By S. R. Goodman, Hsun Hu

A detailed study of texture developmenf in poly crystalline copper atzd 70-30 brass has been completed. Textural changes as a function of deformation are shoum by pole jigmres and by intensity measurements oF- various rejlectiotzs from the rolling plane and the rolling direction. These examinations were accompanied by measurements of stacking fault frequency, hardness changes, and microstructure. Some of the results were briefly presented earlier. Additional results reported here are consistent with the idea that deformation faulting or slip by partial dislocations is of primary importance in the formation of deformation textures in fcc metals. lo examine the idea that deformation faulting is of primary importance in determining whether the texture is the copper type or the brass type an extensive study of the development of polycrystalline textures in copper and 70-30 brass was initiated. Besides the determination of complete pole figures, the intensities of the various reflections from both the rolling plane and the plane perpendicular to the rolling direction, the peak shifts due to deformation stacking faults, and the hardness of the rolled specimens were examined at various reductions from 10 to 99 or 99.5 pct. Mi-crostructures were examined by transmission electron microscopy. Some of the results were briefly presented in an earlier publication.' Since then, additional information has been obtained. This is given in the present paper. EXPERIMENTAL PROCEDURE Material and Specimen Preparation. The material used was a commercial electrolytic copper bar 1i in. wide and 2 in. thick and a 70-30 brass bar la in. wide and 1i in. thick. Chemical analysis indicated a purity of 99.97 pct for the copper, with 0.025 pct 0 as the major impurity. The 70-30 brass was of higher purity with 0.0016 pct 0 as the major impurity. Extreme care was taken in the preparation of the starting material to insure uniformly fine grains with a nearly random initial texture. The two bars were first cold-forged and then annealed to eliminate any original texture. The grains were then refined by several cold rolling (approx 30 pct reduction) and annealing treatments. The + -hr anneals were carried out in a salt bath at 390" to 440°C for copper and at 490°C for brass. The resulting penultimate grain size was 0.06 mm for copper and 0.03 mm for brass, and both showed very little preferred orientation. The number of prior cold rolling and annealing cycles was such that the final thickness after various final reductions of 10 to 95 (for brass) or 99 (for copper) pct was the same (0.020 in.). These annealed strips were rolled in two directions by reversing end for end between passes according to the following schedule: 0.006 in. per pass to 0.100 in., 0.003 in. per pass to 0.050 in., 0.002 in. per pass to 0.025 in., 0.001 in. per pass to 0.020 in. Texture Determination. The development of rolling textures was studied by examining complete pole figures determined from the (111) reflection. Specimens thinned from one face of the strip to half thickness (0.010 in.) were used to obtain the central portion of the pole figures, while specimens thinned from both faces to 0.003 in. were used to obtain the peripheral portion. The reflection and transmission techniques have been described previously. In addition to X-rav pole figures, texture development was also studied b; examining the intensity variation of the (Ill), (200), (2201, (311), (331), (420), and (442) reflections from the rolling plane and from the plane normal to the rolling direction, as a function of deformation. The same specimens used for the central portion of the pole figures were used for the intensity measurements of the various reflections from the rolling plane. For intensity measurements from the plane normal to the rolling direction, composite specimens were prepared by mounting sections cut parallel to the transverse direction of the strip. An epoxy resin was used to bond these sections together, and the entire composite was then mounted in a cold-setting resin to facilitate subsequent polishing and etching to remove distorted metal at the cut. The intensities were expressed in units of the integrated intensities measured from an annealed copper specimen having almost no preferred orientation. Stacking Fault Frequency Determination. Following the analysis of Warren: the stacking fault frequency, a, was determined from the change in the peak separation (A%) of two neighboring reflections of a deformed specimen, as compared with the normal peak separations of a fully annealed specimen. To obtain sufficient intensities for the second-order reflections, (222) and (400), composite specimens were prepared from parallel sections cut from the strip at 30 deg to the rolling direction for copper and 25 deg for the brass.* From texture data, these sections are known to contain a large population of both (111) and (200) planes. Since residual stresses can also cause X-ray line shifts (the direction of line shifts depends upon the sign of the stress), the use of composite specimens consisting of sectioned planes should help compensate for these effects as the residual stresses change sign from the surface to the central section of a rolled strip. Since the amount of peak shift is almost un-measurable in brass rolled 15 pct and in copper rolled

Jan 1, 1969

By Robert B. Smith

The South Texas Mineral Trend is now estimated to contain uranium reserves of 150 million pounds U308 . Within the past year, an estimated 10 million pounds U308 have been added to this gross reserve. It is probable that a similar amount has been identified in previously unknown orebodies that, as yet, have not been delimited or announced. Exploration that was limited in the past to a narrow band containing only the known trend has now expanded into older sediments updip and into younger units towards the coast. Uranium host formations are also now being explored at a considerable depth and distance eastward from known deposits. Only about 30 percent of the potential uranium host rocks in South Texas have been adequately explored. Geology The South Texas uranium deposits are confined mainly to sediments of the Tertiary system. Reserves are divided almost equally between the Whitsett Formation of the Jackson Group, the Catahoula Formation, and the Oakville Formation. A minor amount of the reserves occurs in sands of the Goliad Formation which may be either in the Tertiary or Quaternary Epoch. Figure 1 is a geologic column of the South Texas uranium host formations. These producing formations are marked with a mine symbol but there are also several prospect symbols that denote potentially favorable uranium host formations both younger and older from the producing formations. It is generally accepted by most workers in South Texas that the source for the uranium is the volcanic ash that is abundant within several of the formations. Likewise, the required reductant is considered to be hydrogen sulfide gas, derived from deeper seated hydrocarbon accumulations, that emanate upward along fault zones into favorable host-rock sand units. Within this basic framework of source, host, structure and hydrocarbons is where most of the reserves have been discovered and where most of the current exploration is either concentrating or expanding. Structure in South Texas is predominantly faults. Swarms of faults exist in zones paralleling the coast and running from the Rio Grande to the Sabine River. These faults are usually growth faults with the down-dropped block on the coastward side. Displacement may range from a few feet to a few hundred feet. Dips are near vertical in the younger rocks at the surface but become flatter as the fault cuts older beds in the subsurface. A map of the oil and gas fields in South Texas indicates a correlation between these fault swarms and accumulations of hydrocarbons. It is not coincidental that the known uranium trends closely follow the hydrocarbon accumulations and the faults swarms, all of which supports the theory of uranium concentration by groundwater movement through volcanic ash-rich beds into favorable host rocks impregnated with reducing hydrogen sulfide gases that migrate upward along fault planes from hydrocarbon accumulations. History Newcomers to South Texas are often amazed that active entry is possible in a district that has produced uranium for over 20 years. Understanding the conditions and occurrences of the past would explain why the opportunity still exists for companies not now active in South Texas to become active. Uranium was discovered in the middle 1950's in sandstone units of the Jackson Group at Tordillo Hill in Karnes County. This discovery was followed by a rush involving most of the major uranium exploration companies as well as several of the not-so-major. Those western prospectors who were used to numerous outcrops and neat land subdivisions were further discouraged by the small size and low grade of the deposits. Then after a brief blast, they left South Texas as they found it and returned to the richer diggings of New Mexico and Wyoming. Susquehanna Western was the only one to stay and develop mines in the area. Eventually they discovered enough ore along the Jackson outcrop to warrant constructing a small mill. They managed, with limited budget and diligent effort, to find enough ore to keep the mill going and eventually expanded into exploration in other formations. By the late 1960's, Susquehanna was mining from both the Jackson and Oakville deposits. About this time, the oil companies began to enter the uranium industry and found, that because of sound forward planning, they controlled the uranium on vast tracts of acreage. At this time, which was more than ten years after discovery, there was so little literature on South Texas uranium deposits that the oil companies began following the known trends and off-setting known orebodies. This, and a few kicks on some well gammaray logs, lead to the discovery of new areas in formations that previously had n o uranium discoveries. Still, the following of the trend as it crossed from one formation to another was the main geologic guide. Nowadays, we in South Texas feel that science has entered into the quest to discover new orebodies. The work of Galloway has indicated new pathways to explore. The understanding of multiple stages of oxidation and reduction has created some doubt about areas drilled in the past and abandoned. The expanded use of oil well logs and geochemical prospecting has lured the more progressive exploration companies off the mineral trend and into unexplored areas. Prognostication The fact that uranium exploration in South Texas has been active for only the past ten years is not an indication that South Texas is not a major uranium district. The geology of the South Texas uranium deposits as described here serves only to indicate that similar geology extends in all directions from the known mineral trend as can be seen on Figure 2.

Jan 1, 1979

By D. N. Collins, J. R. Stevens

New expressions in the technical assessment of mineral concentration processes have been defined as Concentration Efficiency: Concentration Index: where h is the percentage of head grade; c, percentage of concentrate grade; maximum percentage of concentrate grade obtainable at 100 pct recovery; and R, percentage of recovery. In developing these expressions, the basic requirements for the technical assessment of concentration operations have been defined and the various expressions suggested by others for asses-sing the results of such operations reviewed and criticized. The derived expression for E, depends on a simple combination of recovery (R) and a new term selectivity (s), where S is (c-h)/(c,,, -h), by definition. Limitations of the new expressions are discussed and examples given of applications to concentration operations. It is also shown that the formulae for E, and I, can be applied to scatter diagrams, multi-component systems, size-assay analyses, and classification data. Many methods of quantifying concentrating operations have been proposed. These include direct presentation of weights and assays together with the derived data for other items such as ratio of concentration, recovery, rejection losses, and enrichment ratio. These terms are now accepted mineral dressing nomenclature, and in the assessment of the results of concentration processes, concentrate grade and recovery are together the most widely accepted measures of concentration efficiency. For practical purposes when the concentrate grade is equal to or greater than a predetermined acceptable value, test or operation results may be assessed by the recovery figures alone. Similarly when recovery is within specification, the operation can be assessed by concentrate grade. The ultimate assessment and selection of a concentration operation is—admittedly with a few ex-ceptions—a matter of economics. There is however an intermediate stage in laboratory and pilot plant testing when evaluations must be made without the assistance of an economic yardstick. Numerous techniques are employed to facilitate such evaluations among which may be mentioned graphical plots of grade vs recovery, cumulative weight vs cumulative recovery, scatter diagrams, etc. The desirability of combining metallurgical results and product weights and assays into a single value has been recognized and discussed by many workers1-" with the resultant suggestion and use of such terms as Metallurgical Efficiency ,' Summation Index,' Selectivity Index,'- and Absolute Efficiency B None of these expressions completely satisfies all the requirements of a selectivity or efficiency formula and it is proposed in this report to define the terms, relating to the technical efficiency of a concentrating operation, concentration index and concentration efficiency. Examples are given of their application and a comparison is made of their use in relation to other formulae. All product grades in this paper will be referred to in terms of mineral percentages and a list of symbols is given in Table I. CONSIDERATION OF EXISTING FORMULAE A number of the existing efficiency and index terms used in quantifying concentrating operations are considered below. Metallurgical Efficiency:

Jan 1, 1961

By R. W. Raymond

to same extent, the assumptions tinderlying Dr. Ilu?ley's con alusions. These amrrmptions are: that 'the loss of metal per million tons of trafffc, depends, first upon the circrtnistances under which the rail is worn; secondly, upon the proportions of its various constituents, ancl that the anlorlnt of loss is afEect~d by eacb constitnent in a cer tain ratio, so that if the circunlstances were the same for all tlie mils, the wear per nliilion tons might he upproxi91ately expre~sed by an equation of the form I + Cc + Pp + SR + Mm = R, io wtlioh I is an unknown valne, dependi~.rg on the quantity of iron (and other ingre dients not determined) in the rail, and assumed to be constant for all the rails ; c, p, s, and m are the experimentally determined quan tities of carhon, phosphorus, sulphur, and manganese, as tabulater1 in YIates VT and VII of Dr. Dudley's paper; and R is the experirnen tdlly dcterlnincd wear per million tons; while C, P, S, and M are onknown wfficients. In other words, it is assunled that the differ ence in wear is proportional to a difference in c, p, s, or m, and that the effects of a change in the amonnt of either are independent of the amount of the rest-—within the experinlental limit5 of the problem. It is also assr~med that sulphar, copper, and other ingredients, not determined, are qually present in all the rails, or at least {lo not affect the wear, since I is taken as constant. Dr. Dudley tacitly assumes the coefficient6 C, P, S, and M to be positive; and assigns certain valries to them, by means of which he redom t.he equation to the form I + Pa: = R, x being equal to cc + Es +Mm i Pp, or tjje uanjbe,. of so-called phosphorus units in the rail. But we do not have R directly given under constant circumstances. The varying weights (per engine, car, or train) and the varying epds, we must neglect for lack of data, and assume that in these rwpects the rails examined have been treated srlbstantially alike. But there remain the varying conditions as to track, which mnst he elirninsted. Dr. Dudley gives six clrlsses, four of which contain 8 rails each, and two 16 rails each. Beginning with the 6~st (tangent grade), take the mean of the figures expressing wear for that clam; and continaing tliis process through the other five, we obtain six expressions in quantity of loss 'by wear, which we assome tc, represent, in their differences, the varying conditions of the trarli, with respect to grade and direction. We now take the mean of these moans (giving double weight to the gmiip containing 16 ohwrvafieras). This general rnean is the 10 of metal per million tons of trafio for a rail of avorage constitution under mean ciroumstances.

Jan 1, 1881

By R. D. Lord

The search for the best practical means of storing sulfide bearing tailings, where there is no residual excess of carbonate material is discussed in this paper• Usually the sulfide content decomposes, with the aid of bacterial action, and the resulting sulfuric acid escapes, along with any heavy-metal solutes, through embankments that are usually porous to some degree• The problem is typified in the tailings of the uranium operations of Elliot Lake, Ont., where mining started some 20 years ago• The approach to tailings disposal paralleled the practice for other hydrometallurgical plants treating gold and base-metal ores• Impoundment areas were designed to retain solids, and a clear and neutral overflow was considered satisfactory practice• Now experience has shown that these areas, some of which have been idle for over a dozen years, release acids in seepage and overflows to an unacceptable degree• To protect natural water courses, neutralizing plants are operated wherever required• Lime slurry is fed continuously into the tailings outflows in a quantity sufficient to raise the pH to 8•5 and precipitate heavy metals that may be in solution• The objection to this procedure is that the plants will require servicing indefinitely, unless a better remedy is found• The problem differs only slightly from that common to base-metal concentrators in that here the ore has been leached with sulfuric acid for the recovery of uranium• Any native content of calcareous material has been digested, and only that added for final neutralization is available to maintain a pH unfavorable to bacterial activity• Chemical oxidation slowly lowers the pH and when this reaches a level of 4•5 or less, bacteria become active and greatly accelerate the formation of acid. The bacterial process is probably at least ten times as fast as the chemical oxidation• Location and Processing The operations referred to, uranium and one copper mine, are located at approximately 46°N and 82°W longitude• This is typical Canadian Shield country, a land of lakes, deeply glaciated and rocky, with sparse soil which supports mixed forest cover• Drainage is to Lake Huron, 25 miles to the south• Average temperature is 45°F, ranging from -40° to +95°F• Annual precipitation is 38 in•, about half of which is snow• The ore is Precambrian, quartz-pebble conglomerate, with mineralization in the matrix• From 5 to 10% pyrite is present• All known means of pre-concentration have been tested, but a bulk sulfuric acid leach has proved the most efficient. Tailings have from the outset been neutralized before release• Current practice is to add ground limestone to bring the pH to 4•5, and then lime to raise the value to 10•5• Environmental regulations have recently been increased and the foregoing meets the new standards• Separate measures are taken to precipitate radium• Remedial Measures Since the outstanding environmental problem is the oxidation of pyrite by bacterial action, the solution is to contain the products, or arrest the process• Given the ambient temperature, favorable half of the time, four items are essential to the activity• 1) Pyrite• 2) Moisture pH < 4•5. 3) Oxygen• 4) Bacteria• Removing any one of these out of the range of tolerance will bring the reactions under control• A variety of proposals considered, and a number tested for the arrest of the process, are: (a) render embankments impermeable, (b) provide an impermeable cover, (c) cover with an oxygen absorbing layer, (d) provide a vegetative cover, (e) flood the site, (f) remove pyrite from current tailings, (g) add excess limestone to current tailings, (h) poison the bacteria• Bank Seal-On existing impoundment areas, where the embankments are several thousand yards in length, it is believed that any program of injecting sealants can have small chance of success• However, a moisture barrier is an indicated specification for future construction, and this can be highly expensive• Surface Seal-Depending on the configuration of the deposit, the downward travel of water should be prevented, and oxygen excluded• Burying a plastic membrane just below the surface has been considered, as has the application of a liquid sealant that would penetrate the surface. The objection to these remedies is the excessive cost of dealing with large areas and the expectation of only temporary benefit as a result• Frost penetration is over 4 ft, and frost action breaks up asphalt paving and all but heavy concrete in a few years• Organic Layer-An oxygen-absorbing layer, such as bark fines from paper mills has been proposed as a surface treatment• Cultivated into the tailings such material might be expected to arrest subsurface oxidation for some years• Estimates are 100 tons per acre of bark fines, or 35 tons per acre of sawdust, and these enormous quantities do not so far give assurance of providing a long-term remedy• Vegatative Cover-Several obvious benefits would result from a good growth of grass or other vegetation on abandoned tailings• While restoring the natural green of the tract the growth would prevent wind-blown dust and reduce erosion• Subsurface oxidation should be reduced, as well as the upward movement of ground moisture as occurs in dry weather. To this end, considerable research and field testing has been carried out to arrive at a formula - a prescription which will provide a self-sustaining growth on the tailings surface, or at least one that would survive with reasonable maintenance attention. Many test plots have been run with different combinations of surface treatment and seed mixtures. Generally, by addition and close cultivation of limestone, lime, and fertilizers, technical success has been demonstrated• Plants with a high tolerance for acid soil seem the more hardy, and a pH above 3 is indicated so that nutrients can be absorbed• Recommendations are for 12 to 15 tons of

Jan 1, 1977

By James W. Shaffer

Aluminum is the most abundant metallic element and forms 8% of the earth&apos;s crust. Because of its chemical activity it does not occur in nature in a metallic form but principally in the silicates, feldspar, mica, shale, and clay. Bauxitic raw materials-bauxitic clay, aluminous laterite, and bauxite-develop from these aluminum silicate sources. Bauxite and aluminous laterite are naturally occurring mixtures of aluminum hydroxides and mineral impurities, and they are the major sources of aluminum. End Uses Bauxite is the basic ore of the aluminum industry. It is refined into aluminum hydroxide and calcined for feed stock to electrolytic smelters. Over 90% of the tonnage mined is refined and smelted into aluminum. The total tonnage consumed by other industries is small in comparison, but bauxite and alumina are important for the manufacture of refractories, ceramics, chemicals, abrasives, pharmaceuticals, catalysts, cements, dessicants, and flame retardants. Some aluminum-containing industrial products are made from clays and other materials but the majority originate from bauxite directly or from aluminum hydroxide and alumina refined from bauxite. Lateritic type bauxite is also used as building and decorative stone. Geology Mineralogy and Properties Bauxite is a mineral raw material composed principally of one or more aluminum hydroxide minerals and impurities of silica, iron oxide, titania, and other elements in minor or trace amounts. The important aluminum hydroxide minerals are gibbsite, boehmite, and diaspore. Bayerite, nordstrandite, and tucanite are naturally occurring aluminum hydroxides but are rare and not commercially important. Mixtures of gibbsite and boehmite are common, boehmite and diaspore less common, and gibbsite and diaspore rare. Gibbsite is aluminum trihydroxide. Boehmite and diaspore are aluminum oxide hydroxides and have essentially the same composition, but diaspore has a greater hardness and a more tightly bonded and denser atomic structure. Although not technically correct, the commercial terms trihydrate and monohydrate are frequently used to distinguish types of bauxite. If bauxite is all or nearly all gibbsite, it is referred to as a trihydrate ore; if boehmite or diaspore or a mixture of both are the dominant minerals, the bauxite is called a monohydrate ore. If substantial amounts of both gibbsite and boehmite are present, the bauxite is frequently referred to as a mixed ore. Properties of major bauxite minerals are shown in Table 1. Silica, iron oxides, and titania are major impurities always present in deposits of bauxitic raw materials.. Silica impurities usually occur as clay minerals, micaceous minerals, or quartz, but cristobalite and feldspar are found in some deposits. The most common clay minerals are kaolins; however, illites and chlorites are often found in small quantities. Varying proportions of aluminum, iron, and clay minerals make bauxite, aluminous laterite, ferruginous laterite, and bauxitic clay deposits gradational with each other. Hematite and goethite are the common iron mineral impurities in many bauxites. Magnetite and ilmenite occur in deposits derived from basic igneous rocks. Other iron minerals associated with bauxite are maghemite, pyrite, siderite, and marcasite. The titanium minerals found in bauxites are anatase, leucoxene, rutile, ilmenite, titaniferous

Jan 1, 1983

By Falih Ergunalp

REGULAR production of chrome in Turkey started in 1860 with the operation of the Bursa deposits (5, Fig. I). Others were discovered at Makri, near Fethiye (3, Fig. I). For 33 years Turkey remained the principal source of this mineral. While new discoveries were coming in elsewhere, Turkey&apos;s output declined until 1921, as a result of four successive wars, which ruined the economics of the country. In 1927 a revival came with the production of 18,000 tons. In that year the Société Minière de Fethiye was formed. This company now operates mines in the Vilayets of Aydin, Denizli, Burdur and Mentese, and it has reached a maximum production of between 80,000 and 90,000 tons annually. The Turkish output therefore increased from 29,000 tons in 1930 to 55,000 tons in 1931; and to 119,009 tons in 1934. The second phase in the increase in chrome production in Turkey came about in 1935, when the Government decided to reorganize and control the mineral industry of the country according to the principles of "government control" of the present regime. Up to that time the mineral resources of the country had been exploited by private concerns. In 1935, the M.T.A. (Maden Tetkik ve Arama) Institute (Institute of Mining Research and Geological Survey) was established by the Government to do the geological and geophysical survey work and discover new mineral resources for the country. Before the establishment of the M.T.A. Institute, the chief chrome-producing region was Fethiye (3 and 4, Fig. I). As a result of the extensive work of this bureau, many new chrome deposits have been discovered and are now in production. The operational field of the mineral industry was given to Eti Bank, another Government-sponsored and Government-controlled establishment. Eti Bank gradually took over the exploitation of existing mines by purchasing them from privately operated companies. Attention was first given to the Zonguldak collieries and to the different chrome deposits scattered over the country. The Guleman mines (14, Fig. 1) were developed and put in operation in 1936. Since then the bulk of Turkish chrome output has come from this mine, which yields the highest grade ore in the world (averaging 52 per cent Cr2O3). In 1939, the recently discovered chrome deposits to the north of Eskisehir went into production, yielding ore having a Cr2O3 content of 51 to 52 per cent. Today, more than ever, the efforts of both the M.T.A. Institute and the Eti Bank are concentrated on finding new deposits and placing them in operation. There are still many promising regions of the country that merit systematic surveying and prospecting for chrome ores. Thus it is probable that Turkey will continue to make noteworthy progress in chrome output. As the annual chrome production of

Jan 1, 1944

By J. D. Sullivan, Chester R. Austin, J. L. Nunes

It is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investi-: gators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson&apos;s1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by - experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from IIoo° to 17oo°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxida- tion of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous clays burned &apos; to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,= the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery0 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the clay, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid; i.e., the sulphur was in combination with the silica. orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By J. D. Sullivan, Chester R. Austin, J. L. Nunes

It is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investi-: gators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson&apos;s1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by - experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from IIoo° to 17oo°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxida- tion of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous clays burned &apos; to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,= the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery0 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the clay, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid; i.e., the sulphur was in combination with the silica. orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By A. Dubé, G. Letendre, C. E. Beaulieu

An experimental study has been made of the time dependence of internal .friction and modulus of rigidity in- freshly quenched steels at room temperature. The effects of frequency, composition, and various thermal treatments are given. The kinetic 1aws observed cannot be fully explained by the so-called first stage of tempering and the transformation of retained austenite. It is suggested that the observed phenomena are due to the progressive immobilization of dislocations introduced by the martensitic transformation. It is generally agreed that the conversion of tetraginal martensite into cubic ferrite and ce-mentite occurs in three stages which at moderate rates of heating take place in the following temperature ranges:&apos;-3 a) The first stage involves mainly a partial loss of tetragonality of martensite and the formation of ?-carbide between 95" and 175oC. b) The second stage consists of the decomposition of retained austenite between 230 and 290&apos; C. c) The third stage covers the formation of ce-mentite between 290o and 400&apos; C. The kinetic laws of these heterogeneous reactions have also been the subject of isothermal studies. Thus, Roberts, Averbach. and cohen3 report a very low reaction rate with a eutectoid steel at room temperature. For example, less than 10 pet of the contraction associated with the first stage is observed after 50 hr at room temperature. Hollonlon, Jaffe, and Buffum4 show that under the same conditions less than 10 pet of the tetragonality is lost. These results have led to the belief that martensite is a relatively stable phase at room temperature. On the other hand, it is well known that important structural changes occur in martensitic steels during the first few minutes at room temperature after quenching. This pretempering has at least two important consequences. In the first place, freshly quenched steels have a tendency to crack at room temperature, a fact which leads to the necessity of tempering as soon as possible after the quench. Another important consequence of pretempering a steel for short periods of time at room temperature is the stabilization of the retained austenite. Thus, as shown by Cohen,5 a very pronounced stabilization is effected with holding periods of 30 min at room temperature. Since these two effects are apparently not caused by the heterogeneous reactions mentioned above, they must be related to the rearrangement of structural defects within the martensite and retained austenite. According to the modern theory of dislocations, the shears required to effect the austenite-marten-site transformation may be realized through the motion of dislocations at the austenite-martensite interface and within the martensite plates.6 In this way, a martensitic transformation closely resembles a plastic deformation. In cold-worked solids, high concentrations of dislocations are left immediately after the plastic deformation and it seems reasonable to assume that appreciable densities of dislocations should also appear in the wake of a martensitic transformation. A considerable part of the high hardness of martensite would then originate in the obstruction of dislocations in analogy

Jan 1, 1961

By J. D. Sullivan, Chester R. Austin, J. L. Nunes

IT is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investigators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson&apos;s1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from 1100° to 1706°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxidation of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous days burned to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,5 the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery6 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the day, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid; i.e., the sulphur was in combination with the silica. Orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By R. B. Hoy, Stanley J. LeFond, K. Reckling

Reported world production of natural diamonds approximates 40,000,000 carats a year (1980). The Republic of Zaire is the leading producer, with an output which is primarily industrial rather than gem grade. The USSR ranks second, the Republic of South Africa third, and Botswana, fourth. Diamonds are also mined in South-West Africa (Namibia), Angola, Ghana, Sierra Leone, and other African countries. In the western hemisphere, Brazil and Venezuela are the principal producers (Fig. 1). A very small output of diamonds is mined today it India, which was the first source of commercial production. In the US, efforts at commercial diamond mining have been confined to a small area near Murfreesboro, AR. The first diamond was found in a kimberlite pipe there in 1906. Small-scale trial mining has not, however, proved economical. Since diamonds were first discovered over 2,000 years ago, only about 260 tons have been mined. In order to obtain I g (5 carats) of diamonds, it is necessary to remove and process approximately 25 tons of rock. Recovering this small percentage involves a combination of highly developed techniques in mining, quarrying, and earth-moving, and extremely sophisticated recovery processes. End Uses Diamonds are used for two unrelated end uses; gem diamonds are jewels of great beauty while industrial diamonds are essential materials of modern industry. Although imitation stones are substituted for the gem diamond, none of these matches its properties sufficiently well to offer real competition. Synthetic industrial diamonds are now of a quality and size that permit them to be substituted for natural diamond in numerous industrial applications. For example, synthetic diamonds are available today in sizes up to 100 stones per carat (14/16 US mesh size). In addition, polycrystalline synthetic diamond inserts, such as De Beers Syndite®, General Electric&apos;s Compax® and Stratapax® and Megadiamond&apos;s Megapax® have replaced natural diamond in turning tools, mining and oil drilling bits and dressing tool applications. Gem Diamonds A diamond is a natural prism. It has the ability to bounce light rays (reflection), to bend them (refraction), and to break them into all colors of the rainbow (dispersion). This ability to modify light gives the diamond three characteristics for providing beauty. First is brilliance, the reflection of light back to the eye. Second is fire, dispersion of light into the colors of the spectrum. Third is scintillation, the "twinkling" that occurs when the diamond is moved (Bauer, 1969). The skill of the diamond cutter is required to unlock the brilliant, fiery beauty of a gem diamond (Fisher, 1966). Diamond-cutting skills have gradually developed over the centuries. The first cutters, in India, learned how to grind one rough diamond against another to remove their "skins" and to give them various shapes. This revealed some fire and beauty, but little compared to that of the diamonds that are cut today.

Jan 1, 1983

By B. M. Larsen

IN endeavoring to put the art of the steelmaker on a more scientific basis, as a means of securing closer control of the product, we must be severely critical of the basis of any theory we use. In particular, we must be careful to distinguish between factors that are primary and those of only secondary importance. The concentration relations that determine the slag-metal equilibria, which are usually more or less closely attained, are of course of primary significance, but a clear picture of the whole process requires that the actual rates of the several reactions be taken properly into account. At the high temperature of the steelmaking furnace, all reactions might be thought to be very rapid, but some of them in fact are not; the essential causes of this condition are important to a proper understanding of the process. This paper aims to present, and to justify, the viewpoint that the most significant reaction is the oxidation of carbon in the metal, the progress of which determines the oxygen pressure levels in slag and metal and produces stirring effects, all of which influence the course of the process as a whole. REACTION RATES AT STEELMAKING TEMPERATURES General experience in reaction rates makes it almost certain that at steelmaking temperatures equilibrium is attained practically instantaneously when the reactants are well distributed in a single liquid phase -that is, in the so-called homogeneous reactions. The actual slowness of some of the reactions in the open-hearth furnace must therefore be attributed to a relatively slow rate of diffusion within the slag or metal phase, which limits the rate at which the reactants can meet each other in the liquid steel or at its surface. That the reactions can be made to go with great rapidity, by proper mixing and stirring of the reacting phases, is indicated by the following illustrations: I. In the Bessemer process there is intimate contact between air and the whole mass of metal, and the reactions are complete in a few minutes. 2. Perrin1 has demonstrated that by pouring liquid steel into slag contained in a deep ladle, and thereby producing almost a slag-metal emulsion, the phosphorus or oxygen content of the steel is adjusted immediately. 3. Barret, Holbrook and Woods observed a quite rapid rate of desulphurization when powdered calcium carbide was stirred vigorously into liquid iron. 4. When a spoonful of liquid steel is poured into a mold containing aluminum wire, the formation and precipitation of alumina occurs in the fraction of a second required to freeze the surface layer of the tiny ingot. The first three examples all show that any means of increasing the effective surface between slag and metal and promoting intimate mixture of the reacting phases, thereby obviating the limitation imposed by diffusion, will enhance the speed of the steelmaking process.

Jan 1, 1941

By B. M. Larsen

In endeavoring to put the art of the steelmaker on a more scientific basis, as a means of securing closer control of the product, we must be severely critical of the basis of any theory we use. In particular, we must be careful to distinguish between factors that are primary and those of only secondary impartance. The concentration relations that determine the slag-metal equilibria, which are usually more or less closely attained, are of course of primary significance, but a, dear picture of the whole process requires that the actual rates of the several reactions be taken properly into account. At the high temperature of the steelmaking furnace, all reactions might be thought to be very rapid, but some of them in fact are not; the essential causes of this condition are important to a proper understanding of the process. This paper aims to present, and to justify, the viewpoint that the most significant reaction is the oxidation of carhon in the metal, the progress of which determines the oxygen pressure levels in slag and metal and produces stirring effects, all of which influence the course of the process as a whole. Reaction Rates at Steelmaking Temperatures General experience in reaction rates makes it almost certain that at steelmaking temperatures equilibrium is attained practically instantaneously when the reactants are well distributed in a single liquid phase —that is, in the so-called homogeneous reactions. The actual slowness of some of the reactions in the open-hearth furnace must therefore be attributed to a relatively slow rate of diffusion within the slag or metal phase, which limits the rate at which the reactants can meet each other in the liquid steel or at its surface. That the reactions can be made to go with great rapidity, by proper mixing and stirring of the reacting phases, is indicated by the following illustrations: 1. In the Bessemer process there is intimate contact between air and the whole mass of metal, and the reactions are complete in a few minutes. 2. Perrinl has demonstrated that by pouring liquid steel into slag contained in a deep ladle, and thereby producing almost a slag-metal emulsion, the phosphorus or oxygen content of the steel is adjustcd immediately. 3. Barret, Holbrook and Wood2 observed a quite rapid rate of desulphurization when powdered calcium carbide was stirred vigorously into liquid iron. 4. When a spoonful of liquid steel is poured into a. mold containing aluminum wire, the formation and precipitation of alumina occurs in the fraction of a second required to freeze the surface layer of the tiny ingot. The first three examples all show that any means of increasing the effective surface between slag and metal and promoting intimate mixture of the reacting phases, thereby obviating the limitation imposed by diffusion, will enhance the speed of the steelmaking process.

Jan 1, 1941

By B. M. Larsen

In endeavoring to put the art of the steelmaker on a more scientific basis, as a means of securing closer control of the product, we must be severely critical of the basis of any theory we use. In particular, we must be careful to distinguish between factors that are primary and those of only secondary impartance. The concentration relations that determine the slag-metal equilibria, which are usually more or less closely attained, are of course of primary significance, but a, dear picture of the whole process requires that the actual rates of the several reactions be taken properly into account. At the high temperature of the steelmaking furnace, all reactions might be thought to be very rapid, but some of them in fact are not; the essential causes of this condition are important to a proper understanding of the process. This paper aims to present, and to justify, the viewpoint that the most significant reaction is the oxidation of carhon in the metal, the progress of which determines the oxygen pressure levels in slag and metal and produces stirring effects, all of which influence the course of the process as a whole. Reaction Rates at Steelmaking Temperatures General experience in reaction rates makes it almost certain that at steelmaking temperatures equilibrium is attained practically instantaneously when the reactants are well distributed in a single liquid phase —that is, in the so-called homogeneous reactions. The actual slowness of some of the reactions in the open-hearth furnace must therefore be attributed to a relatively slow rate of diffusion within the slag or metal phase, which limits the rate at which the reactants can meet each other in the liquid steel or at its surface. That the reactions can be made to go with great rapidity, by proper mixing and stirring of the reacting phases, is indicated by the following illustrations: 1. In the Bessemer process there is intimate contact between air and the whole mass of metal, and the reactions are complete in a few minutes. 2. Perrinl has demonstrated that by pouring liquid steel into slag contained in a deep ladle, and thereby producing almost a slag-metal emulsion, the phosphorus or oxygen content of the steel is adjustcd immediately. 3. Barret, Holbrook and Wood2 observed a quite rapid rate of desulphurization when powdered calcium carbide was stirred vigorously into liquid iron. 4. When a spoonful of liquid steel is poured into a. mold containing aluminum wire, the formation and precipitation of alumina occurs in the fraction of a second required to freeze the surface layer of the tiny ingot. The first three examples all show that any means of increasing the effective surface between slag and metal and promoting intimate mixture of the reacting phases, thereby obviating the limitation imposed by diffusion, will enhance the speed of the steelmaking process.

Jan 1, 1941

By Gerhard Derge

THE extension of metallurgical control of steelmaking processes has always made it desirable to have some quick method for determining the oxygen content of molten steel. To meet the practical demands of the steel industry, this method must also be simple enough so that the sampling can be done by the regular furnace crew. This requirement was kept in mind continually in the work to be described. An oxygen value is required for proper control, whether it be of a rimming steel or of a fully killed steel. However, two factors have discouraged the development of such direct methods: I. The reaction C + FeO -+ Fe + CO is rapid enough to make the correct sampling of the bath a difficult problem. The most generally accepted means of circumventing this difficulty have been the aluminum-killed bomb test of McCutcheon and Rautio1 and the aluminum-killed spoon test of Herty.2 The theory of these tests is that all of the oxygen in the iron is converted to A1203, which can then be determined by chemical methods. Even when simplified so that the analysis is made by a measurement of turbidity, this method is too slow to be used in routine control. Furthermore, the results obtained have never been entirely satisfactory, and some of the reasons for this will be discussed later in this paper. 2. The ordinary chemical methods of analysis for oxygen in steel are not reliable. The only analysis that seems to possess sufficient dependability to be of value is vacuum fusion,3 and the apparatus and technique developed for this have been too complex and slow for routine work. INDIRECT METHODS Indirect methods of estimating the oxygen have been resorted to in mill practice. Generally these depend upon the chemical equilibria involved. The oxygen in the bath is related to other components in the slag or metal that can be analyzed more readily. These methods have many difficulties in common. Steelmaking processes involve a complicated set of interrelated reactions, all of which tend to approach equilibrium at varying rates. The degree to which any particular equilibrium is approached, is not , well established. Moreover, a proper use of theoretical equilibrium constants requires a more extensive knowledge of the activities of the reactants than we now have. This is well illustrated by the irregularities observed when trying to determine the oxygen in the metal by its ratio to the iron oxide in the slag. Equilibrium relations may be used more readily if they are evaluated by plant experience, but the extent of approach to equilibrium remains an undetermined variable and lack of an entirely satisfactory means of determining oxygen for the calibration is felt keenly. For example, the statistical analysis of the relation between carbon and oxygen4 5 illustrates that even in a single plant wide variations exist under normal conditions of operation. Nevertheless, this is one of the best methods now

Jan 1, 1943

By J. S. McNeil, J. U. Messenger

In the drilling of oil wells the control and prevention of lost circulation of the drilling- fluid is a oroblem which is frequently encountered; in many cases existing materials and methods for alleviating this condition have not been adequate. For severe cases of lost circulation in which the simpler methods, such as application of various bridging materials to the mud system, have proven unsatisfactory. a new material and method for applying to the loss zones have been developed which appear to he superior to existing techniques in many respects. The material, called a clay cement, is capable of being handled as a drilling fluid after initial mixing of the solitl ingredients with water and may be pumped down the drill pipe and squeezed into loss zones. After a short period, the material develops a very high gel strength which seals off the zone against further losses of the drilling fluid. In field tests, the process has been demonstrated to be a very effective method for combatting lost circulation. INTRODUCTION Methods of treating lost circulation in rotary-drilled wells by the addition of special materials to drilling fluids have long been in the process of development and are continuing to improve.&apos; However, the annual drilling costs which can be traced directly to lost circulation difficulties still run into the millions of dollars. The loss of mud materials into highly permeable zones may range up to $50,000 per well in some areas. In addition to mud costs, excessive requirements of casing, cement; rig time, and the attendant blowout hazards further emphasize the importance of the need for improved methods of combatting lost circulation. The shortcomings of presently-used materials and methods have led to the development of a new lost returns material in the form of a time-setting clay cement. In field tests this material has proven very successful in plugging off loss zones. which other more conventional materials had failed to do. REVIEW OF PRESENT CORRECTIVE MEASURES The proper control of such operating factors as pump pressure, clearance between pipe and hole, and speed of running pipe in a holez is of primary importance in preventing and minimizing lost circulation problems. These factors, however, concern matters of drilling technique and do not directly involve lost circulation materials. Aside from setting casing past loss zones, three principal methods are generally employed for the purpose of avoiding or combatting lost circulation: (1) adjustment in properties (principally density) of the drilling fluid, (2) addition of fibrous, flaky, granular or other types of bridging materials to the mud system, and (3) the application of cements to the loss zones. The latter method is usually employed only after the first two have proven unsuccessful. In Table I are listed some advantages and disadvantages of the common corrective measures. Frequently, a combination of bridging material and cementing material is used." This combination is based on the premise that a bridge will

Jan 1, 1952

By A. Raman

The Nb-Co system was nuestigated in the range 10 to SO at. pct Co with X-rays. A pt phase with the W6Fe.r-type structure occurs in the system between 46 and 52 at, pct Co. Its unit-cell dimensions are nearly identical to those of the p Phases found in the Nb-Fe and Nb-Ni systems. Two Laves phases, one having the MgZnz-type structure and the other the MgCuz-type structure, already t-eported in the literature, are found to exist in the system. The ,l.IgZnz-type phase occurs between 62 and 64 at. pct Co. A MgNi2-type Laves phase, reported in the literature, is no! obtained. A binalry phase is found to exist belozv I000C around 82 at. pct Co. THE cobalt-rich side of the system Nb-Co has been repeatedly investigated by previous inestiators" and the following intermediate phases are known to occur: NbCo, which crystallizes in the MgCu2-type structure and Nbc03,&apos; reported originally by Wall-bam, which has the MgNiz-type structre. Jordan and uwez&apos; as well as lliott&apos; were unable to find the MgNiz-type phase. Two phases, designated as x and y, were reported by Saito and eck.&apos; The phase x was inferred to have a narrow composition range near 77 at. pct Co. No published work is known to the author which reports the investigations in the niobium-rich portions of the system. This paper presents the results of an investigation in the Nb-Co system between 10 and 80 at. pct Co. EXPERIMENTAL PROCEDURE Two or three grams of the alloys under investigation were prepared using niobium (99.9 pct +) and cobalt (98.8 pct + with 0.14 pct Fe and and 0.03 pct C) in a tungsten-electrode arc furnace under commercial argon atmosphere. They were then wrapped in molybdenum sheets and annealed for a period between 5 days and 1 week at 1300°C in high vacuum (10-" orr) or in evacuated quartz amules for 2 weeks at 1000°C. Powders of -325 mesh size were prepared for X-ray work by crushing and grinding the specimens. Subsequent reannealing of the powders was not undertaken since most of the alloys were brittle and broke easily. X-ray powder patterns of the as-cast and annealed samples were prepared in a Siemens cylindrical camera (57.3 mm radius) with Cr-K, radiation. A Siemens diffrac to meter was used to get the X-ray patterns of some new phases. Metal log raphic examination of the alloys supplemented the X-ray findings. RESULTS The results of the X-ray and microstructural analysis Of the alloys are in in Table I. The lattice parameters of the phases are listed in Table 11 for quick reference. A set of micro photographs in Fig. l(n) to (j) show the microstructures of some alloys. A probable equilibrium diagram is drawn in Fig. 2

Jan 1, 1967

By Frank A. Herald

Through the generous cooperation of the authors of the papers in this chapter, a great wealth of fundamental data is being made available. The same plan of securing and submitting data will be carried forward next year, with the hope of making a nearer approach to complete presentation of the data contemplated in the plan. In order to conserve space, we are printing below such footnotes as have general application to Table 1 in the papers in this chapter: Footnotes to Column Headings Table I In areas where both oil and gas are produced, unless gas is marketed outside the field, such areas are included in column headed "Oil." Manufacture of casinghead gasoline and carbon black is interpreted as outside marketing of gas. Production per acre is determined by dividing into the number of barrels of oil the sum of the number of acres assigned to "Oil" plus such number of acres of the total assigned to "Oil and gas" as represents the portion thereof occupied by oil. Wells producing both oil and gas are classified as "Poducing oil only" unless gas from them is marketed off the lease. W. water; G. gas; A, air. Bottom-hole pressures are preceded by "e." All other figures represent pressures at casinghead with well closed. P, paraffin; A, asphalt; M, mixed. 0 Cam, Cambrian; Ord, Ordovician; Sil, Silurian; Dev, Devonian; Mis, Mississippian; MisL, Lower Mississippian; MisU, Upper Mississippian: Pen. Pennsylvanian; Per. Permian; Tri, Triassic; Jur. Jurassic; CreL, Lower Cretaceous; CreU. Upper Cretaceous; Eoc, Eocene; Olig, Oligocene; Mio. Miocene; Pli. Pliocene. 6, sandstone: SH, sandstone, shaly; Ss, soft sand; H, shale; L, limestone; LS, limestone. sandy; C, chalk; A, anhydrite; D, dolomite; Da. arkosic dolomite; GW, granite wash; P, serpentine. Figures are entered only for fields where the reservoir rock is of pore type. Figures represent, ratio of pore space to total volume of net reservoir rock expressed in per cent. "Par" indicates that the reservoir rock is of pore type but said ratio is not known by the author. "Cav" indicates that the reservoir rock is of cavernous type; "Fis," fissure type. A, anticline; AF, anticline with faulting as important feature; Af, anticline with faulting as minor feature; AM, accumulation due to both anticlinal and monoclinal structure; H, strata are horizontal or near horizontal; MF, monocline-fault; MU, monocline-unconformity; ML, monocline-lens; MC, monocline with accumulation due to change in character of stratum; MI, monocline with accumulation against igneous barrier; MUP, monocline with accumulation due to sealing at outcrop by asphalt; D, dome; Ds, salt dome; T, terrace; TF, terrace with faulting as important feature; N, nose; 9, syncline. Information will be found in text as indicated by symbols: A, name of author, other than above. who has compiled the data on the particular field; C, chemical treatment of wells; G, gas-oil ratios; P, proration; U, unit operation; R, references; W, water; 0. other information.

Jan 1, 1934

By E. P. Valby

A method is presented in which the hydrocarbon weight fractional analyses of the well effluents from a true gas-tip-portion well and a true dark-oil-ring well furnish the basic data for determining the properties of any mixture of production from the two sources. The effect of injected gas on these properties can be computed. Comparison of similar properties of a given well effluent to the properties of mixtures of the basic well effluents will give the relative amounts of production from the two sources and injected gas. Presentation of Problem Oil fields having an area of gas-cap, or light-oil production, over the dark-oil area present a problem of increasing gas-oil ratios during the production of an oil well. The use of pressure maintenance in a field such as above, or a cycling project, wherein residue gas from an absorption plant is injected into the reservoir, adds to the problem, because a part of the increased gas-oil ratio may be due to the production of injected gas. The usefulness of a means to determine the amount of injected gas in a well effluent led to the development of a method in which well-effluent analyses of a true gas-cap-portion well and a true dark-oil-ring well furnish the basic data needed to determine whether injected gas of a known composition is present in a given well effluent. Development op Method The method presented herein is based upon the principle that if two fluids, or well effluents, having different properties are mixed in known proportions by weight, • the properties of their mixtures can be computed. Conversely, if these basic data are known, the properties of a mixed well effauent can be used to compute the relative amounts of each type of well effluent in the mixture. A convenient way of making these computations is to have the fractional analyses of the base well effluents and mixtures expressed in weight fractions The mathematical equations expressing the properties of mixtures will be developed for a two-component system consisting of the well effluents from the dark-oil ring and the gas-cap area. The added effect of injected gas, a third component, will also be developed. The following assumptions have been made in developing the method: 1. The gas-cap and dark-oil fluids exist initially in separate portions of the reservoir. 2. The fluids in each portion exist in a single phase at pressures above the saturation pressure for the dark-oil fluid. 3. The composition of each fluid is substantially constant throughout its respective portion of the reservoir. 4. Changes in reservoir pressure and temperature will not change the composition of the fluid entering the well bore. 5. The injected gas displaces original gas-cap fluid 100 per cent. •• 6. AS the injected gas travels through a

Jan 1, 1945