By J. D. Sullivan, Chester R. Austin, J. L. Nunes

IT is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investigators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson's1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from 1100° to I700°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxidation of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous clays burned to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,5 the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery6 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the clay, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid,i.e., the sulphur was in combination with the silica. Orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By W. M. Mobley

The coal industry in Alabama, centered in Birmingham, has pioneered coal-bene-ficiation practice in the United States. The nature of the coal seams and mining methods employed have necessitated use of equipment and methods best adapted to the local conditions. Although all of the 30 or more coal seams now being mined in the state receive beneficiation, only the three most important producers of coking coals, the Pratt, Mary Lee and Black Creek, are discussed in detail. Nature of the seams, washability characteristics and equipment used are given as examples of the extent of work and progress in this field. The coal seams in Alabama are relatively thin and pitching, making mining difficult and expensive. Most of them are characterized by thin partings of rock or shale in the seam itself, as well as laminations of bone and rash. Mechanical mining methods have increased the occlusions from roof and floor to such an extent that nearly all the coal mined in the state must receive some treatment before it can be put on the market. During the year ending Sept. 30, 1943,' 18,129,792 tons of coal were mined in the state and 14,364,177 tons, or 79.2 per cent, received treatment. Excluding from the total the 1,223,014 tons produced by small wagon mines and the hand-picked lump coal, the amount re- ceiving beneficiation would be more than 90.00 per cent. This is, by far, greater than in any other coal-producing state. The earliest record of coal beneficiation in Alabama was the installation in 1890 of an experimental Lurig washer by Alexander Cunningham, for the Sloss Iron and Steel Co. at its blast furnace in Birmingham.2 In 1894 the Jeffrey Manufacturing Co. introduced the English Robinson washer, a combination of a hydraulic classifier and centrifugal machine. Erskine Ramsay, who has contributed so much to the coal industry, saw its possibilities as well as its mechanical defects and soon had his inventive mind at work. He added a sludge tank of his own design, and many Robinson-Ramsay washers were installed in Alabama and other states. The Stewart jig appeared in 1900, followed by the Montgomery jig in 1910 and both have found extensive use. Increased interest in this field led to new designs, such as the American, Elmore, Burke and Faust. The first Baum-type Norton jig was operated in 1930 and within the last five years six large installations of this type have been made by the McNally-Pitts-burg, Jeffrey and Link-Belt Companies. Wet-washing tables were introduced in 1922 but not extensively used until recently. The two most popular types are the Deister-Overstrom and Deister Plat-O. The coal-cleaning equipment used in Alabama has been relatively simple, yet efficient, but as the amount of impurities in the raw coal has been increased by mechanical mining and labor costs have become higher, much interest has been shown in sand cones, froth flotation and

Jan 1, 1947

By W. M. Mobley

The coal industry in Alabama, centered in Birmingham, has pioneered coal-bene-ficiation practice in the United States. The nature of the coal seams and mining methods employed have necessitated use of equipment and methods best adapted to the local conditions. Although all of the 30 or more coal seams now being mined in the state receive beneficiation, only the three most important producers of coking coals, the Pratt, Mary Lee and Black Creek, are discussed in detail. Nature of the seams, washability characteristics and equipment used are given as examples of the extent of work and progress in this field. The coal seams in Alabama are relatively thin and pitching, making mining difficult and expensive. Most of them are characterized by thin partings of rock or shale in the seam itself, as well as laminations of bone and rash. Mechanical mining methods have increased the occlusions from roof and floor to such an extent that nearly all the coal mined in the state must receive some treatment before it can be put on the market. During the year ending Sept. 30, 1943,' 18,129,792 tons of coal were mined in the state and 14,364,177 tons, or 79.2 per cent, received treatment. Excluding from the total the 1,223,014 tons produced by small wagon mines and the hand-picked lump coal, the amount re- ceiving beneficiation would be more than 90.00 per cent. This is, by far, greater than in any other coal-producing state. The earliest record of coal beneficiation in Alabama was the installation in 1890 of an experimental Lurig washer by Alexander Cunningham, for the Sloss Iron and Steel Co. at its blast furnace in Birmingham.2 In 1894 the Jeffrey Manufacturing Co. introduced the English Robinson washer, a combination of a hydraulic classifier and centrifugal machine. Erskine Ramsay, who has contributed so much to the coal industry, saw its possibilities as well as its mechanical defects and soon had his inventive mind at work. He added a sludge tank of his own design, and many Robinson-Ramsay washers were installed in Alabama and other states. The Stewart jig appeared in 1900, followed by the Montgomery jig in 1910 and both have found extensive use. Increased interest in this field led to new designs, such as the American, Elmore, Burke and Faust. The first Baum-type Norton jig was operated in 1930 and within the last five years six large installations of this type have been made by the McNally-Pitts-burg, Jeffrey and Link-Belt Companies. Wet-washing tables were introduced in 1922 but not extensively used until recently. The two most popular types are the Deister-Overstrom and Deister Plat-O. The coal-cleaning equipment used in Alabama has been relatively simple, yet efficient, but as the amount of impurities in the raw coal has been increased by mechanical mining and labor costs have become higher, much interest has been shown in sand cones, froth flotation and

Jan 1, 1947

By John T. Galey

An intensified search for gas, because of the shortage in the area, led to the completion of 482 wells in southwestern Pennsylvania during 1944. This number was 27 more than the number in 1943, but 118 of the wells were nonproductive. Shallow Development Oil The initial production of the 25 producers completed was slightly less than was obtained from four wells above last yearJs total. The largest well, 20 bbl., was found in the Big Injun (Miss.) sand in Morris township, Washington County, at a depth of 2085 ft. It is currently producing about 3 bbl. per day. Outside the main producing area, a well drilled in Nicholson township, Fayette County, obtained 15 bbl. per day from 1864 to 1866 ft. in the Gantz (U. Dev.) sand. The Federal subsidy of 75¢ per barrel, effective , 1, 1944, which increased to $3.40 the current pipe-line price in this area, seems to have been insufficient stimulus to materially increase drilling for oil, although more repressuring operations are contemplated. Gas The volume of initial open flow of gas developed is off slightly over 10 million cu. ft. from 36 more wells than were completed a year ago, and the average rock pressure of this new gas is more than 100 lb. less than that obtained a year ago. Apparently the best find of this year was reported in Patton township, Allegheny County, where an initial volume of over 4 million cu. ft, was encountered in the Speechley (U. Dev.) sand at a depth of from 3293 to 3303 ft. The rock pressure there, 1190 lb. per sq. in., is nearly virgin. However, this area is fairly well delimited by dry holes and docs not seem nearly so promising from the standpoint of reserves as the Armbrust area, which was discovered several Years ago. In the patton township locality another fair well with 1303 M cu. ft. open flow and 400 lb. Per 59. in. rock pressure completed in the Hundred-Foot (U. Dev.) sand at a a depth of 2125 feet. Armstrong County, as usual, leads in number of producing wells completed with lowest percentage of failures but ranks only fou th in volume of production developed. Only two wells here had more than one million cubic feet capacity, but the rock pessure was under 200 Ib. Per sq. inch. In Fayette County, where the largest portion of new gas was found, activity appears to be shifting eastward. In Luzerne township, four producers having a total combined initial open flow in excess of 10 million cu, ft, were found in the Big Injun (Miss.) sand. The best well was found also in the same area in the Speechley sand (U. Dev.) at a depth of 3460 ft. This was a 2500-M CU. ft. well in Georges township. Several wells of more than a million cubic feet capacity were found in Jackson, Washington, Wayne and Whitley townships, Greene County. None of these, however, was in a new pool.

Jan 1, 1945

By William S. McAleer

Two major trends in the coal industry today focus attention on the need for heat-drying equipment of a simpler, more flexible and less expensive type than has been considered standard equipment for drying coal. These trends are: I. The tremendous growth in the use of mechanical equipment to load coal both in underground mining and strip mining, which necessitates efficient mechanical cleaning of the fine as well as the coarse coal and thus means a growing tonnage of washed fine coal? with its attendant moisture problems. 2. The growing consumer demand for the smaller sizes for use as domestic stoker coal, with increasingly rigid specifications covering size, ash, and moisture analyses. ACCEPTED PRACTICE In the past, when, for example, 4 in. too coal has been washed, there was little trouble in producing a washed product 4 to o with a satisfactory resultant moisture. The 4 to 3/8-in. could be taken from dewatering screens at a surface moisture ranging from 2.5 to 3.5 per cent, depending upon the size consist. The 3/8-in. to o coal was generally dewatered satisfactorily with centrifugal driers, to final surface moistures from 5.5 to 8 per cent, again depending upon size consist. The centrifugal type of drier has definitely proved itself to be the most economical type of machine to handle coal approximately 3/8 in. to o as recovered by dewatering screens or drainage elevators with 15 to 25 per cent surface moisture and turn out a product with moistures as stated above. Sometimes such moistures (5.5 to 8.0 per cent) in the product are satisfactory. If not, an ultimate moisture, lower than 3 per cent, is seldom required and the centrifugal drier removes 70 to 85 per cent of the total moisture to be removed. In certain districts there has been a growing tendency to circumvent the use of centrifugals or other types of driers, by dewatering over screens of the wedge wire type and wasting all the finer sizes. Sometimes all the minus 28-mesh has been wasted and often the size wasted has been as large as 1/8-in. By wasting these finer sizes, a lower moisture can be obtained in the finished product, but taking into account the cost of the tonnage so lost, plus the added cost of ultimately disposing of this wasted tonnage, often the cost will be greater than the cost of heat-drying in a modern plant, which makes possible the recovery of all the tonnage. Moreover, with the moisture standards for domestic stoker equipment even these wasteful approaches to its solution do not solve the problem and there remains only the alternative of heat-drying. HEAT-DRYING Until about four years ago, heat-drying of coal at the preparation plants was confined chiefly to drying the fine sizes (approximately 3/8 in. to 0). Occasional

Jan 1, 1941

By Louis A. Rosales, Kanji Ono

The anomalous behavior of hydrogen in iron is examined and a new model is proposed It is postulated that hydrogen single and di-interstitials are in equilibrium with each other. When the binding enthalpy of the di-interstitial, B, is assumed to be about 10 kcal per mole, the predicted temperature dependence of the solubility agrees reasonably well with the reported data. Effective diffusiuity is calculated assuming the di-interstitials to be immobile. Since the number of mobile single interstitials is greatly reduced at lower temperatures, the effective diffusivity is decreased. A good agreement in the temperature dependence of diffusivity between theory and experiment is provided with B - 10 kcal per mole. The predicted diffusivity is also a function of total concentration of hydrogen and this appears to be Partly responsible for the large scatter in the reported data. HYDROGEN is known to form an interstitial solid solution with iron.''' At elevated temperatures, it has been well-established that hydrogen enters iron in the dissociated form and occupies the interstices, and that diffusion of hydrogen in iron is via the interstitial mechanism. The concentration, c, permeability, P, and diffusivity, D, of hydrogen in iron have been separately determined and are consistent with each other under the steady-state condition for temperatures above approximately 400°C; that is, the relationship P = c-D holds. At lower temperatures, however, anomalous behavior of hydrogen in iron has been observed by many investigators. The results of experimental studies4-'' of the diffusion of hydrogen in iron are summarized in Fig. 1, in which the values of D are plotted against the reciprocal temperature. Although there is an increasing divergence in observed values of D with decreasing temperature, the values of D at temperatures below approximately 200°C are definitely small as compared with the extrapolation from high-temperature data. The lines shown bracket the region containing the most probable data. The observed values of c6," are plotted against the reciprocal temperature in Fig. 2, where the dashed lines represent Geller and sun's'' most probable isobars at 1 and 100 atm. At high external hydrogen pressure and low temperatures, the values of c observed are higher than those expected from high temperature data. It is generally accepted that certain trapping mechanism is responsible for the anomalies, but the nature of the trapping mechanism has not been clarified. Various types of hydrogen traps were suggested in the literature, such as "rifts" in the lattice dislocations, voids, microcracks, and so forth. However, no quantitative account of the observed behavior has been given in terms of these trapping mechanisms. Formation of methane in hydrogen-charged steel was found by ~odgurski." This appears to explain the existence of the so-called "residual" hydrogen,4 but not the observed anomalies of hydrogen in iron. McNabb and Foster' proposed a mathematical analysis in terms of a trapping mechanism. However, the physical significance of the traps was not clarified. The necessity of evaluating five parameters in their theory made comparison with experiment difficult. In the present paper, a model is proposed in which the anomalous behavior of hydrogen is attributed to the formation of hydrogen di-interstitials at lower temperatures. In this model, it is postulated that single and di-interstitials are in equilibrium with each other. (The hydrogen di-interstitial is to be distinguished from a hydrogen molecule which may exist in voids.) It can then be shown that most of the anomalies can be explained by assuming that the di-interstitials are virtually immobile and that the binding enthalpy of the di-interstitial, B, is approximately 10 kcal per mole. Predictions of the theory agree with the available experimental data reasonably well. THEORY The basic postulate of the present analysis is that single and di-interstitials are in equilibrium with each

Jan 1, 1969

By A. E. Powers, J. F. Libsch

THE simultaneous influence of time and temperature upon the tempering process in steel is well known. Hollomon and Jaffe¹ have expressed the effect of time and temperature upon the progress of tempering by a single parameter, T (c + log t); where T is the absolute temperature; t, the tempering time; and c, a constant characteristic of the steel and treatment. It was found that when hardness data for plain carbon and low alloy steels were plotted vs. this parameter, a master tempering curve was obtained which satisfied all the data for a given steel and a given hardening treatment. Roberts, Grobe, and Moersch² successfully applied the tempering parameter to various tool steels, including high speed steel for tempering times ranging from 6 min to 100 hr. The influence of tempering time and temperature upon the physical properties of high speed steel has also been extensively investigated.'" Recently, the use of induction heating for very rapid tempering treatments has received attention. The authors% have shown that tempering treatments of only a few seconds duration may be successfully applied to plain carbon and low alloy steel. However, the influence of such short tempering treatments in high speed steel has not been explored. Since high speed steel is a highly alloyed steel exhibiting physical reactions during tempering that are often relatively slow and large in magnitude, it is an interesting steel for the study of tempering reactions. It was the purpose of the present investigation, therefore, to study the early progress of reactions leading to secondary hardness in high speed steel, type 6-5-4-2, and to determine if induction-tempering treatments of a few seconds duration are able to produce results equal to those of more conventional long-time tempering cycles. Experimental Details The chemical compositions for two different heats of W-Mo high speed steel used in this study are given in Table I. Table II summarizes the heat treatment given various groups of specimens cut 21/2 in. long and centerless ground to ¼ in. diam. Hardening treatments consisted of preheating to 1600°F (870°C) for V2 hr and then oil quenching from 2250°F (1230°C). Heat I was subjected to the high temperature in a salt bath for 3 min, while specimens of heat II were austenitized in a carbon-block muffle furnace for 10 min. Specimens of series E were immediately refrigerated to — 318°F (— 195°C) in liquid nitrogen following the hardening treatment to transform the major portion of the retained aus-tenite. Specimens of series F and G were subzero cooled to — 100°F (-75°C) in a dry ice-alcohol mixture. Induction tempering was performed with a Lepel high frequency converter operating at a frequency of approximately 300,000 cycles per sec. Heating cycles were controlled and recorded for each specimen using a chromel-alumel thermocouple, percussion welded to the surface of the specimen, and a modified high speed instrument with a timer previously used and described.' Temperature oscillation of the specimens, while being held at the tempering temperature, was ± 15°F (8°C). Tempering Treatments: After hardening, specimens were tempered between 900" and 1500°F (480" and 815°C) to study the progress of retained austenite decomposition and secondary hardening. The specimens tempered in salt for 1 hr (series C, G, and I) were considered to represent conventional treatment and are used for comparison with rapid tempering treatments. Several induction-tempering cycles were employed: 1—flash tempering, i.e., induction heating to the tempering temperature and immediately cooling (series A, E, and F); 2—induction heating for 60 sec at temperature (series B); and 3—double-induction tempering by two successive heating and cooling cycles (series D). All specimens tempered by induction were heated at an initial rate of 450°F (250°C) per sec except those of series E, which were heated at an initial rate of 1300 °F

Jan 1, 1952

By J. H. Hamilton, J. R. Lewis, J. H. Dismant, W. M. Fassell

RECENTLY this laboratory undertook the task of preparing some low carbon metallic cobalt by the carbon reduction of precipitated cobalt oxides. The oxides came in two lots and had the compositions given in Table I. Industrially, cobalt rondels' are made by the carbon reduction of cobalt oxide in small reverberatory furnaces at temperatures near but not above 1050 °C. This is a slow and tedious small batch process but does give cobalt metal which is low in carbon (1 pct C). Inasmuch as these cobalt oxides were relatively low in copper and iron it was decided to reduce them with petroleum carbon in a small three-phase electric arc furnace of about 3 to 5 Ib of metal capacity. It was hoped such a procedure would save considerable time and perhaps also indicate an improved commercially feasible process. The furnace was preheated by using small pieces of carbon electrodes to maintain the arc until a temperature of 1500°C was reached. The broken pieces of electrodes were then removed and 500 g of the cobalt oxides and 60 to 100 g of petroleum coke added. At the end of the reduction reaction, a high lime flux was added to the furnace to facilitate the removal of sulphur. Due to the fineness of the cobalt oxide powder used and also to the presence of chlorides there was considerable dust lost in charging the furnace. This was overcome by preparing briquettes composed of the cobalt oxides, charcoal, and a little bentonite to serve as a binder. The results obtained are summarized in Table 11, which shows that the cobalt metal produced in the arc furnace was high in carbon varying from 2.5 to 3.5 pct. This, of course, is much too high. For certain uses, such as in the preparation of permanent magnets, the carbon content of cobalt must be low. It was necessary therefore to find an effective method of reducing the carbon content of the cobalt that had been prepared in the arc furnace. Van Arkel3 recommends the use of Co2O3 as a means of removing carbon from cobalt. Experiments by the authors indicate that carbon is removed with difficulty by this method. Other methods used, including lancing of the molten high carbon cobalt with a jet of oxygen, proved to be ineffective. The method finally used makes use of the fact that cobalt metal is decarburized by carbon dioxide at the temperature of the molten metal. Two methods were used: 1—carbon dioxide was bubbled up through the molten cobalt, and 2— molten cobalt was maintained in a carbon dioxide atmosphere. In the first method the gas was introduced below the surface of the molten metal by means of a quartz tube. A high frequency induction furnace was used to keep the cobalt molten in both of these experiments. This kept the metal somewhat agitated and no doubt was an important factor in hastening the decarburization 'process by the second method. Both methods gave satisfactory results as shown in Table 111. An interesting observation in connection with this 'work was that a small sample of carburized cobalt metal could be decarburized by heating it with an acetylene torch adjusted to give an oxidizing flame. This may have been due to the presence of carbon dioxide in the products of combustion. Samples of molten high carbon steel were decarburized by the same method and it is suggested that nickel and perhaps manganese can be decarburized in a similar manner. Additional work, including rate studies and other theoretical aspects of this problem, is in progress in this laboratory.

Jan 1, 1953

By AIME AIME

The following report is published for the information of the members: Meetings. Two meetings for the reading and discussion of papers, etc., have been held during the year 1907-namely, the Ninety-second meeting, held April 16 to 20 in New York, N. Y., and the Ninety-third meeting, held July 23 to 30 in Toronto, Canada. The proceedings of these meetings, including descriptions of the entertainments and excursions connected therewith, have already been published and distributed to the members of the Institute; the New York meeting in Bi-Monthly Bulletin, No. 15, May, 1907, pp. 541 to 559, and the Toronto meeting in Bi-Monthly Bulletin., No. 17, September, 1907, pp. 847 to 875. In addition to these " Proceedings," there were also published in Bi-Monthly Bulletin, No. 15, May, 1907, an illustrated description of the United Engineering Society building (p1 vi. to xxvi.), and a record of the exercises attending its dedication, including the addresses of Andrew Carnegie, Arthur T. Hadley, Samuel Sheldon, Frederick R. Hutton, John Hays Hammond, and T. C. Martin (pp. xxxviii. to lxv.). At the New York meeting, 43 papers and- discussions were presented, and the names of 297 members and guests were registered at the Institute headquarters., this number, however, does not represent all who were present at the sessions and excursions. At the Toronto meeting, 23 papers and discussions were presented. The number of members and guests registered at the Toronto headquarters was 191, which doubtless does not include the names of all who were present at the sessions, or took part in the numerous excursions and visits around Cobalt.

Mar 1, 1908

By Joseph F. Oesterele, Richard S. McCaffery

This investigation was undertaken to determine the quality of different iron blast-furnace slags as desulfurizing agents, and the possibility of using, in the blast furnace, materials of higher sulfur content than is now common. The solution of the problem would render possible the use of higher sulfur iron ores for pig iron and cokes containing more sulfur than now employed, and the economic manufacture of irons and steels of lower sulfur content. It is generally assumed that the sulfur that reaches the lower part of the iron blast furnace is removed from the pig iron by combining with lime to form calcium sulfide. Most of the sulfur introduced with the charge is in combination with iron or manganese or, perhaps in the coke, as a carbon compound.1 The iron and manganese sulfides are more soluble in the iron than is calcium sulfide, and as the latter is generally said to to be more soluble in the slag than the iron and manganese sulfides, this greater solubility of calcium sulfide in the slag tends to free the metal from sulfur. This greater solubility of the calcium sulfide is used not only to reduce the sulfur contents of the pig iron in the blast furnace, but by this means also low-sulfur steels are produced in the open-hearth and electric furnaces. The reaction2 FeS + CaO + CO = Fe + CaS + CO2 requires a high temperature and strongly reducing conditions in the presence of lime. The constitution of blast-furnace slags, first studied scientifically by Vogt13 indicated certain ranges of composition of the slag in which a

Jan 1, 1923

By Richard S. McCaffery, Joseph F. Oesterele

This investigation was undertaken to determine the quality of different iron blast-furnace slags as desulfurizing agents, and the possibility of using, in the blast furnace, materials of higher sulfur content than is now common. The solution of the problem would render possible the use of higher sulfur iron ores for pig iron and cokes containing more sulfur than now employed, and the economic manufacture of irons and steels of lower sulfur content. It is generally assumed that the sulfur that reaches the lower part of the iron blast furnace is removed from the pig iron by combining with lime to form calcium sulfide. Most of the sulfur introduced with the charge is in combination with iron or manganese or, perhaps in the coke, as a carbon compound.1 The iron and manganese sulfides are more soluble in the iron than is calcium sulfide, and as the latter is generally said to to be more soluble in the slag than the iron and manganese sulfides, this greater solubility of calcium sulfide in the slag tends to free the metal from sulfur. This greater solubility of the calcium sulfide is used not only to reduce the sulfur contents of the pig iron in the blast furnace, but by this means also low-sulfur steels are produced in the open-hearth and electric furnaces. The reaction2 FeS + CaO + CO = Fe + CaS + CO2 requires a high temperature and strongly reducing conditions in the presence of lime. The constitution of blast-furnace slags, first studied scientifically by Vogt13 indicated certain ranges of composition of the slag in which a

Jan 1, 1923

By Toshihisa Adachi, Shosei Serata, Shunsuke Sakurai

The present state of knowledge of three-dimensional rock properties does not provide an adequate basis for evaluating the safety of under- ground structures in situ. Most of the triaxial studies reported in the past have dealt with crushing strength, but have failed to consider the intergranular behavior and triaxial strain state of rocks. Without this information, the structural competence of rocks cannot be accurately assessed. The absolute three-dimensional testing method (ATT) was conceived for the purpose of analyzing the three-dimensional states of stresses and strains in aggregate rocks under conditions commonly encountered in underground structures. In-situ stress-strain states are not simple, even in the simplest possible form of opening, excavated in a homogeneous and isotropic rock medium. In general, there are four basic stress-strain states which are present in underground openings, regardless of the complexity of their geological conditions. They are the yielded, brittle-fractured, stress-relieved, stress-concentrated states, as illustrated in the schematic diagram, Fig. 1. The ATT machine was designed to create and study all these states in the laboratory. A theory describing the aggregate behavior of rocks under these diversified states is essential to evaluate the safety of underground structures. The Griffith theory is limited to tensile failure of ductile materials and therefore does not apply to behavior of aggregate rocks under compression. The Griffith theory also fails to consider the grain boundary characteristics of aggregates, which is the determining factor of rock behavior. The Mohr-Coulomb theory of failure ignores the importance of the intergranular behavior of rocks. An application of the continuum theory to

Jan 1, 1972

By J. H. Ffolliott

ALL of the prospects that later became mines in the Ducktown district were discovered prior to 1854, and most of them were exploited before the turn of the century. It is the purpose of this paper to discuss the exploration and current development of the Boyd mine, discovered in 1853. It is in the heart of the Ducktown Basin, in the extreme southeast corner of Tennessee, and is being developed by the Tennessee Copper Co. GEOLOGY The geology of the district has been fully described in many papers. Probably the most complete description is that of Emmons and Laney.I The rocks of the district are considered to be of Lower Cambrian age and are a part of the Great Smoky formation, consisting mainly of interbedded graywacke and mica schist, in which the ore deposits occur. The ore bodies are included in an area of about 6 sq. miles, 2 miles wide and 3 miles long striking N. 45° E., and may be grouped into three general lode systems. The northeast system, including the East Tennessee, London and Burra Burra ore bodies, and the southeast group, comprising the Polk County, Mary and Calloway deposits, are all characterized by relatively high copper values. The ores of the central system, which includes the Eureka, Boyd, Old Tennessee and Cherokee ore bodies, are low in copper and high in total sulphide content. Boyd mine lies roughly halfway between the Old Tennessee and Eureka ore bodies [ ] and 2500 ft. in the hanging wall of the Burra Burra mine (Fig. 1). Elevation of the surface is about 1725 ft. above sea

Jan 1, 1942

By Sidney A. Swensrud

The writer has been interested for some time in trying to appraise our industry's prospects for gasoline consumption over the next half dozen years or so. Anyone who has even approached the problem knows the intimate relationship to it of the number of automobiles in use— by automobiles I mean both passenger cars and trucks. Probably at least 90 per cent of our gasoline is used in automotive vehicles. Some recent estimates secured from the Department of Commerce show the following breakdown: Per Cent Passenger cars............................................ 60.0 Trucks................................................... 27.4 Busses................................................... 2.9 Taxicabs................................................. 2.2 Subtotal............................................... 92.5 Aviation, motor boats and railroads......................... 0.5 Agricultural: farm tractors, etc.............................. 3.3 Balance (manufacturing, government use, construction, etc.)... 3.7 100.0 Up to the beginning of the depression there was, of course, a constant annual increase in the number of automobiles in use, for each year the industry added to the total inventory or ''population" more new units than were being scrapped, as may be seen in Fig. 1. Few of us in the oil industry needed to give much attention to the detailed figures, although the automobile industry seemed to interest itself in all sorts of calculations of replacement demand vs. new car demand, the average life of the car, the number scrapped, and the like. Probably many people in the oil industry, as well as outside it, were surprised at the way in which automobile registrations and gasoline consumption held up during the early years of the depression. Nor were they greatly perturbed when, as in the last two years, both registrations and consumption began to fall somewhat. That was natural enough; it

Jan 1, 1933

By A. S. Michaels, M. C. Porter, A. Stancell

Previous laboratory studies have demonstrated that the injection of small quantities of reverse wetting agents during water displacement can increase oil recovery from unconsolidated porous media.9 In the present investigation, an attempt has been made to determine more fully the effects of reverse wetting treatments and to clarify the mechanism by which increased oil recovery is effected. Water-oil displacements were performed in beds of 140-200 mesh silica sand. Hexylamine slugs (injected after 0.25 pore volume of water throughput), when adequate in size and concentration, were effective in promoting additional oil recovery. Their effectiveness increased with the quantity of amine injected. However, slugs of sufficient size and concentration to stimulate oil production at water flow rates of 34 ft/day did not do so at 4 ft/day. Visual studies in a glass grid micromodel have shown that the stimulation of oil production, via ayueous hexylamine, is a result of transient changes in the oil wettability of the pore walls. if the amine slug is of sufficient size and concentration to induce significant changes in the adhesion-tension, large continuous oil masses will be formed. if the superficial water velocity is high enough to result in rapid desorption of the amine, a favorable "wettobility gradient" may be established across the masses; under such conditions, high oil mobility is observed, and increased oil recovery results. INTRODUCTION It is generally agreed that the efficiency of oil displacement by water in porous media is limited in part by capillary forces which cause the retention of isolated masses of oil — resulting in the so-called "irreducible minimum oil saturation". Recent estimates10 indicate that there are about 220 billion bbl of petroleum in United States reservoirs which are not economically recoverable with present techniques (such as water flooding). This amounts to almost five times the known recoverable reserves. It has been recognized for some time that a suitable alteration in the water-oil interfacial tension and/or the contact angle, as measured between the water-oil interface and the solid surface, should result in better displacement efficiency. Surface active agents can be used as interfacial tension depressants to accomplish this objective,1,2,7 but unfortunately, the additional oil recovery is seldom commensurate with the treatment cost. In contrast to interfacial tension depressants, the effect of contact angle alterations on water-oil displacements has received relatively little attention in the literature. It is known that the wettability affects the displacement process.3,4,11 Displacements in water-wet systems generally result in lower residual oil saturations than those in oil-wet systems. The effect of "'transient" wettability alterations concurrent with the displacement process have been investigated by Wagner, Leach and coworkers,4,11 wherein it has been demonstrated that the establishment of water-wet conditions during water flooding of oil-wet, oil-saturated porous media is accompanied by significant increase in oil displacement efficiency. Michaels and Timminss studied the effects of transient contact angle alterations resulting from chromatographic transport of reverse wetting agents through unconsolidated sand. It was demonstrated that chromatographic transport of short-chain (C4 through C8) primary aliphatic amines can improve oil recovery and that the recovery increases with the quantity of amine injected (i.e., with either the amine concentration or the volume of the slug injected). Circumstantial evidence indicated that the increased displacement efficiency resulted primarily from transient changes in wettability of the porous medium. In the Present investigation. additional information has been obtained on the effects of reverse wetting treatments and the mechanism by which increased oil recovery is accomplished. Hexylamine slugs of varying size and concentration were chromato-

Jan 1, 1965

By D. S. Rowley, F. C. Appl

Assuming that rock behavior, during cutting with a single diamond, may be approximated by that of a rigid, Coulomb, plastic material, a theory of single diamond cutting action has been developed. Using this theory, the stresses on the diamond cutting surface and the components of the cutting force have been determined. Theoretical results agree reasonably well with available experimental data. The theory of cutting of single diamonds may be used as the basis for subsequent study of the perfonnance of surface set diamond drill bits and other surface set diamond cutting tools. INTRODUCTION For more than twenty years, surface set diamond bits have been used successfully in the mining and petroleum industries to drill and core rock formations that range from medium hard to the hardest known formations. Most extremely hard rock formations cannot be economically drilled or cored by any other means. In view of the growing use and importance of surface set diamond drill bits, it is reasonable to study the way in which these tools cut, and the factors that influence wear of the diamonds. Such knowledge will contribute to better bit design and will improve operating procedures. To analyze the cutting performance of these tools it is appropriate to consider the way in which an individual diamond cuts. Once this is established, the over-all performance of the bits can be determined by considering the total effect of the individual diamonds. In recent years there has been a growing interest in rock mechanics and there now exist several publications dealing with the deformation and failure of rocks. Notable experimental work has been reported by Bredthauer,1 Handin and Hager,2, 3 and Gnirk and Cheatham.4 An extensive collection of data pertaining to rock properties at low confining pressures has been given by Wuerker.5 Cheatham and Gnirk have recently presented an excellent review of the state of knowledge regarding analytical and experimental rock deformation and failure.6 Generally rocks are extremely weak in uniaxial tension, and weak or only moderately strong in uniaxial compression. Both tensile failure and compressive failure are generally brittle in nature. This means that there is little or no deformation or "flow" of the material before shear or tensile fracture occurs. Thus, until fracture occurs, rock behaves very nearly like an elastic material in uniaxial stress. Significant changes in behavior of rock occur under conditions of triaxial compressive stress. There is generally a marked increase in compressive strength and in ductility. It has been demonstrated that the failure becomes plastic (in a macroscopic sense) at sufficiently high values of confining pressure. Sharp wedge chisel indentation studies conducted by Gnirk and Cheatham indicate that many rocks behave in a plastic manner at relatively low triaxial compressive stress states.4 If "failure" under triaxial compressive conditions is considered to be either complete rupture or macroscopic plastic flow, then the general failure characteristics of a rock can be reasonably well represented by the commonly known Mohr envelope. This certainly is not a perfect failure criterion (since the effect of the intermediate principal stress is neglected) but it has been found to be adequate for most engineering purposes. Mohr envelopes usually are constructed graphically using experimental triaxial test data. For purposes of analysis it is convenient to represent the envelope in equation form. Among the several approximate forms appearing in the literature, a parabolic form is suggested by Cheatham,7 and an exponential form is suggested by Paone and Tandanand.8 The exponential form has been adopted for this study, and based on published data, appropriate parameters have been established for 19 rock types. A typical plot of the data compared with the approximate envelope, and a summary of the rock properties and

Jan 1, 1969

By Frederic L. Kadey

Perlite, as a volcanic glass, has been recognized since the Third Century, B.C. (Langford, 1978). The precise details of discovery often become lost in antiquity, and the variations among the stories pertaining to the more recent discovery of perlite as a material of commerce are no exception. Credit in the United States is given to a dentist who, while experimenting with tooth enamels about 1941, discovered that perlite-the rock-intumesced when subjected to heat. At about the same time it is reported that the chief geologist of Silver and Barytes Ores Mining Co. attempted to put out a picnic bonfire on the shores of Milos Island, Greece by throwing beach sand on it. The ensuing pyrotechnic display immediately conjured up in that man's mind the possibility of a new use for the volcanic rock that constituted most of the island. Very little was done with this discovery either here or abroad until after World War II. Today the name perlite is applied to both the hydrated volcanic glass, generally of rhyolitic composition, and to the lightweight aggregate that is produced from the expansion of the glass after it has been crushed and sized. Petrologically, it is defined as a glassy rhyolite that has a pearly luster and concentric, onionskin parting. Occurrences of perlite are restricted to several Tertiary to Quaternary age rhyolitic belts that trend in a generally north-south direction around the world. Commercially suitable deposits generally occur as domes of several hundred feet in height, although glassy zones in welded ash-flow tuffs and others associated with dikes and sills also have been reported. Mining is by ripping and blasting from open pits. Because of weight considerations, perlite usually is shipped to the local market area for subsequent expanding. In the United States, New Mexico leads in production with Arizona, California, Nevada, Idaho, and Colorado following in approximately that order. The principal use for expanded perlite is as a lightweight insulating aggregate in cryogenics, in plaster, concrete, and in loose fill insulation. Expanded perlite is also used in horticultural applications, and after subsequent milling and classification, as a filter aid. The United States is the world's largest producer and consumer of perlite. Table 1 shows the world production of perlite and Table 2 shows the perlite mined, processed, expanded, and sold or used by producers in the United States. Geology Composition and Morphology Any discussion of perlite must take into consideration its dual nomenclature, for it is known by the same name as both the naturally occurring rock and, after processing and expansion, as the lightweight aggregate of commercial significance. In its naturally occurring form, perlite is a rhyolitic glass that contains from 2 to 5% combined water. While perlite also can occur as andesitic or dacitic glass, these latter types are of negligible commercial significance. Table 3 lists the chemical composition of a few typical perlites (Anderson, et al., 1956; Langford, 1979). What sets perlite of commercial significance apart from other volcanic glasses is the fact that under the proper conditions of preparation-crushing and sizing-it will, when rapidly introduced into a flame of sufficient temperature, expand or "pop." All of the elements of composition contribute to the expansibility of the rock. The role of the combined water, however, is the most significant because it is believed not only to produce a fluxing effect in the softening of the highly siliceous glass prior to expansion, but it is also responsible for the explosive force of expansion through volatilization during heating. The current theory of the origin of the water in perlite is now less con-

Jan 1, 1983

By J. R. Dawson, J. A. Glunt

VESTA No. 4 and 5 mines supply most of the high volatile coal required for Jones & Laughlin's byproduct coke plants. Until 1944 all coal produced in these mines was loaded by hand. Pressure to mechanize at Vesta was brought on by the manpower shortage in World War 11, and in 1943 a decision was made to change to mechanical loading. It was the opinion of those concerned that by use of selective mining the coal would be clean enough to be processed by the existing preparation plants. At that time coal cleaning at Jones & Laughlin consisted of hand picking the larger sizes at the mine tipples and wet washing at plants located at the Pittsburgh and Aliquippa Works. A typical section of the Pittsburgh seam as it occurs at Vesta is shown in Fig. 1. The 14 to 16 in. of drawslate immediately over the coal is too soft to be used for roof and must be taken down, leaving the rooster coal just above for roof. In selective mining an attempt is made to mine the coal under the drawslate first and then load out the drawslate separately as refuse. In full seam mining slate and coal are shot down at the same time and loaded out. Mechanical loading at Vesta created new problems. It was found that selective mining, even when carefully applied, increased the refuse in the raw coal to such an extent that the washers at the mills were unable to handle it. Large tonnages of refuse were being transported, a reject disposal problem was created, and good metallurgical coal was being loaded out and lost. In addition, the selective method handicapped operation of the loading machines. Fig. 2 shows how the ash content of the raw coal increased as mechanization proceeded at No. 5 mine. New Preparation Plant: After an exhaustive study of this situation by J & L management, is was decided that a preparation plant should be constructed at the mines, capable of handling full seam mined coal and large enough to process full production of both No. 4 and No. 5 mines. It was decided that from the standpoint of inside operation and haulage the new plant should be located as near as possible to the old No. 5 tipple on the Monongahela River near Vestaburg. Full seam mining at Vesta could be expected to produce a tremendous volume of refuse along with the coal, since 14 to 16 in. of slate would be mined with an average 78 in. of coal. Disposal of this refuse required serious consideration in selecting a plant site. The only area near Vestaburg large enough for disposal of the plant refuse was across the Monongahela River at LaBelle. Ample space was available here, and construction at this location would not interfere with operation at the No. 5 tipple. It had been noted over the years that the sulfur content of the coal produced at Vesta was gradually increasing, and there was every indication that this increase could be expected to continue as the mines developed further from the river. It was decided to construct a three-part separation plant with complete blending facilities to produce both metallurgical and steam coal. In this system an attempt is made to reduce the sulfur in the metallurgical coal in a secondary cleaning process. Construction of the new preparation plant got under way early in 1947 and continued until the spring of 1950. The plant was designed to handle 2400 tph of raw coal containing 30 to 35 pct refuse. Cost of outside buildings and equipment was about $14 million. Total cost of the plant, together with improvements and changes made at this time, was approximately $21 million.

Jan 1, 1957

By Z. F. Oszter

This paper discusses the materials handling problems encountered in cement plants in the areas of raw and finished product grinding and cement storage. It illustrates by examples taken from actual installations, how optimum feed rate is maintained in grinding circuits with properly applied bin dischargers (vibrating hoppers, Mexican feed boxes and aerated bin bottoms) for materials with high moisture content and/or difficult handling characteristics. Initial operating problems with the equipment will be discussed and maintenance requirements will be indicated for comparison purposes. In a modern cement plant, properly functioning bins and feeders are as essential as process control, for no process control system, however sophisticated, can perform efficiently if raw materials do not flow into the plant processing facilities at the required time and rate. Most materials used in the manufacture of portland cement - such as silica sand, iron ore fines, crushed limestone, gypsum, clinker or cement itself-have difficult handling characteristics under specific conditions. High moisture content or even dampness due to condensation may create bin hang-ups, arching and ratholing, all of which result in improper functioning of the feeders or proportioning equipment. The occurrence of these problems in existing cement plants spurred a search for the corrective devices discussed in this article. The equipment investigated included bin dischargers in the form of vibrating hoppers for moist raw materials, Mexican feed boxes for clinker and aerated bin bottoms for cement. Operating experience with different types of bin dischargers showed that the actual performance of some did not come up to the expected level under prevailing operating conditions. The aim of this paper is to record the results of this experience and there- by aid designers and/or operators in selecting the most suitable equipment for their requirements. BIN DISCHARGERS (GENERAL) A discharger is a device that causes stored solids to flow out of a hopper without metering the rate of flow as a feeder does. The investigation discussed here encompasses the following types of bin dischargers used in a cement plant: (1) vibrating hoppers (horizontal motion), (2) whirlpool hoppers (horizontal and vertical motion), (3) aerated bin bottoms (air fluidization), and (4) Mexican feed boxes. Most of the bins used in the cement industry are of the plug flow type. Raw materials with difficult handling characteristics such as high moisture content may cause flow problems when fed through small openings (12 x 18 in.), even if two walls of the bin are vertical.' The most appropriate solution to these flow problems would be the installation of separate mass flow bins for the different materials such as silica sand, iron ore fines, crushed limestone and gypsum, with each bin correctly designed from test data obtained by measuring the flow properties of representative samples. However, limited storage capacity and plant space usually preclude this approach. Quantitative design of bins for flow based on measured flow properties of representative samples of the bulk solid to be handled is no longer an "engineering art," thanks to the basic research done on the flow of bulk solids in bins during the last decade.2, Where space limitations exist, however, or where improvements are being sought for equipment already installed, bin dischargers offer a satisfactory solution to flow problems. They can be applied effectively under flat-bottom bins or mounted to existing plug-flow bins with very little modification to these facilities. In both the foregoing cases, plug flow will be maintained, but the flow channel will be considerably increased so that it is larger than the discharger's bin-side diameter, and material flow can be sustained if the discharger is correctly selected. The main purpose of a bin discharger is to draw the bulk solids across the whole area of the bin outlet, to make the opening fully effective. As long as the bin-side opening of the discharger is large enough

Jan 1, 1969

By L. O. Storey

The McDermitt mine was found as a separate mercury ore-bearing occurrence approximately 305 m (1000 ft) northeasterly and in a different geologic setting from the old Cordero mine, which had been the district's major producer. The following briefly describes the discovery of the new deposit and the Placer Amex lnc. involvement. The Cordero mining property was under lease by Sierra Mineral Management from the owner Fred H. Lenway in February 1971, when the property was brought to the attention of Placer Amex Inc. (known at that time as American Exploration and Mining Co.) by Richard F. Hewlett of Sierra Mineral Management. The property was first examined by Amex geologists in the spring of 1971, who reported favorably on the project. During that year, Sierra Minerals Management had retained Dr. Larry Walters as a consultant. He proceeded to drill test mercury soils anomalies which he had found northeast of the old Cordero mine in an area overlain by recent alluvium and gravel. An area known as the D area was subsequently blocked out and ascribed a tonnage of about 18 1 kt (200,000 st) which occurs in the vicinity of the eastern edge of the currently defined McDermitt ore body. This mineralization was found in flat lying mercury-bearing lakebeds, unlike the steep structurally controlled ore which was mined in the old Cordero mine. It became apparent to Placer Amex that since the chances of much more extensive ore were good in such a geologic environment, additional exploration was warranted. A joint venture was formed in October 1972 by American Exploration and Mining Co. and Sierra Mineral Management to further explore the Cordero property. The project exploration was fully funded and managed by Amex. Sampling began by Placer Amex in the D area where an open trench had exposed the lakebed ore. Visible cinnabar could not account for the high-grade mercury assays taken from the trench, and an unknown mercury mineral was suspected. Subsequent work established the presence of a chlorine-bearing mercury sulfide which may have enriched the lakebeds as a secondary supergene mineral. Early identification of the mercury-bearing mineral corderoite (Hg3Cl2S,) aided in the geologic concepts for the ore occurrence and was helpful in exploring for the expansion of the D area. Corderoite was found occurring with cinnabar in the lakebeds, and in places it is a major contributor. Specimens of the unique ore were given to Dr. Eugene E. Foord and Dr. Pieter Berendsen at Stanford University, who subsequently identified the chemical and crystallographic makeup of the new mineral and described it for the first time as a naturally occurring substance. Metallurgical work on mercury recovery from the newly described mineral was carried out by the Placer Development Ltd. laboratories in Vancouver, and an acceptable recovery system was worked out together with a planned mill design. Step out drilling from the D area by Placer Amex Inc. encountered extensive flat lying lakebed ore. The McDermitt ore body, as subsequently defined by drilling, was found to contain 2.7 Mt (3 million st) of open pittable ore, containing approximately 5 kg/t (10 lb per st) Hg. The ore body gently dips to the north and is found lying mainly in claybeds just above an opalite breccia blanket which overlies the earlier volcanics. Some ore is also found in the opalite breccia. The mine and mill were constructed under an operating joint venture with Placer Amex Inc. and Sterling Mineral Ventures, and production began in June 1975 at the rate of 20,000 flasks per year. The mine is currently in progress.

Jan 1, 1985