By Kenneth K. Humphreys, J. W. Leonard, T. S. Spicer

INTRODUCTION Reasons for Thermal Drying The continuing increase in the percentage of - '/4 in. ( -6.3 mm) coal produced as a result of the increased use of mechanical mining methods has, over the years, tended to shift considerable portions of the work of producing salable coal to the fine coal cleaning section of the preparation

Jan 1, 1979

By Chas. F. Jackson

IN these days the headlines and spotlight have been focused largely upon the new processes developed and new plants erected to meet the multiplied demands for mineral products required for prosecution of the war. By comparison, the less spectacular achievements of the miner, who is meeting the demand for raw material without which these processes and plants would be useless, have received little attention. Attendance at the mining meetings here reported was small, averaging about 35 to 40, but interest was as keen as ever, and evidenced to your reporter that the miner is no less on the job than is the metallurgist. It is evident that the mine operators are not neglecting any improved methods and practices in their struggle to produce more in the face of diminishing labor supply.

Jan 1, 1943

By W. A. Backofen, D. L. Holt

Push-pull fatigue tests have been carried out at 4.2°K, 77oK, and room temperature on two poly crystalline materials of widely different stacking-fault energy (?): pure copper (? - 70 ergs per sq cm) and the Cu-8 wt pct A1 alloy (? - 2.8 ergs per sq cm). Constant stress-amplilude was imposed and measurement was made of the plastic-strain amplitude (ep) at saturation. Lives extended from 104 to 106 cycles. Designating lives at the various temperatures by NRT, N77, and N4.2. the ratios N77/NNT and N4.2/N77 ranged from 3.5 to 18 under the condition of common Ep . Metallo-graphic examination revealed different crack morphology in Cu-8 Al fatigued at room temperature, and at 77" and 4.2oK. At room temperature, cracks lay in or near grain and lain boundavies; at 77o and 4.2oK. cvacks were transcrystalline. Tests on single crystals of Cu-8 A1 showed that such a change in the cracking mode in polycrystallitle material accounted for a factor of- about 3.25 in N77/NRT . The longer life at lower tewperatztre (conslant cp) has heels attributed to two deuelopinents: a reduced production of the dislocation tangles and subgrain boundaries which serve as paths of rapid cracking, and suppression of oxygen chetni-sorption at the crack tip It was concluded that in both materials the luller accounted for an extension of the life at 4.2oK beyond that at room temperature by a factor of 15. XV ECENT experiments on the fatigue of Cu-A1 alloys in the so-called high-cycle range (greater than lo4 cycles) have emphasized the importance of stacking-fault energy (y) as a quantity affecting crack propagation rate and fatigue life.1,2 It was found in comparisons at essentially fixed plastic-strain amplitude that crack growth rate decreased by a factor of about 5 over the composition range from copper (? - 70 ergs per sq cm) to Cu-8 wt pct Al (? - 2.8 ergs per sq cm). The argument was made that, when stacking-fault energy is high, cross slip and climb are favored, so that dislocation tangles and/or subgrain boundaries form more readily under cyclic loading. Since the boundaries and tangles act as paths of rapid crack propagation ,3, 4 life is shortened as a result. However, when stacking-fault energy is reduced (as by alloying), cross slip and climb become more difficult, with the result that substructure formation is retarded and growth rate is also reduced. A purpose of the present work was to investigate the substructure effect in relation to temperature. As temperature is lowered, ? is varied only slightly (if at all), but decreased thermal activation can interfere with cross slip and climb. Thus substructure formation could be curtailed and life increased. Fatigue life in the high-cycle range is also known to be strongly influenced by environment. Working with copper, Wadsworth and Hutchings observed that life in a vacuum of 10-8 mm Hg exceeded life in air by a factor of 20.5 They isolated oxygen as the agent that furthered cracking. While the details are still unclear, a requirement in any mechanism of oxygen-accelerated cracking is that there be chemisorption at the crack tip. That could prevent welding on the compression half cycle,= interfere with reversal of slip,1, 6 or aid in breaking metal-metal bonds at the crack tip.5'7 In the work being reported here, temperature was lowered by immersion in liquid nitrogen and helium, which also served to reduce both the oxygen concentration and chemisorption rate. A possible effect upon life, i.e., a lengthening, had to be recognized. Several researchers have determined fatigue lives at low temperatures presenting their results in the form of stress amplitude (S) vs cycles in life (N) curves.8-11 Such curves reflect, primarily, the fact that metal is strengthened by lowering temperature; effects of substructure and changing environment tend to be masked. The difficulty can be overcome by comparisons based on identical plastic-strain amplitudes, and in the present work the dependence of life on both plastic strain and stress amplitude was established. EXPERIMENTAL Materials. The principal materials were polycrystal-line copper (? - 70 ergs per sq cm)" and the Cu-8 wt pct Al alloy (? - 2.8 ergs per sq cm),I3 the latter being near the limit of solubility of aluminum in copper and having, therefore, the lowest stacking-fault energy in the CU-Al system. Specimens were machined from 0.118-in.-diam cold-swaged rods of high-purity (99.999 pct) copper and the Cu-8 Al alloy, the latter produced initially in a graphite boat by induction vacuum melting a mixture of 99.999 pct Cu and 99.99 pct Al. The machined specimens were annealed to produce mean grain diameters of about 0.070 mm in copper and 0.190 mm in the alloy. Specimen dimensions are given in Fig. 1. Values of the tensile yield stress, ultimate strength, uniform strain (determined by the Considgre construction), and reduction of area, for both materials at 4.2oK, 77oK, and room temperature, are listed in Table I. The tensile apparatus in which these results were obtained has already been described.14 Apparatus. Specimens were fatigued in push-pull with a machine that is illustrated schematically in Fig. 2. The specimen is first soldered into the top grip (1) with Woods metal, and the grip is then screwed into the inner tube (2) which is connected to the drive rod of the Goodmans vibration genera-

Jan 1, 1968

By G. St. J. Perrott

ONE of the important hazards in coal mining is the danger of ignition of explosive mixtures of methane and air or coal dust and air, or both, by the explosives used in blasting the coal. It has long been recognized that certain explosives are more dangerous than others in this respect. In America and abroad, government testing stations have been established for officially passing on the suitability of explosives for use in coal mines. In this country the Federal government is given no power to enforce the use of the approved explosives but merely publishes from time to time, through the Bureau of Mines, those explosives which have passed the tests necessary to place them on the list for use in coal mines. In spite of this lack of police power, the increase in the use of permissible explosives since the promulgation of the first list in 1909 has been rapid. In 1912, only 8 per cent. of the explosives used in coal mines were permissible; in 1925, this figure had increased to 25 per cent. While the past record of permissible explosives has been most gratifying, it is very desirable that we pave the way for further improvement in explosives and blasting methods by learning more about the mechanism of ignition of gas and coal dust by explosives. To this end a considerable amount of investigative work already has been carried out and a large amount yet remains to be done. It is the purpose of this paper to discuss briefly the effect of the characteristics of explosives and method of loading in the borehole on the liability of a blown-out shot to ignite explosive mixtures of gas or dust. For an account of the methods by which an explosive is tested for permissibility for use in coal mines, the reader is referred to Schedule 17-A of the U. S. Bureau of Mines.

Jan 10, 1926

By W. P. Haynes

The 1938 production for all of Rumania amounted to 48.984.200 bbl., as compared with 53.239.500 bbl. in 1937. which represents a drop of 4.255.300 bbl., or 8 per cent. Of the various fields. there are only two major increases in production—Baicoi-Tintea with 3.092.400 bbl. And

Jan 1, 1939

By W. P. Haynes

The 1938 production for all of Rumania amounted to 48.984.200 bbl., as compared with 53.239.500 bbl. in 1937. which represents a drop of 4.255.300 bbl., or 8 per cent. Of the various fields. there are only two major increases in production—Baicoi-Tintea with 3.092.400 bbl. And

Jan 1, 1939

By H. J. Ramey

As fluids move through a wellbore, there is transfer of heat between fluids and the earth due to the diflerence between fluid and geothermal temperatures. This type of heat transmission is involved in drilling and in all producing operations. In certain cases, quantitative knowledge of wellbore heat transmission is very important. This paper presents an approximate solution to the wellbore heat-transmission problem involved in injection of hot or cold fluids. The solution permits estimation of the temperature of fluids, tubing and casing as a function of depth and time. The result is expressed in simple algebraic form suitable for slide-rule calculation. The solution assumes that heat transfer in the wellbore is steady-state, while heat transfer to the earth will be unsteady radial conduction. Allowance is made for heat resistances in the wellbore. The method used may be applied to derivation of other heat problems such as flow through multiple strings in a wellbore. Comparisons of computed and field results are presented to establish the usefulness of the solution. INTRODUCTION During the past few years, considerable interest has been generated in hot-fluid-injection oil-recovery methods. These methods depend upon application of heat to a reservoir by means of a heat-transfer medium heated at the surface. Clearly, heat losses between the surface and the injection interval could be extremely important to this process. Not quite so obvious is the fact that every injection and production operation is accompanied by transmission of heal between wellbore fluids and the earth. Previously, the interpretation of temperature logs',' has been the main purpose of wellbore heat studies. The only papers dealing specifically with long-time injection operations are those of Moss and White3 and Lesem, et al.' The purpose of the present study is to investigate wellbore heat transmission to provide engineering methods useful in both production and injection operations, and basic techniques useful in all wellbore heat-transmission problems. The approach is similar to that of Moss and White:' DEVELOPMENT The transient heat-transmission problem under consideration is as follows. Let us consider the injection of a fluid down the tubing in a well which is cased to the top of the injection interval. Assuming fluid is injected at known rates and surface temperatures, determine the temperature of the injected fluid as a function of depth anti time. Consideration of the heat transferred from the injected fluid to the formation leads to the following equations. For liquid, Eqs. 1, 1A and 2 are developed in the Appendix. These equations were developed under the assumption that physical and thermal properties of the earth and wellbore fluids do not vary with temperature, that heat will transfer radially in the earth and that heat transmission in the wellbore is rapid compared to heat flow in the formation and. thus, can be represented by steady-state solutions. Special cases of this development have been presented by Nowakl and Moss and White.3 Both references are recommended for excellent background material. Nowak' presents very useful information concerning the effect of a shut-in period on subsequent temperatures. Since one purpose of this paper is to present methods which may be used to derive approximate solutions for heat-transmission problems associated to those specifically considered here, a brief discussion of associated heat problems is also presented in the Appendix. Analysis of the derivation presented in the Appendix will indicate that many terms can be re-defined to modify the solution for application to other problems. Before Eqs. 1, 1A and 2 can be used, it is necessary to consider the significance of the over-all heat-transfer coefficient U and the time function f(t). Thorough discussions of the concept of the over-all heat-transfer coefficient may be found in many references on heat transmission. See McAdams5 or Jakob," for example. Briefly, the over-all coefficient U considers the net- resistance to heat flow offered by fluid inside the tubing, the tubing wall, fluids or solids in the annulus, and the casing wall. The effect of radiant heat transfer from the tubing to the casing and resistance to heat flow caused by scale or wax on the tubing or casing may also be included in the over-all coefficient. According to McAdams, on page 136 of Ref. 5>

During the war period of quicksilver activity there were a number of departures from what may be termed the classical quicksilver metallurgy. Attempts were made to beneficiate low-grade ores by gravity concentration and flotation; mechanical furnaces began to replace the Scott furnace and the vertical coarse-ore furnaces, and condensers of sewer tile and redwood tanks were used in place of the older brick and stone condensing chambers. Other developments that have occurred during the current period of quicksilver activity are mainly in the nature of improvement and further refinement of those started during the war period. Each period of quicksilver activity has been accompanied by the proposal of various new processes, including wet methods for the treatment of quicksilver ores and innovations in furnaces, retorts and condenser equipment. As far as the author knows, nothing of economic significance in the way of "new processes" has been developed. There is in fact no real need for any essentially new process for the treatment of quicksilver ores; the direct furnace treatment is simple and inexpensive. Moreover, with rare exceptions, the quicksilver industry has no complex or refractory ore problems corresponding to those which are receiving more and more attention from metallurgists in other branches of the nonferrous field. Untler these conditions improvements in quicksilver metallurgy must be looked for through the adaptation of current developments in engineering and metallurgy generally to the particular needs of quicksilver practice rather than through the invention of new processes. Preliminary Treatment of Quicksilver Ores At Sulphur Bank, in the treatment of old dump material left by the early operators, wet screening is being used as a preliminary step in concentration ahead of flotation. Power shovels and trucks are used to deliver some 400 tons of ore per day to the lower terminal of a hoist, which in turn discharges the material at the top of the screening plant. Wet screening is carried on in two stages. Depending on the character of the material, 1-in. or 2-in. punched screens are used on the first trommel.

Jan 1, 1930

By J. H. Jensen

Bromine is the intermediate member of the halogen family of elements between iodine, a solid: and chlorine, a gas. The name is derived from the Greek "bromos," meaning stench. Bromine is the only nonmetallic element that is liquid at room temperatures with a melting point of -7.2" C and a boiling point of 58.78" C. Reddish brown in color, it dissolves easily in water to yield a red solution. Bromine volatilizes at ordinary temperatures to a red vapor that is very irritating to the eyes, nose, and throat. Density of the liquid is 3.12 and gas weighs 7.59 gpl at standard conditions. As the element is highly active, it exists in nature only as bromide compounds. Bromine was discovered by Antoine Jerome Balard in seawater bitterns in 1826 and first prepared in quantity in 1860. Distribution Bromine is widely distributed in nature and compounds occur in solution in natural brines, in seawater, saline lakes, oil and gas well brines, and in evaporite chloride minerals. The concentration of bromine salts ranges from 60- 65 ppm in seawater to several thousand ppm in oil well brines and saline lakes. The distribution of bromine in marine evaporite minerals and in the solutions from which they crystallized was determined many years ago by H. E. Boeke (1 908). Theoretical aspects regarding the geochemistry of bromine have been published in numerous papers (Raup and Mite, 1969). Bromine occurs in solid solution in carnallite and sylvite associated in potash de- posits; in halite in salt beds; salt in oil shales; and in trona deposits. Its presence is useful as a guide in geochemical exploration. The analysis of small amounts of bromides in the presence of large amounts of chlorides is discussed by W. Schwerdtner (1963). Manganese, iron, and iodine may interfere with the determination. Other analytical methods are discussed at length in the literature (Stenger and Atchison, 1964). Sources and Reserves The sources and reserves of bromine, given in [Table 1], appear ample to meet present and foreseeable requirements in all producing countries. With the occurrence of bromine salts in sea-water and other brines, the potential for bromine production is worldwide. It has been estimated that 99% of all commercially recoverable bromine is in the ocean. However, actual subterranean brines having a higher bromine content than seawater will continue to be the preferred sources of bromine for the foreseeable future. Markets and Prices About 17% (1968) of bromine produced is used in its elemental form, with the balance consumed as bromides and bromates. The largest use for bromine is ethylene dibromide which, together with tetraethyl lead, are used as an antiknock additive in gasoline. Tetra-ethyl lead is the antiknock agent. Ethylene dibromide combines with the lead after combustion in the engine to form a volatile com- pound that escapes from the engine with the exhaust gases.

Jan 1, 1975

By W. F. Flanagan, D. H. Polonis, S. D. Dahlgren

Rotation diffraction patterns of Cu-4.84 wt pct Si polymystalline samples were taken during the course of isothel-ma1 affing of the suPersaturated a phase, a diffraction spots were obserzled to streak during the initial stages of aging, and this streaking was similar to the streaking of a spots observed earlier by Barvett with deformed super saturated samples of the same composition. Although it was suggested that stacking faults were the sole cause of styeaking in the deformed samples, the present study has shown that plates with one small crystallite dimension can also contribute to the streaking when there is lattice coherency across close-packed planes. THE decomposition of the supersaturated a phase in Cu-Si alloys has been reported to occur by means of both thermal and stress activation.1-4 According to the Cu-Si phase diagram,3 Fig. 1, the supersaturated a phase (fcc) is expected to transform during aging by the precipitation of the y phase. The results of earlier studies2,4 have indicated that metastable k phase (hcp with nearly ideal close packing) forms initially at temperatures below the eutectoid temperature, after which the k transforms to the a and y phases. Hof-mann et al.4 have proposed a metastable version of the phase diagram, showing the approximate boundaries for k formation below the eutectoid temperature. In view of the close-packed nature of both the a and k phases, it is essential to consider the role assumed by stacking faults in the transformation. Streaking effects have been reported by Barrett 1 in the rotating crystal X-ray patterns of strained Cu-Si alloys and were attributed to stacking faults rather than particle size effects. This deduction was based on the observation that streaks in the diffraction patterns did not occur tangent to the 220fee Debye ring. It is known that the atom movements involved in faulting leave some X-ray reflections unaffected while others are broadened,' and, in particular, it has been shown that faulting will not cause streaking of 220fee reflections tangent to the 220fee Debye ring as would be expected if all the reflections were broadened.' The formation

Jan 1, 1967

By J. Gordon Parr, M. J. Bibby

In addition to the (bcc) - (cph) transformation at 882°C a second distinct change of slope has been observed on a titanium cooling curve between 905" and 960°C.1,4 Duwez,1 commenting on work by McQuillan,2-4 attributed this arrest to contamination of the specimen with oxygen—a possibility that existed even at the reduced pressure of 10-5 mm Hg at which the experiments were conducted.

Jan 1, 1963

By Allen J. Johnson

Anthracite coals have been divided into three groups: (I) meta-anthracite, a high-carbon coal that is usually very slow to kindle and difficult to burn, at least on conventional equipment; (2) anthracite, a high-carbon low-volatile coal of widely accepted value as both a domestic and industrial fuel; and (3) semianthracite, a coal lying between anthracite and bituminous coal in carbon and volatile content, and also, generally speaking, in burning characteristics. Anthracite Groupings The technical differentiation between these groups, as defined by the A.S.A.-A.S.T.M. Sectional Committee on the Classification of Coals, is as shown in Table I. Tables 2 and 3 show typical analyses of anthracites and semianthracites and Figs. I to 3 show graphically the range of analytical samples. Table 4 shows the commercial sizes of coals. Meta-anthracite and Graphitic Anthracite Typical analyses from virtually every field in the United States indicate that there are few if any extensive deposits of meta-anthracite. Some of the anthracites of Rhode Island contain almost negligible quantities of volatile and would thus fall into the meta-anthracite grouping on a basis of analyses alone. However, their other characteristics indicate that it is doubtful whether they should be considered as fuels at all, but rather as graphite. In fact, this material is being mined for use as foundry facings and furnace linings.4 A typical analysis of Fenners Lodge graphite,4 from Rhode Island, is: graphitic carbon, 55.9 per cent; silica (ash), 40.6; sulphur, 1.6; moisture, 1.9; volatile, o. Other Rhode Island coals possess percentages of volatile that would throw them into the normal anthracite rather than the meta-anthracite class. However, this "volatile" is nearly all noncombustible,3,4 being composed almost entirely of carbon dioxide and inert gases, therefore its definition as volatile is open to discussion, leaving the exact classification of the fuel a moot question. One factor is certain, Rhode Island coal is so different from nor-mal anthracite in both analysis and burning characteristics that it should have a

Jan 1, 1944

By Allen J. Johnson

Anthracite coals have been divided into three groups: (I) meta-anthracite, a high-carbon coal that is usually very slow to kindle and difficult to burn, at least on conventional equipment; (2) anthracite, a high-carbon low-volatile coal of widely accepted value as both a domestic and industrial fuel; and (3) semianthracite, a coal lying between anthracite and bituminous coal in carbon and volatile content, and also, generally speaking, in burning characteristics. Anthracite Groupings The technical differentiation between these groups, as defined by the A.S.A.-A.S.T.M. Sectional Committee on the Classification of Coals, is as shown in Table I. Tables 2 and 3 show typical analyses of anthracites and semianthracites and Figs. I to 3 show graphically the range of analytical samples. Table 4 shows the commercial sizes of coals. Meta-anthracite and Graphitic Anthracite Typical analyses from virtually every field in the United States indicate that there are few if any extensive deposits of meta-anthracite. Some of the anthracites of Rhode Island contain almost negligible quantities of volatile and would thus fall into the meta-anthracite grouping on a basis of analyses alone. However, their other characteristics indicate that it is doubtful whether they should be considered as fuels at all, but rather as graphite. In fact, this material is being mined for use as foundry facings and furnace linings.4 A typical analysis of Fenners Lodge graphite,4 from Rhode Island, is: graphitic carbon, 55.9 per cent; silica (ash), 40.6; sulphur, 1.6; moisture, 1.9; volatile, o. Other Rhode Island coals possess percentages of volatile that would throw them into the normal anthracite rather than the meta-anthracite class. However, this "volatile" is nearly all noncombustible,3,4 being composed almost entirely of carbon dioxide and inert gases, therefore its definition as volatile is open to discussion, leaving the exact classification of the fuel a moot question. One factor is certain, Rhode Island coal is so different from nor-mal anthracite in both analysis and burning characteristics that it should have a

Jan 1, 1944

PRESIDENT AND DIRECTOR CHESTER A. FULTON NEW YORK, N. Y. PAST PRESIDENTS AND DIRECTORS EUCENE MCAULIFFE OMAHA, NEBR. C. H. MATHEWSON NEW HAVEN, CONN. TREASURER AND DIRECTOR ANDREW FLETCHER NEW, YORK, N. Y.

Jan 1, 1944

By Edgar Rickard

E UGAR RICKARD comes of a long line of mining men and was born at Pontgibaud, France, in 1874, where his father was then in the course of his professional work. Later his father came to California and was until his death prominently connected with milling in that state and Nevada. Edgar Rickard grew up at Berkeley, attended the University of California, graduated in 1895 from the mechanical engineering course, and remained a year longer for post-graduate work in the College of Mining. His first job was as assarer for the Mountain Copper Co., Keswick, Cal., in 1896. The following year he was assayer and surveyor for the Cornucopia Mines, Oregon. In 1898, he joined the staff of the Venture Corporation, London, and for two years made examinations for them in various parts of the world. He served as mine manager at Cripple Creek and at the Briseis tin mine, in Tasmania. From 1901 to 1905, he was general manager of the Progress Mining Co. in Lower California, but when his cousin, T. A. Rickard, bought the Mining and Scientific Press he was persuaded to come to San Francisco as business manager of that periodical. A few years later the two cousins went to London and started the Mining Magewine there as a joint venture, Edgar being the business manager. In 1915, he took over control, T. A. Rickard returning to California to devote his time to the Mining u.rbd Scientific Press. In 1917 Edgar Rickard sold out to his British associates and came home to serve in the Food Administration through the war. Rickard was one of the first of the American engineers called to his staff when Herbert Hoover began his relief work by helping stranded Americans home at the be- ginning of the war and he has been with him constantly since in the Commission for Relief in Belgium, the

Jan 1, 1929

By AIME AIME

MEMBERS of the Engineering Education Committee held two meetings at Joplin preliminary to the opening of the main meeting there. The first was held on Sunday afternoon. It was attended by all who had arrived early enough and as among the dozen or' fifteen who were present the heads of a half dozen schools of mines were included it was a representative gathering. C: H. Fulton, chairman of the Committee presided and T. T. Read acted as secretary of the meeting. The chair., man reminded those present that last year there had been some discussion as to the advisability of the proposal, made by Edward Steidle, that a, separate society, devoted to education in the mineral industry, he organized. Many .people had felt that there are already so many societies in existence to demand one's time and attention, that it would be a mistake to add to their number and the counter suggestion had been made that the work of this committee could be so reorganized as to meet all the needs that a separate society could fill. He therefore presented for discussion these four' questions: (1) Shall a subcommittee .be appointed to study, and report in February, 1932, the possibility of the reorganization of the work of the Engineering Education Committee into the equivalent of an' Institute division; (2) if the work is so reorganized what shall be the relation of the work of the Committee (division) to the work of the-Society for the Promotion of Engineering Education; (3.): what are the, cardinal objectives of education for the mineral industry; and (4) what should be done as regards the movement in some institutions to plan their work-in the light of that being done in other institutions, for example, in geophysics?

Jan 1, 1931

By W. A. Hockings, M. E. Volin, A. L. Mular

Batch grinding tests at short times were made in a laboratory rod mill with 10 x 14 mesh quartzite in corn syrup-water mixtures of varying viscosity. The weight fraction broken and size modulus were found to be independent of viscosity up to 20 cp, but at higher viscosities breakage of the feed decreased while the size modulus increased. The mechanisms of the effect of viscosity are discussed on the basis of particle dynamics. The effect of viscosity of the suspending medium on grinding has not been accorded much attention, although both wet and dry grinding are used in bene-ficiation processes and the viscosities of water and air differ greatly. schweyerl investigated the rates of grinding of quartzite in a pebble mill with air, water and glycerol as the suspending media and found the rate in terms of new surface developed per thousand revolutions of the mill to be constant and dependent on viscosity up to 20,000 rev, but to decrease and become independent of viscosity for longer grinding times. Based on considerations of the drag forces exerted on suspended particles and on the grinding media under turbulent and laminar flow conditions, viscosity can be expected to inhibit the rate of grinding in a given system as it changes the flow conditions from turbulent to laminar. The objective of this study was to determine the effect of viscosity of the suspending fluid in the batch grinding of a homogeneous feed of uniform size for short residence times, a region of more practical interest than the long times investigated by Schweyer. In actual grinding operations, the viscosity of the fluid does not change, but the consistency (apparent viscosity) of the pulp increases with additions of fines. In this study the consistency of the pulp was not measured because it was thought that the grinding times were too short to alter the apparent viscosity appreciably.* *Minus 200 mesh quartz at 65% solids has an apparent viscosity of about 25 cp as measured by a simple consistometer. Personal communication from D. F. Kelsall to A. L. Mular. For the purposes of this study, the effect of viscosity on grinding can be shown sufficiently well on the basis of the cumulative weight fraction finer than the feed size at any time, and the size modulus, ku, of the finer than feed sizes. The parameter, ku, is obtained from a form of the Gaudin-Schuhmann equation. METHOD AND MATERIAL The grinding tests were accomplished in a laboratory rod mill 10-1/2 in. long and 8 in. bore with a 20-lb rod charge consisting of two 1-in., eight 3/4-in., eight 1/2-in., and eight 1/4-in. diam rods. The mill speed was 43.2 rpm. Charges of 400 g 10 x 14 mesh Wisconsin quartzite** were ground for times of 60, **Courtesy of Minnesota Mining and Mfg. Co. 120, 180 and 240 sec in 500 cc of fluid made up of corn syrup and water in measured proportions. The temperature of the pulp was measured immediately upon completion of grinding, and the size distribution of the quartzite was determined by a wash-wet-dry screening technique. Corn syrup was chosen because of its high viscosity and ideal viscous behavior, and also because its density is not greatly different from that of water. The viscosity of each fluid mixture was measured with an Ostwald viscometer at 25 C. and a correction was made for the temperature of the pulp according to tabulated values for sucrose solutions. The density differences were so small that they probably did not significantly affect breakage. RESULTS AND DISCUSSION The conditions of the grinding tests, computed viscosities, weight fractions finer than the feed size and values of a and ku are listed in Table I. The values of a and ku were taken from the linear portions of the log-log plots of cumulative weight fraction finer vs size for the various grinding times. The plots for tests in fluids of average viscosity 8.6 cp are shown in Fig. 1. In general all of the sets of curves were linear throughout most of the size

Jan 1, 1965

By N. A. Gokcen, M. N. Dastur

In metallurgical process industries a knowledge of true melting and casting temperatures is very essential for increasing the operating efficiency as well as improving the quality of the finished product. Optical pyrometers are widely used for the purpose because of their cheapness and ease of operation. It is an unfortunate fact, however, that this mode of measuring temperature entails a source of severe error inasmuch as with all non-black bodies, the temperature observed is always below the true temperature owing to deficient emissive power. Hence, the need for emissivity correction arises. In 1913 Bidwell1 obtained emissivity values of 0.36-0.48 for a temperature range of 1520-1800°C. He measured the true temperature of molten iron by sighting into a carbon cavity immersed in the iron under an atmosphere of hydrogen. In 1914 Burgess2 determined the emissivity of a smooth surface of liquid iron free from oxide to be 0.37 under an atmosphere of hydrogen. He claimed to have attained an accuracy of within 5°C at 1500°C with an optical pyrometer using monochromatic light. He reported that no difference appeared to exist between the emissivities of pure iron and of steels containing considerable percentages of carbon, nickel or manganese; nor was there any appreciable variation of emissivity with temperature from 1530 to 1571°C. Wensel and Roeser3 found an elnissivity value of 0.4 for temperatures above 1375°C for cast iron. The average emissivity value for carbon steels reported by Leiber,4 odd,5 Hase6 and Umino7 range from 0.4 to 0.45. Knowles and Sarjant8 made an extensive study of emissivity of molten iron and steel over a wide range of workshop and laboratory conditions. Observations of true temperature were made with immersion thermocouples, and correlated with apparent temperatures indicated by optical pyrorneter readings taken on the pouring stream as it passed over the lip of the crucible. The emissivity of Armco iron was shown to be of the order of 0.4, rising slightly with increasing temperature. But for plain carbon steels containing up to 1.0 pct carbon the emissivity was shown to fall slightly with increasing temperatures. The results of their investigation are in agreement with those of Guthmann.9 Naeser,10 Spencer," Todd5 and Hase6 in regard to the relation between emissivity and temperature for plain carbon steels. However, Goller12 has found a rise of emissivity with increasing temperature for the same steels. Results of several investigations are given in Fig 1. Measurement of True and Apparent Temperatures The necessity for an accurate optical temperature scale for liquid iron in studies of gas-metal equilibria led to this investigation. Experimental measurements were carried out in the induction furnace used by Dastur and Chipman13 in their studies of the reaction of hydrogen with oxygen in liquid iron. The furnace as modified for this work is shown in Fig 2. The atmosphere of the furnace was a mixture of purified argon with hydrogen containing a small controlled amount of water vapor. Gases were preheated by means of a platinum-10 pct rhodium resistance coil. The stream of hydrogen sweeping across the surface of niolten iron vir-

Jan 1, 1950

By Mark R. Lamb

THE various methods of treating pulp in air-agitation tanks offer problems for experiment and study which are fascinating as well as practical. The usual method heretofore has been to fill each tank in turn, agitate the mixture the required period and then discharge the treated pulp into a storage-tank, from which it. is drawn to the filter as required. A later method is to run the pulp from the tube-mill, classifier, thickener, or settler into the first of a set of tanks, and thence continuously or in series through the remaining tanks, finally drawing off the pulp to a continuous filter, or to a pulp-storage tank if the filter is of the intermittent type. It is this method which I propose to discuss here in a preliminary way, with the idea of going exhaustively into the examination of the results of a series of experiments in a later paper. It may be of interest to note that the design of a cyanide-plant has recently been completed in which the estimated cost of the agitation-tanks, storage-tanks, and pumps was 30 per cent higher for the charge-agitation arrangement than for the series plan. The first question in studying the series method is, "What is the actual period of treatment undergone by the pulp?? One first supposes that by chance some of the pulp may get through with little or no treatment, while other portions may stay in the tanks a needlessly long period. The former is not probable or even possible, and the latter is, practically, true to only a limited extent. The greater the number of tanks the greater is the percentage of chance that all the pulp will be treated equally. Without going into the mathematical analysis of the problem (which is of little value, since it is based on problematical premises), its important terms may be clearly grasped by thinking of, or " visualizing," the conditions when,

Jan 1, 1910

By R. Floyd Farris

Al thorough knowledge of the behavior of cement slurries under elevated temperatures and pressures is necessary in order to solve properly the many problems presented in deep-well cementing operations. In the earlier days of the petroleum industry the depths of wells were shallow as compared to those of today, and the subsurface temperatures and pressures were not of sufficient magnitude to affect seriously the problem of proper control of cement-slurry properties. Today, however, the search for new reserves has extended drilling to such depths that bottom-hole temperatures of more than 200°F. and bottom-hole pressures of 3000 to 5000 lb. are not uncommon. Moreover, there is every indication that within the next few years wells will be drilled to even greater depths and bottom-hole temperatures and pressures will be correspondingly higher than those with which we are concerned today. It has been realized for some time that the behavior of cement slurries at high temperatures and pressures might be very different from that at atmospheric tempera-ture-pressure conditions, but while the temperature effects have been investigated with a reasonable degree of thoroughness, the pressure effects have received little public attention. While the trend toward deeper drilling may make changes in cementing technique and the choice of cements imperative, it was the purpose of this investigation to consider factors having a bearing on the latter, only secondary consideration being ,given, for the present, to details of tech-nique and equipment for oil-field use. More specfically, the purpose of this work was to consider the effect of temperature and pressure upon the behavior of cement slurries. Although it has long been recognized that cements thicken and set rapidly with increasing temperatures, practical methods for the quantitative determination of these effects are comparatively recent developments. In 1935 Silcox and Rule1 presented such a method, describing apparatus designed to measure the consistency-time relationship of cement slurries at relatively high temperatures. The practical importance of this apparatus in furnishing useful data for the evaluation of cement slurries for cementing operations has been emphasized in various technical publications by such writers as E. L. Davis,~ I. F. Bing-ham,3 and J. E. Weiler.4 A paper describing the numerous tests now used to evaluate cements for oil wells was presented in 1939 by W. W. Robinson.= Robinson describes the Consistometer and the Thickening-Time Tester, showing similarity of data from the two devices, and points out that the purpose of each apparatus is to determine the allowable time that a cement may be pumped at a given temperature. At the present time, however, it is believed that results from the Thickening-Time Tester and the Consistometer have not given a

Jan 1, 1941