By E. Northcott, F. N. Oberg

By electrostatic separation, course Florida pebble phosphate, too lou-grade to find a ready market, can be upgraded to a satisfactory saleable product. Pebble running from 60 pct bone phosphate of time may be upgraded to 73 to 77 pct BPL depending on the mineralogical. structure of the pebble and the nature of the silica innpurity. High-grade concentrates from Florida pebble phosphate deposits have long been recovered by wet methods. When work was begun in the field, only the coarse pebble (generally +1 mm) was re- covered. In the 1920's a froth flotation process was developed to separate quartz from the finer phosphate fractions, but this method proved unsatisfactory for treating the intermediate fraction (—1 mm +35 mesh). Consequently various other processes were adapted, including agglomerate tabling and spiral separation of reagentized feed. Today the three processes are used—washing and screening for coarse pebble, tabling or spiraling for intermediate sizes, and flotation for —35 mesh material.

Jan 1, 1959

By M. Bevis, A. F. Acton, P. C. Rowlands

Defor~nation twinning and transformation twinning modes most likely to be operative in Fe-Ni and Fe-Ni-C martensites have been determined using a new theory of the crystallography of deformation t~inning.~ This analysis shows that potentially important conventional and nonconventional twinning modes1 have been omitted in previous analyses. Discussion is given on the relevance of the predicted twinning modes to the lattice invariant shear associated with the martensite transformation in steels and to anomalous deformation twinning in Fe-Ni-C martensites. THE two most important criteria which appear to govern operative twinning modes in metallic structures1 are that the magnitude of the twinning shear should be small and that the twinning shear should restore the lattice or a multiple lattice in a twin orientation. The latter criterion ensures that the shuffle mechanism required to restore the structure in a twin orientation is simple. These criteria have been adhered to in the prediction of twinning modes2"6 in bcc and bct single-lattice structures with axial ratios in the range y = 1 to 1.09 as, for example, encountered in martensite occurring in steels. Refs. 2 and 3 in particular consider the martensite transformation in steels and the twinning modes in these cases relate to transformation twinning, and hence the lattice invariant shear associated with the martensite transformation. The list of twinning modes which can be compiled from these sources is incomplete and the ranges of magnitude of shear considered could be unrealistically small, particularly in the case of deformation twinning. The latter consideration is supported by the fact that twinning modes with magnitudes of shear large compared with the smallest shear consistent with a simple shuffle mechanism have been established in, for example, the single-lattice structure mercury7 and the multiple-lattice structure zirconium.&apos; In addition the anomalous deformation twins reported by Ftichrnan4 to occur in a range of Fe-Ni-C martensites still remain unexplained. It is clear that a comprehensive analysis of twinning modes likely to be operative in martensite In steels is required. The results of the application of a new theory of the crystallography of deformation twinningg to these structures are presented in this paper. The theory has been used to determine all shears which restore the lattice or a multiple lattice in a new orientation with magnitude of shear up to a required maximum. The orientation relationships between parent and twinned lattices are not restricted to the classical orientation relationships of reflection in the twin plane or a rotation of 180 deg about the shear direction. PREDICTED TWINNING MODES Twinning modes which restore all or one half of lattice points to their correct twin positions will be referred to as m = 1 and m = 2 modes, respectively. These modes are the most likely to describe operative modes in single lattice structures. The bcc m = 1 and m = 2 modes which have magnitudes of shear s in the range s < 2 and s < 1, respectively, have been given10 and are reproduced here in Tables I and 11. Detailed discussion of the crystallography of these modes and cubic modes in general will be discussed elsewhere (~evis and rocker, to be published). The four twinning elements Kl, &,ql,7)2 as well as the magnitude of shear s are given for each twinning mode, and the twinning modes are given in order of increasing shear. Two twinning modes are given in each row of the tables, the twinning mode Kl, Kz, ql, q2 and the reciprocal twinning mode with elements Kl = K,, Ki = Kl, q: = q2, and 17; = ql. The m = 1 and m = 2 twinning modes which describe twinning shears with small magnitudes of shear and simple shuffle mechanisms in bct crystals with -y = 1 to 1.09 are given in Tables I11 and IV, respectively. On increasing the symmetry of the tetragonal lattice to cubic, that is making y = 1, all modes listed in Tables 111 and IV must reduce to crystallographically equivalent variants of the modes given in Tables I and 11, respectively, or become twinning modes with both shear planes as symmetry planes in the cubic lattice and hence not considered in Tables I and 11. With the exception of this last type of mode only those tetragonal twinning modes which reduce to modes 1.1, 1.2, 2.1, and 2.2 of Tables I and I1 are considered in Tables 111 and IV. For values of y in the range -y = 1 to 1.09 the tetragonal modes and the corresponding cubic twinning modes have approximately the same magnitude of shear. The twinning modes listed in Tables 111 and IV are therefore by the criteria given above the most

Jan 1, 1969

By J. M. Weehuizen

Complete details are given of the drilling method by which two shafts were sunk at the new Beatm&apos;x mine of Staatsmijnen in the Netherlands. The nature of the rock strata in the Dutch mining district determined choice of the drilling rather than the freezing method. Data for each step and details of the equipment used are given in the illustrations. Staatsmijnen was founded in 1902 with government financial backing, but it is run as a private enterprise, on a commercial basis, with the normal fiscal obligations. The company now has four mines in operation with annual outputs amounting to 7 1/2 million tons of coal. In 1952 it was determined that a new mine—the Beatrix—would be opened. Details of the shaft-sinking operation are described in this paper. SHAFT LOCATION The coal-bearing carboniferous rock in the Dutch mining district is overlain almost completely by soft water-bearing strata, which at the site of the new shafts are about 1600 ft thick. The sinking of the new shafts through this soft water-bearing overburden (Fig. 1) is a costly and time-consuming affair. From the two availaible sinking methods: 1) Poetsch&apos;s well known freezing method or 2) the drilling method of Honigmann-de Vooys, the latter was preferred, not only because of its relative cheapness, under the prevailing conditions, but primarily because by using the drilling process, a special type of shaft lining of steel, concrete, and bitumen could be used. The new shafts, located 330 ft apart, have an inner diameter of 18 ft, 4 1/2 in. The boreholes, which have a diameter of 25 ft and which were drilled through nearly 1600 ft of overburden and some 100 ft of carboniferous, each contain more than 29,000 cu yd—by far the largest in the world. DRILLING METHOD The drilling method is based on the use of mud-flush—a thin mixture of clay and water—to keep the borehole filled during the entire drilling period and during insertion of the lining (Fig. 2). The pressure of the mudflush against the borehole wall is greater than that of the water in the surrounding

Jan 1, 1961

By G. R. St. Pierre, A. J. Wilhelem

In connection with the reduction of hematite or magnetite to metallic iron, it appeared desirable to study the rate of reduction of each oxide to the next lower oxide under conditions which excluded all other condensed phases. For this purpose, pellets of Fe,O,, Fe,O,, and oFeOo were prepared. A gas train for the preparation of Ar-Hz-H20 mixtures was employed to establish a continuous flow of a controlled atmosphere over a pellet suspended on a balance. In this manner the following individual reduction steps could be studied: For example, pellets of hematite were reduced solely to magnetite by adjusting the gas atmosphere such that it was oxidizing to wustite. In other words, the reaction was complete when the hematite pellet had been totally converted to magnetite. The pellets were prepared from Baker Chemical ferric oxide. The ferric oxide powder was moistened and handrolled. Air sintering at 950°C produced Fe,0, pellets with a density of 3.65 g per cm3. The pellets ranged in size from 0.6 to 1.2 cm diam. The magnetite and

Jan 1, 1962

By E. A. Anderson, P. W. Ramsey, E. J. Boyle

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By Harold B. Goldman, Don Reining

The sand and gravel industry is the largest nonfuel mineral industry in the nation. In 1981, the production of sand and gravel totaled 755 million tons valued at $2.3 billion. California, which leads the nation with more than 110 million tons, together with Alaska, Texas, Michigan, and Ohio, account for 36% of the total production in the nation (Table 1). In commercial usage, sand applies to rock or mineral fragments ranging in size from particles retained on a No. 200 sieve (0.074 mm openings) to those passing a No. 4 sieve (4.76 mm openings). Gravel consists of rock or mineral fragments larger than 4.76 mm, ranging up to 88.9 mm (3 ½ -in.) maximum size. The construction industry consumes 97% of the sand and gravel produced; the remainder is sand used for specialized products such as glass (see the chapter on "Silica and Silicon"). Utilization The building industry uses sand and gravel chiefly as aggregate in portland cement concrete, mortar, and plaster; the paving industry uses sand and gravel in both asphaltic mixtures and portland cement concrete. Aggregate is commonly designated as the inert fragmental material which is bound into a conglomerate mass by a cementing material such as portland cement, asphalt, or gypsum plaster. Portland Cement Concrete Aggregates Portland cement concrete consists of sand and gravel surrounded and held together by hardened portland cement paste. Concrete mixes commonly contain 15-20% water, 7-14% cement, and 66-78% aggregate. Sand and gravel used as concrete aggregate have to meet many requirements (Goldman, 1956). Premature deterioration of concrete has been traced in many instances to the use of unsuitable aggregates. Asphaltic Aggregate Asphaltic mixtures used predominantly for paving consist of combinations of sand, gravel, and mineral filler (material finer than 0.003 in.), uniformly coated and mixed with asphalt produced in the refining of petroleum. Except for the addition of mineral filler, sand and gravel used as asphaltic aggregate must meet the same general physical requirements as materials used for portland cement concrete aggregate. General Requirements of Aggregates Construction aggregate has many requirements that are difficult to meet if only unprocessed material from natural deposits is used. Suitable material is composed of clean, uncoated, properly shaped particles which are sound and durable. Soundness and durability are terms used to denote the ability of aggre- [ ]

Jan 1, 1983

By E. V. Kleber, V. F. Novy, R. C. Vickery

The constitutional diagram has been determined in part for the sgstem Gd-Fe. Seven intermetallic compounds have been found at compositions corresponding to the following Gd-Fe ratios; 2:3, 1.2, 1:3, 2:7, 1:4, 1:5, and 2:17. The GdFe, com-pound has a congruent melting point above 18000C, whereas all of the remaining compounds melt incongruently, A eutectic exists at 13 wt pct Fe at a temperature of 860°C. ALTHOUGH an increasing amount of information is becoming available on the metallurgy of pure rare earth metals, relatively few studies have been made on alloy systems of the rare earths with the transition metals; iron, nickel, and cobalt. Even less data are extant on gadolinium alloys although it could be expected that such alloys might possess interesting structural and magnetic properties. In this paper, we report investigation of the gadolinium-iron alloy system. Studies on systems containing nickel and cobalt will be presented in subsequent papers. Previous data on gadolinium-iron compounds have been reported by Endter and Klemm1 and Jep-son and Duwez.2 Both reports agree on the existence of the GdFe2 phase, which crystallizes with the C-15type structure (face-centered cubic). This is in accord with results of the present work. EXPERIMENTAL The gadolinium metal used was prepared by met-allothermic reduction of high purity gadolinium fluoride. A typical analysis of the metal thus produced indicated the principal impurities to be oxygen, 0.24 pct, and tantalum, 0.2 pct. The iron metal used for alloying was a reagent grade material. Alloys were prepared by arc melting mixtures of the respective metals. Appropriate quantities of the two component metals were carefully weighed, blended and compacted. The compacts were then melted in an arc furnace consisting of a water-cooled copper hearth plate and a water-cooled tungsten-tipped counter electrode contained in a brass vacuum chamber. The furnace was evacuated to an absolute pressure of less than 1 with the leak rate established as being less than 20 per min. The furnace was then back-filled to a pressure of 25 mm of Hg, with a 75 pct He-25 pct Ar mixture. Arc melting at 25 v and 300 amp was maintained for about 30 to 60 sec until the entire visible area of the sample became molten, by which time surface tension had drawn the molten metal pool into a large bead. After allowing the furnace to cool, the alloy button was inverted and the melting process repeated. A series of melts was made covering entire composition ranges from 100 pct Gd to 100 pct Fe. All samples were examined metallographically in the as-melted condition. As the phase diagram became rationalized, and differential thermal analysis had given indications of temperature arrests, annealing was carried out in vacuo or in argon. Generally, compositions containing more than about 60 pct Gd were heat treated at 750°C and alloys containing less than this quantity of gadolinium were annealed at 1000°C. Prolonged annealing times were of the order of 100 to 200 hr. Metallographic examination was repeated on the annealed materials. Although little material loss was noted during alloy preparation, chemical analyses were made on all specimens prepared. The following standard, analytical techniques were used. Samples were dissolved in hydrochloric acid; insoluble material was filtered off, ignited and fused with potassium pyro-sulfate. The cold melt was leached with dilute acid and the solution thus obtained added to the main sample solution. Gadolinium was always determined gravimetri-callv as oxide from oxalate ignition. Iron was removed from an aliquot sample by electrolysis on a mercury cathode at approximately six volts. Gadolinium in the iron-free electrolyte was then precipitated as oxalate which was subsequently ignited to oxide. Iron was determined volumetrically in an aliquot solution by reduction with stannous chloride fol-

Jan 1, 1962

By G. A. Savanick

Borehole (slurry) mining, where a tool incorporating a water-jet cutter and a downhole slurry pump mines phosphate through a borehole, was field tested in northeastern Florida as part of a US Bureau of Mines program to increase the domestic availability of critical minerals. About 1.5 kt (1700 st) of phosphate ore were mined at 23.6 t/h (26 stph) from a depth of 76 m (250 ft). The borehole was filled with water during mining for roof support and to assist slurry pumping. Underwater cutting was enhanced with an air-shrouded water jet. Mined cavities were backfilled to prevent subsidence after abandonment. Roof subsidence during mining was avoided only when the cavity was filled with water. Environmental monitoring before, during, and after mining included hydrological studies and measurements of water quality. Significant water quality changes occurred only in the zone being mined and were confined to the immediate area of the borehole.

Jan 1, 1986

By J. C. Bradley

THE relation of annealing temperature to conductivity of copper wire has been determined.1 Conductivity hard was 98.26 per cent. After a 10-min. heating at 200° C. it was 98.69. By annealing 10 min. at 300° C. a large increase, to 100.93, occurred. Maximum conductivity, 101.15, was attained after a 500° C. anneal; thereafter it decreased to 100.53 after a 950° C. anneal. If copper is gassed the decrease is much more than this. MATERIAL AND METHOD The work was done on high grade electrolytic copper, 99.942 per cent. copper-plus silver, silver 0.0008 per cent. It was hot-rolled to 3 in., then cold drawn to 0.080 in. The wire was cut into 25 5-ft. lengths and numbered 1 to 25 as cut. Four samples were tested hard. The others were wound into 5-in. diameter coils. For the 100° C. heating a coil was put into water, the water brought to boiling, and the wire kept at this temperature for 10 min. For the higher temperatures the coils were placed in envelopes of sheet copper, a little water added, and the envelopes sealed by folding over the edges twice, and hammering them together. This kept the air out very well. The envelope and wire were brought to the desired temperature; this was maintained for 10 min., then the whole was water-quenched.

Jan 1, 1927

By Edmund M. Warner

Any city dweller who has walked alone along a remote mine passageway has to be impressed by the eerie silence-the total absence of noise except for one&apos;s own breathing and scuffing of boots on the bottom. An underground mine can have tremendous contrasts, from complete silence to the ear piercing clatter of percussion drills working in the mine roof. Noise in underground mining machines is both useful and detrimental. Without characteristic noises that are recognizable to miners, operators would have a more difficult job operating their machines. Noise serves as a warning of approaching machinery, and changes in noise give indication that breakdowns may occur.

Jan 1, 1979

By J. E. Johnson

OF the many items of information necessary to the successful management of the blast-furnace, few are more important than knowledge of the location and movement of the stock-line: whether the furnace is full and has. been kept so; whether the stock is settling regularly or slipping; and, if slipping, how often it has slipped, at what times, and how far at each time. To obtain these data, a man is sometimes stationed at the top of a. pair of mechanically-filled furnaces, simply to watch and gauge them by hand in the old-fashioned way. - A more recent practice is the suspension of test-rods from ropes leading over pulleys to the ground-level, where the ropes are wound on small drums with graduated peripheries and provided with crank-handles, whereby the skip-man or some other person can quickly and conveniently gauge the position of the stock-line in the furnace. I believe the credit for this great improvement belongs to Messrs. McClure & Phillips of Sharon, Pa., who were, as far as I know, the first to apply it, and who have a patent for it. The valuable indications gained by application of the Uehling pyrometer to the down-comer are Dot to be ignored; but the information thus furnished is somewhat indi¬rect, and there is no scale for the translation of "top-tempera¬tures " into " feet down." Moreover, this apparatus as a whole is delicate, and the cost of its installation and maintenance is high. If the record furnished by the Uehling pyrometer is not in the most desirable form, the test-rods, on the other hand, give no record at all, except through the memory, or notes of a man who, to say the least, is not gauging continuously, and who may omit to report an improperly low stock-line, if it be due to a fault of his own.

Mar 1, 1905

By A. L. Holley

The first session was held in the rooms of the American Philosophical Society, on Tuesday evening, February 26th. The President, Dr. T. Sterry Hunt, called the meeting to order, and after a few introductory remarks concerning the importance of theoretical and speculative science, which often involves principles of the highest economic value, and, more than all that, serves to enlarge our conceptions of the universe, and ennoble us, by the cultivation which it affords to our most exalted faculties, proceeded to discuss some points in the chemistry of the atmosphere. It is known that there is in the crust of the earth a great amount of oxidized carbon, not only in the shape of coal, but also in the graphite or plunlbago of the crystalline rocks, in the various bituminous shales or pyroschists, which are found in all succeeding rock-formations, and also in the forms of bitumen and petroleum. All the analogies of nature lead us to conclude that these various carbonaceous substances have had an organic origin, and have been generated by the deoxidation of carbonic acid, a process effected by the growing plant, and attended with the liberation of oxygen. He showed that the carbon of a layer of coal covering the whole earth&apos;s surface to the thickness of one meter, would, in its production from carbonic dioxide, liberate an amount of oxygen equal to that now present in our atmosphere. But bituminous coal contains also a large amount of hydrogen, derived from the deoxidation of water, which implies the liberation of a farther portion of oxygen. The amount from this latter source would equal, for the various coals and asphalts, from one-eighth to one-fourth, and, for the petroleums, onehalf of that set free in the deoxidation of the carbon which these hydrocarbonaceous bodies contain. From what we know of the composition of the stratified rocks, it is probable that they include an amount of deoxidized carbon and hydrogen many times greater than that contained in a layer of coal one meter in thickness, and, consequently, that the disengaged oxygen in past ages must have far exceeded that now present in our atmosphere. To this must be added

Jan 1, 1879

The first session was held in the rooms of the American Philosophical Society, on Tuesday evening, February 26th. The President, Dr. T. Sterry Hunt, called the meeting to order, and after a few introductory remarks concerning the importance of theoretical and speculative science, which often involves principles of the highest economic value, and, more than all that, serves to enlarge our conceptions of the universe, and ennoble us, by the cultivation which it affords to our most exalted faculties, proceeded to discuss some points in the chemistry of the atmosphere. It is known that there is in the crust of the earth a great amount of oxidized carbon, not only in the shape of coal, but also in the graphite or plunlbago of the crystalline rocks, in the various bituminous shales or pyroschists, which are found in all succeeding rock-formations, and also in the forms of bitumen and petroleum. All the analogies of nature lead us to conclude that these various carbonaceous substances have had an organic origin, and have been generated by the deoxidation of carbonic acid, a process effected by the growing plant, and attended with the liberation of oxygen. He showed that the carbon of a layer of coal covering the whole earth&apos;s surface to the thickness of one meter, would, in its production from carbonic dioxide, liberate an amount of oxygen equal to that now present in our atmosphere. But bituminous coal contains also a large amount of hydrogen, derived from the deoxidation of water, which implies the liberation of a farther portion of oxygen. The amount from this latter source would equal, for the various coals and asphalts, from one-eighth to one-fourth, and, for the petroleums, onehalf of that set free in the deoxidation of the carbon which these hydrocarbonaceous bodies contain. From what we know of the composition of the stratified rocks, it is probable that they include an amount of deoxidized carbon and hydrogen many times greater than that contained in a layer of coal one meter in thickness, and, consequently, that the disengaged oxygen in past ages must have far exceeded that now present in our atmosphere. To this must be added

Jan 1, 1879

By AIME AIME

DESTRUCTION of the plants, machines, utilities, tools, materials, and other essentials for peacetime living penalizes not only the owners of the materials destroyed, but the world as a whole. Specifically, the fundamental fallacy of any proposal for the in- discriminate destruction of the German industrial system is that it fails to differentiate between the wartime and the peacetime economy of the Reich. We are for one simple, clear objective-an effective industrial means to keep Germany from starting another war. This objective should not be con- fused, especially before the war is even won, with the appropriate punishment of Germany or with the international arrangements for the long future to be made around the peace table by the representatives of the Allied Nations after victory is achieved. This paper, therefore, does not deal with broad, complex postwar questions of diplomacy and international policy. "Unconditional surrender" implies disarmament of the German armies, the surrender of all arms, munitions, air- planes, and other ordnance material in stock piles or in process. It also should include the elimination of all German war production facilities, such as ordnance plants, munitions plants, and submarine works, and the control of raw materials required by war industries.

Jan 1, 1944

By C. C. Hawes

SILICA is the main impurity in iron ore. It is intimately associated with the iron oxide, sometimes free but more often in the combined state, as a mineral silicate. Its separation and purification sometimes present difficult problems to the analyst. In the absence of any definite knowledge to the contrary, orthosilicic acid. H4SiO4, is supposed to be the only silicic acid made, all other forms, such as metasilicic acid, H2SiO3, representing different degrees of its dehydration. These acids are exceedingly weak but form the most stable compounds found in nature. They are known as the silicate minerals and are formed by the combination of the different metallic oxides

Jan 1, 1936

By Y. Wang, M. M. Singh, H. L. Hartman

Knowledge of the state of stress at the bottom of a drillhole is of practical importance in rock drilling, since the induced stresses must exceed the strength of the rock in order to cause fracture. This note reports on a numerical method to determine the stress distribution at the bottom of a borehole induced by a static bit load and overburden and fluid pressures. The procedure adopted is similar to that for the plane-strain, discrete model employed by Harper and Ang.1,2 The rock medium is considered to be homogeneous, isotropic, and elastic-perfectly-plastic. METHOD OF ANALYSIS AND PROGRAMMING The discrete model adopted consists of two types of points: mass points and stress points. The configuration and numbering notation are depicted in

Jan 1, 1967

By Hiroshi Oikawa, A. G. Guy

Recent experimental evidence has shown that it is often incorrect to neglect the reactions occurring at an interface with respect to the diffusion reactions. By introducing reaction-rate constants and k for the transfer of components 1 and 2 between the a and b phases, a phenomenological description has been devised for the coupled processes of diffusion and in-terfacial reaction. An illustrative example has been analyzed with the aid of a suitable computer program. The results indicate that for kab values on the order of 10&apos;1 cm per sec and Ð values of about 10¯10 sq cm per sec, the interfacial reactions are significant during the first 10 2 to l0 6 sec of a diffusion experiment. Among the observable effects of the interfacial reactions in this case appear to be the burying Kirkendall markers and an anomaly in the initial shifting of these markers. THE study of diffusion between two phases is especially important because of its direct connection to phase transformations. For example, the transformation of austenite to ferrite involves diffusion in the a and ý phases and also an interfacial reaction (trans formation) at the a/? interface. If ferrite and aus-tenite are the two members in a diffusion couple, the same two reactions occur during the diffusion process. The numerical values obtained for the diffusion coefficients and interfacial-reaction constants from diffusion experiments can then be employed to predict phase-transformation behavior. Refinement of the calculations of phase transformation is also suggested by the present method for treating two-phase diffusion. In the recent paper by Nolfi et al.&apos; only the solute com ponent is considered in the interfacial reaction accompanying a phase transformation. The present analysis demonstrates that both components must be considered. It is generally recognized that reactions of some kind must occur at the interface in a two-phase diffusion couple, but usually it is assumed that the interface reaction occurs so rapidly that its effect on the overall process is unobservable because the slower diffusion process determines the kinetics of the process. However, Seith and Heumann 2 pointed out that effects of the interfacial reaction should always occur in the early stages of diffusion, and recently Eifert et al. 3 have shown that interfacial reactions influence the composition and motion of the interface in a/ß Al-Cu diffusion couples during the entire course of prolonged, high-temperature treatments. A general procedure for handling the combined processes of interfacial reaction and diffusion in a binary, two-phase system is to introduce kinetic coefficients for the interface reactions and to develop the system of equations governing the interlinked processes of diffusion and interface reaction. The resulting equations, although not amenable to solution in closed form, can be usefully manipulated by a digital computer. INTERFACIAL REACTIONS IN TWO-PHASE DIFFUSION Consider the general case of diffusion between two solid solutions, a and ß, which are adjacent phases in a binary system, Fig. 1. Two semiinfinite bars having compositions c1 and c0ß are jointed at x = 0. If concentrations are expressed in volume fraction,4

Jan 1, 1970

By Rudolf Gahl

Page Tests Conducted in Small Test Mill................... 577 Demonstration Tests Conducted by Minerals Separation Co....... 577 Flotation Tcsts Conducted by Inspiration Co............. 577 Sampling of Orebody........................ 578 Other Results Obtained in Small Test Mill.............. 580 Tests Conducted in Large Test Mill................... 580 Flow Sheet............................. 580 Discussion of the Value of Preliminary Table Treatment......582 Callow Flotation Installation..................... 585 Flinn-Towne ~nstallation...................... 587 Cole-Bergman Installation...................... 588 Methods Followed in Competitive Tests................ 590 Advantage of Pneumatic Flotation Machines.............. 591 Pneumatic Machines of Minerals Separation Co............. 591 Float Skimming Device......................; 594 Experimental Inspiration Flotation Machine.............. 596 Arrangement of Callow Cells in Series ................ 598 Variations of Flow Sheet....................... 599 Coal Tar as Flotation Agent..................... 600 Experience with Primary Slime.................... 602 Influence of Iron on Flotation..................... 605 Influence of Chemicals on Primary Slime............... 607 Fineness of Crushing Desired.................... 607 Operation of Large Concentrator..................... 608 Flow Sheet of Callow Sections.................... 608 Flow Sheet of Inspiration Sections.................• 609 Inspiration Flotation Machine of Steel Construction.......... 610 Minerals Separation Section..................... 613 Filter Plant............................ 613 Results Obtained in Commercial Concentrator............... 616 Tonnage............................... 616 Air and Power Consumption...................... 616 Floor Space............................ 617 Water Consumption......................... 617 Recovery............................. 618 Oil Consumption.......................... 618 Operating Costs for Flotation..................... 620 Discussion of Results Obtained.................... 620 Prospects for Futurc Development of the Flotation Process......... 621 Porous-Bottom Experiments..................... 622 Raising the Grade of Concentrates.................. 624 Recovering Carbonates by Flotation................. 624 Recovery of Silicates by Flotation.................. 627 General Theory......................... 628 Conclusion............................... 630

Jan 1, 1917

By Forrest K. Pence

Bentonite deposits are known to occur in Texas within the Jackson group of formations. This group represents the uppermost Eocene age sediments found in the coastal plain area of Texas. It outcrops across this area of the state in a narrow band of some 4 to 20 miles width. The outcrop pattern roughly parallels the present Gulf of Mexico shore line and is some 100 miles inland from the Texas shore, Fig 1. The principal bentonite deposits are found in the areas where this outcrop pattern cuts across the south-central Texas counties of Karnes, Gonzales, and Fayette. In these deposits, the better quality bentonite is found in the lower or bottom layers of the volcanic ash deposits in which they occur. Some of these better quality benton-ite~ develop very light colors upon firing and therefore justify their being classified as "white firing." The deposits in Karnes and Gonzales Counties apparently occur in commercial quantity, whereas the white firing strata so far uncovered in Fayette County have been too thin to be classified as yet as "commercial." A study of the ceramic properties of the weathered ash in Gonzales and Karnes Counties was reported in 1941.&apos; Commercial development of the deposit in Gonzales County, 7 miles east of Gonzales, Texas. was started earlier by the Max B. Miller Co. for the purpose of marketing the material as a bleaching clay, and this operation has developed to very sizable proportions. In recent years, this company has offered a specially selected grade of the Gonzales material as a suspending agent in glaze slips. The white firing property especially adapts the material to use in white cover coat enamels. The strata in the deposit are practically horizontal and consist from top to bottom of approximately 2 ft of soil overburden, 10 ft of brown bentonite, 2 ft of coarse white bentonite, and 4 ft of waxy white bentonite overlying a he grained sandstone. The & being made in the quarry is approximately one-half mile in length. Only the bottom 4 ft of waxy bentonite is being recovered, the upper layers being stripped and wasted, Fig 2. It may appear somewhat surprising that the very bottom strata appears to have been the one most completely altered. To confirm this, samples from top to bottom of the various strata were studied microscopically by R. F. Shurtz. Professor of Ceramic Engineering, University of Texas. His interpretation is to the effect that the lower part of the seam was deposited at a much earlier date than the top, and that the lower part was chemically altered to a considerable extent before the upper part of the seam was laid down. The conclusion to be derived from these examinations may be stated briefly to he that the alteration in these strata or parts of strata has proceeded independently of the alteration in other parts of the strata during a considerable geological period. The presence of gypsum and iron stain throughout all of the strata indicates that alteration is now proceeding more or less uniformly throughout. It is contended that the alteration of the original ash to montmorillonite is not a result of the presently operating processes. A deposit which occurs approximately 7 miles southeast of Falls City and just south of the village of Casta-howa, has been explored and leased by J. R. Martin, of San Antonio. Mr. Martin has conducted mining and marketing operations in bentonite for a period of many years and asserts that the white firing strata found in this deposit occurs in commercial quantities. His pit, which is shown in Fig 3, exposes 2 ft of soil overburden, approximately 5 ft of white bentonite having coarse texture, and approximately 5 ft of waxy white bentonite which in turn overlies a brown sandy clay. Here, as in the Gonzales deposit, the most completely altered portion is found at the bottom of the seam, as per following report of microscopic examination by Mr. Shurtz. Sample No. 1: This sample was taken from the top stratum which is one foot thick. It is grayish in color and it contains visible fossilized plants. The color is probably the result of fine carbonaceous material in the rock. Under the microscope the sample is seen to consist of glass and feldspar; the amount of glass predominating. Both these substances are slightly altered. No montmorillonite or other clay mineral can be identified definitely; however, the products of the slight alteration mentioned are probably montmorillonite or mineral gel. Sample No. 2: This sample was taken from the stratum second from the top. This stratum is fourteen inches thick. The sample is light gray. It shows numerous veinlets of greenish translucent material ranging from one-eighth inches wide down to the limit of visibility with the unaided eye. It has the smooth, sub-conchoidal fracture characteristic of some bentonites. Microscopically the sample consists mainly of aggregates of clay minerals. The birefringence of the aggregates is lower than would be expected if the

Jan 1, 1950