By H. Masuda

The lijima Zinc Refinery started operation in 1972, and has today an annual capacity of 200,000t-Zn. The hematite process was employed for the first time and the ideal of waste-free refinery has been pursued for 30 years. In recent years, however, only half of the hematite produced would be sold to the cement industry and hence a reduction of arsenic level has been necessary in order to sell the entire amount produced. The arsenic cementation process with zinc powder, developed through a long time laboratory research was found among some options as the best for the hematite process. The construction work started in 2000 and the facility was put into operation in 2001, As a result in the same year all hematite were sold to the cement industry. The outline of this project, present operations and technical issue are reported in this paper.

Jan 1, 2003

By J. Y. Aubut

The modernization of the CCR Refinery to permanent cathode technology is presently underway. The 360,000 mt/y refinery is being retrofitted to accept the Kidd process. Part of this modernization includes the installation of Kidd stripping machines, and the total replacement of the materials handling equipment. It also involves the reinforcement of building structures to accept the new equipment and the ability to operate in different modes. The future equipment will interface with some existing apparatus, which is being retained for future operations. The whole operation will be automated and will allow product traceability for quality purposes. This retrofit poses important challenges given the size and scope of the modernization project and because it is being undertaken concurrently with normal plant operations.

Jan 1, 1999

By C. W. Vierrether

Mineralogical analysis contributes directly to the selection of applicable beneficiation techniques for a given site. Tentative remediation methods for use on the Sharon Steel tailings in Midvale, Salt lake County, UT, were determined in part by mineralogical characterization. A systematic characterization scheme was employed to identify mineral species, mineral associations, and grain size. This paper presents the mineral content and distribution data collected for site characterization. This data was used to determine areas that were representative of the total tailings at the Sharon Steel site. Although this was the main focus of characterization, other useful information was obtained. The approximate location of "old jig tails" was identified and insight on possible arsenic, mobility through the pile was also obtained from the mineralogical study.

Jan 1, 1991

By J. M. Tourre

1995 have seen a continuation of a positive trend in the Rare Earth industry The availability of a greater diversity of Raw Material has brought additional flexibility to the Producers permitting better economics China remains the major raw material source; Chinese concentrate producers have increased capacity in 1995 (Baotou, Sichuan, etc) China's role in the Rare Earth industry will continue to evolve; the acquisition of a majority equity position by San Huan/CNNC will have a significant impact on both the Rare Earth and Magnet markets Chinese producers are increasing the quality of their products and realize their true values Chinese market, itself, is also changing as the internal needs for separated rare earth's grow Already already producer of Lamps, Loudspeakers, Magnets, and TV tubes, China is in an unique position where the potential of its internal market might be more promising than the prospects outside China 1995 has also seen the application market become more diverse and complex. There are new applications growing at a very strong pace (such as battery alloy), applications that are now penetrating their target markets with significantly increased growth rates (such as bonded NdFeB), and some applications that became more complex requiring much more sophisticated products (such as catalysis). Rare Earth producers have to spend significant ressources in order to monitor the market trends in order to predict the demand and then adjust their raw material mix. Even though there is a greater diversity of raw material available, there is still some Rare Earth elements that are in excess, while other are just in balance. As a consequence rare earth producers invest heavily in R&D in order to develop new applications for these excess elements.

Jan 1, 1997

By Batric Pesic

Gold dissolution with bromine was studied by using the rotating disc technique. Geobram TM 3400 was used as a source of bromine. The parameters studied were: rotating speed, Geobrom 3400 concentration, pH, temperature, sulfuric and hydrochloric acid concentration, and the concentration of various cations (copper, iron, zinc, aluminum, manganese, potassium and sodium) and anions (chloride, bromide, sulfate, nitrate, and iodide) According to the Levich plot and activation energy, gold dissolution was controlled by a chemical reaction rate. Copper, iron, and manganese in their highest oxidation states, aluminum, zinc, sodium and potassium did not have any effect on gold dissolution rate. The presence of manganous ion dramatically decreased the gold dissolution rate. Kinetic performance of bromine, in the form of Geobram TM 3400, was compared with performance of cyanide and thiourea.

Jan 1, 1990

By P. Hanniala, J. Sulanto

"The requirement for the reduction of sulphur dioxide emissions from copper smelters is becoming more and more important. Therefore, the most important question in smelting technology will be how to produce even, high strength SO2 gas in smelter and how to combine smelting and converting. The best sorution in certain cases is to eliminate converters totally.Outokumpu is already responding to this challenge. As a result of extensive research work, Outokumpu Oy has developed the Flash Smelting Process for direct smelting of blister copper from concentrates in one step.The newest process development is the Kennecott-Outokumpu Flash Converting process, where solidified copper matte is converted into blister copper. The production of low volume high SO2 content gases, separation of smelting and converting operations to allow increased on-line availability, and simplified process control are the major benefits of the process which translates to reduced smelter capital and operating costs.Also, it has been studied the use of the same Outokumpu furnace for smelting and converting alternately when the production capacity is low.In this paper, the developments and improvements of the Outokumpu Process are described from the operation and investment cost standpoints"

Jan 1, 1988

By Neeraj Saxena, Madhu Huggahalli, Jerry Bednarski, Ken Grieshaber, David Stoffel

"The use of oxy-fuel burners in secondary aluminum melting applications offers several advantages over air-fuel burners including reduced fuel consumption, faster charge to tap times and lower NOx emissions. Their successful, safe and economical use in a furnace depends on several factors and considerations such as burner and flue placement, metal circulation, charge practices and the type of refractory used in the furnace.These factors required in the successful conversion of furnaces from air-fuel to oxy-fuel based burners are discussed in this paper. Critical parameters are identified and examined using computational fluid dynamics (CFD) simulations. Parameters are estimated via laboratory testing and validated through trials performed at commercial installations. Guidelines and a simplified approach to estimate a priori the economic impact of converting from air-fuel to oxy-fuel are presentedThe final products of this research are simplified and validated tools for modeling aluminum furnaces. These include improved heat and energy balance models and parameterized CFD solutions which provide rapid customization to individual furnace configurations. These tools provide field engineers with immediate and accurate predictions of performance, allowing for repeated precise scenario analyses."

Jan 1, 2001

By George R. St. Pierre

A method for the quantitative description of activity interactions between solutes in a metallic solvent which is consistent with stalistical thermodynamic principles is presented. The chemical potential of a solute in an alloy is derived from the weighted mean of its values in the individual solvent components, µi = S?jµi(i). The weighting factors, ?j, are obtained from the distribution functions. The resulting equation contains far fewer adjustable parameters than the Epsilon Formalism and because of its correct functional form it provides an improved fit to the available data on a variety of alloy systems containing oxygen, carbon, sulfur, nitrogen, and hydrogen. For a binary metallic solvent ( A, B ) containing a solute (i), it is shown that

Jan 1, 1995

By Dhanesh Chandra

In this symposium, research in the area of energy conversion is presented. This symposium has special significance, as we honor three prominent scientists from hydrogen storage research and development field. In this symposium, the majority of papers presented by international scientists and engineers are in the area of hydrogen storage. Other energy conversion papers include magnetic materials, superconductors, and thermal energy storage materials. Recent developments in light-weight high gravimetric hydrogen density hydrides have led to potential use of hydrides for onboard automobile and other applications. This, of course, is significant from environmental concerns of CO2 and other emissions from the current use of carbon based fuels in automobiles. Thus, it is becoming increasingly important to switch to cleaner alternative fuels such as hydrogen [1]. The Challenge of Vehicular Hydrogen Storage as potential hydrogen energy carriers for vehicular applications, with a driving range of approximately 300 miles, require ~5-13 kg of hydrogen stored on-board. In the United States, Centers of Excellence have been established in metal hydrides, chemical hydrides, and carbon-based materials, and abundant scientific and industrial research is being carried on metal hydrides; only some of the current research from the Centers will be reported here. The European commission, Japan Institutions, and others also have numerous hydrogen storage programs in progress. Several international collaborations have also begun between IEA and IPHE scientists to accelerate the progress of development of practical hydrides. A summary of the abstracts is included in this overview.

Jan 1, 2006

By M. E. Karabin, R. J. O'Malley

"A mathematical model of the roll casting process has been developed which predicts macro-variables, such as roll separating force, roll torque, and strip exit speed for a range of roll speeds. Continuum variables, such as interface pressure, interface shear stress, freeze-front shape, and internal temperature distribution are also predicted.The model consists of two independent segments: solidification and rolling. The solidification model is two-dimensional (thickness and rolling direction) and is capable of handling alloy solidification. The solidification model is employed until solidification through the thickness is complete, then the rolling solution is activated.The rolling model is a one-dimensional (rolling direction) mechanical solution based on the von Karman approach, coupled with a two-dimensional thermal solution. The flow stress is expressed as a function of the average through-thickness temperature of the strip.Experiments were performed using a laboratory roll caster to test and refine the model. Experimental strip exit temperatures were used as input to the model. Experimental and predicted roll torque and strip exit speea were forced into agreement at a single reference roll speed to obtain values for the coefficient of friction and the interfacial heat transfer coefficient. Using these values, good agreement was obtained between predicted and experimental torque and strip exit speed over the entire range of roll speeds examined."

Jan 1, 1986

By Jian Wang, Hongyang Cao, Binxiu Wu, Junhong Li, Jimin Wang

"The enrichment and separation of scattered metal indium component in the pressure leaching solution with sulfuric acid from vacuum furnace germanium slag were studied by iron substitute and P204 extraction, which is supplied by shaoguan smelter. The experimental results show that the extracting power of P204 for indium from pressure leach solution is powerful. The optimal technological condition were the ratio of P204 and sulphonating serosene 3:7, phase ratio 1:3, solution pH 1.2, and extracting 5 minute. The enrichment indium solution of 21.7 g/L In at 95.2% recovery ratio was obtained by three-stage counter flow extraction and four- stage counter flow stripping.IntroductionScattered metals, such as Indium and germanium, were inriched as intermediate product or by-product during the metallurgy process of other non-ferrous metals, such as lead, zinc, copper and tin. For example, the indium and germanium were inriched in vacuum furnace germanium slag, which is the by-product of zinc vacuum distillation operation from hard zinc. It is difficult to recovery the indium from the vacuum furnace germanium slag, because the indium content is low, and the chemical composition and phase compositon were complex.Recovery indium from bearing indium zinc slag was researched extensively, such as pressure acid leaching, high temperature evaporation, solvent extraction method[l-7], acid leaching method has the advantages of high leaching rate, which can be separated hydrochloric acid, sulfuric acid and silicon fluoride acid systems. Solvent extraction method has the advantages of low production cost, fast reaction speed, high enrichment ratio, and simple operation."

Jan 1, 2013

BHP Hartley Platinum operates an electric smelting furnace to treat Cu-Ni-PGM concentrate at its plant in Selous, Zimbabwe. The furnace, originally built by others, has experienced problems including severe refractory erosion of the sidewall. Hatch Associates has designed several important improvements to the furnace, including: ? water-cooled copper cooling elements in the slag zone ?air-cooled copper cooling fins at the metal level ?water-cooled copper tapholes ?binding system providing vertical refractory compression ?electrode seals ?new feed pipes Novel construction techniques employed on this project to reduce shutdown duration are discussed.

Jan 1, 1999

By Cyro Takano

This paper is a contribution to fundamentals data on the equilibrium metal/slag for refining silicon in relation to Ca and Al as impurities. Silicon containing 0.1% Al and no Ca was placed in contact with a slag of various contents of CaO, SiO2 and Al2O3. Slag Al2O3 contents were 11.4%, 25.1% and 29.6%, keeping the ratio %CaO/%SiO2 constant and equal to ~0.53. The experiments were conducted at 1550oC, in a graphite crucible with argon atmosphere. The equilibrium was observed with low and medium content of Al2O3. The derived activities coefficients of Ca and Al in dilute solution of Si presented good correlation with those of the literature. Parallel reactions with formations of SiO(g) and CO (g) were also observed.

Jan 1, 2006

By Milton Manrique, Edgar E. Vidal, Patrick R. Taylor

"Ultrafine zirconium carbide powder has been synthesized using zircon concentrate and methane in a thermal plasma reactor. The effect of several experimental variables, such as power used and zircon particle size, on the conversion has been studied. A thermodynamic analysis of the possible reactions and stable compounds was performed. A mathematical model that describes the in-flight decomposition of zircon particles was developed based on a description of the temperature and velocity profiles calculated in the reactor. It was shown that the formation of zirconium carbide from zircon and methane is thermodynamically possible. Complete 'vaporization of zircon in the reactor is predicted when the particle size is below 45flm and the effective power entering the reactor is 15 kW. The powders were collected and characterized by XRD, SEM, TEM and chemical analysis using ICP. Results of the product analysis indicated the presence of zirconium carbide, zirconium oxide, silicon carbide and silicon oxide.IntroductionIn recent years there has been an increased interest in the production of nanometric sized powders of ceramic materials for use in advanced materials applications. One possible method to produce these powders is with a thermal plasma reactor, which offers high temperatures and fast quenching rates. This technology has been called - Thermal Plasma Synthesis - [1].Zirconium Carbide (ZrCx) has typical properties of transition metal carbides: elevated hardness - between alumina and diamond - a high melting temperature of 3420°C and high chemical stability at room temperature [2]. ZrCx has a Bl crystal structure with deficiencies in the number of carbon atoms in the cell with x between 0.6 and 1 [3]. Different methods have been used to produce ZrC, one method is by direct reaction of zirconium hydride or halide with carbon. Other methods used are direct reduction and carburization of zirconium oxide (Zr02) and reaction of metallic zirconium with a caburizing gas such as acetylene [3]. Recently small films of ZrC have been obtained using a sputtering device [4,5]. ZrC has been used in nuclear plants as a low neutron absorbing and high mechanical resistant refractory material and also as a constituent in cathodes made of UC-ZrC [6]. It is also used in the form of tubes, boats and crucibles to handle molten metals and as part of electronic devices used for thermoionic transducers. Recently ZrC has been used along with zirconium diboride (ZrB2) to produce composite materials [7,8]."

Jan 1, 1996

By Yuuki Yoshida

Electrolytic manganese dioxide, EMD, is the positive electrode material of primary batteries and the raw material of LMC used as the positive mass of lithium ion batteries and is currently produced by anodic deposition on and harvesting from a titanium anode in acidic manganese sulfate solutions prepared by dissolving high purity of manganese sulfate into sulfuric acid solutions. This paper presents an alternative method of EMD production using a novel anode, Mn2O3 coated titanium, at lower operating temperature than the current process to explore a possibility of manganese recovery from zinc electrowinning solutions. The Mn2O3/ Ti anode prepared by thermal decomposition of a precursor solution containing Mn (II) showed the anodic deposition of MnO2 by constant current electrolysis and the current efficiency was 95% in maximum, while the current efficiency and the crystallographic structure of deposited MnO2 depended on the current density, the electrolysis time, the bath temperature, and the concentration of Mn(II). The deposited MnO2 was successfully harvested from the anode and the recovery rate was 98%.

By Fathi Habashi

Solid gas reactions of metallurgical importance can be classified into three groups: Physical processes, e.g., drying and sublimation Chemical processes which may be an addition or a thermal decomposition reaction Electrochemical processes which may be addition, oxidation-reduction, or displacement reactions. Examples are given and the role of the boundary layer is emphasized.

Jan 1, 1996

By Takeshi Azakami

By combining the iron reduction process with the usual rotary kiln process, the direct production of metallic zinc from EAF dust is proposed. After thermodynamic estimation and desk-top experiments it is confirmed that the process is hopeful under suitable conditions. In order to get some practical test data the enlargement of the process scale was planned and the bench scale tests were carried on successfully. In these experiments a zinc ingot of PW grade was produced from EAF dust.

Jan 1, 2003

By Ali Akbar Mottahedi

Chromate conversion coating is a process for making a complex layer at the surface of zinc galvanized steel which makes the metal more resistant to corrosion, especially at marine atmosphere, and increases the adhesiveness of color. In this work the influences of various compositions on commercial zinc galvanized steel sheet to the color of chromate conversion coating has been investigated at normal temperature and the factors that affect the control and optimization of the process have been determined. A bath composition of 20 g/liter Cr203 and 10 g/liter NaOH and a dipping time of 50 seconds at room temperature (25-30°C) make a desirable color of chromate coating. A slow agitation at a constant pH of I (with additions of NaOH or H2SO4) assures a constant bath condition and develops the color. This kind of coating has more corrosion resistance and this bath condition and composition are also more economical.

Jan 1, 2003

By Jan G. H. du Preez, C. Viviers, B. J. A. M. van Brecht, H. E. Rohwer, Nicole M. Sumter

"At the basis of metal ion separation lies some particularly metal ion specific chemical property which lends itself towards exploitation. This could be in the form of an anionic complex or a neutral chelate complex. In the former a cationic centre with a particularly high affinity for the complex will have to be designed. In the latter case a stereospecific chelate ligand containing the correct symmetry and type of donor atoms will have to be designed. In both above cases the ""active centre"" can be entered in a from that it can function in different media of hydrophobicity, eg a precipitant, a resin or a solvent extractant. Recent results obtained in this laboratory will be used to illustrate how the above variables can be exploited to develop improved processes for the separation of base metal and platinum group metals.IntroductionThe separation of metal ions in hydrometallurgy can be performed broadly speaking with two major aims. Firstly the separation/removal of a certain group of metal ions, either as a means of preconcentration or as a removal from effluent as part of a purification process and, secondly the removal of a specific metal ion from an industrial stream in order to produce a specific metal in a pure form. This latter operation is by far the most difficult of the two and is becoming more so in the light of the fact that the world is moving in the direction of lower grade ores and increasing pollution. Such a process can be divided into three essential parts, firstly the molecular one in which an active centre is required to obtain specificity, secondly a matrix within which this active centre must function, i.e. as part of a resin or solvent extractant and thirdly the design of the total system to optimize the realization of the operation."

Jan 1, 1996

By W. P. lmrie

The recent years have seen many copper smelting operations become uneconomic due to a combination of low metal prices, high energy and labor costs, environmental requirements and high investment costs for modernization or replacement. Since a copper commodity requirement remains, the industry will recover, but many operations will need to determine which processes can offer the best prospect for economic operation and readiness for reliable investment and implementation. Corporate investment decisions involve the judgment of many factors in addition to topical technical aspects. Consideration of plant management and operational aspects are thus included. Taking account of such proven processes as conventional, flash and continuous smelting, plus modified conventional and new unproven processes, this paper gives a systematic approach to aid optimum choice for a modernization or grassroots investment. Actual achievements in energy form alternates, conservation and cost effectiveness are highlighted, and areas of remaining potential for energy saving are discussed.

Jan 1, 1983