By Robert G. Woolery, S. Ramachandran, James A. Weber, Donald J. Hansen

Union Carbide began looking seriously at heap leaching in 1971. At that time some 1.6 million tons of mineral averaging 0.40 kg U308 /t) (0.80 lb U308) were stockpiled at various sites around the Gas Hills, Wyoming, uranium facility. Several alternatives for economically exploiting these reserves were considered and heap leaching seemed the most attractive. At the time, Western Nuclear Inc. was operating a heap leaching project nearby in which the low-grade ore was leached with sulfuric acid, the product liquor treated in an on site solvent extraction circuit, and the stripped product liquor re-acidified and recycled. The operators were most generous in allowing us to visit their site and in answering our questions. They were also helpful in discussing the problems associated with heap leaching. Their experience confirmed our belief that it was possible to operate a heap leach profitably on material too low grade for conventional milling.

Jan 3, 1978

State of Louisiana, Department of Conservation, Division of Minerals, 126 New Orleans Court bldg , New Orleans, La. Dr. J. A Shaw, Director The Bureau of Scientific Research of the Minerals Division has recently issued the first of a proposed series of Geological Bulletins on the geology of Louisiana, by parishes The bulletin may be had for 25 cents postage by writing to the above address: Geological Bulletin 1, Geology of Iberia Parish (1931) Other bulletins of a more general nature have been published in the past. Bulletin 13, A brief survey of the natural resources of Louisiana (1930) (revised 1931), 14, The clays of the Shreveport area (1927), 16, The clays of Monroe area (1928), 19, The clays of Alexandria area (1929). The latest (Tenth) Biennial Report of the Department of Conservation for 1930-1931, containing a review of the natural resources of the state in the report of the Division of Minerals, may be obtained on payment of 25 cents for postage

Jan 1, 1933

By Henry H. Thomas

In Tasmania a tailrace tunnel to handle water discharged from a turbine generator has been successfully driven by a machine tunneling method similar to that described in the July 1962 issue of Civil Engineering. The Hydro-Electric Commission, Tasmania, is constructing a high- head (2750 ft) power project that will utilize the storage in the Great Lake (1,150,000 acre-ft) at an elevation of 3380 ft. The underground power station will house six vertical shaft turbo-generators, each rated at 50,000 kw. The tailrace tunnel, 16 ft diam and 14,600 ft long, was driven through a reasonably homogeneous hard mudstone. It was decided to excavate this mechanically in the hope of saving some money on excavation and a considerable sum on the ultimate lining of the tunnel. Mechanical engineers from Tasmania worked with the firm of James S. Robbins and Associates of Seattle, Wash., which designed and supplied the "mole."

Jan 4, 1963

By D. Hartley

United States Steel Corp's. Minntac mine is located at Mt. Iron, Minn. on the Mesabi Iron range. The taconite pit is two miles wide, with a maximum depth of 170 ft. Millions of tons of crude ore, waste rock, and surface overburden are handled annually at the mine. All crude ore plus some of the lower-grade rock are rail-hauled; other materials are trucked. Length of rail haul averages 3.5 mi, with a lift of 140 ft. The maximum grade against the load is 1 ½ %. Nine 1200 hp diesel-electric locomotives handle trains of 40-and 50-cu yd side dump cars in crude ore and lower-grade rock service. In addition to this continuous operation, locomotives handle coarse tailings disposal and switching duties on an intermittent basis. All railroad equipment operates under the supervision of a mine control foreman through voice radio communication. The pit foreman also has this frequency available, quickly accommodating any changes in operation that may be required.

Jan 1, 1970

By Arthur Knapp

THE economics of fuel oil must be considered in two aspects; viz., fuel oil as one of a number of competitive fuels and fuel oil as a refined product of petroleum. "Fuel Oil" is usually defined as that product of petroleum which is used in furnaces for the generation of heat by simple combustion. It is true that any product of petroleum used in an internal combustion engine is essentially a fuel oil, but such oils are not included in the class known as "Fuel Oil." FUEL OIL AS ONE OF SEVERAL FUELS For a number of years, the petroleum industry has believed that the petroleum reserves were very limited and that petroleum products would begin to become scarce within a few years. The industry has believed FIG. 1.-DAILY AVERAGE CONSUMPTION OF FUELS BY PUBLIC UTILITY POWER PLANTS. that there would be a gradual but continual rise in prices as a result of this impending scarcity.

Jan 1, 1928

By A. M. E. Eilers

No one who has visited our Western mining districts, and studied the economical part of the beneficiation of the ores occurring all over that vast extent of country, can underrate the high importance of the above subject. By far the larger number of the districts which contain smelting ores, i.e., argentiferous and auriferous lead, or copper ores, are situated in the Great Basin, that great plateau between the Rocky Mountains on the east, and the Sierra Nevada on the west, almost the whole of which is comprised at present in the boundaries of Nevada, Utah, and part of Arizona. This region is essentially a barren country. The extreme dryness of the atmosphere permits but a scanty vegetation in the plains ; and even in the detached mountain-chains running through it-generally from N. to S., or from N. W. to S. E.-there are no trees found except dwarfed pines and mahogany, at the head of sheltered ravines, and a few cottonwoods and willows, which fringe the insignificant streams, before the water sinks in the arid plains. Nearly all the mountain-chains in this region are rich in silver ores. That class of these ores which is adapted to amalgamation, and rich in silver, has been worked with profit for more than ten years. But before the advent of the transcontinental railways, mining was restricted to these ores alone, and the consumption of fuel could be met with the scanty supply of forest trees in the immediate vicinity of the mining districts. Since, however, the Union and Central Pacific Railroads have brought the Great Basin nearer to the commercial centres of the East and the Pacific coast, thus reducing the expenses of freight and labor materially, other silver deposits, containing poorer ores in greater abundance, have been rapidly taken

Jan 1, 1873

By Klaus Schwerdtfeger

The equilibria in the Cr-N system have been investigated in the temperature range 1100° to 1310°C by reacting chromium powder with Nz-Hz gas mixtures. The solubility of nitrogen in chromium in equilibrium with chromium subsitvide ("Cr,N") is given by Chromium subnitride is nonstoichiotnetric; its nitrogen content is always less than that corresponding to the formula CrzN. The lattice paranzeters of quenched samples have been measured; c, and a. parameters are found to increase with increasing nitrogen content. The growth rate of the subnitride layer on chromium plates was measured by a thermogravimetric technique, using a silica spring balance. The self-diffu-sivity obtained from the theoretical analysis of the parabolic rate constant is found to decrease with increasing nitrogen content, i.e., with decreasing vacancy concentration in the nitrogen sublattice. The intrinsic nitrogen diffuivity is derived from another series of rate measurements using "CrzN" plates; the intrinsic diffusivity, DN = 3.2 X 10-a cmZ sec-' at 1200 C, is found to be essentially independent of- the subnitride composition. The concentration gradient was measured in a chromium subnitride layer by the X-ray method and found to be consistent with the derived diffusivity value. TWO chromium nitrides are known to exist:' the nonstoichiometric subnitride "CrzN" and the nitride CrN. In the present work the kinetics of the formation of chromium subnitride from chromium and nitrogen have been investigated at 1100" and 1200°C. In additional experiments the relevant equilibria have been measured. The data are used to evaluate the diffusivity of nitrogen in chromium subnitride. Since chromium nitrides are often found in chromium-containing steels, the results are expected to be helpful in the interpretation of the chemical reactions between chromium steels and nitrogen. Equilibria in the Cr-N system have been determined by several investigators.2"3 The rate of nitriding of chromium was measured by Arkharov et a1 .' in ammonia in the temperature range 800" to 1200°C. The parabolic rate law was observed. Due to the undefined nitrogen activity of the ammonia atmosphere, it is dif- ficult to interpret these rate data theoretically. An additional difficulty arises from the fact that the two-layer scale consisting of CrN and "Cr2N" was formed at the temperatures below 1030°C. The rate of nitriding of technical chromium (95 pct) was measured by Zaks in nitrogen at -1 atm in the temperature range 800" to 1300°C. EXPERIMENTAL METHODS The chromium samples were reacted with Nz-HZ gas mixtures in a vertical tube furnace, wound with Pt-10 pct Rh resistance wire. The gas-tight reaction tube was of high-purity recrystallized alumina. In nitrogen solubility measurements the nitrogen content of chromium was determined by the Kjeldahl method, on samples quenched in the cold part of the furnace. The nonstoichiometry of the subnitride and the nitriding rates were measured thermogravimetrically using a sensitive (+0.1 mg) silica spring balance. For the equilibrium measurements samples of 1 g of chromium powder contained in high-purity alumina crucibles were used. In order to remove most of the oxygen and nitrogen impurities from the chromium, the samples were initially annealed in purified hydrogen until a constant weight was obtained. The chromium plates (approximate dimensions 2 by 1 by 0.08 cm) used for the rate measurements were machined from ingots obtained by arc-melting of iodine-processed chromium. According to manufacturers' specifications the purity of the chromium powder was 99.9 pct Cr and that of the iodine-processed chromium 99.99 pct Cr. Our own spectroscopic analysis of the chromium powder yielded 0.02 pct Fe, 0.05 pct Mn, 0.05 pct Si, and 0.02 pct Ti as major impurities with all the other detectable elements below 0.005 pct. The nitrogen partial pressure of the gas phase was controlled by mixing prepurified hydrogen and nitrogen with constant pressure head capillary flowmeters. Oxygen and water vapor were removed from the mixed gas by passing it through columns of platinized asbestos (450°C) and anhydrone. The gas flowed upward in the furnace with flow rates of 300 to 500 cu cm per min (25"~). Gas tightness of the furnace system was ensured by pressure checks at regular intervals. The furnace temperature was controlled electronically in the usual manner. The reported temperatures were measured with a Pt/Pt-10 pct Rh thermocouple and are estimated to be accurate within ±$C The X-ray measurements were made with a Debye-Scherrer camera and a diffractometer using chromium radiation {\Ka = 2.29092A). EQUILIBRIUM MEASUREMENTS The experimental results of the equilibrium measurements are contained in Tables I to In. Fig. 1 shows the solubility of nitrogen in solid chromium in the temperature range 1100" to 1310°C. In Figs.

Jan 1, 1968

By J. D. Defilippi, E. M. Gilbert, K. G. Brickner

FCC chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Transformation to martensite is considered to be responsible for this behavior in some metastable Cr-Mn-N steels. However, very stable Cr-Mn-N steels also exhibit a ductile-to-brittle transition. The results of this study indicate that deformation faulting is the probable cause of the brittle behavior of stable Cr-Mn-N steels. Deformation faulting accounts for the ductile behavior of these steels in a tension test at -320°F and brittle behavior in an impact test at -320°F. Deformation faulting also accounts for the toPological features observed on the fracture surfaces of impact specimens of these steels. FACE- centered- cubic chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Many Cr-Mn-N steels transform to martensite during deformation,l-5 and several investigatorsl-3 have suggested that the brittle behavior of these steels is caused by martensite formation. However, very stable Cr-Mn-N steels also exhibit brittle behavior. Schaller and Zackeyl reported that a very stable Cr-Mn-N steel (less than 3 pct martensite formed at -320°F) exhibited a transition temperature higher than that for steels in which large volume fractions of martensite formed during testing. The explanation given by Schaller and Zackey for this observation was that in the very stable steel the martensite, because of its higher interstitial content, was more brittle than that formed in their other steels. This explanation was questioned by Tisinai and samans4 and Baldwin.6 Moreover, because the toughness of stainless martensite at cryogenic temperatures is generally very low, this explanation does not account for Thompson's7 observation that small additions of nickel (1 to 3 pct) greatly improve the toughness of high nitrogen (0.35 pct) Cr-Mn-N steels. The present paper summarizes the results of an investigation of the low-temperature brittleness in very stable Cr-Mn-N steels. The importance of the mode of deformation on the toughness of these steels is discussed. Table I. Compositions of the Steels Invertigated, Pet Steel C Mn P S Si Ni Cr N - A 0.09 14.70 0.018 0.011 0.47 0.22 18.40 0.54 B 0.12 14.90 0.001 0.008 0.48 0.14 17.80 0.38 C 0.12 14.95 0.004 0.005 0.62 3.95 18.43 0.38 MATERIALS AND EXPERIMENTAL WORK The compositions of the steels investigated are shown in Table I. Steels A and B had compositions within the limits of a proprietary Cr-Mn-N stainless steel,* whereas Steel C was similar in composition to the proprietary steel except for its 3.95 pct Ni content. All steels were hot-rolled to 1/2-in. thick plate. The plates were subsequently annealed for 1 hr at 2000°F and water-quenched. Standard longitudinal and transverse Charpy V-notch impact specimens were machined from the annealed plates. Duplicate longitudinal and transverse impact specimens were tested at 212", 80°, 32", 0°, -100°,-160°,-200°,-256", and -320°F. Longitudinal tension-test specimens were also machined from the plates and tested at a crosshead speed of 0.05 in. per min at the aforementioned temperatures. The fractured impact and tension-test specimens of all three steels were examined to determine whether martensite had formed during testing. Magnetic, X-ray, electron-diffraction, and electron-microscopy techniques were used to detect the presence of martensite in the highly deformed areas of these specimens. Metallographic examination of highly deformed areas of impact and tension-test specimens revealed the presence of dark-etching bands, such as those shown in Fig. 1. These bands were observed only in deformed samples and were thought to be associated with the low-temperature brittleness of the Cr-Mn-N steels. Accordingly, a sample 1 in. wide by 3 in. long was cut from the 1/2-in.-thick plate of Steel C. This sample was surface-ground to a in. and then cold-rolled 60 pct at -320°F. Thin foils were prepared from the cold-rolled sample and examined in a JEM electron microscope. Brightfield, dark-field, and selected-area diffraction techniques were used to determine the cause of the dark-etching bands. Fractographic experiments were also performed. Impact specimens Of Steels A, B, and C were broken at -320oF, and the fracture surfaces of these specimens were immediately shadowed with carbon. The carbon replicas were examined in a Siemens electron microscope, and attempts were made to correlate the topological features of the fracture surfaces with the deformation mechanisms that could be occurring during an impact test of these steels.

Jan 1, 1970

By M. R. J. Wyllie

In a recent publication1 wetting phase relative permeability was exvressed as: and it was stated that a similar expression applied, mutatis mutandis, to non-wetting phase relative permeability; i.e., In Equations (1) and (2), Sw and S0 are respectively the wetting and non-wetting phase saturations as a fraction of the pore volume; PC is the capillary pressure; I; the wetting phase electrical resistivity index; IN, the analogous non-wetting

Jan 1, 1951

By M. R. J. Wyllie

In a recent publication1 wetting phase relative permeability was exvressed as: and it was stated that a similar expression applied, mutatis mutandis, to non-wetting phase relative permeability; i.e., In Equations (1) and (2), Sw and S0 are respectively the wetting and non-wetting phase saturations as a fraction of the pore volume; PC is the capillary pressure; I; the wetting phase electrical resistivity index; IN, the analogous non-wetting

Jan 1, 1951

By Robert A. Colten, Frederick C. Hull, Robert F. Mehl

It is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth.l,2 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in I939.3 Two types of process were described: (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures; and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth. Both cases are met in the formation of pearlite from austenite (Fig. I);2,4 the former, occurring near the knee of the S-curve, has been named "grain-boundary transformation," and the latter, occurring at temperatures near Ael, has been named "group-nodule transformation." In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important1,2 to obtain data on the rate of nucleation and the rate of growth of pearlite. Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the factors that affect hardenabil-ity; when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite.2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature, and the degree of homogeneity of the parent austenite. The studies are restricted chiefly to plain carbon commercial steels." Previous Data on Rate of nucleation and rate of Growth Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Meh1,l and by Dorn, De Garmo and Flanigan.2, It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc.), austenite grain size, and mode of formation of pearlite at the temperatures given. Except for the approximations of Mehl and the work of Dorn, austenite grain size was disregarded, though it is well known

Jan 1, 1942

By Robert A. Colten, Frederick C. Hull, Robert F. Mehl

It is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth.l,2 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in I939.3 Two types of process were described: (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures; and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth. Both cases are met in the formation of pearlite from austenite (Fig. I);2,4 the former, occurring near the knee of the S-curve, has been named "grain-boundary transformation," and the latter, occurring at temperatures near Ael, has been named "group-nodule transformation." In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important1,2 to obtain data on the rate of nucleation and the rate of growth of pearlite. Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the factors that affect hardenabil-ity; when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite.2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature, and the degree of homogeneity of the parent austenite. The studies are restricted chiefly to plain carbon commercial steels." Previous Data on Rate of nucleation and rate of Growth Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Meh1,l and by Dorn, De Garmo and Flanigan.2, It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc.), austenite grain size, and mode of formation of pearlite at the temperatures given. Except for the approximations of Mehl and the work of Dorn, austenite grain size was disregarded, though it is well known

Jan 1, 1942

By A. A. Smith, J. S. Smart

THE elements silver, cadmium, tin, antimony and tellurium either are found as impurities in commercial coppers or are intentionally added to produce coppers for special uses, When present in small quantities, each of these metals exerts a significant effect on the properties of copper, but despite considerable experience and investigation much remains to be learned about their specific behavior. The presence of extraneous elements, particularly oxygen, complicates the study of individual additions of impurities in the range 0 to 0.05 per cent, and the use of high-purity copper has been found extremely helpful in circumventing these difficulties. It has also been found that individual behavior can be satisfactorily determined from measurements of two commercially important properties, conductivity and softening temperature, according to methods that have been described previously.1,2 Data of this type, obtained in the course of a general investigation of the effects of impurities on the properties of both oxygen-bearing and oxygen-free copper are presented herewith. All samples except those containing cadmium were prepared as 3/8-in. continuously cast oxygen-free rod from pure copper and weighed amounts of a similarly synthesized master alloy. Composition was checked by chemical methods, which in every case verified the calculated analyses. Test wires were cold-drawn one B. and S. number per pass on a string-up machine using four 30-min. 600°C. anneals at 0.3125, 0.257, 0.204 and 0.162 in. and a final cold reduction of 75 per cent to 0.081 in. Some oxygen-bearing samples were produced directly from the 3/8-in. oxygen-free rods by diffusion from a surface scale at 850°C. and drawn to size as listed above, but most of the alloys were remelted in pure graphite and cast through air into a I-in. round mold, The slugs were then hot-rolled to 5/16 in., drawn to 0.162 in., annealed as listed above, and drawn to 0.081 inch. Conductivity wires were annealed for I hr. at 100°C. intervals between 300° and 800°F., using a hydrogen atmosphere for oxygen-free samples and purified nitrogen for the oxygen-bearing type, All samples were quenched from the annealing temperature in 10 per cent H2SO4 and conductivity was measured on a Hoopes bridge that had been checked against a Kelvin bridge. The softening temperatures represent the half-hard stage of the annealing curve as determined by a standard procedure.1 EFFECT OF SILVER Numerous excellent studies of the argentiferous coppers are found in the literature, and these have been adequately

Jan 1, 1943

By C. R. St. John, R. W. Lindsay, Charles R. Austin

MANY of the factors influencing the creep behavior of ferrous alloys have been investigated and reported upon in the literature, including such variables as grain size, steelmaking practice, nature and stability of the microstructure, and the effect of alloying elements in steels. However, with respect to the latter, the microstructures involved are usually heterogeneous and as a result the effect of the addition is related to its effects on the various phases present in the microstructure. In the instances where this structure consists of ferrite and carbide, the behavior of the alloy addition will be related to its action in strengthening ferrite and in opposing temperature softening of ferrite as well as coalescence of carbide. The present paper is the third in a series comprising a comprehensive review of investigations on the properties of iron binary alloys. 1.2 Its purpose is to describe the results of isolating one microstructural phase, namely ferrite, and studying its creep characteristics in both the unalloyed and alloyed conditions. This should aid in establishing to a large degree the importance of ferrite in the creep behavior of steels consisting of the previously mentioned ferrite-carbide aggregate. REVIEW OF PREVIOUS WORK In view of the fact that the present investigation deals only with the effects of silicon, manganese, chromium, molybdenum, nickel, and cobalt, and to a certain extent with the effects of carbon, the review of previous literature will be confined to these elements. Practically no references were encountered dealing with the influence of these elements on the creep characteristics of the isolated phase. However, various contributions have dealt with the creep behavior of low-carbon steels alloyed with the elements under consideration. A particularly concise review in this respect is given by Bullens (Battelle)3 and much of this material has been drawn upon. The definite improvement in creep resistance and high-temperature strength conferred by molybdenum is well known. Published suggestions by the A.S.M.E.4 permit of an increase of some 2000 to 5000 lb. per sq. in. in permissible design loads over a temperature range from 650° to 1000°F. as a consequence of additions of 0.40 to o.60 per cent of this element in carbon steels of the order of o.25 to o.35 per cent carbon content. Babcock and Wilcox Tube Co.5 has published data showing the pronounced increase in stress necessary to cause one per cent creep per 10,000 hr. when additions of 0.5 or 1 per cent molybdenum are made to a plain carbon steel. These data apply to temperatures over a range from 800° to 1000°F.

Jan 1, 1945

By C. R. Hayward

THE CHAIRMAN (ALBERT SAUVEUR, Boston, Mass.).-I am sure we are indebted to Prof: Hayward for his addition to our knowledge of the influence of sulphur on steel. As he has said in this paper, sulphur has had many defenders in recent years. It seems to me, however, that, while it may be old school to believe in the detrimental action of sulphur, it is not yet old school to believe in segregation; that while it may be that 0.1 per cent. of sulphur has no very great effect on the physical properties of steel, a ladle analysis of 0.1 per cent. of sulphur may readily result in 0.2 or 0.3 per cent. sulphur being present in the segregated portion of the ingot, and that, it seems to me, might be a rather serious matter. J. S. UNGER, Pittsburgh, Pa.-Prof. Hayward has presented the results of an investigation along a line to which I have devoted considerable time and attention, and I am particularly pleased to note that his results are in accord with my own and further tend to prove the fact that the old, established prejudice against sulphur is based more on belief than actual facts. I have felt for years that tooo much stress was placed on the harmful influence of certain elements in steel such as sulphur, phosphorus, copper, etc., but it has only been within recent years that efforts have been made to, establish the truth. Practically all the investigations made to date have proven that these elements within reasonable limits are harmless and, in fact, that for certain purposes the addition of these elements is beneficial. In referring to copper, J. E. Stead, Vice-President of the British Iron and Steel Institute, said at their last meeting: "Even today one comes across steel specifications in which copper is barred, which can only be regarded as ail indication of ignorance, if not stupidity, of those who prescribe the composition of steel, for it has been long ago proved that copper in steel, instead of being an evil, is quite harmless, and is sometimes distinctly beneficial." Sulphur owes its evil name to the early days of the manufacture of steel. Chemical analyses were crude, and failure due to either poor raw materials or metallurgical treatment were many. Sulphur being a comparatively easy element to determine with reasonable accuracy, particular attention was called to the amount of sulphur, and the failure was attributed to it, without giving any consideration to other causes. A pre-

Jan 4, 1917

By J. Stuart Warner

The reaction COSO4(c)?CoO(c) + So3(g)was investigated from 950° to 1170OK by two different methods. The sulfate was decomposed in a previously evacuated space and Pso3 calculated from the measured total pressure on the assumption that Pso2 = 2P02. The sulfate was also decomposed under conditions of controlled oxygen pressure. The difference in the results obtained by these experimental techniques is attributed to the effects of thermal diffusion. The standard free energy change for the reaction is given by ?F° = 66,292 + 17.273T log T — 102.57 T (±300 cal/mole). It was found by DTA and X-ray diffraction studies that CoS04 undergoes a transformation at 617°± 4°C. THE metal sulfates may decompose directly to the oxide or pass through one or more intermediate basic sulfates. Provided the oxidation state of the cation does not change in the course of the reaction, the decompositions may be described in general as follows: One of the major objectives of this work was to determine the validity of Eq. [3] as much of the existing sulfate data has been calculated from decomposition pressures by Eq. [5]. The type of apparatus generally used for these measurements consists of a reaction vessel at high temperature which communicates with a manometer at room temperature. A temperature gradient is thus imposed on the gas phase causing thermal diffusion which brings about a partial separation of the different gaseous species present in an initially uniform mixture. The basic theory and experimental facts associated with this phenomenon are summarized elsewhere1 and it will suffice to state here that the heavier gaseous species diffuses down the temperature gradient. Since thermal diffusion destroys the homogeneity of the gas phase, it is not necessarily true that Pso2 = 2Po2 in any particular volume element of the gas phase even though there are twice as many molecules of SO, as of 0, in the gas phase considered as a whole. Under these conditions, the decomposing sulfate gives off SO, which dissociates to SO, and 0, and all three species are distributed throughout the system by thermal diffusion. However, the sulfate will continue to dissociate until the equilibrium value of PSo3 is established on the hot zone. Thermal diffusion may distribute SO2 and O2 throughout the gas phase in any way so long as Eq. [2b] is satisfied in the hot zone; i.e. Pso2(Po2)1/2=K3pso3. When a steady state is reached, we can characterize Pso2 in that

Jan 1, 1962

By T. V. Philip, R. E. Lenhart

When commercial silicon iron sheets of varying magnetic quality are isothermally annealed at high temperatures, extremely large grains develop in the material having good magnetic properties. These grains are of the (110) [001] orientation and are formed by secondary recrystallization. The primary driving force for this secondary recrystallization is grain boundary free energy. For the secondary grains, activation energies of 103 kcal per mole for nucleation, and of 75.5 kcal per mole for growth, were obtained. The activation energy for nucleation of the secondary grains is consistent with a model involving redistribution of a precipitate acting as the primary grain growth inhibitor. SINGLY oriented silicon iron sheet was first produced in 1935.1 The material as commercially produced today has a very highly developed preferred orientation or texture; up to 95 pct of the grains are crystallographically oriented with their (110) planes in the plane of the sheet and their [loo] directions parallel to the rolling direction. This texture, usually written as (110) [00l], is referred to as the "GOSS" or the "cube-on-edge" texture. Because the magnetic properties of this material are superior to those of the nonoriented sheets in the direction of rolling, the oriented silicon iron has acquired tremendous industrial importance especially in the manufacture of transformer cores and other electrical equipment. The commercially produced material is essentially an iron-silicon alloy containing about 3 1/4 pct Si with minor impurities totaling less than 0.15 pct. The silicon steel heat is melted in the open hearth or electric furnace. The ingots are hot rolled, with or without being slabbed, to strips of 0.100 to 0.080 in. thickness. They are then cold reduced to an intermediate thickness, recrystallized, cold reduced to final thickness, decarburized, and finally annealed at a high temperature. During this high-temperature anneal, extremely large grains with the cube-on-edge texture are produced in the sheet. Several papers have appeared in the literature2-10 relating to the production of the Goss-textured material. Most of these describe the textures produced on cold rolling and on subsequent annealing of single crystal or polycrystalline silicon iron. May and Turnbull11,12 have recently shown the necessity of a second-phase dispersed impurity in the material for the production of the Goss texture. However, none of these papers describes in detail the nucleation and growth kinetics of the (110) [001] grains during the final high-temperature anneal.* The present work, therefore, is an attempt to understand the nucleation and growth kinetics of the cube-on-edge grains in the silicon iron sheet during the final high-temperature anneal.

Jan 1, 1962

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By J. H. Frye, C. P. Sun

A Frimary substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced, solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver alloys.1-5 It has been shown that at least four factors are involved: (1) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2,4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work-hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. Calculation of Rates as Work- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By Frank C. Kelton

A method is outlined for the analysis of large cores, developed primarily for the purpose of obtaining reliable data on fractured or vugular limestones. Porosity and fluid saturations are determined by a modified Dean-Stark extraction after initially bringing the samples to 100 per cent liquid saturation by a vacuum-pressure method. Horizontal permeabilities on the whole samples are determined in two directions, parallel and perpendicular to the di-rection of principal fracturing. Results are presented for various types of formations. A comparison is made between data obtained by this special method and the method of conventional analysis, and discussion is given of the relative advantages and limitations of each. In view of this comparison a modified method for the analysis of fractured and vugular formations is proposed, which method retains the advantages of the previously outlined techniques but gives promise of speeding up the analysis. INTRODUCTION For many years the greater part of the production in the Permian Basin was from formations of Permian and Pennsylvanian age. While production from these formations is still the predominant production. deeper prospecting has brought to light older formations with oil productive characteristics. Attempts to core these deeper horizons were at first usually characterized by poor recovery. The old rule of thumb, "good core recovery — poor well" was originated and remained in effect until recently. With the advent of diamond coring and the increased efficiency in drilling and coring operations. the old adage has lost its significance. Formations of Devonian. Silurian and Ordo-vician ages were successfully cored with varying degrees of recovery. The cores thus obtained were surprising and in some case; disappointing. Good recovery from these formations led to speculation as to the feasibility of analysis and the meaning of data obtained from conventional analysis. Commercial laboratories were engaged to analyze these cores. and their results indicated that data obtained by conventional methods would be of little value. From visual inspection it was apparent that in many cases the effective porosity for storage of hydrocarbons. and permeability. were contained largely in fractures and solution cavities rather than in the primary crystalline structure of the formation. In other cases the solution cavities augmented the effective porosity of the primary crystalline structure, or fractures enhanced the permeabiilty of the latter so that the formation might respond favorably to acidization and become commercially productive. Since the spacing of the cavities and fractures was often comparable to the core diameter, it was evident that the entire core should he analyzed instead of small fragments. On the basis of these observations, commercial laboratories were requested to devise a system of analysis which would yield data of practical value. Pro- cedures have accordingly been developed which seem to meet this requirement, and to date nearly 12,000 large core samples have been analyzed. It is the purpose of this paper to describe the methods used, to present typical results for several fractured formations and to compare the data obtained by this special analysis with that obtained by conventional analysis. Certain modifications and alternative procedures are finally suggested to speed up the analysis. CORE ANALYSIS PROCEDURE Fluid Saturations and Porosity The core sample, in segments up to 15 in. in length. is marked, weighed and examined under ultra-violet light to determine the presence of oil saturation. If present, the approximate quantity of oil and its location on intercrystalline, fracture or vugular surfaces is noted. This information is carefully recorded. The degree of fracturing and/or vugular development is also noted. The sample is then placed in a pressure cell and the air evacuated with a high speed vacuum pump. This evacuation is continued only long enough to reduce the pressure to approximately the vapor pressure of water in order not to remove excessive amounts of water. Water is admitted to the cell and allowed to penetrate the sample under atmospheric pressure, filling the pore space initially occupied by air and replacing the small amount of water removed by evacuation. Pressure up to 200 psi is applied to force water into the smaller capillaries, and the sample is left sub-

Jan 1, 1950