with the heat treatment conditions? iii) What is the relation between the w phase and the equilibrium a phase? In a previous paper4 the results of a detailed study of w phase in Ti-V alloys were presented. It was shown that: U During aging the composition of the w phase approached a saturation value of 13.5 to 14.0 at. pct V. ii) w precipitated as cube shaped particles and once precipitation was complete, particle coarsening did not occur. iii) a phase formed initially by direct conversion of w-phase precipitates. In this paper similar measurements are reported on Ti-Mo alloys and some more limited data given on the Ti-Cr, Ti-Fe, Ti-Mn, and Ti-Nb systems. The results i.1 the six systems are then compared. It has been shown previously by electron microscopy that the w precipitates as ellipsoids in both the Ti-Nb system,&apos; and in i-o.&apos; Blackburn and williamsz3 have reported the precipitates in Ti-Fe, Ti-Cr, and Ti-Mn are cubic, i.e., similar to the Ti-V system.476 EXPERIMENTAL METHODS 1) Specimen Preparation. Samples of the compositions shown in Table I were prepared by arc melting. High purity electron beam zone refined titanium (Materials Research Corporation Grade I—total impurity content =250 ppm) was used; the other source materials are given in the table. A commercial Ti-8 wt pct Mn alloy was used for studies of this system. After homogenization the materials were rolled or cut into strip approximately 1/4 in. by 2 in.; the strip was then heated at temperatures of 1200" to 1300°C for several hours by passage of a direct current through the strip in an ultra high vacuum system (<10-torr) and then quenched by admitting high purity helium and switching off the current. This treatment resulted in crystals up to 2 in. by 2 in. by A in., almost all of which had a [100] direction nearly perpendicular to the plane of the strip. The crystals were cut from the strip by spark machining and their composition checked by lattice parameter measurements supported by chemical analysis. 2) X-Ray Diffraction Methods. Lattice parameter measurements were made using a modification of the single crystal spectrometer described by ond. In this technique the crystal angles for reflection on either side of a highly collimated primary beam are measured. Generally the 400 CuK, or the 400 CuKp reflections of the bcc lattice were used. In the as-quenched crystals a precision of 1 in 105 was obtained, but due to line broadening the parameters in aged materials could only be measured to 1 in lo4. This accuracy was, however, quite adequate for the purposes of these experiments and enabled the composition of the p phase to be obtained to 10.1 pct in all systems except Ti-Nb where the lattice parameter change with composition is very small. The precipitation and growth of the w phase was examined using a single crystal goniometer attached to a Phillips diffractometer. The relative intensities and line shapes of b-phase and w-phase reflections

Jan 1, 1970

Minnesota School of Mines Experiment Station, University of Minnesota, Minneapolis, Minn For copies of Bulletins or a list of publications, address The Director Bulletins available are Bulletin 1, Iron mining in Minnesota, by C. E Van Barneveld (1912), $1, 2, Concentration tests on Mesabi ores, by W R Appleby and E Newton (1913), 3, Preliminary concentration tests on Cuyuna ores, by W. R Appleby and E Newton (1915), 4, Bibliography of Minnesota mining and geology, by W. Gregory (1915); 5, Manganiferous iron ores of the Cuyuna district, by E Newton (1918), 7, The future of the Lake Superior district as iron-ore producer, by E W. Davis (1920), 9, Magnetic concentra¬tion of iron ore, by E. W Davis (1921); 10, Ball mill crushing iii closed circuit with screens, by E W Davis (1925); 12, Minnesota manganiferous iron ore in relation to the iron and steel industry, by T L Joseph and S P Kinney (1927). A mining directory of Minnesota, by J J Craig, is published annually.

Jan 1, 1933

By H. R. Hanley

ELECTROLYTIC zinc produced from sulfate solution and, with pure lead anodes is always contaminated with a small and varying percentage of lead. The purpose of this investigation is to determine the characteristics of several lead alloys and their influence on the products of electrolysis and power consumption. The study of alloyed anodes has been a matter of interest for some years. Tainton, Taylor and Ehrlinger prepared a highly interesting paper1 on this subject a year ago, in which the effects of silver-lead and some ternary alloys of lead-silver-tin were described. The present paper describes a study of various combinations of 10 metals. The general plan of the work provides for the fabrication of the alloyed anode, its adequate conditioning by preparatory electrolytic operation, the production of cathode zinc and its analysis, the determination of the anode polarization, and other features. A list of the anodes tested, showing composition and polarization at various current densities together with the lead assay of the cathode zinc, is shown in Table 1.

Jan 1, 1930

By N. J. Grant, F. B. Cuff

DURING a recent investigation of high-purity aluminum,&apos; evidence was found for grain-boundary sliding and migration at room temperature. The investigation was concerned primarily with an electron-microscopic study of a fine (approximately 1 micron) network that appeared on the surface of chemically polished aluminum. The nature of the network will not be discussed since it serves only as markers showing relative displacements in this instance. The pertinent observation, shown in Fig. 1, was made on a flat tensile specimen which had been strained about 8 pct at room temperature. As can be seen in this electron micrograph, a grain boundary has undergone a certain amount of sliding. The reason for the existence of the two differently appearing networks is given in the foregoing reference. For present purposes, however, the transition region can be disregarded. A close study of this picture reveals that in addi- tion to sliding there is a narrow band adjacent to and above the grain boundary. Fig. 2 is a schematic drawing showing the essential features of this band.

Jan 1, 1959

By E. E. Underwood, L. L. Marsh

Aluminum single crystals, alloyed with 0.042 atomic pet Cu and 0.11 and 1.1 atomic pct Mg, were subjected to constant stress creep tests, tensile tests, and hot hardness measurements within a temperature range of 300° to 866OK. Calculations based on Dorn&apos;s temperature-compensated time parameter, 6, gave a value of DH, = 27,000 cal per mol for the activation energy of early creep in aluminum single crystals. Correlations have been obtained for aluminum alloy single crystals with the parameter E for solid solution strengthening, as well as with the parameter F for solid solution hardening, by using a valence of three for aluminum. Limited measurements on tensile specimens show that the slip band density tends to decrease with increasing temperature and with decreasing solute concentration. INCREASING interest is being shown in the mechanisms of plastic deformation in single crystals during tensile and creep testing. The complexity of deformational processes in polycrystalline materials has led to a search for simpler experimental conditions. Numerous creep and tensile investigations have been conducted with pure, metallic single crystals. To a lesser degree, the effects of alloying elements on the tensile properties of single crystals have been determined. However: the literature dealing with the effects of alloying additions in single crystals under creep conditions is vanishingly small. This paper represents an attempt to narrow this gap in the knowledge of the subject. Previous investigations of creep behavior at the Battelle Memorial Institute1-1 have been of great value in the analysis of the present single crystal data. It is equally desirable, however, to ascertain the extent of correspondence between the behavior of single crystal and polycrystalline materials. For this purpose, correlations, similar to those developed for polycrystalline aluminum alloys by Dorn and co-workers, have been made with the single crystal data. The results from this study have tended to confirm and extend those correlations to the case of alloyed single crystals. Materials and Procedures Three dilute binary aluminum alloys were prepared for this investigation from 99.99 + wt pct Al, 99.8 wt pct Mg, and 99.92 wt pct (electrolytic) Cu. The nominal compositions of the alloys were 0.042 atomic pct Cu, and 0.11 and 1.1 atomic pet Mg. Precautions were taken to avoid contamination of the stock during melting and casting of the alloys. After a heat treatment of 8 hr at 925°F the alloys were extruded, then machined into) threaded tensile specimens with a 3 in. reduced section and a 0.505 in. diam. Spectrographic examination showed less than 47 ppm metallic impurities in each alloy. The single crystals were grown by the strain-anneal method, with a critical strain of about 11/4 pet giving the optimum results. In general, 3 in. crystals were obtained with the Al-Cu alloy, but smaller crystals in the magnesium alloys necessitated the use of 2 in. and 1 in. gage lengths with the low and high magnesium alloy specimens, respectively. After an electrolytic polish, the orientation of that portion of the specimen containing the largest single crystal was determined from Laue back-reflection photographs. Tensile tests were conducted at a constant load rate of about 2 lb per min. Creep runs were made in a constant temperature room, under constant stress at the higher creep temperatures, and constant load at the lower temperatures. The eloneation was measured to within ±5 microin. by a specially designed capacitance extensometer. The ex-tensometer arms were attached to the 3 in. specimens at the shoulders of the test piece or, where the crystals were smaller than 3 in., by knife-edge grips.

Jan 1, 1957

By H. C. Burghard, F. R. Brotzen

Experiments were performed to determine the effects of mechanical vibrations on ordering in CuAu. The effects of 5, 10, and 15 kc vibrations were investigated over a range of ordering temperatures of 280° to 360°C. A decrease in the rate of ordering was observed at all frequencies and ordering temperatures. THE effects of mechanical vibrations on certain solid-state reactions have been noted by several investigators. In 1930, Mahoux&apos; reported a substantial increase in the case depth of a steel sample nitrided under the influence of mechanical vibrations over that of an unvibrated sample. Similarly, an accelerating effect of vibrations on the diffusion of chromium in steel was noted. Guillet, in the same year, confirmed the results of Mahoux. More recently Schenck and schmidtmann3 studied the effects of low-frequency, alternating loads on the diffusion of carbon in steel. The results of their experiments, conducted at 500 cycles per min and large strain, (0.2 pct), indicated an acceleration of the process. These workers also reported an increase in case depth of a sample vibrated at 430 kc during a carburizing treatment. Effects of high-frequency vibrations on solid-state reactions have also been investigated by Gudzoff and Gavze6 and Fairbanks and Dewez.7 The former reported an acceleration of the age-hardening process in aluminum alloys. The latter noted changes in the structure and mechanical properties of steel annealed under the influence of vibrations. On the other hand, Altenburg4 and Ehringer5 have given some theoretical reasons and experimental evidence as to the improbability of any effect of vibrations on diffusion. Comprehensive surveys of the effects of vibrations on metallurgical reactions are given by Hiedemann&apos; and Bergmann.9 None of the above investigations led to a physical description of the effects of mechanical vibrations on solid-state reactions. In the present study an attempt was made to gain an understanding of the influence of vibrations on nucleation and diffusion. The order-disorder transformation was chosen for investigation since its mechanism has been extensively discussed in the literature. Moreover, the progress of the transformation may be easily followed by observation of electrical resistance changes. EXPERIMENTAL PROCEDURE The specimens used for the experimental observation of ordering rates were prepared from 50 at. pct Cu-Au alloy wire.* Each specimen consisted of a 0.02-in. diam wire approximately 10 in. long to which two copper potential leads were silver soldered, 2 1/2 in. apart, near one end of the wire. A 1/8-in. diam by 1/4-in. long steel stub was silver soldered

Jan 1, 1960

By W. R. Hibbard

It has been proposed1 on the basis of slip and flow that the ideal deformation texture of drawn wire for face-centered cubic metals is a (111) direction parallel to the wire axis. Under these considerations, an intermediate [loo] texture is permissible but should eventually change to the stable [Ill] orientation. This theory does not explain why copper and its alloys containing up to about 30 pct nickel, 5 pct zinc and 1 pct aluminum were found to have a double [Ill], [100] texture, while alloys with at least 8 pct zinc and 2 pct aluminum developed essentially a single [Ill] texture.1,2 It does suggest, however, that the [loo] component of the former alloys should disappear with additional deformation.3 Some evidence exists to support this suggestion. Howald4 reported that annealed copper wire previously drawn 93.8 pct and 98.5 pct developed a single [Ill] texture. Since, in wire, the drawn and annealed textures are similar, these wires probably had a single [Ill] deformation texture before annealing. In addition, although cold rolled polycrystalline copper and 80-20 brass were found to form different types of pole figures,5,6 single crystals of these metals when rolled from the stable (110) [112] orientation were found to produce essentially the same polo figure.7.8 It may be, therefore, that while the addition of solute elements changes the path by which the final texture is obtained, the final texture is not changed. Experimental Results The wires remaining from the previous investigation1 already drawn about 50 pct reduction in diameter were further drawn to 86 pct and then to 96.4 pct total reduction in diameter. The textures were determined after these stages by transmission X ray photograms taken with a copper K-alpha beam rotated 0 degrees toward the wire axis. It was found that the ratio of the [111].] and [100] intensities of the double texture in copper and its alloys containing 0.94 pct aluminum, 30.70 pct nickel, 2.61 pct zinc and 4.99 pct zinc increased from about 3:l for the 50 pct reduction to about 9:l for the 86 pct reduction. After 96.4 pct reduction, these wires exhibited essentially a single [lll] texture. Summary Thus, the drawn wire deformation texture of copper and its alpha solid solution alloys containing aluminum, nickel or zinc is essentially a single [Ill] texture as predicted by theoretical considerations of slip and flow.&apos; For copper and its alloys containing up to about 1 pct aluminum, 5 pct zinc and at least 30 pct nickel, an intermediate [loo] component is found after about 50 pct reduction in diameter, but disappears after about 95 pct reduction in diameter. For alpha solid solution alloys containing at least about 2 pct aluminum and 8 pct zinc the single [Ill] texture is developed considerably more easily and is found after about 50 pct reduction in diameter. No explanation of this compositional effect is apparent. Similar work is contemplated for cold rolled and cold compressed alloys. References 1. w. R. Hibbard, Jr. and M. K. Yen: Trans. AIME 175, 126. Metals Tech., Feb. 1948, TP 2334. 2. W. R. Hibbard, Jr. and D. E. Trout, 11: Trans. AIME 185, 620. Jnl. of Melals, Sept. 1949, TN 18. 3. W. R. Hibbard. Jr.: Disc. of R. M. Brick&apos;s paper on Deformation Textures, ASM Symp. on Cold Working of Metals, Oct. 1948. 4. T. S. Howald: Disc. of Ref. 1. Trans. AIME, 175, 126. Melals Tech. Aug. 1948, TP 2449. 5. R. M. Brick, D. L. Martin and R. P. Angier: Trans. ASM (1943) 31, 675. 6. 0. Dahl and F. Pawlek: Zlsch. Melall. (1936) 28, 266. 7. C. S. Barrett and F. W. Steadman: Trans. AIME (1942) 147, 57. 8. J. E. Burke and C. S. Barrett: Trans. AIME 175, 106. Melals Tech., Feb. 1948. TP 2327.

Jan 1, 1950