By F. J. Schuh

The drilling industry long has been plagued by failures in the bottom few joints of surface and intermediate casing strings. This paper presents an analysis of the various possible causes of failure and concludes that failures are caused by short-lived, high-energy torque impulses delivered from the drill string through the bit while drilling out the cementing plugs, cement and floating equipment. The magnitude of these torque impulses is shown to be a function of the rotational momentum of the drill string, and a method is derived to calculate the magnitude of these impulses. The available methods of strengthening the bottom joints are reviewed. It is concluded that, while present methods are ineffective, a combination of improved procedures for strengthening and minor restrictions on drillout practices will prevent failures. Introduction In most cases, failure in the bottom few joints of casing strings is not discovered until electric logs record that the bottom one, two or three joints have parted from the casing string and slipped down the hole. However, in some cases the parted section of casing uncovers a high-pressure or lost circulation zone, or shifts laterally restricting the passage of drilling equipment. In these instances extensive remedial work is required to realign the parted pieces and seal the exposed formations. Several methods used to strengthen the bottom joints of casing strings include locking set screws in the couplings, putting wedges in special collars, welding straps across the couplings, welding the couplings and, most recently, using epoxy resin-based, thread-locking compounds. Since none of these techniques has eliminated the problem, this study was initiated to find the cause of failures and to evaluate the available methods of prevention. Mechanics of Casing Failures An analysis of the various possible causes of failure indicates that the casing is unscrewed rather than broken and that therefore failure must occur before the shoe is drilled. Since there is no general agreement as to the causes of casing failure, some possible mechanisms were ATLANTIC RICHFIELD CO. DALLAS, TEX. considered in this analysis. Failure of the bottom joints of casing can occur by only one of three types of stress: tension, torsion or bending. The possible mechanisms of failure were evaluated by determining the forces required to cause casing failure by each of the stresses; and, where applicable, the possibility of failure by fatigue was considered. For casing to part under tension requires a downward load of more than the tensile strength of the casing. The lightest API weight H-40 grade casing requires a bit load on the bottom of the casing of 27,000 to 34,000 Ib per inch of bit diameter (Table 1). Since maximum drill collar weights seldom exceed 10,000 Ib per inch of bit diameter, it is apparent that casing strings cannot be parted by the downward load of the drill string. The second mechanism considered was failure by bending. This mechanism requires that the lowermost casing joints be free to be deflected laterally until the bending stress exceeds the strength of the pipe. To fail, the casing (at a height L above the shoe) requires a force and deflection' at the shoe of To deflect the casing shoe with the drill string obviously requires a dog-leg at the casing shoe. This dog-leg must have a rate of change equal to or greater than the change in curvature of the deflected casing, which is given by

Jan 1, 1969

By J. H. Wernick

IN temperature-gradient zone-melting1 a molten zone is moved through a solid or across a solid surface by the establishment of a temperature gradient. This technique has both practical and fundamental aspects. One practical application is to make p-n junctions for semiconductive devices, particularly for devices in which the junctions are desired within the semiconductor. From a fundamental point of view, the technique is being investigated as a method for determining diffusivities in liquid alloys, and preliminary diffusivity results have been reported by the writer." In this paper, the effects of crystal orientation, temperature, and molten zone thickness in temperature-gradient zone-melting, and the bearing of these effects on diffusivity measurements and n-p-n junction formation are discussed. Experimental Procedure An effect of crystal orientation was noted in early experiments. To facilitate its study, movements of wire zones across a surface, rather than through the body of a single crystal, were observed for various surface planes and travel directions. The experirr-entai setup is illustrated in Fig. 1. The graphite end-section for the high temperature heater has an apron about 1/16 in. above the upper surface of the crystal. This apron insures that the surface temperature of the block is equal to or greater than the temperature within the block at every point, Thus, the zone does not penetrate the block and convection in the liquid is minimized. The experi-through a block is shown in Fig. 2,

Jan 1, 1958

By John K. Berry

The handling and disposal of mine water is a much larger problem than is apparent at first glance. Many more tons of water are removed from underground coal mines in the United States each year than tons of coal. In the old anthracite region of Pennsylvania the average was around 36 tons of water for each ton of coal produced, while bituminous mines average about 5 or 6 tons. Water encountered in the mines may come from several different sources. In mines with light cover and without a firm solid roof, rain may seep directly into the workings. This is also true of deeper mines where pillar falls have broken the roof to the surface. The top under creek beds is generally faulty and broken and water comes through the roof at this point. Deeper mines are frequently overlain by water-bearing strata and pillar breaks and faulty top can admit water, while places running to the dip often accumulate water which comes up through the bottom. In all cases, except where passing under a year-round stream, the amount of water made is usually pretty closely connected with the weather-more water during the rainy season, less in the dry, although the deeper a mine is, the longer it is before changes in rainfall are felt. Another source of water, not connected with seasonal changes, is old water, accumulated over a period of time in abandoned workings of the mine, or from flooded adjacent mines. Here the water filters through the coal, the parting, or comes up through cracks in the bottom. Similarly, core holes, drilled to prospect the property, can be a source of unexpected water and modern safety requirements for dust-allaying water at the working faces can turn a pleasant working area into a soggy mess over the weekend if the system is not properly maintained and operated. Why water must be disposed is obvious. If allowed to accumulate, sooner or later the mine will fill up, or at least it will become "roofed" in low places, blocking ventilation and traffic. But it must also be controlled long before it reaches this stage. Water standing in the working faces is unpleasant for the men who have to work there and also cuts down on the amount of work they can do, as they must watch where they step all the time. It is especially unpleasant in low coal.

Jan 1, 1973

By A. W. Dana, F. J. Shortsleeve, A. R. Troiano

The phenomenon of flake formation which may occur during cooling or room temperature aging of large steel sections is caused by a combination of hydrogen and stress. As such, the transformation characteristics of austenite in a particular section play a major role in the occurrence of flakes. Isothermal and continuous cooling studies demonstrated that flake formation is particularly sensitive to nature, distribution, and relative proportions of the microconstituents in the cooled sections. In the absence of transformation stresses, abnormally high hydrogen contents could be tolerated without flaking. Flakes were not found in the absence of transformation stresses. No correlation existed between average hydrogen content and flake formation where cooling stresses were low. Hydrogen in the steel was a necessary but not sufficient condition for flake formation. DESPITE a long history of laboratory and commercial investigations, the mechanics of hairline crack or flake formation in large steel sections remains unresolved. Recent publications1-5 emphasize that flaking is still a serious problem.* immediate cause of flaking is the pressure exerted by entrapped hydrogen gas that collects in small internal cavities or voids during cooling. When the temperature of steel is low enough to preclude extensive plastic flow, the cavity pressures cause local brittle fractures (flakes). 2—The microsegregation and transformation stress theory. According to this theory, flaking results from stresses arising from the volume changes accompanying the formation of martensite and/or low temperature bainite after a large portion of the section has transformed at elevated temperatures. The proponents of the hydrogen theory suggest that stresses from other sources may be additive to the stresses produced by hydrogen and may, in some cases, provide the increment of stress necessary to produce flakes. However, the critical aspect of this theory is that no stress, except that produced by hydrogen pressure, is believed to be sufficient in itself to produce flakes. For practical considerations, this means that the only safe thermal cycle is one that reduces the hydrogen content to some low critical level below which flaking will not occur regardless of the state of transformation. On the other hand, the transformation stress theory does not rule out the embrittling effect of hydrogen. This theory simply proposes that flaking does not occur in the absence of transformation stresses. With the transformation stress theory as a basis, commercial antiflaking cycles would be designed to complete the transformation of austenite prior to cooling to ambient temperatures. Both of these theories appear compatible with industrial experience. Antiflaking cycles, such as cooling at extremely conservative rates or soaking for periods of time in the upper subcritical temperature ranges prior to cooling to ambient temperatures, may allow the following: 1—diffusion of hydrogen out of the section and, as a consequence, reduction of the hydrogen content to some safe minimum value (hydrogen pressure theory) and 2—complete decomposition of the austenite at rela-

Jan 1, 1956

By Eugene A. Stephenson, Leon J. Pepperberg

The natural gas industry is essentially a byproduct of the oil industry. When first discovered the gas was usually regarded as a nuisance, and even when found immediately associated with oil, or suspected to be so, it was customary to blow it freely into the air, in the hope that gas would shortly be replaced by a flow of oil. The early methods of production,' transportation, and utilization were neither economical nor efficient; the chief value of gas was based on its use as a fuel, with no regard to (1) its effect. upon the oil with which it was associated, (2) its importance as a lifting agent, or (3) to its possibilities for the manufacture of byproducts. The spread of scientific research among major gas and oil companies, manufacturers, and academic groups, has gradually brought recognition of the fact that many of the technical problems bearing on production, transportation and utilization are common to both the gas and the oil industry. A few of the problems that have received serious study, and from which highly gratifying results have been obtained, are: (1) gas measurement, (2) oil well and gas well capacity tests, (3) elimination of field waste, (4) design of pipe lines and compressor stations, (5) extraction of constituents which might interfere with the normal flow of gas through the line, (6) control of reservoir pressure, (7) estimation of reserves of both oil and gas, (8) control of water encroachment, (9) measurement of factors which influence fluid movement through sands, (10) solubility of gases in oils, (11) effect of dissolved gases upon the properties of the solution. These investigations have demonstrated that almost every problem relating to oil production also involves some phase of natural gas engineering. During the past 15 years the use of experimental methods for the discovery and measurement of obscure, influencing factors, which cannot be determined purely by hydrodynamic or thermodynamic analyses, have contributed much towards the progress made in solving the problems of the oil and gas industries. Most of the experimental work on

Jan 1, 1934

By P. Rama Rao, D. H. Sastry, T. R. Anantharaman

Deformation (a) and twin (a') stacking-fault densities in cold - wor ked filings of fcc silver alloys containing 2, 4, and 6 wt pct Sb have been estimated from Debye-Scherrer peak shifts and asymmetries, respectively. Evidence has been obtained for a possible strain-induced transformation in a two-phase alloy containing 9.0 zut pct Sb. Using Fourier analysis of X-ray line profiles, the effective particle sizes and root mean square strains have been determined for the three fcc alloys in the cold-worked condition. The values of the compound fault probability 0.5a + a') evaluated from peak shifts and asymmetries are in reasonable apeement with those derived from peak broadening. COLD work of fcc metals may produce both deformation and twin (also called growth) stacking faults, which can be detected and quantitatively estimated by X-ray diffraction techniques.' In addition to peak broadening, deformation faults produce a shift in peak positions and twin faults an asymmetry of the Debye-Scherrer reflections. Besides stacking faults, a reduction in the size of coherently diffracting domains and distortion within these also broaden the powder reflections of deformed fcc metals and alloys. Fourier analysis' of peak shapes provides quantitative infor- mation about the effective domain sizes, lattice strains, and also the compound fault probability (1.5a + a'), where a and a' represent deformation-and growth-fault density, respectively. The Paterson method2 for determination of a from peak shifts, the warren3 or wagner4 method for evaluation of a' from peak asymmetries, and the Fourier analysis for quantitative estimates of all the contributory causes of peak broadening have, in the course of the last decade, been extensively applied to obtain data for a number of deformed fcc metals and alloys. One of the useful results of earlier measurements of a in several solid solutions is a correlation between a and the solute valence as well as electron concentration per atom (p) in alloy systems based on a particular solvent. The work of Smallman and westmacott5 on Cu-Zn, Cu-A1, and Cu-Sn, of Foley, Cahn, and ~aynor' on Cu-Si and Cu-Ge, and of Rama Rao and Anantharaman7 on Cu-Si and Cu-Sb has revealed a common trend in the increase of a with p and also a with valency of the solute. Cahn and Davies' and Ad-ler and wagnerg have observed similar trends for silver alloys containing cadmium, indium, and tin. Data on a for silver alloys with a pentavalent solute element are not, however, available. It is primarily to fill this need that the present investigation on Ag-Sb alloys was undertaken. Utilizing the Patersonand Warren methods, values of a and a', respectively, have been determined in three silver alloys containing 2, 4, and 6 wt pct Sb. By Fourier analysis of the broadening of Debye-Scherrer peaks, effective particle sizes, lattice strains, and the compound fault probability (1.5a +a') have also been evaluated.

Jan 1, 1967

By John J. Schanz

INTRODUCTION The two prior Seeley W. Mudd books on mineral economics devoted their final chapters to themes having to do with the future. In 1932, the last chapter in Mineral Economics8 was "The Future Value of Mineral Property" by J. R. Finlay. Both the first edition (1959) of Economics of the Mineral Industries7 and the slightly revised second edition (1964) closed with "Minerals and Man's Future" by Zay Jeffries. We are not inclined in this third AIME volume on mineral economics to ignore the tradition of the prior volumes. Moreover, it always is fitting and proper to close a book about the mineral industries by examining in a rather general way the challenges and uncertainties that are perpetually strewn in our path as we pick our way into the future. Unlike its predecessor volumes, which were written to acquaint the nonspecialist with the economic characteristics of mineral resources and to provide data about the mineral industries, this edition was also designed with the mineral economics student and practicing specialist in mind. Thus it is anticipated that it will be both a reference as well as suitable for use as a textbook. Consequently, this closing examination of our changing perspectives about mineral resources devotes some space to the past events and current status of mineral economics as a field of study. The fears and forecasts of the past can be a perceptive and usually deflating way to begin an examination of the future. As we look up and down the track of time from the 1975 platform, we find that many of the past views of the future were transient in character, others were imperfect in their prognosis, while others were based on fears that now seemed unfounded. But down through the years some of the observations or expressions of concern have a persistency which perhaps reflects some elemental characteristics of mineral resources. On these "truths" rest our contemporary understanding of the economics of the mineral industries. The uncertainties and priorities for the next 25 or more years, not surprisingly, have a somewhat different mix than those that seemed most compelling to our predecessors in 1932 or 1959. So it is appropriate that we review how the perspective of the mineral economist has changed over the span of a half century. In light of the particular interest of AIME on the role technology must play, it is fitting that we close with some observations on that topic. THE EMERGENCE OF MINERAL ECONOMICS AS A FIELD OF STUDY The publication of Mineral Economics by the AIME in 1932 as a Seeley W. Mudd volume marked the end of emerging interest in

Jan 1, 1976

By Cyril Stanley Smith, Earl W. Palmer

STRIP of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner. Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal. The effect is known as "earing" and the protuberances are called "ears." Other terms frequently heard are "tips," "scallops," and "corners." It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip. 'Numerous papers dealing with various aspects of the earing effect have appeared in the literature, those listed in the references1 being especially interesting and valuable. An investigation of the factors influencing earing of brass cups has been in progress in the laboratories of the American Brass Co. for several years, and it was thought desirable to make some of the results generally available in summarized form. The present paper discusses many factors that do and do not contribute to ear formation. In addition, a section is devoted to methods of minimizing the earing tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced. In the space available, it is impossible to quote detailed experimental procedures and numerical results. However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill. MECHANISM OF EAR FORMATION It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions. The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup. A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip. The two-ear form that sometimes appears is also traceable to gauge variations. However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself.

Jan 1, 1942

By W. G. Pariseau, C. H. Schmuck, Fei Duan

The Homestake Mine is located in steeply dipping Precambrian metasediaents, an environment common to a number of world class ore bodies. Development of a pronounced plane of schistosity raises a question concerning the importance of anisotropy to the design of vertical crater retreat stopes. Little is known about the actual influence of elastic anisotropy in such -circumstances; even less is known about strength anisotropy. A cautious step- by-step approach was therefore taken towards a numerical assessment of the role of anisotropy in the analysis of stress and stability. The sequence of analyses begins with elementary test problems for computer program checks and proceeds to the analysis of a study stope area between the 6950 and 7100 Levels of the Homestake Mine. Anisotropy (orthotropy) is important at the Homestake Yine. No simple guidelines for evaluating in advance the need for plastic and strength anisotropy in design analysis appear to be forthcoming, ;o that some physical properties testing is necessary where the question is in doubt

Jan 1, 1984

By D. T. Goettge, E. L. Robinson

The phase changes occurring in low carbon steel during hot strip mill rolling are shown to be metallurgically significant when related to commonly used temperature control points, particularly finishing and coiling temperatures. In combination, these temperatures are shown to have an important influence on the level and uniformity of hardness, grain size, and carbide characteristics of the finished hot and cold rolled sheets. PRODUCTION of wide flat-rolled products ordinarily requires a number of operations in sequence to prepare the material for shipment to the customer. Most products are tailor-made for specific end uses, with each operation contributing certain properties to the finished material. Since the characteristics imparted to the semifinished product by a given step in processing carry through to the finished product in varying degrees, it is important that the intermediate stages of production of flat-rolled strip be carried out with the same care which characterizes the last or finishing operations. The step of hot strip mill rolling is common to the production of all of the various types of flat-rolled product; therefore, the hot strip rolling is an especially important point at which to recognize and control those variables which have an effect on the surface characteristics and metallurgical properties of the finished product and which influence the ease of conducting subsequent operations. Orders entered at a producing mill usually show an end use or describe an article or part into which the ordered product is to be fabricated. Applying his experience as to the properties necessary in a finished sheet to suit the end use and to perform successfully in the fabrication involved, the metallurgist selects a steel of suitable composition and deoxidation practice, and slabs of appropriate dimensions are produced for rolling on the hot strip mill. At this stage of processing, the metallurgist faces the problem of controlling hot strip mill practice in the light of his diagnosis of the properties necessary to meet the end use, paying due attention to the accompanying problem of producing a strip which can meet processing requirements on subsequent units in the mill. It is the purpose of this paper to describe some of the factors which he must consider in solving these problems and to indicate some of the principles which guide him. Equipment, Physical Requirements of the Strip, and Temperature Measurement The metallurgist must, of course, be familiar with the physical layout of the mill, the temperature-measuring equipment available, and the physical requirements of the hot strip product before he can apply his metallurgical knowledge to the problem; hence, the first section will consist of a brief discussion of these matters. The usual hot strip mill consists of reheating furnaces, five or six roughing stands including a scale-breaker, holding table, and second scalebreaker, six-stand finishing mill, runout table with spray cooling facilities, and coilers. A schematic diagram of a typical layout is shown in Fig. 1. Slab temperatures are primarily a function of heating time and furnace temperatures, while mill speeds, spray practice, drafting practice, available water pressure, temperature of the cooling water, cross sectional dimensions of the strip, coil size, and equipment limitations, either singly or in combination, determine what rolling temperatures are practical on a given hot strip mill unit. Thus, it is possible that a set of temperatures which can be utilized successfully on one mill cannot be used on another. However, adjustments in temperatures and rolling practice can usually be made to develop the desired metallurgical properties. In addition to the metallurgical properties developed through proper temperature control, the hot strip mill must also provide strip with certain physical attributes which may be summarized as follows: Strip Cross Section—The strip contour should conform to a section which will give the best results in the cold reduction operation. This is generally recognized as a strip with 0.001 to 0.003 in. crown or shoulder-to-shoulder convexity depending on width, and freedom from concave, flat, or wedge-shaped cross sections which cause metal buildup in cold reduction. Excessive drop off in thickness at the edges can also be very detrimental in cold reducing to light gages. Gage, Width, and Camber—All of these must be controlled. For example, rundown or increasing thickness from the front to the back of the coil results in nonuniformity in the thickness of hot-rolled sheet product and in added difficulty with gage and welds in cold reduction. Similarly, excessive width variation is the cause of guide trouble and excessive edge scrap at later stages of processing, while excessive camber is the source of a variety of processing troubles. Type of Oxide—Product intended for pickling should have a predominance of the type of oxide most easily removable in sulfuric acid. It is generally recognized that this type is obtained by use of maximum table cooling water and cold coiling

Jan 1, 1957

By William L. Fink, L. A. Willey

Since so many different curves have been published for the solid solubility of zinc in aluminum, it seems desirable to definitely establish the correct curve by two or more independent methods. The curve published in part I1t was based entirely upon X-ray measurements because the other methods employed at that time were not satisfactory. The present paper (the seventeenth of this series on high-purity aluminum alloys) describes the determination of the solid solubility of zinc in aluminum by the measurement of electrical resistivity at temperature and by microscopic examination. Since the publication of our part I in 1932, an investigation of the solubility relations in the aluminum-zinc system has been reported by Schmid and Wassermann2, who obtained their solubility results from lattice-parameter measurements on heat-treated and quenched specimens. The diagram that they published is shown in Fig. 1. In this investigation they also found by X-ray measurements that the parameter of the gamma phase changed continuously with zinc content and at such a rate that it would be identical with that of the beta phase at 60 atomic per cent zinc. It was concluded therefore that the beta and gamma phases, from the point of view of structural relationship, are one single phase. They also suggested a gap of immiscibility between 270" and 350" C. The complete boundary in this region could not be determined satisfactorily by the method employed and therefore was not shown in their diagram. Aluminum-zinc Alloys Materials Used.—Electrolytically refined aluminum3 was used in preparing the alloys for the work reported in this paper. Chemical analysis showed the following impurities: 0.004 to 0.005 per cent silicon, 0.006 to 0.008 per cent iron and 0.005 to 0.006 per cent copper. Also,

Jan 1, 1936

By Clarence O. Babcock

A simple robust rock bolt load gage was tested in the laboratory to define its characteristic behavior and to obtain a measure of its performance. The gage uses three vibrating wire sensors crimped 120 (2.09 rad) apart into the outer surface of a hollow cylindrical steel, tube. The resonant frequencies of the wires change as the gage is loaded. This change is read with a Creare meter developed for the Bureau of Mines on a previous contract to read borehole stress gage results. A statistical analysis of data obtained defines the variables influencing results. A U.S. patent (3,914,992) assigned by the author to the Dept. of the Interior was granted Oct. 28, 1975.

Jan 1, 1978

By R. H. Sweetser

There are probably as many variations of the method for blowing-in blast-furnaces as there are furnace superintendents. That some of these variations are poor practice is shown by the troublesome and sometimes disastrous experiences of many furnace-men, even within the last few years. It is the object of this paper to put on record a blowing-in practice that has gradually developed to the point where the results are sure, safe, and satisfactory; and also to bring into discussion several variations that are questionable. The blowing-in of a modern blast-furnace is one of the greatest of metallurgical operations. On its degree of success depends much of the future life of the lining and the subsequent behavior of the furnace; and it involves possibilities of danger to the men engaged in the work. The objects to be attained are the heating of the interior of the furnace to the high temperature necessary for smelting iron; the starting of the smelting process; and the gradual movement of the stock in its downward course. The most critical points are the placing of the kindling-wood, the " bringing down " of the gas, the closing of the iron-notch, and the first cast. The lighting of the first gas, the opening of the cinder-notch for the first flush, and the running of the first cast are anxious times for the superintendent and the furnace-men. Drying-Out the Furnace. As soon as a furnace-lining is completed it should be thoroughly dried out, whether it is to be blown-in soon or not; and the longer it is dried, the better for the furnace. At least two weeks is desirable; but good results can be had with 10 days of firing. The crudest and least desirable method of drying is to build a wood fire in the bottom of the furnace, throwing the wood in through a tuyere-arch, and using the iron-notch for

Jan 1, 1913

By Kazutami Imai

Effects of heavy metal ions on the growth and the activities of iron and sulfur oxidation of Thiobacillus ferrooxidans were investigated. Mercuric, silver, and stannous ions inhibited both of the growth and the iron- oxidizing enzyme system of the bacterium. On the other hand, uranyl ion inhibited the growth, but it gave almost no effect on the iron-oxidizing enzyme system. The inhibitory effect of uranyl sulfate on the growth of the bacterium is intensified on lowering the cultivating ' temperature from 28 ºC to 7 ºC. In the concentration of 10-3M, cadmium and copper ions inhibited colloidal sulfur-oxidizing activity of the cells 69 and 52 %, respectively, though they did not inhibit the iron-oxidizing activity at all in the concentration. On the contrary, stannous chloride did not givr any effect on the sulfur-oxidizing activity of the cells, though it inhibited the iron-oxidizing activity 55 % in the concentration of 10-3M. Several differences were observed among the cytochrome systems of cell-free extracts of the cells grown on iron and on sulfur.

Jan 1, 1976

By H. H. Power, Charles R. Houssiere

THE development of effective and dependable methods for drilling through the so-called "heaving-shale" horizons, particularly in the Gulf Coast area, is believed to comprise a major contribution to drilling technology, and to the task of finding and developing our undiscovered oil pools. Many mechanical remedies have been proposed and are in use in troublesome areas for combating heaving shale. However, in conducting a research program it was concluded that the physical and chemical properties of shales should be investigated, and the effect of added chemicals on such properties determined. As a preliminary step, the effect of chemicals on bentonitic suspensions was determined in accordance with recent contributions in the field of ceramics. The most plausible theoretical explanations for the behavior of the clay minerals involved are offered in the paper that follows. It is hoped that subsequent investigation of actual shale from troublesome wells will be aided by the initial work done on bentonitic suspensions of known composition. INTRODUCTION Formations variously designated as "heaving shale," "sloughing shale" and "caving shale" impede and may even preclude drilling of oil wells, particularly in certain parts of the Gulf Coast. In a previous paper1 it has been stated that the development of effective and dependable methods for drilling through these troublesome beds is believed to comprise a major contribution to drilling technology, and to the task of finding and developing our undiscovered oil pools. Since the attack on the heaving-shale problem by mechanical means was principally a matter of field investigation, it was concluded that a research program should be concerned with the physical and chemical properties of heaving shales, and the effect of added chemicals on such properties. It was realized that a study of shales required an advanced knowledge of the behavior of the individual clay minerals. A thorough review of the literature led the authors to the conclusion that very recent contributions2.3 in the field of ceramics furnished the most plausible theoretical explanations for the behavior of clay minerals. Accordingly, these fundamental ideas will be used in an attempt to explain the behavior of more complex systems whose composition and replaceable ions are known. In order to obtain comparable results it was deemed important to select an easily procurable clay of uniform characteristics. Accordingly, Wyoming bentonite, which is marketed under the name of "Volclay,"* was used for the preliminary investigations. The chemical analysis reported by the distribution is given as follows:

Jan 1, 1941

By Woolsey McA. Johnson

In metallurgical circles it is known widely, but somewhat vaguely, that the ease of reduction of metallic oxides depends largely on the way they hare been prepared. It is likewise known that different forms of carbon have different and greatly varying reducing powers. It is the purpose of this paper to show somewhat more definitely and scientifically these facts. Some years ago the writer published an account of pyrometric determinations of the reduction temperature of zinc oxides variously prepared and of several kinds.' In said paper it was shown that the temperature at which zinc oxide evolves zinc according to the equa-tion ZnO + C = Zn + CO depends upon the nature of the two reacting bodies. The determina-tions had a range of accuracy of from 2° to 6°C., whereas differences were found to amount to an extreme of 90' C. So the differences are real ones and must have a definite cause. The equation of boiling water, (H2O)4 D 4 (H2O) has a fixed temperature for equilibrium of 100° C. at 760 mm. pressure. In general, all equations reacting in the liquid or the gaseous phase have well-defined constant physical conditions which govern the equilibrium point and reaction velocities. In a reaction where we have one or more solid phases, the tempera ture conditions requisite for the unbalancing of the stable system are found to vary. These variations are due to the fact that in a solid there is a very complex molecule and it is not a question solely of the tearing away of two interlocked atoms, but also of the destruction of a complex molecule containing hundreds, or possibly thousands, of smaller molecules. In other words, there are two forces to be overcome: a certain

Jan 1, 1914

By F. C. Blickensderfer

During 1914 and 1915, extensive experiments were conducted at the concentrator of The Detroit Copper Mining Co. of Arizona, at Morenci, Ariz., in order to test the relative grinding efficiencies of the Marathon, the Chilean and the Hardinge Mills. The Marathon mill used in the experiments was the first one ever built by the manufacturers; and since this was the first time that it was given a thorough tryout, with such remarkable results, the data have been assembled in the following paper and submitted in the interests of the milling profession. Description of the Flow Sheet The concentrator flow sheet, as it existed at the time of these tests, is shown in Fig. 1. The total mill feed, as delivered from the crushing plant, had as its maximum size 1-in. material. This material was screened dry on Cole Zig-Zag screens fitted with 4-mesh openings; the oversize going to one pair of coarse rolls, the undersize to five Wilfley tables fitted with Butchart National riffles. The coarse-roll product was elevated and screened wet on Zig-Zag screens fitted with 4-mesh openings, the undersize going to the five tables mentioned above and the oversize to one pair of fine rolls. The fine-roll product was elevated and screened together with the coarse-roll product; so that, before any concentrating operations took place, the total mill feed was reduced to pass a 4-mesh screen. After concentration on Butchart-riffled tables, the tailings from these tables passed to de-sliming hoppers, where two products were formed, viz., an overflow and a discharge. The discharge constituted the feed for the Chilean mills. It contained 16 per cent. slime (—200 mesh) and 3 parts of water to 1 of solids. The concentrator was equipped regularly with four Chilean mills (Monadnock type) to the unit; but, in order to

Jan 1, 1917

By Oliver B. Hopkins

Peru produced approximately 15,838,610 bbl. of oil during 1938, which was 1,618,406 bbl. below its production during 1937. As in recent years, the entire output of the country came from the La Brea-Parinas, Lobitos-Restin, and Zorritos fields, which are all situated along the northwestern coast. Outside of the proven areas, the drilling of test wells was continued by the Peruvian Government on the reserved zone near Zorritos. Six wells have been completed or are drilling. Of these one is a gas well at 2619 ft. and one is dry at 1415 ft. It is reported that three standard and two rotary rigs are being used. In southern Peru, in the Pirin region north of Lake Titicaca, the Government made a geological study of the National Reserve. In eastern Peru, the Cia. Petrolera El Ganso Azul continued its activities in the montana region, where its first well was reported to have had a show of oil at 1000 feet. There was also renewal of leasing activity in eastern Peru, where approximately 380,000 acres of new leases were filed on near Contamana. La Brea-Parinas Estate.—Production of crude oil on this property of International Petroleum Co. Ltd. amounted to 13,137,988 bbl. which was

Jan 1, 1939

By Oliver B. Hopkins

Peru produced approximately 15,838,610 bbl. of oil during 1938, which was 1,618,406 bbl. below its production during 1937. As in recent years, the entire output of the country came from the La Brea-Parinas, Lobitos-Restin, and Zorritos fields, which are all situated along the northwestern coast. Outside of the proven areas, the drilling of test wells was continued by the Peruvian Government on the reserved zone near Zorritos. Six wells have been completed or are drilling. Of these one is a gas well at 2619 ft. and one is dry at 1415 ft. It is reported that three standard and two rotary rigs are being used. In southern Peru, in the Pirin region north of Lake Titicaca, the Government made a geological study of the National Reserve. In eastern Peru, the Cia. Petrolera El Ganso Azul continued its activities in the montana region, where its first well was reported to have had a show of oil at 1000 feet. There was also renewal of leasing activity in eastern Peru, where approximately 380,000 acres of new leases were filed on near Contamana. La Brea-Parinas Estate.—Production of crude oil on this property of International Petroleum Co. Ltd. amounted to 13,137,988 bbl. which was

Jan 1, 1939

Jan 1, 1925